CA1144680A - Thermoplastic polymer compositions - Google Patents

Thermoplastic polymer compositions

Info

Publication number
CA1144680A
CA1144680A CA000349885A CA349885A CA1144680A CA 1144680 A CA1144680 A CA 1144680A CA 000349885 A CA000349885 A CA 000349885A CA 349885 A CA349885 A CA 349885A CA 1144680 A CA1144680 A CA 1144680A
Authority
CA
Canada
Prior art keywords
parts
styrene
composition according
weight
poly
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired
Application number
CA000349885A
Other languages
French (fr)
Inventor
Shinichi Izawa
Jun Sugiyama
Nobutoshi Kosaka (Deceased)
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Asahi Dow Ltd
Original Assignee
Asahi Dow Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Asahi Dow Ltd filed Critical Asahi Dow Ltd
Application granted granted Critical
Publication of CA1144680A publication Critical patent/CA1144680A/en
Expired legal-status Critical Current

Abstract

Abstract of the Disclosure A thermoplastic polymer having well-balanced physical properties, especially impact strength and gloss, is provided, which comprises an aromatic polyether resin, a styrene polymer and/or rubber-enforced styrene polymer, and inorganic filler, and a thermoplastic elastomer.

Description

This invention relates to thermoplastic polymer compositions containing inorganic fillers and having well- -~
balanced physical properties.
Aromatic polyether resins become the object of public attention as being broadly employable plastics, - due'to thei'r superior properties, such as heat resistance, electrical characteristics, mechanical strength, resistivity to hot water, and acid- and alkali-resistivities. But, the biggest weakness of the resin is its insufficient mechanical strength, particularly its impact strength, when used as engineering plastics. To overcome the weakness, a process, in which'a styrene polymer is blended, has been disclosed, ''' for example,' in U.S. Patent No. 3,383,435. An attempt has been made,' in general, to blend an inorganic filler to the plastics, in order to increase the tinting susceptability and to improve weatherability, heat resistance, electrical characteristics, rigidity, etc. Such kind of improvement may be also performed, by blending an inorganic filler to -the aromatic polyether resins containing a rubber-enforced styrene polymer.` But, the problem in this case is in the remarkable decrease:of-the impact strength.
The'inventors hàve accomplished the present invention through'finding out a thermoplastic polymer composition having good appearance, which' avoids such'decrease'of the impact strength.' ~k 4~80 Thus, the present invention is to provide a thermoplastic polymer Composition having well-balanced physical properties, which comprises:
(a) an aromatic polyether resin, (b) a Styrene polymer and/or a rubber-enforced styrene polymer, (C) an inorganic filler, and (d) a thermoplastic elastomer, wherein the amount of the said thermoplastic elastomer is 0 from 10 to 150 parts by weight, based on 100 parts by weight of the said inorganic filler.
The aromatic polyether resin referred to in the present invention includes Various aromatic polyethers, such as poly~henylene ethers~ and itS styrene-grafted copolymers.
The polyphenylene ether referred to in the present invention includes the compounds represented by the general formula~

~ }n wherein Rl and R2 represent individually an alkyl group having 1 to 4 carbon atoms or a halogen atom, and n repreSentS the degree of polymerization. Specific examples of the polyphenylene ethers include poly ( 2,6-dimethylphenylene-, ~

;80 1,4-ether), poly(2,6-diethylphenylene~1,4-ether), poly(2-methyl-6-ethylphenylene-1,4-ether), poly(2-methyl-6-chlorophenylene-1,4-ether), poly(2,6-dichlorophenylene-1,4-ether), poly(2,6-di-n-propylphenylene-1,4-ether), poly(2-methyl-6-n-butylphenylene-1,4-ether) and poly(2-methyl-6-bromophenylene-1,4-ether~.
The degree of polymerization, n, is from 50 to 300, preferably from 70 to 250.
The styrene-grafted aromatic polyether referred to herein involves the above-mentioned polyethers, parti-cularly, polyphenylene ethers, grafted with a styrene compound, such as styrene, ~-methylstyrene, dimethyl-styrenes, vinyltoluenes, tert -butylstyrenes, chloro-styrenes, and other aromatic monovinyl compounds.
15 The styrene compound may be used in combination with a copolymerizable vinyl compound. For example, meth-acrylic acid esters such as methyl methacrylate or ethyl methacrylate,-acrylic acid esters such as butyl acrylate or 2-ethylhexyl acrylate, or unsaturated nitrile compounds such as acxylonitrile or methacrylonitrile can be employed.
Such a copolymerizable vinyl monomer is used in an amount of 0 to 100 parts by weight, preferably 0 to 70 parts by weight based on 100 parts by weight of the styrene compound.
Further, two or more styrene compounds may be used.
The amount of the styrene compound to be grafted with the aromatic polyether may be within the range of from 20 to 200 parts by weight, preferably from 25 to 170 parts -11~4f~80 by weight, based on 100 parts by weight of the polyether.
The styrene compound-grafted aromatic polyethers used in the invention may be prepared according to, for example, the processes disclosed in U.S. Patent No. 3,929,930 and U.S. Patent No. 4,097,556.
The styrene polymers as referred to in the present invention are those polymerized according to the conventional process from a styrene compound mentioned above or from a mixture of the styrene compound with a copolymerizable vinyl compound as mentioned above.
The rubber-enforced, or rubber-modified, styrene polymers mentioned in the present invention are the styrene polymers as described above, containing a cross-linked conjugated diolefin polymer, as rubber-enforcing component, in a dispersed island state. The rubber-enforced styrene polymer may be prepared by a mass polymerization process or a mass-suspension.polymerization process, or an emulsion polymerization process.
The typical examples of the conjugated diolefin polymers are polybutadiene, polyisoprene, styrene-butadiene copolymer, and the like.
The rubber enforced or modified styrene polymer comprises from 55 to 97 parts by weight of the polystyrene and 3 to 45 parts by weight of the conjugated diolefin-styrene graft copolymer in a dispersed island state.
The inorgan~c filler mentioned in the present , invention includes particulated inorganic compounds, such as titanium oxide, ~inc oxide, antimony oxide, white lead, barium sulfate, magnesium hydroxide, calcium carbonate, alumina, kaolin, talc, gypsum, clay, zeolite, carbon black, diatomaceous earth, asbestos, calcium silicate, powered mica, graphite, and the like. In order to minimize the decrease of impact strength and to keep the excellent appearance, the particle size of the inorganic filler is desirably of not larger than 5 ~.
The thermoplastic elastomer referred to in the present invention includes thermoplastic block elastomers from a conjugated diolefin and a styrene compound, and thermoplastic graft polymers from a polyolefin grafted with a styrene compound.
The thermoplastic block elastomers from a conju-gated diolefin and a styrene compound, as mentioned above, have the structure represented by the following general formula, (1) ( A - B )m+l and/or
(2) B ~ A - B )m+l and/or (3~ A-~B - A )m wherein A is a polymer block consisting of a styrene compound; B is a conjugated diolefin polymer block, and m is an integer from 1 to 20. The styrene compound may be seIected from those illustrated above. Butadiene, iso-prene and the like, may be mentioned as the typical .
~.

11~4f~80 conjugated diolefin.
Preferable thermoplastic block elastomer as mentioned in the above formula include styrene-butadiene block copolymer and styrene-isoprene block copolymer, in which A/B is S0/50 to 25/75, and the molecular weights of each blocks are 5,000 to 40,000 of A and 20,000 to 200,000 of B, with the total molecular weight of 50,000 to 300,000.
The polyolefin employed for the preparation of the thermoplastic graft polymer, as mentioned above, include low-density polyethylene, high density polyethylene, poly-propylene, ethylene-propylene copolymer, and copolymers of ethylene and a vinyl compound copolymerizable with ethylene.
The styrene compound to be grafted to the polyolefin is preferably selected from those illustrated above. The amount of the styrene compound grafted to the polyolefin as mentîoned above may be from 5 to 100 parts by weight, preferably from 7 to 50 parts by weight, based on 100 parts - by weight of the polyolefin.
In the present invention, the amount of the thermo-plastic elastomer (d) is from 10 to 150 parts by weîght, preferably from 20 to 50 parts by weight, based on 100 parts by weight of the inorganic filler (c). In case of less than 10 parts by weight of the amount, the decrease of impact strength can not be prevented. In case of higher than 150 parts by weight, g}oss and feeling at the surface is - deteriorated, and the apparent practicality is remarkably ~ .
.
. . .

injured. At the amount between 20 and 50 parts by weight, a resin composition having the most superior balance of the physical properties, is attained.
In the present invention, the amount of the aromatic polyether resin (a) is preferably and practically from 40 to 90 % by weight, based on the total amount of (a) and (b) components.
The amount of the inorganic filler (c) is desirably and practically from 1 to 30 ~ by weight, based on total weight of (a), (b), (c) and (d) components.
The quantitative relationship can be shown as the oblique lines portion on the triangular chart in Drawing.
Any method or means may be employed to blend the components which constitute the present invention.
Extruder, heating rolls, Banbury mixer, kneader, etc. are generally known and equally adaptable.
It is a matter of course that the thermoplastic polymer composition according to the invention may be added with other additives, such as plasticizer, tinting agent, flame retarder, stabilizer, etc.
- The plasticizer in the present invention means, in general, such additive as to improve processability and moldability of resins and to increase softness, elasticity, flexi~ility, etc. Exempli~ied are triphenyl phosphate, tricresyl phosphate, octyldiphenyl phosphate, and other phosphate esters; dioctyl phthalate, dibutyl phosphate, ethyl phthalylethyl glycolate, glycerol aliphatic carboxy-lates, neopentylpolyol aliphatic carboxylates, and other esters; N-ethyl-p-toluenesulfonamide, and other sulfon-amides; epoxidized linseed oil, epoxidized soybean oil,epoxidized butyl stearate, and other epoxidized fatty oils; low molecular weight polyolefins, liquid paraffin, solid paraffin, microwax, and other waxes. The tinting agent means such additive as to be used for coloring of resin pellets. Exemplified are azo, phthalocyanin, and other organic pigments; oxide, sulfide, and sulfate of metals, channel black, simple elements, and other inorganic pigments; and dyestuffs.
The flame retarder used in the invention means in~us~vel~ such organic and inorganic compounds as to be added to yield incombustibility to resins. Exemplified are phosphate esters employable as plasticizer, diphenyl chloride, triphenyl chloride, chlorinated naphthalin, tetrachlorophthalic anhydride, and other chlorinated aromatic compounds; tetrabromobisphenol-A, tetrabromo-phthalic anhydride, ~decabromodiphenyl ether, and other brominated aromatic compounds; and phosphorous-containing compounds represented by the following formula, Rl ~ R2 X=P O

,~, Rl ~J R

~p_C~2-N~--C~N~c N~C~2 wherein X represents O or S; Y represents H, OH or CH3;
and Rl and R , respectively, show H, CQ, Br, or alkyl radical of carbon number 1 to 4.
The stabilizer in the present invention means in general, such additive as to increase the stabilities to heat, light, oxygen, and other environmental conditions, during the molding process or usage of resins. Exemplified are barium licinolate, zinc licinolate, calcium stearate, barium stearate, zinc stearate, calcium laurate, and other metal soap type stabilizers; 2,4-bis-styrylphenol, 2,4,6-tristyrylphenol, 2,2'-methylenebis(4-methyl-6-tert.-butylphenol), and other phenol stabilizers; and benzo-phenone and benzotriazole light absorption agents.
The invention will more fully be described with respect to the working examples, in which all "part" and percentages are by weight.
In the examples, the impact strength means Izod ` .` 11~4~80 impact strength according to ASTM-256, and gloss as the standard for appearance i-s e-st~matea according to ASTM-523, with the results represented as gloss ~alue.
EXample 1 A mixture of 50 parts of polyphenylene ether obtained by polymerization of 2,6-dimethylphenol and having molecular weight of 14,000, 15 parts of styrene, and 1.5 parts of di-tert.-butyl peroxide is blended by means of HENSCHEL mixer, and the mixture is-treated with a twin-screw extruder at the resin temperature of 260C in melt-mixed state, thereby to complete the graft polymerization to form a styrene-grafted polyphenylene ether resin(as the aromatic polyether resin). A graft copolymer (as the rubber-enforced styrene polymer) is prepared by graft polymerization, in emulsion, of 60 parts of styrene onto 40 parts of poly-butadiene rubber latex of 0.3 ~ average particle size.
A mixture of 80 parts of the above mentioned aromatic polyether resin, 20 parts of the rubber-enforced styrene polymer, 5 parts of titanium oxide (0.4 ~ particle size), 20. and 2 parts (corresponding to 40 parts, based on 100 parts of the inorganic filler) of styrene-butadiene block copolymer (TUFP~ENE*of Asahi Chemical Inudstry Co., Ltd.) (as the thermoplastic elastomer), is homogeneously blended by means of a blender-and treated with a single-screw extruder at the cylinder temperature of 280C, thereby to complete melt-mi.xing.

~B 11 * trade maxk li~4~80 The thermoplastic polymer composition thus-obtained is formed to test pieces by means of a screw in-line type injection molding machine at cylinder temperature of 300C
and mold temperature of 90C. The physical properties of the test pieces show 17.5 Kg-cm/cm of Izod impact strength and 76 of gloss value.
Referring Example Eighty parts of the aromatic polyether resin and 20 parts of the rubber-enforced styrene polymer, the both being the same ones as employed in Example 1, are melt-mixed by means of a single-screw extruder, and formed to test pieces according to the same conditions as in Example 1.
The pieces have 22.0 Kg.cm/cm of Izod impact strength and 88 of gloss value.
Comparative Example 1 The'similar thermoplastic polymer composition as in Example 1, but containing no thermoplastic elastomer, is formed to test pieces according to the similar conditions as in Example'l, having 12.6 Kg-cm/cm of Izod impact strength and 82 of gloss value. It is obvious that the impact strength is remarkably decreased due to the inorganic filler, when compared with the result in Referring Example.
Example 2 The similar thermoplastic polymer composition as in Example l, excepting that the amount of the thermoplastic elastomer is 5 parts (corres'ponding to 100 parts, based on 1144~i80 100 parts of the inorganic filler), is formed to test pieces according to the similar conditions as in Example 1. The pieces show 18.3 Kg.cm/cm of Izod impact strength and 60 of gloss value.
Example 3 A thermoplastic polymer composition, prepared from 80 parts of the aromatic polyether resin similar to that in Example 1, 20 parts of the rubber-enforced styrene polymer similar to that in Example 1, 7 parts of titanium oxide, and 3 parts of styrene-grafted ethylene-methyl methacrylate copolymer (containing 10 % of methyl methacrylate and 15 ~ of styrene), as the thermoplastic elastomer, is formed to test pieces according to the similar conditions as in Example 1. The pieceS show 17.6 Kg-cm/cm of Izod impact strength and 72 of gloss value.
Example 4 ~ thermoplastic polymer composition, obtained from 80 parts of the aromatic polyether resin similar to that in Example 1, 20 parts of the rubber-enforced styrene polymer similar to that in Example 1, 10 parts of zinc oxide (0.8 particle size), and 5 parts (corresponding to 50 parts, based on 100 parts of the inorganic filler) of the thermo-plastic elastomer similar to that in Example 1, is formed - to test pieces according to the similar conditions as in Example 1, having 17.0 Kg cm/cm of Izod impact strength and 68 of gloss value.
: :.
., .

Comparative Example 2 The similar thermoplastic polymer composition as in Example 4, but containing no thermoplastic elastomer, is formed to test pieces according to the similar conditions as in Example 1, showing 10.5 Kg-cm/cm of Izod impact strength and 75 of gloss value.
Example 5 A thermoplastic polymer composition made from 80 parts of the aromatic polyether resin similar to that in Example 1, 20 parts of the rubber-enforced styrene polymer similar to that in Example 1, 10 parts of gypsum (5 ~
particle size), and 5 parts (corresponding to 50 parts, based on 100 parts of the inorganic filler) of the thermo-plastic elastomer similar to that in Example 1, is formed ~ 15 to test pieces according to the similar conditions as in Example l, showing 15.8 Kg-cm/cm of Izod impact strength - and 55 of gloss value.
Comparative Example 3 The similar thermoplastic polymer composition as in Example 5, but containing no thermoplastic elastomer, is formed to test pieces having 9.9 Kg-cm/cm of Izod impact strength and 70.4 of gloss value.
Example 6 A mixture of 50 parts of a polyphenylene ether obtained from 2,6-dimethylphenol and having number average molecular weight of 12,000, 10 parts of styrene, and 0.7 ` ` `` 11~4~80 part of di-tert.-butyl peroxide, is blended by means of HENSCHEL mixer, and then passed through a twin-screw extruder having 40 m/m diameter and kept at a temperature of 230C, thereby to obtain a graft copolymer. A mixture of 45 parts of the aromatic polyether resin thus-obtained, 40 parts of rubber-enforced polystyrene (STYRON*492 of ~sahi-Dow), 15-parts of t-he rubber-enforced styrene polymer as employed in Example'l, 10 parts of clay, and 4 parts of TUFPRENE is blended well by means of a blender, and then transferred into a single-screw extruder having 40 m/m diameter and kept at a temperature of 230C, thereby to obtain a thermoplastic polymer composition, having 14.4 Kg-cm/cm of Izod impact strength and 62 of gloss value.
'Example 7 A mixture of 60 parts of the aromatic polyether as employed in Example'6, 40 parts of a rubber-enforced polystyrene (STYRON XH801 of Asahi-Dow), 5 parts of powdered mica, and 7 parts of a low density polyethylene grafted with 20 % of styrene, is blended with a blender, and then passed through a single-screw extruder having 40 m/m diameter and kept at a temperature'of 230C, thereby to obtain a thermoplastic polymer composition, having 20.0 Kg-cm/cm of Izod impact strength and 70 of gloss value.
Example 8 A mixture of 50 parts of a polyphenylene ether B~ 15'-* trade mark obtained from 2,6-dimethylphenol and having number average molecular weight of 11,000, 8 parts of styrene, and 0.8 part of di-tert.-butyl peroxide is blended by means of HENSCHEL mixer, and then passed through a twin-screw extruder having 40 m/m diameter and kept at a temperature of 240C, thereby to obtain a graft copolymer. A mixture of 50 parts of the aromatic polyether resin thus-obtained, 50 parts of the rubber enforced polystyrene as employed in Example 7, 4 parts of talc, and 6 parts of TUFPRENE, is melt-kneaded, thereby to obtain a thermoplastic polymer composition, having 24.6 Kg-cm/cm of Izod impact strength and 58 of gloss value.
Example 9 A mixture of 75 parts of the aromatic polyether resin as employed in Example 8, 25 parts of a rubber enforced polystyrene (STYRON 492 of Asahi-Dow), 8 parts of titanium oxide, 1~5 parts of TUFPRENE and 4 parts of a low molecular weight polyethylene wax, is blended by means of a blender, and then melt-kneaded by passing through a twin-screw extruder having 40 m/m diameter and kept at a temperature of 220C, thereby to obtain a thermoplastic polymer composition, which has 16.2 Kg-cm/cm of Izod impact strength and 80 of gloss value.
Example 10 A mixture of 50 parts of a polyphenylene ether obtained from 2,6-dimethylphenol and having number average li~4~80 molecular weight of 11,000, 9 parts of styrene, 5 parts of an ethylene-methyl methacrylate copolymer containing 5 mole ~ of methyl methacrylate,' and 0.7 part of di-tert.-butyl peroxide, is blended by means of ~ENSCHEL mixer, and then passed thr'ough'a twin-screw extruder having 40 m/m diameter and kept at a temperature'of 220C, thereby to obtain a graft copolymer'. A mixture'of 85 parts of the thus-obtained aromatic polyether resin, 15 parts of a rubber-enforced polystyrene'polymer as employed in Example 1, 2 parts of titanium oxide, 0.2'part of carbon black, and 2 parts of styrene-butadiene-styrene type block copolymer (KRATON*-1101 of Shell), is blended by means of a blender, and then passed through a single-screw extruder havi~g 30 m/m diameter and kept at a temperature of 230C, to obtain a thermoplastic polymer'composition, having 21.6 Kg-cm/cm of Izod impact strength'and 66 of gloss value.
Examples l-l to 14 In preparing the thermoplastic polymer composition in Example'10, various kinds of additives are added, prior to the'treatment by the extruder having 30 m/m diameter.
The'results are'set forth in Table 1.

* trade mark 1~4~i~0 .

Table 1 Additives Physical properties Izod impact Amount strength Gloss Examples Kind (part) (Kg.cm/cm) value 11 triphenyl phosphate 8 16.9 75 12 calcium stearate' 0.5 2,2'-methylenebis(4- 22.2 69 methyl-6-tert.-butyl- 1.5 Iphenol 13 mineral oil 1.0 ~ decabromodiphenyl 13.9 62 ethe'r 10.5 14 low molecular weight 2.1 polyethylene 25.0 70 Zinc sulfide' 1.4 .
Example-15 A mixture'of 50 parts of a polyphenylene ether obtained from 2,6-dimethylphenol and having number average molecular weight of 12,400, 8 parts of styrene, 5 parts of ethylene-propyrene'copolymer, and 0.6 part of di-tert.-butyl peroxide,' is blended by means of HENSCHEL mixer, and then passed through a twin-screw extruder having 40 m/m diameter and kept at a ~emperature of 220C, to obtain a graft copolymer. A mixture of 55 parts of the thus-obtained aromatic polyether resin, 45 parts of a rubber-enforced polystyrene (STYRON XH801 of Asahi-Dow), 30 parts of calcium .
., .

11~4~80 silicate, 40 parts of TUFPRENE, and 5 parts of a low molecular weight polyethylene wax, is blended by means of a blender, and then passed through a single-screw extruder having 30 m/m diameter and kept at a temperature of 220C, thereby obtained a thermoplastic polymer composition, hav-ing 13.3 Kg-cm/cm of Izod impact strength and 51 of gloss value.
Example 16 A mixture of 65 parts of the aromatic polyether resin as employed in Example 15, 10 parts of the rubber-enforced styrene polymer as employed in Example 1, 25 parts of a rubber-enforced polystyrene (STYRON 475S of Asahi-Dow), 3 parts of titanium oxide, 1 part of TUFPRENE, and 4 parts of a phosphorous compound represented by the following formula;

~ P--CH2--NH-- C~ ~C--NH--CH2--P

~ ~

is blended by means of a blender, and then passed through a single-screw extruder having 40 m/m diameter and kept at a temperature of 230C, thereby to obtain a thermo-plastic polymer composition, having 31.0 Kg-cm/cm of Izod impact strength and 83` of gloss value.

.

1`1~4~80 Example 17 A mixture of 50 parts of the aromatic polyether resin as employed in Example 15, 50 parts of a rubber-enforced polystyrene (STYRON 492 of Asahi-Dow), 12 parts of asbestos, 16 parts of the low density polyethylene grafted with styrene as employed in Example 7, and 2 parts of triphenyl phosphate, is blended by means of a blender, and then passed through a twin-screw extruder having 30 m/m diameter and kept at a temperature of 210C, thereby to obtain a thermoplastic polymer composition, having 19.2 Kg-cm/cm of Izod impact strength and 60 of gloss value.
Example 18 A mixture of 70 parts of the aromatic polyether resin as employed in Example 15, 30 parts of a rubber-enforced polystyrene'(STYRON XH801 of Asahi-Dow), l.l parts of carbon black, 1.5 parts of TUFPRENE, and 1.0 part of mineral oil, is blended by means of a blender, and then passed through'a single-screw extruder having 30 m/m dia-meter and kept at a temperature of 230C, thereby to obtain a thermoplastic polymer composition, having 24.5 Kg-cm/cm of Izod impact strength and 76 of gloss value.
EXa~ple l9 A mixture'of 50 parts of a polyphenylene ether obtained from 2,6-dimethylphenol and having number average molecular weight of 14,500, 6 parts of styrene, and 0.4 part of di-tert.-butyl peroxide, is blended by means of : .

11~4~80 .

HENSCHEL mixer, and passed through a twin-screw extruder having 30 m/m diameter and kept at a temperature of 250C, to obtain a graft copolymer. A mixture'of 40 parts of the thus-obtained aromatic polyether resin, 60 parts of a rubber-enforced polystyrene'(STYRON~470 of Asahi-Dow), 1.5 parts of titanium oxide, 0.5 part of TUFPRENE* and 4 parts of a phosphorous compound represented by the following formula;
` ~
O P--' H

is blended by means of a blender, and passed through a single-screw extruder having 40 m/m diameter and kept at a ~ 15 temperature of 220C~thereby to obtain a thermoplastic polymer composition, having 14.6 Kg-cm/cm of Izod impact strength'and 88 of gloss value.
Exa~ple 20 , A mixture of 60 parts of the aromatic polyether resin as employed in Example l9, 40 parts of a rubber-enforced polystyrene tSTYRON*475S of Asahi-Dow), 20 parts of talc, 7 parts of an ethylene-propyrene copolymer resin grafted with'20 %'by weight of styrene, and 0.3 part of Channel Black* is blended by means of a blender, and then passed through'a twin-screw extruder having 40 m/m diameter and kept at a temperature'of 230C, thereby to obtain B

* trade mark 11'~4~80 a thermoplastic polymer composition, having 16.9 Xg-cm/cm of Izod impact strength ~nd 70 of gloss value.
Example 21 A mixture of 90 parts of the aromatic polyether resin as employed in Example 19, 10 parts of the rubber-enforced styrene polymer as employed in Example 1, 50 parts of clay, 10 parts of TUFPRENE, 8 parts of a low molecular weight polyethylene wax, and 1 part of mineral oil, is blended by means of a blender, and then passed through a twin-screw extruder having 30 m/m diameter and kept at a temperature of 260C, thereby to obtain a thermoplastic polymer composition, having 14.2 Kg-cm/cm of Izod impact strength and 59 of gloss value.
Example 22 A mixture of 70 parts of a polyphenylene ether prepared from 2,6-dimethylphenol and having num~er average molecular weight of 13,000, and 30 parts of polystyrene (STYRON 685 of Asahi-Dow), is melt-kneaded by passing through a twin-screw extruder having 30 m/m diameter and kept at a temperature of 290C, to obtain a graft copolymer.
A mixture of 70 parts of the thus-obtained aromatic poly-ether resin, 30 parts of a rubber-enforced polystyrene (STYRON XH801 of Asahi-Dow), 3 parts of graphite, 4 parts of the low density polyethylene grafted with styrene as employed in Example 7, 0~5 part of mineral oil, and 0.5 part of calcium stearate, is blended by means of a blender, 4 ,~-1 i80 and then passed through a single-screw extruder having 40 m/m diameter and kept at a t~mperature of 240C, thereby to obtain a thermoplastic polymer composition, having 16.8 Kg cm/cm of Izod impact strength and 75 of gloss value.
Example 23 A mixture of 45 parts of a polyphenylene ether obtained from 2,6-dimethylphenol and having number average molecular weight of 11,800, 55 parts of a rubber-enforced polystyrene (STYRON 475S of Asahi-Dow), 2.1 parts of powdered mica, 3 parts of TUFPRENE, and 3 parts of tri-phenyl phosphate, is blended by means of a blender, and passed through a twin-screw extruder having 30 m/m diameter and kept at a temperature of 300C, thereby to obtain a thermoplastic polymer composition, having 17.7 Kg-cm/cm of Izod. impact strength and 78 of gloss value.

Claims (44)

THE EMBODIMENTS OF THE INVENTION IN WHICH AN EXCLUSIVE
PROPERTY OR PRIVILEGE IS CLAIMED ARE DEFINED AS FOLLOWS:
1. A thermoplastic polymer composition com-prising:
(a) an aromatic polyether resin;
(b) a polymer selected from the group consist-ing of a styrene polymer, a rubber-enforced styrene poly-mer and mixtures thereof;
(c) an inorganic filler; and (d) a thermoplastic elastomer;
wherein, component (a) comprises from 40 to 90%, by weight, of components (a) and (b); component (c) com-prises from 1 to 30%, by weight, of components (a), (b), (c) and (d); and component (d) comprises from 10 to 150 parts, by weight, per 100 parts, by weight, of component (c).
2. A composition according to claim 1, wherein the said aromatic polyether resin is a polyphenylene ether.
3. A composition according to claim 1, wherein the said aromatic polyether resin is a polyphenylene ether grafted with a styrene compound.
4. A composition according to claim 3, wherein the amount of the styrene compound to be grafted with the aromatic polyether is within the range of from 20 to 200 parts by weight per 100 parts by weight of the poly-ether.
5. A composition according to claim 3, wherein the amount of the styrene compound to be grafted with the aromatic polyether is within the range of from 25 to 170 parts by weight per 100 parts by weight of the polyether.
6. A composition according to claim 2, wherein the polyphenylene ether is a polymer having the recurring unit of the formula:

wherein R1 and R2 represent individually an alkyl group having 1 to 4 carbon atoms or a halogen atom, and n represents the degree of polymerization.
7. A composition according to claim 6, wherein the degree of polymerization, n, is from 50 to 300.
8. A composition according to claim 6, wherein the degree of polymerization, n, is from 70 to 250.
9. A composition according to claims 2, 3 and 6, wherein the polyphenylene ether is a poly(2,6-dimethyl-phenylene-1,4-ether), poly(2,6-diethylphenylene-1,4-ether), poly(2-methyl-6-ethylphenylene-1,4-ether), poly(2-methyl-6-chlorophenylene-1,4-ether), poly(2,6-dichlorophenylene-1,4-ether), poly(2,6-di-n-propylphenylene-1,4-ether), poly(2-methyl-6-n-butylphenylene-1,4-ether) and poly(2-methyl-6-bromophenylene-1,4-ether).
10. A composition according to claims 2, 3 and 6, wherein the polyphenylene ether is a poly(2,6-dimethyl-phenylene-1,4-ether).
11. A composition according to claim 1, wherein the said rubber-enforced styrene polymer comprises from 55 to 97 parts by weight of polystyrene and 3 to 45 parts by weight of a conjugated diolefin-styrene graft copolymer in dispersed island state.
12. A composition according to claim 1, wherein the said styrene polymer is selected from the group consisting of polystyrene, poly-.alpha.-methylstyrene, styrene-acrylonitrile copolymer, styrene-methacrylonitrile copolymer, styrene-acrylic acid copolymer, styrene-methacrylic acid copolymer, and styrene-methacrylate ester copolymer.
13. A composition according to claim 1, wherein the said inorganic filler is selected from the group consisting of titanium oxide, zinc oxide, antimony oxide, white lead, barium sulfate, magnesium hydroxide, calcium carbonate, alumina, kaolin, talc, gypsum, clay, zeolite, carbon black, diatomaceous earth, asbestos, calcium silicate, powdered mica and graphite.
14. A composition according to claim 13, wherein the average diameter of the inorganic filler is not larger than about 5 microns.
15. A composition according to claim 1, wherein the said thermoplastic elastomer is a styrene-conjugated diolefin block copolymer.
16. A composition according to claim 15, wherein the styrene-conjugated diolefin block elastomer is a block elastomer represented by a formula selected the group consisting of:
(1) (A-B)m+1, (2) B?A-B)m+1, (3) A?B - A )m and mixtures thereof wherein A is a polymer block consisting of a styrene compound, B is a conjugated diolefin polymer block, and m is an integer from 1 to 20.
17. A composition according to claim 16, wherein the said block elastomer is a styrene-butadiene block copolymer, in which A/B is 50/50 to 25/75, and the molecular weights of each blocks are 5,000 to 40,000 of A and 20,000 to 200,000 of B, with the total molecular weight of 50,000 to 300,000.
18. A composition according to claim 1, wherein the said thermoplastic elastomer is a polyolefin grafted with a styrene compound.
19. A composition according to claim 18, wherein the said polyolefin is selected from the group consisting of low density polyethylene, high density polyethylene, poly-propylene, ethylene-propylene copolymer, and ethylene-polymerizable vinyl compound copolymer.
20. A composition according to claim 18, wherein the amount of the styrene compound to be grafted with the polyolefin is within the range of from 5 to 100 parts by weight per 100 parts by weight of the polyolefin.
21. A composition according to claim 18, wherein the amount of the styrene compound to be grafted with the polyolefin is within the range of from 7 to 50 parts by weight per 100 parts by weight of the polyolefin.
22. A composition according to claim 1, wherein the amount of the said aromatic polyether resin is from 40 to 90 % by weight, based on the total weight of the components (a) and (b).
23. A composition according to claim 1, wherein the amount of the said inorganic filler is from 1 to 30 % by weight, based on the total weight of the components (a), (b), (c), and (d).
24. A composition according to claim 1, wherein the amount of the said thermoplastic elastomer is from 20 to 50 parts by weight, per 100 parts by weight of the said inorganic filler.
25. A composition according to claim 1 comprising additionally an additive, including flame retardant, stabilizer, plasticizer and pigment.
26. A thermoplastic polymer composition consisting of (a) a polyphenylene ether grafted with a styrene compound, (b) a polymer selected the group consisting of a styrene polymer, a rubber-enforced styrene polymer and mixtures thereof.
(c) an inorganic filler, (d) a thermoplastic elastomer selected from styrene-conjugated diolefin block copolymer and styrenic polymer grafted polyolefin, and (e) an additive, including flame retardant, stabilizer, plasticizer and pigment, wherein the amount of the said thermoplastic elastomer is from 10 to 150 parts by weight, per 100 parts by weight of the said inorganic filler;
the amount of the said styrenic polymer grafted poly-phenylene ether is from 40 to 90 % by weight, based on the total weight of the components (a) and (b);
the amount of the said inorganic filler is from 1 to 30 %
by weight, based on the total weight of the components (a), (b), (c), and (d); and the amount of the said additive is upto 20 parts by weight, per 100 parts by weight of the components (a), (b), (c), and (d).
27. A composition according to claim 26, wherein the amount of the styrene compound to be grafted with the polyphenylene ether is within the range of from 20 to 200 parts by weight per 100 parts by weight of the poly-phenylene ether.
28. A composition according to claim 26, wherein the amount of the styrene compound to be grafted with the polyphenylene ether is within the range of from 25 to 170 parts by weight per 100 parts by weight of the poly-phenylene ether.
29. A composition according to claim 26, wherein the polyphenylene ether is a polymer having the recurring unit of the formula:

wherein R1 and R2 represent individually an alkyl group having 1 to 4 carbon atoms or a halogen atom, and n represents the degree of polymerization.
30. A composition according to claim 29, wherein the degree of polymerization, n, is from 50 to 300.
31. A composition according to claim 29, wherein the degree of polymerization, n, is from 70 to 250.
32. A composition according to claims 26, 27 and 28 wherein the polyphenylene ether is a poly(2,6-dimethyl-phenylene-1,4-ether), poly(2,6-diethylphenylene-1,4-ether), poly(2-methyl-6-ethylphenylene-1,4-ether), poly(2-methyl-6-chlorophenylene-1,4-ether), poly(2,6-dichlorophenylene-1,4-ether), poly(2,6-di-n-propylphenyiene-1,4-ether), poly(2-methyl-6-n-butylphenylene-1,4-ether) and poly(2-methyl-6-bromophenylene-1,4-ether).
33. A composition according to claims 26, 27 and 28, wherein the polyphenylene ether is a poly(2,6-dimethyl-phenylene-1,4-ether).
34. A composition according to claim 26, wherein the said rubber-enforced styrene polymer comprises from 55 to 97 parts by weight of polystyrene and 3 to 45 parts by weight of a conjugated diolefin-styrene graft copolymer in dispersed island state.
35. A composition according to claim 26, wherein the said styrene polymer is selected from the group consisting of polystyrene, poly-.alpha.-methylstyrene, styrene-acrylonitrile copolymer, styrene-methacrylonitrile copolymer, styrene-acrylic acid copolymer, styrene-methacrylic acid copolymer, and styrene-methacrylate ester copolymer.
36. A composition according to claim 26, wherein the said inorganic filler is selected from the group consisting of titanium oxide, zinc oxide, antimony oxide, white lead, barium sulfate, magnesium hydroxide, calcium carbonate, alumina, kaolin, talc, gypsum, clay, zeolite, carbon black, diatomaceous earth, asbestos, calcium silicate, powdered mica and graphite.
37. A composition according to claim 36, wherein the average diameter of the inorganic filler is not larger than about 5 microns.
38. A composition according to claim 26, wherein the said thermoplastic elastomer is a styrene-conjugated diolefin block copolymer.
39. A composition according to claim 38, wherein the styrene-conjugated diolefin block elastomer is a block elastomer represented by a formula selected from the group consisting of:
(1) (A-B)m+1, (2) B?A-B)m+1, (3) A?B-A)m and mixtures thereof wherein A is a polymer block consisting of a styrene compound, B is a conjugated diolefin polymer block, and m is an integer from 1 to 20.
40. A composition according to claim 39, wherein the said block elastomer is a styrene-butadiene block copolymer, in which A/B is 50/50 to 25/75, and the molecular weights of each blocks are 5,000 to 40,000 of A and 20,000 to 200,000 of B, with the total molecular weight of 50,000 to 300,000.
41. A composition according to claim 26, wherein the said thermoplastic elastomer is a polyolefin grafted with a styrene compound.
42. A composition according to claim 41, wherein the said polyolefin is selected from the group consisting of low density polyethylene, high density polyethylene, polypropylene, ethylene-propylene copolymer, and ethylene-polymerizable vinyl compound copolymer.
43. A composition according to claim 41, wherein the amount of the styrene compound to be grafted with the poly-olefin is within the range of from 5 to 100 parts by weight per 100 parts by weight of the polyolefin.
44. A composition according to claim 41, wherein the amount of the styrene compound to be grafted with the poly-olefin is within the range of from 7 to 50 parts by weight per 100 parts by weight of the polyolefin.
CA000349885A 1977-09-27 1980-04-15 Thermoplastic polymer compositions Expired CA1144680A (en)