CA2059522C

CA2059522C - Nonwoven fibrous embossed plastic film

Info

Publication number: CA2059522C
Application number: CA002059522A
Authority: CA
Inventors: Leopoldo V. Cancio; Thomas R. Ryle; Pai-Chuan Wu
Original assignee: Clopay Corp
Current assignee: Clopay Corp
Priority date: 1989-09-01
Filing date: 1990-08-15
Publication date: 1995-02-14
Anticipated expiration: 2010-08-15
Also published as: US5143774A; ES2041180T3; IE902988A1; DE69001611D1; AU6283990A; AR244990A1; WO1991003367A1; IE61245B1; NO920746L; EP0489782A1; CA2059522A1; DK0489782T3; DE69001611T2; NO920746D0; EP0489782B1; AU640407B2; BR9007604A; JPH0773880B2; JPH05500339A; MX173810B

Abstract

An embossed thermoplastic liquid barrier film is disclosed having a visible nonwoven fibrous three-dimensionally em-bossed pattern having raised fiber bosses (5) intersecting other raised fiber bosses (6) in the film on both sides. The films have thicknesses of about 0.5 to about 2 mils and an embossed depth to provide the visible nonwoven fibrous three-dimensionally em-bossed pattern with the film having a soft hand feel.

Description

WO9l/03367 PCT/US90/04612 ~ o59 5 22 NONWOVEN FIBROUS EMBOSSED PLASTIC FILM
BACKGROUND OF THE INVENTION
Beginning several decades ago, plastic film began to achieve wide spread use in the fabrication of many useful articles, quite often as a replacement for woven fabrics. Early in the development of plastic film as,a substitute for woven fabrics, patterns were created by imposing the image of a woven fabric into a film during the process of making the film. Wire screens, along with other mechanical implements, were later employed to create plastic films having various designs. As technology developed, metal rolls having engraved patterns were employed in the production of embossed plastic films which would simulate various designs. During this period of time, the person of ordinary skill in the art who made useful articles from plastic film, typically disposable diapers, covers, water repellent clothing, and the like, worked with the film on machinery and observed or studied its characteristics. Refinements or adjustments in the machinery as well as the material took place in order to produce useful articles from such~embossed plastic films on hi~h speed production machinery.
U.S. Patent No. 3,484,&3S which issued in 1969 is directed to a plastlc film embossed with a pattern simulatin~ a woven taffeta desi~n and t~.e fil.
had an especlally desirable characteristic of ed~e curl resistance during machine processing into useful articles. _m.bossed plasti~ fil~ disclosed i~ this patent offere~ si~nlficant improvement over t~.e earlier taffeta desi~n which existed in the prl_r art.

Another example of a simulated taffeta design is given in U.S. Patent No. 3,911,187. This describes the embossing of a film with a pattern of latitudinally and longitudinally alternating hollow protruberances and depressions on each side of the film, the sidewalls of adjacent protruberances and depressions being planarly connected and each hollow protruberance on one side of the film -forming a depression on the other. There are therefore no channels running between the edges of the film which is said to result in a greatly reduced light reflectivity or glass and tendency to edge-curl.
The simulated taffeta design disclosed in the above mentioned patents is only an example of many different designs created and employed by film fabricators in their effort to simulate woven fabrics or achieve other various visual appearances and physical properties which were advantageous from a manufacturing or consumer standpoint.

2~

Another one of such ~.any--desi~ns is referred to in the art as a matte finish. A matte finish has heretofore been characterlzed by a rather dull finish on a plastic film with no visually perceptible pat-tern. Matte finishes have been produced in films by the employment of sand-blasted embosslng rollers.
~ith the advancement of technciogy lncluding new formulations ln polymer comoosi~iGns of the polyolef1n type, particularly polyethylene, polvpropylene and polybutadiene and their copciv,.,ers, .he problem of handling various films has become complex. While there is a considerable amount of knowledge available to a perscn of skill in this art, behavio~s o~ poly-mers, or their properties under various physlcal con-ditions, such as machine stress and other conditions, are not readily understood. One might say the plastic film technology is, indeed, more of an art than a science and experience has proven that problems in this area of the art are not as easilv understood or solved owing to the unknown factors in handlinq s~ch polymeric compositions under machine st ess either in the manufacture or fabrication of such polymers into useful articles.
U.S. Pat. No. 4,376,147 ~hich issued in 1983 is directed to an embossed thermoplastic polyolefin film simulating a matte finish having excellent winding characteristics without edge curl, extremely low gloss even on both sldes and sood tape adhesion values, among o~her advantages, theretorcre unachieve.
- in prior matte films. In contradlstinct~on ~o the prior art sand-blasted matte ~ilms, ,he r ilm or the U.S. Pat. ~To, ~ / 376,i~7 has an embossed Fattern comprisin~ emDossed llnes or channel~ e areas whicr.
are parallel to the free lengthwise eàges cr .~e fil~.
The embossed lines provide a generall~ rectan~ular pattern with parallel and transverse lines numbering within the range of 15C to about 300 lines per inch (60 to 120 lines per centimetre).

Employing such an embossed pattern, the surface of the film appears to the unaided eye as a very dull sur-face. Up to that point in the state of the art the matte film of the mentioned patent achieved a balance of physical surface characteristics theretofore unachieved in known matte films.
More recently, issued U.S. Pat. No.

4,546,029 is directed to a random embossed thermo-plastic polyolefin film simulating a matte or dull finish having excellent roll or winding characteris-tics and processability without edge curl. Moreover, among its other important attributes, theretofore unachieved in prior art diaper matte films, it has relatively equal tape adhesion on both sides of the random embossed film. This is an important feature in diaper films which enables diapers to be used more effectively and conveniently without tearing the film.
The random pattern comprises an asymmetric arrangement of asymmetrically raised bosses and depressed areas on one side of the film, and correspondingly, underlying asymmetrically depressed areas and raised bosses on the opposite side of the film. The asymmetric bosses and depressions are of such height and area on the surfaces of both sides of the film such that the unaided eye of an observer does not detect any pattern in the film, even though it is an embossed random pattern. Such a combination of design and embossed depth had been unachleved in plastic films and, quite surprisin~ly, a unique balance or physical properties had been obtained.
As evidenced bv the above back~round, 2roduction of plastic f ilm has ~een a continuouslv i~provin~ technolo~y and there are demands for ~urthe-innovation.

SUMMARY OF T~E INVENTION
An embossed thermoplastic liquid barrier film in accordance with the invention has a visible three-dimensionally embossed pattern in the film on both sides, the pattern comprising raised areas and depressed areas therebetween, the film having a thickness of 0.5 to 2 mils (12.5 to 50 ~m) and an embossed depth sufficient to provide the visible embossed pattern characterised in that the pattern is a non-woven fibrous pattern, in that, on the film top side, the pattern comprises raised random fibre bosses intersecting other random fibre bosses the bosses being raised at different heights and having depressed areas therebetween to provide the visible pattern and, on the opposite film side, the pattern comprises a pattern substantially corresponding and underlying the film top side pattern, the top side pattern of raised random fibre bosses and depressed areas therebetween overlying respectively corresponding depressed fibre areas and raised fibre bosses on the underside of the film.
In contrast to plastic films simulating woven or matte-like finishes, the film simulates the appearance of a non-woven fibrous web. The non-woven fibrous embossed film provides a barrier against liquid and yet indeed provides the appearance and feel of a non-woven fibrous web.
In one of its aspects, the non-woven fibrous embossed plastic film provides a three-dimensional effect with a realistic visual appearance. In other words, upon inspection by an unaided eye, individual fibres appear to stand out from the surface and a non-woven fibrous appearance is created. Yet, the film does provide a soft hand feel thereby eliminating the artificial effect otherwise attributable to plastic substrate. Accordingly, a new dimension in embossed plastic films is provided after several decades of embossed film development as set forth ln the back~round of this invention.
The visible nonwoven fibrous embossed pattern comprises on the film tCp side ralsed random fiber bosses intersectin~ other random fiber ~osses.
The bosses are raised at varyin~ hei~hts and have depressed areas there~etween to provide a three-di.~,en-sionally visible pattern. On t.~e opposite fil~ side another visible nonwoven fibrous embossed pattern is p-ovided substantially corres?onding to and underi~ina the film top side pattern.

The films are relatively thin, particularly on the order of about 0.5 to about 2 mils (12.5 to 50 ~m). The surface of the film is dull and has a gloss on the order of about 4 to about 7 as measured by 45 head. It has been surprisingly found that a non-woven fibrous texture may be embossed in a plastic film to provide a three-dimensional effect and yet have a soft hand feel with a non-glossy surface. The overall embossed depth of the film will vary but will tend to be on the order of about 6 to about 10 mils (lS0 to 250 ~m) for a film of about 0.5 to 2 mils (12.5 to 50 ~m) thickness.

DETAILS OF T~E INVENTION
The nonwoven fibrous e~bosseà fil~ is ~ade from any one of a number of sui.able plastic ~ate-rials, preferably of the thermoDlastic type and particularly polyolefins including polyethylene, polypropylene, polybutadiene and copolymers of such polyolefins such as ethylene vinyl acetate, ethylene methyl acrylate and ethylene propylene diene monomer (EPDM). These polymers may be modified with conven-tional fillers, stabilizers, additives and the like.
These film materials are e~bossed to give the nonwoven fibrous appearance for a number of applications includinq diapers, napkins and underpad applications as well as other r,edical disposable articles w-here the nonwoven appearance is deslrable.
A preferred polyolefin film is ultralow, low density or medium density polyethylene. As is under-stood in the art, ultralow density polyethylene has a density of 0.890-0.912 with increasinq density to 0.916 to 0.935 for low density polyethylene. Linear low density polyethylene having a density of 0.918 to 0.941 is also very suitable.
Blends of the above ultralow density polyethylene, conventional high pressure polyethylene and low pressure linear low density polyethylene may be emploved. For instance, 80% ultralow densi.y polyethylene at a density of 0.912 may be blenaed with 20% high pressure low density polyethylene at a density of 0.922 with a blend density of approximately 0.914. In order to achieve a soft and quiet product, the modulus, referred to as 1% secant modulus, of the 2~95~2 formulated film may vary within the range of about 5,000 psi to 40,000 psi (35 to 270 MN/m2), with 5,000 psi to 20,000 psi (35 to 135 MN/m2) preferred. A soft and quiet product is obtained with polyethylene having a modulus in the range of about 5,000 psi to 20,000 psi (35 to 135 MN/m2). A modulus in this range provides for a soft, quiet and good hand-feel diaper for instance.
The above plastic films can be embossed with the nonwoven fibrous design according to any one of a number of well-known techniques. A preferred method involves the introduction of thermoplastic material in a plastic state between a steel embossing roll and a smooth resilient roll or rubber roll which form a nip for embossing film. These techniques are considered to be conventional as described in the above mentioned patents.
The invention will be further understood with reference to the drawings in which:
Fig. 1 is a non-magnified photographic view of the nonwoven fibrous embossed film of this invention from a top (metal embossing roll side) of the film;
Fig. 2 is a non-magnified photographic view of the embossed film of Fig. 1 when viewed from the underside (rubber roll side) of the film;

VLS:jj W O 91/03367 PC~r/US90/04612 Fig. 3 is a non-magnified photographic view of another nonwoven fibrous film of this invention from a top (metal embossing roll side) of the film;
Fig. 4 is a non-magnified photographic view of the underside of the film of Fig. 3.
Fig. 5 is a photograph of a film like that shown in Fig. 1 on a magnified scale about 25x that shown in Fig. 1.
Fig. 6 is a diagramatic partial cross-section through a film like that shown in Fig. 5.
With reference to the photographs of Figs. 1and 3, a polyethylene film is shown in top view on the metal roll side of the film (Fig. 1) and the underside of the film (Fig. 3). With reference to the Fig. 1 top view, raised random fiber bosses 5 are shown intersecting other random fiber bosses 6 in three-dimensions with respect to one another. This is better shown in the magnified view of Fig. 5 showing the top view of a film like that shown in Fig. 1 on a magnified scale of 25x. Thus, with reference to both Figs. 1 and 5, the bosses 5, 6 are raised at different heights and also have depressed areas therebetween in order to provide the visual appearance of a nonwoven fibrous web. The embossed continuous film still is a liquid barrier. On the underside or rubber roll side of the film, as shown in Fig. 2, the raised random fiber bosses 7 intersect raised random fiber bosses 8 20~9~22 to substantially underly and correspond to the visual pattern on the top side of the thinly embossed film. The photographic representations of the underside or rubber roll side of the film are not intended to correspond exactly with the photographic top or metal roll side of Figure 1. Nevertheless, it is to be understood that in the thin films on the order of about 0.5 to about 2 mils thickness (12.5 to 50 ~m), the top side pattern of raised random fiber bosses and surrounding depresslons have corresponding depressed fibers and raised fiber areas or bosses on the underside of the film. This is diagramatically shown in Fig. 6 in partial cross-section showing the relationship of top side fiber bosses 5, 6 to underside fiber bosses 7, 8.
Top side bosses S, 6 intersect and are raised at different heights and have depressed areas there-between generally shown at 13 in Fig. 6. It should be clearly understood that Fig. 6 is diagramatic and not intended to represent the exact film structure because thin plastic film and polymers do not predictably behave when an actual slice would be made there~hrough to relieve s.resses in molecular s.ructure. This will be understood by a person of skill in this art.
The nonwoven fibrous pattern is actually formed by an engraving roll havlng a distribution of elonaated fiber depressions and raised fiber areas simulating nonwoven fibers in three-dimensional arr2y.

11 2059~22 The process of engraving, master tooling and detalls thereof are no~ essential to this inventior,. With reference to the photographic magnifications of the drawing, the r,etai roll side or the embosslr.a roil is mirrored in the plastic film.
With respect to Figs. 2 and 4 another embodiment of the nonwoven fibrous plastic film is shown from the t^F and opposite side of the t~inly embossed film. The same characterizatlon ~ith respec~
to the film sho~n in Flgs. 1 and ~ applies tc Figs. 2 and 4 except 'hat the embossed pattern o. r~ised random fiber bosses 9 intersect fiber bosses 10 on the top side of Fig. 2 to provide a finer fiber visual effect in three dimensions than that of Figs. 1 and 3 in magnified vie~. The opposite side as shown in Fig.
4 substantially corresponds to the top side of Fig. 2 as providing a finer nonwoven fibrous appearance raised random fiber bosses 11 intersectlng fiber bosses 12. As lndicated above, in order to provide a three-dimensior,al affect, the depth of the emDoss must be sufficient to ~ive the appearance and fiber feel.
Thus, ln fil~s on the order cr about 0.5 to 2bout 2 mils (12.5 to 50 ~m) in thickness, an embossed depth on the order of about 6 to about 10 mils (150 to 250 ~m) is obtained. As demonstrated by Figures 1-5, the average fibre diameter may vary from about 5 to about 100 mils (0.125 to 2.5 mm) and may be continuous filaments or staple fibres of 1 to 3 inches (25 mm to 75 mm) in length, W O 91/03367 PC~r/US90/04612 depending upon the nonwoven fibrous appearance that is being sought.
The "embossed depth" is determined by (a) measuring overall cross-sectional thickness of the film from the top side of the raised fiber bosses to the opposite undermost fiber ridges (or bosses) on the underside, (b) measuring or determining the average film thickness and subtracting (a) from (b). This measurement may be made in a number of manners. For instance, a standard l inch micrometer may be used in a manner known to those of ordinary skill in the art, to measure the embossed depth by measuring (a) and (b). For purposes of this invention, the film thick-ness may be calculated, based on film density. The lS embossed depth is the difference between the film embossed gauge as measured by a micrometer and the film thickness calculated on the basis of film den-sity. The film embossed gauge is normally measured by a TMI Model 549M load micrometer with a 2 inch diameter anvil.
The nonwoven fibrous embossed pattern as photographically depicted as shown in Figs. 1-4 has a number of advantages as indicated above. The pattern simulates a nonwoven fibrous fabric or cloth appear-ance heretofore unachieved in embossed plastic films.It has also been found that this film may be processed advantageously and employed in diaper, napkin and underpad applications as well as other medical dispos-able articles where a nonwoven appearance is desir-able. Amonq its other unique featur~s, the film has very low gloss on both sldes. rilms of this invention may be provided with the nonwoven appearance and still have a soft, quite and good hand-feel for these various applications.
A nonwoven fibrous embossed plastic film is formed by embossing with a system of embossinq rollers as well understood at this ~lme in the art with reference to the patents incorporated in the back-ground of the invention. The àescriptions in these patents are incorporated herein by reference so that one of ordinary skill in the art may obtain further details of embossinq processes.
In a preferred form, low to medium density polyethylene, for instance, is formed into a nonwoven fibrous film by a slot-die extrusion means. For example, the low to ~edium density poly-ethylene material is heated to a temperature of about 300-500 F (150-260 C) and then introduced in a web form through a slot into the nip of a steel and rubber roll system referred to above. The plastic material, upon being introduced between the nip of the rolls, is film-formed and at the same time textured with the non-woven fibrous embossed pattern of the steel embossing roll. Under suitable embossing pressure, for instance 14 20~9522 of about 75-120 pounds per linear inch (130-210 N/cm), a thin film having the embossed design may be produced. In achieving the preferred film thickness of between about 0.5 to about 2 mils (12.5 to 50 ~m), along with the necessary emboss depth of about 6 to about 10 mils (150 to 250 ~m), conditions are contrclled in a manner ~ell within the skill of those knowledgeable in the art of producing e~bossed ~il~s with ,he understanding or this lnvention. ~he factors wnicn are considered ~ay ~e varle~ dependina upon the Fias~ aterial used znc :~e c.^arac-e~ S~i_a to be obtalned in the resultan~ hus, process conditions ~hat are obviously con~-siled to produce embossed f~l~ include temperature, ~ressu-e exerted between the nip of the embossing roll or system, the depth of the engraved design on the steel roll and the hardness of the rubber roll. Again, with reference to Figs. 1-2, a specific nonwoven fibrous e~bossed film is shown and may be produced accor~ nq .o the above embossing technique that results in a ccarse entangled fiber appearance with a surface gloss o~ aDout ~-7 as determined by a 45 head technique ~.~ST~-' Techn~sue D-2457). The overall ~aterial thic~;ness 5 O~ rhe order of about 1.2 mils ~30 ~m) with an overall depth of about 8 (200 ~m). For a specific polyethylene film as shown by Figures 3-4, a finer fibrous appearance is demonstrated by the surface gloss of about 5.5 and a material thickness of about 1.2 (30 ~m) with an overall embossed depth of about 8 (200 ~m).

WO9l/03367 PCT/US90/04612 ^

Having described the above invention in its preferred parameters, various modifications may be made as understood by a person of ordinary skill in this art in view of this specification.
What is claimed is:

Claims

1. An embossed thermoplastic liquid barrier film having a visible three-dimensionally embossed pattern in the film on both sides, the pattern comprising raised areas and depressed areas therebetween, the film having a thickness of 0.5 to 2 mils (12.5 to 50 µm) and an embossed depth sufficient to provide the visible embossed pattern characterised in that the pattern is a non-woven fibrous pattern, and in that, on the film top side, the pattern comprises raised random fibre bosses (5, 9) intersecting other random fibre bosses (6, 10), the bosses (6, 10) being raised at different heights and having depressed areas therebetween to provide the visible pattern and, on the opposite film side, the pattern comprises a pattern substantially corresponding and underlying the film top side pattern, the top side pattern of raised random fibre bosses (5, 6, 9, 10) and depressed areas therebetween overlying respectively corresponding depressed fibre areas and raised fibre bosses (7, 8, 11, 12) on the underside of the film.

2. An embossed film as claimed in Claim 1 wherein the thermoplastic is polyethylene or polypropylene or a copolymer thereof.

3. An embossed film as claimed in Claim 1 wherein the thermoplastic is low to medium density polyethylene.

4. An embossed polyethylene liquid barrier diaper or pad film for disposable hygienic and surgical liquid barrier applications having a visible three-dimensionally embossed pattern in the film on both sides, the film having a thickness of 0.5 to 2 mils (12.5 to 50 µm) characterised in that the film has an embossed depth of 6 to 10 mils (150 to 250 µm), in that the pattern is a non-woven fibrous pattern, and in that, on the film top side, the pattern comprises raised random fibre bosses (5, 9) intersecting other random fibre bosses (6, 10), the bosses (6, 10) being raised at different heights and having depressed areas therebetween to provide the visible pattern and, on the opposite film side, the pattern comprises a pattern substantially corresponding and underlying the film top side pattern, the top side pattern of raised random fibre bosses (5, 6, 9, 10) and depressed areas therebetween overlying respectively corresponding depressed fibre areas and raised fibre bosses (7, 8, 11, 12) on the underside of the film.

5. An embossed film as claimed in any one of claims 1, 2, 3 or 4 wherein the film has a thickness of 1 mil (25 µm) and an embossed depth of 8 mils (200 µm).