CA2141536C - Abrasion wear resistant coated substrate product - Google Patents

Abrasion wear resistant coated substrate product Download PDF

Info

Publication number
CA2141536C
CA2141536C CA002141536A CA2141536A CA2141536C CA 2141536 C CA2141536 C CA 2141536C CA 002141536 A CA002141536 A CA 002141536A CA 2141536 A CA2141536 A CA 2141536A CA 2141536 C CA2141536 C CA 2141536C
Authority
CA
Canada
Prior art keywords
interlayer
oxide
diamond
thickness
nitride
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
CA002141536A
Other languages
French (fr)
Other versions
CA2141536A1 (en
Inventor
Bradley J. Knapp
Fred M. Kimock
Steven James Finke
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Morgan Chemical Products Inc
Original Assignee
Morgan Chemical Products Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Morgan Chemical Products Inc filed Critical Morgan Chemical Products Inc
Publication of CA2141536A1 publication Critical patent/CA2141536A1/en
Application granted granted Critical
Publication of CA2141536C publication Critical patent/CA2141536C/en
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Abstract

The coated substrate product finds particular application in eyeglass and sunglass lenses, architectural glass, analytical instrument windows, automotive windshields and laser bar code scanners for u se in retail stores and supermarkets. The product has greatly improved wear resistance for severe abrasive environments and comprises a substantially optically transparent substrate (1), a chemically vapor deposited first interlayer (2) bonded to the substra te and a chemically vapor deposited outer layer (3) of substantially optically transparent diamond-like carbon bonded to the interlayer and away from the substrate.

Description

ABRASION FEAR RESISTANT COATED SUBSTRATE PRODUCT
FIELD OF THE INVENTION
This invention relates generally to coated substrate products. More particularly, the invention relates to a substantially optically transparent coated substrate product comprised of a parent substrate, one or more interlayers and a diamond-like carbon layer, and to a method for producing same.
BACKGROUND OF THE INVENTION
The properties of glass make it an ideal substrate material for use in many applications. In particular, the combination of optical transparency, with reasonable strength at a nominal cost, allows the widespread use of glass products.
Glass, however, does suffer from several limitations. Glass is not a particularly hard material, and consequently it abrades in many applications. Additionally, class is chemically reactive with many alkaline substances and with hydrofluoric acid. New applications and superior performance in existing applications could be thus realized for glass products if glass were more abrasion resistant and less chemically reactive. Examples of glass products which could benefit from improv"d abrasion resistance include eyeglass and sunglass lenses, architectural glass, analytical instrument windows, automotive windshields and laser bar code scanners for use in retail stores and supermarkets.
Diamond-like carbon films (DLC) are well known in the art and have been recognized as potential coatings to enhance the abrasion resistance of various substrate materials, including glass. The DLC coatings possess excellent optical properties and exhibit excellent resistance to abrasion and chemical attack by various acids, including hydrofluoric acid. However, it has been found that the DLC coatings will impart improved abrasion resistance to a substrate only if the adherence of the coating to the parent substrate is excellent.
The most obvious and common approach to coating the glass substrate is to apply the DLC coating directly onto a clean glass surface.
However, this approach often results in a DLC coating which displays poor adhesion and therefore, poor abrasion resistance. DLC coatings are typically under significant compressive stress. This stress greatly affects the ability of the coating to remain adherent to the glass substrate. Additionally, glass often contains many alkali oxides and other additives which can inhibit the bonding of the Si02 in the glass to the carbon atoms in the DLC coating. It is currently believed that the reaction between the SiO2 in glass and the DLC is essential for the coating to exhibit excellent adhesion. Therefore, less obvious methods are required to produce a glass substrate with a highly adherent DLC coating which provides excellent abrasion resistance.
In addition to glass substrates, many other optically transparent substrate materials, such as sapphire, glassy-ceramics, salts (NaCI, KBr, KC:I, etc.), metal fluorides and metal oxides could benefit from a DLC coating, but contain elements which inhibit the bonding of the DLC layer.
Many methods for depositing DLC have been demonstrated, including radio frequency plasma deposition, ion beam sputter deposition from a carbon target, ion beam sputtered carbon with ion beam assist, direct ion beam deposition, dual ion beam deposition, laser ablation deposition from a carbon target, and ion beam assisted evaporation of carbon. Many of these prior art techniques have been used to deposit DLC on glass substrates, however, the emphasis of the prior art has not been on the adhesion of the DLC to the glass substrate or on the abrasion resistance of the coated subsnrate product.
Illustrative are the following references: U.S. Patent Nos. 4,746,538; 4,400,410;
4,383,728;
4,504,519; 4,603,082; 4,060,660; 4,877,677; 4,569,738 and 4661409; 3apanese ' Patent Nos. 63/221841; 631221840; 63/195266; 1147068; 1147067; 64--2001;
59-X6906 and 51128686; European Patent Nos. DD-203903; SU 1006402; European Patent Application #EPO 243541 (WO 87/02713); Deutchman, et al.; Proc.
SPIE-Int. Soc. Opt. Eng. 1146, 124-34, 1989; Collins, et al., Proc. SPIE-Int.
Soc. , Opt. Eng. 1146, 37-47, 1989; Liou, et al., Proc. PIE-Int. Soc. Opt. Eng. 1146, t 12-20, 1989; Bubenzer, et al., Proc. DARPA Workshop Diamond-Like Carbon Coat., Meeting date 1982, Issue AD-A 136 766, 33-47, edited by B. Bendow in <<~<::
WO 94J03331 _ '~ ~ ~ ~ ~ ~ PCT/jJS93/05257 ., .

NBS Spec. Publ. 669, 249-54, 1984; NBS Spec. Publ. 638, 482-82, 1984;
Bubenzer, et al., NBS Spec. PubI. 638, 477-81, 1984; Appl. Phys. Lett. 55, 631-3, 1989; J. Vac. Sci. Technol A7, 2307-10, 1989; and D. Nir, Thin Solid Films, 144, 20I-9, 1986. These references do not however describe the use of transparent , interlayers to improve the adhesion of the.amorphous carbon coating to the substrate or substantially optically transparent DLC coatings with greatly improved wear resistance for severe abrasive envirnoments.
SUMMARY OF THE INVENTION
This invention provides a coated substrate product with superior abrasion wear resistance and reduced chemical reactivity. More particularly, this invention provides a diamond-like carbon coating to the surface of an optically transparent substrate which is highly adherent and exhibits greatly improved wear resistance for severe abrasive environments. Still more particularly, this invention provides a coated substrate with improved ease of cleaning. This invention also provides a low cost and efficient process for producing a coated substrate product with superior abrasion wear resistance.
The disclosed abrasion wear resistant coated substrate product substantially reduces or eliminates the disadvantages and shortcomings associated with the prior art techniquesy The invention discloses a substantially optically .
transparent composite structure which comprises a parent substrate, one or more intermediate layers and a diamond-like carbon layer in which at least one of the intermediate layers has thickness in the range of about 1 micron (pm) to about 20Iam. The invention also discloses a method for fabricating the coated substrate product. ' According to the method, the substrate surface is initially chemically ' a de-greased. In the second step, the substrate surface is bombarded with energetic s gas ions to assist in the removal of residual hydrocarbons, as well as alkali metals ! :::
and other additives. After the substrate surface has been sputter-etched, one or more interlayers are chemically vapor deposited on the substrate, followed by the ;
deposition of a diamond-like carbon layer. Once the requisite number of W~ X4103331 ~ ~ ~ ~ PCT/US93/05257 interlayers and diamond-like carbon layers have been deposited, the coated substrate is cooled and removed from the reactor.
BRIEF DESCRIPTION OF THE DRAWINGS
Further features and advantages will become apparent from the following and more particular description of the preferred embodiment of the invention, as illustrated in the accompanying drawings, in which like reference characters generally refer to the same parts or elements throughout the views, and in which:
Figure 1 is a cross-sectional view of the coated substrate product in accordance with the present invention;
Figure 2 is a cross-sectional view of the coated substrate product in accordance with a further embodiment of the prevent invention;
Figure 3 is a cross-sectional view of the coated substrate product in accordance with a still further embodiment of the present invention; and Figure 4 is a graph of the ratio of scans per defect versus the interlayer thickness of the coating of a coated bar-code scanner window product in accordance with the present invention.
DETAILED DESCRIPTION OF THE INVENTION
In accordance_with the present invention, the disclosed abrasion wear resistant coated substrate product substantially reduces or eliminates the disadvantages and shortcomings associated with the prior art techniques. As illustrated in Figures 1-3, the disclosed invention is a substantially optically transparent composite structure which comprises a parent substrate, one or more intermediate layers (interlayers) and a diamond-like carbon layer. By the term of "substantially optically transparent", it is intended to mean transparent to light in the visible region of the elecuomagnetic spectrum, which is generally between nanometers and approximately 750 nanometers wavelength. A highly important t technical advantage of the invention is that the resultant multilayer composite . ' structure produces a highly abrasion wear resistant surface on various substrate materials, particularly glass.

_, WO 94103331 ' ' ~ .~ ,, r~ ~ ~; PC'f/US93/05257 ,,.:_ j _ In the preferred embodiment form of the invention, as illustrated in Figure l, a first interlayer 2 (or adhesion-mediating layer) is chemically vapor deposited onto a parent substrate 1 which comprises a substantially optically i transparent amorphous material, a single crystal, polycrystalline materials, glass, salt materials, ceramic materials and/or mixtures thereof. 13y the term of "chemically vapor deposited", it is intended to mean materials deposited by vacuum deposition processes, including thermal evaporation, electron beam evaporation, magnetron sputtering, ion beam sputtering from solid precursor materials; thermally-activated deposition from reactive gaseous precursor materials;
glow discharge, plasma, or ion beam deposition from gaseous precursor matf;rials.
Preferably, the first interlayer 2 is deposited onto the parent substrate 1 by ion beam or magnetron sputtering.
Atmospheric pressure deposition methods including arc-spray or plasma-spray deposition from gaseous or solid precursor materials, or ZS thermally-activated deposition from reactive gaseous precursor materials may additionally be employed to deposit the first interlayer 2.
The first interlayer 2 generally comprises a substantially optically transparent material devoid of alkali metal atoms and fluorine, and capable of forming a strong chemical bond to the substrate 1 and the diamond-like carbon layer 3. By the term of "strong chemical bond", it is intended to mean that the interlayer is composed of a significant amount of an element or elements which are capable of undergoing a chemical reaction with carbon to form carbide-bonding.
The absence of alkali metals and fluorine is essential to achieve a highly adherent interface between the first interlayer 2 and the diamond-like carbon layer 3.
Thus, the first interlayer 2 must also have the property of providing a barrier to diffusion of alkali metals and additives from the parent substrate 1 to the diamond-like carbon layer 3. In the preferred embodiment form of the invention, the first 1:
interlayer comprises silicon nitride, titanium nitride, tantalum nitride, hafnium nitride, zirconium nitride, boron nitride, yttrium oxide, germanium oxide, hafnium oxide, silicon oxide, silicon dioxide, tantalum oxide, titanium oxide, zirconium oxide, silicon carbide, germanium carbide, mixtures thereof, and chemically bonded r, ,:r...
WO 9/03331 ~ ~ PCT/US~3/05257 .w (,. .
-s-combinations thereof. By the term "oxide", it is intended to mean a stoichiometrically oxidized material, or a partially oxidized material which contains excess metal atoms, or is deficient in oxygen. By the term "nitride", it is intended to mean a material composed of a stoichiometric amount of nitrogen or a material which either contains excess nitrogen atoms, or is deficient in nitrogen. By the term "carbide", it is intended to mean a material composed of a stoichiometric amount of carbon or a material which either contains excess carbon atoms, or is deficient in carbon.
By the term "chemically bonded combinations" it is intended to mean a combination of at least two of the foregoing materials which are joined by chemical bonds, e.g. silicon oxide and silicon nitride to form silicon oxy-nitride.
In the case of a single interlayer, first interlayer 2 ranges from approximately lpm to 20pm in thickness. Preferably, the first interlayer 2 is from about 5A thick to about lpm in those cases in which there are at least one other interlayer.
Following deposition of the first interlayer 2 onto the parent substrate 1, the diamond-like carbon layer 3 is chemically vapor deposited onto the coated substrate. The diamond-like carbon layer ~ can be from 10 ~ to 20pm in thickness. Preferably, the diamond-like carbon layer 3 is at least 50 ~ thick.
To further enhance the abrasion wear resistance of the structure, more than one interlayer or a plurality of alternating interlayers and diamond-like carbon layers 3 may be deposited onto the parent substrate 1. It has been found that this arrangement allows for the deposition of a greater total thickness of DLC
material, which provides a further increase in abrasion resistance. Thus, in further envisioned embodiments of the invention not shown the structure may comprise a parent substrate 1,' two different and separately deposited first interlayers
2 and a ' diamond-like carbon layer 3; or a parent substrate 1 and two or more pairs of first 1., interlayers 2 and diamond-like carbon layers 3. -It has unexpectedly been found that in severe wear environments, the ' abrasion resistance of the coated substrate product can be dramatically improved by ' using a relatively thick, e. g. in the range of about lum to about 20pm, first ;;;;.:
WO 94/43331 ' ' PCT/US93/05257 ,a::;:::,:.
.: 2141c~3b interiayer 2 between parent substrate 1 and DLC layer 3. Such a highly abrasion wear resistant and corrosion resistant coated substrate product is obtained by depositing such a relatively thick film of at least one interlayer 2 having a hardness i greater than that of substrate 1 and then depositing a comparatively thin, e.g. at least 50 A., layer of DLC as the top coat. In addition to serving as the bonding layers between substrate 1 and DLC top layer 3, interlayer(s) 2 provide a hard "structural support layer" for DLC layer 3. The thinner DLC top most layer provides a low friction, corrosion-resistant, protective surface for the substrate.
The resulting coated substrate product has greater commercial utility than similar products in which the substrate is deposited with thin interlayer(s) 2 followed by a relatively thick DLC layer 3 in the following two cases. The first case is if the optical absorption coefficient of DLC layer 3 is too high to allow a thick DLC
layer to be deposited while simultaneously meeting stringent optical transparency requirements for the coated product. The second case is if the deposition rate of DLC layer 3 is much lower than that of interlayer(s) 2, using a thick interlayer 2 to achieve the required degree of abrasion resistance is more economical than using a thick DLC layer 3.
In another embodiment of the invention, as illustrated in Figure 2, a second interlayer 4 is chemically vapor deposited onto the coated substrate and positioned such that the second interlayer 4 is disposed between the first interlayer 2 and the diamond-like carbon layer 3. The second interlayer 4 would similarly comprise a substantially optically transparent material devoid of alkali metal atoms ' and fluorine, and capable of forming a strong chemical bond to the first interlayer 2 and the diamond-like carbon layer 3. The second interlayer may comprise a substantially optically transparent silicon nitride, titanium nitride, tantalum.nitride, d ;.
hafnium nitride, zirconium nitride, boron nitride, yttrium oxide, germanium oxide, hafnium oxide, silicon oxide, silicon dioxide, tantalum oxide, titanium oxide, F. :.
zirconium oxide, silicon carbide, germanium carbide, mixtures thereof, and chemically bonded combinations thereof.
Since the second interlayer 4 provides a diffusion barrier for alkali metal atoms, fluorine and/or any additional additives which would adversely effect i .: .
~._.
WO 94J~3331 PCT/LjS93/05257 21~1~3~
. ., ., ~ .:..
_g_ the adherence of the diamond-like carbon layer 3, the first interlayer could further comprise a substantially optically transparent aluminum oxide, cerium oxide, tin oxide, thorium oxide, lithium oxide, sodium oxide, potassium oxide, rubidium -oxide, cesium oxide, francium oxide, beryllium oxide, magnesium oxide, calcium oxide, strontium oxide, cerium oxide, radium oxide, barium fluoride, cerium fluoride, magnesium fluoride, thorium fluoride, calcium fluoride, neodymium fluoride, lead fluoride, sodium fluoride, lithium fluoride, zinc selenide, zinc sulfide, mixtures thereof, and chemically bonded combinations thereof.
The second interlayer 4 can be from 5 ~ to 20pm in thickness.
Preferably, second interlayer 4 is at least 10 ~ thick. Still more preferably, second interlayer 4 has a thickness in the range of lpm to ZOpm in the case in which the thickness of first interlayer(s) 2 is in the SA to lpm range to achieve the unexpected results of greatly improved abrasion resistance in severe wear environments for the coated substrate product.
The second interlayer 4 may alternatively comprise a substantially optically transparent metallic material capable of reflecting visible light and capable of forming a strong chemical bond with the first interlayer 2 and the diamond-like carbon layer 3, selected from the following two groups. In the first group, the metallic material may consist of silicon, germanium, hafnium, molybdenum, tungsten, yttrium, tantalum, titanium and zirconium. These metallic materials all form a strong chemical bond to the diamond-like carbon layer 3.
The second group of metallic materials comprises vanadium, niobium, chromium, manganese, xhenium, technetium, iron; cobalt, iridium, rhodium, nickel, palladium, platinum, copper, silver, gold, zinc, ruthenium, indium, aluminum, tin, osmium, thallium, lead, antimony, bismuth and polonium. Among the second group of metallic materials, rhenium, iridium, tin, indium, aluminum, nickel, iron, chromium, copper, gold, silver and platinum are preferable as second A
interlayer 4. Although these materials will provide a diffusion barrier to alkali , .
metal atoms and fluorine, they will not form a strong carbide bond with the diamond-like carbon layer 3. Therefore, if any of these second group metallic materials are selected for the second interlayer 4, a third interlayer (not shown) _C~_ must be disposed between the second interlayer 4 and the diamond-like carbon layer 3. The third interlayer would similarly comprise a substantially optically transparent material devoid of alkali metal atoms and fluorine and selected from the group consisting of silicon nitride, titanium nitride, tantalum nitride, hafnium nitride, zirconium nitride, boron nitride, yttrium oxide, geranium oxide, hafnium oxide, silicon oxide, silicon dioxide, tantalum oxide, titanium oxide, zirconium oxide, silicon carbide, geranium carbide, mixtures thereof, and chemically bonded combinations thereof. Although it is not necessary, this third interlayer may be employed with the aforementioned first group of metallic materials.
The metallic second interlayer 4 can be from 5 A to 1000 in thickness. Preferably, the metallic second interlayer 4 is at least 10 A
thick.
In yet another embodiment of the invention, as illustrated in Figure
3, the embodiment illustrated in Figure 2 and discussed above is provided with a second composite layer comprising a first interlayer 2 and a diamond-like carbon la~~er 3. The resultant multilayer structure would thus be a parent substrate 1, a first interlayer 2, a second interlayer 4, a diamond-like carbon layer 3, a second interlayer 4 and a diamond-like carbon layer 3. The structure may alternatively comprise a parent substrate 1, two first interlayers 2, a diamond-like carbon layer 3, a first interlayer 2 and a diamond-like carbon layer.
By choosing the appropriate interlayer 2, 4 and diamond-like carbon layer 3 thicknesses, criteria which are known in the art of optical coating design could be employed in each of the aforementioned embodiments of the present invention to produce quarter wavelength stacks and ocher "dielectric stack"
coating configurations. In these dielectric stack configurations, optical interference effects could be used to produce wavelength-selective mirrors or anti-reflection films. By choosing the appropriate thickness of at least one of the interlayers 2, 4 and diamond-like carbon layer 3, the reflection of light at predetermined wavelength ranges may be either minimized or maximized. Superior abrasion wear resistance and environmental durability currently unavailable with conventional optical coatings could thus be realized by the incorporation of the dielectric stack configurations into the present invention.

. ;., ,..y.y ~..; -.~:..: .... : ~ ~..~'~: ; , ,:': . . :;. ~ .:,...,.;. ;-..:' . ...: ~.,:~' , ~ w:~ ,:~ ~ .::~ :: . :.: :'.:~ . .~;'~... ,...:: ..,..
~.: ~ .... ,.:':.
~x ". . -~ .'-. : ~ . . . .; - ,, .: . _ . . . ..'. ,.. .. .,..; ..-~. . ~.: .
. . . , ; ;.. .. ..., ..... ..... ., . ..... ,,:; , :. ,.; ~",: ~ ,... ,,. "
.,. ...
::..
WO 94/03331 . PCT/U~93105257 ~._ ~2~~1~3~
-lo-The method of the present invention teaches those skilled in the art how to fabricate the transparent abrasion wear resistant coated substrate product.
According to the method, the first step involves chemically de-greasing the surface of the parent substrate 1. The substrate 1 is then placed into a chemical vapor deposition reactor vacuum chamber and the air evacuated from the chamber to less than approximately 5 x 10-6 Torr.
In the next step the surface of the substrate 1 is sputter etched with energetic ions or atoms to assist in the removal of residual hydrocarbons, as well as alkali metals and other additives which are commonly present on the surface of the substrate materials, particularly glass. It has been found that the concentration of alkali metals (Na, Ca) at the surface of glass substrates was significantly reduced as a function of ion sputter-etching time and that increased sputter-etching time substantially improved the adhesion of the diamond-like carbon layer 3.
[See Examples A-Z]. Therefore, it is concluded that the removal of alkali metals and other additives is essential to a achieve a highly adherent interface between parent substrate 1 and the diamond like carbon layer 3.
The sputter-etching may be performed with a beam of inert gas ions, hydrogen ions or oxygen ions; a glow discharge ar a plasma of inert gas, hydrogen or oxygen. In the preferred embodiment form of the invention, sputter-etching is performed with a beam of energetic gas ions at an energy of at least 200 eV.
Following the sputter-etching step one or more interlayers are chemically vapor deposited onto the parent substrate 1. During a first cycle any of the aforementioned conventional chemical vapor deposition methods may be employed to deposit the interlayers 2, 4 (Fig. 2 & 3). The deposition rate of each interlayer 2,4 is generally in the range of about 0.1-10 microns/hour.
The,total thickness of each interlayer can be in the range of about 5 t~ to 20pm. In the preferred embodiment of the invendan, the thickness of at least one interlayer is in I , the range of about lpm to 20pm and the total thickness for each of the other .
interlayers is at least 10 ~.
After the chemical vapor deposition of one or more interlayers onto the parent substrate l, a diamond-like carbon layer 3 is deposited onto the coated :.;:"
,. WO 94!03331 J ~ ~ PCT/US93/05257 i:'-, _11_ I
I
substrate. The diamond-like carbon layer 3 can be deposited by the following ~, conventional methods: (i) direct ion beam deposition, dual ion beam deposition, glow discharge, RF-plasma, DC-plasma, or microwave plasma deposition from a carbon-containing gas or a carbon- containing vapor which can also be mixed with hydrogen, nitrogen-containing gases, oxygen containing gases andlor inert gas, (ii) electron beam evaporation, ion-assisted evaporation, magnetron sputtering, ion beam sputtering, or ion-assisted sputter deposition from a solid carbon target material, or (iii) combinations of (i) and (ii).
In the preferred embodiment form of the invention, the diamond-like carbon layers) is deposited by ion beam deposition from a hydrocarbon gas or carbon vapor. The ion beam deposition may also be performed in combination with an inert gas or hydrogen.
The deposition rate of the diamond-like carbon layer 3 is generally in the range of about 0.1-10 microns/hour. The total thickness of the diamond-like carbon layer is generally in the range of about 10 A to 20pm. Preferably, the thickness of the diamond-like carbon layer 3 is at least 50 t~ thick.
After the deposition of the appropriate interlayers and diamond-like carbon layers) 3, as detailed in the aforementioned embodiments. The coated substrate product is cooled by extinguishing the deposition process and passing an inert gas over the substrate until it has reached substantially room temperature.
The coated substrate product, exhibiting superior abrasion wear resistance, is then removed from the reactor.
The examples which follow illustrate the superior performance of the invention. The examples are for illustrative purposes only and are not meant to limit the scope of the claims in any way. .

PCT/US93/05257 ~,.._, . , ; ', -.;, :... ;..;
WO 94/03331 . . ~'~~.'~' .

Example A
A 2" x 2" x 0.375" thick float glass plate was cut from a glass bar code scanner window and coated by the following procedure. The glass plate was chemically cleaned by trichloromethane followed by methanol solvents in an ultrasonic bath. The sample was removed and blown dry with nitrogen gas. The glass plate was then mounted onto a substrate holder and part of the substrate surface was masked. The sample was then inserted into a vacuum chamber which was then evacuated to 8 x 10'' Torr. The sample was sputter-etched for 1 minute by a beam of Ar+ ions at an energy of 500 eV and a current density of 0.5 mA/cm2. The sample was then coated by direct ion beam deposition using a~n 11 cm ion beam source operated on CH4 gas at a pressure of 7.2 x 10'5 Ton. The ion energy was 75 eV and the ion beam current density was 0.30 mA/cm2. A
transparent coating of 3000 ~ thickness was deposited. The sample was removed and scratch-tested by rubbing a sharp piece of glass or a glass jar across the interface between the coated and uncoated (masked) areas. While the uncoated area showed deep and wide scratches, no scratches were observed on the DLC-coated area. The coating was tested far adhesion by alternately immersing the sample in baths of boiling water (for 2 minuees) and ice water (for 2 minutes).
After one thermal cycle, the_ coating peeled off of the glass substrate.
Example B
A 2" x 2" x 0.375" thick float glass plate was chemically cleaned, mounted, masked, and ion sputter-etched in vacuum for 10 minutes by the procedure described in Example A. Next, a 100-~ thick layer of Si0= was deposited onto the glass plate by Ar+ ion beam sputter deposition from a quartz target. Then, a diamond-like carbon layer of 3,000 tt thickness was deposited by the method described in Example A. The coating could not be scratched when rubbed by a sharp piece of glass or a glass jar. The coating remained adherent ;.
after 5 thermal cycles between boiling water and ice water. ~ ' Example C i A 2" x 2" x 0.375" thick float glass plate was chemically cleaned, ' mounted, masked, and ion sputter- etched in vacuum by the procedure described in Example B. Next, a 1,000-~ thick layer of SiOZ was deposited onto the glass plate by Ar+ ion beam sputter deposition from a quartz target. Then, a diamond-like carbon layer of 3,000 ~ thickness was deposited by the method described in Example A. The coating could not be scratched when rubbed by a sharp piece of glass or a glass jar. The coating remained adherent after 5 thermal cycles between boiling water and ice water.
Example D
A 2" x 2" x 0.375" thick float glass plate was chemically cleaned, mounted, masked, and ion sputter-etched in vacuum by the procedure described in Example B. Next, the coating described in Example B was repeated three times in sequence, so the total coating thickness deposited onto the glass place was 9,300 ~. The coating could not be scratched when rubbed by a sharp piece of glass or a glass jar. The coating remained adherent after 5 thermal cycles between boiling water and ice water.
Example E
A 2" x 2" x 0.375" thick float glass plate was chemically cleaned, mounted, masked, and ion sputter-etched in vacuum by the procedure described in Example A, except the sputter-etching time was 5 minutes. Next, a 800 t~ thick layer of A1,03 was deposited onto the glass plate by Ar'' ion beam sputter deposition from an aluminum oxide target. Then, a diamond-like carbon layer of 200 A thickness was deposited by the method described in Example A. Tile coating could not be scratched when rubbed by a sharp piece of glass. After 24 hours, the coating peeled off the substrate.
Example F
A 1" diameter x .06" thick soda lime glass disk was chemically cleaned, mounted, masked, and ion sputter-etched in vacuum by the procedure described in Example A. Next, a 10,000 A thick layer of A1,03 was deposited onto the glass plate by Ar+ ion beam sputter deposition from an aluminum oxide target. Then, a 300-A thick layer of SiO, was deposited over the A1,0, layer by Ar+ ion beam sputter deposition fram a quartz target. Next, a diamond-like carbon layer of 200 ~ thickness was deposited by the method described in Example A.

-14- , _ ...
'~'he coating could not be scratched when rubbed by a sharp piece of glass.
After 5 thermal cycles between boiling water and ice water, the coating remained adherent.
Examine G .
A 6" x 6" x 0.375" thick float glass plate was initially coated with about 2,000 ~ of Sn~z by thermally activated deposition from an organo-tin compound. The plate was then chemically cleaned by the procedure described in Example A, mounted, masked, and installed into a vacuum chamber which was then evacuated to 3.5 x 10'6 Torr. The sample was sputter-etched for 2 minutes by a beam of Ar+ dons at an energy of 500 eV and a current density of 0.5 mA/crn'.
Next, a 1,000-A thick layer of Si02 was deposited over the SnO~ layer by Ar+
ion beam sputter deposition from a quarts target. Then, a diamond-like carbon layer of 2,000 ~ thickness is deposited by the method described in Example A. After 5 thermal cycles between boiling water and ice water, the coating remained adherent.
Example H
A 6" x 6" x 0.375" thick float glass plate coated with about 2,000 t~
of SnO, was chemically cleaned by the procedure described in Example A, mounted, masked, and installed into a vacuum chamber which was then evacuated to 6 x 10'' Torr. The sample was sputter-etched for 2 minutes by a beam of Ar+
ions at an energy of 500 eV-and a current density of 0.5 mA/cm2. Then, a diamond-like carbon layer of 2,000 ~ thickness was deposited by the method described in Example A. During deposition, the DLC coating began to peel off of the substrate, indicating poor adhesion.
Example I
A 27 mm diameter x 2 mm thick sapphire window was ultrasonically cleaned in trichloromethane, followed by acetone, and then methanol, and blown dry with nitrogen gas. The sapphire sample was mounted into the vacuum coating system and, after evacuation, sputter-etched for 3 minutes as described in Example A. Then, a 1000-A thick layer of diamond-like carbon was -deposited onto the sapphire substrate using the conditions described in Example A.
A powdery carbon material was observed on the surface of the substrate upon removal from the coating chamber indicating that the coating was not adherent.

i.:;;
WO 94/03331 ~ ~ ~ ~, PCT/US93/05257 Example J
A 27 mm diameter x 2 mm thick sapphire window was cleaned, M ;
mounted into a vacuum coating system, evacuated, and sputter-etched for 1 minute using the conditions described in Example A. Then, a 100-t~ thick layer of Si02 was deposited onto the sapphire substrate using the conditions described in Example B. Next, a transparent, 1000-~ thick layer of diamond-like carbon was deposited onto the sapphire substrate using the conditions described in Example A.
The diamond-like carbon coating was very adherent, and could not be scratched with 50-micron quartz powder.
Example K
A 27 mm diameter x 2 mm thick sapphire window was cleaned, mounted into a vacuum coating system, evacuated, and sputter-etched for 1 minute using the conditions described in Example A. Then, a 50-~ thick layer of Si was ' deposited onto the sapphire substrate by Ar+ ion beam sputter deposition from a Si target. Next, a transparent, 1000-A thick layer of diamond-like carbon was deposited onto the sapphire substrate using the conditions described in Example A.
Subsequent optical spectroscopy analysis of the coating revealed that the Si layer had been converted into a transparent layer of SiC by this process. The diamond-like carbon coating was very adherent, and could not be scratched with 50-micron quartz powder.
Example L
A 130 mm diameter x 1 mm thick aluminosilicate disk was mounted ;
into a vacuum coating system, evacuated, and sputter-etched for 5 minutes, using the conditions described in Example A. Then, a 100-A thick layer of SiO~ was deposited onto the aluminosilicate substrate using the conditions described in ' Example B. Next, a 150-A thick layer of diamond-like carbon was deposited onto _, the aluminosilicate subsuate using the conditions described in Example A: The coating was very adherent, and could not be scratched with a sharp piece of glass.
Example M <' A S.5" x S.5" x 0.18" thick plate of Corning Code #9984-Pyroceram~ (Note: Pyroceram~ is a glass/ceramic material composed at ..> ..
... ....
.. '.
t.;:
WO 94/03331 ,, Pf."T/US93/05257 ..~ ' ' -1~- i i least of rutile, aluminum oxide, and magnesium silicate.) was cleaned in isopropyl alcohol, blown dry with nitrogen gas, mounted into a vacuum coating system, evacuated, and sputter-etched for 15 minutes using the conditions described in Example A. Then, a 200-A thick Iayer of SiO2 was deposited onto the substrate as '.
described in Example B. Next, a transparent, 2000-A thick layer of diamond-Iike carbon was deposited onto the substrate using the conditions described in Example A. The coating was very adherent, and could not be scratched by a sharp piece of glass.
Example N
A 5.5" x 5.5" x O.lg" thick plate of borosilicate glass was cleaned in isopropyl alcohol, blown dry with nitrogen gas, mounted into a vacuum coating system, evacuated, and sputter-etched for 15 minutes using the conditions described in Example A. Then, a 200-~. thick layer of Sz0= was deposited onto the substrate as described in Example B. Next, a transparent, 2000-~ thick layer of diamond-like carbon was deposited onto the substrate using the conditions described in Example A. The coating was very adherent, and could not be scratched by a sharp piece of glass.
Example O
A 2" x 2" x 1/4" thick piece float glass and a 70 mm diameter x 3 mm thick neutral gray glass sunglass lens were ultrasonically cleaned in isopropanol, and blown dry with nitrogen gas. The substrates were mounted into the vacuum coating system and, after evacuation, sputter-etched fox 5 minutes as described in Example A. Then, a 100-t~ thick layer of Si0= was deposited onto the substrates using the conditions described in Example B. Next, a 100-t~ thick layer j of Si was deposited on top of the SiO, layer by Ar+ ion beam sputter deposition from a Si target. Finally, a 1,000-A thick layer of transparent diamond-like carbon was deposited on top of the Si layer using the conditions described in Example A.
The coating was very adherent, and could not be scratched with a sharp piece of glass which could easily scratch the un-coated glass substrates. The coating on the E
sunglass lens exhibited an intense blue-purple reflected color.
Example P

..

A 2" x 2" x 1/4" thick piece of float glass and a 70 mm diameter x 3 mm thick neutral gray glass sunglass lens were ultrasonically cleaned in isopropanol, and blown dry with nitrogen gas. The substrates were mounted into the vacuum coating system and, after evacuation, sputter-etched for 5 minutes as S described in Example A. Then, a 100-~ thick layer. of Si02 was deposited onto the substrates using the conditions described in Example B. Next, a 100-~ thick layer of Cr metal was deposited by Ar+ ion beam sputter deposition from a Cr t rget.
Next, a second 100-A thick layer of Si02 was deposited on top of the Cr layer.
Finally, a 1,000-~ thick layer of transparent diamond-like carbon was deposited on top of the SiO, layer using the conditions described in Example A. The coating was very adherent, and could not be scratched with a sharp piece of glass which could easily scratch the un-coated glass substrates. The coating on the sunglass lens exhibited a bright blue reflected color.
Exam le An adherent, abrasion-resistant quarter-wavelength stack reflecting coating was formed on glass substrates. The layer thicknesses were chosen to maximize reflectance at a wavelength of 450 nanometers. The refractive index of the deposited Si4= layers was about 1.5, and the refractive index of the deposited DLC layers was about 2.05. The coating was formed as follows: , A 2" x 2" x 1/4" thick piece of float glass and a 70 mm diameter x 3 mm thick neutral gray glass sunglass lens were ultrasonically cleaned in isopropanol, and blown dry with nitrogen gas. The substrates were mounted into the vacuum coating system and, after evacuation, sputter-etched for 5 minutes as described in Example A. Then, a ?50-A thick layer of Si02 was deposited onto the i substrates using the conditions described in Example B. Next, a 550-A thick layer '.
of transparent diamond-like carbon was deposited on top of the first SiO, layer using the conditions described in Example A. Next, a 750-t1 thick layer of SiOZ
s:::: .
was deposited on top of the first DLC layer using the conditions described in Example B. Finally, a 5S0-~ thick layer of transparent diamond-like carbon was ' v .
deposited on top of the second SiO~ layer using the conditions described in ;
Example A. The coating was very adherent, and could not be scratched with a _ i.
t:;, t.: s:-' WO 94/03331 PCJf/US93/05257 .
r4 , ~ i -sharp piece of glass which could easily scratch the un-coated glass substrates. The coating exhibited a light yellow-blue reflected color on the sunglass lens, and a M
light blue reflected color on the glass plate.
Example R
A 5.7" x 5.7" x 0.375" soda-lime, float glass plate was cleaned with soap and water followed by rinsing with isopropanol and drying with nitrogen gas.
The glass plate was mounted onto a substrate holder which was in a vacuum chamber. The vacuum chamber was then evacuated to a pressure of 5 x 10'6 Torn Next, the sample was sputter-etched for 10 minutes with a beam of Ar+ ions at an energy of 500 eV and a current density of 0.5 mA/cm'. A 3000-~, layer of SiO
was then deposited by ion beam sputter deposition by bombarding a silica target with a beam of NZ+ ions. Next a 1-micron layer of "silicon oxy-nitride" was deposited onto the glass plate by bombarding a Si target with a beam of N,+
ions in the presence of air. After deposition of the silicon oxy-nitride, a 1001 thick layer of diamond-like carbon was deposited using a 11 cm ion beam source operated on methane gas at a pressure of 1.4 x 10'° Torr. The beam energy was 75 eV
and the beam current density was 0.3 mA/cm'-. The coating was very adherent to the glass substrate.
Example S
A 5.7" x 5.7" x 0.375" float glass substrate was cleaned and mounted in a vacuum chamber as in Example R. The chamber was evacuated to a pressure of 5 x 10'6 Torr. The sample was ion beam sputter-etched as in Example R. Next, a 3000-A Si02 layer was deposited as in Example R. Then, a 2-micron silicon oxy-nitride Layer was deposited as described in Example R. Finally, a ~ DLG layer was deposited as in Example R. The coating was very adherent to the glass substrate.
i f v 1,, .wi. ' WO 94103331 ~ PCT/US93/05257 ;
-1~-Examgle T t . .. !
A 5.7" x 5.7" x 0.375" float glass substrate was cleaned and mounted in a vacuum chamber as in Example R. The chamber was evacuated to 4 x 10'' Torn. The sample was ion beam sputter-etched as in Example R. Next, a 3000-~ Si02 layer was deposited as in Example R. Then, a 3-micron silicon oxy-nitride layer was deposited as described in Example R. Finally, a 100-t~ DLC
layer was deposited as in Example R. The coating was very adherent to the glass substrate.
Example U
5.7" x 5.7" x 0.375" float glass substrate was cleaned and mounted in a vacuum chamber as in Example R. The chamber was evacuated to 4 x 10-6 Ton. The sample was ion beam sputter-etched as in Example R. Next, a 3000-~ , Si02 layer was deposited as in Example R. Then, a 4-micron silicon oxy-nitride layer was deposited as described in Example R. A 100-~ DLC layer was deposited as in Example R. The coating was very adherent to the glass substrate.
Example V
Four neutral gray tempered sunglass lenses were cleaned by the chemical cleaning procedur~used in Example R. The lenses were subsequently mounted onto a graphite plate. One-half of the surface was masked. The graphite plate was then mounted in a vacuum chamber and the chamber was evacuated to 5 x 10'~ Torr. The lenses were Ar'" ion beam sputter-etched as in Example R.
Then, a 3000-~ Si0= layer was deposited as in Example R. Next a 0.5-micron silicon i oxy-nitride layer was deposited as in Example R. Finally, a 200-A DLC layer was deposited as in Example R. The coating was very adherent to the sunglass lenses.
Example W i Four tempered sunglass lenses were cleaned, mounted, and masked ,,;, as in Example V. The graphite plate was then mounted in a vacuum chamber and the chamber was evacuated to 2 x 10'~ Torr. The lenses were Ar+ ion beam sputter-etched for as in Example R. A 3000-~ SiO~ layer was deposited as in Example R. A 1 micron silicon oxy-nitride layer deposited as in Example R. A ' WO 94/03331 ~ ~ ~ PCI'/US93/05257 ,, . ~,y~' ;, ~,... :_.

200-A DLC layer was deposited as in Example R. The coating was very adherent to the sunglass lenses.
Example X
Four tempered sunglass lenses were cleaned, mounted, and masked S as in Example W. The graphite plate was then mounted in a vacuum chamber and the chamber was evacuated to 4 x 10-6 Torr. The lenses were Ar~ ion beam sputter-etched for as in Example R. Next, a 3000-~ SiOz layer was deposited as in Example R. A 2-micron silicon oxy-nitride layer was deposited as in Example R.
A 200-~ DLC layer was deposited as in Example R. The coating was very adherent to the sunglass lenses.
Example Y
Four tempered sunglass lenses were prepared and coated as in Example X except the silicon oxy-nitride thickness was increased to 3 microns.
The coating was very adherent to the sunglass lenses.
Example Z
Four tempered sunglass lenses were prepared and coated as in Example V except the silicon oxy-nitride thickness was increased to 4 microns.
The coating was very adherent to the sunglass lenses.
Specific examples of the use of thick interlayer(s) 2 with a thin DLC
layer 3 were shown in Examples R-Z. In these Examples, the coated substrate products are supermarket laser bar code scanner windows designed to stop damage from impacting cans and bottles for a period of at least five years, and glass sunglass lenses designed to withstand severe abrasion by sand. In Examples R-Z, the glass substrates were coated with a first interlayer 2 of silicon dioxide, a second interlayer 2 of a chemical combination of silicon oxide and silicon nitride ' (so-called "silicon oxy-nitride") and finally a top layer of DLC. The silicon dioxide layer was several thousands of A thick, the "silicon oxy-nitride"
layer E.:,,,:
ranged in thickness from 0.5 micron to four microns, and the DLC layer thickness was 100 ~ or 200 ~. In severe tests, the abrasion resistance was found to increase dramatically with the thickness of the silicon oxy-nitride interlayer.

r.a.;-, .
v . WO 94/03331 2 ~ 4 ~ j ~ ~ PCT/US93/05257 ':: ; ' l..: .

One particular example of the effect of the interlayer thickness on abrasion resistance is shown in Figure 4. Figure 4 shows results obtained from a Tagucchi study of diamond-like carbon coated bar-code scanner windows used in grocery stores. One of the parameters investigated in this study was the thickness of an interlayer of silicon oxy-nitride deposited onto a SiO, interlayer which in turn ;
was deposited onto a soda-lime float glass substrate. A 10011 thick layer of DLC
was deposited onto the silicon oxy-nitride (see Examples R-U). These coated windows were installed into a grocery store bar code scanner in which the number of items scanned over each window was recorded. At the end of the test, the I0 windows were removed and the number of scratches visible to the unaided eye were counted. Figure 4 is a plot of the number of items scanted across each window divided by the number of scratches observed on the window at the end of the test. It is desirable to increase the number of scans/defect in order to increase the lifetime of the window. Figure 4 shows that increasing the silicon oxy-nitride IS layer from one to four microns thickness dramatically improves the abrasion resistance.
Analogous results were obtained for a similar coating structure on glass sunglass.lenses. Lenses were produced with silicon oxy-nitride interlayers of 0.5, I, 2, 3 and 4 microns thickness (see Examples V-Z). These lenses were then 20 scratched with #2 quartz particles under an applied pressure of 33 pounds per square inch. This test simulates severe sand abrasion. For a silicon oxy-nitride thickness of 0.5 microns (Example V) significant damage to the substrate was observed. As the silicon oxy-nitride thickness was increased to 1 micron (Example V~, the number of scratches penetrating the coating decreased dramatically, but a t 25 significant number of fine scratches which indented the substrate through the coating, but did not break through the coating were observed using an optical i microscope. At a thickness of 2 microns (Example X), scratches which punctured r:
i:.,~
the coating were not observed, but some indentation type scratches still occurred.
At thickness of 3 and 4 microns (Example Y and Z, respectively) no indication of 30 any type of scratch was observed by optical micoscopy.

!: :' f: ' .

2~.41~3~

Examples R-Z showed that in severe abrasion tests, the abrasion resistance of the coated substrate product increases dramatically with the thickness of a hard, silicon oxy-nitride interlayer. These tests also demonstrate that the coating thickness required to achieve the desired degree of abrasion resistance is application specific.
From the foregoing description, one of ordinary skill in the art can easily ascertain that the present invention provides a novel method for producing a substantially optically transparent multilayer composite structure. A highly important technical advantage of the invention is that superior abrasion wear resistance is achieved by use of a multilayer transparent stnrcture comprised of a parent subsuate> one or more interlayers and a diamond-like carbon outer layer.
Without departing from the spirit and scope of this invention, one of ordinary skill can make various changes and modifications to the invention to adapt it to various usages and conditions. As such, these changes and modifications are properly, equitably, and intended to be, within the full range of equivalents of the following claims.

Claims (141)

WHAT IS CLAIMED IS:
1. A coated substrate product comprised of a substantially optically transparent substrate which is transparent to light in the visible region of 350 to approximately 750 nanometers and which comprises a material selected from the group consisting of an amorphous material, a single crystal, polycrystalline materials, glass, salt materials, ceramic materials and mixtures thereof and at least one composite layer having a thickness in the range of about 1µm to about 20µm, said composite layer comprising a chemically vapor deposited first interlayer bonded to said substrate, and a chemically vapor deposited outer layer of substantially optically transparent diamond-like carbon which is transparent to light in the visible region of 350 to approximately 750 nanometers and is bonded to said first interlayer and away from said substrate;
said first interlayer and comprising a substantially optically transparent material devoid of alkali metal atoms and fluorine, which first interlayer is transparent to light in the visible region of 350 to approximately 750 nanometers and is selected from the group consisting of silicon nitride, titanium nitride, tantalum nitride, hafnium nitride, zirconium nitride, boron nitride, yttrium oxide, germanium oxide, hafnium oxide, silicon oxide, silicon dioxide, tantalum oxide, titanium oxide, zirconium oxide, silicon carbide, germanium carbide, mixtures thereof, and chemically bonded combination thereof and capable of forming a strong chemical bond to said substrate and a strong chemical bond to said diamond-like carbon outer layer, whereby said product has greatly improved wear resistance for severe abrasive environments.
2. The product of Claim 1 wherein the thickness of said first interlayer is in the range of about 1µm to about 20µm.
3. The product of Claim 1 wherein the thickness of said diamond-like carbon outer layer is at least 50 .ANG. thick.
4. The product of Claim 1 wherein the thickness of at least one of said composite layers and said diamond-like carbon outer layer is selected to maximize the reflection of light at predetermined wavelengths.
5. The product of Claim 1 wherein the thickness of said diamond-like carbon layer corresponds to integer multiples of quarter wavelength optical thickness at predetermined wavelengths.
6. The product of Claim 1 wherein the thickness of said first interlayer and said diamond-like carbon layer corresponds to integer multiples of quarter wavelength optical thickness at predetermined wavelengths.
7. The product of Claim 1 wherein said composite layer comprises said first interlayer toward said substrate, a second interlayer which is transparent to light in the visible region of 350 to approximately 750 nanometers disposed immediately adjacent to said first interlayer and away from said substrate of a substantially optically transparent material devoid of alkali metal atoms and fluorine and capable of forming a strong chemical bond to said first interlayer and a strong chemical bond to diamond-like carbon, and said diamond-like carbon outer layer disposed immediately adjacent to said second interlayer and away from said substrate.
8. The product of Claim 7 wherein said second interlayer comprises a substantially optically transparent metallic material capable of reflecting visible light selected from the group consisting of silicon, germanium, hafnium, molybdenum, tungsten, yttrium, tantalum, titanium and zirconium.
9. The product of Claim 8 wherein the thickness of said first interlayer is in the range of about 5.ANG. to about 20µm and the thickness of said second interlayer is in the range of about 10.ANG. to about 1000.ANG..
10. The product of Claim 7 wherein said second interlayer comprises a substantially optically transparent metallic material capable of reflecting visible light selected from the group consisting of vanadium, niobium, chromium, manganese, rhenium, technetium, iron, cobalt, iridium, rhodium, nickel, palladium, platinum, copper, silver, gold, zinc, ruthenium, indium, aluminum, tin, osmium, thallium, lead, antimony, bismuth and polonium.
11. The product of Claim 10 wherein the thickness of said first interlayer is in the range of about 5.ANG. to about 20µm and the thickness of said second interlayer is in the range of about 10.ANG. to about 1000.ANG..
12. The product of Claim 10 including a third interlayer disposed between said second interlayer and said diamond-like carbon outer layer of a substantially optically transparent material which third interlayer is transparent to light in the visible region of 350 to approximately 750 nanometers and is devoid of alkali metal atoms and fluorine and capable of forming a strong chemical bond with said second interlayer and said diamond-like carbon outer layer.
13. The product of Claim 12 wherein said third interlayer comprises a substantially optically transparent material selected from the group consisting of silicon nitride, titanium nitride, tantalum nitride, hafnium nitride, zirconium nitride, boron nitride, yttrium oxide, germanium oxide, hafnium oxide, silicon oxide, silicon dioxide, tantalum oxide, titanium oxide, zirconium oxide, silicon carbide, germanium carbide, mixtures thereof, and chemically bonded combinations thereof.
14. The product of Claim 13 wherein the thickness of at least one of said composite layers, said third interlayer and said diamond-like carbon outer layer is selected to minimize the reflection of light at predetermined wavelengths.
15. The product of Claim 13 wherein the thickness of at least one of said composite layers, said third interlayer and said diamond-like carbon outer layer is selected to maximize the reflection of light at predetermined wavelengths.
16. The product of Claim 13 wherein the thickness of said third interlayer and said diamond-like carbon outer layer corresponds to integer multiples of quarter wavelength optical thickness at predetermined wavelengths.
17. The product of Claim 13 wherein the thickness of said first interlayer, said third interlayer and said diamond-like carbon outer layer corresponds to integer multiples of quarter wavelength optical thickness at predetermined wavelengths.
18. The product of Claim 7 wherein said first interlayer further comprises a substantially optically transparent material selected from the group consisting of aluminum oxide, cerium oxide, tin oxide, thorium oxide, lithium oxide, sodium oxide, potassium oxide, rubidium oxide, cesium oxide, francium oxide, beryllium oxide, magnesium oxide, calcium oxide, strontium oxide, barium oxide, radium oxide, barium fluoride, cerium fluoride, magnesium fluoride, thorium fluoride, calcium fluoride, neodymium fluoride, lead fluoride, sodium fluoride, lithium fluoride, zinc selenide, zinc sulfide, mixtures thereof, and chemically bonded combinations thereof.
19. The product of Claim 7 wherein said second interlayer comprises a substantially optically transparent material selected from the group consisting of silicon nitride, titanium nitride, tantalum nitride, hafnium nitride, zirconium nitride, boron nitride, yttrium oxide, germanium oxide, hafnium oxide, silicon oxide, silicon dioxide, tantalum oxide, titanium oxide, zirconium oxide, silicon carbide, germanium carbide, mixtures thereof, and chemically bonded combinations thereof.
20. The product of Claim 19 wherein the thickness of said first interlayer is in the range of about 5.ANG. to about 1µm and the thickness of said second interlayer is in the range of about 1µm to about 20µm.
21. The product of Claim 20 wherein said first interlayer comprises silicon dioxide and said second interlayer comprises a chemically bonded combination of silicon oxide and silicon nitride.
22. The product of Claim 21 the thickness of said diamond-like carbon outer layer is at least 50 .ANG. thick.
23. The product of Claim 19 wherein the thickness of at least one of said composite layers, said second interlayer and said diamond-like carbon outer layer is selected to minimize the reflection of light at predetermined wavelengths.
24. The product of Claim 19 wherein the thickness of at least one of said composite layers, said second interlayer and said diamond-like carbon outer layer is selected to maximize the reflection of light at predetermined wavelengths.
25. The product of Claim 19 wherein the thickness of said second interlayer and said diamond-like carbon outer layer corresponds to integer multiples of quarter wavelength optical thickness at predetermined wavelengths.
26. The product of Claim 19 wherein the thickness of said first interlayer, said second interlayer and said diamond-like carbon layer corresponds to integer multiples of quarter wavelength optical thickness at predetermined wavelengths.
27. The product of Claim 19 wherein said composite layer comprises two different and separately deposited said second interlayers, and said diamond-like carbon outer layer disposed immediately adjacent to said plurality of said second interlayers.
28. The product of Claim 7 wherein said composite layer includes a chemically vapor deposited :fourth interlayer disposed between said second interlayer and said diamond-like carbon outer layer of a substantially optically transparent material devoid of ;alkali metal atoms and fluorine and capable of forming a strong chemical bond to said second interlayer and said diamond-like carbon outer layer.
29. The product of Claim 28 wherein said first interlayer and said second interlayer comprise a substantially optically transparent material selected from the group consisting of silicon nitride, titanium nitride, tantalum nitride, hafnium nitride, zirconium nitride, boron nitride, yttrium oxide, germanium oxide, hafnium oxide, silicon oxide, silicon dioxide, tantalum oxide, titanium oxide, zirconium oxide, silicon carbide, germanium carbide, aluminum oxide, cerium oxide, tin oxide, thorium oxide, lithium oxide, sodium oxide, potassium oxide, rubidium oxide, cesium oxide, francium oxide, beryllium oxide, magnesium oxide, calcium oxide, strontium oxide, barium oxide, radium oxide, barium fluoride, cerium fluoride, magnesium fluoride, thorium fluoride, calcium fluoride, neodymium fluoride, lead fluoride, sodium fluoride, lithium fluoride, zinc selenide, zinc sulfide, mixtures thereof, and chemically bonded combinations thereof.
30. The product of Claim 28 wherein said fourth interlayer comprises a substantially optically transparent material selected from the group consisting of silicon nitride, titanium nitride, tantalum nitride, hafnium nitride, zirconium nitride, boron nitride, yttrium oxide, germanium oxide, hafnium oxide, silicon oxide, silicon dioxide, tantalum oxide, titanium oxide, zirconium oxide, silicon carbide, germanium carbide, mixtures thereof, and chemically bonded combinations thereof.
31. The product of Claim 30 wherein the thicknesses of said first and second interlayers are in the range of about 5.ANG. to about 1µm and the thickness of said fourth interlayer is in the range of about lum to about 20µm.
32. The product of Claim 28 wherein the thickness of at least one of said composite layers, said second interlayer, said fourth interlayer and said diamond-like carbon. outer layer is selected to minimize the refection of light at predetermined wavelengths.
33. The product of Claim 28 wherein the thickness of at least one of said composite layers, said second interlayer, said fourth interlayer, and said diamond-like carbon outer layer is selected to maximize the reflection of light at predetermined wavelengths.
34. The product of Claim 28 wherein the thickness of said second interlayer, said fourth interlayer and said diamond-like carbon layer corresponds to integer multiples of quarter wavelength optical thickness at predetermined wavelengths.
35. The product of Claim 28 wherein the thickness of said first interlayer, said second interlayer, said fourth interlayer and said diamond-like carbon layer corresponds to integer multiples of quarter wavelength optical thickness at predetermined wavelengths.
36. A coated substrate product comprised of a substantially optically transparent substrate which is transparent to light in the visible region of 350 to approximately 750 nanometers and which comprises a material selected from the group consisting of an amorphous material, a single crystal, polycrystalline materials, glass, salt materials, ceramic materials and mixtures thereof, a first composite layer and at least one second composite layer;
said first composite layer having a thickness in the range of about 1µm to about 20µm and comprising a chemically vapor deposited first interlayer bonded to said substrate of a substantially optically transparent material capable of forming a strong chemical bond to said substrate which first interlayer is transparent to light in the visible region of 350 to approximately 750 nanometers and which is selected from the group consisting of silicon nitride, titanium nitride, tantalum nitride, hafnium nitride, zirconium nitride, boron nitride, yttrium oxide, germanium oxide, hafnium oxide, silicon oxide, silicon dioxide, tantalum oxide, titanium oxide, zirconium oxide, silicon carbide, germanium carbide, aluminum oxide, cerium oxide, tin oxide, thorium oxide, lithium oxide, sodium oxide, potassium oxide, rubidium oxide, cesium oxide, francium oxide, beryllium oxide, magnesium oxide, calcium oxide, strontium oxide, barium oxide, radium oxide, barium fluoride, cerium fluoride, magnesium fluoride, thorium fluoride, calcium fluoride, neodymium fluoride, lead fluoride, sodium fluoride, lithium fluoride, zinc selenide, zinc sulfide, mixtures thereof, and chemically bonded combinations thereof, a second interlayer bonded to and disposed immediately adjacent to said first interlayer and away from said substrate of a substantially optically transparent material devoid of alkali metal atoms and fluorine and capable of forming a strong chemical bond to said first interlayer and a strong chemical bond to diamond-like carbon, and a first substantially optically transparent diamond-like carbon layer which is transparent to light in the visible region of 350 to approximately 750 nanometers and which is bonded to and disposed immediately adjacent to said second interlayer and away from said substrate;
said second composite layer which is transparent to light in the visible region of 350 to approximately 750 nanometers and which is bonded to and disposed immediately adjacent to said first composite layer and away from said substrate comprising a chemically vapor deposited third interlayer disposed immediately adjacent to said first diamond-like carbon layer of a substantially optically transparent material devoid of alkali metal atoms and fluorine and capable of forming a strong chemical bond to diamond-like carbon and a second substantially optically transparent diamond-like carbon layer bonded to and disposed immediately adjacent to said third interlayer and away from said substrate, whereby said coated substrate product has greatly improved wear resistance for severe abrasive environments.
37. The product of Claim 36 wherein said second interlayer and said third interlayer comprise a substantially optically transparent material selected from the group consisting of silicon nitride, titanium nitride, tantalum nitride, hafnium nitride, zirconium nitride, boron nitride, germanium oxide, hafnium oxide, silicon oxide, silicon dioxide, tantalum oxide, titanium oxide, yttrium oxide, zirconium oxide, silicon carbide, germanium carbide, mixtures thereof, and chemically bonded combinations thereof.
38. The product of Claim 36 wherein the thickness of said second interlayer is in the range of about 1µm to about 20µm.
39. The product of Claim 38 wherein the first interlayer comprises silicon dioxide and said second interlayer comprises a chemically bonded combination of silicon oxide and silicon nitride.
40. The product of Claim 36 wherein said first composite layer comprises at least one pair of separately deposited said second interlayers.
41. The product of Claim 36 wherein the thickness of said first interlayer, said second interlayer and said third interlayer is at least 2µm thick.
42. The product of Claim 36 wherein the thickness of said first diamond-like carbon layer and said second diamond-like carbon layer is at least 50 .ANG.
thick.
43. The product of Claim 42 wherein the thickness of at least one of said first interlayer, said second interlayer, said third interlayer, said first diamond-like carbon layer and said second diamond-like carbon layer is selected to minimize the reflection light at predetermined wavelengths.
44. The product of Claim 36 wherein the thickness of at least one of said first interlayer, said second interlayer, said third interlayer, said first diamond-like carbon layer and said second diamond-like carbon layer is selected to maximize the reflection of light at predetermined wavelengths.
45. The product of Claim 36 wherein the thickness of said second interlayer, said third interlayer, said first diamond-like carbon layer and said second diamond-like carbon layer corresponds to integer multiples of quarter wavelength optical thickness at predetermined wavelengths.
46. The product of Claim 36 wherein the thickness of said first interlayer, said second interlayer, said third interlayer, said first diamond-like carbon layer and said second diamond-like carbon layer corresponds to integer multiples of quarter wavelength optical thickness at predetermined wavelengths.
47. The product of Claim 36 wherein said third interlayer comprises a substantially optically transparent material selected from the group consisting of silicon nitride, titanium nitride, tantalum nitride, hafnium nitride, zirconium nitride, boron nitride, germanium oxide, hafnium oxide, silicon oxide, silicon dioxide, tantalum oxide, titanium oxide, yttrium oxide, zirconium oxide, silicon carbide, germanium carbide, mixture, thereof, and chemically bonded combinations thereof.
48. The product of Claim 47 wherein said second interlayer comprises a substantially optically transparent metallic material capable of reflecting visible light selected from the group consisting of silicon, germanium, hafnium, molybdenum, tungsten, yttrium, tantalum, titanium and zirconium.
49. The product of Claim 48 wherein the thickness of said first interlayer is in the range of about 5.ANG. to about 20µm and the thickness of said second interlayer is in the range of about 10 .ANG. to about 1000 .ANG..
50. The product of Claim 47 wherein said second interlayer comprises a substantially optically transparent metallic material capable of reflecting visible light selected from the group consisting of vanadium, niobium, chromium, manganese, rhenium, technetium, iron, cobalt, iridium, rhodium, nickel, palladium, platinum, copper, silver, gold, zinc, ruthenium, indium, aluminum, tin, osmium, thallium, lead, antimony, bismuth and polonium.
51. The product of Claim 50 wherein the thickness of said first interlayer is in the range of about 5.ANG. to about 20µm and the thickness of said second interlayer is in the range of about 10 .ANG. to about 1000 .ANG..
52. The product of Claim 50 including a fourth interlayer disposed between said second interlayer and said first diamond-like carbon layer of a substantially optically transparent material devoid of alkali metal atoms and fluorine and capable of forming a strong chemical bond with said second interlayer and said first diamond-like carbon layer.
53. The product of Claim 52 wherein said fourth interlayer comprises a substantially optically transparent material selected from the group consisting of silicon nitride, titanium nitride, tantalum nitride, hafnium nitride, zirconium nitride, boron nitride, yttrium oxide, germanium oxide, hafnium oxide, silicon oxide, silicon dioxide, tantalum oxide, titanium oxide, zirconium oxide, silicon carbide, germanium carbide, mixtures thereof, and chemically bonded combinations thereof.
54. The product of Claim 53 wherein the thickness of at least one of said fast interlayer, said fourth interlayer, said third interlayer, said first diamond-like carbon layer and said second diamond-like carbon layer is selected to minimize the reflection of light ac predetermined wavelengths.
55. The product of Claim 52 wherein the thickness of at least one of said first interlayer, said fourth interlayer, said third interlayer, said first diamond-like carbon layer and said second diamond-like carbon layer is selected to maximize the reflection of light at predetermined wavelengths.
56. The product of Claim 52 wherein the thickness of said fourth interlayer, said third interlayer, said first diamond-like carbon layer and said second diamond-like carbon layer corresponds to integer multiples of quarter wavelength optical thickness at predetermined wavelengths.
57. The product of Claim 52 wherein the thickness of said first interlayer, said fourth interlayer, said third interlayer, said first diamond-like carbon layer and said second diamond-like carbon layer corresponds to integer multiples of quarter wavelength optical thickness at predetermined wavelengths.
58. The product of Claim 36 wherein said first composite layer includes a fifth interlayer disposed between said second interlayer and said first diamond-like carbon layer of a substantially optically transparent material devoid of alkali metal atoms and fluorine and capable of forming a strong chemical bond with said second interlayer and said diamond-like carbon outer layer.
59. The product of Claim 58 wherein said third interlayer and said fifth interlayer comprise a substantially optically transparent material selected from the group consisting; of silicon nitride, titanium nitride, tantalum nitride, hafnium nitride, zirconium nitride, boron nitride, yttrium oxide, germanium oxide, hafnium oxide, silicon oxide, silicon dioxide, tantalum oxide, titanium oxide, zirconium oxide, silicon carbide, germanium carbide, mixtures thereof, and chemically bonded combinations thereof.
60. The product of Claim 59 wherein the thickness of said first and second interlayers sire in the range of about 5.ANG. to about 20µm and the thickness of said fifth interlayer is in the range of about lµm to about 20µm.
61. The product of Claim 58 wherein said second interlayer comprises a substantially optically transparent material selected from the group consisting of silicon nitride, titanium nitride, tantalum nitride, hafnium nitride, zirconium nitride, boron nitride, yttrium oxide, germanium oxide, hafnium oxide, silicon oxide, silicon dioxide, tantalum oxide, titanium oxide, zirconium oxide, silicon carbide, germanium carbide, aluminum oxide., cerium oxide, tin oxide, thorium oxide, lithium oxide, sodium oxide, potassium oxide, rubidium oxide, cesium oxide, francium oxide, beryllium oxide, magnesium oxide, calcium oxide, strontium oxide, barium oxide, radium oxide, barium fluoride, cerium fluoride, magnesium fluoride, thorium fluoride, calcium fluoride, neodymium fluoride, lead fluoride, sodium fluoride, lithium fluoride, zinc selenide, zinc sulfide, mixtures thereof, and chemically bonded combinations thereof.
62. The product of Claim 58 wherein the thickness of at least one of said first interlayer, said second interlayer, said fifth interlayer, said first diamond-like carbon layer, said third interlayer and said second diamond-like carbon layer is selected to minimize the reflection of light at predetermined wavelengths.
63. The product of Claim 58 wherein the thickness of at least one of said first interlayer, said second interlayer, said fifth interlayer, said first diamond-like carbon layer, said third interlayer and said second diamond-like carbon layer is selected to maxirnia:e the reflection of light at predetermined wavelengths.
64. The product of Claim 58 wherein the thickness of said second interlayer, said third interlayer, said fifth interlayer said first diamond-like carbon layer and said second diamond-like carbon layer corresponds to integer multiples of quarter wavelength optical thickness at predetermined wavelengths.
65. 'The product of Claim 58 wherein the thickness of said first interlayer, said second interlayer, said third interlayer, said fifth interlayer said first diamond-like carbon layer and said second diamond-like carbon layer corresponds to integer multiples of quarter wavelength optical thickness at predetermined wavelengths.
66. A chemical vapor deposition method for producing an abrasion wear resistant coated substrate product comprising:
chemically de-greasing the surface of a parent substrate which is substantially optical;y transparent to light in the visible region of 350 to approximately 750 nanometers and which comprises a material selected from the group consisting of an amorphous material, a single crystal, polycrystalline materials, glass, salt materials, ceramic materials and mixtures thereof to remove hydrocarbon contamination;
placing said substrate into a chemical vapor deposition reactor vacuum chamber and evacuating the air from said chamber;
sputter-etching the surface of said substrate with energetic gas ions to remove traces of residual hydrocarbon and to preferentially reduce the concentration of alkali metal atoms and alkali metal oxides at the substrate surface;
chemically vapor depositing at least one composite layer having a thickness in the range of about 1,µm to about 20,µm by chemically vapor depositing during a first cycle a substantially optically transparent interlayer at least 1,µm thick onto said substrate;
chemically vapor depositing during said first cycle a substantially optically transparent diamond-like carbon outer layer which is transparent to light in the visible region of 350 to approximately 750 manometers and having a thickness of at least 50 .ANG. thick onto said coated substrate;
said interlayer comprising a substantially optically transparent material devoid of alkali metal atoms and fluorine, which interlayer is transparent to light in the visible region of 350 to approximately 750 manometers and is selected from the group consisting of silicon nitride, titanium nitride, tantalum nitride, hafnium nitride, zirconium nitride, boron nitride, yttrium oxide, germanium oxide, hafnium oxide, silicon oxide, silicon dioxide, tantalum oxide, titanium oxide, zirconium oxide, silicon carbide, germanium carbide, mixtures thereof, and chemically bonded combinations thereof and capable of forming a strong chemical bond to said substrate and a strong chemical bond to said diamond-like carbon outer layer;

cooling said coated substrate by extinguishing said deposition process and passing an inert gas over said substrate until the temperature of said substrate has reached substantially room temperature during said cool-down step; and recovering a coated substrate product exhibiting greatly improved wear resistance for severe abrasive environments.
67. The method of Claim 66 wherein the thickness of said interlayer is in the range of about 1µm to about 20µm.
68. The product of the method of Claim 66.
69. The method of Claim 66 wherein the thickness of at least one of said composite layers and said diamond-like carbon outer layer is selected to maximize the reflection of light at predetermined wavelengths.
70. The method of Claim 66 wherein the thickness of said diamond-like carbon layer corresponds to integer multiples of quarter wavelength optical thickness at predetermined wavelengths.
71. The method of Claim 66 wherein the thickness of said interlayer and said diamond-like carbon layer corresponds to integer multiples of quarter wavelength optical thickness at predetermined wavelengths.
72. The method of Claim 66 wherein said composite layer comprises said interlayer which comprises a first interlayer toward said substrate, a second interlayer which is transparent to light in the visible region of 350 to approximately 750 nanometers disposed immediately adjacent to said first interlayer and away from said substrate of a substantially optically transparent material devoid of alkali metal atoms and fluorine and capable of forming a strong chemical bond to said first interlayer and a strong chemical bond to diamond-like carbon, and said diamond-like carbon outer layer disposed immediately adjacent to said second interlayer and away from said substrate.
73. The method of Claim 72 wherein said second interlayer comprises a substantially optically transparent metallic material capable of reflecting visible light selected from the group consisting of silicon, germanium, hafnium, molybdenum, tungsten, yttrium, tantalum, titanium and zirconium.
74. The method of Claim 73 wherein the thickness of said first interlayer is in the range of about 5.ANG. to about 20µm and the thickness of said second interlayer is in the range of about 10.ANG. to about 1000.ANG..
75. The method of Claim 72 wherein said second interlayer comprises a substantially optically transparent metallic material capable of reflecting visible light selected from the group consisting of vanadium, niobium, chromium, manganese, rhenium, technetium, iron, cobalt, iridium, rhodium, nickel, palladium, platinum, copper, silver, gold, zinc, ruthenium, indium, aluminum, tin, osmium, thallium, lead, antimony, bismuth and polonium.
76. The method of Claim 75 wherein the thickness of said first interlayer is in the range of about 5.ANG. to about 20µm and the thickness of said second interlayer is in the range of about 10.ANG. to about 1000.ANG..
77. 'Che method of Claim 75 including a third interlayer disposed between said second interlayer and said diamond-like carbon outer layer of a substantially optical'y transparent material which third interlayer is transparent to light in the visible region of 350 to approximately 750 manometers and is devoid of alkali metal atoms and fluorine and capable of forming a strong chemical bond with said second interlayer and said diamond-like carbon outer layer.
78. The method of Claim 77 wherein said third interlayer comprises a substantially optically transparent material selected from the group consisting of silicon nitride, titanium nitride, tantalum nitride, hafnium nitride, zirconium nitride, boron nitride, yttrium oxide, germanium oxide, hafnium oxide, silicon oxide, silicon dioxide, tantalum oxide, titanium oxide, zirconium oxide, silicon carbide, germanium carbide, mixtures thereof, and chemically bonded combinations thereof.
79. The method of Claim 78 wherein the thickness of at least one of said composite layers, said third interlayer and said diamond-like carbon outer layer is selected to minimized the reflection of light at predetermined wavelengths.
80. The method of Claim 78 wherein the thickness of at least one of said composite layers, said third interlayer and said diamond-like carbon outer layer is selected to maximize the reflection of light at predetermined wavelengths.
81. The method of Claim 78 wherein the thickness of said third interlayer and said diamond-like carbon outer layer corresponds to integer multiples of quarter wavelength optical thickness at predetermined wavelengths.
82. The method of Claim 78 wherein the thickness of said first interlayer, said third interlayer and said diamond-like carbon outer layer corresponds to integer multiples of quarter wavelength optical thickness at predetermined wavelengths.
83. The method of Claim 72 wherein said first interlayer further comprises a substantially optically transparent material selected from the group consisting of aluminum oxide, cerium oxide, tin oxide, thorium oxide, lithium oxide, sodium oxide, potassium oxide, rubidium oxide, cesium oxide, francium oxide, beryllium oxide, magnesium oxide, calcium oxide, strontium oxide, barium oxide, radium oxide, barium fluoride, cerium fluoride, magnesium fluoride, thorium fluoride, calcium fluoride, neodymium fluoride, lead fluoride, sodium fluoride, lithium fluoride, zinc selenide, zinc sulfide, mixtures thereof and chemically bonded combinations thereof.
84. The method of Claim 72 wherein said second interlayer comprises a substantially optically transparent material selected from the group consisting of silicon nitride, titanium nitride, tantalum nitride, hafnium nitride, zirconium nitride, boron nitride, yttrium oxide, germanium oxide, hafnium oxide, silicon oxide, silicon dioxide, tantalum oxide, titanium oxide, zirconium oxide, silicon carbide, germanium carbide, mixtures thereof and chemically bonded combinations thereof.
85.The method of Claire 84 wherein the thickness of said first interlayer is in the range of about 5.ANG. to about lam and the thickness of said second interlayer is in the range of about 1µm to about 20µm.
86. The method of Claim 84 wherein said first interlayer comprises silicon dioxide and said second interlayer comprises a chemically bonded combination of silicon oxide and silicon nitride.
87. The method of Claim 86 the thickness of said diamond-like carbon outer layer is at least 50 .ANG. thick.
88. The method of Claim 84 wherein the thickness of at least one of said composite layers, said second interlayer and said diamond-like carbon outer layer is selected to minimize the reflection of light at predetermined wavelengths.
89. The method of Claim 84 wherein the thickness of at least one of said composite layers, said second interlayer and said diamond-like carbon outer layer is selected to maximize the reflection of light at predetermined wavelengths.
90. The method of Claim 84 wherein the thickness of said second interlayer and said diamond-like carbon outer layer corresponds to integer multiples of quarter wavelength optical thickness at predetermined wavelengths.
91. The method of Claim 84 wherein the thickness of said first interlayer, said second interlayer and said diamond-like carbon layer corresponds to integer multiples of quarter wavelength optical thickness at predetermined wavelengths.
92. The method of Claim 84 wherein said composite layer comprises two different and separately deposited said second interlayers, and said diamond-like carbon outer layer disposed immediately adjacent to said plurality of said second interlayers.
93. The method of Claim 72 wherein said composite layer includes a chemically vapor deposited fourth interlayer disposed between said second interlayer and said diamond-like carbon outer layer of a substantially optically transparent material devoid of alkali metal atoms and fluorine and capable of forming a strong chemical bond to said second interlayer and said diamond-like carbon outer layer.
94. The method of Claim 93 wherein said first interlayer and said second interlayer comprise a substantially optically transparent material selected from the group consisting of silicon nitride, titanium nitride, tantalum nitride, hafnium nitride, zirconium nitride, boron nitride, yttrium oxide, germanium oxide, hafnium oxide, silicon oxide, silicon dioxide, tantalum oxide, titanium oxide, zirconium oxide, silicon carbide, germanium carbide, aluminum oxide, cerium oxide, tin oxide, thorium oxide, lithium oxide, sodium oxide, potassium oxide, rubidium oxide, cesium oxide, francium oxide, beryllium oxide, magnesium oxide, calcium oxide, strontium oxide, barium oxide, radium oxide, barium fluoride, cerium fluoride, magnesium fluoride, thorium fluoride, calcium fluoride, neodymium fluoride, lead fluoride, sodium fluoride, lithium fluoride, zinc selenide, zinc sulfide, mixtures thereof and chemically bonded combinations thereof.
95. The method of Claim 93 wherein said fourth interlayer comprises a substantially optically transparent material selected from the group consisting of silicon nitride, titanium nitride, tantalum nitride, hafnium nitride, zirconium nitride, boron nitride, yttrium oxide, germanium oxide, hafnium oxide, silicon oxide, silicon dioxide, tantalum oxide, titanium oxide, zirconium oxide, silicon carbide, germanium carbide, mixtures thereof and chemically bonded combinations thereof.
96. The method of Claim 95 wherein the thicknesses of said first and second interlayers are in the range of about 5.ANG. to about 1µm and the thickness of said fourth interlayer is in the range of about 1µm to about 20µm.
97. The method of Claim 93 wherein the thickness of at least one of said composite layers, said second interlayer, said fourth interlayer and said diamond-like carbon outer layer is selected to minimize the reflection of light at predetermined wavelengths.
98. The method of Claim 93 wherein the thickness of at least one of said composite layers, said second interlayer, said fourth interlayer, and said diamond-like carbon outer layer is selected to maximize the reflection of light at predetermined wavelengths.
99. The method of Claim 93 wherein the thickness of said second interlayer, said fourth interlayer and said diamond-like carbon layer corresponds to integer multiples of quarter wavelength optical thickness at predetermined wavelengths.
100. The method of Claim 93 wherein the thickness of said first interlayer, said second interlayer, said fourth interlayer and said diamond-like carbon layer corresponds to integer multiples of quarter wavelength optical thickness at predetermined wavelengths.
101. A chemical vapor deposition method for producing an abrasion wear resistant coated substrate product comprising:

chemically de-greasing the surface of a parent substrate which is substantially optically transparent to light in the visible region of 350 to approximately 750 nanometers and which comprises a material selected from the group consisting of an amorphous material, a single crystal, polycrystalline materials, glass, salt materials, ceramic materials and mixtures thereof to remove hydrocarbon contamination;
placing said substrate into a chemical vapor deposition reactor vacuum chamber and evacuating the air from said chamber;
sputter-etching the surface of said substrate with energetic gas ions remove traces of residual hydrocarbon and to preferentially reduce the concentration of alkali metal atoms and alkali metal oxides at the substrate surface;
chemically vapor depositing a composite layer comprising a first composite having a thickness in the range of about 1µm to about 20µm and at least one second composite layer by chemically vapor depositing onto said substrate a first interlayer of a substantially optically transparent material capable of forming a strong chemical bond to said substrate which first interlayer is transparent to light in the visible region of 350 to approximately 750 nanometers and which is selected from the group consisting of silicon nitride, titanium nitride, tantalum nitride, hafnium nitride, zirconium nitride, boron nitride, yttrium oxide, germanium oxide, hafnium oxide, silicon oxide, silicon dioxide, tantalum oxide, titanium oxide, zirconium oxide, silicon carbide, germanium carbide, aluminum oxide, cerium oxide, tin oxide, thorium oxide, lithium oxide, sodium oxide, potassium oxide, rubidium oxide, cesium oxide, francium oxide, beryllium oxide, magnesium oxide, calcium oxide, strontium oxide, barium oxide, radium oxide, barium fluoride, cerium fluoride, magnesium fluoride, thorium fluoride, calcium fluoride, neodymium fluoride, lead fluoride, sodium fluoride, lithium fluoride, zinc selenide, zinc sulfide, mixtures thereof, and chemically bonded combinations thereof;
chemically vapor depositing a second interlayer immediately adjacent to said first interlayer and away from said substrate of a substantially optically transparent material devoid of alkali metal atoms and fluorine and capable of forming a strong chemical bond to said first interlayer and a strong chemical bond to diamond-like carbon;
chemically vapor depositing a substantially optically transparent first diamond-like carbon layer which is transparent to light in the visible region of 350 to approximately 750 nanometers and having a thickness of at least 200 A thick onto said coated substrate;
chemically vapor depositing immediately adjacent to said first diamond-like carbon layer a third interlayer of a substantially optically transparent material devoid of alkali metal atoms and fluorine and capable of forming a strong chemical bond to diamond-like carbon;
chemically vapor depositing a second substantially optically transparent diamond-like carbon layer onto said third interlayer;

cooling said coated substrate by extinguishing said deposition process and passing an inert gas over said substrate until the temperature of said substrate has reached substantially room temperature during said cool-down step; and recovering a coated substrate product exhibiting greatly improved wear resistance for severe abrasive environments.
102. The method of Claim 101 wherein said second interlayer and said third interlayer comprise a substantially optically transparent material selected from the group consisting of silicon nitride, titanium nitride, tantalum nitride, hafnium nitride, zirconium nitride, boron nitride, germanium oxide, hafnium oxide, silicon oxide, silicon dioxide, tantalum oxide, titanium oxide, yttrium oxide, zirconium oxide, silicon carbide, gernnanium carbide, mixtures thereof, and chemically bonded combinations thereof.
103. The method of Claim 101 wherein the thickness of said second interlayer is in the range of about 1µm to about 20µm.
104. The method of Claim 103 wherein the first interlayer comprises silicon dioxide and said second interlayer comprises a chemically bonded combination of silicon oxide and silicon nitride.
105. The method of Claim 101 wherein said first composite layer comprises at least one pair of separately deposited said second interlayers.
106. The method of Claim 101 wherein the thickness of said first interlayer, said second interlayer and said third interlayer is at least 2µm thick.
107. The method of Claim 101 wherein the thickness of said first diamond-like carbon layer and said second diamond-like carbon Layer is at least 50 .ANG.
thick.
108. The method of Claim 107 wherein the thickness of at least one of said first interlayer, said second interlayer, said third interlayer, said first diamond-like carbon layer and said second diamond-like carbon layer is selected to minimize the reflection light at predetermined wavelengths.
109. The method of Claim 101 wherein the thickness of at least one of said first interlayer, said second interlayer, said third interlayer, said first diamond-like carbon layer and said second diamond-like carbon layer is selected to maximize the reflection of Fight at predetermined wavelengths.
110. The method of Claim 101 wherein the thickness of said second interlayer, said third interlayer, said first diamond-like carbon layer and said second diamond-like carbon layer corresponds to integer multiples of quarter wavelength optical thickness at predetermined wavelengths.
111. The method of Claim 101 wherein the thickness of said first interlayer, said second interlayer, said third interlayer, said first diamond-like carbon layer and said second diamond-like carbon layer corresponds to integer multiples of quarter wavelength optical thickness at predetermined wavelengths.
112. The method of Claim 101 wherein said third interlayer comprises a substantially optically transparent material selected from the group consisting of silicon nitride, titanium nitride, tantalum nitride, hafnium nitride, zirconium nitride, boron nitride, germanium oxide, hafnium oxide, silicon oxide, silicon dioxide, tantalum oxide, titanium oxide, yttrium oxide, zirconium oxide, silicon carbide, germanium carbide, mixtures thereof, and chemically bonded combinations thereof.
113. The method of Claim 112 wherein said second interlayer comprises a substantially optically transparent metallic material capable of reflecting visible light selected from the group consisting of silicon, germanium, hafnium, molybdenum, tungsten, yttrium, tantalum, titanium and zirconium.
114. The method of Claim 113 wherein the thickness of said first interlayer is in the range of about 5.ANG. to about 20um and the thickness of said second interlayer is in the range of about 10.ANG. to about 1000.ANG..
115. The method of Claim 112 wherein said second interlayer comprises a substantially optically transparent metallic material capable of reflecting visible light selected from the group consisting of vanadium, niobium, chromium, manganese, rhenium, technetium, iron, cobalt, iridium, rhodium, nickel, palladium, platinum, copper, silver, gold, zinc, ruthenium, indium, aluminum, tin, osmium, thallium, lead, antimony, bismuth and polonium.
116. The method of Claim 115 wherein the thickness of said first interlayer is in the :range of about 5.ANG. to about 20µm and the thickness of said second interlayer is in the range of about 10.ANG. to about 1000.ANG..
117. The method of Claim 115 including a fourth interlayer disposed between said second interlayer and said first diamond-like carbon layer of a substantially optically transparent material devoid of alkali metal atoms and fluorine and capable of forming a strong chemical bond with said second interlayer and said first diamond-like carbon layer.
118. The method of Claim 117 wherein said fourth interlayer comprises a substantially optically transparent material selected from the group consisting of silicon nitride, titanium nitride, tantalum nitride, hafnium nitride, zirconium nitride, boron nitride, yttrium oxide, germanium oxide, hafnium oxide, silicon oxide, silicon dioxide, tantalum oxide, titanium oxide zirconium oxide, silicon carbide, germanium carbide:, mixtures thereof, and chemically bonded combinations thereof.
119. The method of Claim 117 wherein the thickness of at least one of said first interlayer, said fourth interlayer, said third interlayer, said first diamond-like carbon layer and said second diamond-like carbon layer is selected to minimize the reflection of light at predetermined wavelengths.
120. The method of Claim 117 wherein the thickness of at least one of said first interlayer, said fourth interlayer, said third interlayer, said first diamond-like carbon layer and said second diamond-like carbon layer is selected to maximize the reflection of light at predetermined wavelengths.
121. The method of Claim 117 wherein the thickness of said fourth interlayer, said third interlayer, said first diamond-like carbon layer and said second diamond-like carbon layer corresponds to integer multiples of quarter wavelength optical thickness at predetermined wavelengths.
122. The method of Claim 117 wherein the thickness of said first interlayer, said fourth interlayer, said third interlayer, said first diamond-like carbon layer and said second diamond-like carbon layer corresponds to integer multiples of quarter wavelength optical thickness at predetermined wavelengths.
123. The method of Claim 101 wherein said first composite layer includes a fifth interlayer disposed between said second interlayer and said first diamond-like carbon layer of a substantially optically transparent material devoid of alkali metal atoms and fluorine and capable of forming a strong chemical bond with said second interlayer and said diamond-like carbon outer layer.
124. The method of Claim 123 wherein said third interlayer and said fifth interlayer comprise a substantially optically transparent material selected from the group consisting of silicon nitride, titanium nitride, tantalum nitride, hafnium nitride, zirconium nitride, boron nitride, yttrium oxide, germanium oxide, hafnium oxide, silicon oxide, silicon dioxide, tantalum oxide, titanium oxide, zirconium oxide, silicon carbide, germanium carbide, mixtures thereof, and chemically bonded combinations thereof.
125. The method of Claim l24 wherein the thickness of said first and second interlayers are in the range of about 5.ANG. to about 20µm and the thickness of said fifth interlayer is in the: range of about 1µm to about 20µm.
126. The method of Claim 123 wherein said second interlayer comprises a substantially optically transparent material selected from the group consisting of silicon nitride, titanium nitride, tantalum nitride, hafnium nitride, zirconium nitride, boron nitride, yttrium oxide, germanium oxide, hafnium oxide, silicon oxide, silicon dioxide, tantalum oxide, titanium oxide, zirconium oxide, silicon carbide, germanium carbide, aluminum oxide, cerium oxide, tin oxide, thorium oxide, lithium oxide, sodium oxide, potassium oxide, rubidium oxide, cesium oxide, francium oxide, beryllium oxide, magnesium oxide, calcium oxide, strontium oxide, barium oxide, radium oxide, barium fluoride, cerium fluoride, magnesium fluoride, thorium fluoride, calcium fluoride, neodymium fluoride, lead fluoride, sodium fluoride, lithium fluoride, zinc selenide, zinc sulfide, mixtures thereof, and chemically bonded combinations thereof.
127. The method of Claim 123 wherein the thickness of at least one of said first interlayer, said second interlayer, said fifth interlayer, said first diamond-like carbon layer, said third interlayer and said second diamond-like carbon layer is selected to minimize the reflection of light at predetermined wavelengths.
128. The method of Claim 123 wherein the thickness of at least one of said first interlayer, said second interlayer, said fifth interlayer, said first diamond-like carbon layer, said third interlayer and said second diamond-like carbon layer is selected to maximize the reflection of light at predetermined wavelengths.
129. The method of Claim 125 wherein the thickness of said second interlayer, said third interlayer, said fifth interlayer said first diamond-like carbon layer and said second diamond-like carbon layer corresponds to integer multiples of quarter wavelength optical thickness at predetermined wavelengths.
130. The method of Claim 123 wherein the thickness of said first interlayer, said second interlayer, said third interlayer, said fifth interlayer said first diamond-like carbon layer and said second diamond-like carbon layer corresponds to integer multiples of quarter wavelength optical thickness at predetermined wavelengths.
131. The method of Claim 72 wherein said first interlayer further comprises a substantially optically transparent material selected from the group consisting of aluminum oxide, silicon oxide, silicon dioxide, silicon nitride, mixtures thereof and chemically bonded combinations thereof, and said second interlayer comprises substantially optically transparent silicon oxy-nitride.
132. The method of Claim 131 wherein the substrate is a bar code scanner window.
133. The method of Claim 131 wherein said first interlayer is about 10 .ANG.
to 1 µm thick.
134. The method of Claim 131 wherein said second interlayer is about 1 µm to 20 µm thick.
135. The method of Claim 134 wherein said first interlayer is aluminum oxide.
136. The method of Claim 134 wherein said first interlayer is silicon dioxide.
137. The method of Claim 134 wherein said first interlayer is silicon oxy-nitride and the atomic concentration of nitrogen in said second interlayer is greater than the atomic concentration of nitrogen in said first interlayer.
138. The product of the method of Claim 101.
139. The product of the method of Claim 135.
140. The product of the method of Claim 136.
141. The product of the method of Claim 137.
CA002141536A 1992-08-03 1993-06-03 Abrasion wear resistant coated substrate product Expired - Lifetime CA2141536C (en)