CA2233028C - Thin film formation process - Google Patents
Thin film formation process Download PDFInfo
- Publication number
- CA2233028C CA2233028C CA002233028A CA2233028A CA2233028C CA 2233028 C CA2233028 C CA 2233028C CA 002233028 A CA002233028 A CA 002233028A CA 2233028 A CA2233028 A CA 2233028A CA 2233028 C CA2233028 C CA 2233028C
- Authority
- CA
- Canada
- Prior art keywords
- layer
- porous
- forming
- thin film
- substrate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
A process for thin film formation is provided which comprises a step of separation of a substrate constituted of a nonporous Si layer, a porous Si layer formed thereon, and a less porous Si layer formed further thereon into the nonporous Si layer and the less porous Si layer at the porous Si layer, wherein the separation is caused by projecting a laser beam through the side face of the substrate. From the separated substrate, an SOI substrate is prepared, and the non porous Si layer is recycled to the SOI
substrate production process. This SOI substrate production process saves the consumption of the material and lowers the production cost. The substrates are separated definitely. A process for producing a photoelectric transducing apparatus such as solar cells with material saving and low cost is also provided in which the porous layer is separated definitely without strong adhesion between the substrate and a jig.
substrate production process. This SOI substrate production process saves the consumption of the material and lowers the production cost. The substrates are separated definitely. A process for producing a photoelectric transducing apparatus such as solar cells with material saving and low cost is also provided in which the porous layer is separated definitely without strong adhesion between the substrate and a jig.
Description
(~A
THIN FILM FORMATION PROCESS
BACKGROUND OF THE INVENTION
Field of the Invention The present invention relates to a process for forming a thin film for an SOI substrate, or a photoelectric transducer such as solar cells and area sensors.
Related Background Art The integrated circuit formed on a substrate of structure of SOI (semiconductor on insulator) has various advantages over integrated circuits formed on a usual silicon wafer, such as (1) ease of separation of a dielectric material and potentiality of high integration, (2) high resistance against radiation ray, (3) low floating capacity and high speed processing, (4) no welling process required, (5) capability of latch-up prevention, and (6) high speed and low energy consumption owing to formation of a thin complete depletion type field effect transistor.
For formation of a substrate of the SOI structure, methods are disclosed in U.S. Patent 5,371,037, and T.
Yonehara et al., Appl. Phys. Lett., vol.64, 2108 (1994). Figs. 16A to 16E, and Figs. 17A to 17D show the processes. In the drawings, the numerals 1 and 5 indicates an Si wafer, 2 a nonporous Si layer, 3 a porous Si layer, 4 an epitaxial Si layer, 6 a single crystalline Si layer, and 7 an Si oxide layer. Si wafer 1 as a device substrate shown in Fig. 16A is anodized to prepare a substrate constituted of nonporous Si layer 2 and porous Si layer 3 formed thereon as shown in Fig. 16B. Epitaxial layer 4 is formed on the surface of porous Si layer 3 as shown in Fig. 16C. Separately, Si wafer 5 as a supporting substrate shown in Fig. 16D is provided, and the surface is oxidized to form a substrate constituted of monocrystalline Si layer 6 and Si oxide layer 7 on the surface as shown in Fig. 16E. The substrate (2, 3, 4) of Fig. 16C is turned over, and is placed on the substrate (6, 7) of Fig. 16E with epitaxial layer 4 and Si oxide layer 7 counterposed as shown in Fig. 17A.
The two substrates are bonded by adhesion of epitaxial layer 4 to Si oxide layer 7 as shown in Fig. 17B. Then nonporous Si layer 2 is removed mechanically by grinding from the non-bonded layer side to uncover porous Si layer 3 as shown in Fig. 17C. Porous Si layer 3 is removed by wet etching with an etching solution for selective etching of porous Si layer 3 as shown in Fig. 17D to obtain an SOI substrate having epitaxial layer 4 of extremely uniform thickness for a semiconductor of an SOI substrate.
In the above process for producing the substrate of an SOI structure, nonporous Si layer 2 is removed from the substrate of Fig. 17B by grinding to obtain the substrate of Fig. 17C. Therefore, one substrate 1 to be worked into two-layers of nonporous layer 2 and porous layer 3 is required for production of each one SOI substrate. Japanese Patent Application Laid-Open No. 7-302889 discloses a method of repeated use of nonporous Si layer 2 in the SOI substrate production process. In the disclosed process, parts 4,7,6 for the SOI substrate is separated from part 2 at porous layer 3 by applying a pulling, squeezing, or shearing force, or inserting a jig into porous layer 3, and separated nonporous Si layer 2 is used repeatedly as Si wafer l of Fig. 16A.
Nowadays, most of solar cells employ amorphous Si for the structure suitable for large area. However, monocrystalline Si and polycrystalline Si are also noticed for the solar cells in view of the transducing efficiency and the life thereof. Japanese Patent Application Laid-Open No. 8-213645 discloses a process of providing a thin film solar cell at a low cost. In this process, porous Si layer 3 is formed on Si wafer 1; thereon, p+-type Si layer 21, p-type Si layer 22, and n+-type Si layer 23 are grown epitaxially for solar cell layers; protection layer 30 is formed on n+-layer 23;
jig 31 is bonded to reverse face of Si wafer 1 and jig 32 is bonded onto the surface of protection layer 30 by adhesive 34; jigs 31,32 are pulled respectively in opposite directions to break porous Si layer 3 mechanically to separate solar layers 21,22,23. The solar cell layers 21,22,23 are interposed between two plastic substrate to provide a flexible thin film solar cell. This disclosure mentions repeated use of Si wafer 1, and partial notching 33 of the edge side face of porous Si layer 3 by mechanical method or laser beam irradiation.
In production of SOI substrates, the process disclosed the aforementioned Japanese Patent Application Laid-Open No. 7-302889 enables reduction of the production cost by repeated use of the Si wafer.
However, this method is not satisfactory in reproducibility.
In production of solar cells, the process disclosed in the above Japanese Patent Application Laid-Open No. 8-213645 does not always allow definite separation at the porous Si layer, causing occasionally cracking in the epitaxial layer to result in lower production yield. Further, this process conducts the separation by mechanical pulling, which requires strong adhesion between the jig and the monocrystalline Si layer and is not suitable for mass production.
SUMMARY OF THE INVENTION
An object of the present invention is to provide a process for forming a thin film at a low cost with definite separation of a wafer with efficient utilization of the wafer with effective use of the resource with high productivity in production of photoelectric transducer devices such as solar cells.
After comprehensive studies for solving the above problems, the process below has been found by the inventors of the present invention. The process of the present invention for forming a thin film comprises a step of separation of a substrate constituted of a nonporous layer, a porous layer formed thereon, and a less porous layer which has a less porosity than that of the porous layer formed further on the porous layer into the nonporous layer and the less porous layer at the porous layer, the step of separation being caused by projecting a laser beam through the side face of the substrate into the center of the substrate.
The laser beam is preferably focused onto the side edge face of the porous layer to swell the porous layer. The porous layer is formed on the nonporous layer desirably by anodization of an Si wafer. The nonporous layer may be pulled by applying a slight force to the substrate by a vacuum chuck brought into close contact with the face reverse to the porous layer side.
The laser beam is preferably an excimer laser beam in the present invention. The laser beam may be projected to plural sites of the porous layer. The laser beam may be focused by a cylindrical lens linearly and is projected along the porous layer.
The aforementioned less porous layer is preferably formed on the porous layer by epitaxial growth. After the epitaxial layer is bonded to a supporting substrate having an insulation layer at least on the surface, the separation is caused at the porous layer. The porous layer remaining on the epitaxial layer is removed to utilize the epitaxial layer and the insulation layer respectively as a semiconductor layer and an underlaying insulation layer of an SOI substrate. The supporting substrate having an insulating layer at least on the surface is preferably prepared by oxidation of the surface of an Si wafer. Otherwise, an insulating layer is formed on the epitaxial layer surface; it is bonded to a supporting substrate;
separation is caused at the porous layer; the remaining porous layer is removed from the epitaxial layer; and the epitaxial layer and the insulating layer are employed respectively as the semiconductor layer and the underlying insulation layer of the SOI substrate.
The supporting substrate may be either an Si wafer having an oxidized surface or a quartz substrate.
The less porous layer may be formed, after the formation of the porous layer by anodization of the wafer, by subsequent anodization with less current density. After the bonding of the less porous layer to the supporting substrate, the separation is caused, and the less porous layer may be employed as a photoelectric transducing layer of a photoelectric transducer. The photoelectric transducing layer may be made of an epitaxial layer. The substrate and the layers are preferably formed from silicon.
BRIEF DESCRIPTION OF THE DRAWINGS
Fig. 1 illustrates a separation step in Embodiment 1 in which a laser beam is projected to a porous Si layer.
Fig. 2 illustrates substrates after the separation.
Fig. 3 illustrates a step for producing an SOI
substrate by employing an Si wafer as the base material in Embodiment 1.
Fig. 4 illustrates an SOI substrate produced by a step for producing an SOI substrate by employing an Si wafer as the base material in Embodiment 1.
Figs. 5A, 5B, 5C, and 5D illustrate steps for producing an SOI substrate by employing a quartz plate as the base material in Embodiment 1.
Figs. 6A, 6B, 6C, and 6D illustrate steps for producing an SOI substrate by employing an Si wafer as the base material in Embodiment 1.
Figs. 7A, 7B, 7C, and 7D illustrate steps for producing an SOI substrate.
Figs. 8A, 8B, 8C, and 8D illustrate steps for producing an SOI substrate.
Fig. 9 illustrates a separation step in Embodiment 2 in which a laser beam is projected to a porous Si layer.
Fig. 10 illustrates a separation step in Embodiment 3 in which a laser beam is projected to a porous Si layer.
Fig. 11 illustrates a separation step in Embodiment 4 in which a laser beam is projected to a porous Si layer.
Figs. 12A, 12B and 12C illustrate processes for producing a monocrystalline Si solar cell.
Fig. 13 illustrates a separation step in Embodiment 5 in which a laser beam is projected to a porous Si layer.
Fig. 14 illustrates substrates after the separation.
Figs. 15A is a perspective view of a monocrystalline Si solar cell, and Fig. 15B is a sectional view thereof.
Figs. 16A, 16B, 16C, 16D and 16E illustrate steps of producing an SOI substrate.
Figs. 17A, 17B, 17C and 17D illustrate steps of producing an SOI substrate.
Fig. 18 illustrates a conventional process for producing a solar cell.
DESCRIPTION OF THE PREFERRED EMBODIMENTS
The present invention is described by reference to Embodiments 1 to 8. Embodiments 1 to 4 describe production of an SOI substrate. Embodiments 5 to 7 describe production of photoelectric transducing device such as solar cells and area sensors. Embodiment 8 describes a method in which the layer for the separation is formed by ion implantation. The present invention covers not only the described Embodiments but also combination of the Embodiments.
In Embodiment 1 of producing an SOI substrate, a laser beam is employed for separation of the wafer to be recycled and the SOI substrate at the porous layer.
The laser beam is projected to the side face (edge face) in parallel with the plate-shaped substrates at a laser intensity adjusted to reach the substrate center.
The laser beam is projected to relatively fragile layer such as larger porosity layer or a defective layer having micro-bubbles and absorbed thereby. The porous fragile layer having absorbed the laser beam becomes more fragile, whereby the less porous layer on the porous fragile layer and nonporous layer are separated at the fragile layer. The method of laser beam projection is described in detail in the following Embodiments.
Fig. 1 illustrates the separation process of this embodiment. In Fig. 1, the same reference numerals are used as in Figs. 16A to 16E and Figs. 17A to 17D. The numeral 10 indicates a lens, 11 an optical microscope, 12 a vacuum chuck, and 13 a laser beam. LS indicates a laser source, and ATL indicates an article constituted of layers 2, 3, 4, 6, and 7 before the separation. A
laser beam is projected to the side wall of porous layer 3 from laser source LS. Laser source LS is an excimer laser of high output employing XeCl, KrF, ArF, or the like. The output capacity is preferably in the range from 300 mJ/cm2 to 1 J/cm2, more preferably about 500 mJ/cm2. The excimer laser emits W light, so that lens 10 is made of quartz or fluorite capable of transmitting the UV light. With this optical system, the laser beam is converged to have a projection area width to 0.1 ~um. Optical microscope 11 is employed, as necessary, to confirm the precise projection of laser beam 13 to porous layer 3 of 0.1 to 30 ~m thick. Since porous layer 3 is fragile and can readily be broken for separation in comparison with nonporous layer 2 and epitaxial layer 4 as a less porous layer, laser beam 13 need not be strictly projected only to porous layer 3.
The laser source LS for emitting laser beam 13 is preferably an excimer laser apparatus of high power, but may be an Ar laser, or a YAG laser. For promoting the layer separation, a liquid such as water, methyl alcohol, ethyl alcohol, and isopropyl alcohol may be incorporated into porous layer 3 by injection or adsorption. The liquid, which has a larger thermal expansion coefficient than the solid like Si, promotes the layer separation by expansion.
Vacuum chuck 12 as the substrate holder has a cavity for holding a gas, and holds substrate ATL, before the separation, by contact with the outside face of nonporous layer 2 or monocrystalline layer 6 by evacuation of the gas. In this Embodiment, a pair of vacuum chucks 12 can rotate around the axis at the center of the substrate to project laser beam 13 to the entire side wall of the porous layer 3. Vacuum chucks 12 may be employed only for fixing and rotating the substrate, but may also be employed for applying slight pulling force to the substrate to promote the layer separation.
The laser beam penetrates the side wall of porous layer 3 to the proximity to the center of substrate ATL. Porous layer 3 becomes more fragile by absorption of the laser berm to cause separation of substrate ATL
without break of the nonporous portion.
By the separation, substrate 4,7,6 for the SOI
substrate and substrate 2 to be recycled are separated from each other at porous layer 3. In Fig. 2, portions 3' of porous layers remains on the surfaces (separation plane) of the respective substrates. By reducing sufficiently the thickness of porous layer 3 formed by the anodization, the remaining portions can be made absent practically from one or both of the substrates.
A process for thin film formation by the wafer separation as shown in Fig. 1 is described below.
Firstly, the substrate for the bonding is prepared. Fig. 3 is a sectional view of an apparatus for anodizing an Si wafer. The numeral 1 indicates an Si wafer, 27 an etching solution of hydrofluoric acid type contained in vessel RV, 28 a positive metal electrode, and 29 a negative metal electrode. Si wafer 1 to be anodized is preferably of a p-type, but may be of an n-type of low resistance. An n-type wafer having holes formed by projection of a light beam can also be readily made porous. In Fig. 3, a voltage is applied between positive electrode 28 at the left side and negative electrode 29 at the right side, and Si wafer 1 is placed parallel to the both electrodes to apply an electric field perpendicular to the face of Si wafer in the etching solution. Thereby wafer 1 is made porous from the side of negative electrode 29. Concentrated hydrofluoric acid (49~ HF) is employed as etching solution 27 of the hydrofluoric acid type. Since gas bubbles are generated from Si wafer l, an alcohol is preferably added as a surfactant into etching solution 27 to remove the bubbles. The alcohol includes methanol, ethanol, propanol, and isopropanol. Instead of surfactant addition, the solution may be stirred by a stirrer during the anodization.
The thickness of the porous layer is preferably in the range from 0.1 to 30 ,um.
Negative electrode 29 is preferably made of a material resistant against the hydrofluoric acid, such as gold (Au) and platinum (Pt). Positive electrode 28 is also made preferably of a material resistant against the hydrofluoric acid, but may be made of any generally used metal material. The anodization is conducted at a maximum current density of several hundred mA/cm2 or less, but should be more than 0 mA/cm2. The current density is selected so that a high-quality epitaxial layer can be formed on the resulting porous Si layer and the separation can readily be caused at the porous layer. Specifically, at a larger current density in the anodization, the density of Si in the porous Si layer becomes lower, and the volume of the pores is larger, and the porosity (ratio of the pore volume to the total volume of the porous layer) thereof is larger. In spite of many pores formed in the interior of the Si layer, the resulting porous Si retains its monocrystallinity. Owing to the monocrystallinity of the porous Si layer, another monocrystalline Si layer can be grown epitaxially thereon.
For formation of an epitaxial Si layer having no lamination defect, the porosity of the porous Si layer is preferably smaller at the portion to be brought into contact with the epitaxial Si layer. On the other hand, for easy separation of the device substrate and the SOI substrate at the porous Si layer, the porosity of the porous Si layer is preferably larger.
Therefore, ideally, the porosity of the porous Si layer is smaller at the outermost surface, and is larger at the side near to the nonporous Si layer. Fig. 4 is a sectional view illustrating the ideal state of the porous Si layer. Porous Si layer 3a, the surface side portion of porous Si layer 3, is formed with a smaller porosity, and porous Si layer 3b, the nonporous Si layer side portion of porous Si layer 3, is formed with a larger porosity. For obtaining this structure, the initial stage of the anodization is conducted at a lower current density to prepare portion 3a, and the later stage of the anodization is conducted at a higher current density to prepare portion 3b. With this structure, the separation of the substrate occurs only at layer 3b, and an epitaxial Si layer can be formed without lamination defect on porous Si layer 3a. The epitaxial Si layer is formed preferably by a growth process such as molecular beam epitaxial growth, plasma CVD, low pressure CVD, photo-assisted CVD, bias sputtering, and liquid phase growth. Particularly, low temperature growth is preferred.
As described above, Si wafer 1 shown in Fig. 5A is made porous at the surface as shown in Fig. 5B.
Thereby Si wafer 1 comes to have the structure constituted of nonporous Si layer 2 and porous Si layer 3 laminated thereon.
Subsequently, nonporous epitaxial Si layer 4 is formed on porous Si layer 3 as shown in Fig. 5C. If necessary, the surface of epitaxial Si layer 4 is thermally oxidized to form Si oxide layer 8 of thickness between 0.05 ~m to 2 ~m as shown in Fig. 5D.
As described above, substrate PW called a prime wafer, a bond wafer, or a device substrate is treated before the bonding.
On the other hand, substrate HW called a handle wafer, a base wafer, or a supporting substrate is treated as described below.
An Si wafer is provided, and if necessary, the surface thereof is thermally oxidized to form an Si oxide film of thickness ranging from 0.05 to 3 ~m.
The process of bonding and separation of the substrates is explained below by reference to Figs. 6A
to 6D.
The surface of Si oxide layer 8 on epitaxial Si layer 4 of substrate PW is confronted with the surface of Si oxide layer 7 of substrate HW, and both faces are bonded at room temperature as shown in Fig. 6A. Then the bonding between Si oxide layer 8 and Si oxide layer 7 is strengthened by anode bonding, pressing, or heat treating, or combination thereof to form an article ATL
comprising the bonded substrates as shown in Fig. 6B.
Bonded article ATL having the structure shown in Fig. 6B is placed between a pair of vacuum chucks 12 of the device shown in Fig. 1. With rotation of article ATL, an excimer laser beam is projected to and focused on the portion of porous Si layer 3 of the side face of article ATL. The projected excimer laser beam is absorbed by the entire of the porous Si layer. In such a manner, nonporous Si layer 2 of substrate PW side is separated from substrate HW as shown in Fig. 6C. By the separation, epitaxial Si layer 4 is transferred onto the surface of substrate HW. Porous Si layer 3 having been broken by absorption of the laser beam may remain on one or both of nonporous Si layer 2 and epitaxial Si layer 4. Fig. 6C shows porous Si layer 3 remaining only on epitaxial Si layer 4.
Porous Si layer 3, when it remains on the side of substrate HW, is removed selectively by selective etching. In the selective etching, the porous Si layer is etched more than the nonporous Si layer by nonelectrolytic wet chemical etching by use of an etching solution such as hydrofluoric acid, a mixture of hydrofluoric acid with an alcohol, and a mixture of hydrofluoric acid with aqueous hydrogen peroxide. In particular, by use of a mixture of hydrofluoric acid with hydrogen peroxide, the selective etching ratio of the porous Si layer to the nonporous Si layer is as high as about 105. Thus, epitaxial Si layer 4 remains in a uniform thickness on the surface of substrate HW.
Thereby an SOI substrate having extremely uniform semiconductor layer 4 on the insulation layer as shown in Fig. 6D.
Separated nonporous layer 2 is again used as the prime wafer for production of another SOI substrate.
In the process for producing the SOI substrate in this Embodiment, the supporting substrate may be a complete insulating substrate such as a glass substrate and a quartz substrate. Figs. 7A to 7D illustrate the steps of producing an SOI substrate by use of quartz substrate as the supporting substrate. The device substrate PW at the upper side in Fig. 7A is prepared in the same manner as described by reference to Fig. 5A
to 5D. Quartz substrate 9 as supporting substrate HW
is confronted with an Si oxide layer 8 and are bonded tightly by anode bonding, pressing, or thermal treatment, or combination thereof as shown in Fig. 7B.
Then, the two substrate is separated by projection of a laser beam in the same manner as described before.
Epitaxial Si layer 4 and porous Si layer 3 are transferred onto quartz substrate 9 as shown in Fig.
7C. The remaining porous Si layer 3 is selectively removed in the aforementioned manner. Thus an SOI
substrate is obtained which is constituted of quartz base plate 9 and nonporous monocrystalline thin Si film CA 02233028 l998-03-23 4 formed thereon as shown in Fig. 7D.
In another process of preparing the SOI substrate of this Embodiment, an Si wafer is used as the supporting substrate, and an insulating layer of an SOI
structure is formed by forming an Si oxide layer on the epitaxial Si layer on the device substrate side without forming the Si oxide layer on the Si wafer side. Figs.
8A to 8D shows this process. The upper device substrate in Fig. 8A is prepared in the same manner as described by reference to Fig. 5. The surface of monocrystalline Si layer 5 of an Si wafer is counterposed with the surface of Si oxide layer 8, and bonded thereto. The bonding can be strengthened by anode bonding, pressing, or heating, or combination thereof. Thus article ATL is obtained as shown in Fig.
8B. Article ATL is separated at the porous Si layer to transfer epitaxial Si layer 4 of nonporous monocrystalline Si onto nonporous Si layer 5 as supporting substrate HW by means of the apparatus shown in Fig. 1. If porous Si layer 3 remains on epitaxial Si layer 4 of supporting substrate HW as shown in Fig.
8C, it is selectively removed by the aforementioned method. Thus an SOI substrate is obtained as shown in Fig. 8D.
Embodiment 2 An SOI substrate is produced in this Embodiment by utilizing an excimer laser beam for separating, at the porous Si layer, the Si wafer to be recycled and the substrate to be worked into an SOI substrate. The excimer laser beam is focused on one point and is allowed to scan with the substrate plate fixed.
Fig. 9 illustrates the separation step. The laser beam is focused on the side face of article ATL with lens 10, and is allowed to scan along the circumference by aid of guide 14. The same reference numbers are used to indicate the same articles as in Fig. 1. In this Embodiment, monocrystalline Si layer 6 as nonporous layer and nonporous Si layer 2 constituting article ATL are fixed from the outside by chucks 12.
The laser beam 13 from an excimer laser apparatus is focused and projected onto one point on the side wall of porous Si layer 3 through lens 10. Lens 10 is allowed to move together with laser beam 13 for the scanning to separate the SOI substrate composed of layers 4, 7, 6 from substrate 2 at porous Si layer 3 to recycle substrate 2 to the production steps. The less porous layer 4 on the layers 6, 7 is obtained. The other steps and the materials are the same as in Embodiment 1.
Embodiment 3 An SOI substrate is produced in this Embodiment by utilizing excimer laser for separating the Si wafer to be recycled and the SOI substrate at the porous Si layer. The excimer laser beam is focused linearly by a cylindrical lens and is projected along the side face of the porous Si layer.
Fig. 10 illustrates the separation step. The numeral 15 indicates a cylindrical lens. The same reference numbers are used to indicate the same articles as in Fig. 1. The laser beam is focused linearly in a vertical direction for efficient projection onto the side face of porous Si layer 3 of an extremely small thickness of O.l to 30 ~m. In place of cylindrical lens 15, a toric lens may be used to project linearly focused laser beam to the curved side wall of porous Si layer 3. The other steps are the same as in Embodiment 1.
Embodiment 4 An SOI substrate is produced in this Embodiment by utilizing excimer laser for separating, at the porous Si layer, the Si wafer to be recycled and the SOI
substrate. The excimer laser beams are focused linearly by cylindrical lenses and are projected along the end face of the porous Si layer. In the laser beam projection, as shown in Fig. 11, the laser light is separated into four beams, and laser beams 13 are respectively focused linearly and projected with four cylindrical lenses 15 from four directions along the end face of porous Si layer 3. In this Embodiment, monocrystalline Si layer 6 and nonporous Si layer 2 are fixed from the outside by chucks 12. The other steps are the same as in Embodiment 1.
Embodiment 5 A solar cell is produced in this Embodiment.
Figs. 12A to 12C illustrate the steps of forming a photoelectric transducing layer for transducing light energy to electric energy. An p-type Si wafer 1 is provided as shown in Fig. 12A. The surface of Si wafer 1 is made porous by anodization as explained before by reference to Fig. 3 to prepare a substrate constituted of nonporous Si layer 2 of wafer 1 and porous Si layer 3 formed thereon as shown in Fig. 12B. On porous Si layer 3, an epitaxial Si layer to serve as photoelectric transducer 18 is formed as shown in Fig.
12C by molecular beam epitaxial growth, plasma CVD, low pressure CVD, photo-assisted CVD, bias sputtering, liquid crystal growth method, or a like method to prepare a substrate PW.
The epitaxial Si layer is allowed to grow with addition of a dopant for use as a photoelectric transducing layer. Thereby, the epitaxial layer has PN
junction caused by lamination of an n+ layer, a p~
layer, and a p+ layer formed in this order on porous Si layer 3. The surface of the p+ layer of photoelectric transducing layer 18 grown epitaxially is bonded and connected to backside metal electrode 16 formed preliminarily on the surface of plastic substrate 17.
Then vacuum chuck 12 is brought into close contact with the outside of nonporous Si layer 2. A laser beam 13 from an excimer laser apparatus is focused and projected through lens 10 onto porous Si layer 3.
Although the laser light is focused onto one point in Fig. 13, the laser beam may be projected in any way as described in Embodiments 1 to 4. In such a manner, substrate HW to be used as a solar cell is separated at porous Si layer 3 from substrate PW to be recycled to production process as shown in Fig. 14.
A meshed surface metal electrode 19 is formed on the surface of photoelectric transducing layer 18 as shown in Fig. 15A. Wiring 24 is connected to surface metal electrode 19 and backside metal electrode 16.
Protection layer 20 is formed on the surface metal electrode 19. Fig. 15B is a sectional view taken at 15B-15B in Fig. 15A. Photoelectric transducing layer 18 is constituted of the layers of n+ layer 23 in contact with surface metal electrode 19, p layer 22, and p+ layer 21 in contact with backside metal electrode 16, arranged in this order from the upper side. In Figs. 15A and 15B, surface metal electrode l9 is shown in a shape of a mesh to transmit light. However, it may be replaced by a transparent electrode made of a material like IT0. Backside metal electrode 16 serves also a back reflector for returning unabsorbed transmitted light to photoelectric transducing layer 18, so that it is preferably made of a metallic material having high reflectivity.
CA 02233028 l998-03-23 According to this Embodiment, many solar cells of a monocrystalline thin film can be produced from one Si wafer. Therefore, this Embodiment is advantageous in transducing efficiency, cell life, and production cost.
Further, the substrate is separated by projecting a laser beam to the porous Si layer to cause thermal expansion and distortion of the crystal without application of strong pulling force without necessity of strong bonding between the substrate and the jig or the like. From this point also, the process of this Embodiment is advantageous in production cost.
Embodiment 6 A solar cell is produced in this Embodiment also.
In the above Embodiment 5, photoelectric transducer 18 iS constituted of an epitaxial Si layer formed on porous Si layer 3, whereas in this Embodiment, porous Si layer of a small porosity per se is utilized, as it is, as photoelectric transducing layer 18. In Embodiment 1, it is described that the porosity of the porous Si layer can be varied by changing the current density in anodization. Specifically, in anodization explained by reference to Fig. 3, the higher density of the electric current flowing from electrode 28 to electrode 29 makes larger the porosity of porous Si layer formed on Si wafer 1, while the lower density of the current makes smaller the porosity. By this phenomenon, the surface of p~ type Si wafer 1 is made porous by forming a porous Si layer of a smaller porosity by controlling the current density lower, and porous Si layer 3b of larger porosity is formed under it on nonporous layer 2. To the outermost layer of porous Si layer 3a, donor ions such as P and As are implanted to make the outermost layer on n-type, thereby forming photoelectric transducing layer having porous Si layer of small porosity having PN junction.
Thereafter, the porous Si layer of a smaller porosity as the photoelectric transducer is bonded to backside metal electrode 16 as shown in Fig. 13. The other steps are conducted in the same manner as in Embodiment 5.
According to this Embodiment, many solar cells of a monocrystalline thin film can be produced from one Si wafer. Therefore, this Embodiment is advantageous in transducing efficiency, cell life, and production cost.
Further, epitaxial growth is not conducted in the process of this Embodiment, the production cost is lower than that of Embodiment 5. The photoelectric transducing layer 18 is composed of a porous Si layer of smaller porosity with the monocrystallinity maintained, and light is scattered appropriately by the pores to result in high transducing efficiency.
Embodiment 7 An area sensor is produced. In this Embodiment, a photoelectric transducing layer of monocrystalline thin film is formed from an Si wafer in the same manner as in Embodiment 5 or 6. On this photoelectric transducing layer, optical sensors are arranged two-dimensionally, and matrix wiring is provided. The matrix wiring is formed, for example, by providing a row wiring in place of surface metal electrode 19 in Figs. 15A and 15B and providing a line wiring in place of backside metal electrode 16 in Figs. 15A and 15B.
This Embodiment is advantageous in transducing efficiency, cell life, production cost, area enlargement, and so forth, since many area sensors of a monocrystalline thin film can be produced from one Si wafer.
Embodiment 8 An Si wafer is prepared as one substrate. Over the entire face of the Si wafer, hydrogen ions or rare gas ions are implanted in a prescribed depth by mean of an ion implanter to form a defective layer of microbubbles in the interior of the Si wafer.
Separately, another Si wafer is prepared as the supporting substrate. This supporting substrate is oxidized at the surface, and is bonded to the surface of the above Si wafer having a microbubble-defective layer.
To the bonded wafer article, an excimer laser beam is projected at around the microbubble-defective layer of the side face of the article in a manner shown in Fig. 1, 9, 11, or 13. Thereby, the defective layer is made more fragile by absorption of the excimer laser beam. Then the two wafers are separated.
In such a manner, the monocrystalline Si layer on the defective layer of the one substrate Si layer is transferred onto the silicon oxide film on the other substrate. The microbubble formation by ion implantation is described in detail in U.S. patent No.
THIN FILM FORMATION PROCESS
BACKGROUND OF THE INVENTION
Field of the Invention The present invention relates to a process for forming a thin film for an SOI substrate, or a photoelectric transducer such as solar cells and area sensors.
Related Background Art The integrated circuit formed on a substrate of structure of SOI (semiconductor on insulator) has various advantages over integrated circuits formed on a usual silicon wafer, such as (1) ease of separation of a dielectric material and potentiality of high integration, (2) high resistance against radiation ray, (3) low floating capacity and high speed processing, (4) no welling process required, (5) capability of latch-up prevention, and (6) high speed and low energy consumption owing to formation of a thin complete depletion type field effect transistor.
For formation of a substrate of the SOI structure, methods are disclosed in U.S. Patent 5,371,037, and T.
Yonehara et al., Appl. Phys. Lett., vol.64, 2108 (1994). Figs. 16A to 16E, and Figs. 17A to 17D show the processes. In the drawings, the numerals 1 and 5 indicates an Si wafer, 2 a nonporous Si layer, 3 a porous Si layer, 4 an epitaxial Si layer, 6 a single crystalline Si layer, and 7 an Si oxide layer. Si wafer 1 as a device substrate shown in Fig. 16A is anodized to prepare a substrate constituted of nonporous Si layer 2 and porous Si layer 3 formed thereon as shown in Fig. 16B. Epitaxial layer 4 is formed on the surface of porous Si layer 3 as shown in Fig. 16C. Separately, Si wafer 5 as a supporting substrate shown in Fig. 16D is provided, and the surface is oxidized to form a substrate constituted of monocrystalline Si layer 6 and Si oxide layer 7 on the surface as shown in Fig. 16E. The substrate (2, 3, 4) of Fig. 16C is turned over, and is placed on the substrate (6, 7) of Fig. 16E with epitaxial layer 4 and Si oxide layer 7 counterposed as shown in Fig. 17A.
The two substrates are bonded by adhesion of epitaxial layer 4 to Si oxide layer 7 as shown in Fig. 17B. Then nonporous Si layer 2 is removed mechanically by grinding from the non-bonded layer side to uncover porous Si layer 3 as shown in Fig. 17C. Porous Si layer 3 is removed by wet etching with an etching solution for selective etching of porous Si layer 3 as shown in Fig. 17D to obtain an SOI substrate having epitaxial layer 4 of extremely uniform thickness for a semiconductor of an SOI substrate.
In the above process for producing the substrate of an SOI structure, nonporous Si layer 2 is removed from the substrate of Fig. 17B by grinding to obtain the substrate of Fig. 17C. Therefore, one substrate 1 to be worked into two-layers of nonporous layer 2 and porous layer 3 is required for production of each one SOI substrate. Japanese Patent Application Laid-Open No. 7-302889 discloses a method of repeated use of nonporous Si layer 2 in the SOI substrate production process. In the disclosed process, parts 4,7,6 for the SOI substrate is separated from part 2 at porous layer 3 by applying a pulling, squeezing, or shearing force, or inserting a jig into porous layer 3, and separated nonporous Si layer 2 is used repeatedly as Si wafer l of Fig. 16A.
Nowadays, most of solar cells employ amorphous Si for the structure suitable for large area. However, monocrystalline Si and polycrystalline Si are also noticed for the solar cells in view of the transducing efficiency and the life thereof. Japanese Patent Application Laid-Open No. 8-213645 discloses a process of providing a thin film solar cell at a low cost. In this process, porous Si layer 3 is formed on Si wafer 1; thereon, p+-type Si layer 21, p-type Si layer 22, and n+-type Si layer 23 are grown epitaxially for solar cell layers; protection layer 30 is formed on n+-layer 23;
jig 31 is bonded to reverse face of Si wafer 1 and jig 32 is bonded onto the surface of protection layer 30 by adhesive 34; jigs 31,32 are pulled respectively in opposite directions to break porous Si layer 3 mechanically to separate solar layers 21,22,23. The solar cell layers 21,22,23 are interposed between two plastic substrate to provide a flexible thin film solar cell. This disclosure mentions repeated use of Si wafer 1, and partial notching 33 of the edge side face of porous Si layer 3 by mechanical method or laser beam irradiation.
In production of SOI substrates, the process disclosed the aforementioned Japanese Patent Application Laid-Open No. 7-302889 enables reduction of the production cost by repeated use of the Si wafer.
However, this method is not satisfactory in reproducibility.
In production of solar cells, the process disclosed in the above Japanese Patent Application Laid-Open No. 8-213645 does not always allow definite separation at the porous Si layer, causing occasionally cracking in the epitaxial layer to result in lower production yield. Further, this process conducts the separation by mechanical pulling, which requires strong adhesion between the jig and the monocrystalline Si layer and is not suitable for mass production.
SUMMARY OF THE INVENTION
An object of the present invention is to provide a process for forming a thin film at a low cost with definite separation of a wafer with efficient utilization of the wafer with effective use of the resource with high productivity in production of photoelectric transducer devices such as solar cells.
After comprehensive studies for solving the above problems, the process below has been found by the inventors of the present invention. The process of the present invention for forming a thin film comprises a step of separation of a substrate constituted of a nonporous layer, a porous layer formed thereon, and a less porous layer which has a less porosity than that of the porous layer formed further on the porous layer into the nonporous layer and the less porous layer at the porous layer, the step of separation being caused by projecting a laser beam through the side face of the substrate into the center of the substrate.
The laser beam is preferably focused onto the side edge face of the porous layer to swell the porous layer. The porous layer is formed on the nonporous layer desirably by anodization of an Si wafer. The nonporous layer may be pulled by applying a slight force to the substrate by a vacuum chuck brought into close contact with the face reverse to the porous layer side.
The laser beam is preferably an excimer laser beam in the present invention. The laser beam may be projected to plural sites of the porous layer. The laser beam may be focused by a cylindrical lens linearly and is projected along the porous layer.
The aforementioned less porous layer is preferably formed on the porous layer by epitaxial growth. After the epitaxial layer is bonded to a supporting substrate having an insulation layer at least on the surface, the separation is caused at the porous layer. The porous layer remaining on the epitaxial layer is removed to utilize the epitaxial layer and the insulation layer respectively as a semiconductor layer and an underlaying insulation layer of an SOI substrate. The supporting substrate having an insulating layer at least on the surface is preferably prepared by oxidation of the surface of an Si wafer. Otherwise, an insulating layer is formed on the epitaxial layer surface; it is bonded to a supporting substrate;
separation is caused at the porous layer; the remaining porous layer is removed from the epitaxial layer; and the epitaxial layer and the insulating layer are employed respectively as the semiconductor layer and the underlying insulation layer of the SOI substrate.
The supporting substrate may be either an Si wafer having an oxidized surface or a quartz substrate.
The less porous layer may be formed, after the formation of the porous layer by anodization of the wafer, by subsequent anodization with less current density. After the bonding of the less porous layer to the supporting substrate, the separation is caused, and the less porous layer may be employed as a photoelectric transducing layer of a photoelectric transducer. The photoelectric transducing layer may be made of an epitaxial layer. The substrate and the layers are preferably formed from silicon.
BRIEF DESCRIPTION OF THE DRAWINGS
Fig. 1 illustrates a separation step in Embodiment 1 in which a laser beam is projected to a porous Si layer.
Fig. 2 illustrates substrates after the separation.
Fig. 3 illustrates a step for producing an SOI
substrate by employing an Si wafer as the base material in Embodiment 1.
Fig. 4 illustrates an SOI substrate produced by a step for producing an SOI substrate by employing an Si wafer as the base material in Embodiment 1.
Figs. 5A, 5B, 5C, and 5D illustrate steps for producing an SOI substrate by employing a quartz plate as the base material in Embodiment 1.
Figs. 6A, 6B, 6C, and 6D illustrate steps for producing an SOI substrate by employing an Si wafer as the base material in Embodiment 1.
Figs. 7A, 7B, 7C, and 7D illustrate steps for producing an SOI substrate.
Figs. 8A, 8B, 8C, and 8D illustrate steps for producing an SOI substrate.
Fig. 9 illustrates a separation step in Embodiment 2 in which a laser beam is projected to a porous Si layer.
Fig. 10 illustrates a separation step in Embodiment 3 in which a laser beam is projected to a porous Si layer.
Fig. 11 illustrates a separation step in Embodiment 4 in which a laser beam is projected to a porous Si layer.
Figs. 12A, 12B and 12C illustrate processes for producing a monocrystalline Si solar cell.
Fig. 13 illustrates a separation step in Embodiment 5 in which a laser beam is projected to a porous Si layer.
Fig. 14 illustrates substrates after the separation.
Figs. 15A is a perspective view of a monocrystalline Si solar cell, and Fig. 15B is a sectional view thereof.
Figs. 16A, 16B, 16C, 16D and 16E illustrate steps of producing an SOI substrate.
Figs. 17A, 17B, 17C and 17D illustrate steps of producing an SOI substrate.
Fig. 18 illustrates a conventional process for producing a solar cell.
DESCRIPTION OF THE PREFERRED EMBODIMENTS
The present invention is described by reference to Embodiments 1 to 8. Embodiments 1 to 4 describe production of an SOI substrate. Embodiments 5 to 7 describe production of photoelectric transducing device such as solar cells and area sensors. Embodiment 8 describes a method in which the layer for the separation is formed by ion implantation. The present invention covers not only the described Embodiments but also combination of the Embodiments.
In Embodiment 1 of producing an SOI substrate, a laser beam is employed for separation of the wafer to be recycled and the SOI substrate at the porous layer.
The laser beam is projected to the side face (edge face) in parallel with the plate-shaped substrates at a laser intensity adjusted to reach the substrate center.
The laser beam is projected to relatively fragile layer such as larger porosity layer or a defective layer having micro-bubbles and absorbed thereby. The porous fragile layer having absorbed the laser beam becomes more fragile, whereby the less porous layer on the porous fragile layer and nonporous layer are separated at the fragile layer. The method of laser beam projection is described in detail in the following Embodiments.
Fig. 1 illustrates the separation process of this embodiment. In Fig. 1, the same reference numerals are used as in Figs. 16A to 16E and Figs. 17A to 17D. The numeral 10 indicates a lens, 11 an optical microscope, 12 a vacuum chuck, and 13 a laser beam. LS indicates a laser source, and ATL indicates an article constituted of layers 2, 3, 4, 6, and 7 before the separation. A
laser beam is projected to the side wall of porous layer 3 from laser source LS. Laser source LS is an excimer laser of high output employing XeCl, KrF, ArF, or the like. The output capacity is preferably in the range from 300 mJ/cm2 to 1 J/cm2, more preferably about 500 mJ/cm2. The excimer laser emits W light, so that lens 10 is made of quartz or fluorite capable of transmitting the UV light. With this optical system, the laser beam is converged to have a projection area width to 0.1 ~um. Optical microscope 11 is employed, as necessary, to confirm the precise projection of laser beam 13 to porous layer 3 of 0.1 to 30 ~m thick. Since porous layer 3 is fragile and can readily be broken for separation in comparison with nonporous layer 2 and epitaxial layer 4 as a less porous layer, laser beam 13 need not be strictly projected only to porous layer 3.
The laser source LS for emitting laser beam 13 is preferably an excimer laser apparatus of high power, but may be an Ar laser, or a YAG laser. For promoting the layer separation, a liquid such as water, methyl alcohol, ethyl alcohol, and isopropyl alcohol may be incorporated into porous layer 3 by injection or adsorption. The liquid, which has a larger thermal expansion coefficient than the solid like Si, promotes the layer separation by expansion.
Vacuum chuck 12 as the substrate holder has a cavity for holding a gas, and holds substrate ATL, before the separation, by contact with the outside face of nonporous layer 2 or monocrystalline layer 6 by evacuation of the gas. In this Embodiment, a pair of vacuum chucks 12 can rotate around the axis at the center of the substrate to project laser beam 13 to the entire side wall of the porous layer 3. Vacuum chucks 12 may be employed only for fixing and rotating the substrate, but may also be employed for applying slight pulling force to the substrate to promote the layer separation.
The laser beam penetrates the side wall of porous layer 3 to the proximity to the center of substrate ATL. Porous layer 3 becomes more fragile by absorption of the laser berm to cause separation of substrate ATL
without break of the nonporous portion.
By the separation, substrate 4,7,6 for the SOI
substrate and substrate 2 to be recycled are separated from each other at porous layer 3. In Fig. 2, portions 3' of porous layers remains on the surfaces (separation plane) of the respective substrates. By reducing sufficiently the thickness of porous layer 3 formed by the anodization, the remaining portions can be made absent practically from one or both of the substrates.
A process for thin film formation by the wafer separation as shown in Fig. 1 is described below.
Firstly, the substrate for the bonding is prepared. Fig. 3 is a sectional view of an apparatus for anodizing an Si wafer. The numeral 1 indicates an Si wafer, 27 an etching solution of hydrofluoric acid type contained in vessel RV, 28 a positive metal electrode, and 29 a negative metal electrode. Si wafer 1 to be anodized is preferably of a p-type, but may be of an n-type of low resistance. An n-type wafer having holes formed by projection of a light beam can also be readily made porous. In Fig. 3, a voltage is applied between positive electrode 28 at the left side and negative electrode 29 at the right side, and Si wafer 1 is placed parallel to the both electrodes to apply an electric field perpendicular to the face of Si wafer in the etching solution. Thereby wafer 1 is made porous from the side of negative electrode 29. Concentrated hydrofluoric acid (49~ HF) is employed as etching solution 27 of the hydrofluoric acid type. Since gas bubbles are generated from Si wafer l, an alcohol is preferably added as a surfactant into etching solution 27 to remove the bubbles. The alcohol includes methanol, ethanol, propanol, and isopropanol. Instead of surfactant addition, the solution may be stirred by a stirrer during the anodization.
The thickness of the porous layer is preferably in the range from 0.1 to 30 ,um.
Negative electrode 29 is preferably made of a material resistant against the hydrofluoric acid, such as gold (Au) and platinum (Pt). Positive electrode 28 is also made preferably of a material resistant against the hydrofluoric acid, but may be made of any generally used metal material. The anodization is conducted at a maximum current density of several hundred mA/cm2 or less, but should be more than 0 mA/cm2. The current density is selected so that a high-quality epitaxial layer can be formed on the resulting porous Si layer and the separation can readily be caused at the porous layer. Specifically, at a larger current density in the anodization, the density of Si in the porous Si layer becomes lower, and the volume of the pores is larger, and the porosity (ratio of the pore volume to the total volume of the porous layer) thereof is larger. In spite of many pores formed in the interior of the Si layer, the resulting porous Si retains its monocrystallinity. Owing to the monocrystallinity of the porous Si layer, another monocrystalline Si layer can be grown epitaxially thereon.
For formation of an epitaxial Si layer having no lamination defect, the porosity of the porous Si layer is preferably smaller at the portion to be brought into contact with the epitaxial Si layer. On the other hand, for easy separation of the device substrate and the SOI substrate at the porous Si layer, the porosity of the porous Si layer is preferably larger.
Therefore, ideally, the porosity of the porous Si layer is smaller at the outermost surface, and is larger at the side near to the nonporous Si layer. Fig. 4 is a sectional view illustrating the ideal state of the porous Si layer. Porous Si layer 3a, the surface side portion of porous Si layer 3, is formed with a smaller porosity, and porous Si layer 3b, the nonporous Si layer side portion of porous Si layer 3, is formed with a larger porosity. For obtaining this structure, the initial stage of the anodization is conducted at a lower current density to prepare portion 3a, and the later stage of the anodization is conducted at a higher current density to prepare portion 3b. With this structure, the separation of the substrate occurs only at layer 3b, and an epitaxial Si layer can be formed without lamination defect on porous Si layer 3a. The epitaxial Si layer is formed preferably by a growth process such as molecular beam epitaxial growth, plasma CVD, low pressure CVD, photo-assisted CVD, bias sputtering, and liquid phase growth. Particularly, low temperature growth is preferred.
As described above, Si wafer 1 shown in Fig. 5A is made porous at the surface as shown in Fig. 5B.
Thereby Si wafer 1 comes to have the structure constituted of nonporous Si layer 2 and porous Si layer 3 laminated thereon.
Subsequently, nonporous epitaxial Si layer 4 is formed on porous Si layer 3 as shown in Fig. 5C. If necessary, the surface of epitaxial Si layer 4 is thermally oxidized to form Si oxide layer 8 of thickness between 0.05 ~m to 2 ~m as shown in Fig. 5D.
As described above, substrate PW called a prime wafer, a bond wafer, or a device substrate is treated before the bonding.
On the other hand, substrate HW called a handle wafer, a base wafer, or a supporting substrate is treated as described below.
An Si wafer is provided, and if necessary, the surface thereof is thermally oxidized to form an Si oxide film of thickness ranging from 0.05 to 3 ~m.
The process of bonding and separation of the substrates is explained below by reference to Figs. 6A
to 6D.
The surface of Si oxide layer 8 on epitaxial Si layer 4 of substrate PW is confronted with the surface of Si oxide layer 7 of substrate HW, and both faces are bonded at room temperature as shown in Fig. 6A. Then the bonding between Si oxide layer 8 and Si oxide layer 7 is strengthened by anode bonding, pressing, or heat treating, or combination thereof to form an article ATL
comprising the bonded substrates as shown in Fig. 6B.
Bonded article ATL having the structure shown in Fig. 6B is placed between a pair of vacuum chucks 12 of the device shown in Fig. 1. With rotation of article ATL, an excimer laser beam is projected to and focused on the portion of porous Si layer 3 of the side face of article ATL. The projected excimer laser beam is absorbed by the entire of the porous Si layer. In such a manner, nonporous Si layer 2 of substrate PW side is separated from substrate HW as shown in Fig. 6C. By the separation, epitaxial Si layer 4 is transferred onto the surface of substrate HW. Porous Si layer 3 having been broken by absorption of the laser beam may remain on one or both of nonporous Si layer 2 and epitaxial Si layer 4. Fig. 6C shows porous Si layer 3 remaining only on epitaxial Si layer 4.
Porous Si layer 3, when it remains on the side of substrate HW, is removed selectively by selective etching. In the selective etching, the porous Si layer is etched more than the nonporous Si layer by nonelectrolytic wet chemical etching by use of an etching solution such as hydrofluoric acid, a mixture of hydrofluoric acid with an alcohol, and a mixture of hydrofluoric acid with aqueous hydrogen peroxide. In particular, by use of a mixture of hydrofluoric acid with hydrogen peroxide, the selective etching ratio of the porous Si layer to the nonporous Si layer is as high as about 105. Thus, epitaxial Si layer 4 remains in a uniform thickness on the surface of substrate HW.
Thereby an SOI substrate having extremely uniform semiconductor layer 4 on the insulation layer as shown in Fig. 6D.
Separated nonporous layer 2 is again used as the prime wafer for production of another SOI substrate.
In the process for producing the SOI substrate in this Embodiment, the supporting substrate may be a complete insulating substrate such as a glass substrate and a quartz substrate. Figs. 7A to 7D illustrate the steps of producing an SOI substrate by use of quartz substrate as the supporting substrate. The device substrate PW at the upper side in Fig. 7A is prepared in the same manner as described by reference to Fig. 5A
to 5D. Quartz substrate 9 as supporting substrate HW
is confronted with an Si oxide layer 8 and are bonded tightly by anode bonding, pressing, or thermal treatment, or combination thereof as shown in Fig. 7B.
Then, the two substrate is separated by projection of a laser beam in the same manner as described before.
Epitaxial Si layer 4 and porous Si layer 3 are transferred onto quartz substrate 9 as shown in Fig.
7C. The remaining porous Si layer 3 is selectively removed in the aforementioned manner. Thus an SOI
substrate is obtained which is constituted of quartz base plate 9 and nonporous monocrystalline thin Si film CA 02233028 l998-03-23 4 formed thereon as shown in Fig. 7D.
In another process of preparing the SOI substrate of this Embodiment, an Si wafer is used as the supporting substrate, and an insulating layer of an SOI
structure is formed by forming an Si oxide layer on the epitaxial Si layer on the device substrate side without forming the Si oxide layer on the Si wafer side. Figs.
8A to 8D shows this process. The upper device substrate in Fig. 8A is prepared in the same manner as described by reference to Fig. 5. The surface of monocrystalline Si layer 5 of an Si wafer is counterposed with the surface of Si oxide layer 8, and bonded thereto. The bonding can be strengthened by anode bonding, pressing, or heating, or combination thereof. Thus article ATL is obtained as shown in Fig.
8B. Article ATL is separated at the porous Si layer to transfer epitaxial Si layer 4 of nonporous monocrystalline Si onto nonporous Si layer 5 as supporting substrate HW by means of the apparatus shown in Fig. 1. If porous Si layer 3 remains on epitaxial Si layer 4 of supporting substrate HW as shown in Fig.
8C, it is selectively removed by the aforementioned method. Thus an SOI substrate is obtained as shown in Fig. 8D.
Embodiment 2 An SOI substrate is produced in this Embodiment by utilizing an excimer laser beam for separating, at the porous Si layer, the Si wafer to be recycled and the substrate to be worked into an SOI substrate. The excimer laser beam is focused on one point and is allowed to scan with the substrate plate fixed.
Fig. 9 illustrates the separation step. The laser beam is focused on the side face of article ATL with lens 10, and is allowed to scan along the circumference by aid of guide 14. The same reference numbers are used to indicate the same articles as in Fig. 1. In this Embodiment, monocrystalline Si layer 6 as nonporous layer and nonporous Si layer 2 constituting article ATL are fixed from the outside by chucks 12.
The laser beam 13 from an excimer laser apparatus is focused and projected onto one point on the side wall of porous Si layer 3 through lens 10. Lens 10 is allowed to move together with laser beam 13 for the scanning to separate the SOI substrate composed of layers 4, 7, 6 from substrate 2 at porous Si layer 3 to recycle substrate 2 to the production steps. The less porous layer 4 on the layers 6, 7 is obtained. The other steps and the materials are the same as in Embodiment 1.
Embodiment 3 An SOI substrate is produced in this Embodiment by utilizing excimer laser for separating the Si wafer to be recycled and the SOI substrate at the porous Si layer. The excimer laser beam is focused linearly by a cylindrical lens and is projected along the side face of the porous Si layer.
Fig. 10 illustrates the separation step. The numeral 15 indicates a cylindrical lens. The same reference numbers are used to indicate the same articles as in Fig. 1. The laser beam is focused linearly in a vertical direction for efficient projection onto the side face of porous Si layer 3 of an extremely small thickness of O.l to 30 ~m. In place of cylindrical lens 15, a toric lens may be used to project linearly focused laser beam to the curved side wall of porous Si layer 3. The other steps are the same as in Embodiment 1.
Embodiment 4 An SOI substrate is produced in this Embodiment by utilizing excimer laser for separating, at the porous Si layer, the Si wafer to be recycled and the SOI
substrate. The excimer laser beams are focused linearly by cylindrical lenses and are projected along the end face of the porous Si layer. In the laser beam projection, as shown in Fig. 11, the laser light is separated into four beams, and laser beams 13 are respectively focused linearly and projected with four cylindrical lenses 15 from four directions along the end face of porous Si layer 3. In this Embodiment, monocrystalline Si layer 6 and nonporous Si layer 2 are fixed from the outside by chucks 12. The other steps are the same as in Embodiment 1.
Embodiment 5 A solar cell is produced in this Embodiment.
Figs. 12A to 12C illustrate the steps of forming a photoelectric transducing layer for transducing light energy to electric energy. An p-type Si wafer 1 is provided as shown in Fig. 12A. The surface of Si wafer 1 is made porous by anodization as explained before by reference to Fig. 3 to prepare a substrate constituted of nonporous Si layer 2 of wafer 1 and porous Si layer 3 formed thereon as shown in Fig. 12B. On porous Si layer 3, an epitaxial Si layer to serve as photoelectric transducer 18 is formed as shown in Fig.
12C by molecular beam epitaxial growth, plasma CVD, low pressure CVD, photo-assisted CVD, bias sputtering, liquid crystal growth method, or a like method to prepare a substrate PW.
The epitaxial Si layer is allowed to grow with addition of a dopant for use as a photoelectric transducing layer. Thereby, the epitaxial layer has PN
junction caused by lamination of an n+ layer, a p~
layer, and a p+ layer formed in this order on porous Si layer 3. The surface of the p+ layer of photoelectric transducing layer 18 grown epitaxially is bonded and connected to backside metal electrode 16 formed preliminarily on the surface of plastic substrate 17.
Then vacuum chuck 12 is brought into close contact with the outside of nonporous Si layer 2. A laser beam 13 from an excimer laser apparatus is focused and projected through lens 10 onto porous Si layer 3.
Although the laser light is focused onto one point in Fig. 13, the laser beam may be projected in any way as described in Embodiments 1 to 4. In such a manner, substrate HW to be used as a solar cell is separated at porous Si layer 3 from substrate PW to be recycled to production process as shown in Fig. 14.
A meshed surface metal electrode 19 is formed on the surface of photoelectric transducing layer 18 as shown in Fig. 15A. Wiring 24 is connected to surface metal electrode 19 and backside metal electrode 16.
Protection layer 20 is formed on the surface metal electrode 19. Fig. 15B is a sectional view taken at 15B-15B in Fig. 15A. Photoelectric transducing layer 18 is constituted of the layers of n+ layer 23 in contact with surface metal electrode 19, p layer 22, and p+ layer 21 in contact with backside metal electrode 16, arranged in this order from the upper side. In Figs. 15A and 15B, surface metal electrode l9 is shown in a shape of a mesh to transmit light. However, it may be replaced by a transparent electrode made of a material like IT0. Backside metal electrode 16 serves also a back reflector for returning unabsorbed transmitted light to photoelectric transducing layer 18, so that it is preferably made of a metallic material having high reflectivity.
CA 02233028 l998-03-23 According to this Embodiment, many solar cells of a monocrystalline thin film can be produced from one Si wafer. Therefore, this Embodiment is advantageous in transducing efficiency, cell life, and production cost.
Further, the substrate is separated by projecting a laser beam to the porous Si layer to cause thermal expansion and distortion of the crystal without application of strong pulling force without necessity of strong bonding between the substrate and the jig or the like. From this point also, the process of this Embodiment is advantageous in production cost.
Embodiment 6 A solar cell is produced in this Embodiment also.
In the above Embodiment 5, photoelectric transducer 18 iS constituted of an epitaxial Si layer formed on porous Si layer 3, whereas in this Embodiment, porous Si layer of a small porosity per se is utilized, as it is, as photoelectric transducing layer 18. In Embodiment 1, it is described that the porosity of the porous Si layer can be varied by changing the current density in anodization. Specifically, in anodization explained by reference to Fig. 3, the higher density of the electric current flowing from electrode 28 to electrode 29 makes larger the porosity of porous Si layer formed on Si wafer 1, while the lower density of the current makes smaller the porosity. By this phenomenon, the surface of p~ type Si wafer 1 is made porous by forming a porous Si layer of a smaller porosity by controlling the current density lower, and porous Si layer 3b of larger porosity is formed under it on nonporous layer 2. To the outermost layer of porous Si layer 3a, donor ions such as P and As are implanted to make the outermost layer on n-type, thereby forming photoelectric transducing layer having porous Si layer of small porosity having PN junction.
Thereafter, the porous Si layer of a smaller porosity as the photoelectric transducer is bonded to backside metal electrode 16 as shown in Fig. 13. The other steps are conducted in the same manner as in Embodiment 5.
According to this Embodiment, many solar cells of a monocrystalline thin film can be produced from one Si wafer. Therefore, this Embodiment is advantageous in transducing efficiency, cell life, and production cost.
Further, epitaxial growth is not conducted in the process of this Embodiment, the production cost is lower than that of Embodiment 5. The photoelectric transducing layer 18 is composed of a porous Si layer of smaller porosity with the monocrystallinity maintained, and light is scattered appropriately by the pores to result in high transducing efficiency.
Embodiment 7 An area sensor is produced. In this Embodiment, a photoelectric transducing layer of monocrystalline thin film is formed from an Si wafer in the same manner as in Embodiment 5 or 6. On this photoelectric transducing layer, optical sensors are arranged two-dimensionally, and matrix wiring is provided. The matrix wiring is formed, for example, by providing a row wiring in place of surface metal electrode 19 in Figs. 15A and 15B and providing a line wiring in place of backside metal electrode 16 in Figs. 15A and 15B.
This Embodiment is advantageous in transducing efficiency, cell life, production cost, area enlargement, and so forth, since many area sensors of a monocrystalline thin film can be produced from one Si wafer.
Embodiment 8 An Si wafer is prepared as one substrate. Over the entire face of the Si wafer, hydrogen ions or rare gas ions are implanted in a prescribed depth by mean of an ion implanter to form a defective layer of microbubbles in the interior of the Si wafer.
Separately, another Si wafer is prepared as the supporting substrate. This supporting substrate is oxidized at the surface, and is bonded to the surface of the above Si wafer having a microbubble-defective layer.
To the bonded wafer article, an excimer laser beam is projected at around the microbubble-defective layer of the side face of the article in a manner shown in Fig. 1, 9, 11, or 13. Thereby, the defective layer is made more fragile by absorption of the excimer laser beam. Then the two wafers are separated.
In such a manner, the monocrystalline Si layer on the defective layer of the one substrate Si layer is transferred onto the silicon oxide film on the other substrate. The microbubble formation by ion implantation is described in detail in U.S. patent No.
5,374,564.
The above description is made regarding the case of Si wafer, but the present invention can be applied to other semiconductors other than Si, such as SiGe, Ge, SiC, GaAs, and InP.
According to the present invention, many monocrystalline thin Si film can readily be produced by projecting a laser beam from the side face of a substrate into the center portion of the porous layer to cause absorption of laser beam by the porous layer.
Since the laser beam does not cause impurity contamination, the resulting thin Si film has high quality, and the resulting SOI substrate also has high quality. In production of SOI substrates, the material is used with less waste, resulting in low production cost and resource saving. The produced photoelectric transducing apparatus also has high quality. In production of photoelectric transducing apparatus also, the material is used with less waste, resulting in low production cost and resource saving.
The above description is made regarding the case of Si wafer, but the present invention can be applied to other semiconductors other than Si, such as SiGe, Ge, SiC, GaAs, and InP.
According to the present invention, many monocrystalline thin Si film can readily be produced by projecting a laser beam from the side face of a substrate into the center portion of the porous layer to cause absorption of laser beam by the porous layer.
Since the laser beam does not cause impurity contamination, the resulting thin Si film has high quality, and the resulting SOI substrate also has high quality. In production of SOI substrates, the material is used with less waste, resulting in low production cost and resource saving. The produced photoelectric transducing apparatus also has high quality. In production of photoelectric transducing apparatus also, the material is used with less waste, resulting in low production cost and resource saving.
Claims (48)
1. A process for forming a thin film comprising the steps of:
providing a substrate having:
a nonporous layer;
a porous first layer formed on the nonporous layer;
and a second layer which is less porous than the porous first layer; and separating the substrate by projecting a laser beam through the side face of the substrate into the center of the substrate.
providing a substrate having:
a nonporous layer;
a porous first layer formed on the nonporous layer;
and a second layer which is less porous than the porous first layer; and separating the substrate by projecting a laser beam through the side face of the substrate into the center of the substrate.
2. The process for forming a thin film according to claim 1, wherein the separating step further comprises a step of focussing the laser beam on the side face of the porous first layer to swell the porous first layer.
3. The process for forming a thin film according to claim 1, wherein the providing step further comprises a step of forming the porous first layer in the nonporous layer by anodizing a Si wafer.
4. The process for forming a thin film according to claim 1, wherein the separating step further comprises a step of projecting the laser beam onto plural sites of the porous first layer.
5. The process for forming a thin film according to claim 1, wherein the separating step further comprises the steps of:
bringing the face of the nonporous layer reverse to the porous first layer into close contact with a vacuum chuck; and applying a slight pulling force by the vacuum chuck to the substrate.
bringing the face of the nonporous layer reverse to the porous first layer into close contact with a vacuum chuck; and applying a slight pulling force by the vacuum chuck to the substrate.
6. The process for forming a thin film according to claim 1, wherein the laser beam is an excimer laser beam.
7. The process for forming a thin film according to claim 1, wherein the separating step further comprises the steps of:
converging the laser beam linearly by a cylindrical lens; and projecting the linearly converged laser beam along the porous first layer.
converging the laser beam linearly by a cylindrical lens; and projecting the linearly converged laser beam along the porous first layer.
8. The process for forming a thin film according to claim 3, wherein the providing step further comprises a step of forming the second layer which is a nonporous epitaxial layer by epitaxial growth on the porous first layer.
9. The process for forming a thin film according to claim 8, the process further comprises the steps of:
bonding the nonporous epitaxial layer to a supporting substrate with interposition of an insulating layer;
separating the nonporous epitaxial layer at the porous first layer;
removing the porous first layer remaining on the nonporous epitaxial layer; and employing the nonporous epitaxial layer and the insulating layer respectively as a semiconductor layer and an underlying insulating layer of an SOI substrate.
bonding the nonporous epitaxial layer to a supporting substrate with interposition of an insulating layer;
separating the nonporous epitaxial layer at the porous first layer;
removing the porous first layer remaining on the nonporous epitaxial layer; and employing the nonporous epitaxial layer and the insulating layer respectively as a semiconductor layer and an underlying insulating layer of an SOI substrate.
10. The process for forming a thin film according to claim 9, the process further comprising the steps of:
providing a Si wafer having an oxidized surface as the supporting substrate; and employing the oxidized surface as the insulating layer.
providing a Si wafer having an oxidized surface as the supporting substrate; and employing the oxidized surface as the insulating layer.
11. The process for forming a thin film according to claim 8, the process further comprising the steps of:
forming an insulating layer on the nonporous epitaxial layer;
bonding the nonporous epitaxial layer to a supporting substrate;
separating the nonporous epitaxial layer from the porous first layer;
removing the porous first layer remaining on the nonporous epitaxial layer; and employing the nonporous epitaxial layer and the insulating layer respectively as a semiconductor layer and an underlying insulating layer of an SOI substrate.
forming an insulating layer on the nonporous epitaxial layer;
bonding the nonporous epitaxial layer to a supporting substrate;
separating the nonporous epitaxial layer from the porous first layer;
removing the porous first layer remaining on the nonporous epitaxial layer; and employing the nonporous epitaxial layer and the insulating layer respectively as a semiconductor layer and an underlying insulating layer of an SOI substrate.
12. The process for forming a thin film according to claim 11, wherein the supporting substrate is a quartz substrate.
13. The process for forming a thin film according to claim 11, the process further comprising a step of preparing the supporting substrate by oxidizing a surface of a Si wafer.
14. The process for forming a thin film according to claim 3, wherein the providing step further comprises a step of forming the second layer by anodizing the Si wafer at a current density lower than that used in forming the porous first layer by anodizing.
15. The process for forming a thin film according to claim 8 or 14, the process further comprising the steps of:
bonding the second layer to a supporting substrate;
separating the second layer at the porous first layer and employing the second layer as a photoelectric transducing layer of a photoelectric transducing apparatus.
bonding the second layer to a supporting substrate;
separating the second layer at the porous first layer and employing the second layer as a photoelectric transducing layer of a photoelectric transducing apparatus.
16. The process for forming a thin film according to claim 1, wherein the providing step further comprises a step of providing a substrate having:
the nonporous layer, the porous first layer, and the second layer, which are respectively composed of silicon.
the nonporous layer, the porous first layer, and the second layer, which are respectively composed of silicon.
17. The process for forming a thin film according to claim 16, wherein the separating step further comprises a step of focussing the laser beam on the side face of the porous first layer to swell the porous first layer.
18. The process for forming a thin film according to claim 16, wherein the providing step further comprises a step of forming the porous first layer on the nonporous layer by anodizing a Si wafer.
19. The process for forming a thin film according to claim 16, wherein the separating step further comprises a step of projecting the laser beam onto plural sites of the porous first layer.
20. The process for forming a thin film according to claim 16, wherein the separating step further comprises the steps of:
bringing the face of the nonporous layer reverse to the porous first layer into close contact with a vacuum chuck; and applying a slight pulling force by the vacuum chuck to the substrate.
bringing the face of the nonporous layer reverse to the porous first layer into close contact with a vacuum chuck; and applying a slight pulling force by the vacuum chuck to the substrate.
21. The process for forming a thin film according to claim 16, wherein the laser beam is an excimer laser beam.
22. The process for forming a thin film according to claim 16, wherein the separating step further comprises the steps of:
converging the laser beam linearly by a cylindrical lens; and protecting the linearly converged laser beam along the porous first layer.
converging the laser beam linearly by a cylindrical lens; and protecting the linearly converged laser beam along the porous first layer.
23. The process for forming a thin film according to claim 18, wherein the providing step further comprises a step of forming the second layer which is a nonporous epitaxial layer by epitaxial growth on the porous first layer.
24. The process for forming a thin film according to claim 23, the process further comprising the steps of:
bonding the nonporous epitaxial layer to a supporting substrate having an insulating layer at least on the surface thereof;
separating the nonporous epitaxial layer at the porous first layer;
removing the porous first layer remaining on the nonporous epitaxial layer; and employing the nonporous epitaxial layer and the insulating layer respectively as a semiconductor layer and an underlying insulating layer of an SOI substrate.
bonding the nonporous epitaxial layer to a supporting substrate having an insulating layer at least on the surface thereof;
separating the nonporous epitaxial layer at the porous first layer;
removing the porous first layer remaining on the nonporous epitaxial layer; and employing the nonporous epitaxial layer and the insulating layer respectively as a semiconductor layer and an underlying insulating layer of an SOI substrate.
25. The process for forming a thin film according to claim 24, the process further comprising the steps of:
providing a Si wafer having an oxidized surface as the supporting substrate having an insulating layer at least on the surface thereof; and employing the oxidized surface as the insulating layer.
providing a Si wafer having an oxidized surface as the supporting substrate having an insulating layer at least on the surface thereof; and employing the oxidized surface as the insulating layer.
26. The process for forming a thin film according to claim 23, the process further comprising the steps of:
forming an insulating layer on the nonporous epitaxial layer;
bonding the nonporous epitaxial layer to a supporting substrate;
separating the nonporous epitaxial layer from the porous first layer;
removing the porous first layer remaining on the nonporous epitaxial layer; and employing the nonporous epitaxial layer and the insulating layer respectively as a semiconductor layer and an underlying insulating layer of an SOI substrate.
forming an insulating layer on the nonporous epitaxial layer;
bonding the nonporous epitaxial layer to a supporting substrate;
separating the nonporous epitaxial layer from the porous first layer;
removing the porous first layer remaining on the nonporous epitaxial layer; and employing the nonporous epitaxial layer and the insulating layer respectively as a semiconductor layer and an underlying insulating layer of an SOI substrate.
27. The process for forming a thin film according to claim 26, wherein the supporting substrate is a quartz substrate.
28. The process for forming a thin film according to claim 26, the process further comprising a step of preparing the supporting substrate by oxidizing a surface of a Si wafer.
29. The process for forming a thin film according to claim 18, wherein the providing step further comprises a step of forming the second layer by anodizing the Si wafer at a current density lower than that used in forming the porous first layer by anodizing.
30. The process for forming a thin film according to claim 18 or 29, the process further comprising the steps of:
bonding the second layer to a supporting substrate;
separating the second layer from the porous first layer; and employing the second layer as a photoelectric transducing layer of a photoelectric transducing apparatus.
bonding the second layer to a supporting substrate;
separating the second layer from the porous first layer; and employing the second layer as a photoelectric transducing layer of a photoelectric transducing apparatus.
31. The process for forming a thin film according to claim 1, wherein the providing step further comprises a step of forming the porous first layer by injecting hydrogen ions or ions of rare gas into the substrate.
32. A process for forming a thin film comprising the steps of:
forming a substrate having:
a nonporous layer;
a porous first layer formed on the nonporous layer;
and a second layer which is less porous than the porous first layer; and separating the second layer from the nonporous layer;
wherein the separating step comprises a step of projecting a laser beam onto the side face of the substrate toward the center of the substrate.
forming a substrate having:
a nonporous layer;
a porous first layer formed on the nonporous layer;
and a second layer which is less porous than the porous first layer; and separating the second layer from the nonporous layer;
wherein the separating step comprises a step of projecting a laser beam onto the side face of the substrate toward the center of the substrate.
33. The process for forming a thin film according to claim 32, wherein the separating step further comprises a step of focussing the laser beam on the side face of the porous first layer to swell the porous first layer.
34. The process for forming a thin film according to claim 32, wherein the forming step further comprises a step of forming the porous first layer on the nonporous layer by anodizing a Si wafer.
35. The process for forming a thin film according to claim 32, wherein the separating step further comprises a step of projecting the laser beam onto plural sites of the porous first layer.
36. The process for forming a thin film according to claim 32, wherein the separating step further comprises the steps of:
bringing the face of the nonporous layer reverse to the porous first layer into close contact with a vacuum chuck; and applying a slight pulling force by the vacuum chuck to the substrate.
bringing the face of the nonporous layer reverse to the porous first layer into close contact with a vacuum chuck; and applying a slight pulling force by the vacuum chuck to the substrate.
37. The process for forming a thin film according to claim 32, wherein the laser beam is an excimer laser beam.
38. The process for forming a thin film according to claim 32, wherein the separating step further comprises the steps of:
converging the laser beam linearly by a cylindrical lens; and projecting the linearly converged laser beam along the porous first layer.
converging the laser beam linearly by a cylindrical lens; and projecting the linearly converged laser beam along the porous first layer.
39. The process for forming a thin film according to claim 32, wherein the second layer is a nonporous layer.
40. The process for forming a thin film according to claim 32, the process further comprising the steps of:
bonding the second layer to a supporting substrate with interposition of an insulating layer;
separating the second layer from the porous first layer;
removing the porous first layer remaining on the second layer; and employing the second layer and the insulating layer respectively as a semiconductor layer and an underlying insulating layer of an SOI substrate.
bonding the second layer to a supporting substrate with interposition of an insulating layer;
separating the second layer from the porous first layer;
removing the porous first layer remaining on the second layer; and employing the second layer and the insulating layer respectively as a semiconductor layer and an underlying insulating layer of an SOI substrate.
41. The process for forming a thin film according to claim 32, the process further comprising the steps of:
forming an insulating layer on the second layer;
bonding the second layer to a supporting substrate;
separating the second layer from the porous first layer;
removing the porous first layer remaining on the second layer; and employing the second layer and the insulating layer respectively as a semiconductor layer and an underlying insulating layer of an SOI substrate.
forming an insulating layer on the second layer;
bonding the second layer to a supporting substrate;
separating the second layer from the porous first layer;
removing the porous first layer remaining on the second layer; and employing the second layer and the insulating layer respectively as a semiconductor layer and an underlying insulating layer of an SOI substrate.
42. The process for forming a thin film according to claim 40 or 41, wherein the supporting substrate is a quartz substrate.
43. The process for forming a thin film according to claim 40 or 41, the process further comprising a step preparing the supporting substrate by oxidizing the surface of a Si wafer.
44. The process for forming a thin film according to claim 32, wherein the forming step further comprises a step of forming the second layer by anodizing the Si wafer at a current density lower than that used in forming the porous first layer boy anodizing.
45. The process for forming a thin film according to claim 40 or 41, the process further comprising the steps of:
bonding the second layer to a supporting substrate;
separating the second layer from the porous first layer; and employing the second layer as a photoelectric transducing layer of a photoelectric transducing apparatus.
bonding the second layer to a supporting substrate;
separating the second layer from the porous first layer; and employing the second layer as a photoelectric transducing layer of a photoelectric transducing apparatus.
46. The process for forming a thin film according to claim 32, the process further comprising forming a substrate having:
the nonporous layer, the porous first layer, and the second layer, which are respectively composed of silicon.
the nonporous layer, the porous first layer, and the second layer, which are respectively composed of silicon.
47. A process for forming a semiconductor film comprising the steps of:
preparing a first substrate having a nonporous semiconductor layer on a porous layer;
forming a multilayered structure by bonding the first substrate and a second substrate so as to arrange the nonporous semiconductor layer inside the resulting structure; and irradiating the porous layer with a laser beam to expand the porous layer, whereby the multilayered structure is divided at the porous layer.
preparing a first substrate having a nonporous semiconductor layer on a porous layer;
forming a multilayered structure by bonding the first substrate and a second substrate so as to arrange the nonporous semiconductor layer inside the resulting structure; and irradiating the porous layer with a laser beam to expand the porous layer, whereby the multilayered structure is divided at the porous layer.
48. A process for forming a thin film comprising the steps of:
implanting hydrogen ions or rare gas ions into a substrate to form an ion-implanted layer;
forming a composite member by bonding the substrate and another substrate; and dividing the composite member at the ion-implanted layer, wherein the dividing step is comprised of a step of irradiating a side face of the ion-implanted layer with laser beam.
implanting hydrogen ions or rare gas ions into a substrate to form an ion-implanted layer;
forming a composite member by bonding the substrate and another substrate; and dividing the composite member at the ion-implanted layer, wherein the dividing step is comprised of a step of irradiating a side face of the ion-implanted layer with laser beam.