CA2269582C - Method for manufacturing electrode for battery - Google Patents

Method for manufacturing electrode for battery Download PDF

Info

Publication number
CA2269582C
CA2269582C CA002269582A CA2269582A CA2269582C CA 2269582 C CA2269582 C CA 2269582C CA 002269582 A CA002269582 A CA 002269582A CA 2269582 A CA2269582 A CA 2269582A CA 2269582 C CA2269582 C CA 2269582C
Authority
CA
Canada
Prior art keywords
electrode
active material
process according
water
current collector
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CA002269582A
Other languages
French (fr)
Other versions
CA2269582A1 (en
Inventor
Tadayoshi Iijima
Junichi Satoh
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
TDK Corp
Original Assignee
TDK Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by TDK Corp filed Critical TDK Corp
Publication of CA2269582A1 publication Critical patent/CA2269582A1/en
Application granted granted Critical
Publication of CA2269582C publication Critical patent/CA2269582C/en
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

A method for manufacturing electrode for battery by which electrode active material layers can be firmly provided on both surfaces of the conductive substance collector of an electrode. In the method, the electrode active material layers are formed on both surfaces of the conductive substance collector by successively applying electrode paint containing an electrode active material, binder, solvent, and acid to both surfaces of the conductive substance collector in such a way that, after the electrode paint is applied to one surface of the conductive substance collector, the applied paint is dried and the rear surface of the conductive substance collector is washed with water before applying the paint to the rear surface.

Description

SPECIFICATION
Title of the Invention:
Process for Producing Electrode for Battery Technical Field:
The present invention relates to a process for producing an electrode for a battery. In particular, the present invention relates to a process for producing an electrode for a battery, wherein an electrode active material layer can be firmly formed on both surfaces of a current collector for the electrode.
Background Art:
An electrode used in a lithium ion secondary battery is formed at present by applying a coating containing an electrode active material to both surfaces of a current collector of the electrode and drying it. In particular, a coating for the cathode contains a cathode active matex-ial and a binder, wherein the cathode active material is suitably dispersed therein in such a manner that it is not broken. The cathode coating is first applied to one surface of a metal foil as the electrode current collector and, after drying, it is also applied to the other surface thereof in the same manner as above, and then dried. Thus, the electrode active material layers are formed on both surfaces of the current collector for the electrode. Finally, the current collector for the electrode having the electrode active material layers formed on both surfaces thereof is cut into pieces, which is then used as the electrodes.
In the case where the coating film is formed on such a metal foil in the pxzor art, the adhesion between the metal foil and the electrode active material layer is insufficient to cause a problem in that the electrode active mateual layer is peeled off. For solving this problem, there have been proposed, for example, a method wherein a resin content of an electrode coating is increased and a method wherein an acid is added. Also, Japanese Patent Unexamined Published Application (hereinafter referred to as "J. P. KOKAI") No. Hei 2-discloses and specifically descizbes that the adhesion is improved by using an acid.
However, when such an acid is used, another problem is posed.
Specifically, when the electrode active material layer is formed on one surface (hereinafter referred to as "sux-face A") of the electrode current collector and then the same layer is formed on the other surface (hereinafter referred to as "suWace B") thereof, the adhesion of the current collector to surface B is much decreased as compared with the adhesion of that to surface A. Therefore, the electrode thus prepared has a problem of the peeling off of the electrode active material layer, particularly from the back sux~'ace (sunace B) of the electrode current collector. When such a peeling occurs, the capacity of the battery produced therefrom is lowered, or the electrode active material layer thus peeled off is interposed between a separator and, for example, a cathode electrode, and it breaks the separator to cause the short circuit of the cathode electrode and the anode electrode, disadvantageously. Such a product is, therefore, not practically usable as a battery element.
Therefore, the object of the present invention is to provide a process for producing an electrode for a battery by successively applying an electrode coating containing an electrode active material, a binder, a solvent and an acid to both surfaces of an electrode current collector to obtain an excellent adhesion between the electrode active material layer and the electrode current collector and not to cause the peeling-off of the electrode active material layers from both surfaces of the electrode current collector.
Disclosure of the Invention:
After intensive investigations made for the purpose of attaining the above-described object, the inventors have found that the above-descxzbed object can be effectively attained by a process for applying an electrode coating containing an electrode active matexzal, a binder, a solvent and an acid to both surfaces of an electrode current collector successively, wherein after applying the electrode coating to one surface of the electrode current collector and drying it, the other surface thereof is cleaned with water prior to the application of the electrode coating thereto. The present invention has been completed on the basis of this finding.
Mode for Carrying Out the Invention:
The detailed description will be made on the present invention.
The electrode coating used in the present invention contains an electrode active material, a binder, a solvent and an acid.
The electrode active materials usable herein are not particularly limited and those used hitherto as the electrode active materials are usable.
The matexzals used as the electrode active materials are various, and they are selected suitably depending on the use for the cathode or anode.
Carbonaceous matexzals are those usually used as the cathode active materials.
The carbonaceous materials are those used hitherto and not particularly limited.
They are, for example, amorphous carbon, acetylene black, petroleum coke, coal coke, artificial graphite, natural graphite, graphite carbon fibers and di~cultly graphitizable carbon'':
The anode active matexzals are those used hitherto. Various cathode active matexzals are usable without particular limitation. Various cathode active materials such as lithium cobaltate and lithium manganate are usable.
The electrode coating in the present invention contains usually 10 to 75 % by weight, based on the solid content of the electrode coating, and preferably 25 to 55 % by weight, of the electrode active material.
Any binder may be useable so long as it is conventionally used in this technical field, without particular limitation. The binder includes, for example, polyacrylonitx7le (PAN), polyethylene terephthalate, polyvinylidene fluoxzde (PVDF) and polyvinyl fluox-ide.
The binder is used in an amount of 1 to 40 parts by weight, preferably 2 to 25 parts by weight, and particularly 5 to 15 parts by weight, per 100 parts by weight of the electrode active material.
The solvent is not particularly limited and any of those used hitherto for the preparation of electrode coatings can be used. The solvent includes, for example, N-methylpyrrolidone (NMP), pyrrolidone, N-methylthiopyrrolidone, dimethylformamide (DMF), dimethylacetamide and hexamethylphosphamide.
They are used either alone or in the form of a mixture of them.
The solvent is used in such an amount that the solid content (non-volatile matter content) of the electrode coating is 10 to 80 % by weight, preferably 30 to GO % by weight and particularly preferably 35 to 45 % by weight.
The acid may be either an organic acid or an inorganic acid. As the acids, weak acids are preferred, and weak organic acids are particularly preferred. Preferred examples of the weak organic acids include oxalic acid, formic acid and malefic acid, and hydrates of these acids.
The acid is used in an amount of usually 0.001 to 5 parts by weight, preferably 0.01 to 3 parts by weight, per 100 parts by weight of the electrode active material.
When the electrode active material has a low electric conductivity, an electric conductor can be used, if necessary. As the electric conductors, the above-described carbonaceous materials are usable. In this case, the electxzc conductor is used in an amount of usually 1 to 25 parts by weight, preferably to 15 parts by weight and particularly preferably 5 to 10 parts by weight, per 100 parts by weight of the active matexzal.
Metal foils are preferably used as the electrode current collectors in the present invention. The metal matexzals for the electrode current collectors are not particularly limited, and vax-ious metal materials used hitherto for this purpose are usable. Such metal matexlals are, for example, copper, aluminum, stainless steel, nickel and iron.
The electrode coating used in the present invention is prepared by mixing the above-described ingredients together, and it is in the form of a slurry.
The electrode active matexzal must be suitably dispersed in the electrode coating to such an extent that it is not broken. The mixing and dispersion are conducted by means of a planetary mixer, ball mill or the like.
The electrode coating is applied to both surfaces of the electrode current collector and dried to form the electrode active material layers.
The electrode coating can be applied to the electrode current collector by a well-known method such as extrusion coating, gravure coating, reverse roll coating, dip coating, kiss coating, doctor coating, knife coating, curtain coating or screen printing.
The electrode coating thus applied is deed by a method which vanes depending on the kind of the solvent. For example, it can be dried with hot air of a temperature of 80 to 300°C.
In the present invention, the electrode active material layer is formed by applying the electrode coating to one surface of the electrode current collector and then dried under the above-descizbed conditions. Before the electrode coating is applied to the back sul.~face (the other surface, surface B) of the electrode current collector and dried, this surface to be coated must be cleaned with water. By this cleaning operation, the adhesion of the electrode active material layer to the back surface (suWace B) of the electrode current collector can be remarkably improved. Water used for the cleaning may be any of pure water (distilled water), ion-exchanged water, tap water, industrial water, well water, etc. Among them, pure water and ion-exchanged water having a low impunity content are preferred.
The electrode current collector can be cleaned by, for example, a method which comprises winding a cloth around a roller, impregnating the cloth with water and rotating it to bring it into contact with the current collector; a method which compx-ises winding a cloth around a rod, impregnating the cloth with water and reciprocating the rod widthwise in contact with the electrode current collector; or a method wherein water or water vapor is directly jetted to the electrode current collector. Other embodiments of the cleaning method are obvious to those skilled in the art. However, in immersion methods such as a dipping method, bad effects may be exerted, such as falling-off of the dried coating layer and, therefore, the layer must be carefully protected by, for example, masking.
For facilitating the drying operation after the cleaning, a mixture of water and an organic solvent may be used for the cleaning so far as the cleaning effect is not reduced. The organic solvents usable herein are those highly soluble in water such as methanol, ethanol and acetone.
The amount of the organic solvent is usually 0 to 60 % by weight, preferably 0 to 50 % by weight, based on the mixture.
The cleaning temperature is usually 5 to 50°C, preferably 10 to 40°C.
When this temperature is excessively low, the cleaning effect is reduced and, on the contrary, when it is excessively high, the foil is possibly denatured after the cleaning. When the temperature is kept in this range, water vapor can be used in place of water. The term "water" thus indicates herein not only water but also water vapor.
When the electrode coating is applied to the back surface of the electrode current collector, the surface is preferably dry. Therefore, the water is wiped off with a dry cloth or air is blown against the electrode current collector to dry it.
The thickness of the electrode having the electrode active matez-ial layers on both sides of the current collector can be controlled, if necessary, by roller pressing or the like.
The electrode matez~al thus obtained is then cut into pieces having predetermined width and length. Preferably, a part of the electrode current collector is left free from the electrode active material layer so as to provide electric contact with the outside. The material partially lacking the electrode active material layer can be formed by, for example, a method wherein an uncoated part is formed in the coating step or a method wherein the electrode active material layer is once formed and then a part thereof is removed.
The adhesion of the electrode active mateual layer, formed at first on one surface (surface A) of the electrode current collector, to this surface A
is higher than that of the electrode active material layer, formed on the other surface (surface B) thereof, to this sux~'ace B. The reasons why the adhesion to the surface B is inferior to that of the surface A have not been elucidated yet.
Although it has not been theoretically proved yet, the mechanism is supposed to be as follows: The acid contained in the coating is evaporated duxzng the drying and adheres to the surface B of the electrode current collector to form some compound with a metal of the electrode current collector. Although it was considered to solve such a problem of the poor adhesion, by differentiating the ratio of the electrode active material to the binder on the surface Afrom the ratio on the surface B, such a method causes a problem that the variety of the electrode coatings to be prepared is increased in number, and the steps in the production process are increased to make the process complicated. The inventors have found that the cleaning of the surface B with water after the coating of the sux~ace A and before the coating of the sux~'ace B of the current collector is very effective in efficiently improving the adhesion without necessitating such complicated steps.
Examples The following Examples will further illustrate the present invention, which by no means limit the scope of the present invention.
Example 1 1. Composition for Cathode Coating Material:
The coating composition for the cathode is as follows:
Graphite (cathode active material) 100 Acetylene black (electric conductor) 5 PVDF (binder) 10 NMP (solvent) 115 Oxalic acid dihydrate (acid) 1 The cathode coating was prepared as descxzbed below.
parts by weight of the binder were dissolved in 50 parts by weight of 10 the solvent to obtain 60 parts by weight of a lacquer. 10 parts by weight of the lacquer was added to 5 parts by weight of acetylene black and the resultant mixture was kneaded. The balance (50 parts by weight) of the lacquer and 65 parts by weight of the solvent were added to the kneaded mixture, and they were thoroughly mixed together. 100 parts by weight of the cathode active material was mixed therein and then 1 part by weight of oxalic acid dihydrate was added thereto to obtain the cathode coating.
2. Preparation of Cathode:
The cathode coating prepared as descxzbed above, was applied to a rolled copper foil having a thickness of 18 ,ccm by the nozzle coating method and then dried in a drying furnace at 110°C (coating of surface A). The back surface (surface B) of the foil having the coated surface A was wiped with a non-woven fabric impregnated with water and then dxzed. The foil was rolled and the back surface (sux-face B) was coated in the same manner as that for surface A.
The electrode current collector having the electrode active material layers on both surfaces was compression-molded with a roller press and cut into pieces to be used as cathodes.
The same procedure as that of Example 1 was repeated except that the pure water was replaced by tap water.
The same procedure as that of Example 1 was repeated except that the pure water was replaced by water/ethanol (weight ratio: 1/1).
The same procedure as that of Example 1 was repeated except that the pure water was replaced by water/ethanol (weight ratio: 1/3).
Comparative Example 1 The same procedure as that of Example 1 was repeated except that surface B was coated directly after the coating of surface A without any treatment, to obtain a sample of Comparative Example 1.
Comparative Exams The same procedure as that of Example 1 was repeated except that the pure water was replaced by ethanol, to obtain a sample of Comparative Example 2.
Corryarative Example 3 The same procedure as that of Example 1 was repeated except that the pure water was replaced by methyl ethyl ketone, to obtain a sample of Comparative Example 3.
3. Evaluation method:
l~Ptermination of Contact Anglg The contact angles at three points, close to one another, of the surface of each sample (copper foil having uncoated surface B) were determined with a contact angle meter (CA-D; a product of Kyowa Kaimen Kagaku K. K.) by using pure water as the liquid for the determination, and the average of them was taken as the contact angle of the sample. The larger the contact angle, the higher the hydrophobicity.
The electrode current collector was cut into pieces of 1 cm x 10 cm. A
pressure-sensitive adhesive double coated tape was applied to a supporting plate. An end part (3 cm) of the surface, to be tested, of the electrode current collector (surface with electrode active material layer) was stuck on the tape.
The electrode current collector was bent at such a curvature that it would not be broken off, while the other unstuck edge was pulled at a constant rate of 2 cm/sec with a tensile testing machine, to conduct the peeling test. The degree of exposure of the copper foil was determined according to the following cntena:
A: Less than 20 % of the copper foil was exposed.
B: 20 to 80 % of the copper foil was exposed.
C: More than 80 % of the copper foil was exposed.

The electrode active material layer remaining after the above-described tests was rubbed five times with a cotton swab impregnated with methyl ethyl ketone, and the solvent resistance thereof was evaluated according to the following criteria:
A: The electrode active material layer was not peeled off at all.
B: The electrode active material layer was slightly peeled off .
C: The electrode active mateizal layer was wholly peeled off after rubbing five times or less.
D: The electrode active matezzal layer was wholly peeled off after rubbing twice or less.
The test results are shown in following Table 1.

Table 1 Contact An 1e Peelin ResistanceSolvent Resistance Surface A 81.7 A A
(before coatin ) Example 1 75.0 A B

Example 2 70.3 A B

Example 3 62.3 A B

Example 4 45.5 A C

Comp. Ex. 1 41.1 B D

Comp. Ex. 2 40.0 A D

Comp. Ex. 3 23.2 B D

It is thus clear that the adhesion of the electrode active material layer to the back suWace is improved by cleaning the back surface with water after forming the electrode active material layer on the front suz~face of the electrode current collector and before the application of the electrode coating to the back surface. Thus, according to the process of the present invention, the crack formation in the electrode active matexzal layer and the peeling-off of the layer from the electrode current collector can be effectively prevented. Further, since the amount of the binder in the electrode coating is reduced, the relative amount of the electrode active material can be increased.

Claims (12)

What is claimed is:
1. A process for producing an electrode for a battery by successively applying an electrode coating containing an electrode active material, a binder, a solvent and an acid to both surfaces of an electrode current collector, wherein after applying the electrode coating to one surface of the electrode current collector and drying it, the other surface thereof is cleaned with water prior to the application of the electrode coating thereto.
2. The process according to claim 1, wherein the cleaning is conducted by using water or a mixture of water and an organic solvent.
3. The process according to claim 2, wherein the cleaning is conducted by using pure water.
4. The process according to claim 2, wherein the cleaning is conducted by using the a mixture of water and an organic solvent.
5. The process according to claim 4, wherein the organic solvent is methanol, ethanol or acetone.
6. The process according to claim 4, wherein the organic solvent is used in an amount of 0 to 60 % by weight based on the mixture of water and the organic solvent.
7. The process according to claim 1, wherein the electrode active material is a cathode active material or a anode active material.
8. The process according to claim 7, wherein the cathode active material is a carbonaceous material.
9. The process according to claim 8, wherein the carbonaceous material is selected from the group consisting of amorphous carbon, acetylene black, petroleum coke, coal coke, artificial graphite, natural graphite, graphite carbon fibers and difficultly graphitizable carbon.
10. The process according to claim 1, wherein the acid is selected from the group consisting of oxalic acid, formic acid, maleic acid, and hydrates of them.
11 The process according to claim 10, wherein the acid is used in an mount of 0.001 to 5 parts by weight per 100 parts by weight of the electrode active material.
12. The process according to claim 1, wherein the electrode current collector is made of copper.
CA002269582A 1996-10-23 1997-10-23 Method for manufacturing electrode for battery Expired - Fee Related CA2269582C (en)