CA2367350C - Highly conductive molding compounds and fuel cell bipolar plates comprising these compounds - Google Patents

Highly conductive molding compounds and fuel cell bipolar plates comprising these compounds Download PDF

Info

Publication number
CA2367350C
CA2367350C CA002367350A CA2367350A CA2367350C CA 2367350 C CA2367350 C CA 2367350C CA 002367350 A CA002367350 A CA 002367350A CA 2367350 A CA2367350 A CA 2367350A CA 2367350 C CA2367350 C CA 2367350C
Authority
CA
Canada
Prior art keywords
composition
resin
set forth
conductive
group
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CA002367350A
Other languages
French (fr)
Other versions
CA2367350A1 (en
Inventor
Kurt I. Butler
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Quantum Composites Inc
Original Assignee
Quantum Composites Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Quantum Composites Inc filed Critical Quantum Composites Inc
Publication of CA2367350A1 publication Critical patent/CA2367350A1/en
Application granted granted Critical
Publication of CA2367350C publication Critical patent/CA2367350C/en
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

A conductive polymer is disclosed which is suitable for use in applications which require corrosion resistance including resistance to corrosion when subjected to acidic flow at temperature ranging from -40 to 140 degrees Fahrenheit and which can be molded into highly intricate and thin specimens which exhibit consistent conductivity, sufficient strength and flexibility, and appropriate surface characteristics. In particular the invention involves molding unsaturated prepolymer resin composition, which have high loadings of conductive fillers. Further to enable the necessary characteristics, the compositions include rheological modifiers such as Group II oxides and hydroxides; carbodiamides; aziridines; polyisocyanates;
polytetrafluoroethylene (PTFE); perfluoropolyether (PFPE), and polyethylene. Ostensibly, these modifiers act to alter the apparent molecular weight and three dimensional prepolymer network structures correcting rheological deficiencies which otherwise lead to excessive resin particulate separation during the molding process and large variances in bulk conductivity across the plate surface. The composition is disclosed for use in electrochemical cells, such as fuel cells.

Description

HIGHLY CONDUCTIVE MOLDING COMPOUNDS AND FUEL CELL BIPOLAR
PLATES COMPRISING THESE COMPOUNDS
Field of Invention The field of invention is highly conductive compositions that are particularly useful for molding processes such as those using thermosetting bulk molding compositions. These molding compositions can be formed into high definition complex configurations. For example, they can be molded into thin plate-like specimens (e.g. 60 to 200 thousandths of an inch) having an intricately patterned network of very narrow, relatively smooth, flow passages.
These specimens are used as electrochemical cell bipolar plates. These plates desirably have a bulk conductivity of at least 40, 50, 60, 70, 80, 90 or even Slcm. They also have desirable surface characteristics; heat, temperature, chemical and shrink resistance; strength; and cost.
Background Of The Invention Conductive polymers have applications in providing alternatives to traditional conductive materials, which often involve greater labor expenses to manufacture into complex parts. In particular, in instances where the demand justifies significant volumes of a product, polymer molding expenses may prove far more cost effective than comparable machining expenses for other materials. However in the past, it has proved difficult to achieve both a high level of conductivity and desirable molding characteristics. Generally, high level weight percentages of an appropriate filler in a polymeric matrix are necessary to achieve satisfactory levels of conductivity. However, these high load levels lead to problems with the strength, durability, and moldability of the resulting composition.
One area in particular where it would be beneficial to solve the previously mentioned strength, durability, and molding issues is for application in fuel cells.
Electrochemical fuel cells have great appeal as a potentially limitless energy source that is clean and environmentally friendly.
These fuel cells can, in addition, be constructed at an appropriate scale for small scale energy consumption, such as household use, or for industrial scale use, and even for commercial power generation. They have portable applications to power small appliances (such as computers or camping equipment), or automobiles and other forms of transportation. Although these different applications involve differences in size, the fundamental construction remains the same for generation of power varying from less than one to a few thousand kilowatts.
Basically, a fuel cell is a galvanic cell in which the chemical energy of a fuel is converted directly into electrical energy by means of an electrochemical process. The fundamental components of the fuel cell are an electrode comprising an anode and a cathode, eletrocatalysts, and an electrolyte. Work has been done in perfecting both liquid and solid electrolyte fuel cells and the present invention may find use in both types of fuel cells.
Solid electrolytes include polymeric membranes, which act as proton exchange membranes typically fueled by hydrogen. These membranes usually comprise a perfluorinated sulphonic acid polymer membrane sandwiched between two catalyzed electrodes that may utilize platinum supported on carbon as an electrocatalyst. Hydrogen fuel cells form a reaction chamber, which consumes hydrogen at the anode. At the cathode, oxygen reacts with protons and electrons at the electrocatalytic sites yielding water as the reaction product. A three-phase interface is formed in the region of the electrode and a delicate balance must be maintained between the electrode, the electrolyte, and the gaseous phases.
Systems involving the use of other electrolytes have also been studied. These would include alkaline fuel cells, phosphoric acid fuel cell, molten carbonate fuel cells, and solid oxide fuel cells. However, the principles are similar, as are some of the issues in perfecting these products.
A fuel cell reactor may comprise a single-cell or a multi-cell stack. In any case, the cell includes at least two highly conductive flow field plates that serve multiple functions. These plates may function as current collectors that provide electrical continuity between the fuel cell voltage terminals and electrodes. They also provide mechanical support (for example for the membrane/electrode assembly). In addition, these plates act to transport reactants to the electrodes and are essential to establishing the previously mentioned delicate phase balance.
Typically, the fuel cell plates are thin relatively flat plate members that include a highly complex network of interconnecting channels that form the flow field area of the plate. The configuration of these channels is highly developed in order to maintain the proper flow of reactants and to avoid channeling or the formation of stagnant areas, which results in poor fuel cell performance. It is critical that the flow of the reactants is properly managed, and that the electrocatalysts are continuously supplied with precisely the appropriate balance of reactants. Thus, it is essential for the plates to define and maintain clear passages within the highly engineered flow labyrinth.
Moreover, in order to assure a satisfactory life, the plates must be able to resist surface corrosion under a variety of conditions. For example, fuel cells may be placed outside and subject to ambient weather. Thus, the cells must be resistant to stress cracking and corrosion at temperatures ranging from -40 to 200 degrees Fahrenheit. Further, since the conditions within the cell are corrosive, the cells must also be resistant to chemical attack at these temperatures from various corrosive substances. For example, the plates may be subjected to de-ionized water, methanol, formic acid, formaldehyde, heavy naptha, hydrofluoric acid, tertafluoroethylene, and hexafluoropropylene depending on the fuel cell type. Moreover, the conditions within the fuel cell may lead to elevated temperatures, i.e. from 150 to 200 degrees Fahrenheit, as well as elevated pressures, i.e. from ambient to 30 p.s.i. Corrosive decomposition needs to be avoided since it almost certainly would cause a system failure by changing the flow patterns within the fuel cell.
Past attempts at solving the various requirements for fuel cell plates have included the use of metal and machined graphite plates. The use of metal plates result in higher weight per cell, higher machining costs and possibly corrosion problems. Machined graphite plates solve the weight and corrosion problems but involve high machining cost and result in fragile products, especially when prepared as very thin plates. Some use of graphite/poly(vinylidene fluoride) plates has been made but these have been characterized as being expensive and brittle and having long cycle times.
U. S. Patent No. 4,197,178 teaches the working and compositions of electrochemical cells. U.S. Patent No. 4,301,222 teaches graphite based separators for electrochemical cells.
Summary Of The Invention In the past, known conventional bulk molding compounds have been modified to be conductive by the addition of large amounts of conductive filler, such as graphite. During molding it was observed that the liquid resin phase separated from the filler and was exuded from the molding. Further, it was observed that this occurrence tended to cause cracking in molded specimens that were thin. Moreover, bulk conductivity measurements at different locations within the specimen Were inconsistent. In accordance with the present invention, it was discovered that compositions could be formulated which solved the foregoing issues. In particular, the formulations involve the use of a resin matrix with high loadings of a conductive filler; various additional additives, such as initiators, mold-release agents, and carbon black; and one or more rheological agents selected from the group comprising group II oxides and hydroxides, alkaline earth oxides, carbodiamides, aziridines, polyisocynates, polyethylene, polytetrafluorethylene, pertluoropolyether, fumed silica and clays.
One possible explanation for the mechanism by Which the molding agents work, is that they act to build the apparent molecular weight of the prepolymer (e.g.
vinyl ester resin or unsaturated polyester resin). Alternatively, these agents may promote flow such as by reducing shear during molding. The use of these rheological agents eliminates phase separation, as well as cracking and inconsistent conductivity measurements. It is anticipated that these problems are a result of the complex configuration of the specimens being molded along with the very high concentrations of conductive filler.
In addition to solving molding and cracking problems it is anticipated that other properties such as the coefficient of thermal expansion, electrical and thermal conductivity, shrink resistance and mechanical properties may be more uniform and/or otherwise improved as a result of the use of the present invention. In addition to the foregoing improvements it was found that a resin composition of the invention demonstrated a higher glass transition temperature and resulted in an improvement in the hot strength of the molded part. Further improvements are also possible by optimizing both gel time and cure time for the prepolymer by controlling initiator type and amount and inhibitor type and amount.
The foregoing improvements in specimens molded from these compositions enable the low cost mass production of bipolar plates as an additional embodiment of the invention. These could be used for portable fuel cells, as well as stationary power units.
Brief Description Of The Drawings Figure 1 is an illustration of a bipolar fuel cell plate that can be made in accordance with the present invention; and Figure 2 is an illustration of a fuel cell assembly utilizing a bipolar cell plate.
Detailed Description Of The Invention The invention relates to improvements in conductive molding compositions. In particular, the compositions can be used in compression molding processes and in injection molding processes. Further these compositions enable the production of thin and intricate specimens that have high concentrations of conductive filler.
Sheet molding and bulk molding compositions are described in U.S.
Patents 5,998,510; 5,342,554; 5,854,317; 5,744,816; and 5,268,400.
One component of a molding resin composition is a crosslinkable prepolymer such as an unsaturated polyester resin or vinyl ester resin.
Desirably the prepolymer has a relatively low molecular weight such as from about 200 to about 5000 (weight average). They are described in detail with examples in the above patents. The polyester resins are the condensation product derived from the condensation of unsaturated polybasic acids and/or anhydrides with polyols such as dihydroxy or trihydroxy compounds. Desirably, these polyester resins are the esterification reaction product of diacids, or anhydrides of diacids, generally having from about 3 to about 12, or more preferably from about 4 to about 8 carbon atoms, with a polyol or a cyclic ether having from about 2 to about 12, or more preferably from about 2 to about 6 carbon atoms.
In general, the vinyl ester resins that can be used are the reaction products of epoxy resins and a monofunctional ethlenically unsaturated carboxylic acid. More specifically, these vinyl ester resins are the reaction product of an epoxy terminated oligomer, for example, an epoxy functionalized bisphenol A with an acrylic acid, or methacrylic acid forming acrylic terminal groups on the oligomer. The vinyl esters have predominantly terminal unsaturation while the unsaturated polyesters have predominantly internal unsaturation.
Another component of the molding composition is one or more unsaturated monomers that are copolymerizable with the resin. Desirably, this component is capable of dissolving the resin component at room temperature.
Thus, in one embodiment the resin is dissolved in the monomeric component prior to being combined with the remaining components. Examples of suitable monomers are styrene, alpha-methyl styrene, chloro-styrene, vinyl toluene, divinyl benzene, diallylphthalate, methyl methacrylate, and mixture of these, with preferred monomers being styrene and methyl methacrylate. The ratio of monomers) to resin is desirably from about 40:60 to about 75:25 and preferably from about 40:60 to about 65:35 by weight.
Another component to the molding composition is fillers. In accordance with the invention the predominant filler is a conductive filler in order to impart electrical conductivity of the final molded product. A preferred filler is graphite particles, in particular, a synthetic crystalline graphite particle, such as currently supplied by Ashbury Graphite in Ashbury, New Jersey under the designation Ashbury~ 4012. This graphite is characterized as having less than 10%
particles greater than 150 microns and less than 10% smaller than 44 microns in diameter. Other graphite fillers include: Ashbury A99, Ashbury 3243, Ashbury modified 4012, Ashbury 3285, Ashbury 230U; TimrexR~ KS 75 and 150, and TimrexR KC 44, all sold by TIMCAL of Westlake, Ohio; and Calgraph~ Sold by SGL Technic Inc of Valencia, California. This filler is used at a loading of at least 50% by weight. Other conductive fillers such as other forms of graphite (including graphite pitch-based fibers), metal particles, or metal coat particles may be used in conjunction with the graphite filler, or even alone. Desirably conductive fillers are at least about 50, about 60, or about 65 weight percent of the molding composition. More desirably the filler is more than about 70 or 71 percent to about 78 weight percent of the molding composition. Alternatively this amount can be expressed as at least about 250 phr, more preferably at least about 275, or even 300 phr. Alternatively stated the conductive fillers are present in an effective amount to result in a bulk conductivity of at least about 40, about 50, about 60, about 70, about 80, about 85, about 90 or about 96 S/cm when measured in accordance with ASTM Test Standard No. F1529-97 for a molded article having a thickness from about 0.060 to about 0.200 inches.
Current technology in fuel cell plates uses a bulk conductivity of at least about 55, and preferably at least about 70.
An initiator is another component of the molding composition. The initiator initiates the copolymerization of the resin and the monomer(s).
Initiators include any free radical initiator capable of forming radicals in the correct concentration under the molding conditions. They may include peroxides, hydroperoxides, redox systems, diazo compounds, persulfates, perbenzoates etc. The initiators are typically used in amounts of about 0.05 to about 5 weight percent, and more preferably about 0.1 to about 2 weight percent.
Alternatively, these amounts can be expressed in parts per hundred parts by weight of resin, i.e. from about 0.5 to about 4.0 phr, preferably from about 0.7 to about 3.0 phr, and most preferably from about 0.8 to about 2.25 phr. Alternatively high temperature initiators such as Di-cup, e.g. dicumyl peroxide can be used for molding applications where higher iniation temperatures are desirable.
An essential component to the improved molding composition is a rheological modifier, which may act to increase the molecular weight such as by chain extension of the resin prepolymer. Suitable modifiers include Group II
oxides and hydroxides, such as calcium or magnesium oxide; carbodiamides;
aziridines; and polyisocyanates. It is believed that the foregoing modifiers act chemically by co-reacting into the polymer backbone at carboxy or hydroxy sites. Other suitable modifiers include polytetrafluoroethylene (PTFE);
pertluoropolyether (PFPE), and polyethylene. These modifiers may act to reduce shear and thus promote flow in the composition during molding. Fumed silica is an example of a substance which may act mechanically to increase molding viscosity and therefore be a suitable rheological modifier for this invention. Combinations of two or more rheological modifiers may be desirable for optimum properties. In this application they are used to modify the resin structure to prevent phase separation of the resin from the conductive filler (in particular in view of the high loadings of the conductive filler, i.e. over 50% or even 65% by weight or more of graphite). The modifiers are further used in general to enable the achievement of a high definition conductive polymeric fuel cell plate.
Desirably the rheological modifiers are used in an effective amount to prevent phase separation during molding. For the purpose of this application molding will desirably be at pressures from about 400 to about 5000 psi, and preferably from about 2000 to about 3500 psi, and most preferably from about 2500 to about 3000 psi. Desirable amounts of group II oxides (including group II
hydroxides and mixtures of these compounds) is from about 0.1 to about 1 or about 2 weight percent, more desirably from about 0.2 or about 0.3 to about 0.7 or about 0.8 weight percent. This can also be expressed as from about 0.5 to about 4.0 phr, preferably from about 1.0 to about 3.0 phr, and most preferably from about 1.5 to about 2.5 phr. Specific preferred compounds include magnesium oxide, or magnesium hydroxide or calcium oxide. Examples of a suitable magnesium oxide additive is 99% pure magnesium oxide sold under the trademark "Elastomag" from Morton Thiokol, Inc. in Danvers, MA. Other examples include a magnesium oxide dispersion sold under the tradename "pg-_g_ 9033" by Plasticolors, and a magnesium hydroxide dispersion also sold by Plasticolors under the tradename "pg-91146". Another suitable magnesium hydroxide is Barcroft~, which is a powdered version. Examples of aziridine compounds include polyfunctional aziridines supplied by EIT, Inc. under the trade designation XAMA~, including XAMA-2, which is identified as trimethylol propane-tris (beta-(N-aziridinyl) proprionate), and, in particular, XAMA-7, which is identified as pentaerythritol-tris-(beta-(aziridinyl) proprionate); a product of Sybron Chemicals, under the tradename lonac~ including PFAZ-322, identified as a trifunctional aziridine; and including CX-100, a product of Zeneca Resins, identified as a polyfunctional aziridine. Desirable amounts of aziridine and/or polyisocyanate modifiers is from about 1 to about 10 or about 15 weight percent, and more desirably from about 2 or about 3 to about 8 or about 9 weight percent. This can also be expressed as from about 0.5 to about 20 phr, preferably from about 1 to about 17 phr, and most preferably from about 2 to about 15 phr. Polyisocyanates in general are described in more detail in U.S.
5,268,400 column 6, line 59 through column 7, line 17. A specific diisocyanate which can be used is diphenylmethane diisocyanate such as that sold by ICI
Americas of West Deptford, New Jersey, under the trademark "Rubinate" R MF-1780. Additionally, a suitable diisocynate is Lupranate~ MP102, solvent free urethane-modified diphenylmethane diisocyanate from BASF. Desirable amounts of polytetrafluoroethylene (PTFE) (and/or perfluoropolyether (PFPE)) is from about 0.5 to about 1 or about 2 weight percent, more desirably from about 0.6 or about 0.7 to about 1.8 or about 1.3 weight percent. This can also be expressed as from about 0.5 to about 20 phr, preferably from about 3 to about 15 phr, and most preferably from about 5 to about 12 phr. A suitable fine particle PTFE powder is sold under the trademark "Marzon #5 by Marshall Products Company of West Chester Pennsylvania. It is preferable to use a linear low-density polyethylene such as sold by Equistar of Houston Texas under the tradename FN 510 It is preferable to use it in amounts of from about 3 to about 20 phr, more preferably from about 4 to about 17, and most preferably from about 5 to about 15 phr. Fumed silica could be used at from about 0.5 to about 20 phr, preferably from about 1 to 10 phr.

Other optional components to a molding composition include urethane based or urethane containing oligomers or polymers, low shrinkage additives like polyvinyl acetate or polyethylene; fibrous reinforcing agents such as cotton glass microfibers or graphite microfibers; flexibilizing agents; mold release agents; polymerization inhibitors to inhibit premature polymerization during storage or the initial stages of molding; viscosity modifiers like fumed silica; and mold lubricant like stearates of calcium, zinc or magnesium. Carbon black may be added to influence the surface conductivity and to change the appearance of the molded product. Suitable carbon blacks include an electrically conductive low residue carbon black having a nitrogen surface area m2/g of 270, a STSA
surface Area m2/g of 145 a sieve residue at 35 mesh of Oppm and at 325 mesh of 20 ppm as sold under the trademark Conductex 975 by Columbia Chemicals of Jamesburg, NJ. Also, suitable conductive carbon black is supplied by Akzo Nobel Chemicals of Chicago, Illinois under the tradename Ketjenblack EC-300 J and EC-600JD. Cabot Corporation of Boston MA also supplies a conductive carbon black. It is noted that polyethylene and fumed silica can function as the theological modifier in addition to the foregoing functions.
The molding compositions may be formulated and mixed using a variety of mixing conditions including either continuous or batch and using a variety of known mixing equipment. Specific examples are set forth in the example section. The compositions may be advantageously stored for reasonable times before molding. The compositions can be molded by a variety of methods including compression molding and injection molding. The compositions can be molded under typical conditions for these types of molding including at pressures from about 400 to about 5000 psi, and preferably from about 2000 to about 3500 psi, and most preferably from about 2500 to about 3000 psi and temperatures at from about 225 to about 400 degrees Fahrenheit. Dwell times are from about 70 seconds to about four minutes. The compositions are useful for molding complex configurations including thin or intricate conductive articles such as those having a thickness from about 0.050 to about 0.200 inches, and more preferably from about 0.060 to about 0.150 inches. The compositions are useful for articles having bulk conductivity of at feast 40, 50, 60, 70, 80, 85, 90 or even 96 S/cm at a thickness given above. The articles from the composition desirably have tensile strength from about 1500 to about 5000 psi as measured in accordance with ASTM test No.D638 and flexural modulus from about 2500 to abaut 10,000 psi when tested in accordance with ASTM test no.D790.
Molded products made from the compositions of the present invention are useful for a variety of applications demanding complex configurations, conductivity, as well as strength, and corrosion resistance. One particularly advantageous product which can be made by compression molding is a bipolar plate for use in fuel cells. An example c>f such a plate is shown in Figure 1. The drawing of this plate is intended to illustrate the molding capabilities of the conductive compound of the present invention. It is not necessarily intended to provide optimal, or even operative, field flow design.
It should not limit the invention in any way. The plate 10 includes a fluid flow face with one or more generally parallel and or serpentine flow channels 12.
The flow channels receive and transmit fluids through ports 14 and 16 which are in fluid communication with corresponding entry and exit fluid manifolds 18 and 19. The plate has a dimension which will vary from 1 to 20 inches in length and width, and having a thickness of 0.02 to 0.3 inch, with a cross-sectional depth of the flow channel in the range of about 0.005 to 0.080 inch.
The cross-sectional width of a land separating adjacent flow channel sections is in the range of 0.01 to 0.1 inch. The plate may include a number of peripheral through holes 20 that act as a manifold for fuel transportation.
Figure 2 illustrates the unassembled components of a fuel cell. This fu~ei cell has a base unit 32 YNh~ch includes debcssed means to accept a reformer 34 and a fuel cell stack 36 which is comprised of a plurality of bipolar plates 40 which are sandwiched between a stack cap 42 and a stack base 44. The fuel cell further includes a heat exchanger 38. An enclosure 30 provides a leak-proof housing for the unit.
Examples The following examples use the components set forth below.

Resin A is Hetron~ 922 available from Ashland Chemical Co. in Columbus Ohio. It is a low viscosity epoxy vinyl ester resin. It is about 55 wt.
solids and about 45 wt. °~ reactive monomer.
Resin B is Atlac~ 382ES from Reichhold Chemicals, Inc. in Research Triangle Park, NC. It is characterized as a bisphenol fumarate resin. It was diluted to about 55 wt. % solids with styrene.
Resin C is Dion~ 6694 diluted to 55 wt. % solids in styrene. It is available from Reichhold Chemicals, Inc. It is characterized as a modified bisphenol fumarate polyester.
Resin D is 42-2641 from Cook Composites and Polymers in Kansas City, MO. It was diluted to 55 wt. % solids with styrene. It is characterized as an unsaturated polyester resin.
Resin E is ATLAC~ 3581-61 from Reichhold Chemicals, Inc. It is characterized as a vinyl ester resin at 19 wt %, polyester at 27 wt °~
and urethane polymer at 4 wt % combined with 50 wt °~ styrene. Thus, it was diluted to 50 wt % solids with styrene.
Resin F is 580-05 from Reichhold Chemicals, Inc. It is characterized as a urethane-modified vinyl ester resin. It was diluted to 54 wt % solids with styrene.
Resin G is 9100 from Reichhold Chemicals, Inc. It is characterized as a bisphenol-epoxy vinyl ester. It was diluted to 54-58 wt % solids with styrene.
Resin H is Dow Derakane~ 88084 from Dow Chemicals, Inc. It is characterized as an elastomer-modified vinyl ester resin. It was diluted to wt % solids with styrene.
Resin I is 9480-00 from Reichhold Chemicals, Inc. It is characterized as an epoxy novolac vinyl ester. It was diluted to 53.5 wt % solids with styrene.
Resin J is Atlac 31-632 from Reichhold Chemicals, Inc. It is an unsaturated isocyanurate vinyl ester resin.
Rheological Modifier A is Elastomag from Morton Thiokol. Inc. in Danvers, MA. It is characterized as 99% pure magnesium oxide.
Rheological Modifier B is a polyisocyanate. The material used in these experiments is 40-7263 from Cook Composites and Polymers. It is characterized by a NCO content of 17.7 to 20.9, a viscosity of 110-170, a flash point of 87 °F., and a crystallization point of 40 °F.
Rheological Modifier C is RCI RD THL55 (also known as RD-1070) from Reichhold, Inc. It is specifically a polyurethane resin.
Rheological Modifier D is Rubinate 1780 available from ICI. It is characterized as a polymeric methylene diphenyl diisocyanate.
Rheological Modifier E is Marzon #5 from Marshall Products Company of West Chester, PA. It is characterized as a finely divided powder polytetra-fluorethylene.
Rheological Modifier F is FN-510, a linear low density polyethylene Initiator A is Vazo~ (2,2-azo bisisobutyronitrile) available from Dupont, I
& B Industrial and Biochemical Dept, Wilmington DE.
Initiator B is tert-butyl peroxy isopropyl carbonate (Triginox~ BPIC) available from Durr Marketing in Pittsburgh, PA.
Initiator C is t-butylperbenzoate (TBPB) available from Durr Marketing.
Initiator D is 1,3 di-t-butyl peroxy-3,5,5 trimethylcyclohexane catalyst (Trig~ 29875) available from Durr Marketing.
The mold release agent is calcium stearate.
Graphite A is a synthetic, crystalline graphite available from Asbury Graphite in Asbury, NJ. It is characterized by having less than 10% greater than 150 microns and less than 10% smaller than 44 microns in diameter. It is available under the designation 4012.
Graphite B is a very fine conductive particulate graphite available from SGL Technic of Valencia, California under the trade designation SGL 02.
Graphite C is a conductive particulate graphite available from SGL
Technic of Valencia California under the trade designation SGLVFINE.
Graphite D is available from Asbury Graphite in Asbury, NJ. It is a modified version of the 4012 product.
Graphite E is a conductive flake graphite available from Asbury Graphite in Asbury, NJ. under the trade designation 3243. It is characterized by having less than 18% greater than 75 microns and less than 65% smaller than 44 microns in diameter.

Graphite F is a conductive flake graphite available from Asbury Graphite in Asbury, NJ. under the trade designation 230U. It is characterized by having 100% smaller than 44 microns in diameter.
Graphite G is a synthetic graphite available from Asbury Graphite in Asbury, NJ under the trade designation A99. It is characterized by having less than 3% greater than 44 microns and less than 99 % smaller than 44 microns in diameter.
Graphite H is a synthetic graphite available under the designation KS 75, from Timrex America, Inc. It is characterized by having less than 95% greater than 96 microns and less than 95% smaller than 75 microns in diameter.
Graphite I is a synthetic graphite available under the designation KS 150, from Timrex America, Inc. It is characterized by having at least 95% less than 180 microns in diameter.
Graphite J is a synthetic graphite available under the designation KC44, from Timrex America, Inc. It is characterized by having at least 90%
less than 48 microns in diameter.
Carbon Black B is characterized as an electrically conductive low residue carbon black having a nitrogen surface area m2/g of 270, a STSA
surface Area m2/g of 145 a sieve residue at 35 mesh of Oppm and at 325 mesh of 20 ppm as sold under the tradename Conductex 975 by Columbia Chemicals of Jamesburg, NJ.
Carbon Black C is conductive carbon black supplied by Cabot Corporation of Boston, MA under the tradename, Black Pearls, while Graphite D is supplied by this company under the designation XC-72.
Carbon Black E is conductive carbon black supplied by Akzo Nobel Chemicals of Chicago, Illinois under the tradename Ketjenblack EC-300 J
and EC-600JD. EC-300 J has an iodine absorption of 740-840 mg/g; a pore volume of 310-345 cm3/100g and an apparent bulk density of 125-145 kg/m3. EC-600 JD has an iodine absorption of 1000-1150 mg/g; a pore volume of 480-510 cm3/100g and an apparent bulk density of 100-120 kg/m3.

The Glass fibers were from Owens-Corning Fiberglass and are characterized as continuous glass filaments hammermilled into a specific length used as a reinforcing and filler medium.
The inhibitor was 2,6-di-tertbutyl-p-cresol (25% in vinyl toluene).
The molding compositions are generally prepared by adding the resin, monomer initiator, inhibitor, mold release agent, and theological modifier (if present) to a high shear cowels disperses and blending for 2 minutes. The conductive filler is added to the mix in a Baker Perkin Mixer and mixed 15 minutes. When mixing is complete the composition is put in a suitable barrier bag and allowed to mature for approximately one day before molding.
The molding parameters for the molding compositions are as follows:
Molding temperature for plaques was 295 °F with a molding time of minutes and a charge weight of 173 g. The molding temperature for prototype bipolar plates was 290 °F with a molding time of 3 minutes and a charge weight of 300 g. It was observed that the use of specific thermosetting resins with a conductive filler in combination with various theological additives (thickeners) improved the bipolar plate composition in regards to having a product which can be used in mass production of electrochemical, e.g. fuel, cell bipolar plates.
The results of the formulation changes include non-cracking molding compound, better hot strength out of the mold, lower production costs, shorter cycle times, better overall electrical conductivity, increased mechanical properties, and better theological characteristics.
In Table IA the Control L-23012 suffered from cracking during molding of a plate and had non-uniform conductivity and resistivity along the surface of the plate due to phase separation of the conductive filler and resin during molding. Samples L-23185, L-23120, L-23119 and L-23126 had desirable properties.
In Table IB Samples L-23125, L-23186, L-23039 had desirable properties. Samples L-23184 and L-23022 had lower than optimal bulk conductivity and higher than optimal resistivity.

In Table IC Samples L-23023, L-23063, L-23024, L-323027, and L-23026 had lower than optimal bulk conductivity and higher than optimal resistivity.
In Table ID Samples L-23209 and L-23215 had good properties.
Samples L-23028, L-23210, and L-23211 had lower than optimal bulk conductivity and higher than optimal resistively.
The components are presented in grams in the following tables.

Table IA
Component Control L-23185 L-23120 L-23119 L-23126 Resin A 30.1 g Resin B

Resin C 19.95g Resin D 17.13 15.63 23.33 ' Initiator 0.6g (A) 0.4 (B) 0.4 (B) 0.4 (B) 0.4 (B) Inhibitor 0.1 0.1 0.1 0.1 0.1 Mold 1.2 1.2 1.2 1.2 1.2 i Release ~ I

Graphite 68g 75 I 78 78 i A

Graphite 68 I
B

Graphite t C

Modifier - I 0.35g A i Modifier - 6.17 ~ 4.67 6.97 ' B

Glass fibers l Bulk 85 85 90 90 70 Conductivity ' i S/cm Areal 300 260 260 260 220 Conductivity I
S/cm2 ' I

Tensile psi 3500 3700 3600 3100 3500 Flexural 4100 5500 4300 3500 4200 psi Resistivity 70.9 87.51 71.2 37.7 Table IB
Component L-23125 L-23186 L-23039 L-23184 L-23022 ~

Resin A ' Resin B 19.95 29.95 Resin C 22.65 27.65 Resin D 23.33g Initiator 04 (B) 0.4 (C) 0.4 (B) 0.4 (C) 0.4 (B) I, I

Inhibitor 0.1 0.1 0.1 0.1 ~ 0.1 Mold 1.2 1.3 1.2 1.3 I 1.2 'i Release Graphite 34 70 68 70 I 68 i A

Graphite 34 B

Graphite C

Modifier 0.55 0.35 0.55 ! 0.35 A

Modifier 6.97 ~ ~ i B

Glass fibers 5 10 Bulk 70 70 65 45 40 Conductivity Slcm Areal 210 210 200 140 140 Conductivity S/cm2 Tensile psi 3400 3000 2800 3000 4100 Flexural 4200 3700 3800 4000 5000 psi Resistivity 58.13 123.8 117.6 155.6 222.1 I

Table IC
Component L-23023 L-23063 L-23024 L-23027 L-23026 I, Resin A

Resin B 29.95 29.95 29.95 Resin C 29.95 29.950 i Resin D

Initiator 0.4 (C 0.4 (B) 0.4 (D) 0.4 (C) 0.4 (B) ) I

Inhibitor 0.1 0.1 0.1 0.1 1 0.1 Mold 1.2 1.2 1.2 1.2 1.2 Release Graphite 68 68 68 68 I 68 A

Graphite ' B

Graphite C I

Modifier 0.35 0.35 0.35 0.35 0.35 A

Modifier B

Glass fibers Bulk 40 40 35 30 ~ 30 Conductivity S/cm Areal 140 120 130 90 90 Conductivity ;
SIcm2 Tensile psi 4200 3500 3100 4700 4300 Flexural 4900 4200 3400 6000 5300 ' psi Resistivity 205.9 - 181.7 320.9 246.8 OHMS/M2 i Table 1 D
' Component L-23028 L-23209 L-23210 L-23211 L-23215 Resin A

Resin B

Resin C 29.95 28.65 22.65 Resin D 21.49 21.49 Initiator 0.4 (D) 0.4(B) 0.4 (BO 0.4 (B) 0.4 (B) !, Inhibitor 0.1 0.1 0.1 0.1 ~ 0.1 I

Mold 1.2 1.2 1.2 1.3 'I 1.3 Release i ' Graphite 68 42 42 , 70 Graphite 26 I
B

Graphite 0.35 26 26 I
C

Modifier 0.35 0.55 0.55 A

Modifier 8.81 8.81 B

Glass fibers Bulk 30 77 25 45 ~ 79 i Conductivity ~
S/cm I

Areal 100 227 74 132 233 Conductivity S/cm2 i Tensile psi 3800 2700 3900 3000 2600 I

Flexural 5100 3900 5500 4500 4300 psi Resistivity 220.9 62.02 377.8 186.46 102.74 Table 2A
Component 23012 23039 23022 23023 23063 Resin A 100 Resin B 100 100 100 100 Initiator 1.99 A

Initiator 2.01 1.34 1.34 ' B

Initiator 1.34 C

Inhibitor 0.33 0.50 0.33 0.33 0.33 Release 3.99 6.02 4.01 4.01 4.01 I
I
Agent ~

Graphite 225.91 340.85 227.05 227.05 j A 227.05 Modifier 1.17 1.17 1.17 i A

Fiber A 50.13 Bulk 85 65 I 40 40 I 40 ' I
Conductivity S/cm Areal 300 200 140 140 120 Conductivity S/cm2 Tensile 3500 2800 ~ 4100 4200 3500 psi Flexural 4100 3800 5000 4900 4200 psi Table 2B
Component 23024 23119 23186 23184 23027 i Resin B 100 Resin C 100 100 100 100 i Initiator 2.01 ~ I
B

Initiator 1.77 1.45 1.34 C ~

Initiator 1.34 i I
D

Inhibitor 0.33 0.50 0.44 0.36 0.33 Release 4.01 6.02 5.74 4.70 4.01 Agent ~

Graphite 227.05 390.98 309.05 253.16 227.05 A '~ I
I

Modifier 1.17 1.75 2.43 1.99 1.17 A ,, , Fibers A 22.08 ~ I

Bulk 35 90 70 45 '~ 30 ' Conductivity i S/cm Areal 130 260 210 140 90 Conductivity ' S/cm2 I ~ , Tensile psi 135 , 260 I 210 140 ; 90 Flexural 3100 3100 3000 3000 4700 psi Table 2C
Component 23026 23028 23211 23215 23185 I, Resin C 100 100 100 100 Resin D 100 Initiator 1.34 1.40 1.77 2.34 B

Initiator 1.34 D

Inhibitor 0.33 0.33 0.35 0.44 0.58 ' I

Release 4.01 4.01 4.54 5.74 7.01 Agent ~ '~ ' ~
I

Graphite 227.05 227.05 150.09 ',, 437.83 A 309.05 Graphite 90.75 C

Modifier 1.17 1.17 1.92 2.43 j A I

Modifier B 36.02 Fiber B ' 22.08 ~ ' Bulk 30 ~ 30 45 79 ',, 85 Conductivity i S/cm I

Areal 90 I 100 132 233 260 ' Conductivity i S/cm2 Tensile psi 4300 ~ 3800 3000 2600 i 3700 Flexural 5300 5100 4500 4300 psi 5500 Table 2D
Component 23120 23126 23125 23209 23210 Resin D 100 100 100 100 I 100 Initiator 2.56 1.71 1.71 1.86 1.86 B ~

Inhibitor 0.64 0.43 0.43 0.43 0.47 I
I

Release 7.68 5.14 5.14 5.58 5.58 j Agent Graphite 499.04 145.74 195.44 195.44 A I I

Graphite 291.47 145.74 120.99 j, B ~

Graphite ~ 120.99 C

Modifier 29.88 29.88 29.88 41.00 41.00 i B 'i Bulk 90 70 70 77 ~~ 25 i Conductivity I

S/cm Areal 260 220 210 227 74 Conductivity I
S/cm2 i Tensile 3600 3500 3400 2700 ~ 3900 psi j Flexural 4300 4200 4200 3900 5500 ps i Table 3A
Component 23227 23236 23237 23274 23275 Resin D 100 100 100 100 100 Initiator 1.56 1.44 1.51 2.34 2.34 B

Inhibitor 0.52 0.48 0.50 0.58 0.58 Release 6.24 5.77 6.06 7.01 7.01 Agent Graphite 390.02 350.96 368.50 420.32 420.32 A

Carbon A 17.51 Modifier 21.68 22.12 28.22 36.02 36.02 B

Fiber C 11.68 Bulk g0 Conductivity S/cm Tensile 2672 psi Flexural 6543 psi Density 1.67 1.75 1.77 g/cm3 I

Shrink mils/in -1.5 ~ -1.83 I -2.25 Table 3B
Component 23292 23293 23343 23344 23345 Resin D 100 100 100 100 100 ' Initiator 1.48 1.56 1.44 1.29 1.20 B

Inhibitor 0.49 0.52 0.48 0.43 0.40 I
I

Release 5.93 6.24 5.75 5.14 4.80 Agent j Graphite 370.74 395.22 349.78 299.91 272.22 A !, Modifier 15.67 16.48 21.71 21.68 21.70 B

Bulk 72.5 58 Conductivity i S/cm Tensile psi 2170 2547 2448 2679 Flexural 4616 ~ 6503 5423 5897 psi Density 1.67 1.73 1.71 I
g/cm3 i Shrink mils/in-2.17 -2.08 -2 Table 3C
Component 23346 23347 23348 23349 23350 Resin D 100 100 100 100 100 Initiator 1.09 1.03 0.95 0.90 0.84 B

Inhibitor 0.36 0.34 0.32 0.30 0.28 Release 4.37 4.13 3.80 3.61 3.36 Agent 'i Graphite 236.79 216.57 190.11 174.70 154.19 A

Modifier 21.68 21.69 21.67 21.69 21.67 B

Tensile 3083 3053 2923 3107 3470 psi Flexural 5715 5766 5666 5398 5378 psi Density 1.75 1.71 1.73 1.7 1.64 g/cm3 i Shrink mils/in-3 -3.5 -3.33 -4 -5 Table 3D
Component 23351 23352 23360 23361 23362 Resin D 100 100 100 100 100 Initiator 0.80 0.75 2.27 2.21 2.14 B

Inhibitor 0.27 0.25 0.57 0.55 0.54 Release 3.22 3.02 6.81 6.62 6.43 Agent Graphite 142.05 125.75 425.41 413.45 402.14 A

Modifier 21.68 21.73 32.16 28.45 24.93 B

Bulk 85.5 Conductivity ' S/cm Tensile psi 2787 2629 2155 Flexural 6167 5998 6017 psi Density 1.72 1.71 1.65 1.73 1.68 g/cm3 ', Shrink mils/in-1.67 -1.83 -1.42 -1.42 -0.67 I

_28_ Table 4A
Component 23364 23365 23366 23367 23368 Resin D 100 100 100 100 100 Monomer A 9.72 8.18 7.05 6.20 5.53 Initiator 1.46 1.23 1.06 0.93 0.83 B

Inhibitor 0.49 0.41 0.35 0.31 0.28 Release 5.83 4.91 4.23 3.72 3.32 Agent ~

Graphite 340.30 265.85 211.57 170.54 138.31 A

Modifier 28.43 28.34 28.35 28.37 28.35 B ~

Bulk 55.99 36.57 32.86 18.37 13.59 Conductivity S/cm Tensile psi 2647 2697 2701 2880 2992 Flexural 6044 6131 6149 7002 7338 I
psi Density 1.75 1.74 1.71 1.72 1.71 g/cm3 Shrink mils/in-2.5 -2.83 -3.17 -3.33 -3.83 Table 4B
Component 23369 23370 23371 23372 23373 Resin D 100 100 100 100 100 Initiator 1.36 1.15 1.00 0.89 0.79 B

Inhibitor 0.45 0.38 0.33 0.30 0.26 Release 5.42 4.61 4.01 3.55 3.18 Agent Graphite 316.17 249.52 200.33 162.48 132.45 A

Modifier 28.27 28.21 28.21 28.21 28.21 B I

Bulk 49.49 27.74 25.05 14.01 8.12 i Conductivity S/cm Tensile 2974 3358 3014 2952 3154 psi t Flexural 6394 6099 6520 6312 6071 psi Density 1.72 1.76 1.69 1.73 1.72 I
g/cm3 I

Shrink mils/in-3.5 -2.5 -2.83 -3.17 -3.53 ''~

Table 4C
Component 23443 23444 23445 23466 23467 Resin D 100 100 100 100 100 Initiator 1.84 1.72 1.56 1.81 1.54 B

Inhibitor 0.46 0.43 0.39 0.45 0.39 Release 5.52 5:15 4.69 5.44 4.62 i, Agent ~

Graphite 322.14 291.85 253.91 317.17 250.29 A

Modifier 30.23 30.04 30.08 28.23 28.23 B

Bulk 36 21.2 15 39 21 Conductivity S/cm Tensile 2312 2765 psi Flexural 6154 5994 psi Density 1.76 1.76 1.75 1.75 1.73 g/cm3 Shrink mils/in-2 -2 -2.33 -1.67 -1.83 Table 4D
Component 23468 23469 23470 23471 23505 Resin D 100 100 100 100 100 Initiator 1.69 1.75 1.95 2.11 1.48 B

Inhibitor 0.42 0.44 0.49 0.53 0.37 Release 5.08 5.25 5.85 6.33 4.45 Agent Graphite 287.77 284.46 331.55 369.39 241.01 A

Modifier 28.23 28.23 28.23 28.23 23.47 B

Fiber D 17.51 19.50 21.11 Bulk 34 45 60 61 ' Conductivity S/cm ' Tensile 2466 2804 1797 2010 2821 psi Flexural 5272 7390 6682 4726 4898 psi Density 1.71 1.6 1.62 1.58 1.75 t I
g/cm3 i ~

Shrink mils/in-2.33 -2 -1.42 -1.67 -2.5 Table 5A
Component 23506 23507 23508 23509 23510 Resin D 100 100 100 100 I 100 t Initiator 1.63 1.75 1.45 1.59 1.70 B

Inhibitor 0.41 0.44 0.36 0.40 0.43 Release 4.89 5.24 4.34 4.77 5.11 Agent Graphite 277.10 305.41 235.17 270.38 298.00 A

Modifier 23.47 23.47 20.48 20.48 20.48 B

Bulk 55 45 52 60 65 Conductivity S/cm Tensile 2680 2645 2483 psi Flexural 4556.7 5264.4 4773.67 psi Density 1.74 1.74 1.79 1.78 ~ 1.76 g/cm3 Shrink mils/in-2.5 -2.33 -2.33 -2.42 -1.75 '~

Table 5B
Component 23566 23567 23568 23581 23582 Resin D 100 100 100 100 100 Initiator 1.85 1.79 1.75 1.77 1.83 B

Inhibitor 0.46 0.45 0.44 0.44 0.46 Release 5.54 5.38 5.26 5.30 5.50 Agent Graphite 346.42 336.32 328.95 313.33 329.82 A

Modifier 20.48 20.48 B

Modifier 7.62 4.48 2.19 I
D

Bulk 92 ~ 94 Conductivity i I
S/cm i Density 1.77 1.78 i 1.75 1.79 1.76 g/cm3 Shrink mils/in-1.67 -1.25 -1.25 -1.67 -1.58 Table 5C
Component 23583 23584 23585 23592 23593 Resin D 100 100 100 100 10 Initiator 1.90 1.98 2.07 1.88 1.97 B

Inhibitor 0.48 0.50 0.52 0.47 0.49 I

Release 5.71 5.95 6.20 5.63 5.91 Agent Graphite 347.62 366.88 387.80 352.11 369.46 A ;

Modifier 20.48 20.48 20.48 B

Modifier 9.39 14.78 D i Bulk 88 59 Conductivity S/cm Density 1.78 1.75 1.71 1.71 1.71 g/cm3 Shrink mils/in-1.5 -1.25 -1.25 -1.67 -1.67 Table 5D
Component 23594 23721 23722 23723 23724_ ', Resin D 100 100 100 100 100 Initiator 2.07 2.19 2.24 1.94 2.00 B

Inhibitor 0.52 0.55 0.56 0.48 0.50 Release 6.22 6.57 6.71 5.82 6.00 , Agent Graphite 388.6 410.51 419.23 354.03 365.18 A

Modifier 27.53 30.24 22.70 26.56 B ',, Modifier 20.73 D

Bulk 86 93 68 65 Conductivity S/cm ' Density 1.71 1.74 I 1.77 1.77 1.78 i ~,, g/cm3 Shrink mils/in-1.25 -1.42 -1.08 -1.5 -1.25 Table 6A
Component 23725 23726 23727 23728 23729 Resin D 100 100 100 100 100 Initiator 2.14 1.90 2.14 1.90 2.14 B

Inhibitor 0.54 0.48 0.54 0.48 ' 0.54 Release 6.43 5.71 6.43 5.71 6.43 I, Agent i Graphite 402.14 347.62 I
D

Graphite 402.14 347.62 E

Graphite 402.14 F

Modifier 24.93 20.48 24.93 20.48 ~ 24.93 B I~

Bulk 96 75 81 62 I
Conductivity I
S/cm Density 1.77 1.78 1.81 1.8 g/cm3 Shrink mils/in-1.67 -2.33 -0.83 -1 I

Table 6B
Component 23730 23731 23732 23733 23734 Resin D 100 100 100 100 100 Initiator 1.90 2.14 1.90 2.14 2.14 B

Inhibitor 0.48 0.54 0.48 0.54 0.54 Release 5.71 6.43 5.71 6.43 6.43 i Agent Graphite 249.33 249.33 A

Graphite 152.82 I
E

Graphite 347.62 152.82 F ~~

Graphite 402.14 347.62 I I
G

Modifier 20.48 24.93 I 20.48 24.93 24.93 B I

Bulk 32 30 48 ~, 25 Conductivity S/cm Density 1 '81 1 '81 g/cm3 Shrink mils/in -1.33 -1.83 I, Table 6C
Component 23735 23736 23737 23738 23739 , Resin D 100 100 100 100 100 i Initiator 2.14 2.14 1.90 1.90 1.90 B

Inhibitor 0.54 0.54 0.48 0.48 0.48 I

Release 6.43 6.43 5.71 5.71 5.71 Agent Graphite 249.33 249.33 215.52 215.52 215.52 A ~ I

Graphite 152.82 D

Graphite E i 132.10 Graphite 152.82 132.10 i F

Graphite 152.82 132.10 G ' Modifier 24.93 24.93 '~ 20.4820.48 20.48 B

Bulk 38 90 ; 50 26 31 Conductivity I
S/cm Density 1.79 1.67 1.79 1.8 1.8 I, 'i g/cm3 Shrink mits/in-2.08 -1.58 -1.83 -2.33 -2.67 ~I

Table 6D
Component 23740 23755 23756 23757 23758 Resin D 100 100 100 100 100 Initiator 1.90 2.17 2.20 1.93 1.95 !, B

Inhibitor 0.48 0.54 0.55 0.48 0.49 Release 5.71 6.52 6.61 5.78 5.85 Agent Graphite 215.52 407.61 413.22 341.81 356.10 A ~, Graphite 132.10 D i Modifier 20.48 23.91 22.87 19.52 l B I 18.54 Modifier 2.72 5.51 2.41 4.88 D

Bulk 68 70 97 92 89 i Conductivity S/cm Density 1.75 1.77 1.67 1.79 1.79 i g/cm3 Shrink mils/in-1.83 -1.83 -1.83 -2 -2.17 I, Table 7A
Component 23803 23804 23805 23806 23830 Resin D 100 100 100 100 100 Initiator 2.06 2.09 2.16 2.19 2.16 B

Inhibitor 0.52 0.52 0.54 0.55 0.54 I

Release 6.19 6.27 6.49 6.58 6.49 i Agent Graphite 376.29 381.20 394.59 405.48 394.59 A ;

Modifier 25.26 25.59 25.59 26.30 30.00 B

Modifier 5.15 6.53 10.81 6.85 6.76 E

Bulk 62 83 83 90 ~ I
i Conductivity S/cm Density 1.77 1.77 1.76 1.77 1.79 i g/cm3 I

Shrink mils/in-1.83 -1.50 , -1.33 -1.67 -1.58 ~, Table 7B
Component 23831 23832 23833 23834 23835 Resin D 100 100 100 100 100 Initiator 2.11 2.18 2.23 2.09 2.09 I
B ~
' Inhibitor 0.53 0.54 0.56 0.52 0.52 Release 6.33 6.54 6.69 6.27 6.27 Agent Graphite 385.22 397.82 406.69 A

Graphite 381.20 H

Graphite 381.20 I

Modifier 25.59 25.61 25.63 25.59 25.59 B

Modifier 6.81 6.96 6.53 6.53 E

Density 1.74 1.76 1.72 g/cm3 Shrink mils/in-1.42 -1.33 ~ -1.25 Table 7C
Component 23836 23837 23838 23839 23840 Resin D 100 100 100 100 100 Initiator 2.09 2.24 2.24 2.24 2.24 B

Inhibitor 0.52 0.56 0.56 0.56 0.56 Release 6.27 6.71 6.71 6.71 6.71 Agent Graphite 408.28 408.28 408.28 408.28 A I

Graphite 381.20 i J

Carbon B 0.56 Carbon C 0.56 Carbon D 0.56 Carbon E 0.56 Modifier 25.59 25.56 25.56 25.56 25.56 B

Modifier 6.53 6.99 6.99 6.99 6.99 E

Modifier 8.39 8.39 8.39 8.39 I
F I

Densit 1.77 1.80 1.76 1.74 Y I
glcm3 Shrink mils/in -1.08 -0.92 -1.17 -1.08 Table 7D
Component 23878 23879 23880 23881 23896 I

Resin D 100 100 100 100 100 Initiator 2.26 2.37 2.28 2.39 1.48 B

Inhibitor 0.57 0.59 0.57 0.60 0.49 I

Release 6.79 7.11 6.83 7.16 5.93 Agent , Graphite 418.55 444.31 421.41 447.49 370.74 A I, Modifier 25.57 25.59 25.57 25.60 5.68 B

Modifier 9~9g ' C i Modifier ~ 7.12 7.46 I
E

Modifier 11.88 12.44 5.69 ' 5.97 F

Table 8A
Component 23297 23301 23363 23422 23302 t I

Resin E 100 ~ 100 100 100 Initiator 1.56 1.38 1.06 1.75 i B ', 1.33 I

Inhibitor 0.52 0.46 0.44 0.35 0.58 Release 6.24 5.50 5.31 4.24 7.00 Agent ~ I

Graphite 395.22 343.88 331.86 240.03 466.74 A I

Modifier 5.98 2.66 1.28 2.65 2.68 B

Modifier 10.50 4.63 2.26 4.66 4.67 C

Bulk 72.5 35 Conductivity S/cm Density 1.62 1.53 1.6 g/cm3 Shrink mils/in -2.33 -1.33 -0.92 Table 8B
Component 23423 23452 23453 23454 23455 Resin D 50.03 60.00 70.03 80.00 !

Resin E 100 I ' Resin F 49.97 40.00 29.97 20.00 ~, !, Initiator 2.40 2.14 ~ 2.14 2.14 2.14 B

Inhibitor 0.80 0.54 0.54 0.54 0.54 Release 9.61 6.43 6.43 6.43 6.43 i Agent Graphite 680.54 402.14 402.14 402.14 402.14 A , I
~

Modifier 2.64 24.93 24.93 24.93 24.93 B , ' Modifier 4.64 ' C I

Bulk 63 70.5 70 83.5 Conductivity I ' S/cm Tensile 2441 2497 2404 2561 psi Flexural 5030 5126 j 4284 5391 psi Density 1.47 1.71 1.74 1.75 1.66 i g/cm3 j Shrink mils/in-0.25 -1.17 -1.58 -1.67 -1.42 i Table 8C
Component 23530 23531 23646 23647 23648 Resin F 100 100 Resin G 100 100 100 Initiator 1.85 1.79 1.81 1.91 2.02 B

Inhibitor 0.46 0.45 0.45 0.48 0.50 I

Release 5.54 5.38 5.42 5.72 6.06 I
i Agent I

Graphite 346.42 336.32 338.75 357.65 378.60 A

Modifier 5.24 11.11 17.62 B

Modifier 7.62 4.48 D

Bulk 86 58 I 46 Conductivity I
S/cm Tensile 2305.56 2155.56 psi Flexural 4548.8 ~ 4421.3 ~
psi Density 1.69 1.75 1.71 1.72 1.65 g/cm3 Shrink mils/in-0.42 -1.67 -1.58 -1.42 -1.33 I

Table 8D
Component 23649 23650 23651 23688 Resin D 53.96 Resin I 100 100 100 Resin J 46.04 Initiator 1.75 1.77 I 1.79 B

Initiator 2.08 D

Inhibitor 0.44 0.44 0.45 0.52 Release 5.26 5.31 5.38 6.25 Agent Graphite 328.95 331.86 336.32 385.42 A

Modifier 15.63 B

Modifier 2.19 3.10 4.48 D

Modifier 10.94 F

Bulk 93 79 64 Conductivity S/cm Density 1.77 1.74 i g/cm3 1.73 Shrink mils/in-1.5 -1.08 -1.5 While in accordance with the Patent Statutes, the best mode and preferred embodiment have been set forth, the scope of the invention is not limited thereto, but rather by the scope of the attached claims.

Claims

CLAIMS:

1. A composition comprising:
a) an unsaturated prepolymer resin which comprises one or more of unsaturated polyester and vinyl ester resin;
b) an unsaturated material copolymerizable with said resin and including a terminal ethylene group;
c) at least 50% by total weight of the composition comprising an conductive filler;
d) an initiator to initiate said copolymerization; and e) a theological modifier to prevent phase separation between said resin and said conductive filler during molding, said theological modifier being one or more compositions selected from the group consisting of Group II oxides and hydroxides, carbodiamides, aziridines, polyisocyanates, polytetrafluoro-ethylene, perfluoropolyether, polyethylene and fumed silica.

2. The composition as set forth in claim 1, wherein the theological modifier is from about 0.5 % to about 15 % by total weight of the composition.

3. The composition as set forth in claim 2, wherein the conductive filler is a particulate or flake filler and the amount of said conductive filler is at least 60 Weight percent of the composition.

4. The composition as set forth in claim 3, wherein the conductive filler is a graphite filler and the amount of said conductive filler is at least 65 weight percent of the composition.

5. The composition as set forth in claim 1, wherein said theological modifier comprises magnesium oxide and/or calcium oxide and is from about 0.1 to about 2 weight percent based on the Weight of said composition.

6. The composition as set forth in claim 1, wherein said theological modifier 13. The composition as set forth in claim 12, wherein said initiator is a free radical initiator.

14. The composition as set forth in claim 13, wherein said initiator is selected from the group consisting of peroxides, hydroperoxides, redox systems, diazo compounds, persulfates, and perbenzoates, and is used in amounts of about 0.05 to about 5 weight percent based on the total weight of the composition.

15. The composition as set forth in claim 14, further comprising carbon black.

16. The composition as set forth in claim 14, further comprising reinforcing fillers.

17. An electrochemical cell flow field plate comprising:
a molded thermosetting resin composition having a thickness from about 0.050 to about 0.200 inches and a bulk conductivity of at least 55 S/cm, said molded resin composition being the reaction product of at least:
a) an unsaturated prepolymer resin which comprises one or more of unsaturated polyester and vinyl ester resin;
b) an unsaturated material copolymerizable with said resin and including a terminal ethylene group;
c) at least 50% by total weight of the composition comprising an conductive filler;
d) an initiator to initiate said copolymerization; and e) a rheological modifier to prevent phase separation between said resin and said conductive filler during molding, said rheological modifier being one or more compositions selected from the group consisting of Group II oxides and hydroxides, carbodiamides, aziridines, polyisocyanates, polytetrafluoro-ethylene, perfluoropolyether, polyethylene, and fumed silica.

18. The electrochemical cell flow field plate as set forth in claim 17, wherein said rheological modifier is from about 0.5 % to about 15 % by total weight of the composition.

19. The electrochemical cell flow field plate as set forth in claim 18, wherein the conductive filler is a particulate filler and the amount of said conductive filler is at least 60 weight percent of the composition.

20. The electrochemical cell flow field plate as set forth in claim 19, wherein the filler is a graphite filler and the amount of said conductive filler is at least 65 weight percent of the composition.

21. The electrochemical cell flow field plate as set forth in claim 17, wherein said rheological modifier comprises magnesium oxide and/or calcium oxide and is from about 0.1 to about 2 weight percent based on the weight of said composition.

22. The electrochemical cell flow field plate as set forth in claim 17, wherein said rheological modifier is one or more of aziridine and polyisocyanate and is from about 1 to about 10 weight percent based on the weight of said composition.

23. The electrochemical cell flow field plate as set forth in claim 17, wherein said rheological modifier is of an amount to prevent cracking of a part molded at a pressure from about 400 to about 5000 psi and to a thickness of from about 0.050 to about 0.200 inches.

24. The electrochemical cell flow field plate as set forth in claim 17, wherein said modifier comprises one or more of polytetrafluoroethylene, perfluoro-polyether and is from about 0.1 to about 5 weight percent based on the weight of said composition.

25. The electrochemical cell flow field plate as set forth in claim 17, wherein comprising carbon black.

32. The electrochemical cell flow field plate as set forth in claim 30, further comprising reinforcing fillers.

33. A conductive molding composition comprising:
a) 100 parts by weight of an unsaturated prepolymer resin which comprises one or more of unsaturated polyester and vinyl ester resin;
b) an unsaturated monomer selected from the group consisting of styrene, alpha-methyl styrene, chloro-styrene, vinyl toluene, divinyl benzene, diallylphthalate, and methyl methacrylate, and mixture thereof; wherein the ratio of monomers to unsaturated prepolymer resin is from about 40:60 to about 72:25 by weight of the a and b, c) at least about 225 phr of an conductive filler such that a molded product made from said composition has a bulk conductivity of at least about 55 S/cm when measured in accordance with ASTM Test No. F1529-97;
d) from about 0.5 to about 4.0 phr of an initiator to initiate said copolymerization; and e) from about 0.5 to about 20 phr of a rheological modifier which is one or more compositions selected from the group consisting of Group II oxides and hydroxides, carbodiamides, aziridines, polyisocyanates, polytetrafluoro-ethylene, perfluoropolyether, polyethylene, and fumed silica and mixtures thereof.

34. The conductive molding composition as set forth in claim 33, wherein said prepolymer resin is selected from the group consisting of epoxy vinyl resin, bisphenol fumarate resin, modified bisphenol fumarate polyester resin, unsaturated polyester resin, urethane modified vinyl ester resin, urethane-modified vinyl ester resin, bisphenol-epoxy vinylester resin, elastomer-modified vinyl ester resin, epoxy novolac vinyl ester resin and unsaturated isocyanurate vinyl ester resin.

35. The conductive molding composition as set forth in claim 34, wherein the conductive filler is a particulate or flake filler and the amount of said conductive filler is at least 250 phr.

36. The conductive molding composition as set forth in claim 35, wherein the conductive filler is a graphite filler and the amount of said conductive filler is at least 275 phr.

37. The conductive molding composition as set forth in claim 33, wherein said rheological modifier comprises magnesium oxide and/or calcium oxide.

38. The conductive molding composition as set forth in claim 33, wherein said rheological modifier is one or more of aziridine, carbodiamide and polyisocyanate and is from about 0.5 to about 20 phr.

39. The conductive molding composition as set forth in claim 33, wherein said modifier comprises one or more of polytetrafluoroethylene, perfluoropolyether and is from about 0.5 to about 20 phr.

40. The conductive molding composition as set forth in claim 33, wherein said rheological modifier is polyisocyanate and is from about 0.5 to about 20 phr.

41. The conductive molding composition as set forth in claim 33 wherein said copolymerizable material is one or more monomers selected from the group consisting of styrene and methyl methacrylate.

42. The conductive molding composition as set forth in claim 33 wherein said initiator is selected from the group consisting of peroxides, hydroperoxides, redox systems, diazo compounds, persulfates, and perbenzoates, and is used in amounts of about 0.05 to about 20 phr.

43. The conductive molding composition as set forth in claim 42, further comprising carbon black.

44. The conductive molding composition in claim 43, further comprising reinforcing fillers.

45. A molded conductive article comprising a cured reaction product of:
a) 100 parts by weight of an unsaturated prepolymer resin, which comprises one or more of unsaturated polyester and vinyl ester resin;
b) an unsaturated monomer selected from the group consisting of styrene, alpha-methyl styrene, chloro-styrene, vinyl toluene, divinyl benzene, diallylphthalate, and methyl methacrylate, and mixture thereof, Wherein the ratio of monomers to unsaturated prepolymer resin is from about 40:60 to about 72:25 by weight of the two components, c) at least about 225 phr of a conductive filler such that said composition has a bulk conductivity of at least about 55 S/cm when measured in accordance with ASTM Test No. F1529-97;
d) from about 0.5 to about 4.0 phr of an initiator to initiate said copolymerization; and e) from about 0.5 to about 20 phr of a rheological modifier which is one or more compositions selected from the group consisting of Group II oxides and hydroxides, carbodiamides, aziridines, polyisocyanates, polytetrafluoro-ethylene, perfluoropolyether, polyethylene, and fumed silica and mixtures thereof.

46. The molded conductive article as set forth in claim 45, wherein said initiator is selected from the group consisting of peroxides, hydroperoxides, redox systems, diazo compounds, persulfates, and perbenzoates, and is used in amounts of about 0.5 to about 4phr.

47. The molded conductive article as set forth in claim 46, further comprising carbon black.

48. The molded conductive article in claim 46, further comprising reinforcing fillers.

49. The molded conductive product as set forth in claim 45, wherein said unsaturated prepolymer resin is one or more resins selected from the group consisting of epoxy vinyl resin, bisphenol fumarate resin, modified bisphenol fumarate polyester resin, unsaturated polyester resin, urethane modified vinyl ester resin, urethane-modified vinyl ester resin, bisphenol-epoxy vinylester resin, elastomer-modified vinyl ester resin, epoxy novolac vinyl ester resin and unsaturated isocyanurate vinyl ester resin.

50. A method of molding highly loaded polymer Which is a reaction product of a composition comprising:
a) an unsaturated prepolymer resin which comprises one or more of unsaturated polyester and vinyl ester resin;
b) an unsaturated material monomer copolymerizable with said resin and including a terminal ethylene group;
c) at least 50% by total weight of the composition comprising a conductive filler;
d) an initiator to initiate said copolymerization;
said method comprising the addition prior to curing of a rheological agent selected from the group comprising Group II oxides and hydroxides; carbodi-amides; aziridines; polyisocyanates; polytetrafluoroethylene (PTFE); perfluoro-polyether (PFPE), polyethylene, and fumed silica; and subsequently molding said composition under heat and pressure to iniate, cure and form said polymer.

51. The method as set forth in claim 50, wherein said molding is either compression molding or injection molding.
CA002367350A 1999-03-19 2000-03-17 Highly conductive molding compounds and fuel cell bipolar plates comprising these compounds Expired - Fee Related CA2367350C (en)