CA2413355A1 - Soil-resistant coating for glass surfaces - Google Patents

Soil-resistant coating for glass surfaces Download PDF

Info

Publication number
CA2413355A1
CA2413355A1 CA002413355A CA2413355A CA2413355A1 CA 2413355 A1 CA2413355 A1 CA 2413355A1 CA 002413355 A CA002413355 A CA 002413355A CA 2413355 A CA2413355 A CA 2413355A CA 2413355 A1 CA2413355 A1 CA 2413355A1
Authority
CA
Canada
Prior art keywords
water
glass
sheet
sputtering
exterior surface
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CA002413355A
Other languages
French (fr)
Other versions
CA2413355C (en
Inventor
Annette Krisko
Klaus Hartig
Roger D. O'shaughnessy
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Cardinal CG Co
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Publication of CA2413355A1 publication Critical patent/CA2413355A1/en
Application granted granted Critical
Publication of CA2413355C publication Critical patent/CA2413355C/en
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Abstract

A glass article which has a water-sheeting coating and a method of applying coatings to opposed sides of a substrate are described. In one embodiment, a water-sheeting coating 20 comprising silica is sputtered directly onto an exterior surface of the glass. The exterior face of this water-sheeting coating is substantially non-porous but has an irregular surface. This water-sheeting coating causes water applied to the coated surface to sheet, making the glass article easier to clean and helping the glass stay clean longer. In one method of the invention, interior and exterior surfaces of a glass sheet are cleaned. Thereafter, both surfaces are coated with a water-sheeting coating by sputtering silica directly onto the exterior surface of the sheet of glass. If so desired, both the interior surface and the exterior surface can be applied during the same pass through the same sputter coating apparatus while the glass maintains a constant orientation wherein the interior surface is positioned above the exterior surface.

Claims (9)

1. A multi-pane insulated glass unit comprising:
a) first and second panes of glass held in a spaced-apart relationship by a spacer to define a sealed interpane space, the first pane having an exterior surface oriented away from the second pane and exposed to periodic contact with water, the second pane having an interior surface exposed to the interpane space and an exterior surface oriented away from the first pane;
b) a first water-sheeting coating carried on the exterior surface of the first pane; and c) a second water-sheeting coating carried on the exterior surface of the second pane;
the first and second water-sheeting coatings each comprising silica sputtered directly onto the respective surface of the first and second panes and having an exterior face that is substantially non-porous but has an irregular surface, the first and second water-sheeting coatings each reducing the contact angle of water on the respective surface of the first and second panes to below 25~ and causing water applied thereto to sheet.
2. A method of rendering surfaces of a pane of glass resistant to soiling and staining, comprising:
a) providing a sheet of glass having a clean interior surface and a clean exterior surface;
b) sputtering silica directly onto the interior surface of the sheet of glass, thereby yielding a first water-sheeting coating having a contact angle with water below about 25~ which causes water applied to said interior surface to sheet; and c) sputtering silica directly onto the exterior surface of the sheet of glass, thereby yielding a second water-sheeting coating having a contact angle with water below about 25~ which causes water applied to said exterior surface to sheet.
3. The method of claim 2 further comprising exposing one of the interior and exterior surfaces of the sheet of glass to periodic contact with water, the water-sheeting coating on the exposed surface reducing soiling and staining that would otherwise result from the periodic contact with water.
4. The method of claim 2 wherein the first and second wafer-sheeting coatings are sputtered from a silicon target in an oxygen-containing sputtering chamber.
5. A method of coating two sides of a pane of glass in a single pass through a coating apparatus, comprising:
a) providing a sheet of glass having a clean first surface and a clean second surface;
b) providing a sputtering chamber having a plurality of rollers that define a substrate support therein, the chamber having an upper target positioned above the support and being adapted to downwardly sputter, the chamber having a lower target positioned below the support and being adapted to upwardly sputter;
c) positioning the sheet of glass in the chamber such that the first surface of the sheet of glass rests on one or more of the rollers and is oriented toward the lower target, whereby the second surface of the sheet of glass is oriented toward the upper target;
d) sputtering the lower target to deposit a first water-sheeting coating on the first surface of the glass, the first water-sheeting coating having a contact angle with water below about 25~ which causes water applied to said first surface to sheet; and e) sputtering the upper target to deposit a second water-sheeting coating on the second surface of the glass, the second water-sheeting coating having a contact angle with water below about 25~ which causes water applied to said second surface to sheet.
6, The method of claim 5 wherein the upper and lower targets are sputtered substantially simultaneously.
7. The method of claim 5 wherein the upper and lower targets comprise silicon and are sputtered in an oxidizing atmosphere.
8. A method of rendering a glass surface resistant to soiling and staining, comprising:
a) providing a sheet of glass having a clean interior surface and a clean exterior surface;
b) providing a sputtering line comprising a series of sputtering chambers, each sputtering chamber having a plurality of rollers that define a substrate support, the sputtering line having an upward sputtering chamber with a lower target positioned below the rollers in that chamber;
c) positioning the sheet of glass in the upward sputtering chamber such that the exterior surface of the sheet of glass rests on two or more of the rollers in that chamber; and d) sputtering the lower target to deposit silica directly onto the exterior surface of the glass, thereby yielding a water-sheeting coating having a contact angle with water below about 25~ which causes water applied to the exterior surface to sheet, the sputtered silica travelling between said two or more rollers before being deposited on the exterior surface of the sheet of glass.
9. The method of claim 8 wherein the lower target comprises silicon and is sputtered in an oxidizing atmosphere.
CA2413355A 2000-06-21 2001-06-19 Soil-resistant coating for glass surfaces Expired - Lifetime CA2413355C (en)