CN1127772A - Water stereo colour paint - Google Patents
Water stereo colour paint Download PDFInfo
- Publication number
- CN1127772A CN1127772A CN 95110629 CN95110629A CN1127772A CN 1127772 A CN1127772 A CN 1127772A CN 95110629 CN95110629 CN 95110629 CN 95110629 A CN95110629 A CN 95110629A CN 1127772 A CN1127772 A CN 1127772A
- Authority
- CN
- China
- Prior art keywords
- water
- pigment
- slurry
- ethylene glycol
- add
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The multi-colour paint composition for decoration of building wall mainly contains titanium oxide, prepicitated calcium carbonate, carboxymethylcellulose, hydroxypropylcellulose, borax, sodium sulfate, sodium chloride, glycol, polyvinyl acetate emulsion, mica powder, metallic powder, pigment and water, and features no damage to human body, high adhesion and hardness, resisting acid, alkali and ageing, good stability for storage, and strong 3-D effect.
Description
The present invention relates to a kind of coating composition, particularly a kind of water stereo colour paint.
Coating of multi-colour pattern is generally popular in countries in the world, China introduces this technology and equipment from Japanese Northwest paint company and produces from the later stage eighties, its product has become on the domestic construction market upsurge kind in the ornamental building coating, this coating is with its elegance, abrasion resistance globality and the fashionable Jin nation of weather resistance face, universal gesture is arranged greatly, but this coating is oil bag oil and oil-in-water-type coating of multi-colour pattern, it has adopted a large amount of benzene, ether, virulent solvent such as nitro-cotton, that gives people healthyly brings very big influence, not only produce, the constructor is injured, and the occupant also deeply hurts, this coating uses nitro-cotton and a large amount of materials such as organic solvent in addition, so it is inflammable and explosive, smell is big, toxicity is big, serious environment pollution, present flourishing consanguinity generally bans use of, also ban use of in succession in China part big and medium-sized cities, various countries' successive turn is studied the Water-borne modification coating of multi-colour pattern for this reason, and the aqueous colorful pattern coating of having developed at present all exists the product cost height, starting material are bought difficulty, and its investment of production equipment is big, and product shelf life is short.Defectives such as facing difference of hardness are difficult to apply.
The object of the present invention is to provide a kind of nontoxicity, stereoscopic sensation is strong, cohesiveness good, hardness is high, water-fastly wash, less investment, cost is low, the storage time is long water stereo colour paint.
Task of the present invention is finished with following mode: a kind of water stereo colour paint, mainly form by titanium dioxide, light calcium carbonate, carboxymethyl cellulose, hydroxypropylcellulose, borax, sodium sulfate, sodium-chlor, ethylene glycol, polyvinyl acetate emulsion, mica powder, metal powder and pigment and water; Its weight percent is: titanium dioxide 3-10, light calcium carbonate 2-8, carboxymethyl cellulose 1-2, hydroxypropylcellulose 0.1-1, borax 0.5-5, sodium sulfate 0.5-3, sodium-chlor 0.1-1, ethylene glycol 1-10, polyvinyl acetate emulsion 3-15, mica powder 0.2-5, metal powder 0.3-3, pigment 0.4-0.6, water 40-60.The optimum formula weight percent of coating is: titanium dioxide 8, light calcium carbonate 6, carboxymethyl cellulose 1.5, hydroxypropylcellulose 0.5, borax 2.5, sodium sulfate 2.4, sodium-chlor 0.8, ethylene glycol 9.8, polyvinyl acetate emulsion 13, mica powder 4.6, metal powder 0.48, pigment 0.42 and water 50 are formed.Pigment is to be mixed by two or more pigment to constitute.Claim to join raw material in proportion, evenly promptly get the A slurry with stirring to block in carboxymethyl cellulose and borax and the water adding reactor at normal temperatures; After afterwards the adding polyvinyl acetate emulsion stirs with stirring in water and the Cornstarch adding reactor, add ethylene glycol again, stir and promptly get the B slurry, with hydroxypropylcellulose, sodium sulfate and sodium chloride solution mix C slurry, mica powder, metal powder, pigment and ethylene glycol mixed promptly get D slurry, with above-mentioned make A slurry and B slurry add to stir in the reactor and block even back and add C liquid, add again and add D again after tired matter lime carbonate stirs and starch.
Water stereo colour paint cementability of the present invention is strong, sticking power 100%, water-fast washing greater than 6000 times, facing is washed not dry linting repeatedly, colour-fast, the foul that is coated with on the facing can be washed as newly, acid and alkali-resistance, and weather changes, flame retardant properties is good, anti-aging, cover with paint, lacquer, colour wash, etc. the surface hardness height, anti-collision, anti-portrayal, with short production cycle, comparable existing coating of multi-colour pattern shortens for 2/3 man-hour, and this coating is stable is stored in more than 12 months, its facing is bright in luster, the stereoscopic sensation that extra-heavy is arranged, elegant style, facing are color spot distribution, decorative pattern is obvious, in a great variety, construction is simple, and is convenient, this coating does not with an organic solvent wait objectionable impurities, nontoxic, tasteless, "dead", do not have any environmental pollution, life-time service is harmless to the person, produces " the no three wastes ", the starting material wide material sources, convenient transportation, cost is low, only is 1/5 of oiliness coating of multi-colour pattern, small investment of production equipment, the used starting material of this coating do not have any corrodibility to equipment, can save expensive enamel reaction still and the anti-still of stainless steel, and this product can be widely used in the wall fitting of public place buildings and luxurious hotel dwelling house.
Below the present invention is further detailed explanation:
The embodiment of the invention: at first claim to join starting material, claim that by weight percentage joining starting material is: titanium dioxide 8, light calcium carbonate 6, carboxymethyl cellulose 1.5, hydroxypropylcellulose 0.5, borax 2.5, sodium sulfate 2.4, sodium-chlor 0.8, ethylene glycol 9.8, polyvinyl acetate emulsion 13, mica powder 4.6, metal powder 0.48, pigment 0.42 and water 50.After claiming to prepare above-mentioned raw materials, carry out following substep preparation work, at first with starting stirrer in carboxymethyl cellulose and borax and the water adding reactor, after making it to stir, promptly get the A slurry and pour out standby at normal temperatures; Second step was that an amount of water is added in the reactor, start stirrer after, add the titanium dioxide back that stirs and add polyvinyl acetate emulsion and stir, add ethylene glycol again, promptly get after stirring B starch pour out standby; The 3rd step was with hydroxypropylcellulose and sodium sulfate, sodium chloride solution mix C liquid, the 4th step was mica powder, metal powder, pigment and ethylene glycol to be mixed promptly get the D slurry, the 5th step was the A of above-mentioned preparation slurry and B slurry to be added to stir in the reactor successively block even back adding C liquid, adding light calcium carbonate again stirs then and to filter, remove its moisture, get product.The 6th step was the water that adds identical weight by the weight of above-mentioned finished product, and mix D liquid and can pack warehouse-in, this coating can be determined color according to the design of decorative pattern colour table, this coating can be by the above-mentioned finished product that obtains, dissolve the water of identical weight at the construction field (site), add packing D liquid going along with again, after stirring, once spray the construction surface with compressor and spray gun by the constructional method of oil spout lacquer, can form the multicolour pattern facing.
Claims (4)
1. a water stereo colour paint is characterized in that mainly being made up of titanium dioxide, light calcium carbonate, carboxymethyl cellulose, hydroxypropylcellulose, borax, sodium sulfate, sodium-chlor, ethylene glycol, polyvinyl acetate emulsion, mica powder, metal powder and pigment and water; Its weight percent is: titanium dioxide 3-10, light calcium carbonate 2-8, carboxymethyl cellulose 1-2, hydroxypropylcellulose 0.1-1, borax 0.5-5, sodium sulfate 0.5-3, sodium-chlor 0.1-1, ethylene glycol 1-10, polyvinyl acetate emulsion 3-15, mica powder 0.2-5, metal powder 0.3-3, pigment 0.4-0.6, water 40-60.
2. according to the described water-bearing type solid paint of claim 1, it is characterized in that the optimum formula weight percent of coating is: titanium dioxide 8, light calcium carbonate 6, carboxymethyl cellulose 1.5, hydroxypropylcellulose 0.5, borax 2.5, sodium sulfate 2.4, sodium-chlor 0.8, ethylene glycol 9.8, polyvinyl acetate emulsion 13, mica powder 4.6, metal powder 0.48, pigment 0.42 and water 50 are formed.
3. according to the described water stereo colour paint of claim 1, it is characterized in that pigment is to be mixed by two or more pigment to constitute.
4. the manufacture method of a water stereo colour paint is characterized in that claiming to join raw material in proportion evenly promptly gets the A slurry with stirring to block in carboxymethyl cellulose and borax and the water adding reactor at normal temperatures; After afterwards the adding polyvinyl acetate emulsion stirs with stirring in water and the Cornstarch adding reactor, add ethylene glycol again, stir and promptly get the B slurry, with hydroxypropylcellulose, sodium sulfate and sodium chloride solution mix C slurry, mica powder, metal powder, pigment and ethylene glycol mixed promptly get D slurry, with above-mentioned make A slurry and B slurry add the back that stirs in the reactor and add C liquid, add again and add D after light calcium carbonate stirs again and starch.