DE19834487A1 - Non-woven organic fiber fleece containing 0.1-2 wt.% of a soluble polymer having a viscosity average mol. wt. of at least 1,000,000 is useful for the absorption of organic liquids. - Google Patents

Non-woven organic fiber fleece containing 0.1-2 wt.% of a soluble polymer having a viscosity average mol. wt. of at least 1,000,000 is useful for the absorption of organic liquids.

Info

Publication number
DE19834487A1
DE19834487A1 DE19834487A DE19834487A DE19834487A1 DE 19834487 A1 DE19834487 A1 DE 19834487A1 DE 19834487 A DE19834487 A DE 19834487A DE 19834487 A DE19834487 A DE 19834487A DE 19834487 A1 DE19834487 A1 DE 19834487A1
Authority
DE
Germany
Prior art keywords
polymer
organic
fibers
organic liquids
fleece
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
DE19834487A
Other languages
German (de)
Inventor
Wolfgang Immel
Steffen Immel
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SPEZIAL POLYMER LEUNA GmbH
Original Assignee
SPEZIAL POLYMER LEUNA GmbH
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SPEZIAL POLYMER LEUNA GmbH filed Critical SPEZIAL POLYMER LEUNA GmbH
Priority to DE19834487A priority Critical patent/DE19834487A1/en
Publication of DE19834487A1 publication Critical patent/DE19834487A1/en
Withdrawn legal-status Critical Current

Abstract

A felt/fleece (I) for the adsorption of organic liquids(II) contains (A) inorganic or organic fibers and (B) 0.1-2 wt.% of a polymer having a viscosity average mol. wt. of at least 1,000,000 that is soluble in (II). An Independent claim is included for a process for the adsoption of (II) by contacting (II) with (I) for 5-10 minutes before removal of (I).

Description

Die vorliegende Erfindung betrifft Vliese zur Adsorption von organischen Flüssigkeiten, enthaltend anorganische oder organische Fasern (A) und 0,1 bis 2,0 Gew.-%, bezogen auf die gesamte Zusammensetzung, eines in solchen organischen Flüssigkeiten löslichen Polymeren (B) mit einem Molekulargewicht (Viskositätsmittel Mv) von wenigstens 1.000.000.The present invention relates to nonwovens for the adsorption of organic liquids, containing inorganic or organic fibers (A) and 0.1 to 2.0 wt .-%, based on the total composition, a polymer soluble in such organic liquids (B) with a molecular weight (viscosity average Mv) of at least 1,000,000.

Es ist bekannt, nicht gewebte Fasern, zum Beispiel aus Polypropylen, Zellulose, Polyurethan, Baumwolle und Textilfasern zur Adsorption von Öl und Kohlenwasserstoffen auf Wasser und auf festen Oberflächen zu verwenden. Für den praktischen Einsatz werden daraus Vliese, Schläuche, Kissen, Matten, perforierte Matten, Saugstrümpfe, Flocken, Binden zum Abdichten von Leckagen und Netzschläuche hergestellt.It is known to use non-woven fibers, for example made of polypropylene, cellulose, polyurethane, Cotton and textile fibers for the adsorption of oil and hydrocarbons on water and to be used on solid surfaces. For practical use, nonwovens, Hoses, pillows, mats, perforated mats, absorbent stockings, flakes, bandages for sealing of leaks and mesh tubing.

Es ist ferner bekannt, hochmolekulare Polymere, beispielsweise Polyisobutylen, zur Bekämpfung unkontrollierter Ölausschüttungen auf Wasser zu verwenden. Dabei vermischt man zweckmäßigerweise diese hochmolekularen Polymere als Pulver, oder bereits in geeigneten organischen Lösungsmitteln gelöst, mit Wasser und sprüht dieses Gemisch mit Hilfe einer Wasserkanone oder anderen Sprüheinrichtungen auf die mit Öl verunreinigte Wasseroberfläche auf. Dabei löst sich das hochmolekulare Polymere im Öl und bildet einen viskoelastischen Film, der mit Skimmern und Vliesen oder Füllmaterial, z. B. aus nicht gewebten Polypropylenfasern, leicht entfernt werden kann.It is also known to use high molecular weight polymers, for example polyisobutylene Combat uncontrolled oil spills on water. Mixed up one expediently these high molecular weight polymers as powder, or already in Suitable organic solvents dissolved with water and sprayed this mixture with the help a water cannon or other spray device on the one contaminated with oil Water surface. The high molecular polymer dissolves in the oil and forms one viscoelastic film with skimmers and fleeces or filler, e.g. B. not woven polypropylene fibers, can be easily removed.

In der US-A 5,030,591 wird ein Verfahren zur Entfernung von organischen Flüssigkeiten wie beispielsweise Ölen auf festen Oberflächen beschrieben, wobei man einen adsorbierenden Feststoff mit mindestens 2 Gew.-%, bezogen auf die gesamte Zusammensetzung, eines fein verteilten Polymeren, welches in organischen Flüssigkeiten löslich ist, vermischt. Das dabei eingesetzte Polymere ist hochmolekular. Die erhaltene Mischung wird als Pulver auf die organischen Flüssigkeiten aufgetragen, mit diesen vermengt und anschließend gemeinsam mechanisch entfernt. Als adsorbierender Feststoff werden Sägemehl, Holzfasern, gemahlene Maisstrünke und granulierte Torifasern angeführt. Das Polymere ist ein Polyisobutylen mit einem Molekulargewicht (Viskositätsmittel Mv) von mindestens 1.000.000.US-A 5,030,591 describes a method for removing organic liquids such as For example, described oils on solid surfaces, using an adsorbent Solid with at least 2 wt .-%, based on the entire composition, one fine distributed polymers, which is soluble in organic liquids. That included The polymer used is high molecular weight. The mixture obtained is powdered on the organic liquids applied, mixed with them and then together mechanically removed. Sawdust, wood fibers and ground are used as the adsorbing solid Corn stalks and granulated tori fibers listed. The polymer is a polyisobutylene a molecular weight (viscosity average Mv) of at least 1,000,000.

Aus der DE-A 197 27 363.7 ist bekannt, daß Mischungen aus getrockneten und calcinierten Montmorilloniten, Sepiolithen und Atapulgit mit einer Korngröße von 0,1-2 mm und 0,1-­ 1,5% eines Polyisobutylenpulvers mit einem Molekulargewicht (Viskositätsmittel Mv) von mindestens 1.000.000 und einer Korngröße von mindestens 50µ, besonders geeignet sind, organische Flüssigkeiten wie Benzin, Dieselöle, Hydrauliköle, Erdöl, Paraffinöl, Benzol, Toluol oder auch halogenierte Derivate von flüssigen Kohlenwasserstoffen und andere organische Kohlenwasserstoffe, in denen das Polymere löslich ist, mechanisch zu entfernen. Dabei wurde besonders auf die durch das Polymere störende Fadenbildung in Kontakt zu den zu entfernenden organischen Lösungsmitteln hingewiesen, die besonders bei Polymerkonzen­ trationen von über 2 Gew.-% auftritt und die die mechanische Entfernung erschwert.From DE-A 197 27 363.7 it is known that mixtures of dried and calcined Montmorillonites, sepiolites and atapulgite with a grain size of 0.1-2 mm and 0.1- 1.5% of a polyisobutylene powder with a molecular weight (viscosity average Mv) of at least 1,000,000 and a grain size of at least 50µ are particularly suitable, organic liquids such as gasoline, diesel oils, hydraulic oils, petroleum, paraffin oil, benzene, toluene or also halogenated derivatives of liquid hydrocarbons and other organic Mechanically remove hydrocarbons in which the polymer is soluble. It was especially the thread formation in contact with the fibers, which is disruptive due to the polymer  removing organic solvents, particularly in the case of polymer concentrates trations of over 2 wt .-% occurs and which complicates the mechanical removal.

Für einige Anwendungsbereiche bei der Entfernung störender organischer Flüssigkeiten, wie zum Beispiel Ölfilmen, ist es wünschenswert, möglichst flache, leicht zu handhabende und gut abdeckende Materialien einsetzen zu können, die die organische Flüssigkeit gut aufsaugen und adsorbieren können. Derartige Materialien sind bislang noch nicht bekannt gewesen, da die bislang beschriebenen Adsorbentien als pulverförmiges Granulat zum Einsatz kommen.For some applications in the removal of disruptive organic liquids, such as For example, oil films, it is desirable to be as flat, easy to use and good as possible to be able to use covering materials that absorb the organic liquid well and can adsorb. Such materials have not yet been known because the Adsorbents described so far can be used as powdered granules.

Der vorliegenden Erfindung Iag daher die Aufgabe zu Grunde, diesem Nachteil abzuhelfen und ein adsorbierendes Vlies zur Verfügung zu stellen, welches leicht auf die mit organischen Flüssigkeiten verunreinigte Oberfläche aufgebracht werden kann. Weiterhin erstreckte sich die vorliegende Erfindung auch auf ein Verfahren zur Herstellung derartiger adsorbierender Vliese sowie auf ein Verfahren zur Adsorption von organischen Flüssigkeiten und auf die Verwendung der adsorbierenden Vliese als Sperrschichten gegen das weiter Ausbreiten von organischen Flüssigkeiten.The present invention is therefore based on the object of remedying this disadvantage and to provide an absorbent fleece that is easily matched to those with organic Liquids contaminated surface can be applied. Furthermore, the The present invention also relates to a method for producing such absorbent nonwovens as well as a process for the adsorption of organic liquids and on the Use of the absorbent nonwovens as barrier layers against the further spreading of organic liquids.

Demgemäß wurde ein Vlies zur Adsorption von organischen Flüssigkeiten gefunden, enthaltend anorganische oder organische Fasern (A) und 0,1 bis 2,0 Gew.-%, bezogen auf die gesamte Zusammensetzung, eines in solchen organischen Flüssigkeiten löslichen Polymeren (B) mit einem Molekulargewicht (Viskositätsmittel Mv) von wenigstens 1.000.000.Accordingly, a fleece for the adsorption of organic liquids was found containing inorganic or organic fibers (A) and 0.1 to 2.0 wt .-%, based on the total composition, a polymer soluble in such organic liquids (B) with a molecular weight (viscosity average Mv) of at least 1,000,000.

Unter der Bezeichnung Vlies sollen dabei auch Matten, Binden oder Saugstrümpfe verstanden werden.The term fleece is also understood to mean mats, sanitary napkins or absorbent stockings become.

Als anorganische oder organische Fasern (A) werden vor allem Polypropylen, Zellulose, Polyurethane, Baumwolle und Textilfasern verwendet, wobei Polypropylenfasern bevorzugt sind. Derartige Fasern weisen insbesondere eine Faserlänge von mindestens 1 mm auf. Vorzugsweise werden nicht gewebte Fasern (A) eingesetzt.In particular, polypropylene, cellulose, Polyurethanes, cotton and textile fibers are used, with polypropylene fibers being preferred are. Such fibers in particular have a fiber length of at least 1 mm. Non-woven fibers (A) are preferably used.

Bezogen auf die gesamte Zusammensetzung enthalten die erfindungsgemäßen Vliese ferner 0,1 bis 2,0 Gew.-%, insbesondere 0,1 bis 1,9 Gew.-% und besonders bevorzugt 0,1 bis 1,5 Gew.- % eines in organischen Flüssigkeiten löslichen Polymeren (B).Based on the overall composition, the nonwovens according to the invention also contain 0.1 up to 2.0% by weight, in particular 0.1 to 1.9% by weight and particularly preferably 0.1 to 1.5% by weight % of a polymer soluble in organic liquids (B).

Dieses weist ein Molekulargewicht (Viskositätsmittel Mv) von mindestens 1.000.000, insbesondere von mindestens 2.000.000 und besonders bevorzugt von mindestens 5.000.000 auf.This has a molecular weight (viscosity average Mv) of at least 1,000,000, in particular of at least 2,000,000 and particularly preferably of at least 5,000,000 on.

Das Viskositätsmittel Mv wird aus der Lösungsviskosität einer Lösung des Polymeren (B) in Isooctan bei 20°C nach DIN 53728 bestimmt. Als Meßgerät dient ein Ubbelohde- Viskosimeter. Das Viskositätsmittel Mv errechnet sich aus der Formel
The viscosity agent Mv is determined from the solution viscosity of a solution of the polymer (B) in isooctane at 20 ° C. according to DIN 53728. An Ubbelohde viscometer serves as the measuring device. The viscosity average Mv is calculated from the formula

Die Ermittlung des zur Bestimmung des Viskositätsmittels Mv benötigten Staudingerindex Jo erfolgt nach der Schulz-Blaschke-Beziehung aus der gemessenen Grenzviskosität η und der Lösungskonzentration.The determination of the Staudinger index Jo required for determining the viscosity agent Mv follows the Schulz-Blaschke relationship from the measured intrinsic viscosity η and the Solution concentration.

Vorzugsweise wird das Polymere (B) als Polymerpulver mit einer Teilchengröße von mindestens 50 µm, insbesondere von mindestens 100 µm, verwendet.The polymer (B) is preferably used as a polymer powder with a particle size of at least 50 microns, especially at least 100 microns used.

Das in der erfindungsmäßigen Zusammensetzung vorliegende Polymere (B) muß in den organischen Flüssigkeiten, die adsorbiert werden sollen, löslich sein. Beispiele für solche Polymere (B) sind hochmolekulare Polyisobutylene, Polyisoprene, Polybutadiene und andere kautschukartige Polymere, die sowohl als Homo- als auch als Copolymere verwendet werden können. Deren Viskositätsmittel Mv sollte mindestens 1.000.000, vorzugsweise 2.000.000 betragen und so hoch sein, daß sie einer organischen Flüssigkeit, in der sie gelöst sind, viskoelastische Eigenschaften verleihen. Derartige Polymere (B) sind im Handel erhältlich. Das als Polymeres (B) besonders bevorzugt verwendete hochmolekulare Polyisobutylen wird durch kationische Polymerisation von Isobutylen bei tiefen Temperaturen hergestellt. Es kann auch unter der Marke OPPANOL B® von der BASF Aktiengesellschaft bezogen werden.The polymer (B) present in the composition according to the invention must be in the organic liquids that are to be adsorbed are soluble. Examples of such Polymers (B) are high molecular weight polyisobutylenes, polyisoprenes, polybutadienes and others rubbery polymers which are used both as homo- and as copolymers can. Their viscosity agent Mv should be at least 1,000,000, preferably 2,000,000 and be so high that they are an organic liquid in which they are dissolved, impart viscoelastic properties. Such polymers (B) are commercially available. The high molecular weight polyisobutylene used as polymer (B) is particularly preferred cationic polymerization of isobutylene produced at low temperatures. It can also can be obtained from BASF Aktiengesellschaft under the OPPANOL B® brand.

Vorzugsweise wird Polyisobutylenpulver mit einem Molekulargewicht (Viskositätsmittel Mv) von mindestens 1.000.000, insbesondere von mindestens 2.000.000 und besonders bevorzugt von mindestens 5.000.000 und einer Korngröße von mindestens 50µ, insbesondere von mindestens 100µ, mit bis zu 2 Gew.-% in das nicht gewebte Fasermaterial, beispielsweise aus einem Polypropylen, untergemischt.Polyisobutylene powder with a molecular weight (viscosity average Mv) is preferably used. of at least 1,000,000, in particular of at least 2,000,000 and particularly preferred of at least 5,000,000 and a grain size of at least 50µ, in particular of at least 100μ, with up to 2 wt .-% in the non-woven fiber material, for example a polypropylene, mixed.

Überraschenderweise konnte durch die viskoelastischen Eigenschaften des Polyisobutylens in Verbindung mit den Fasern eine noch intensivere Entfernung der organischen Lösungsmittel auf festem Boden und insbesondere auf Wasser festgestellt werden.Surprisingly, the viscoelastic properties of polyisobutylene in Connection with the fibers an even more intensive removal of the organic solvents be found on firm ground and especially on water.

Damit das Polymere (B) direkt mit den aufzunehmenden organischen Flüssigkeiten, beispielsweise auf Wasser, in Berührung kommt, wird das aus vorzugsweise nicht gewebten Fasern hergestellte Vlies zunächst mit einem wasserlöslichen Kleber, im speziellen mit einem Kleber auf Ethylvinylacetat-Basis, beschichtet und anschließend das Polymere (B) in Pulverform aufgestreut. Zusätzlich kann der Kleber eingefärbt werden, sodaß man für die praktische Anwendung leicht die Seite, auf der sich das Polymere (B) befindet, erkennen kann. Auf diese Weise ist das erfindungsgemäße Vlies leicht herstellbar.So that the polymer (B) directly with the organic liquids to be absorbed, on water, for example, comes from preferably non-woven Fibers made of fibers first with a water-soluble adhesive, especially with a Ethyl vinyl acetate-based adhesive, coated and then the polymer (B) in Sprinkled in powder form. In addition, the adhesive can be colored, so that one for the practical application can easily recognize the side on which the polymer (B) is located. In this way, the fleece according to the invention is easy to produce.

Durch die direkte Berührung des Polymeren (B) mit dem Film aus organischen Flüssigkeiten bildet sich ein Polymerfilm, der über das aus nicht gewebten Polypropylenfasern hergestellte Vlies rückstandslos von der zu reinigenden Oberfläche, beispielsweise Wasser, abgezogen werden kann.By direct contact of the polymer (B) with the film of organic liquids a polymer film forms over that made from non-woven polypropylene fibers  Non-woven is removed without residue from the surface to be cleaned, for example water can be.

Ebenso überraschend war, daß die aus den nicht gewebten Fasern, insbesondere aus Polypropylen, mit dem Zusatz des Polymeren (B) gefertigten Gegenstände wie Vliese, Matten und Saugstrümpfe eine erheblich verbesserte Sperrwirkung zeigten, die ein Unterlaufen und weiteres Ausbreiten der auslaufenden organischen Flüssigkeiten verhinderte.It was also surprising that the nonwoven fibers, in particular Polypropylene, with the addition of the polymer (B) manufactured objects such as nonwovens, mats and socks showed a significantly improved barrier effect, which undermined and prevented further spreading of the leaking organic liquids.

Diese Sperrwirkung zeigt sich auch besonders wirkungsvoll bei Schlängelleitungen zur Eindämmung von ausgelaufenen organischen Flüssigkeiten auf fließenden Gewässern. Durch die Übertragung der viskoelastischen Eigenschaften des Polymeren (B) auf das Öl während des Eindämmvorganges bildet sich ein zusammenhängender Film, der auch bei etwa 3-5 mal höheren Strömungsgeschwindigkeiten des Gewässers im Vergleich zu Schlängelleitungen, die nicht das Polymere (B) enthalten, noch festgehalten wird.This blocking effect is also particularly effective for snake lines Containment of leaking organic liquids on flowing water. By the transfer of the viscoelastic properties of the polymer (B) to the oil during the Containment process forms a coherent film, which is also about 3-5 times higher flow velocities of the water compared to serpentine lines does not contain the polymer (B), is still held.

Aus nicht gewobenen Fasern, beispielsweise aus Polypropylen, hergestellte ein- und mehrlagige Matten, in denen das Polyisobutylenpulver zwischen den Lagen eingestreut und/oder bereits im Gewebe eingebunden wurde, sind geeignet, den Untergrund von Böden gegen einsickernde organische Flüssigkeiten zu schützen. Dies hat den Vorteil, daß im Ereignisfall je nach Beaufschlagung durch die organischen Flüssigkeiten lediglich die ein- oder mehrlagige Matte ausgetauscht zu werden braucht. Damit erübrigt sich ein kostenintensiver Aushub von kontaminiertem Untergrund.Single and multi-ply made from non-woven fibers such as polypropylene Mats in which the polyisobutylene powder is sprinkled between the layers and / or already in Tissues have been integrated are suitable to prevent the subsoil from seeping in protect organic liquids. This has the advantage that depending on the event Exposure to the organic liquids only the single or multi-layer mat needs to be replaced. This eliminates the need for expensive excavation of contaminated surface.

Es hat sich als besonders vorteilhaft herausgestellt, daß durch den Zusatz des Polymeren (B) bei nicht gewobenen Vliesen bei Wässern, die durch Öl oder andere organische Flüssigkeiten kontaminiert sind, beim Durchfließen der mit dem Polymeren (B) präparierten Vliese, aber auch beim Darüberfließen, der Anteil an organischen Flüssigkeiten aufgrund der übertragenen viskoelastischen Eigenschaften des Polymeren (B) weitgehend zurückgehalten wird.It has proven to be particularly advantageous that the addition of the polymer (B) in the case of non-woven nonwovens in the case of water caused by oil or other organic liquids are contaminated when flowing through the nonwovens prepared with the polymer (B), however even when flowing over, the proportion of organic liquids due to the transferred Viscoelastic properties of the polymer (B) is largely retained.

Ebenso überraschend zeigt sich der Zusatz des Polymeren (B) bei nicht gewobenen Fasern, die als Binden zum Abdichten von organischen Flüssigkeiten, z. B. von Kohlenwasserstoffen, führenden Leitungen verwendet werden. Hier führt der Zusatz des Polymeren (B) dazu, daß sich mit den auslaufenden organischen Flüssigkeiten eine Sperrschicht ausbildet, die ein weiteres Auslaufen des Kohlenwasserstoffs an der Leckage verhindert.The addition of the polymer (B) is also surprising in the case of non-woven fibers as a bandage for sealing organic liquids, e.g. B. of hydrocarbons, leading lines are used. Here the addition of the polymer (B) leads to the fact that a barrier layer forms with the leaking organic liquids, which a prevents further leakage of the hydrocarbon at the leak.

Die zu entfernenden organischen Flüssigkeiten werden erfindungsgemäß dadurch adsorbiert und beseitigt, daß ein anorganische oder organische Fasern (A) enthaltendes Vlies zusammen mit einem in diesen organischen Flüssigkeiten löslichen polymeren (B) eingesetzt wird, wobei man das diese anorganischen oder organischen Fasern (A) und 0,1 bis 2,0 Gew.-% Polymere (B) enthaltende Vlies mit der mit organischen Flüssigkeiten verunreinigten Oberfläche zunächst in Kontakt bringt und nach etwa 5 bis 10 Minuten wieder entfernt. The organic liquids to be removed are thereby adsorbed according to the invention and removes a nonwoven containing inorganic or organic fibers (A) is used with a polymer (B) which is soluble in these organic liquids, where one that these inorganic or organic fibers (A) and 0.1 to 2.0 wt .-% polymers (B) containing fleece with the surface contaminated with organic liquids initially in contact and removed after about 5 to 10 minutes.  

Das erfindungsgemäße Vlies eignet sich insbesondere zur Entfernung von organischen Flüssigkeiten wie Benzin, Diesel, Hydrauliköl, Erdöl, Paraffinöl, Kerosin, Benzol, Toluol oder Xylol. Neben diesen organischen Flüssigkeiten können noch andere flüssige Kohlenwasserstoffe damit wirksam von Wasseroberflächen oder Erdoberflächen beseitigt werden. Weiterhin können die erfindungsgemäßen Vliese auch als Sperrschichten gegen das weitere Ausbreiten von organischen Flüssigkeiten eingesetzt werden. The fleece according to the invention is particularly suitable for removing organic Liquids such as petrol, diesel, hydraulic oil, petroleum, paraffin oil, kerosene, benzene, toluene or Xylene. In addition to these organic liquids, other liquid liquids can be used This effectively removes hydrocarbons from water or earth surfaces become. Furthermore, the nonwovens according to the invention can also act as barrier layers against this further spreading of organic liquids can be used.  

BeispieleExamples Vergleichsbeispiel AComparative Example A

Eine 1 × 1 m große Metallwanne wurde zu 2/3 mit Wasser gefüllt. Anschließend wurde auf die Wasseroberfläche 1 Liter Dieselkraftstoff gegeben.A 1 × 1 m large metal tub was 2/3 filled with water. Subsequently, the Water surface given 1 liter of diesel fuel.

Mit 30 × 50 cm großen Vliestüchern aus nichtgewobenen Polypropylenfasern wurde nun versucht, den ausgeschütteten Dieselkraftstoff aufzunehmen und damit von der Wasser­ oberfläche zu entfernen. Dazu wurden die Vliestücher aus nichtgewobenen Polypropylenfasern zunächst auf die Wasser-Dieselkraftstoff-Oberfläche aufgelegt. Nach 2-3 Minuten war durch Gelbfärbung der Vliestücher erkennbar, daß Dieselkraftstoff durch die Vliestücher aufge­ nommen wurde.With 30 × 50 cm fleece wipes made of non-woven polypropylene fibers was now tries to absorb the spilled diesel fuel and thus from the water remove surface. For this purpose, the non-woven cloths made of non-woven polypropylene fibers first placed on the water-diesel fuel surface. After 2-3 minutes was through Yellowing of the non-woven cloths recognizable that diesel fuel through the non-woven cloths was taken.

Nach Entfernen der Vliestücher von der Wasseroberfläche konnte beobachtet werden, daß sich auf der Wasseroberfläche noch Schlieren befanden, die von nicht durch die Vliestücher aufgesaugtem Dieselkraftstoff herrührten.After removing the non-woven cloths from the water surface, it was observed that there were still streaks on the surface of the water that were not covered by the fleece cloth sucked up diesel fuel.

Auch durch weiteres Auflegen von neuen Vliestüchern konnten die von restlichem Dieselkraftstoff herrührenden Schlieren nicht restlos von der Wasseroberfläche entfernt werden.Also by further laying on new fleece cloths, those of the rest could Diesel streaks not completely removed from the water surface become.

Beispiel 1example 1

Wie im Vergleichsbeispiel A beschrieben wurde unter gleichen Bedingungen versucht, mit Hilfe von 30 × 50 cm großen Vliestüchern aus nichtgewobenen Polypropylenfasern Diesel­ kraftstoff von einer Wasseroberfläche zu entfernen.As described in Comparative Example A, attempts were made under the same conditions with With the help of 30 × 50 cm non-woven fabrics made of non-woven polypropylene fibers Diesel remove fuel from a water surface.

Im Gegensatz zum Vergleichsbeispiel A war das Vliestuch in diesem Fall mit 20 g Polymerem (B) pro m2 Vlies beschichtet, wobei das Polymere (B) ein Polyisobutylen mit einem Molekulargewicht (Viskositätsmittel Mv) von mindestens 5.600.000 ist. Das verwendete Polymere (B) hatte eine Korngrößenverteilung von mehr als 100 µm. Der Anteil des Polymeren (B) bei dem beschichteten Vlies betrug 0,1-1,5 Gew.-%.In contrast to comparative example A, the nonwoven cloth was coated with 20 g of polymer (B) per m 2 of nonwoven, the polymer (B) being a polyisobutylene with a molecular weight (viscosity average Mv) of at least 5,600,000. The polymer (B) used had a particle size distribution of more than 100 μm. The proportion of polymer (B) in the coated nonwoven was 0.1-1.5% by weight.

Analog dem Vergleichsbeispiel A wurden die Vliestücher aus nichtgewobenen Polypropylen­ fasern mit der mit dem Polyisobutylen (B) beschichteten Seite auf die Wasser-Dieselkraftstoff- Oberfläche aufgelegt. Nach 2-3 Minuten war ebenfalls an der Gelbfärbung der Vliestücher erkennbar, daß Dieselkraftstoff durch die Vliestücher aufgenommen wurde. Analogous to Comparative Example A, the nonwoven fabrics were made from non-woven polypropylene fibers with the side coated with the polyisobutylene (B) onto the water-diesel fuel Surface applied. After 2-3 minutes the yellow fleece was also yellow recognizable that diesel fuel was absorbed by the fleece cloths.  

Nach Entfernen der Vliestücher von der Wasseroberfläche konnte beobachtet werden, daß sich auf der Wasseroberfläche keine von Dieselkraftstoff herrührenden Schlieren mehr befanden. Durch die Verwendung von mit dem Polyisobutylen (B) beschichteten Vliestüchern aus nicht­ gewobenen Polypropylenfasern war es möglich, den auf der Wasseroberfläche befindlichen Dieselkraftstoff nahezu restlos zu entfernen.After removing the non-woven cloths from the water surface, it was observed that there were no more streaks from diesel fuel on the water surface. By using non-woven cloths coated with the polyisobutylene (B) woven polypropylene fibers, it was possible to find those on the water surface Almost completely remove diesel fuel.

Beispiel 2Example 2

Das Beispiel 2 wurde analog dem Beispiel 1 durchgeführt, wobei statt Dieselkraftstoff Hydrau­ liköl auf die Wasseroberfläche aufgegeben wurde.Example 2 was carried out analogously to Example 1, with Hydrau instead of diesel fuel Liköl was placed on the water surface.

Im Verhalten der mit dem Polyisobutylen (B) beschichteten Vliestücher aus nichtgewobenen Polypropylenfasern zeigten sich keine Abweichungen gegenüber Beispiel 1, was bedeutet, daß das auf der Wasseroberfläche befindliche Hydrauliköl nahezu restlos entfernt werden konnte.In the behavior of the non-woven nonwoven fabrics coated with the polyisobutylene (B) Polypropylene fibers showed no deviations from Example 1, which means that the hydraulic oil on the water surface could be removed almost completely.

Beispiel 3Example 3

Das Beispiel 3 wurde analog dem Beispiel 2 durchgeführt, wobei statt Hydrauliköl Benzin auf die Wasseroberfläche aufgegeben wurde.Example 3 was carried out analogously to Example 2, with petrol instead of hydraulic oil the water surface was abandoned.

Im Verhalten der mit dem Polymeren (B) beschichteten Vliestücher aus nichtgewobenen Poly­ propylenfasern zeigten sich keine Abweichungen gegenüber Beispiel 2, d. h., das Benzin konnte nahezu vollständig von der Wasseroberfläche entfernt werden.In the behavior of the nonwoven poly nonwoven fabrics coated with the polymer (B) propylene fibers showed no deviations from Example 2, i. that is, the gasoline could be removed almost completely from the water surface.

Claims (11)

1. Vlies zur Adsorption von organischen Flüssigkeiten, enthaltend anorganische oder organische Fasern (A) und 0,1 bis 2,0 Gew.-%, bezogen auf die gesamte Zusammensetzung, eines in solchen organischen Flüssigkeiten löslichen Polymers (B) mit einem Molekulargewicht (Viskositätsmittel Mv) von wenigstens 1.000.000.1. fleece for the adsorption of organic liquids containing inorganic or organic fibers (A) and 0.1 to 2.0% by weight, based on the total composition, of a polymer (B) having a molecular weight which is soluble in such organic liquids (Viscosity average Mv) of at least 1,000,000. 2. Vlies nach Anspruch 1, wobei als Fasern (A) thermoplastische Polymere verwendet werden.2. Nonwoven according to claim 1, wherein thermoplastic polymers are used as fibers (A). 3. Vlies nach den Ansprüchen 1 oder 2, wobei als Fasern (A) Polyurethane verwendet werden.3. Nonwoven according to claims 1 or 2, wherein polyurethanes are used as fibers (A). 4. Vlies nach den Ansprüchen 1 oder 2, wobei als Fasern (A) Polypropylene verwendet werden.4. Nonwoven according to claims 1 or 2, wherein polypropylenes are used as fibers (A) become. 5. Vlies nach den Ansprüchen 1 bis 4, wobei ein Polymer (B) mit einem Viskositätsmittel Mv von wenigstens 2.000.000 in das aus nicht gewebten Fasern hergestellte Vlies eingestreut wird.5. Nonwoven according to claims 1 to 4, wherein a polymer (B) with a viscosity agent Mv of at least 2,000,000 is sprinkled into the nonwoven fabric. 6. Vlies nach den Ansprüchen 1 bis 5, wobei als Polymer (B) ein Polymerpulver mit einer Teilchengröße von mindestens 50 µm eingesetzt wird.6. Nonwoven according to claims 1 to 5, wherein the polymer (B) is a polymer powder with a Particle size of at least 50 microns is used. 7. Vlies nach den Ansprüchen 1 bis 6, wobei als Polymer (B) Polyisobutylen verwendet wird.7. Nonwoven according to claims 1 to 6, wherein polyisobutylene is used as polymer (B). 8. Verfahren zur Adsorption von organischen Flüssigkeiten, wobei ein anorganische oder organische Fasern (A) enthaltendes Vlies zusammen mit einem in diesen organischen Flüssigkeiten löslichen Polymeren (B) eingesetzt wird, dadurch gekennzeichnet, daß man das anorganische oder organische Fasern (A) und 0,1 bis 2,0 Gew.-%, bezogen auf die gesamte Zusammensetzung, des Polymeren (B) enthaltende Vlies anschließend mit der zu adsorbierenden organischen Flüssigkeit in Kontakt bringt und nach etwa 5 bis 10 Minuten wieder entfernt.8. Process for the adsorption of organic liquids, wherein an inorganic or fleece containing organic fibers (A) together with an organic in these Liquid-soluble polymers (B) is used, characterized in that the inorganic or organic fibers (A) and 0.1 to 2.0 wt .-%, based on the total Composition, the polymer (B) containing fleece then with the adsorbing organic liquid and after about 5 to 10 minutes removed again. 9. Verfahren nach Anspruch 8, dadurch gekennzeichnet, daß man als Polymer (B) ein Polyisobutylen mit einem Viskositätsmittel Mv von wenigstens 1.000.000 verwendet.9. The method according to claim 8, characterized in that one as a polymer (B) Polyisobutylene with a viscosity average Mv of at least 1,000,000 is used. 10. Verwendung des Vlieses gemäß einem der Ansprüche 1 bis 7 zur Entfernung von organischen Flüssigkeiten.10. Use of the fleece according to one of claims 1 to 7 for the removal of organic liquids. 11. Verwendung des Vlieses gemäß einem der Ansprüche 1 bis 7 als Sperrschicht gegen das weitere Ausbreiten von organischen Flüssigkeiten.11. Use of the fleece according to one of claims 1 to 7 as a barrier against further spreading of organic liquids.
DE19834487A 1998-07-31 1998-07-31 Non-woven organic fiber fleece containing 0.1-2 wt.% of a soluble polymer having a viscosity average mol. wt. of at least 1,000,000 is useful for the absorption of organic liquids. Withdrawn DE19834487A1 (en)