|Inventors||Volker Benz, Michael Blumenschein, Markus Krall|
|Original Assignee||Roehm Gmbh & Co. Kg|
|Export Citation||BiBTeX, EndNote, RefMan|
|Referenced by (13), Classifications (13), Legal Events (8)|
|External Links: USPTO, USPTO Assignment, Espacenet|
 1. Field of the Invention
 The invention relates to a photovoltaic element in which a plurality of photovoltaic cells are enclosed between two plastic plates.
 2. Discussion of the Background
 Photovoltaic elements containing photovoltaic cells embedded in plastic between transparent panes are generally known. These elements are used for applications such as roofing and illuminating bus stops.
 German Patent Application 4443317 describes a photovoltaic element in which a plurality of photovoltaic cells are embedded in an elastic plastic material between two polymethyl methacrylate plates. The photovoltaic cells are protected against ingress of water and against mechanical influences, such as impacts.
 German Patent Application 3801989 describes a cladding panel of insulating glass in which photovoltaic solar generators in the air space between two glass panes are attached to one of the panes using an elastic plastic. Thereafter the solar generator is encapsulated with hot-melt adhesive or enveloped with sheeting.
 Adhesives for methyl methacrylate plastics are known. The adhesive bonding of polymethyl methacrylate parts by means of nitroethane or nitromiethane is known from German Unexamined Application (DE-OS) 2737270. Polymerization adhesives that are based on polymethyl methacrylate or methyl methacrylate and that can be cured by means of UV or visible light are described in, for example, European Patent Applications 436205 or 548740. The use of lower alkyl formates in volatile adhesives or adhesive lacquers based on polymethyl methacrylate is known from European Patent Application 663419. An advantageous adhesive bonding technique for polymethyl methacrylate parts using solvent adhesives in combination with viscous polymerization adhesives is described in European Patent Application 675184.
 Photovoltaic elements as described in German Patent Application 3801989 or 443317 offer good protection to the photovoltaic cells, since these are fixed between the plates by means of an embedding agent. This fixation method is expensive, however. Above and beyond this, especially under conditions of prolonged exposure, the danger exists that the embedding medium will interact chemically with the embedded cells, possibly destroying the cells. Furthermore, impact loads are transmitted from the surrounding plates via the embedding medium to the photovoltaic cells, possibly causing damage. A further problem is presented by moisture condensation in the cavities, possibly leading to fogging of the panes and thus to a reduction of photovoltaic output and even to destruction of the cells.
 Therefore, a need exists to provide an improved photovoltaic element, which is simple to manufacture and protects the cells effectively against chemical or mechanical influences.
 It is an object of the present invention to provide a photovoltaic element that protects the photovoltaic cells against chemical and mechanical influences and is easy to manufacture.
 This and other objects have been achieved according to the present invention, the first embodiment of which provides a photovoltaic element, comprising:
 two plane or curved plates (1) and (2), which are joined by a circumferential seal (3) at a spacing ranging from 2 to 20 mm, thus forming a cavity (4) in which there are enclosed a plurality of photovoltaic cells (5), each of which is attached to only one of the two plates (2) using an adhesive (6), at least this plate (2) being transparent;
 wherein both plates (1) and (2) are made of plastic that is permeable to water vapor and the adhesive with which the photovoltaic cells are attached covers at most 30% of the area of the individual photovoltaic cells.
FIGS. 1 and 2 are purely schematic drawings, which are not to scale. They are provided merely for better illustration of the invention and are not to be construed as limitative in any way.
FIG. 1 shows a schematic front view of a photovoltaic element of the present invention with 12 photovoltaic cells. For simplicity, adhesive (6) is shown only for the top left photovoltaic element. Barrier layer (3 a) and adhesive layer (3 b) are visible through transparent plate (2) resting thereon. Plate (1) is disposed there behind. Conductor tracks (7) and lead (7′) are shown purely schematically.
FIG. 2 shows a photovoltaic element of the present invention from the side and in cross section. From this view there can be seen 5 photovoltaic cells (5) with associated adhesive (6) disposed one above the other. Conductor tracks (7) and lead (7′) are not shown. Spacer pads (8) are firmly joined only to plate (1).
 The present invention provides for a photovoltaic element having two planar or curved plates (1) and (2), which are joined by a circumferential seal (3) at a spacing ranging from 2 to 20 mm, thus forming a cavity (4) in which there are enclosed a plurality of photovoltaic cells (5), each of which is attached to only one of the two plates (2) using an adhesive (6). At least the plate (2), to which the photovoltaic cells (5) are attached is transparent. However, both plates can be transparent. Both, plates (1) and (2) are made of plastic that is permeable to water vapor. The adhesive with which the photovoltaic cells are attached covers at most 30% of the area of the individual photovoltaic cells.
 The photovoltaic element comprises two planar or curved plates (1) and (2), which are joined by a circumferential seal (3) at a spacing ranging from 2 to 20 mm, preferably 4 to 10 mm, thus forming a cavity (4). The spacing includes all values and subvalues therebetween, especially including 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13, 14, 15, 16, 17, 18 and 19 mm.
 It is essential to the invention that plates (1) and (2) are made of plastic that is permeable to water vapor. This offers the advantage that little or no moisture condensation can form in cavity (4) of the photovoltaic element, even after relatively long time, and that existing moisture condensation can escape once again.
 Within the context of the present invention a plastic that is permeable to water vapor is a plastic with a moisture absorption capacity of at least 0.5%, preferably at least 2%, more preferably at least 5% and most preferably at least 10%. Examples of such plastic include polymethyl methacrylate, polycarbonate, polyester, polystyrene and polyvinyl chloride. A preferred plastic is a cast or extruded polymethyl methacrylate, because of its relatively high moisture absorption capacity of about 2% associated with high transparency and good mechanical characteristics. Polycarbonate is also preferred, since it offers the advantage of relatively high permeability to water vapor.
 Plates (1) and (2) can be made of different plastics, but preferably the same plastic material is used.
 Plate (1) can be designated as the rear plate which faces away from the light, whereas plate (2) has the function of transmitting the light for the photovoltaic cells. Plate (2) must therefore be sufficiently transparent, which is the case if the light transmission factor (according to DIN 67507) is at least 60%, preferably at least 70%, especially preferably at least 85%.
 Preferred plate thicknesses for plate (2) range from 4 to 20 mm, more preferably 4 to 12 mm. The plate thickness includes all values and subvalues therebetween, especially including 5, 6, 7, 8, 9, 10, 11, 12, 13, 14, 15, 16, 17, 18 and 19 mm.
 If only one side of the photovoltaic element has to be transparent, plate (1) can be made of less transparent plastic material which, for example, is translucent or colored. Plate (1) may also comprise a plastic member, such as a multiple multiribbed plate which, because of its thickness or its geometry, is not very transparent.
 As plate (1) there can be used, for example, a multiribbed plate of polymethyl methacrylate or of polycarbonate. The photovoltaic element can then be used as a thermally insulating roofing or paneling element.
 Likewise, there can be used as plate (1) a sound-absorbing wall panel of polymethyl methacrylate, to the entirety or part of which there is attached a plate (2).
 The use of polymethyl methacrylate for plates (1) and (2) has in particular the advantage of good deformability. For example, not only planar photovoltaic elements but also curved forms, such as barrel vaults for roofing elements, can be made easily. The deformation can also be applied subsequently by bending of planar elements, preferably in the thermoplastic condition (heat forming). Subsequent bending is also possible with the other cited thermoplastic forms.
 Attachment of the Photovoltaic Cells
 In cavity (4) there are enclosed a plurality of photovoltaic cells (5), each of which is attached only to plate (2) using an adhesive (6), which covers at most 30%, preferably at most 20%, especially preferably at most 10% of the surface area of the individual photovoltaic cells.
 The one-sided bond between the plate (2) and the cells (5) fixes the cells such that impacts on the plates are transmitted only via the adhesive and not over the entire surface, thus reducing the danger of damage due to impact. In order to reduce the impact danger even more, an elastic adhesive is preferably used, such as two-sided adhesive tape comprising compliant acrylate adhesive. For example, a cell having an area of 10×10 cm can be fixed to one of the two plates with one or two strips having an area of 0.5×5 cm.
 Particularly suitable elastic adhesives are acrylate adhesive tapes on the basis of elastic acrylates with relatively high contents, such as 10 to 100 wt %, of ethyl acrylate or butyl acrylate. Optionally a plasticizer can be contained in the acrylate adhesive tape. The amount of the ethyl acrylate or butyl acrylate in the acrylate adhesive tape includes all values and subvalues therebetween, especially including 20, 30, 40, 50, 60, 70, 80 and 90 wt %.
 Fixation with a one-sided adhesive bond (6) offers a further advantage. If the adhesive is designed to be attached to the light-absorbing side of the cells, only little of the surface is covered and so the light absorption of the cells is only slightly reduced. This can be the case, for example, when the cells are mounted in a roofing element that is accessible for viewing from the underside. In this case it is advisable to apply the adhesive strips on the roof side facing away from the observer, thus also imparting a more advantageous optical effect, especially since almost all adhesive take on a certain golden appearance in the course of time. A transparent adhesive is preferably used in order to minimize the extent by which the adhesive strips reduce the light absorption of the cells.
 The adhesive can be, for example, a double-sided adhesive tape, a glue or a polymeric adhesive.
 Photovoltaic Cells
 Standard photovoltaic cells (5) have a usually square surface with edge length ranging from about 10 to 15 cm and thickness from 0.5 to 2 mm. The achievable power ranges from 1.3 to 2 watt. The edge length includes all values and subvalues therebetween, especially including 11, 12, 13 and 14 mm. The thickness includes all values and subvalues therebetween, especially including 0.6, 0.7, 0.8, 0.9, 1.0, 1.1, 1.2, 1.3, 1.4, 1.5, 1.6, 1.7, 1.8 and 1.9 mm. The power includes all values and subvalues therebetween, especially including 1.4, 1.5, 1.6, 1.7, 1.8 and 1.9 watt.
 As a rule, the cells are disposed side-by-side in square or rectangular arrays comprising, for example, 10×6 cells or similar numbers, with cell-to-cell spacings of 1 to 3 cm. The ratio of the area of the photovoltaic cells to the total area of the photovoltaic elements ranges from 20 to 80, preferably 40 to 60% and most preferably 45-55%.
 The individual cells of such arrays are connected together to form electrical units by means of conductor tracks (7), also known as “strings”. To collect the electric power or the generated current, at least one lead (7′) must be brought out of the photovoltaic element. When the elements are connected in series, it is expedient to bring out one line or cable from each of the first and last elements, respectively.
 Plates (1) and (2) enclosing the photovoltaic cells are spaced apart by 1.5 to 6, preferably 2 to 4 mm. The distance includes all values and subvalues therebetween, especially including 2, 2.5, 3, 3.5, 4, 4.5, 5 and 5.5 mm. This distance can be maintained by spacers. It is important that the photovoltaic cells between the plates be enclosed by a circumferential seal. This prevents ingress of moisture into the element. The circumferential seal The photovoltaic elements are surrounded by means of a circumferential seal (3), through which lead (7′) for collecting current can be conveniently brought out. The purpose of circumferential seal (3) is to enclose the elements' water tightly. The circumferential seal can comprise a plurality of layers, especially two layers, in which case an inner layer first acts as a barrier layer (3 a) between the photovoltaic cells, thus allowing a polymerization adhesive to be used as the outer layer or adhesive layer (3 b), without trapping, in cavity (4), solvent or monomer vapors that may later lead to stress corrosion cracking.
 The circumferential seal can be made, for example, of polymethyl methacrylate, polyurethane, EPDM or polysilicone rubber.
 Manufacture of the Photovoltaic Elements
 The photovoltaic elements are fixed on plate (2) using the adhesive mentioned herein above.
 For plane photovoltaic elements the circumferential seal can be installed by, for example, fitting together four rectangular rods (cross section of 10×10 mm, for example, length as needed) of polymethyl methacrylate in the form of a rectangular frame around the photovoltaic elements and, using a suitable solvent, such as methylene chloride, joining them together with plate (2) and with one another by moistening the contact surfaces. It is important that the solvent be allowed to evaporate thoroughly, for a duration of 1 to 4 hours, for example, before plate (1) is placed on the circumferential frame.
 If the cavity to be enclosed is large, it may be expedient, in addition to the circumferential seal, to install spacers (8) of the same height at intermediate positions. Such spacers only have to be adhesively bonded to either plate (1) or plate (2), however, in order to maintain tolerance to warping in the element as a whole. As an example, small pads of polymethyl methacrylate can be used.
 Plates (1) and (2) can now be permanently sealed outside the barrier layer with an adhesive layer using a circumferential bead. Preferably a viscous polymethyl methacrylate polymerization adhesive is used as adhesive layer. After complete polymerization of the adhesive layer, the photovoltaic element is mechanically stable. The barrier layer, which then is firmly bonded adhesively only to plate (2), nevertheless adequately prevents methyl methacrylate vapors from the polymerization adhesive from entering the cavity during or after polymerization of the adhesive layer, because it bears sealingly on plate (1).
 To prevent material stresses, the photovoltaic element can also be subjected to tempering, for example for 2 to 5 hours at 70° C.
 The sealing effect can be further improved by applying a small amount of solvent on the upper side of the polymethyl methacrylate frame before plate (1) is placed in position, thus causing slight dissolution of the surface of the polymethyl methacrylate. The small amount of solvent evaporates almost immediately, however, and then plate (1) is placed in position after a short waiting period such as 1 to 5 minutes. As a result, plate (1) bonds adhesively at least slightly to the frame, thus improving the sealing effect or barrier effect.
 As an alternative to the polymethyl methacrylate frame described herein above, the circumferential seal can also be made from an elastic material, in which case spacers such as pads of the same plastic material as that of plate (2) are preferably used as well. The spacers can be fixed to plate (2) or also to plate (1) with a solvent adhesive. In this case a circumferential elastic seal is produced, which is somewhat higher than the spacers. Thus, after plate (1) has been placed on the spacers and pressed down on the circumferential seal, a sealed cavity enclosing the photovoltaic elements is formed.
 As elastic material for the circumferential seal there can be used a polyurethane adhesive, a polysilicone rubber or a solvent adhesive containing polymer. The latter can be, for example, polymethyl methacrylate in solvent (such as dichloromethane, nitromethane, methyl formate, ethyl formate, methylene chloride), polycarbonate in solvent (tetrahydrofuran), polyvinyl chloride or polystyrene in solvent. For polycarbonate plates, adhesives based on polyurethane in particular are suitable. For polymethyl methacrylate plates, compliant acrylate adhesives such as polyethyl acrylate dissolved in ethyl acetate are most preferred.
 Thereafter plates (1) and (2) are firmly joined by a commercial polymerization adhesive. Suitable polymerization adhesives for polymethyl methacrylate are described in, for example, European Patent Application 548740. As a rule, such adhesives contain approximately 30 wt % of polymer (polymethyl methacrylate) dissolved in monomer (methyl methacrylate) as well as one or if necessary more polymerization initiators.
 Having generally described this invention, a further understanding can be obtained by reference to certain specific examples which are provided herein for purposes of illustration only, and are not intended to be limiting unless otherwise specified.
 In a preferred arrangement, a plurality of photovoltaic cells (5), for example an array of 10×10 cells with intermediate spacings of about 1 cm, were fixed on a polymethyl methacrylate plate (2) with a surface area of 150×150 cm and a thickness of 1 cm, using for each two transparent adhesive strips (6) measuring, for example, 0.5×5 cm and comprising double-sided elastic acrylate adhesive tape, the cells being connected by conductor tracks (7).
 Current-collecting cable (7′) of the electric cell assembly was brought out on one side. For the sake of clarity, the outgoing cabling of the first cell is not shown. A plurality of polymethyl methacrylate spacer pads (8) measuring 1×1 cm and having a thickness of 1 mm were attached adhesively by moistening the interface to plate (2) with methylene chloride.
 A barrier layer (3 a) comprising a compliant acrylate adhesive (polyethyl acrylate dissolved in ethyl acetate) was now applied on the assembly of photovoltaic cells.
 After evaporation of the solvent, which was complete about 24 hours after application of barrier layer (3 a), second plate (1) of polymethyl methacrylate (3 b) was placed in position and the rims are sealed with a polymethyl methacrylate polymerization adhesive (adhesive layer 3 b). Under these conditions, adhesive layer (3 a) prevents monomer vapors from the polymerization adhesive from entering photovoltaic cells (5).
 Thereafter the element was stored for 360 days at 85% relative humidity and 80° C. Neither moisture condensation in the interior nor damage to the photovoltaic cells or to the connecting conductors was observed under these conditions. The element was found to be fully functional after this period.
 The priority document of the present application, German patent application 200 02 827.8, filed Feb. 17, 2000, is incorporated herein by reference.
 Obviously, numerous modifications and variations on the present invention are possible in light of the above teachings. It is therefore to be understood that within the scope of the appended claims, the invention may be practiced otherwise than as specifically described herein.
|Citing Patent||Filing date||Publication date||Applicant||Title|
|US7110680||Jul 12, 2002||Sep 19, 2006||Fujitsu Limited||Method and system for forward pumping Raman amplification in an optical network|
|US7666466 *||Mar 5, 2007||Feb 23, 2010||Michael Gumm||Elastomeric waterproofing and weatherproofing photovoltaic finishing method and system|
|US8716592 *||Jul 12, 2004||May 6, 2014||Quanex Ig Systems, Inc.||Thin film photovoltaic assembly method|
|US8759664||Dec 22, 2010||Jun 24, 2014||Hanergy Hi-Tech Power (Hk) Limited||Thin film solar cell strings|
|US8993364||Jan 9, 2014||Mar 31, 2015||Hanergy Hi-Tech Power (Hk) Limited||Integrated thin film solar cell interconnection|
|US20050178428 *||Oct 15, 2004||Aug 18, 2005||Solar Roofing Systems Inc.||Photovoltaic system and method of making same|
|US20060005874 *||Jul 12, 2004||Jan 12, 2006||Ferri Louis A||Thin film photovoltaic assembly method|
|US20070012352 *||Jul 11, 2006||Jan 18, 2007||Bp Corporation North America Inc.||Photovoltaic Modules Having Improved Back Sheet|
|US20100147356 *||Sep 30, 2009||Jun 17, 2010||Britt Jeffrey S||Thin film solar cell string|
|US20130180575 *||Jul 20, 2012||Jul 18, 2013||Nanosolar, Inc.||Structures for Solar Roofing|
|US20140020735 *||Jul 19, 2013||Jan 23, 2014||Hitachi High-Technologies Corporation||Resin substrate solar cell module|
|US20150121780 *||Apr 25, 2013||May 7, 2015||Onyx Solar Energy S.L.||Walkable photovoltaic floor|
|WO2009085736A2 *||Dec 16, 2008||Jul 9, 2009||Truseal Technologies Inc||Hot melt sealant containing desiccant for use in photovoltaic modules|
|U.S. Classification||136/251, 438/67, 136/244, 438/66|
|International Classification||H01L31/042, E04D13/18, C09J4/02, H01L31/048, H01L31/04|
|Cooperative Classification||H01L31/048, Y02B10/12, Y02E10/50|
|Apr 18, 2002||AS||Assignment|
|Jul 8, 2002||AS||Assignment|
Owner name: ROEHM GMBH & CO. KG, GERMANY
Free format text: CORRECTIVE ASSIGNMENT TO CORRECT THE EXECUTION DATES, THE THIRD ASSIGNOR S NAME, AND THE ASSIGNEE SADDRESS PREVIOUSLY RECORDED ON REEL 012814, FRAME 0076;ASSIGNORS:BENZ, VOLKER;KRALL, MARKUS;BLUMENSCHEIN, MICHAEL;REEL/FRAME:012903/0071;SIGNING DATES FROM 20010308 TO 20010312
|Jan 12, 2006||FPAY||Fee payment|
Year of fee payment: 4
|Jan 8, 2010||FPAY||Fee payment|
Year of fee payment: 8
|Feb 25, 2010||AS||Assignment|
Owner name: EVONIK ROHM GMBH,GERMANY
Free format text: CHANGE OF NAME;ASSIGNOR:ROHM GMBH;REEL/FRAME:023998/0789
Effective date: 20070925
Owner name: ROHM GMBH,GERMANY
Free format text: CHANGE OF ENTITY;ASSIGNOR:ROHM GMBH & CO. KG;REEL/FRAME:023998/0760
Effective date: 20060607
Owner name: ROHM GMBH, GERMANY
Free format text: CHANGE OF ENTITY;ASSIGNOR:ROHM GMBH & CO. KG;REEL/FRAME:023998/0760
Effective date: 20060607
Owner name: EVONIK ROHM GMBH, GERMANY
Free format text: CHANGE OF NAME;ASSIGNOR:ROHM GMBH;REEL/FRAME:023998/0789
Effective date: 20070925
|Feb 21, 2014||REMI||Maintenance fee reminder mailed|
|Jul 16, 2014||LAPS||Lapse for failure to pay maintenance fees|
|Sep 2, 2014||FP||Expired due to failure to pay maintenance fee|
Effective date: 20140716