US20010028055A1 - Quantum dot infrared photodetector (QDIP) and methods of making the same - Google Patents
Quantum dot infrared photodetector (QDIP) and methods of making the same Download PDFInfo
- Publication number
- US20010028055A1 US20010028055A1 US09/850,138 US85013801A US2001028055A1 US 20010028055 A1 US20010028055 A1 US 20010028055A1 US 85013801 A US85013801 A US 85013801A US 2001028055 A1 US2001028055 A1 US 2001028055A1
- Authority
- US
- United States
- Prior art keywords
- quantum dots
- quantum dot
- layer
- quantum
- growth
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
A photodetector capable of normal incidence detection over a broad range of long wavelength light signals to efficiently convert infrared light into electrical signals. It is capable of converting long wavelength light signals into electrical signals with direct normal incidence sensitivity without the assistance of light coupling devices or schemes. In the apparatus, stored charged carriers are ejected by photons from quantum dots, then flow over the other barrier and quantum dot layers with the help of an electric field produced with a voltage applied to the device, producing a detectable photovoltage and photocurrent. The photodetector has multiple layers of materials including at least one quantum dot layer between an emitter layer and a collector layer, with a barrier layer between the quantum dot layer and the emitter layer, and another barrier layer between the quantum dot layer and the collector.
Description
- This application is a division of U.S. application of U.S. Ser. No. 09/291,020 filed Apr. 14, 1999.
- This invention relates to apparatus and methods for converting light signals into electrical signals. More particularly, the invention relates to a semiconductor photodetector device and a method for converting electromagnetic radiation such as infrared signals into electrical signals using self-assembled semiconductor quantum dots.
- Presently, state-of-the art photodetectors are either based on interband transitions in bulk material or quantum wells, or intersubband transitions in quantum wells. The interband transition devices operate mainly in the visible and near infrared wavelength range due to the energy difference between the conduction and valence band of semiconductors. The intersubband devices operate with multiple layers of quantum wells, in which carriers are confined to quantum dimensions in 1 direction (perpendicular to the surface of the device), and are free to move in the other 2 directions (in the plan of the quantum wells).
- Such quantum well infrared photodetectors (QWIPs) are being used successfully for detecting InfraRed (IR) light for detectors and sensors and for imaging purposes. A major limitation of these QWIPs is that due to the transition selection rules they are not sensitive to normally incident light, and only have narrow response range in the IR. Consequently, normal incidence detection over a broad range in the IR can only be achieved with complicated light coupling devices and/or schemes, and by combining layers with different sets of quantum wells each having its own narrow response range.
- Multiple layers of Self-Assembled Quantum Dots (QD) can be grown by epitaxy of highly strained semiconductors embedded in barrier spacers. Due to the small size of the quantum dots, which typically have diameters of about 200 Angstroms, quantum mechanics dictate the energy position of energy levels allowed in the quantum dots. Infrared light detection is achieved by the transitions of charged carriers from confined energy levels in the quantum dots to higher confined energy levels in the quantum dots, and/or from confined energy levels in the quantum dots to higher energy states in the wetting layer which is formed underneath the quantum dots in the self-assembling growth, and/or from confined energy levels in the quantum dots to higher energy states in the barrier material.
- In contrast to the QWIPs, QDIPs are sensitive at normal incidence, and have a broad response range. The QDIPs do not suffer from the normal incidence limitation because of the unique symmetry resulting from confining the carriers in all 3 directions, and have a much broader response range in the infrared compared to the present QWIP design because the self-assembled quantum dots naturally grow with an inhomogeneous broadening in the size dispersion and with intersublevel energies which are both suitable for the long wavelength range. Growth and fabrication can be accomplished with well established and simple growth and fabrication techniques.
- There has been a real need for photodetectors capable of normal incidence detection over a broad range to efficiently convert infrared light into electrical signals, which is satisfied by the present invention, which provides an apparatus and method capable of converting broad ranges of long wavelength light signals into electrical signals with good efficiencies.
- The present invention also provides an apparatus and method capable of converting broad ranges of long wavelength light signals into electrical signals with direct normal incidence sensitivity without the assistance of light coupling devices/schemes.
- These and other embodiments are realized by apparatus and a method in which stored charged-carriers are ejected by photons from quantum dots, then flow over the other barrier and quantum dot layers with the help of an electric field produced with a voltage applied to the device, therefore resulting in a detectable photovoltage and photocurrent.
- The apparatus takes the form of a photodetector comprising multiple layers of semiconductor materials including a least 1 quantum dot layer between an emitter layer and a collector layer, with a first barrier layer between the quantum dot layer and the emitter layer, and another barrier layer between the quantum dot layer and the collector. In the case where multiple quantum dot layers are used, barriers separate the quantum dot layers. The emitter and collector are preferably doped to act as a reservoir of charge carriers and to conduct the current during detection and for operation under applied bias. The charge carriers are introduced in the quantum dot layer by either doping the barrier and/or the dot layers, and/or after redistribution of the charge carriers and adjustment of the Fermi level. The level of doping in the various regions of the device and the scheme of doping is preferably adjusted to set the Fermi level such that the desired number of energy levels in the quantum dots are occupied with charge carriers to achieve the targeted range of detection wavelengths. Also preferably, the size and the number of quantum dots per unit area is adjusted from the growth parameters in conjunction with the doping to achieve the desired detection range while optimizing the detection efficiency for the wavelengths of interest. Similarly, the choice of the barrier material, height, and thickness is adjusted in conjunction with the quantum dot size to set the detection range, to select a balance between low detector capacitance and low carrier transit time, and to achieve the desired growth mode in the self-assembling growth. For multiple layers of quantum dots very thin barriers will result in coupled zero-dimensional states in vertically self-organized quantum dots, thicker barriers will result in isolated zero-dimensional states in vertically self-organized quantum dots, and thick barriers will result in isolated zero-dimensional states in uncorrelated independent quantum dot layers.
- In a preferred form of the invention the layers of the semiconductor materials are grown on a substrate from materials consisting essentially of gallium, indium, aluminum, arsenic, phosphorus, and possibly nitrogen, using known techniques such as molecular beam epitaxy, or metalorganic chemical vapor deposition, or chemical beam epitaxy, with dopant such as silicon, beryllium, or other. The carriers are introduced by n-doping or p-doping the quantum dots and/or the barriers, either continuously, or using modulation doping layers.
- On GaAs substrates, the quantum dot material can be InGaAs, AlInAs, InP, or other alloys of AlGaInAsP, with barriers of AlGaAs or AlGaInP. On InP substrate, the quantum dot material can be InGaAs. Alloys with nitrogen can be used with the above group III-V materials in cases where high band gap materials are desirable. On group IV substrates, Si can be used for the barrier, and SiGe or some of the group III-V materials mentioned above for the quantum dot material. The substrate is needed to give structural integrity to the very thin layers of the device and to allow proper crystal growth. The emitter and the collector are preferably doped with the type of carriers which will be used in the quantum dots to detect the infrared light. The type of charged carrier is preferably chosen in conjunction with the size of the quantum dots, and with the thickness and height of the barriers, to obtain the desired spectral response.
- The photodetector is exposed to electromagnetic radiation, and in particular infrared radiation, having no required specific orientation of the polarization vector with respect to the surface of the device. Light of substantially all polarizations and angles of incidence can be detected because of the symmetry and shape of the self-assembled quantum dots which preferably take a form resembling an hemispherical cap, a lens shape, a disk shape, a pyramidal or truncated and/or rounded pyramid shape. The self-assembled quantum dots are obtained with the spontaneous island formation during the epitaxy of highly strained semiconductor materials. The details of the self-assembling growth are preferably arranged to establish the shape, symmetry, and size of the quantum dots and therefore set the quantum dot energy levels to optimize the detection response in the desired spectral range.
- In accordance with an embodiment of the invention, a photodetector is comprised of multiple layers of semiconductors with an emitter, a collector, a series of quantum dot layers disposed between the emitter and collector layer with barriers separating the quantum dot layers, a first barrier layer between the emitter layer and the series of quantum dot layers, and a last barrier layer between the collector layer and the series of quantum dot layers. The quantum dot layers have one or more zero-dimensional levels confined below the barrier energy, with the quantum dot energy levels containing some charge carriers that can be excited to higher energy levels using incident photons and flow from the quantum dots to the collector with the charge carriers that can be replaced by other charge carriers originating from the emitter.
- In accordance with another embodiment, a method of producing self-assembled quantum dots having an adjustable number of confined levels and having an adjustable intersublevel spacing which relies on spontaneous island formation during the epitaxy of highly strained semiconductors comprises selecting a barrier material and a quantum dot material wherein the amount of their lattice-mismatch dictates the critical thickness required to obtain the spontaneous island formation, and their bandgap difference determines the possible number of confined states in conjunction with the intersublevel spacing, growing some thickness of the barrier material which has a lattice constant close to the lattice constant of the substrate used, depositing, at a specified growth rate, the quantum dot material at a substrate temperature which will produce quantum dots having the appropriate size to obtain the intersublevel spacing, stopping the growth of the quantum dot material after the desired number of quantum dots per unit area is reached, pausing the-growth for a predetermined amount of time to allow for self-assembling growth to form the quantum dots in shapes and sizes which will give the intersublevel spacing, and growing a thickness of the barrier material to cover the quantum dots and return to a planar growth front at a substrate temperature which may be varied during the growth and which will optimize the quality of the quantum dots.
- In accordance with another embodiment, a method of converting light signals to electrical signals is comprised of storing charged carriers in semiconductor quantum dots having zero-dimensional levels established by the size and composition of the quantum dots and the height of the confining potential of the barriers, exposing the quantum dots to electromagnetic radiation having sufficient energy to eject stored carriers from the quantum dot layers by photoemission, and applying a bias voltage across emitter and collector layers between which a series of quantum dot layers containing the quantum dots are located and which quantum dot layers, emitter and collector layers are separated by barriers, and cause the carriers ejected from the quantum dot layers by photoemission to flow to the collector, while replacing the ejected carriers from the quantum dot layers with carriers originating from said emitter.
- In accordance with another embodiment, a photodetector is comprised of multiple layers of quantum dots and a barrier separating each layer of quantum dots from an adjacent layer of quantum dots, an emitter layer and a collector layer, and a corresponding barrier separating each of the emitter layer and collector layer from an adjacent layer of quantum dots on respective opposite ends of the multiple layers of quantum dots, conductors for applying a bias voltage between the collector and emitter, and means for allowing electromagnetic radiation to be exposed to at least some of the layers of quantum dots.
- A better understanding of the invention can be gained from the following detailed description of the preferred embodiments when read in conjunction with the accompanying drawings in which:
- FIG. 1 is a partial, greatly magnified view of the layer structure of a photodetector in accordance with an embodiment of the invention;
- FIG. 2 is a schematic energy level diagram depicting transitions which can be used to detect the light with the photodetector of FIG. 1;
- FIG. 3 is a 77K photoluminescence spectra demonstrating the good optical quality of a QDIP photodetector structure grown with 50 layers of InAs quantum dots with GaAs barriers, and revealing interband transitions involving the energy levels depicted in FIG. 2;
- FIG. 4 is an example of spectral response measured with a QDIP photodetector with 50 layers of InAs quantum dots with Al0.35Ga0.65As barriers; and
- FIG. 5 is an example of the responsivity measured as a function of the voltage applied on the QDIP photodetector of FIG. 4 for a detection wavelength of 5 microns.
- FIG. 1 illustrate a portion of the photodetector in accordance with an embodiment of the invention. The photodetector comprises multiple layers of semiconductor materials. These layers include, from bottom to top, a
bottom contact layer 6 which serves as a collector or an emitter which will preferably be doped to provide carriers and for conductivity, afirst barrier layer 12 which can be doped continuously or modulation doped as shown to provide carriers and for conductivity, and at least a firstquantum dot layer 14. - For enhanced performance, the photodetector will preferably have multiple layers of quantum dots, in which case a
barrier 18 will separate the firstquantum dot layer 14 from a secondquantum dot layer 24. Thebarrier 18 can be doped continuously or modulation doped (16 and 20) to provide carriers and for conductivity. In the case of modulation doping, multiple layers of doping can be used in thebarrier 18. For example FIG. 1 illustrates the case where two modulation dopedlayers - The distance d3 between the
quantum dot layer 14 and the dopedlayer 16 can be adjusted to optimize the number of carriers and to engineer the built-in field after the charge transfer which occurs in modulation doping. Similarly additional quantum dot layers and barriers can be added until the preferred number of quantum dot layers is reached, the quantum dot layers being separated by a barrier, giving a repeating sequence with a period d4. The lastquantum dot layer 25 is followed by thelast barrier layer 26 which can be doped continuously or modulation doped as shown at 28 to provide carriers and for conductivity. - Following the
last barrier layer 26, atop contact 30 serves as the other of a collector or an emitter which will preferably be doped to provide carriers and for conductivity. These layers are very thin; for instance in a preferred form of the device described below, the thickness d2 of a quantum dot together with the wetting layer which forms below the quantum dots is about 45 Angstroms. Hence, it is necessary to provide asubstrate 2 on which to grow the layers and to give structural integrity to the device. Thesubstrate 2 should typically have a thickness between 0.1 and 1 mm and should be covered with abuffer layer 4 below thebottom contact 6. Thebuffer layer 4 serves to initiate proper growth conditions and to establish the desired conductivity between thesubstrate 2 and thebottom contact 6. - The
substrate 2 andbuffer layer 4 can be either conductive or insulating depending on the optical and electrical properties desired for these layers.Undoped buffer 4 andsubstrate 2 is preferred in the cases where the transmission of the long wavelength light through the bottom of the structure is of consideration, and conductingbuffer 4 andsubstrate 2 is preferred in the cases where it is desirable to have a bottomelectrical contact 8 be conductive through to thesubstrate 2. - In a preferred embodiment a planar geometry is obtained by exposing the
bottom contact 6 in some region of the device using lithography and etching techniques such as wet etchings or dry etchings after mask patterning. Photocurrent andphotovoltage 10 can be measured between thebottom metal contact 8 and atop metal contact 32 which makes ohmic contacts with thetop contact 30.Contacts bias voltage 34 to the photodetector. - As mentioned above, in a preferred form of the invention the layers of the semiconductor materials are grown on a
substrate 2 from materials consisting essentially of gallium, indium, aluminum, arsenic, phosphorus, and possibly nitrogen, using known techniques such as molecular beam epitaxy, or metaloorganic chemical vapor deposition, or chemical beam epitaxy, with dopant such as silicon, beryllium, or other. The carriers are introduced by n-doping or p-doping the quantum dots and/or the barriers, either continuously (for example throughout most of thetop contact 30 and bottom contact 6), or using modulation doping layers (for example 12, 16, 20, 28, etc. in the barrier layers). - On
GaAs substrates 2, thequantum dot material substrate 2 is GaAs; the quantum dot layers (14, 24, etc) consist essentially of Inx1Ga1−x1As wherein x1 equals 0.15 to 1, preferably about 0.5 to 1 and specifically 1; the barriers (12, 18, 26, etc) consists of Alx5Ga1−x5As with x5 equals to 0 to 1, preferably about 0 to 0.4, and more preferably 0. - The emitter and the collector are preferably doped with the type of carriers which will be used in the quantum dots to detect infrared light. The type of charge carrier is preferably chosen in conjunction with the size of the quantum dots, and with the thickness and height of the barriers, to obtain the desired spectral response. In the exemplary embodiment of the invention, the carriers are electrons provided by silicon doping.
- In the case where multiple layers are used to increase the response of the photodetector, preferably, all barriers (12, 18, 26, etc) and quantum dot layers (14, 24, etc) can respectively have the same nominal alloy composition and thicknesses, but alternatively, the value of the alloy composition, doping, and thicknesses of each layer can be set individually to tailor the response of the photodetector to specific requirements. In particular, the material chosen, the alloy and size of the quantum dots can be changed throughout the stack of multiple layers to vary the quantum dot energy levels and therefore provide a wider range of spectral response.
- The amount of semiconductor material required to form the self-assembled quantum dots (14, 24, etc.) depends on the relative strain between the
substrate 2 and the quantum dots. The number of quantum dots per unit area can be adjusted by varying the amount of material deposited in the quantum dot layers. The size of the quantum dots can be adjusted by the substrate temperature used during the growth of each quantum dot layer. As mentioned above, the size and the number of quantum dots per unit area is adjusted from these growth parameters in conjunction with the doping to achieve the desired detection range while optimizing the detection efficiency for the wavelengths of interest. Similarly, the choice of the barrier material, height, and thickness is adjusted in conjunction with the quantum dot size to set the detection range, to select a balance between low detector capacitance and low carrier transit time, and to achieve the desired growth mode in the self-assembling growth. For multiple layers of quantum dots, very thin barriers will result in coupled zero-dimensional states in vertically self-organized quantum dots, thicker barriers will result in isolated zero-dimensional states in vertically self-organized quantum dots, and thick barriers will result in isolated zero-dimensional states in uncorrelated independent quantum dot layers. - FIG. 2 illustrates a partial band diagram for a quantum dot layer of the device of FIG. 1. In this figure, the vertical direction represents the energy of the carriers in the structure, and the horizontal direction represents the position of the carriers within the photodetector structure. Due to the small size of the
quantum dots 14, quantum mechanics will dictate the values of energy levels (32,34,36,38,40,44) localized in the lowband gap material 14,by thebarriers - The self-assembled quantum dots effectively give a zero-dimensional potential with a quasi-parabolic confinement, and consequently the energy spacing between the adjacent levels (also called the intersublevel spacing) is roughly constant between the various levels. The number of allowed energy levels and intersublevel spacing is determined by the shape and size of the quantum dot, the height of the confining potential between the barriers (12, 18) and the quantum dot (14), and by the carrier effective mass. Experimental assessment of these energy levels can be obtained by probing the interband transitions and observing the state filling in photoluminescence.
- For example, FIG. 3 is a 77K photoluminescence spectra which demonstrate the good optical quality of an exemplary QDIP photodetector structure grown with 50 layers of InAs quantum dots, modulation-doped with electrons in GaAs barriers. The spectra of FIG. 3 reveal interband transitions involving the energy levels depicted in FIG. 2, with the wetting layer transition and 4 quantum dot transitions. The intersublevel spacing measured for this photodetector is about 60 meV for the total of both the electron and the hole contributions, of which about ⅔ originates from the electron intersublevel spacing. It can therefore be concluded that the electron intersublevel spacing for these quantum dots is about 40 meV.
- The carriers are introduced by doping and fill the quantum dot energy levels up to the Fermi level EF (42) (see FIG. 2) in accordance with the level degeneracy, Hund's rule for filling orbitals, and Coulomb interaction and renomalization energies. For example, first the ground state EQD 1 (32) can accommodate 2 carriers, one spin up, and one spin down, then the first excited state EQD 2 (34) can accommodate 4
carriers 2 spin up and 2 spin down, etc. The level of doping is therefore determined taking into account the desired position of theFermi level 42 in the quantum dot to fill the appropriate number of energy levels. This will determine which energy levels and intersublevel transitions will participate in the photodetection given that transitions are improbable to originate from empty energy levels above the Fermi level and improbable if the final energy level is completely filled. - For example, modulation doping to a level of 1×1011cm2 gives 1000 carriers/μm2, giving 10 carriers/QD for a quantum dot density of 100 QD/μm2. The infrared light detection will be achieved by the photon-mediated transitions of charged carriers from confined energy levels in the quantum dots (32,34,36,38) to higher confined energy levels in the quantum dots (40), and/or from confined energy levels in the quantum dots (32,34,36,38) to higher energy states in the wetting layer (44) which is formed underneath the quantum dots in the self-assembling growth, and/or from confined energy levels in the quantum dots (32,34,36,38) to higher energy states in the barrier material (48). Light of sufficient energy will excite the carriers from a lower quantum dot energy level to the upper energy levels allowing the carriers to overcome the
barrier 18, and then relax moving along the band edge toward thecollector 30. Anelectric field 46 can be applied to the photodetector by applying a bias across theemitter 6 and the collector 30 (FIG. 1), to assist with thephotocarrier flow 48 and the tunneling across the barriers due to theelectric field 46. If light is continuously applied to thequantum dots 14, a continuous stream of carriers will be excited out of the quantum dots and travel along the band edge to thecollector 30. The barrier layer dimensions are such as to allow a continuous tunneling of carriers from theemitter 6 through the barriers to thequantum dots 14 at a rate sufficient to replace the carriers depleted from the quantum dots by photoemission. Therefore it is possible for the QDIP photodetector to continuously convert the energy of a light signal into an electrical signal. - When used as a photodetector for high speed, the pulsed light signal will cause a burst of carriers to be excited out of the quantum dots and flow to the
collector 30. The rate at which-the carriers can tunnel though the barrier layers to the quantum dots must then at least be as great as the rate at which the carriers are depleted from the quantum dots by the pulsed light signal through photoemission. - The QDIPs will not suffer from the normal incidence limitation because the unique symmetry resulting from confining the carriers in all 3 directions will give finite matrix elements for intersublevel transitions with a polarization vector in any arbitrary direction. It is also expected that the localized nature of the level of origin in the intersublevel transition can contribute to having low dark current. The QDIP photodetector will have a much broader response range in the infrared compared to typical QWIP designs because the self-assembled quantum dots naturally grow with an inhomogeneous broadening in the size, and/or composition and/or strain. For example a photodetector with an active area of 100 microns by 100 microns with 50 layers of quantum dots having an average density of 100 QD/square-micron will contain 50 million quantum dots having small differences in the values of their energy levels. With various possible scenarios for the intersublevel transitions as described above, a broad spectral range of response in the infrared with good efficiency is obtained.
- FIG. 4 is an example of spectral response measured with light incident normal on a QDIP photodetector with 50 layers of InAs quantum dots with Al0.35Ga0.65As barriers modulation doped with electrons, and FIG. 5 is an example of the responsivity measured as a function of the voltage applied on the same QDIP photodetector of FIG. 4 for a detection wavelength of 5 microns. It can be appreciated that the QDIP photodetector has a broad range of detection (here between about 3.5 microns and 6.2 microns), with peak responsivity reaching close to 1 A/W at a wavelength of 5 microns. It should be noted from the above that the QDIP has a good response at normal incidence over a broad range of wavelengths. For many applications, it is believed that the overall responsivity would be proportional to the wavelength-integrated response which would be higher than the one shown in FIG. 5 by a factor directly proportional to the bandwidth of the response.
- Because the fabrication of the quantum dots relies on the self-assembling growth which can combine highly mismatched semiconductor material, the QDIP photodetectors provide an enhanced liberty in the choice of the semiconductor used for the fabrication. This results in a great coverage of possible wavelengths of operation, in addition to the broad range of response for any particular design of device as discussed above. The upper limit in energy is limited by how deep the
level 32 can be with respect to level 48 (FIG. 2), giving a minimum wavelength of about 1.2 microns for a high barrier and a deep quantum dot. There is no similar restriction at long-wavelengths because the quantum dot size and energy levels can be tailored to make the transitions shallow and/or adjust the intersublevel spacing to a small value allowing detection up to 50 microns and possibly beyond. For longer wavelengths however, it will be desirable to operate the device at lower temperatures to avoid thermal excitation of the carriers to the upper levels which causes larger dark current and reduced detectivity. - The QDIP as described herein is based on zero-dimensional heterostructures and can benefit from the properties unique to quantum dots. One obvious advantage gained from using quantum dots in the present invention is that the QDIP is sensitive at normal incidence. The QDIP can also have a broad response range due the inhomogeneous broadening in the ensemble of quantum dots and due to the possibility of various intersublevel transitions. For QDIPs having a wide wavelength response range, the wavelength-integrated responsivity is greatly enhanced. For QDIPs where the wavelength response range is made as narrow as possible, the peak responsivity is greatly enhanced. The QDIP also provides low dark currents. The self-assembled growth method used offers a wide range of possible materials with large lattice mismatched between the semiconductors, therefore increasing the choice of available material for fabrication.
- A person understanding the above-described invention may now conceive of alternative designs, using the principles described herein. All such designs which fall within the scope of the claims appended hereto are considered to be part of the present invention.
Claims (2)
1. A method of producing self-assembled quantum dots having an adjustable number of confined levels and having an adjustable intersublevel spacing which relies on spontaneous island formation during the epitaxy of highly strained semiconductors comprising:
selecting a barrier material and a quantum dot material wherein the amount of their lattice-mismatch dictates a critical thickness required to obtain the spontaneous island formation, and their bandgap difference determines a possible number of confined states in conjunction with the intersublevel spacing;
growing some thickness of the barrier material which has a lattice constant close to the lattice constant of the substrate used;
depositing, at a specified growth rate, the quantum dot material at a substrate temperature which will produce quantum dots having an appropriate size to obtain the intersublevel spacing;
stopping the growth of the quantum dot material after a desired number of quantum dots per unit area is reached;
pausing the growth of the quantum dot material for a predetermined amount of time to allow for self-assembling growth to form the quantum dots in shapes and sizes which will give the intersublevel spacing; and
growing a thickness of the barrier material to cover the quantum dots and return to a planar growth front at a substrate temperature which may be varied during the growth and which will optimize the quality of the quantum dots.
2. The method of claim 15 wherein the intersublevel spacing is between 5 meV and 150 meV, the number of confined states is between 1 and 20, the substrate is GaAs, the barrier material is Alx1Ga1−x1As and the quantum dots are comprised of Alx4(1−x3)Ga(1−x4)(1−X3)Inx3As.