Publication numberUS20020155939 A1
Publication typeApplication
Application numberUS 10/131,237
Publication dateOct 24, 2002
Filing dateApr 25, 2002
Priority dateAug 21, 1996
Publication number10131237, 131237, US 2002/0155939 A1, US 2002/155939 A1, US 20020155939 A1, US 20020155939A1, US 2002155939 A1, US 2002155939A1, US-A1-20020155939, US-A1-2002155939, US2002/0155939A1, US2002/155939A1, US20020155939 A1, US20020155939A1, US2002155939 A1, US2002155939A1
InventorsHiromitsu Seto, Yukihito Nagashima, Isamu Kuroda, Shigekazu Yoshii
Original AssigneeNippon Sheet Glass Co., Ltd.
Export CitationBiBTeX, EndNote, RefMan
External Links: USPTO, USPTO Assignment, Espacenet
Ultraviolet/infrared absorbent low transmittance glass
US 20020155939 A1
Abstract
Ultraviolet/infrared absorbent low transmittance glass having an almost neutral color such as turquoise blue and deep green and exhibiting low or middle visible light transmittance, low total solar energy transmittance, and low ultraviolet transmittance is formed of base glass containing: 65 to 80 wt. % SiO2; 0 to 5 wt. % Al2O3; 2 to 10 wt. % MgO; 5 to 15 wt. % CaO (a total amount of MgO and CaO is 7 to 15 wt. %); 10 to 18 wt. % Na2O; 0 to 5 wt. % K2O (a total amount of Na2O and K2O is 10 to 20 wt. %); and 0 to 5 wt. % B2O3, and colorants including: 1.25 to 2.2 wt. % total iron oxide (T-Fe2O6) expressed as Fe2O3; 0.001 to 0.018 wt. % CoO; 0 or less than 0.0008 wt. % Se; and 0.028 to 0.2 wt. % NiO.
Images(1)
Previous page
Next page
Claims(19)
What is claimed is:
1. An ultraviolet/infrared absorbent low transmittance glass consisting of base glass comprising:
65 to 80 wt. % SiO2;
0 to 5 wt. % Al2O3;
greater than 2 to less than or equal to 10 wt. % MgO;
5 to 15 wt. % CaO wherein a total amount of MgO and CaO is 7 to 15 wt. %;
10 to 18 wt. % Na2O;
0 to 5 wt. % K2O wherein a total amount of Na2O and K2O is 10 to 20 wt. %;
0 to 5 wt. % B2O3,
and colorants comprising:
1.25 to 2.2 wt. % total iron oxide (T-Fe2O3) expressed as Fe2O3;
0.001 to 0.018 wt. % CoO;
0 to 0.0008 wt. % Se; and
0.028 to 0.2 wt. % NiO.
2. An ultraviolet/infrared absorbent low transmittance glass as claimed in claim 1, wherein T-Fe2O3 is equal to or greater than 1.25 wt. % and less than 1.8 wt. %.
3. An ultraviolet/infrared absorbent low transmittance glass as claimed in claim 1, wherein T-Fe2O3 is between 18 wt. % and 2.2 wt. %.
4. An ultraviolet/infrared absorbent low transmittance glass as claimed in claim 1, wherein Se is less than 0.0004 wt. %.
5. An ultraviolet/infrared absorbent low transmittance glass as claimed in claim 4, wherein Se is less than 0.0002 wt. %.
6. An ultraviolet/infrared absorbent low transmittance glass as claimed in claim 4, wherein Se is less than 0.0001 wt. %.
7. An ultraviolet/infrared absorbent low transmittance glass as claimed in claim 1, wherein NiO is equal to or greater than 0.028 wt. % and less than 0.05 wt. %.
8. An ultraviolet/infrared absorbent low transmittance glass as claimed in claim 1, wherein NiO is between 0.05 wt. % and 0.2 wt. %.
9. An ultraviolet/infrared absorbent low transmittance glass as claimed in claim 1, wherein said colorant further comprises CeO2 in an amount of no greater than 2.0 wt. % and/or TiO2 in an amount of no greater than 2.0 wt. %.
10. An ultraviolet/infrared absorbent low transmittance glass as claimed in claim 1, wherein the amount of FeO calculated as Fe2O3 is in the range from 15 to 40% of T-Fe2O3.
11. An ultraviolet/infrared absorbent low transmittance glass as claimed in claim 1, wherein the glass with a thickness of 4 mm has a total solar energy transmittance (TG) smaller than a visible light transmittance (YA) by the C.I.E. illuminant A, and YA is in a range from 23% to 50% and TG is in a range from 7% to 35%.
12. An ultraviolet/infrared absorbent low transmittance glass as claimed in claim 11, wherein YA is between 25% and 40% and TG is between 20% and 35%.
13. An ultraviolet/infrared absorbent low transmittance glass as claimed in claim 11, wherein the glass has a color defined by the following CIELAB coordinates −9<a*<−6 and −3<b*<3.
14. An ultraviolet/infrared absorbent low transmittance glass as claimed in claim 1, wherein said glass has an ultraviolet transmittance of no greater than 6%.
15. An ultraviolet/infrared absorbent low transmittance glass as claimed in claim 1, wherein the glass has a dominant wavelength is in the range of 480 to 520 nanometers when a measurement is made based on a glass thickness of 4 mm using illuminant C.
16. An ultraviolet/infrared absorbent low transmittance glass as claimed in claim 1, wherein the glass has an excitation purity less than 11% when a measurement is made based on a glass thickness of 4 mm using illuminant C.
17. An ultraviolet/infrared absorbent low transmittance glass as claimed in claim 1, wherein NiO is included in the glass such that the glass has a turquoise blue or deep green color by the reinforcement of air blast cooling.
18. An ultraviolet/infrared absorbent low transmittance glass consisting of base glass comprising:
65 to 80 wt. % SiO2;
0 to 5 wt. % Al2O3;
greater than 2 to less than or equal to 10 wt. % MgO;
5 to 15 wt. % CaO wherein a total amount of MgO and CaO is 7 to 15 wt. %;
10 to 18 wt. % Na2O;
0 to 5 wt. % K2O wherein a total amount of Na2O and K2O is 10 to 20 wt. %; and
0 to 5 wt. % B2O3,
and colorants without Se comprising:
1.25 to 2.2 wt. % total iron oxide (T-Fe2O3) expressed as Fe2O3;
0.001 to 0.018 wt. % CoO; and
0.028 to 0.2 wt. % NiO.
0.003 to 0.2 wt. % NiO.
19. An ultraviolet/infrared absorbent low transmittance glass as claimed in claim 18, wherein NiO is included in the glass such that the glass has a turquoise blue or deep green color by the reinforcement of air blast cooling.
Description
    CROSS REFERENCE TO RELATED APPLICATION
  • [0001]
    This is a continuation-in-art application of patent application Ser. No. 909,728 filed on Aug. 12, 1997 abandoned, Ser. No. 189,638 filed on Nov. 10, 1998 abandoned, and Ser. No. 09/524,589 filed on Mar. 14, 2000.
  • BACKGROUND OF THE INVENTION AND RELATED ART STATEMENT
  • [0002]
    The present invention relates to an ultraviolet/infrared absorbent low transmittance glass. More particularly, it relates to an ultraviolet/infrared absorbent low transmittance glass which has an almost neutral color such as turquoise blue shade and deep green shade so that it is useful for windows of vehicles or buildings when used in combination with a glass having green shade with high visible light transmittance, and which has low or middle visible light transmittance, low total solar energy transmittance, and low ultraviolet transmittance so. that it is suitable for use as privacy glazing in a vehicle.
  • [0003]
    Recently, a variety of glasses with ultraviolet/infrared absordability to be used as a vehicle windshield have been proposed with the view of preventing degradation of luxurios interior-materials and reducing cooling load of the vehicle In view of privacy protection, glass with relatively low visible light transmittance is preferably used for a rear window glass of a vehicle. Such kinds of &ss include the followings.
  • [0004]
    For example a dark gray colored infrared absorbent glass disclosed in Japanese Patent Publication No 7-29813 consists of soda-lime-silica glass including coloizets consisting of 1.00 to 1.7 weight percent Fe2O3 (total iron), at least 0.27 weight percent FeO, 0.002 to 0.005 weight percent Se, and 0.01 to 0.02 weight percent CoO. The glass exhibits luminous transmittance less than 32 percent and total solar infrared transmitance less than 15 percent at 3.0 mm thickness.
  • [0005]
    A dark gray colored glass disclosed in Japanese Unexamined Published Patent Application No. 8-57232 consists of soda-lime-silica glass including colorants consisting of 0.8 to 1.4 weight percent Fe2O3 (total iron), less than 0.21 weight percent FeO, 0.05 to 1.0 weight percent TiO2, 0.02 to 0.05 weight percent CoO, and 0.0005 to 0.015 weight percent Se.
  • [0006]
    A neutral gray colored glass disclosed in claim 25 of U.S. Pat. No. 5,393,593 has a base glass composition comprising 66 to 75 weight percent SiO2, 10 to 20 weight percent Na2O, 5 to 15 weight percent CaO, 0 to 5 weight percent MgO, 0 to 5 weight percent Al2O3, and 0 to 5 weight percent K2O, and colorants consisting of 1.00 to 2.2 weight percent Fe2O3 (total iron), at least 0.20 weight percent FeO, 0.0005 to 0.005 weight percent Se, and 0.010 to 0.030 weight percent CoO. The glass exhibits luminous transmittance less than 35 percent and total solar infrared transmittance less than 20 percent at 3.9 mm thickness.
  • [0007]
    A soda-lime-silica glass disclosed in Japanese Publication of PCT No 8-506314 has a neutral color by including primary iron given by the following expression:
  • [0008]
    FeO (weight percent)≧0.007+(optical concentration −0.036)/2.3 and 0.25 to 1.75 weight percent Fe2O3 and at least one selected from a group consisting of Se, Co3O4, Nd2O3, NiO, MnO, V2O5, CeO2, TiO2, CuO, and SnO. The glass exhibits luminous transmittance more than 32 percent, ultraviolet transmittance less than 25 percent, direct solar ener trasmittance at least 7 percent less than the luminous transmittance, and dominant wavelengths preferably less than 570 nanometers at 4 mm thickness. Certain embodiments thereof may be used as a privacy glazing.
  • [0009]
    In both the dark gray colored infrared absorbent glass disclosed in Japanese Patent Publication No. 7-29813 and the dark gray colored glass disclosed in Japanese Unexamined Published Patent Application No. 8-157232, a great quantity of Se is used for providing a desiale color. Such a great quantity of Se is unpreferable for the environment because Se has toxicity and is easy to vaporize. The above dark gray glass including 0.05 to 1.0 weight percent TiO2 as an essential component is unpreferable because TiO2 is expensive to increase the batch cost.
  • [0010]
    The neutral gray colored glass disclosed in U.S. Pat. No. 5,393,593 is also unpreferable because of the great content of Se. The great content of FeO is preferable in view of heat ray absorptivity, FeO is on the contrary not preferable because it selectively absorbs infrared ray in a wavelength from 1,000 to 1,200 nanometers so that in case the glass is produced by a normal melting furnace, it absorbs most efficient portion in flame luminance distribution so as to lower the temperature of bottom base of the furnace and then contribute to various defects.
  • [0011]
    Though the aforementioned glass with low visible light transmitance is superior in view of privacy protection, an occupant in a vehicle cabin sees outside quite unclearly through the glass. On the other hand a glass with middle transmittance can be sufficient to some extent for both privacy protection and safety. These types of glass are chosen according to portions in a vehicle and circumferences.
  • [0012]
    The aforementioned glass includes selenium in high concentration to provide optical properties, without essentially including nickel.
  • [0013]
    The glass of Japanese Publication PCT No. 8-506314, which can be used for privacy protection, is provided with a neutral color by including colorants consisting all of nickel, selenium, and cobalt, just as described in this specification. However, it is necessary to add a great quantity of Se since the content of nickel is low.
  • OBJECT AND SUMMARY OF THE INVENTION
  • [0014]
    It is an object of the present invention to provide an ultraviolet-infrared absorbent low transmittance glass which has an almost neutral color such as turquoise blue and deep green and which has low or middle visible light transmittance, low ultraviolet transmittance and low total solar energy transmittance.
  • [0015]
    The ultraviolet infrared absorbent low transmittance glass of the present invention consists of a base glass, that is, the major constituents comprising:
  • [0016]
    65 to 80 wt. % SiO2;
  • [0017]
    0 to 5 wt. % Al2O3;
  • [0018]
    greater than 2 to less than or equal to 10 wt. % MgO;
  • [0019]
    5 to 15 wt. % CaO wherein a total amount of MgO and CaO is 7 to 15 wt. %;
  • [0020]
    10 to 18 wt. % Na2O;
  • [0021]
    0 to 5 wt. % K2O wherein a total amount of Na2O and K2O is 10 to 20 wt. %;
  • [0022]
    0 to 5 wt. % B2O3,
  • [0023]
    and colorants comprising:
  • [0024]
    1.25 to 2.2 wt. % total iron oxide (T-Fe2O3) expressed as Fe2O3;
  • [0025]
    0.001 to 0.018 wt. % CoO;
  • [0026]
    0 to 0.0008 wt. % Se; and
  • [0027]
    0.028 to 0.2 wt. % NiO.
  • BRIEF DESCRIPTION OF THE DRAWING
  • [0028]
    [0028]FIG. 1 is a diagram showing changes ian color shade during reinforcing process in each example.
  • PREFERRED EMBODIMENTS
  • [0029]
    The description will be made as regard to an ultraviolet/infrared absorbent low transmittance glass composition. It should be noted that components will be represented with percentage by weight.
  • [0030]
    SiO2 (silica) is a principal component for forming skeleton of glass. Less than 65% SiO2 lowers the durability of the glass and mare than 80% SiO2 raises the melting temperature of the glass so high.
  • [0031]
    Al2O3 is a component or improving the durability of the glass. More than 5% Al2O3 raises the melting temperature of the class so high. The preferable range of Al2O3 is between 0 1% and 2%.
  • [0032]
    MgO and CaO improve the durability of the glass and adjust a devitrification temperature and viscosity of the glass during molding. More than 10% MgO raises the devitrification temperature. Less than 5% or more than 15% CaO raises the devitrification temperature of the glass. The durability of the glass is lowered when the total amount of MgO and CaO is less than 7%, while the devitrificaton temperature is increased when the total exceeds 15%.
  • [0033]
    NaO and KO prompt the glass to melt. The efficiency of promotion of melting becomes poor when Na2O is less than 10% or the total of Na2O and K2O is less than 10%, while the durability of the glass is lowered when Na2O exceeds 18% or the total of Na2O and K2O exceeds 20%. K2O is preferable not to exceed 5% because of its expensive cost.
  • [0034]
    B2O3 is a component for improving the durability of the prompting to melt, and yet enhancing the ultraviolet absorption. B2O3 should be less than 5%, since the transmittance is reduced also at a visible range so that the color of the glass is easy to tint yellow and difficulties during molding are caused due to the vaporization of B2O3 when B2O3 exceeds 5%.
  • [0035]
    Iron oxide is present in the form of Fe2O3 and the form of FeO in the glass Fe2O3 is a component for improving the ultraviolet absorptivity and FeO is a component for improving the heat ray absorptivity.
  • [0036]
    When the total amount of iron oxide expressed as Fe2O3 (T-Fe2O) is less than 1.2% the efficiency of ultraviolet and infrared absorptivity becomes small so as not to provide desired optical properties. On the other hand, when T-Fe2O3 exceeds 2.2%, there is an unpreferable possibility that the temperature around a crown of a glass melting furnace exceeds its refractory temperature due to absorption of the heat ray by the ferrous oxide. In addition in case of successively producing glass by a glass melting furnace with T-Fe2O3 exceeding 2.2%, long time is required to alter a glass composition in the furnace. T-Fe2O3 content is preferably equal to or more than 1.2% and less than 1.8% (more preferably between 1.25% and 1.35%) or between 1.8% and 2.2%.
  • [0037]
    Equal to or more than 1.2% and less than 1.8% T-Fe2O3 can offer advantages of small load to the furnace because the glass composition in the succesive glass melting furnace is altered to another composition within a short time. In this case, sufficient efficiency of ultraviolet absorptivity is sometimes not obtained only by iron. However, the efficiency of ultraviolet absorptivity can be improved by adding, for example, CeO2TiO2 within the ranges defined by the present invention.
  • [0038]
    Particularly 1.25% to 1.35% T-Fe2O3 can offer the aforementioned advantages and sufficient efficiency of ultraviolet absorptivity only by iron.
  • [0039]
    1.8% to 2.2% T-Fe2O3 makes the time longer to change the glass composition in the furnace, and the load to the furnace becomes greater. However, great efficiency of ultraviolet absorptivity can be obtained with low batch cost.
  • [0040]
    Fe2O3 has a function of particularly increasing the absorptivity in ultraviolet range when glass is reinforced by air blast cooling. This means that the glass of this invention can obtain enough efficiency of ultraviolet absorptivity without using expensive ultraviolet absorbent such as CeO2 and TiO2. Then T-Fe2O3 is in the range mentioned above, the desired color shade of the glass can be obtained after discoloration due to the reinforcement process by air blast cooling.
  • [0041]
    The ratio (by weight) of FeO/T-Fe2O3 is preferably between 10% and 40%. When the ratio is less than 10%, enough heat ray absorptivity can not be obtained because of a small amount of FeO.
  • [0042]
    Then the FeO/T-Fe2O3 ratio exceeds 40%, the visible light transmittance is reduced and the color is of a blue tint. In addition, nickel sulfide particles are sometimes present in the molten glass because of a great quantity of Fe2+ having reducing characteristics in the molten glass. The FeO/T-Fe2O3 ratio exceeding 40% causes streaks with enough silica and causes silica scum. The FeO/T-Fe2O3 ratio in a range between 10% and 40% brings a green shade which is an almost neutral color having high ultraviolet absorbability and high heat ray absorptivity. In this case, values convorted to Fe2O3 are used for the content of FeO.
  • [0043]
    CoO is a component for forming an almost neutral color such as turquoise blue shade and deep green shade by cooperating with Se and/or NiO, and Fe2O3 for controlling the visible light transmittance. Less than 0.001% CoO can not form a desired color shade and makes the visible light transmittance too high. More than 0.03% CoO makes the color of too blue tint and reduces the visible light transmittance. Equal to or less than 0.018% (180 ppm) of CoO makes the color shade of the glass dark green.
  • [0044]
    Se contributes a pink color, so that it reduces the excitation purity with the aid of a complementary color of CoO. Then NiO is included, Se may not be always included. More than 0.0008% Se reduces the visible light transmittance. Then using Se, the content thereof is preferably in a range of equal to or less than 0.0008% (8 ppm), more preferably equal to or less than 4 ppm, yet more preferably equal to or less than 2 ppm, most preferably equal to or less than 1 ppm. The more deep color the glass has, the lower its visible light transmittance becomes and the glass generally has the high excitation purity and the strong color impression even in the same color co-ordinate. Se of less than 0.0008% (8 ppm)in the glass decreases the excitation purity of the glass and makes the glass to have a soft color at the same color tone without losing the objective green or blue shade green color of the glass. As mentioned, the desired color shade can be obtained with a significantly smaller amount of Se than the amount conventionally required or without Se.
  • [0045]
    NiO is a component for controlling the visible light transmittance and for reducing the excitation purity as CoO. When NiO is more than 0.2%, nickel sulfide stones are sometimes present in the product and the visible light transmittance is reduced. In addition, the obtained shade becomes too greenish. The content of NiO is in a range between equal to or more than 0.028% and less than 0.2% preferably in a range between 0.05% and 0.2% for low visible light transmittance.
  • [0046]
    Then the concentration of NiO in the glass is too high. there is a possibility that NiO coagulates to form a nickel sulfide stones. However, when NiO is in the range defined by this invention, the desired color shade can be obtained without producing the nickel sulfide stones.
  • [0047]
    It is known that the coordination number of NiO varies according to the rate of cooling glass so that the color of the glass varies. This is because the cooling varies the coordination number of oxide around Ni2+ from 6 into 4 and thus varies the optical absorption. The absorption of N2+ with 6 coordinating atoms exists around 430 nanometers so as to contribute yellow to the glass, while the absorption of Ni2+ with 4 coordinating atoms exists from 500 to 640 nanometers. Therefore, the excitation purity would be reduced to obtain the preferable shade by using Ni2+ with 4 coordinating atoms. Windshields of a passenger car are normally reinforced by air blast cooling for safety. The reinforcement process by air blast cooling also varies the coloring condition of NiO. In the present invention, the desired color shade can be obtained without adding Se by the discoloration due to the reinforcement process by air blast cooling.
  • [0048]
    CeO2 is a component for improving the ultraviolet absorptivity and is present in the form of Ce3+ or in the form of Ce4+ in glass. Particularly, Ce3+ is effective in absorbing ultraviolet with less absorptivity in the visible range. In the present invention, oxide of Ce3+ is also expressed in terms of CeO2 and is included in the total amount of CeO2.
  • [0049]
    TiO2 is a component for improving the ultraviolet absorptivity particularly by interaction with FeO. TiO2 can be added to improve the ultraviolet absorptivity within such a range as not to lose the almost neutral color such as turquoise blue shade and deep green shade, or to add a yellow tint in order to obtain the desired color shade. The use of expensive CeO2, TiO2 increases the cost so that it is not preferable to use more than 2% CeO2, TiO2.
  • [0050]
    One or more than two among MnO, V2O5, MoO3, CuO, Cr2O3, and the like may be added as colorant and SnO2 within a rang from 0% to 1% total may be added as a reducing agent in such a range as not to lose middle transmittance and the almost neutral color such as turquoise blue shade and deep green shade. To further securely prevent the formation of nickel sulfide stones, ZnO may be added in a range from 0% to 1%.
  • [0051]
    In the present invention, when measured by using C.I.E. standard illuminant “A”, the total solar energy transmittance (TG) is preferably lower than the visible light transmittance (YA). it is preferable that YA is in a range from 23 to 50% and TG is in a range from 7 to 35% when the measurement is made based on a glass thickness of 4 mm. More preferably, YA is in a range from 25 to 40% and TG is in a range from 20 to 35%. In cse of using L* a* b* color system, the chromaticity, expressed by a* and b*, of the glass color are preferably in ranges of −9<a*<−6 and −3<b*<3, respectively.
  • [0052]
    In the present invention, the glass preferably has YA between 10% and 25% and TG between 10% and 35% at a thickness from 3.1 to 5 mm. In this case, the chromaticity, expressed by a* and b* under L* a* b* color system, of the glass color is preferably in ranges of −7a*<−2 and −3<b*<7, respectively.
  • [0053]
    When measured by using C.I.E. standard illuminant “C” over the wavelength range 380 to 770 nanometers, the glass of the present invention preferably has optical properties with dominant wavelengths in the range of 480 to 580 and excitation purity less than 11%.
  • [0054]
    The glass of the present invention preferably exhibits ultraviolet transmittance defined by ISO 9050, less than 6%.
  • EXAMPLES
  • [0055]
    Hereinafter, the mode of carrying out the present invention will be described referring to some examples.
  • Examples 1 Through 42
  • [0056]
    Glass raw material is prepared by adding at least one of a group consisting of ferric oxide, titanium oxide, cerium oxide, cobalt oxide, metallic selenium, and nickel oxide into a standard soda-lime silica glass batch composition, also adding carbonaceous reducing agent (concretely, coke powder etc.) at a ratio of about 0.01 parts by weight per 100 parts of the glass raw material therein, and mixing them. The glass raw material thus prepared is heated and melted in an electric furnace at 1500 C. for 4 hours. The molten glass is flowed onto a stainless plate and annealed to the room temperature as long as 16 hours to obtain a 6 mm thick glass plate. The glass plate is then polished in such a manner that the thickness reduces to 4 mm to become a sample. Each sample is measured in the visible light transmittance by the C.I.E illuminant A(YA), the total solar energy transmittance (TG). the ultraviolet transmittance by ISO 9050(TUV), the dominant wavelength by the illuminant C(DW), and the excitation purity (Pe). Before measuring the optical properties, some of the samples are cooled by blasting air after re-heating in order to reinforce them.
  • [0057]
    Tables 1-4 show base glass compositions of the obtained samples, T-Fe2O3 concentration, FeO (converted to Fe2O3)/T-Fe2O3 rate, CoO concentration, Se concentration, NiO concentration, CeO2 concentration, and TiO2 concentration. The numerals in Tables are indicated as a percentage of the weight except that CoO concentration, Se concentration, and NiO concentration are expressed in ppm. The percentages of SiO2 are indicated without figures after decimal points because the figures after decimal points are rounded off. Tables 1-4 also show the optical properties of the respective samples.
  • [0058]
    All of the samples of Examples 1 through 21 are characterized by visible light transmittance (YA) between 23% and 50%, total solar energy transmittance (TG) between 7% and 30%, and ultraviolet transmittance (TUV) less than 6%. These are also characterized by dominant wavelength (DW) measured by using the illuminant C between 480 and 525 nanometers, and excitation purity less than 11%.
  • [0059]
    It is shown that Examples 2-6, 10, and 11 have the same or improved properties as the glass of Example 1, although these are free of NiO.
  • [0060]
    The examples 7-9, 12-16 have the same or improved properties as the glass Example 1, although these are free of Se.
  • [0061]
    In Examples 2-9, the furnace's load during melting can be reduced because of small amount of T-Fe2O3.
  • [0062]
    Examples 10-16 have improved ultraviolet absorptivity and improved infrared absorptivity because of large amount of T-Fe2O3.
  • [0063]
    In order to enhance the ultraviolet absorptivity, relatively large amount of TiO2 is added in Examples 17-19, and CeO2 is added in Example 20. These examples have large ultraviolet absorptivity without losing the visible light transmittance and total solar ultraviolet transmittance.
  • [0064]
    Example 21 is added with CuO in order to reduce the total solar ultraviolet transmittance, and can exhibit high infrared absorptivity without losing the visible light transmittance and the ultraviolet absorptivity.
  • [0065]
    Examples 6, 7, and 14 have high visible light transmittance while having high infrared absorptivity and yet have high ultraviolet absorptivity so that these are superior in prevention of degradation of interior materials and reduction of cooling load of the vehicle. Therefore, these are suitable for the privacy protection type of visible light transmission glass, for example, rear windows of vehicles, windows of buildings, and the like.
  • [0066]
    The ultraviolet absorptivity and the infrared absorptivity of Examples 22-29 are slightly small. These samples contain smaller amount of T-Fe2O3 and the FeO/T-Fe2O3 ratio is set relatively low, so that they are superior in productivity.
  • [0067]
    Among these examples, Examples 23-29 have the same or improved properties as the glass of other examples, although these are free of Se.
  • [0068]
    Example 25 exhibits middle visible light transmittance and low infrared/ultraviolet transmittance.
  • [0069]
    Examples 26, 28, and 29 exhibit low visible light transmittance and low infrared/ultraviolet transmittance.
  • [0070]
    Examples 30-35 and 38 show results of measuring optical properties before and after the reinforcement process by air blast cooling.
  • [0071]
    Among these examples, Examples 30-32 exhibit middle visible light transmittance and low infrared/ultraviolet transmittance and have an almost neutral color such as turquoise blue shade and deep green shade. The ultraviolet transmittance is improved about 1.5% by the reinforcement process.
  • [0072]
    Examples 33-35 exhibit low visible light transmittance and low infrared/ultraviolet transmittance. The ultraviolet transmittance is improved about 2% by the reinforcement process.
  • [0073]
    Each of Examples 30-35 has a preferable color shade which is an almost neutral color of gray tint through the reinforcement process. FIG. 1 shows a coordinate diagram of colors indicated by a*, b* for illustrating how points are moved by the reinforcement process in the aforementioned examples.
  • [0074]
    It would be apparent from the diagram that all of the points move toward the origin according to the reinforcement process so that the colors become closer to the desired color shade, i.e. almost neutral colors having reduced excitation purity.
  • [0075]
    Therefore, when the glass compositions of the examples mentioned above are used for windshields of vehicles and windows of building good effects of preventing degradation of interior materials and of privacy protecting can be expectant
  • Comparative Examples 1-4
  • [0076]
    Table 5 shows glass components and optical properties of Comparative Examples which are made in the same manner as Examples 1-35 but the glass components are different.
  • [0077]
    All of Comparative Examples 1-4 have components out of the range of the present invention. Comparative Example 1 contains NiO as a colorant, an amount of which is out of the claimed range, and Comparative Example 2 contains T-Fe2O3, an amount of which is out of the claimed range. Comparative Example 3 has the same components as the example of Japanese Unexamined Published Patent Application No. H8-157232 as referred above and Comparative Example 4 has the same components as the example of U.S. Pat. No. 5,393,593, as referred above. IT should be noted that the optical properties of Comparative Example 3 are indicated in values converted beed on a glass thickness of 5 mm and the optical properties of Comparative Example 4 are indicated in values converted based on a glass thickness of 3.9 mn
  • [0078]
    It would be apparent from Table 5 that as compared with the examples of the present invention, Comparative Examples 1 and 2 do not have an almost neutral color such as turquoise blue shade and deep green shade and yet do not exhibit low or middle visible light transmittance, low infrared transmittance, and low ultraviolet transmittance. Comparative Examples 3 and 4 are not preferable in view of productivity and environment because a large amount of expensive and poisonous Se is used therein.
  • Examples 36, 37, Comparative Example 5
  • [0079]
    Table 6 shows glass components and optical properties of Examples 36,37 and Comparative Example 5 which are made in the same manner as Examples 1-35 except the glass components are different.
  • [0080]
    As shown in Table 6, Se in the glass with a very small amount decreases remarkably an excitation purity of the glass while changing scarcely a color tone of the glass. More than 2 ppm of Se in the glass changes the color tone of the glass remarkably from green to green shade brown or green shade gray.
  • [0081]
    As detailed above, according to the present invention, an ultraviolet/infrared absorbent low transmittance glass which exhibits low or middle visible light transmittance, low total solar energy transmittance, and low ultraviolet transmittance and which has an almost neutral color such as turquoise and deep green, can be provided.
  • [0082]
    The ultraviolet/infrared absorbent low transmittance glass having the almost neutral color such as turquoise and deep green can exhibit the effect of preventing degradation and discoloration of interior materials and the privacy protecting effect when the glass is used for a rear window glass of a vehicle, a window of a building, or the like.
  • [0083]
    The specification refers to the disclosure of application Ser. No. 909,728 filed on Aug. 12, 1997 abandoned, No.189,638 filed on Nov. 10, 1998, abandoned, and No. 09/524,589 filed on Mar. 14, 2000.
    TABLE 1
    Example 1 2 3 4 5 6 7 8 9 11 12
    SiO2 71 71 71 71 71 71 71 71 71 71 71
    Al2O3 1.6 1.6 1.6 1.6 1.6 1.6 1.6 1.6 1.6 1.6 1.6
    MgO 3.6 3.6 3.6 3.6 3.6 3.6 3.6 3.6 3.6 3.6 3.6
    CaO 7.7 7.7 7.7 8.4 7.7 7.7 7.7 7.7 7.7 7.7 7.7
    Na2O 13.7 13.7 13.7 13.1 13.7 13.7 13.7 13.7 13.7 13.7 13.7
    K2O 0.9 0.9 0.9 0.9 0.9 0.9 0.9 0.9 0.9 0.9 0.9
    B2O3 0.2
    T-Fe2O3 1.9 1.3 1.7 1.5 1.4 1.4 1.7 1.5 1.4 1.9 1.8
    FeO/T-Fe2O3 0.24 0.28 0.24 0.24 0.25 0.27 0.26 0.24 0.26 0.20 0.23
    CeO2
    TiO2 0.03 0.03 0.03 0.03 0.03 0.03 0.03 0.03 0.03 0.03 0.03
    Se (ppm) 3 5 2 3 4 3 3 1
    CoO (ppm) 100 95 113 107 101 92 94 96 98 125 119
    NiO (ppm) 30 150 200 250
    YA 30.8 38.2 34.1 35.1 37.0 36.2 35.4 38.2 37.5 33.1 32.9
    TG 18.7 23.5 20.6 21.7 23.3 20.0 19.7 23.4 23.3 20.6 19.5
    Tuv (ISO) 1.9 5.7 2.8 3.4 4.4 5.1 3.0 4.6 5.5 1.7 2.1
    dominant 519 492 494 496 495 498 499 498 497 499 495
    wavelength Dw 4.5 7.4 7.7 5.9 6.0 7.1 6.8 6.7 6.8 6.2 8.2
    excitation purity P e
  • [0084]
    [0084]
    TABLE 2
    Example 12 13 14 15 16 17 18 19 20 21
    SiO2 70 70 70 70 70 71 71 69 70 71
    Al2O3 1.6 1.6 1.6 1.6 1.6 1.6 1.6 1.6 1.6 1.6
    MgO 3.6 3.6 3.6 3.6 3.6 3.6 3.6 3.6 3.6 3.6
    CaO 7.7 8.4 8.4 8.4 8.4 8.4 8.4 7.7 8.4 7.7
    Na2O 13.7 13.1 13.1 13.1 13.1 13.1 13.1 13.7 13.1 13.7
    K2O 0.9 0.9 0.9 0.9 0.9 0.9 0.9 0.9 0.9 0.9
    B2O3 0.5
    T-Fe2O3 2.2 2.2 1.9 1.8 1.3 1.3 1.5 1.4 1.3 1.3
    FeO/T-Fe2O3 0.34 0.30 0.24 0.22 0.31 0.28 0.29 0.30 0.40 0.23
    CeO2 1
    TiO2 0.03 0.03 0.03 0.03 0.5 0.5 0.5 1.6 0.03 0.03
    Se (ppm) 5 2
    CoO (ppm) 98 100 90 92 130 95 75 115 75 110
    NiO (ppm) 300 300 50 100 300 500 500
    others CuO
    0.22
    YA 23.0 23.2 35.6 37.7 31.9 38.0 30.4 28.0 30.4 43.9
    TG 10.2 11.1 19.3 21.8 20.5 23.2 15.4 16.1 15.4 28.1
    Tuv (ISO) 0.9 1.0 1.9 2.6 4.0 3.7 3.9 1.6 3.9 3.8
    dominant 511 517 499 500 497 516 520 525 514 492
    wavelength Dw 7.3 6.6 7.4 6.6 7.5 4.1 8.3 9.8 8.3 9.6
    excitation purity P e
  • [0085]
    [0085]
    TABLE 3
    Example 22 23 24 25 26 27 28 29
    SiO2 71 71 71 70 71 71 71 71
    Al2O3 1.6 1.6 1.6 1.6 1.6 1.6 1.6 1.6
    MgO 3.6 3.6 3.6 3.6 3.6 3.6 3.6 3.6
    CaO 7.7 7.7 7.7 7.7 7.7 7.7 7.7 7.7
    Na2O 13.7 13.7 13.7 13.7 13.7 13.7 13.7 13.7
    K2O 0.9 0.9 0.9 0.9 0.9 0.9 0.9 0.9
    B2O3
    T-Fe2O3 1.2 1.4 1.7 1.3 1.3 1.4 1.3 1.3
    FeO/T-Fe2O3 0.24 0.21 0.19 0.19 0.16 0.17 0.17 0.17
    CeO2 0.4
    TiO2 0.03 0.03 0.03 0.03 0.50 0.03 0.03 0.03
    Se (ppm) 3
    CoO (ppm) 110 130 100 120 300 80 180 200
    NiO (ppm) 390 250 300 600 1900 1050 1000
    YA 37.9 35.4 37.4 38.3 18.7 17.7 20.2 19.9
    TG 21.2 28.4 24.6 29.8 25.2 21.8 21.1 23.2
    Tuv (ISO) 5.6 8.3 2.6 3.6 4.9 8.1 6.4 6.8
    dominant 496 496 510 499 485 565 555 543
    wavelength Dw 5.9 6 4.7 5.3 16.1 22.9 9.7 5.9
    excitation purity P e
  • [0086]
    [0086]
    TABLE 5
    Comparative
    Example 1 2 3 4
    SiO2 71 71 72 66
    Al2O3 1.6 1.6 1.7 3.1
    MgO 3.6 3.6 4.1 3.1
    CaO 8.4 8.4 7.8 7.9
    Na2O 13.1 13.1 13.5 17.8
    K2O 0.9 0.9 0.5
    B2O3
    T-Fe2O3 1.4 1.0 1.4 1.5
    FeO/T-Fe2O3 0.61 0.21 0.17 0.18
    CeO2
    TiO2 0.03 0.03 0.1
    Se (ppm) 43 40
    CoO (ppm) 135 150 235 213
    NiO 2200 300
    thickness (mm) 4 4 5 3.9
    YA 12.6 40.0 17.1 15.6
    TG 7.2 33.1 16.6 16.7
    Tuv (ISO) 8.8 21.7 2.5 4.7
    dominant 587 483 530 576
    wavelength Dw
    excitation purity Pe 18.0 20.5 3.9 8.9
  • [0087]
    [0087]
    TABLE 6
    Comparative
    Example Example 26 Example 37 Example 5
    SiO2 71 71 71
    Al2O3 1.6 1.6 1.6
    MgO 3.6 3.6 3.6
    CaO 7.7 7.7 7.7
    Na2O 13.7 13.7 13.7
    K2O 0.9 0.9 0.9
    B2O3
    NiO (ppm) 770 770 770
    Se (ppm) 0 1 2.1
    CoO (ppm) 180 180 180
    TiO2 0.03 0.03 0.03
    t-Fe2O3 1.26 1.26 1.26
    FeO/T-Fe2O 0.216 0.214 0.209
    YA 21.8 21.4 20.5
    TG 18.6 18.6 18.5
    L* 54.6 54.1 53.1
    a* −8.8 −8.5 −7.8
    b* −0.0 0.9 1.2
    dominant 496.4 499.6 501.8
    wavelength Dw
    excitation purity Pe 6.38 5.16 4.37
  • [0088]
    [0088]
    TABLE 7
    Example 38 39 40 41 42
    SiO2 70.5 70.5 70.5 70.5 70.5
    Al2O3 1.6 1.6 1.6 1.6 1.6
    CaO 8.0 8.0 8.0 8.0 8.0
    MgO 3.7 3.7 3.7 3.7 3.7
    Na2O 13.9 13.9 13.9 13.9 13.9
    K2O 0.8 0.8 0.8 0.8 0.8
    T-Fe2O3 1.25 1.3 1.25 1.27 1.4
    FeO/T-Fe2O3 0.23 0.18 0.23 0.23 0.21
    TiO2 0.03 0.03 0.02 0.03 0.06
    Se (ppm) <1
    CoO (ppm) 110 120 170 130 130
    NiO (ppm) 310 300 450 280 330
    before after
    YA (%) 37.3 35.0 38.4 30.1 30.7 34.3
    TG (%) 26.6 25.5 30.1 26.5 26.1 24.3
    Tuv(iso) (%) 10.1 7.6 6.8 8.2 7.2 5.6
    L* 67.57 66.66 85.56 62.82 68.03 66.33
    a* −9.33 −8.65 −9.73 −7.53 −10.63 −11.3
    b* −1.3 −1.34 −0.33 −2.52 −3.12 −0.59
    Dw (nm) 493.6 493.3 495.7 490.9 491.2 495.3
    P e (%) 6.9 6.7 6.13 8.87 9.61 7.57