US 20050008821 A1
There is disclosed a method and apparatus for producing a polymeric film that accurately replicates a complex mold surface at least a portion of which surface has microstructured or nano-structured dimensions. A polymeric powder is electrodeposited on an underlying mold surface. Then the powder is cured to create a polymeric film. Finally the film is removed from the mold surface.
1. A method of producing a polymeric film that accurately replicates a complex mold surface at least a portion of which surface has microstructured or nano-structured dimensions, comprising the steps of:
(a) electrodepositing a polymeric powder on an underlying mold surface;
(b) curing the powder to create a polymeric film; and
(c) removing the polymer film.
2. The method of
3. The method of
4. The method of
5. The method of
6. The method of
7. The method of
8. The method of
9. The method of
10. The method of
11. The method of
12. The method of
13. The method of
14. The method of
15. The method of
16. The method of
17. The method of
18. The method of
19. The method of
20. The method of
21. The method of
22. The method of
23. The method of
24. The method of
25. The method of
26. The method of
27. The method of
28. The method of
29. The method of
30. A method of making a polymer film having at least one area of complex pattern of recesses and raised areas above and below the plane of the film, with the pattern shapes including at least some of small macrostructure dimensions, comprising the steps of
(a) electrodepositing a polymeric powder into the facing areas of opposed mold faces defining the pattern shapes to be formed;
(b) transporting the opposing faces through a cure station where the powder is melted and then coated; and
(c) stripping the cured film from the opposing mold faces.
31. The method of
32. An article comprising a polymeric film having a portion which is a surface area of a complex array of microstructure of optically precise dimensions and wherein said article is formed by curing a powder which has been electrodeposited against a mold surface defining the shape of at least a portion of the article.
33. The article of
34. The article of
35. The article of
36. The article of
37. The article of
38. The article of
39. The article of
40. The article of
41. Apparatus for continuously producing a web of film having a complex microstructured or nano-structured pattern in at least a portion thereof, comprising:
(a) a mold having the microstructured or nano-structured pattern in a surface thereon;
(b) means for electrodepositing a polymeric powder onto said surface;
(c) means for effecting a cure of said powder to form a film having the desired microstructured or nano-structured pattern thereon; and
(d) means for facilitating removal of said film from said mold.
42. The apparatus of
43. The apparatus of
44. The apparatus of
45. The apparatus of
46. The apparatus of
This application claims the benefit of U.S. provisional patent application Ser. No. 60/485,268, entitled “A Process And Apparatus for Fabricating Precise Microstructures And Polymeric Molds for Making Same.”
Fabrication of microstructured and nano-structured products known to be of interest in various industries include arrays of structured elements having optical applications, such as lenticular lenses, Fresnel lenses, light guides, diffusers, retro-reflective films, micro-lens arrays, brightness enhancement film (BEF) and LED arrays. Other applications include , biomedical components, micro-fluidic products, tissue culture media, micro-electrical-mechanical (MEMS), micro-acoustical, Chemical Mechanical Planerization (CMP), fuel cells, and other geometries that benefit from high speed, precision, microfabrication technology that provides high volume commercialization at economical cost.
The present invention has novel advantages because mold cost and fabrication time is reduced, which translates to faster scale-up and commercialization but also benefits from higher manufacturing speed than the prior art. The invention also allows the use of a wider range of materials than the prior art, including both thermoplastic, and thermoset polymers, either potentially loaded with other second phase or filler materials such as, for example, ceramic, glass or metal powders. Such latitude in prior art processing does not exist or creates significant tool wear. The present invention provides the ability to microform materials withstanding higher use temperatures or that become polymer composites, having improved mechanical, electrical or optical properties which are of significant benefit for some end use applications, beyond the narrow range of typically used polymers.
The present invention adapts several commercially known techniques to achieve novel results.
In accordance with the present invention, polymeric products can be made by electrodepositing powdered polymer by means of a variation of the process generally known as powder coating. This process, sometimes referred to as solventless or dry painting, does not require the use of any liquids and therefore eliminates the problems associated with air entrapment. Powder is applied to the mold from the bottom up eliminating the possibility of air being trapped and speed is only limited by the melt time and cure rate of the polymer.
The powder coating industry is well known for coating metal substrates but has more recently made significant innovations to reduce both the cure temperature and cure time thereby allowing temperature-sensitive substrates such as wood and PVC to be coated. Two of the major industry innovators are Rohm and Haas Morton Powder Coatings (MPC) and Dupont Powder Coatings. Some of the typical polymers used for the powder coating process are acrylics, generally recommended for extreme weather-resistance, epoxy resins for pipe and office furniture, epoxy-polyesters for light fixtures and shelving, polyesters for paneling, automotive components & garden furniture and silicones for high-temperature applications such as barbecue grills.
Application equipment to dispense the powder is quite sophisticated and complete systems from companies such as ITW-Gema, and Wagner provide complete automated systems that apply powder electrostaticly to parts on a conveyer-line and are then cured. Of specific interest is equipment which has been designed for continuous webs such as coil coating. Powder is applied to moving steel coils at relatively high speed (20-30 ft min.) and thickness of 50-200 microns (0.002″-0.008″) then cured and wound up into rolls. This equipment is substantially similar to what would be required to make continuous rolls of microstructured film as described in this application.
Conventional powder coatings are heat cured at temperatures that range from 300° F. and higher. These are useful for fabrication processes that use metal molds or high melt temperature polymeric molds, but in some cases there are advantages to using polymeric molds that have lower temperature stability. For fabrication processes that use low temperature polymeric molds, low temperature powder coatings are of value. Of particular interest are some of the recently developed. UV powder coatings, which can cure in 1-5 seconds at temperatures as low as 125-175° F. Low temperature curing powder coatings are also of value when combining different layers of polymers to achieve products that have specific physical, chemical or optical properties.
Powder particle sizes range from 5-20 microns in diameter but it is possible to achieve even smaller sizes. The ability to achieve small particle sizes is important to some aspects of this invention because in some applications, there is a need to replicate microstructures with high aspect-ratios or with very small functional features. In the case of a high-aspect ratio feature, a mold with a recessed microstructure only 10 microns wide and 50 microns deep (5:1 aspect ratio) the associated powder would have to be small enough to fill the recessed opening of the mold.
The present invention relates to a process and apparatus used to microfabricate precision microstructures, nano-structures and the methods of making polymer molds. Typically microstructures are considered to be in the range of 0.010 inches (250 microns) to 0.000393 inches (1 micron) and nano-structures to be below 0.00000393 inches (0.001 microns). For purposes of convenience only, the phrase microstructure as used herein shall be deemed to include those small macrostructures requiring precision optical configurations that require precise dimensions, angles and surfaces, such as cube-corner reflection; parabolic surfaces for LED's; dihedrals for light guides and others known to those skilled in the optics art. In some instances, the present invention also has great utility in forming complex patterns of precise optical configurations in relatively small macrostructures, in the range of 1 mm to 10 mm..
A primary object of the invention is to provide a method and apparatus for creating a polymeric film that accurately replicates a complex mold surface at least a portion of which surface has microstructured or nano-structured dimensions.
Another object of the invention is to provide an article comprised of a layer of polymeric material at least a portion of which contains a surface area of a complex array of microstructure of optically precise dimensions.
Another object of the invention is to provide a process for forming molds that contain microstructured and nano-structured patterns by electrodeposition of layers of thermoplastic or thermoset polymers (with and without incorporation of second phase materials).
Another object of the invention is to provide apparatus for continuously forming thermoplastic or thermoset precision microstructured products using either polymeric or metal molds.
Another object of the invention is to continuously form polymeric products having precision microstructures and nano structures.
Another object of the invention is to provide apparatus and a process to form precision microstructures in polymers with multiple hard or soft layers.
Another object of the invention is to provide polymeric molds and microstructured products from commercially available polymer layers rather than custom formulating polymers.
Another object of the invention is to form polymeric precision microstructures with through holes or vias.
In summary, there is provided a method of producing a polymeric film that accurately replicates a complex mold surface at least a portion of which surface has microstructured or nano-structured dimensions, comprising the steps of:
(a) electrodepositing a polymeric powder on an underlying mold surface;
(b) curing the powder to create a polymeric film; and
(c) removing the polymer film
In further summary, there is provided an apparatus for continuously producing a web of polymeric film that accurately replicates a complex mold surface at least a portion of which surface has microstructured or nano-structured dimensions, comprising:
(a) means for electrodepositing a layer of polymeric powder onto an underlying mold surface;
(b) means for effecting a cure of said powder to create a polymeric film; and
(c) means for facilitating removal of the film from the mold.
In further summary, there is provided an article comprising a polymeric film having a portion which is a surface area of a complex array of microstructure of optically precise dimensions and wherein said article is formed by curing a powder which has been electrodeposited against a mold surface defining the shape of at least a portion of the article.
An important advantage of the invention is the ability to make polymeric molds as part of the apparatus to form precision microstructures. Since many of these powdered polymers and particularly the UV cure version can be deposited and polymerized into a mold at low cure temperatures, a polymeric mold becomes a faster and less expensive alternative to metal molds described in prior art.
Such a polymer mold has multiple cost and process advantages. By fabricating a polymeric mold consisting of high glass transition polymer or thermosetting polymer, it is possible to replicate lower glass transition polymers using the process described in U.S. Pat. No. 4,486,363 or any improved versions of hot polymer embossing without the cost or time required to build large cylindrical metal molds.
Apparatus and methods are disclosed for fabricating a polymeric mold by electrostatically applying a powdered polymer layer on to a master microstructured pattern. Master patterns can be made by a number of recognized methods such as diamond turning, ruling, deep reactive ion etching (DRIE) or other techniques that provide such patterns. The master pattern or an electroformed copy of the master pattern can be used to make polymeric copies quickly and inexpensively that can be assembled by tiling methods known in various industries. This assembly of parts into a larger mold can be used in conjunction with further disclosed assembly apparatus such as die cutting and precision positioning equipment to provide larger molds for use in fabricating microstructured products.
It has also been demonstrated that pieces of a polymer film mold can be adhered to a stronger backing such as stainless steel or other suitable substrates that would give the composite additional strength and durability as well as electrostatic conductivity.
Another method to make a polymeric mold would be to provide a small and inexpensive electroformed mandrel to fabricate a polymer mold of any length or even continuous rolls of such molds by the use of a scaled down version of the apparatus described in U.S. Pat. Nos. 4,486,363 or 4,601,861.
Yet another method to make a polymeric mold would be to first fashion a small mold as a small continuous belt, then apply a polymer layer continuously that will provide replication of the small mold to provide a mold of any required length.
One of the primary advantages of this technique is that the master pattern or mold fills from the bottom up as the powder is deposited. Making polymeric molds by embossing as defined in U.S. Pat. Nos. 4,486,363 and 4,601,861 requires the viscous polymer to be pushed down from the top, trapping air during the process and is limited to thermoplastic polymers. In accordance with the present invention, small particle size and, in particular, sub-micron and nano-scale particles have advantages in filling sub-micron and nano-scale complex features as compared to the viscosity and surface tension limitations of hot-polymer or liquid replication found in embossing or casting techniques.
Another primary advantage is that the polymer layers can be made from thermoset or UV curable polymers which have much higher service temperature and dimensional stability.
Using any of the above methods to provide a polymeric mold, powdered polymers available from various industry sources can be used to make either individually replicated parts with microstructured patterns or continuously fabricated film wound into rolls.
The present invention is a significant enhancement of the typical formation of conventional powder coating materials, wherein thermoplastic or thermosetting polymers are ground to fine particles sizes and combined with pigments to provide color, and other additives specifically designed to ensure adhesion to a variety of different substrates. The present invention allows for the elimination of pigments and adhesion promoters thus permitting conventional powder coating apparatus to electro-deposit pure powdered polymers on to molds, where they then can be cured in place and then removed as a continuous film.
Commercially available or custom formulated powdered polymers can be selected based on the final products requirements for physical properties, chemical resistance, weatherability, service temperature, refractive index and light transmission among others.
The simplest form of this invention would be to use a powder version of the acrylic or polycarbonate polymers used in the prior art (U.S. Pat. Nos. 4,486,363 and 4,601,861), then electrostatically apply the powder into a mold, cure the layer with the replicated pattern now locked in the polymer and remove the layer form the mold. Since the need for these two polymers has been well established in the field of optical and other light management microstructures, they would be among the preferred embodiments of this invention.
In conjunction with the novel method of making a polymeric mold one of the primary advantages of this technique to fabricate microstructured products is that the mold fills from the bottom up as the powder is deposited. Prior art requires the polymer to be melted and the high viscosity liquid pushed down from the top while trapping air during the process and making it more difficult to achieve the levels of precision required in smaller micro and nano-structured precise patterns.
Another primary advantage of using a powder layer to fill the mold is that the microstructure features typically represent a minority cross-section of the entire product and can be quickly filled then laminated to a thicker backing thus eliminating the need to melt and form the entire substrate. An example of this is Brightness Enhancing Film (BEF) known in the industry to improve the brightness efficiency of notebook computer screens. This film typically is 0.006 inch (150 microns) thick with a microstructure having a cross section of typically 0.005 inch (12 microns). In accordance with the present invention, the need to melt and reform 0.006 inch (150 microns) polycarbonate is unnecessary if the features are replicated with powdered polymer, cured and then laminated to the polycarbonate backing.
Another primary advantage is the speed of application and cure speed compared to prior art. Typical industry speeds for powder coating and especially continuous powder coating such as for coil coating steel sheet can be 20-30 feet per minute (6-9 meters) at width up to 8-10 feet (2.4-3 meters).
An additional advantage is that different powder formulas can be applied in layers. If a hard outer surface of the microstructure is required the first thickness of powder could be nylon or other sufficiently hard materials, followed by as many different layers as required. During the cured phase they will all fuse together forming gradients of hardness. The fused multilayer film with the microstructured pattern now locked in is now removed from the mold. This layering technique is particularly useful for fabricating micro-needles which must be hard enough at the tip to puncture skin but resilient enough at the base not to shear-off under stress. The same can be done for other physical properties, such as modulus or resiliency, linear expansion coefficients and tailored chemical properties such as resistance to acid, caustic, moisture barrier properties or resistance to solvent-base chemicals.
Yet another advantage is a means to produce precision through-holes in polymers, or micro-vias, by partially filling a mold leaving the top of the microstructures uncovered. The use of a soft polymeric backing-film can insure removal of any powder on the tips of the mold and a planer surface on the packed powder. Once cured, the polymer can be removed leaving a precision structured through-hole or via formed by the projected microstructure in the mold. An additional advantage of this method allows the holes to be made in a variety of shapes, such as a circle, triangle, square, etc and tapered to any degree, as determined by the mold structure.
Still another advantage of this invention also allows microstructures to be formed onto ridged substrates. Once the mold is filled with the powdered polymer, it can be laminated to a ridged polymeric sheet and then cured; thereby fusing the microstructured pattern to a much thicker support member. An example of this advantage can be demonstrated by laminating and then fusing clear, polymeric micro-prisms to a thick sheet of ridged clear backing. Typical ranges for the microstructures could be 64 micron tall micro-prisms (0.0025 inch) fused to 0.375 inch ridged sheet. The resulting combination would provide a retro-reflective, micro-prismatic product ridged enough to be a ready made road sign. Normally, micro-prismatic retro-reflective sheeting as described in U.S. Pat. Nos. 4,486,363 and 4,601,861 must be manufactured with adhesive backing and then later applied to a treated aluminum panel that provides a rigid support member. The described novel approach attaches the micro-prisms directly to a polymeric support member such as polycarbonate or another clear impact resistant polymer; eliminating the adhesive and fabrication operations, significantly reducing cost and fabrication time.
Another advantage of this invention is to use polymer powder directly from the polymerizing process, bypassing the need to form pellets and extrude film. This is of particular advantage for polymers such as polycarbonate which are first generated as powder, then pellets and then extruded into film. In the case where some polymers are not normally produced as powder, it still may be an advantage to grind the polymer into powder, rather than extrude pellet into film and then try to replicate the film.
Another advantage of using powder directly from the reactor is the absence of additives that are necessary for the extrusion or injection molding process that would improve optical properties such as bulk absorbitivity and light transmission.
While the drawings depict preferred embodiments of the present invention, they are by way of example only and it is not intended to limit the scope of the invention. It is expected that variations and further modifications as well as further applications of the principles of the invention will occur to others skilled in the art and while differing from the foregoing, remain within the spirit and scope of the invention as described.
An electrostatic gun 21 such as Wagner's Corona PEM-C3 Manual Spray Gun is used to apply a 0.004″ layer of epoxy based 445-100-1 CORVEL® GREEN powder 3 from Rohm and Haas Morton Powder Coatings, with a particle size of 10 microns. A source of infra red radiation 22 such as an electric or gas IR emitter at a temperature of 350° F. (176° C.) for two minutes is used to melt and flow the powder 23 which then cures as a polymer film 24. The master pattern 20 may be metal or polymeric as long as it is dimensionally stable at the cure temperature required for the polymers being applied. One of the primary advantages of using powder to form the polymeric layer over the master pattern is that it fills the pattern from the bottom up as the powder is being deposited, eliminating air entrapment, one of the problems common to prior art embossing or casting techniques.
Normally, substrates that are powder coated are surface treated with an adhesion promoting chemical bath prior to application of the powder to assure adhesion of the powder coating. In this case however since the objective is to melt, cure and then remove the polymer as a film with the pattern replicated on the surface 24, the surface treatment of the master pattern 20 was omitted prior to application of the powder. In addition, since most powder coating products are formulated with adhesion promoting additives each product has to be tested to insure it will separate from the master pattern or mold. In some cases adhesion promoting additives may be intentionally omitted from a powder formulation if it is found to interfere with the removal process.
The epoxy based 445-100-1 CORVEL® worked well but the process is not limited to this product. Many other thermoplastics or thermoset powdered polymers 23 commercially available from suppliers such as Rohm and Haas Morton Powder Coatings or Dupont Powder Coatings are suitable for the process. The powder selection and size would be dependant on the end use of the finished product. The suitability of commercially available powder coatings for this application is based on several factors including chemical, physical and optical properties, melt point and the ability to release from the mold substrate. Among the thermoplastics are polyesters, acrylics, urethanes, Nylons, polypropylenes, polyethylenes, polyvinylchlorides and silicones. Among the thermosets are epoxies, epoxy- polyesters, and UV curable formulations.
There is a also an unexpected significant advantage in using powdered polymer produced directly from the polymerizing process and bypassing the need to extrude film for some microfabrication processes. This is of particular advantage for polymers such as polycarbonate which are normally made as a powder, which is then formed into pellets and then extruded into film before it is re-melted and pressed into molds. Additionally, other commercially available extrusion grade thermoplastic resins, not normally used for powder coating, such as polycarbonates from GE Plastics or acrylics from AtoFina can be bought in pellet form and ground into powder for electrostatic application such as described in this application.
Microscopic examination of the removed polymer film 24 showed there was accurate replication of the lenticular pattern 25 in the polymer which is flexible enough to handle, bend and itself be used as a mold.
The same conditions were also used for a metal substrate made of nickel with a lenticular microstructure on the surface, the only exceptions being that the vacuum metallized layer was not needed since the metal substrate was already conductive.
The prior art or other equipment used to emboss thin film similar to the equipment herein would include film produced hereby as a mold, as disclosed in greater detail in U.S. Publication 20030232174 published Dec. 18, 2003, the subject matter of which is incorporated herein in full by reference.
The hot film 54, now with the pattern transferred to the surface, is solidified again by cooling station 55. The PVC film 50 and PENN carrier film 51 are now removed together from the mold 56, then wound into rolls 57.
Microscopic examination of the film 57 removed from the mold 30 showed good replication of the Fresnel grooves. Using the same machine and conditions, 0.006 inch (150 micron) polysulfone film was scribed with grove lines of 0.001 inch (25 microns) depth and used as a mold to replicate the pattern in Auto Haas DR100 impact modified PMMA. Microscopic examination demonstrated good replication of the groove pattern. As a result it was determined that higher melt point polymer molds such as polycarbonate, polysulfone and others can be used as a mold to accurately form copies of lower melt point substrates such as PVC, acrylic and other lower melting point polymers.
FIF 12B is a side view of
Double band presses of this type can heat and then cool polymer substrates as thick as 0.25 inches thick (2.54 cm) at high speeds as high as 30 to 60 feet per min (10-20 meters min) or more. Apparatus such as disclosed double-band press is capable of processing temperatures as high as 662° F. (350° C.) and pressure as high as 1430 psi (100 bar). The combination of high temperature and high pressure over the entire surface of the belt makes this apparatus uniquely suited as a means to continuously fabricate microstructured and nano-structured polymer layers.
A powder coating device of this type is used to apply thick layers of polymers once the initial layer has covered the micro features and been cured. Since the first electrodeposited layer has now replicated the microstructures or nano-structures with optical precision the balance of the coating can be applied in macro cross-sections and fused to the first layer to achieve thickness greater than would normally be done using standard powder coating techniques. By this means the process could achieve thicknesses of several-millimeters if desired.
While the invention has been described in conjunction with a preferred embodiment, it will be obvious to one skilled in the art that other objects and refinements of the present invention may be made with the present invention within the purview and scope of the present invention.
The invention, in its various aspects and disclosed forms, is well adapted to the attainment of the stated objects and advantages and others. The disclosed details are not to be taken as limitations on the invention, except as those details may be included in the appended claims. The embodiments of the invention in which an exclusive property or privilege is claimed are as follows: