US 20050133361 A1
A lift mechanism for and a corresponding use of a magnetron in a plasma sputter reactor. A magnetron rotating about the target axis is controllably lifted away from the back of the target to compensate for sputter erosion, thereby maintaining a constant magnetic field and resultant plasma density at the sputtered surface, which is particularly important for stable operation with a small magnetron, for example, one executing circular or planetary motion about the target axis. The lift mechanism can include a lead screw axially fixed to the magnetron support shaft and a lead nut engaged therewith to raise the magnetron as the lead nut is turned. Alternatively, the support shaft is axially fixed to a vertically moving slider. The amount of lift may be controlled according a recipe based on accumulated power applied to the target or by monitoring electrical characteristics of the target.
1. In a magnetron sputter reactor including a chamber sealable to a sputtering target, a support in said reactor for holding a substrate to be processed, and a magnetron placeable on a backside of said target opposite said support, a magnetron control system comprising:
a lift mechanism affixed to a support of said magnetron capable of varying a distance of said magnetron from said backside of said target; and
a controller for controlling a degree of said varying said distance during processing of a sequence of substrates.
2. The lift mechanism of
3. A sputter reactor, comprising:
a target affixed to vacuum chamber;
a pedestal within said chamber for support a substrate in opposition to said target;
a magnetron positioned on a back side of said target;
a power supply selectively applying power to said target to excite a plasma within said chamber to thereby sputter material from a front side of said target onto said substrate;
a mechanism for varying a spacing between said magnetron and said target; and
a controller controlling said mechanism to adjust said spacing during a predetermined sequence of depositing said material onto a plurality of said substrates.
4. The reactor of
5. A method of sputtering onto a substrate support on a support in a sputtering reactor chamber including a target fixed to said chamber and a magnetron disposed on a back of said target opposite said support, comprising:
plural first steps of exciting a plasma in said chamber and depositing material of said target onto sequential ones of a plurality of substrates; and
plural second steps of lifting said magnetron away from said backside of said target performed during or after different ones of said first steps.
6. The method of
7. The method of
8. The method of any
9. A magnetron sputtering method, comprising adjusting a magnetic field, which is assisting generation of a plasma in sputtering a target, in compensation for erosion of a front of said target by particles from said plasma.
10. The method of
11. The method of
12. The method of
13. The method of
14. A method for use with a plasma sputter reactor chamber mounting a target facing an interior of the chamber and with a magnetron positioned on the backside of said target exteriorly of the chamber, comprising the steps of:
exciting a plasma in said chamber so as to deposit material of said target onto sequential ones of a plurality of substrates;
lifting said magnetron away from the backside during or after said exciting of said plasma or deposition of material; and
a controller controlling a degree of said lifting at an intermediate time of processing of said plurality of substrates.
15. The method of
16. The method of
17. The method of
18. The method of
19. The method of claims 14, further comprising rotating said magnetron about a central axis of said target to execute circular movement about said central axis.
20. The method of
21. A hollow cathode sputter reactor, comprising:
a vacuum chamber arranged about a central axis;
a support within said chamber for holding a substrate to be processed;
a sputter target sealable to said chamber and having a right cylindrical vault arranged about said central axis in opposition to said support formed by a generally disk-shaped roof and a generally tubular sidewall;
a magnet assembly disposed adjacent a back surface of either said roof or said sidewall; and
a lift mechanism supporting said magnet assembly and controllably varying a distance between said magnet assembly and said back surface.
22. The reactor of
This application claims benefit of U.S. provisional application Ser. No. 60/529,209, filed Dec. 12, 2003. It also is related to concurrently filed U.S. patent application entitled MECHANISM FOR VARYING THE SPACING BETWEEN SPUTTER MAGNETRON AND TARGET.
The invention relates generally to sputter deposition of materials. In particular, the invention relates to a movable magnetron that creates a magnetic field to enhance sputtering.
Sputtering, alternatively called physical vapor deposition (PVD), is the most prevalent method of depositing layers of metals and related materials in the fabrication of integrated circuits. The more conventional type of sputtering, as originally applied to integrated circuits as well as to other applications, deposits upon a workpiece a planar layer of the material of the target. However, the emphasis has recently changed in the use of sputtering for the fabrication of integrated circuits because vertical interconnects through inter-level dielectrics having the high aspect ratios now being used present a much greater challenge than the horizontal interconnects. Furthermore, the horizontal interconnects are being increasingly implemented by electrochemically plating copper into horizontally extending trenches while sputtering is being reserved for liner layers deposited onto the sidewalls in the holes in which the vertical interconnects are formed or also deposited onto the walls of the horizontal trenches.
It has long been known that sputtering rates can be increased by the use of a magnetron 10, illustrated in the schematic cross-sectional view of
The target erosion presents several problems if the lifetime of the target 12 is to be maximized. First, the erosion pattern should be made as uniform as possible. In conventional planar sputtering, uniformity is improved by forming the magnets 16, 18 in a balanced, relatively large closed kidney-shaped ring and rotating the magnetron about the central axis of the target. Secondly, the erosion depth can be compensated by adjusting the spacing between the target and the wafer being sputter deposited, as disclosed by Tepman in U.S. Pat. No. 5,540,821. Futagawa et al. disclose a variant in U.S. Pat. No. 6,309,525. These schemes have primarily addressed the dependence of deposition rate on the separation between the wafer and the effective front face of the target 12. These approaches do not address how the erosion affects the magnetic enhancement of sputtering.
The erosion problem has been complicated by the need to produce a highly ionized sputter flux so that the ionized sputter atoms can be electrostatically attracted deep within high aspect-ratio holes and be magnetically guided, as has been explained for an SIP reactor by Fu et al. in U.S. Pat. No. 6,306,265, incorporated herein by reference in its entirety. The apparatus described therein uses a small triangularly shaped magnetron to effect self-ionized sputtering, taking into account three factors. First, it is advantageous to reduce the size of the magnetron in order to concentrate the instantaneous sputtering to a small area of the target, thereby increasing the effective target power density. Secondly, the concentrated magnetic field of the small magnetron increases the plasma density adjacent the portion of the target being sputtered, thereby increasing the ionization fraction of the target atoms being sputtered. The ionized sputter flux is effective at being attracted deep within high aspect-ratio holes in the wafer. However, the target erosion affects the effective magnetic field at the target face being sputtered, thereby changing the sputtering rate and the ionization fraction. Thirdly, the small magnetron makes uniform target sputtering that much more difficult. Various magnetron shapes, e.g., triangular have been used to increase the uniformity of sputtering, but their uniformity is not complete. Instead, annular troughs are eroded into the target even in the case of rotary magnetrons.
Two major operational effects are readily evident in the use of conventional rotary magnetrons, particularly small magnetrons. First, as illustrated in the plot 26 of the graph of
Hong et al. have presented a planetary magnetron as a solution to the uniformity problem for a high-density plasma reactor in U.S. patent application Ser. No. 10/152,494, filed May 21, 2002, now published as Application Publication 2003-0217913, and incorporated herein by reference in its entirety. As illustrated in the cross-sectional view of
According to the invention, a magnetron 70 positioned in back of the target 34 projects its magnetic field in front of the target 34 to create a high-density plasma region 72, which greatly increases the sputtering rate of the target 34. If the plasma density is high enough, a substantial fraction of sputtered atoms are ionized, which allows additional control over the sputter deposition. Ionization effects are particularly pronounced in sputtering copper, which has a high self-sputtering yield, as copper ions are attracted back to the copper target and sputter further copper. The self-sputtering allows the argon pressure to be reduced, thereby reducing wafer heating by argon ions and reducing argon scattering of copper atoms, whether ionized or neutral, as they travel from the target 34 to the wafer 42.
In the described embodiment, the magnetron 70 is substantially circular and includes an inner magnetic pole 74 of one magnetic polarization with respect to and extending along a central axis 76 of the chamber 32 as well as the target 34 and pedestal electrode 40. It further includes an annular outer pole 78 surrounding the inner pole 74 and of the opposed magnetic polarity along the central axis 76. A magnetic yoke 80 magnetically couples the two poles 74, 78 and is supported on a carrier 81. The total magnetic intensity of the outer pole 78 is substantially greater than that of the inner pole 74, for example by a factor of greater than 1.5 or 2.0, to produce an unbalanced magnetron which projects its unbalanced magnetic portion towards the wafer 42 to thereby confine the plasma and also guide sputtered ions towards the wafer 42. Typically, the outer pole 78 is composed of plural cylindrical magnets arranged in a circle and having a common annular pole piece on the side facing the target 34. The inner pole 74 may be composed of one or more magnets, preferably with a common pole piece. Other forms of magnetrons are encompassed by the invention.
The high plasma densities achieved by this configuration as well as that of Fu et al. are achieved in part by minimizing the area of the magnetron 70. The encompassing area of the magnetron 70 is typically less than 10% of the area of the target 34 being scanned by the magnetron 70. The magnetron/target area ratio may be less than 5% or even less than 2% if uniform sputtering is otherwise maintained. As a result, only a small area of the target 34 is subject to an increased target power density and resultant intensive sputtering. That is, the sputtering at any instant of time is highly non-uniform. To compensate for the non-uniformity, a rotary drive shaft 82 rotated by a drive source 84 and supporting the magnetron 70 circumferentially scans the magnetron 70 about the chamber axis 76. However, as has been described with respect to the reactor of Fu et al., the resultant annular troughs in the target may produce significant radial non-uniformity in the sputtering.
Hong et al. significantly reduce the sputtering non-uniformity by the use of a planetary scanning mechanism 90 to cause the magnetron 70 to move along a planetary or other epicyclic path over the back of the target 34 with respect to the central axis 76. Their preferred planetary gear mechanism 90 for achieving planetary motion includes, as additionally and more completely illustrated in
Because the DC power supply 54 delivers a significant amount of power to the target 34 and a high flux of energetic ions bombard the target 34 thereby heating the target 34, it is conventional to immerse the magnetron 70 as well as the planetary mechanism 90 in a cooling water bath 116 enclosed in a tank 118 sealed to the target 34 and the fixed drive-shaft housing 94. Unillustrated fluid lines connect the bath 116 with a chiller to recirculate chilled deionized water or other cooling fluid to the bath 118.
The planetary magnetron scanning, because of its convolute path across the target 34, greatly improves the uniformity of target erosion so that the target 34 is more uniformly eroded and results in a nearly planar sputtering surface even as the target is eroded. As a result, the target utilization is greatly improved. Nonetheless, as the target 34 erodes generally uniformly, the magnetic field at its sputtering face is changing and apparently on average decreasing. The change affects the sputtering rate, which as described above has been observed to decrease. The plots presented in
A second set of non-uniformity problems is not immediately addressed by the planetary scanning mechanism. The small area of the magnetron 70 advantageously produces a high target power density and high plasma density and hence increases sputtering rate and increases the fraction of ionized sputter atoms which are drawn deep within high aspect-ratio holes to coat the sides and bottom of via holes. However, the magnetic field and hence the plasma density depend upon the distance between the target sputtering surface and the magnetron. As a result, as the target 34 is being sputtered, even if uniformly, the plasma density is changing and hence the sputtering rate and the ionization rate upon which the via sidewall coverage depends are changing. The effect is exacerbated for a small magnetron because the gradient of the magnet field is greater. As a result, the changing magnetic field and plasma density destabilizes the process causing variation in bottom and sidewall coverages across the lifetime of the target. It has generally been accepted that the high-performance sputtering is different at the end of the lifetime of the target than at the beginning. Plot 122 in
Halsey et al. in U.S. Pat. No. 5,855,744 show an apparatus for deforming a linear magnetron as it scans across a rectangular target. In one embodiment, multiple actuators moving shafts along multiple respective axes deform the magnetron. Mizouchi et al. in U.S. Pat. No. 6,461,485 discloses a single vertical actuator for compensating for end effects in linear scanning.
Demaray et al. in U.S. Pat. No. 5,252,194 discloses a slider mechanism for vertically moving a large magnetron to adjust the magnetic field at the front of the target.
Schultheiss et al. in U.S. Pat. No. 4,927,513 discloses a magnetron lift mechanism to control magnetic properties of sputtered layers.
The invention includes the method and apparatus for compensating erosion of a plasma sputtering target by moving the magnetron away from the back of the target as the front of the target is eroded. The compensation provides a more constant magnetic field and plasma density at the surface of the target being sputtered and results in a more stable sputtering process.
The lift mechanism may include a lead screw mechanism including a lead screw and lead nut. The lead screw may be axially fixed to the magnetron and a lead nut threadably engaged with the lead screw. Rotation of the lead nut vertically moves the magnetron. The lead screw may be azimuthally fixed while the lead nut is axially fixed. The lead nut may be manually moved or moved under the control of a motor or other actuator coupled to the lead nut by a gear or a linear lead screw mechanism or linear actuator.
The amount of lift my be dictated by a predetermined recipe or by a measured cumulative power applied to the target. Alternatively, the target resistance or power characteristic or the physical erosion depth may be monitored to determine when additional lift is required.
The magnetron lift mechanism may also be used to control the magnetic field at the face of the sputtering target for control of the sputtering process other than simple compensation of target erosion.
The erosion of the front of the target in magnetron sputtering can be compensated by moving the magnetron away from the back of the target. As illustrated in
Although other implementations are possible, the lift mechanism 124 can be easily incorporated into the conventional design by allowing the housing 94 to be axially movable by the lift mechanism while still maintaining its fluid seal to the tank 118.
A first embodiment of the invention used to verify the effects of compensating the magnetron-to-target spacing uses a series of shims of varying thickness placed between the magnetron 70 of
Actual experimental data using a copper target and a planetary magnetron in the reactor of
These results could be improved particularly for target and bias power by more frequently moving the magnetron with a finer resolution. These results also show that target and bias voltages are sensitive indicators of the amount of erosion and hence the need for spacing compensation. These voltages are easy to monitor during production. Current is another sensitive measurement for electrical supplies generating constant power. Alternatively, if the power supplies are set to generate constant voltage or current, the complementary quantity or power may be measured. These electrical measurements typically amount to monitoring the resistance of the plasma under some set electrical condition. Therefore, the compensation can be dynamically controlled by measuring one or both of these voltages (or other quantities) during production and comparing them to baseline values. When the deviation exceeds a threshold, the compensation may be performed to bring the measured value closer to the baseline value. It is also possible to optically or otherwise measure the physical depth of erosion of the target and use the depth measurement to initiate the compensation. Nonetheless, it has proven satisfactory to keep track of cumulative target power and move the magnetron at values experimentally determined for a given sputter recipe.
Although the first embodiment relying on shims is effective, it clearly presents operational difficulties as the sputter reactor needs to be shut down and the magnetron removed from the water bath to allow manual replacement of its shims. It is greatly desired to perform the spacing compensation from outside the water bath and preferably under computerized electrical control.
One set of embodiments is based on converting the stationary housing 94 to a vertically movable but in large part azimuthally fixed housing 94 driven by a lead screw mechanism 130, as illustrated in the cross-sectional view of
A tail 140 of the housing 94 axially passes through an aperture in the tank roof 142 but is azimuthally fixed by other means. The fixed gear 92 of the planetary mechanism is fixed to the end of the housing tail 140. As a result, when the housing 94 is vertically moved, the fixed gear 92, the drive plate 96, and the rest of the planetary mechanism 90 and magnetron 70 are also vertically moved along the central axis 76.
A support collar 146 is fixed to the tank roof 142 and sealed to it with an O-ring placed in an O-ring groove 147. An annular bellows 148 surrounding the upper portion of the housing tail 140 is sealed on opposed ends to the housing 94 and to the inner portion of the support collar 146 to slidably seal the fluid in the bath 116 from the exterior as well as from most of the mechanical parts of the lift mechanism 130 while allowing axial movement between the housing 94 and drive shaft 82 on one hand and the tank roof 142 on the other. The bellows 148 should accommodate a movement of about ¾″ (2 cm) corresponding to the usable thickness of the target 34. Other types of slidable fluid seals are possible. The fixed collar 146 rotatably supports an internally threaded lead nut 150 through two ring bearings 152, 154. An inner retainer ring 156 fixed to the lead nut 150 and an outer retainer ring 158 fixed to the collar 146 trap the upper bearing 152 against the lead nut 150 and the collar 146. Another similar retainer ring configuration beneath the lead nut 150 traps the lower bearing 154. The lead nut 150 can thus rotate about the central axis 76 but is axially fixed to the tank top 142.
The external threads of a azimuthally fixed but vertically movable lead screw 164 engage the internal threads of the lead nut 150. The lead screw 164 supports the housing 94 on its upper surface. The housing 94 may be fixed to the lead screw 164 or guide pins may couple them to prevent relative rotational movement. A plurality of screws 166 hold the lead screw 164 to the tank top 142 through compression springs 168. As a result, the lead screw 164 is rotationally fixed as it engages the rotatable lead nut 150 but the compression springs 168 accommodate limited vertical motion of the lead screw 164. The axial fixing of the lead nut 150 to the tank top 142 provides a wide mechanical base for the heavy rotating magnetron, thereby reducing shimmy and allowing the reduction of the clearance between the magnetron 70 and the back of the target 34.
In operation, if the lead nut 150 is rotated clockwise, the azimuthally fixed lead screw 164 rises and lifts the housing 94 and the attached rotary shaft 82 and magnetron 70 away from the target 34. Counter-clockwise rotation of the lead nut 150 produces the opposite axial movement of lowering the magnetron 70 toward the target 34. The lift drive mechanism for rotating the lead nut 150 is easily formed outside of the cooling bath 116. Two types of lift drive mechanisms will be described.
A first embodiment of a rotational lift drive includes a spur gear drive 170 illustrated in the orthographic view of
An optical position sensor 175 includes two arms 175 a, 175 b spaced to accommodate the gear ledge 173 as it rotates in lifting the magnetron. One arm 175 a contains an optical emitter, such as an light emitting diode, while the other arm 175 b contains a light detector, such as a photodiode. The position sensor 175 is used to calibrate the rotation of the gear 172 using the gear ledge 173 as a flag. The lift motor 176 rotates the gear 172 toward the position sensor 175 until the gear ledge 173 enters between the arms 175 a, 175 b of the position sensor 175 and blocks the emitted light from the optical detector. The controller notes that position as a home position. The stepper motor 176 is then stepped in the opposite direction by a controlled number of pulses to a desired rotation location of the gear 172 and hence vertical position of the magnetron. Other position sensors may be used.
The drive shaft motor 84 may be vertically mounted on the tank roof 142 through a motor mount 180. The drive shaft motor 84 drives a motor drive gear 182 through optional unillustrated gearing to reduce the rotation rate. A shaft drive gear 186 is formed in a capstan 188 fixed to the drive shaft 82. A ribbed belt 190 is wrapped over both the motor drive gear 182 and the shaft drive gear 186 so that the motor 84 rotates the drive shaft 82 in executing the planetary motion of the magnetron 70. Because the drive shaft 82 and the attached shaft drive gear 186 are raised and lowered in operation relative to the motor mount 180 and attached motor drive gear 182, the teeth of at least the shaft drive gear 186 must be wide enough to accommodate the slip or axial movement of the belt 190 relative to teeth of that gear 186 and the motor drive gear 182 may be formed with two rims to limit the axial movement of the belt 190 on that gear 182. A rotary fluid coupling 194 is mounted on the top of the drive shaft 82 to allow cooling water lines to be connected to the central bore 132 of the rotating drive shaft 82.
A second embodiment of a rotational lift drive includes a lead screw mechanism 200 illustrated in the orthographic, partially sectioned view of
The second embodiment of
The lead nut lift mechanism offers several advantages. It is concentric about the lift axis and the support shaft for the magnetron. The magnetron is supported on an azimuthally fixed lead screw threaded into a larger lead nut that is axially fixed to a yet larger structure. Hence, the lead nut lift mechanism offers low vibration and flexing of the relatively heavy rotating magnetron. The design is mechanically simple, thereby increasing reliability and reducing cost.
A second type of lift mechanism is a double slider mechanism 230 illustrated orthographically in
A bracket 250 illustrated orthographically in
A slider drive mechanism includes a plate 276 fixed to end of the slider case 234 which passes the end of the slider shaft 240 to be fixed to a slider gear 278. The plate 276 also supports below a vertically oriented slider motor 280 having a drive shaft fixed to a motor gear 282. A ribbed belt 284 is wrapped around the slider and motor gears 278, 282 so that the slider motor 280 can move the slider 234 up and down within the slider case 250 to thereby vertically move the housing 94 and attached magnetron 70 relative to the tank roof 142 and the back of the target 34.
A modified double slider mechanism 290 illustrated orthographically in
The described compensation mechanisms may be used in a number of ways for compensating target erosion. It is possible to perform the lifting and compensating during the plasma excitation and sputter deposition, but it is preferable instead to perform it after one wafer is processed and before the next one is processed. Even though motor controlled, the mechanisms may be essentially manually controlled by on occasion instructing the lift motor to move a set amount corresponding to a desired lift of the magnetron. However, the lift compensation algorithm is advantageously incorporated into the recipe for which a machine is being used and a computerized controller performs the compensation as well as controls the other chamber elements according to the recipe. In view of the limited axial throw of about 2 cm and the large number of wafers which maybe deposited with a single target over many weeks of even continuous processing, it is reasonable to compensate the spacing on only an occasional basis, for example, once an hour or once a day or more specifically after a large number of wafers have been processed.
In a control procedure emphasizing the optimized process in which the reactor is being used, the amount of displacement may be determined empirically for a given combination of target, magnetron, initial target/magnetron spacing, and general operating conditions developed for a step in the fabrication of a chip design A convenient unit of target usage is total kilowatt-hours of use since the target was fresh so that the process recipe keeps a running total of kilo-watt hours and adjusts the spacing as a function of the total kilowatt-hours according to a compensation algorithm incorporated into the process recipe and set during development of the recipe. The compensation may be controlled once a set period for this unit has passed. For a given process, wafer count is nearly as good a usage unit.
A dynamic control algorithm may also be effective. As is evident from the plots 122, 127 of
It is also possible to directly measure the position of the sputtering surface of the target by optical or other means or to measure the thickness of the target by separate electrical means, both approaches providing a measurement of target erosion.
It is desirable that the compensation be directly measurable by a feedback measurement, for example, the angular position of the set nut or of the linear position of the slider or an angular displacement of one of the rotary parts, all measured from a known position. For example, the position sensor 175 of
It is noted that the baseline magnetron-to-target spacing may vary from one recipe to another and the described lift mechanisms may be used to initially obtain the baseline spacing for a fresh target as well as to maintain it during extended target usage.
A computerized controller 316 is conventionally used to control the sputtering operation according to a process recipe stored within the controller 316 on a recordable medium 318, such as a recordable disk. The controller 316 conventionally controls the target power supply 54 as well as other conventional reactor elements 44, 48, 58, 84, and 114. Additionally according to the invention, the controller 316 controls the stepper motor 176 with a controlled series of pulses and a directional signal to drive the magnetron 70 a controlled distance in either direction. The controller 316 stores the current position of the magnetron 70 and, if additional movement is desired, can incrementally move the magnetron 70. However, on startup or after some unforseen interrupt, the controller 316 raises the magnetron 70 away from the target 34 until the position sensor 314 detects the flag 312. The setting of the stepper motor 176 at this flagged position determines a home position. Thereafter, the controller 316 lowers the magnetron 70 to a desired position or spacing S from the target 34. This limit detection maybe implemented by the position sensor 175 of
The recipe stored within the controller 316 may contain the desired compensation rate, for example, as a function of kilowatt hours of power applied to the target 34 from the power supply 54 or alternatively as a compensation for variation in target voltage. The controller 316 can monitor the applied power through a watt meter 320 connected between the power supply 54 and the target. However, the power supply 54 is often designed to deliver a selectable constant amount of power. In this case, the total power consumption can be monitored by software within the controller 316 with no direct power measurement. The controller 316 may also monitor the target voltage with a voltmeter 322 connected to the power supply line to the target 34. As mentioned previously, target voltage is a sensitive indicator of the need to compensate the spacing between magnetron and target.
The spacing compensation may be advantageously applied to the roof magnetron used with a target having an annular vault formed in its surface, as has been described by Gopalraja et al. in U.S. Pat. No. 6,451,177, incorporated herein by reference in its entirety. The invention can also be applied to a sputter reactor having a hollow cathode magnetron 330 schematically illustrated in
Permanent magnets 336, usually axially aligned, are placed around the exterior of a circumferential sidewall 338 of the target 332 to serve several functions including intensifying the plasma adjacent the sidewall 338. However, in some implementations, the magnets are horizontally aligned to create a bucking field within the vault adjacent the sidewall 338. According to the invention, motors or other types of actuators 340 selectively move the magnets 336 radially with respect to the central axis 334 to compensate for sputtering erosion of the target sidewalls 338. The hollow cathode magnetron 330 may additionally include a roof magnetron 342 positioned in back of a disk-shaped roof 342 of the target 332. The roof magnetron 342 may be stationary or be rotated about the central axis 334. According to the invention, a motor or other actuator 346 maybe used to axially move the roof magnetron 342 along the central axis 334 to compensate for erosion of the target roof 344. However, as has been previously discussed, the various magnet movements may be used alternatively to tune the sputtering process to an initial state as well as to maintain it there.
An alternative hollow cathode magnetron 350 schematically illustrated in
The compensation mechanism is not limited to those which have been described. For example, especially in the case that the magnetron executes only simple rotary motion, the rotary shaft supporting the magnetron can be directly lifted if an additional dynamic or slidable seal allows leak-free axial movement of the rotary shaft. Other types of lift mechanisms and lift drives may be used in achieving the control or compensation of the target/magnetron spacing However, the lead-screw lift mechanism 130 of
Although the above described lift mechanisms have been described for raising a magnetron away from the target backside, they may be used as well to lower the magnetron. Also, the apparatus maybe used for purposes other than compensating for target erosion.
Although the invention has been developed for copper sputtering, it may be used for sputtering other materials dependent on the target material and whether a reactive gas is admitted to the chamber. Such materials include nearly all metals and metal alloys and their reactive compounds used in sputter deposition, including but not limited to Cu, Ta, Al, Ti, W, Co, Ni, NiV, TiN, WN, TaN, Al—Cu alloys, Cu—Al, Cu—Mg, etc.
The invention may be also applied to other magnetrons such as the more conventional large kidney-shaped magnetrons and to other magnetrons not intended to ionize the sputtered atoms. Nested magnetrons are not required. Long-throw sputter reactors can benefit from the invention. Inductive RF power may be coupled into the magnetron sputter reactor to increase the source power. Although the invention is particularly useful with scanned magnetrons, it may also be applied to stationary magnetrons. It may also be applied to magnets used more for confining the plasma and guiding ions rather than strictly for increasing the plasma density.
Accordingly, the invention greatly stabilizes a sputtering process over the lifetime of the target with relatively minor additions to the sputter apparatus.
The above described embodiments do not encompass all possible implementations and uses of the invention. The coverage of the invention should be determined primarily by the specific language of the claims.