|Publication number||US20050139705 A1|
|Application number||US 10/719,120|
|Publication date||Jun 30, 2005|
|Filing date||Nov 21, 2003|
|Priority date||Nov 21, 2003|
|Also published as||WO2005051824A1|
|Publication number||10719120, 719120, US 2005/0139705 A1, US 2005/139705 A1, US 20050139705 A1, US 20050139705A1, US 2005139705 A1, US 2005139705A1, US-A1-20050139705, US-A1-2005139705, US2005/0139705A1, US2005/139705A1, US20050139705 A1, US20050139705A1, US2005139705 A1, US2005139705A1|
|Inventors||Michael McGovern, Edgar Earnhart|
|Original Assignee||Eastman Kodak Company|
|Export Citation||BiBTeX, EndNote, RefMan|
|Patent Citations (16), Referenced by (10), Classifications (7), Legal Events (1)|
|External Links: USPTO, USPTO Assignment, Espacenet|
The present application is related to U.S. Ser. No. ______, filed concurrently herewith, of Michael R. McGovern and Edgar G. Earnhart, entitled “An Improved Web-Winding Device”, Atty. Docket No. 87085/CEB; and
U.S. Ser. No. ______, filed concurrently herewith, of Michael R. McGovern and Edgar G. Earnhart, entitled “Method Of Manufacturing A Web-Winding Device”, Atty. Docket No. 87086/F-P.
The invention relates generally to the field of web-winding devices. More particularly, the invention concerns a web-winding means particularly well suited for photographic film material based on silver halide technology.
Traditionally, motion picture film stock cores, such as those defined by the Society of Motion Picture and Theater Equipment (SMPTE) standard ANSI-SMPTE 37M or ISO 1039-1995, have been injection molded from thermoplastic high impact polystyrene (HIPS) molding compounds. The HIPS resin has been the material of choice mostly driven by cost, ease of injection molding, and suitability for the state of motion picture film production and cinema projection technology. Cores produced from HIPS resins have been used to produce motion picture cores from multi-cavity tools or molds now for over forty years.
Over time the total amount (as measured in length) of motion picture film and the tightness of wrap (with a resultant hoop stress on the core) has increased. The spooling process (manufacturing and printing) has evolved into a high-speed process where motion picture film is spooled at a speed of thousands of meters per minute to achieve greater productivity rates. A result of these improvements is a finished core product with a much greater weight and stress but with no change in the basic design of the motion picture core to compensate. Moreover, the demands of cinematographers for low light sensitive films and the demands from consumers for high-quality theatre experience have increased demands for film cleanliness in raw stock and printing production. The high speed of the spooling process combined with the poor overall wear property of the current thermoplastic HIPS resin result in the generation of a tremendous amount of HIPS dust and debris at the mounting interface of the core with the winding machine spindle. The generation of this level of debris creates high production losses and nightmarish housekeeping issues. The present invention resolves all of these issues plus creates an opportunity of reuse of cores which was never done with the HIPS resins due to the potential of damage from handling, transportation and use. Core crush, a form of permanent deformation, is exemplary of the damage from handling where a fully spooled motion picture core sustains sufficient impact energy to literally crush the core resulting in complete failure of the part. Needless to say, this form of damage is particularly costly and frustrating to motion picture printing customers because: 1) film telescopes and comes off of whatever is left of the damaged core; and/or 2) the core cannot be installed onto the winding spindle.
There have been several attempts in the art to solve aspects of the above problems. In U.S. Pat. No. 4,042,399 by Kiesslich teaches the disclosure of a photographic element having improved slip. However, a shortcoming of this development is that the surface of the photographic element is required to be coated with a polyester film to improve slip.
Another prior art film transport development is described in U.S. Pat. No. 5,694,629 by Stephenson, III et al. The transport mechanism of Stephenson uses slip clutches made of polycarbonate to improve slip.
In U.S. Pat. No. 4,049,861 by Nozari a web-winding device is disclosed that requires the use of abrasion resistant coatings including polyesters and polycarbonates to reduce web slipage.
Therefore, a need persists in the art for a web-winding means that has a mounting surface with substantially reduced friction, is substantially damage resistant, and does not generate deleterious debris during typical web-winding and unwinding operations.
It is, therefore, one object of the invention to provide a web-winding means that is far more durable and less debris generating than existing developments.
Another object of the invention is to provide a web-winding means that have far superior mechanical integrity than prior art models.
Yet another object of the invention is to provide a method of making a web-winding means that is far more durable and generates less debris than existing devices.
The present invention is directed to overcoming one or more of the problems set forth above. Briefly summarized, a web-winding means comprises a generally cylindrical support structure having an outer web wrapping surface for receiving at least one convolution of a web. The web wrapping surface has a surface texture less than 0.5 microns Ra to produce a static coefficient of friction x, between the outer web wrapping surface and first contact surface of the at least one convolution of web. As a result, the first contact surface of the at least one convolution of the web and a second contact surface of an at least a partial second convolution of the web produces a static coefficient of friction x2, wherein x1 is less than x2.
The web-winding means of the present invention has numerous advantages over prior developments, including: substantially improved overall mechanical properties; a stronger core to withstand the higher hoop stress and resist core crush; lower friction and wear which results in a significant reduction in airborne debris that results in product contamination issues and ability to reuse cores; and an enhancement in the surface finish of the working surface of the core that comes into contact with the film which facilitates the cinching of the leader portion of the film.
The above and other objects, features, and advantages of the present invention will become more apparent when taken in conjunction with the following description and drawings wherein identical reference numerals have been used, where possible, to designate identical features that are common to the figures, and wherein:
FIGS. 5(a) and 5(b) are charts of a quantitative assessment of debris generated from film cores of various materials;
Referring now to the drawings, and particularly to
Referring again to
Referring again to
Referring again to
It is apparent that the solution to the current problems associated with a web-winding device 10 as described in the previous Figures requires a material with: a) static coefficient of friction between web-winding device surface and inner web surface comparable to current developments; b) lower deleterious particle generation between annular portion surface 17 and web-winding machine spindle surface 8 than current developments; c) higher elastic modulus than current developments; and d) lower plastic creep than current developments.
Referring to FIGS. 5(a) and 5(b), examples are shown of quantitative experimental results of studies of volume loss of various materials from web-winding means 10 (as shown in
Referring to Table I below, wear rate coefficients are calculated based on the volume loss measurements discussed in
Wear Rate Coefficient Test Results Wear Rate Volume Loss Force Stroke Coefficient V F s k Core Material m3 N m m3/Nm ECP Check Core (HIPS) 2.240E−06 4.497E−05 NOVA 5104 HIPS 2.060E−06 4.136E−05 BASF Ultradur B4520 PBT 1.200E−09 2.409E−08 BASF Ultradur 4300 0.000E+00 1.961 0.0254 0.000E+00 K4 20% G.B. PBT GE Lexan WR-2210 0.000E+00 0.000E+00 PC + Lube GE Valox 325 PBT 1.100E−08 2.208E−07 BASF Ultradur B4500 PBT 1.100E−08 2.208E−07
K = V/(F · s)
Injection molded motion picture cores formed from the materials above will be produced from semi-crystalline PBT resin with a typical specific gravity (solid) of 1.31 grams per cubic centimeter with an intrinsic viscosity between 5000 to 6000 poise.
The antioxidant (AO) package that is very common for PBT resins is a typical combination of a primary AO such as a sterically hindered phenol (2,6-Di-tert.butyl-p-cresol from the alkylidene-bisphenols family) in conjunction with a secondary AO component such as from the phosphite or phosphonite group both of which are short-chained organics. Typical levels of the AO package range from 0.20% to 1.0% by weight with a preferred aim weight percent of 0.5.
Described film cores have a generally cylindrical support structure having an outer web wrapping surface for receiving at least one convolution of a web; an annular portion with keyway for mounting core onto film winding machine and transmitting torque thru the core to the film for wind tension; a support structure a web capture slot (gate) for securing a portion of the web in said support structure prior to the web being wrapped along the web wrapping surface; sensible features in the support structure for determination of orientation when mounting on a film winding machine for the purpose of correct web capture slot orientation; and a web wrapping surface capable of providing a cinch wrap engagement of the film to the web wrapping surface that allows winding of film to the core without use of the web capture slot.
The following are exemplary of the web-winding means of the invention composing a 0.5% by weight AO modified PBT resin formulations:
In accordance with Example 1, web-winding means composes a 4,4′-Di-tert-octyldiphenylamine material.
In accordance with Example 2, web-winding means composes pentaerythrityl tetrakis-3-(3,5-Di-tert-butyl-4-hydroxyphenyl)-proprionate.
In accordance with Example 3, web-winding means composes pentaerythrityl tetrakis-3-(3,5-Di-tert-butyl-4-hydroxyphenyl)-propionate with N,N′-hexamethylenebis-3-(3,5-Di-tert-butyl-4-hydroxyphenyl)-propionamide.
In each of the above examples, typical mechanical properties for this PBT grade resin include:
Alternative suitable materials for an injection molded web-winding device 10 of the invention include:
Referring again to
Referring yet again to
Referring again to
The invention has been described with reference to a preferred embodiment; however, it will be appreciated that a person of ordinary skill in the art can effect variations and modifications without departing from the scope of the invention.
|Cited Patent||Filing date||Publication date||Applicant||Title|
|US3447674 *||Jul 14, 1967||Jun 3, 1969||Fraser William T||Winding core|
|US3885751 *||Mar 26, 1974||May 27, 1975||Kienzle Apparate Gmbh||Tape carrier for record tapes and the like|
|US4042399 *||Jul 15, 1975||Aug 16, 1977||E. I. Du Pont De Nemours And Company||Photographic element with improved slip|
|US4049861 *||Feb 19, 1976||Sep 20, 1977||Minnesota Mining And Manufacturing Company||Abrasion resistant coatings|
|US4281805 *||Nov 14, 1979||Aug 4, 1981||Agfa-Gevaert N.V.||Apparatus and method for coiling a moving web|
|US4576344 *||Jul 18, 1985||Mar 18, 1986||Teijin Limited||Polyester film roll|
|US4749617 *||Dec 18, 1985||Jun 7, 1988||Minnesota Mining And Manufacturing Company||Composite article containing rigid layers|
|US4767186 *||Oct 6, 1987||Aug 30, 1988||North American Philips Consumer Electronics Corp.||Front projection screen with rear light concentrating lens array|
|US4989802 *||Nov 7, 1988||Feb 5, 1991||Fuji Photo Film Co., Ltd.||Core for web material|
|US5039024 *||Jul 16, 1987||Aug 13, 1991||Polyplastics Co., Ltd.||Method of fixedly mounting tape on core portion of reel made of plastics|
|US5144474 *||Nov 28, 1989||Sep 1, 1992||Delphi Technology, Inc.||Perforated processing apparatus and method|
|US5252369 *||Aug 10, 1992||Oct 12, 1993||Fuji Photo Film Co., Ltd.||Core for web material|
|US5414032 *||Sep 28, 1992||May 9, 1995||Fuji Photo Film Co., Ltd.||Resin composition for a core for web material|
|US5441212 *||Nov 22, 1993||Aug 15, 1995||L-S Electro-Galvanizing||Mandrel sleeve adaptor|
|US5694629 *||May 1, 1995||Dec 2, 1997||Eastman Kodak Company||Film transport mechanism with torque limiting clutch|
|US5873543 *||Jun 21, 1995||Feb 23, 1999||Emtec Magnetics Gmbh||Winding hub for information carriers in tape form|
|Citing Patent||Filing date||Publication date||Applicant||Title|
|US7384455||Oct 31, 2005||Jun 10, 2008||Caterpillar Inc.||Filter service system and method|
|US7410529||May 27, 2005||Aug 12, 2008||Caterpillar Inc.||Filter service system and method|
|US7419532 *||Feb 28, 2006||Sep 2, 2008||Caterpillar Inc.||Deposition system and method|
|US7462222||Oct 5, 2004||Dec 9, 2008||Caterpillar Inc.||Filter service system|
|US7468085||Dec 19, 2005||Dec 23, 2008||Caterpillar Inc.||System and method for cleaning a filter|
|US8252093||Jul 29, 2008||Aug 28, 2012||Cheryl Lynn Sellers||Filter service system and method|
|US8608834||Aug 27, 2012||Dec 17, 2013||Caterpillar Inc.||Filter service system and method|
|US20060070359 *||Oct 5, 2004||Apr 6, 2006||Caterpillar Inc.||Filter service system|
|US20060070361 *||May 27, 2005||Apr 6, 2006||Caterpillar Inc.||Filter service system and method|
|US20060144223 *||Feb 28, 2006||Jul 6, 2006||Sellers Cheryl L||Deposition system and method|
|U.S. Classification||242/160.4, 242/610.6|
|International Classification||B65H75/10, G03C3/00|
|Cooperative Classification||B65H75/10, B65H2701/5122|
|Nov 21, 2003||AS||Assignment|
Owner name: EASTMAN KODAK COMPANY, NEW YORK
Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:MCGOVERN, MICHAEL R.;EARNHART, EDGAR G.;REEL/FRAME:014744/0301;SIGNING DATES FROM 20031120 TO 20031121