Patents

  1. Advanced Patent Search
Publication numberUS20050146258 A1
Publication typeApplication
Application numberUS 11/040,318
Publication dateJul 7, 2005
Filing dateJan 20, 2005
Priority dateJun 2, 1999
Also published asUS7696684, US8026661, US8648524, US8678871, US20080088225, US20090230412, US20110299011, US20110312116, US20140204295
Publication number040318, 11040318, US 2005/0146258 A1, US 2005/146258 A1, US 20050146258 A1, US 20050146258A1, US 2005146258 A1, US 2005146258A1, US-A1-20050146258, US-A1-2005146258, US2005/0146258A1, US2005/146258A1, US20050146258 A1, US20050146258A1, US2005146258 A1, US2005146258A1
InventorsShimon Weiss, Michael Schlamp, A. Alivisatos
Original AssigneeShimon Weiss, Schlamp Michael C., Alivisatos A. P.
Export CitationBiBTeX, EndNote, RefMan
External Links: USPTO, USPTO Assignment, Espacenet
Electronic displays using optically pumped luminescent semiconductor nanocrystals
US 20050146258 A1
Abstract
A multicolor electronic display is based on an array of luminescent semiconductor nanocrystals. Nanocrystals which emit light of different colors are grouped into pixels. The nanocrystals are optically pumped to produce a multicolor display. Different sized nanocrystals are used to produce the different colors. A variety of pixel addressing systems can be used.
Images(7)
Previous page
Next page
Claims(26)
1-20. (canceled)
21. A multicolor display apparatus, comprising:
an array of semiconductor nanocrystals forming a pixel array of different colors, wherein the sizes of the nanocrystals determine the colors; and
a pixel addressing system operatively associated with the nanocrystal array for selectively optically exciting the nanocrystals to produce a luminescent color pattern of pixels.
22. The apparatus of claim 21 wherein the pixel addressing system includes a backlight source.
23. The apparatus of claim 22 wherein the backlight source is a source of ultraviolet light or blue light.
24. The apparatus of claim 22 wherein the pixel addressing system comprises a multielement backlight source, wherein each source element is independently operable.
25. The apparatus of claim 22 wherein the backlight source comprises source elements including LEDs or semiconductor lasers.
26. The apparatus of claim 22 wherein the backlight source comprises source elements comprising sources of ultraviolet light or blue light.
27. The apparatus of claim 21 wherein the pixel addressing system comprises:
a backlight source; and
a liquid crystal modulator positioned between the backlight source and the nanocrystal array.
28. The apparatus of claim 27 further comprising an analyzer between the nanocrystal array and liquid crystal modulator.
29. The apparatus of claim 27 further comprising an analyzer positioned between the backlight source and liquid crystal modulator.
30. A method comprising:
providing a transparent panel;
forming an array of pixels on the panel, wherein the array of pixels comprises a first discrete pixel comprising first nanocrystal particles of a first size and a second discrete pixel comprising second nanocrystal particles of a second size; and
providing a pixel addressing system operatively associated with the array of pixels, wherein the pixel addressing system is adapted to excite the first nanocrystal particles in the first discrete pixel using light comprising a wavelength to cause the first pixel to produce a first color and to excite the second nanocrystal particles in the second discrete pixel using light of the same wavelength to cause the second discrete pixel to produce a second color.
31. The apparatus of claim 30 wherein the pixel addressing system includes a light source that produces only one wavelength of light.
32. The apparatus of claim 30 wherein the pixel addressing system includes a backlight source and a liquid crystal modulator.
33. The apparatus of claim 30 wherein forming the array of pixels comprises depositing the first nanocrystal particles and the second nanocrystal particles on the panel.
34. The apparatus of claim 30 further comprising providing a long pass filter in operative association with the array of pixels.
35. A method comprising:
forming an array of semiconductor nanocrystals forming a pixel array of different colors on a panel, wherein the sizes of the nanocrystals determine the colors; and
providing a pixel addressing system operatively associated with the nanocrystal array for selectively optically exciting the nanocrystals to produce a luminescent color pattern of pixels.
36. The apparatus of claim 35 wherein the pixel addressing system includes a light source that produces only one wavelength of light.
37. The apparatus of claim 35 wherein the pixel addressing system includes a backlight source and a liquid crystal modulator.
38. The apparatus of claim 35 wherein forming the array comprises depositing the nanocrystals on the panel.
39. The apparatus of claim 35 further comprising providing a long pass filter in operative association with the array of pixels.
40. A multicolor display apparatus comprising:
a pixel array comprising at least first and second individually addressable pixels of different colors, the at least first pixel comprising a plurality of nanocrystals of a first size and the at least second pixel comprising a plurality of nanocrystals of a second size different from said first size, wherein the different sizes of the nanocrystals determine the different colors;
a pixel addressing system operatively associated with the pixel array for selectively optically exciting the nanocrystals in the first and second pixels.
41. The apparatus of claim 40 wherein the pixel addressing system includes a backlight source.
42. The apparatus of claim 41 wherein the backlight source is a source of ultraviolet light or blue light.
43. The apparatus of claim 41 wherein the pixel addressing system comprises a multielement backlight source, wherein each source element is independently operable.
44. The apparatus of claim 41 wherein the backlight source comprises source elements including LEDs or semiconductor lasers.
45. The apparatus of claim 41 wherein the backlight source comprises source elements comprising sources of ultraviolet light or blue light.
Description

This invention was made with U.S. Government support under Contract No. DE-AC03-76SF0098 between the U.S. Department of Energy and the University of California for the operation of LAWRENCE BERKELEY NATIONAL LABORATORY (LBNL). The U.S. Government may have certain rights to this invention.

BACKGROUND OF THE INVENTION

1. Field of the Invention

This invention relates generally to electronic displays and more particularly to multi-color electronic displays based on luminescent semiconductor nanocrystals.

2. Description of the Related Art

Flat panel display technologies are currently displacing cathode ray tube (CRT) displays. CRT's main disadvantages are volume, weight and power consumption. On the other hand, CRT's image quality, resolution, and color are still unsurpassed. An alternative technology, which has already made it to the market, is that of liquid crystal displays (LCDs).

In liquid crystal displays, an image is produced by turning “on” or “off” pixels by selectively passing or blocking light from a backlight. This is done with the help of sheet polarizers and by controlling the polarization state of the light as it traverses the liquid crystal. In a color display, each screen pixel is actually made of three separate dots, each with a respective red, green, or blue filter printed on the glass in front of it (a fourth white dot may also be included to adjust contrast). These three primary colors are mixed in various amounts to form the variety of colors the user sees. Since the backlight is unpolarized and its spectrum is broad, a considerable amount of light is dissipated on the sheet polarizers and color filters, making these displays energy inefficient.

Other important flat panel display technologies which are currently being developed are field emitters, plasma displays and multi-color semiconductors and polymeric light emitting diodes based on electroluminescence and/or optical pumping.

A nanocrystal (or nanometer crystal) is an organic or inorganic single crystal particle having an average cross-section no larger than about 20 nm (200 Angstroms), and preferably no larger than about 10 nm (100 A) and a minimum average cross-section of about 1 nm or in some instances even a smaller average cross-section, i.e. down to about 0.5 nm (5 A). Typically the nanocrystals will have an average cross-section ranging in size from about 1 nm (10 A) to about 10 nm (100 A). A semiconductor nanocrystal is a nanocrystal of group II-VI (e.g. CdS, CdSe, CdTe, ZnS, ZnSe, ZnTe), or group III-V (e.g. GaAs, InAs, InGaAs, InP) semiconductor compounds. Also included are group IV semiconductors such as silicon or germanium, and organic semiconductors. Nanocrystals are capable of emitting electromagnetic radiation upon excitation. The color of the emitted light depends on the size of the crystal and the material. The larger the crystal, the more red the output, and the wider the emission band. Nanocrystals generally have narrow emission bands, i.e. the wavelength band of emission does not exceed about 40 nm in the visible and preferably does not exceed about 20 nm. The width of the emission band scales with energy, not wavelength. Nanocrystals also generally have a broad absorption band, i.e. the electromagnetic radiation absorption continuously increases from the onset which occurs near to but at slightly higher energy than the emission band.

The growth of core/shell semiconductor nanocrystals is described in Xiaogang Peng et al., “Epitaxial Growth of Highly Luminescent CdSe/CdS Core/Shell Nanocrystals with Photostability and Electronic Accessibility,”J. Am. Chem. Soc. 1997, 119, 7019-7029. U.S. Pat. No. 5,505,928 to Alivisatos et al. describes the preparation of III-V semiconductor nanocrystals. U.S. Pat. No. 5,262,357 to Alivisatos et al. describes formation of thin films from nanocrystal precursors. U.S. Pat. No. 5,751,018 to Alivisatos et al. describes the bonding of semiconductor nanocrystals to solid surfaces.

U.S. Pat. No. 5,537,000 to Alivisatos et al. describes an electroluminescent device having an electron transport layer of semiconductor nanocrystals. The device has a hole injection layer, a hole transport layer, the nanocrystal electron transport layer, and an electron injection layer. Device output color is controlled by voltage as well as nanocrystal size and type. A flat panel display is produced from an array of the electroluminescent devices.

The use of luminescent semiconductor nanocrystals in biological probes is described in U.S. patent application Ser. No. 08/978,450.

SUMMARY OF THE INVENTION

The invention is a multi-color electronic display which utilizes arrays of luminescent semiconductor nanocrystals for pixel elements. Each pixel or addressable color element is formed of a number of suitably sized nanocrystals to produce a desired color. While the display can be based on the three primary colors, red, green and blue, greater flexibility in using many more different colors by selecting suitably sized nanocrystals to produce different colors is possible. In addition to the pixel array formed of the nanocrystals, the display includes a pixel addressing (including optical pumping) system. In one illustrative embodiment, a backlight source with a pixelated array of elements is used. In a second illustrative embodiment, a liquid crystal modulator is used to modulate a backlight. In a third illustrative embodiment, a modulated laser is raster scanned over the pixel array. Light of a single wavelength can be used to excite the nanocrystals of all colors. Ultraviolet or blue light sources are preferred. If UV backlight is used, all the pixels contain the appropriate sized nanocrystals; however, if blue excitation is used, then the blue pixels can contain no, nanocrystals and merely pass the backlight directly. A long-pass filter having the appropriate wavelength typically covers the pixel array.

BRIEF DESCRIPTION OF THE DRAWINGS

FIGS. 1A-G are simplified cross-sectional views of different embodiments of an optically pumped luminescent semiconductor nanocrystal based electronic display with three types of pixel addressing systems.

FIG. 2A illustrates one excitation scheme based on UV excitation.

FIG. 2B illustrates an alternate excitation scheme based on blue excitation.

DETAILED DESCRIPTION OF INVENTION

The invention comprises a color display which is based on the luminescence phenomena in semiconductor nanocrystals. It takes advantage of the following properties: (1) color tunability of the luminescence is obtained by quantum confinement through size control; (2) the luminescence of such nanocrystals is very narrow, i.e. spectrally pure; (3) the luminescence quantum efficiency of core-shell nanocrystals is very high; (4) the nanocrystals are photostable; (5) the absorption lineshape of the nanocrystals continues above an onset (which depends on particle size). Therefore, the luminescent semiconductor nanocrystals are capable of being excited over a broad bandwidth, yet exhibit emission in a narrow wavelength band. Thus, UV or blue light (UV/blue) as well as other color light may be used to excite different size nanocrystals with different emission spectra. For example, the same UV/blue light can be used to excite blue, red and green pixels to get the three needed primary RGB display colors with a single excitation source. Alternatively nanocrystals with any other colors can be used. More than just three colors can be used, i.e. any number of display colors, e.g. 25, could be used. While the invention is described primarily with reference to RGB pixels illuminated by UV or blue light, the principles of the invention apply to any color nanocrystals illuminated by any suitable color source.

As used herein, the term pixel refers to an independently addressable single color element, i.e. a group of red emitting nanocrystals which form a red color element on the display are referred to as a red pixel. The term pixel could be used to describe a combined element including a color element of each of the colors, e.g. a pixel with red, green and blue dots or subpixel elements. However, since each of the color elements must be separately addressable, it is simpler to refer to each color element as a pixel.

The display can be based on many different pixel addressing technologies. As used herein, the pixel addressing system includes both the excitation or optical pumping source and the means for addressing or exciting individual pixels in the array in a selected pattern. The modulation of the light for the display purpose can be achieved by direct modulation of a backlight source if it is pixelated and each pixel can be addressed and turned “on” and “off” by electronic means (FIGS. 1A-C, G). That will be the case, for example, for an array of individual UV/blue light emitting diodes (LEDs) or semiconductor lasers in the UV/blue region (based, for example, on GaN/InGaN technology) or a fabricated array of addressable two-dimensional LEDs or vertical cavity surface emitting lasers (VECSELs). The back light can also be modulated external to the source, as in the case of a liquid crystal display, where the backlight will be modulated when passing through the liquid crystal (FIGS. 1D-E). Pixels can also be addressed by a single-modulated laser beam which is raster scanned across the display, similar to rastering an electron beam in a CRT (FIG. 1F).

Instead of using color filters as in conventional LCDs, the screen “dots” are made of luminescent semiconductor nanocrystals. Each R, G, or B pixel, for example, contains single-sized, very high quantum-yield, very stable, core-shell nanocrystals with a very narrow emission spectrum (approx. 20-40 nm) in the red, green or blue. The nanocrystals can be deposited on a glass or other transparent panel by various techniques, e.g. by direct printing by inkjet technology, or by chemical bonding through specific glass and nanocrystal surface derivitization and patterning techniques, or by embedding nanocrystals in a polymer film and then patterning. Nanocrystals can also be dissolved in a liquid. Pixelation in this case is achieved by etching micro-wells into the panel and sealing individual size nanocrystals in solution into different wells. The concentration/optical density of nanocrystals in each dot is optimized such that the excitation light is efficiently absorbed to provide bright emission from the nanocrystals with minimal reabsorption.

Illustrative embodiments of an optically pumped luminescent semiconductor nanocrystal based display (showing three pixels), with three different pixel addressing systems, are shown in FIGS. 1A-G. The electronic displays 10 a-f of FIGS. 1A-F include a plurality or array 12 of nanocrystals 14, 18, 22 which form a plurality of pixels 16, 20, 24 of different colors. As shown the plurality or array 12 of nanocrystals include a group of red light emitting nanocrystals 14 which form a red pixel 16, a group of green light emitting nanocrystals 18 which form a green pixel 20, and a group of blue light emitting nanocrystals 22, which form a blue pixel 24. Display 10 g of FIG. 1G has a blue pixel 24 without nanocrystals. While an electronic display based on the three primary colors RGB is illustrated, the nanocrystal approach provides great flexibility in using virtually any number of different of colors since the colors can easily be obtained by selecting the proper sized nanocrystals to produce a desired color. The nanocrystal array 12 may be sandwiched between a glass or other transparent plate 26 and long-pass filter 28 (FIGS. 1A, D, E, F). The nanocrystals can be deposited, as solids or even in a liquid medium, on glass panel 26 in a number of different ways, including but not limited to the exemplary techniques described above. Alternately, the nanocrystal array 12 and plate 26 can be reversed (FIG. 1B, G), or plate 26 can be omitted (FIG. 1C), or filter 28 can be omitted (FIG. 1G).

While the nanocrystal array 12 is similar in the display embodiments 10 a-g of FIGS. 1A-G, the pixel addressing systems (including optical pumping sources) 40 a-c are of three different types. In FIG. 1A, backlight source 30 a is formed of a plurality or array of addressable or individually and independently operable source elements 42 a, b, c which correspond to an associated pixel 16, 20, 24 respectively. The source elements 42 a, b, c are typically UV or blue LEDs or semiconductor lasers (the schematic representations include associated electronics). As source elements 42 a, b, c are turned on and off, the associated pixels 16, 20, 24 are turned on and off, producing a color display. To avoid diffraction effects, backlight source 30 a should be as close to nanocrystal array as possible, i.e. contacting panel 26 (distance D=0).

Variations in displays using addressing system 40 a are shown in FIGS. 1B, C. In FIG. 1A, backlight source 30 a is separated from nanocrystal array 12 by plate 26. In order to get array 12 even closer to source 30 a to reduce diffraction effects, array 12 and plate 26 can be reversed, as shown in FIG. 1B. Display 10 b has array 12 deposited on plate 26, but backlight source 30 a is up against the array 12 side of plate 26 instead of the opposite side. Since array 12 is in contact with backlight source 30 a, it may be possible to deposit array 12 directly on source 30 a, and omit plate 26 altogether, to from display 10 c, as shown in FIG. 1C.

In FIG. 1D, display 10 d has an addressing system 40 b in which backlight source 30 b is a single source. Light from backlight source 30 b is modulated by a liquid crystal modulator 44 positioned between source 30 b and nanocrystal array 12. Light from backlight source 30 b, which is typically an ultraviolet or blue light source, passes through polarizer 34 into the liquid crystal 32. Liquid crystal 32 is modulated by electrical signals applied on contacts 36 on opposed faces thereof, to produce the appropriate patterns of excitation signals to excite the nanocrystal array 12. The modulated excitation, light from the liquid-crystal 32 passes through an analyzer 38 which is a polarizer with its axis orthogonal to that of polarizer 34 and through glass plate 26 into the nanocrystal array 12. When the part of liquid crystal 32 which corresponds to a pixel is off, light passing through polarizer 34 is blocked by analyzer 38. When the liquid crystal 32 is turned on, the liquid crystal rotates the polarization of the light passing through so that the light is passed by analyzer 38 to array 12 to excite the pixel. If soure 30 b is polarized, then polarizer 34 can be omitted. The position of array 12 and plate 26 can also be reversed as in FIG. 1B. FIG. 1E shows a display 10 e which is similar to 10 d. Backlight 30 b is a slab or waveguide 46 which is end pumped by pump source 48 and emits light along a lateral side.

In FIG. 1F, the optical pumping source (addressing system) 40 c of display 10 f is a single laser 30 c which can be modulated and raster scanned across the nanocrystal array 12. Thus as the output, beam of laser 30 c sweeps across the nanocrystal array 12 in a pattern, the output beam is turned on and off depending on whether a particular pixel 16, 20, 24 is to be on or off during that particular scanning cycle.

FIG. 1G shows a display, 10 g which is similar to display 10 b, but which utilizes the excitation scheme of FIG. 2B. Blue pixel 24 is formed as an open space without nanocrystals and passes blue light from source 30 a. No filter 28 is required over the blue pixels.

Although illustrated with these three optical pumping systems, various other optical pumping schemes can also be used. Any color excitation light source can be used. The only requirement is that the light source have higher photon energy compared to the color of the display. An infra-red (IR) display could be produced.

Various backlight excitation schemes can also be used, e.g. as illustrated in FIGS. 2A, B. If. UV backlight excitation is used (scheme A, FIG. 2A), all 3 RGB pixels contain the appropriate size nanocrystals. If blue excitation is used (scheme B, FIG. 2B) the blue pixel will contain no nanocrystals and pass the backlight directly (FIG. 1G). In scheme A, a long-pass filter with the appropriate cut-off wavelength (pass RGB but not UV excitation light) will pass the emitted light from the nanocrystals and block unwanted excitation light from passing through. In this case the filter will cover all pixels. In scheme B an appropriate long pass filter (pass RG but not blue light) will be implemented only for green and red pixels (no filter for blue pixels). If the optimal optical density is large enough (OD about 2), no filters are needed because the backlight will be entirely absorbed by the nanocrystals.

This invention makes very efficient use of the backlight since the photo-luminescence quantum efficiency is very high and there are no absorbing filters. Optical pumping of nanocrystals is much superior to electrical pumping (electroluminescence) and should provide for very efficient, bright and vivid colors. The spectral purity of the emission and ability to control the color of emission allows the display to span the whole chromaticity diagram and therefore obtain any desired color with high quality.

In the case of a liquid crystal display implementation, the use of polarized UV/blue laser backlight can eliminate one of the sheet polarizers, making the device even more efficient.

Other advantages of optically-pumped nanocrystal based displays are in: (1) the ease and simplicity of fabrication; (2) they can be used for flexible and large area displays; (3) they are compatible with very high resolution displays (especially when pumped with UV/blue light); (4) high extinction coefficients can be achieved with thin films; (5) very, good size distribution will eliminate self absorption because of Stokes shift.

Changes and modifications in the specifically described embodiments can be carried out without departure from the scope of the invention which is intended to be limited only by the scope of the appended claims.