US 20050151256 A1
A dielectric wiring structure and method of manufacture therefor. The wiring structure includes air dielectric formed in a hemisphere. The wiring structure also includes, in embodiments, a method of simultaneously forming a MEMS structure with a transistor circuit using substantially the same steps. The MEMS structure of this embodiment includes freestanding electrodes which are not fixed to the substrate.
19. A method of forming a wiring structure comprising the steps of:
forming a removable dielectric structure with wiring contained within the removable dielectric structure, the wiring including wire levels; and
etching multiple regions of the removable dielectric structure to form air gaps,
wherein the wiring extends from within the etched region to an adjacent non-etched perimeter region.
20. The method of
21. The method of
22. The method of
forming a vent hole in the capping layer;
removing the removable dielectric layer; and
plugging the vent hole.
23. The method of
forming a permanent structure in contact with and supporting the wiring while forming the removable dielectric structure; and
etching the permanent structure exposed within the multiple etched regions,
wherein the step of etching the permanent structure first includes etching the multiple etched regions, and the wiring and the permanent structure are contained within the removable dielectric structure.
24. The method of
the permanent structure is a horizontal layer in contact with the wiring contained within the removable dielectric structure; and
the horizontal layer is at least two horizontal layers;
the etching step is an isotropic etch which etches the removable structure and further etches through at least one of the horizontal layers thereby forming the multiple etched regions, the multiple etched regions are sections of multiple hemispheres.
25. The method of
refilling the multiple etched regions with a removable dielectric layer;
forming a permanent layer on a surface of the non-etched perimeter region prior to the refilling step; and
capping the etched multiple regions after the refilling step,
wherein the multiple etched regions are formed by isotropic etching through a capping layer formed by the capping step which is substantially removed.
26. The method of
27. The method of
28. The method of
29. The method of
forming a permanent structure for at least one of the wire levels of the wiring by etching a wire trench and a via trench in the removable dielectric structure, wherein the permanent structure includes:
depositing a metal liner in the wire trench;
electroplating copper on the metal liner; and
polishing the metal liner and the copper from a surface of the removable dielectric structure, and
depositing a layer of dielectric on the metal liner which is to form a permanent layer.
30. A method of forming a wiring structure comprising the steps of:
forming at least a transistor on a substrate in a first region;
forming a multilayered stack wiring level containing at least one conductor and removable material layer in a second region adjacent to the first region;
patterning the at least one conductor to form an electrode of a micro-electromechanical (MEMS) device;
simultaneously forming removable interlevel dielectric overlying the transistors of the first region and surrounding the multilayer stack of the second region which connect to the transistors;
forming wires which interconnect with the MEMS device;
forming air dielectric by removing the removable interlevel dielectric simultaneously overlying the transistors in the first region and the second region; and
removing the removable material to form a moveable electrode.
31. The method of
simultaneously forming a permanent dielectric within the second region overlying the transistors of the first region, wherein
the permanent dielectric being resistant to attack by a method used to remove the removable dielectric,
the permanent dielectric interconnects and supports the wiring, and
the permanent dielectric connects to and supports the at least the conductor of the multilayer stack wiring level.
32. The method of
forming trenches in the removable dielectric; depositing a conductive layer on walls of the trenches;
electroplating copper on the surface of the conductive layer; and
polishing the copper from a top surface of the removable dielectric to leave a copper line within the trenches.
33. The method of
the multilayered stack wiring layer is at least two multilayered stack wiring layer,
one of the at least two multilayered stack wiring layers has a top conductor layer,
the method including the further steps of:
forming trenches in the removable dielectric, wherein at least a first set of trenches in the second region being formed over an edge of the multilayered stack wiring layer;
depositing a contact in at least a second set of trenches contacting a top conductor layer of one of the multilayered stack wiring layers; and
forming vents in the first region and the second region.
34. A method of forming a micro electromechanical structure with two moveable elements comprising the steps of:
forming a first layer which includes a first area of at least one material which will become a first moveable element;
depositing a removable dielectric to form a first removable spacer;
forming a second layer which includes a second area of at least one material which will become a second moveable element onto the removable spacer, the second area overlying the first area;
forming and patterning a material which overlies the first area and the second area, wherein the patterned material is a mask for etching;
etching a first edge of the first area and a second edge of the second area where the second edge directly overlies said first edge;
depositing a resistant material which is resistant to a method used to remove the removable spacer to form a layer which connects the first edge to the second edge; and
removing the removable dielectric.
35. The method of
36. The method of
This application is a continuation-in-part of U.S. application Ser. No. 09/064,546 filed on Apr. 22, 1998, and now issued as U.S. Pat. No. ______.
1. Field of the Invention
The present invention is related to microelectronics and, more particularly, to microelectronics having air dielectric wiring for reduced capacitance or having a cavity which contains micro-mechanical or micro-electromechanical structures.
2. Background Description
Integrated circuit (IC) performance is dependent upon individual circuit performance. Individual circuit performance is dependent on the load the circuit must drive. For field effect transistor (FET) circuits, the primary load is capacitive. The primary source of the circuit load capacitance is inter-circuit wiring capacitance. Thus, IC performance can be improved by reducing wiring capacitance.
Typical IC chips with a large number of logic circuits include multiple layers of wires, called wiring layers, stacked one on top of another and separated by dielectric material. The ideal dielectric is air or, at least has the same dielectric constant as air. There are several approaches to providing an air dielectric in IC chips.
Another type of microelectronic chip includes micro-electromechanical (MEM) devices, preferably integrated on the same substrate with transistors and their interconnections. Motion of the MEM devices requires that they be within a gas or vacuum filled cavity.
One approach is to remove the dielectric around the wires, suspending the wiring in air. The suspended wires are uncovered with any dielectric and are supported, mechanically, only by interlevel metal studs used to form the circuit. Although scanning electron microscopic (SEM) images of such structures clearly show that small lengths of wire are self supporting, longer lengths of wire are not self-supporting. So, longer lengths of unsupported wire are susceptible to shorting.
For example, U.S. Pat. No. 4,899,439 entitled “Method of Fabricating A High Density Electrical Interconnect” to Potter et al. teaches building pillars from the substrate under the wires extending upward to upper wiring levels wherever support is required. However, because wiring channels must be allocated for these pillars, the pitch or density of wires is reduced by as much as half.
Another approach is to stiffen the wires, such as taught in U.S. Pat. No. 5,148,260 entitled “Semiconductor Device Having an Improved Air Bridge Lead Structure” to Inoue et al., wherein the metal lines are formed from a stiffer composite metal that is less likely to deform than typical wiring metals. This approach reduces, but does not eliminate shorting in an air dielectric IC structure. Further, Inoue et al., also requires including some support pillars, although not as many are required as in Potter et al.
Both Potter et al. and Inoue et al. teach structures that are formed using conventional techniques, with the removable dielectric material removed through several repeating layers of metal studs and metal lines. Material may be backfilled around the freestanding wires to provide a dielectric other than air.
Gravity is the primary focus in abating shorting problems in prior art freestanding IC wiring structures. Other accelerations such as vibrations and impact are also a problem. Thus, to counteract gravity, a strong support is provided from below the wires.
The above examples of the prior art incur a substantial wiring density penalty because the support pillars extend through several wiring levels, all the way up from an underlying substrate. These small diameter support pillars are formed level by level and so, must be lined up at each level with an underlying level.
To simplify this critical alignment requirement, a stiff intermediate planar layer may be formed on each support pillar level. Thus, the pillars would support the planar layer and the planar layer supports another pillar level. For this type structure, pillars need not line up from level to level. However, any dielectric must be removed after the planar layer is formed by complex venting and filling steps or the dielectric is trapped under the permanent planar layer.
A typical prior art approach, when using planar layers to construct freestanding structures, is to form an air dielectric on a layer by layer basis. For example, in U.S. Pat. No. 5,144,411 entitled “Method and Structure for Providing Improved Insulation in VLSI and ULSI Circuits”, to Kaanta et al. (hereinafter Kaanta), a planar dielectric layer is formed directly below the next higher level of metal lines but above a lower layer of metal lines or on pedestals above the lower layer of metal lines with a complex process requiring extra masks. Kaanta teaches etching access openings through the planar layer, removing the dielectric and plugging the openings. Presumably, the next level of metal lines is formed on top of the planar dielectric by Reactive Ion Etch (RIE) of a metal layer which was deposited on the planer dielectric. Each successive metal layer is formed on top of a permanent planar layer of dielectric.
In Kaanta, the wire is anchored on only a single surface of the wire, and that surface is a flat surface on the underside of the wire. The flat surface, in turn, is anchored to the planar layer. Such a structure, stemming from the RIE method used to pattern the metal on top of the planar layer is susceptible to detachment from shear forces in a direction parallel to the planar layer. A more stable structure is needed to increase the stability of the structure. Furthermore, it is difficult to pattern certain metals such as copper by RIE, and thus an alternative method is needed.
U.S. Pat. No. 5,444,015 entitled “Larce (sic) Scale IC Personalization Method Employing Air Dielectric Structure for Extended Conductors” to Aitken et al. (Hereinafter Aitken), assigned to the assignee of the present invention, teaches an approach similar to Kaanta that reduces the extra masks by forming openings in a removable dielectric for studs and supports simultaneously.
In Aiken, however, the wire is anchored on only a single surface of the wire, and that surface is a flat surface on the underside of the wire which is anchored to the planar layer. Such a structure, stemming from the deposition of metal onto a completely planar layer, may be susceptible to detachment from shear forces in a direction parallel to the planar layer.
Also, the support dimensions in Aitken are not as large as studs. After forming support openings, Aitken teaches depositing dielectric to fill the support locations and line stud openings. An anisotropic etch removes support dielectric from the bottom of the stud openings that are filled with metal in subsequent steps. Aitken stud opening diameters must be wider (twice the thickness of the dielectric tube) than the studs themselves, which must be larger than the minimum process dimension.
Prior art structures are typically supported by pedestals. The circuit design tools must keep track of whether inter-level features are studs or pedestals. Further, circuit design is more complicated because the wiring and the support pedestals must be accounted for on each wiring level.
None of the methods of the previously discussed prior art is useful when the metal lines are patterned by polishing, such as by chemical-mechanical polishing (CMP). The industry is moving toward copper wiring which is patterned by CMP. A method for forming an air dielectric is needed which is compatible with copper processing.
Although Kaanta and Aitken can both have planar layers in their structures, they both suffer from previously mentioned structural weaknesses toward shear forces.
Freestanding Micro-Electromechanical Structures (MEMS)
Prior art MEM devices use freestanding self supporting structures composed of a sequence of polysilicon, metal, or sometimes silicon nitride studs and lines. Structures are supported by the underlying substrate. The interlevel freestanding structure is generally a conductor which is supported by the underlying substrate. In these structures, the electrical interconnects are at the substrate level, and the interconnects can not be made directly to overlying wiring or to the outside of the structure without first connecting down to the substrate. It is further noted that in the prior art systems, no unrelated structures, transistors or wiring are based below the MEM device because the substrate is needed for electrical contacts and to support the MEM structure. See for example, U.S. Pat. No. 5,367,136 to Buck, U.S. Pat. No. 5,578,976 to Yao, Gretillat et. al. in “IEEE Micro-Electro-Mechanical Systems Workshop, 1995, pg. 97-101”, or Goldsmith et. al. in “IEEE Microwave and Guided Wave Letters, 8 No. 8, pp. 269-271.
Although MEMS have been integrated with electrical transistors and circuits on silicon (Bustillo et. al. Proceedings of the IEEE 85, No. 8, August 1998, on page 1556-1558) there is no known prior art related to integration of MEMS with electrical transistors and circuits which include wiring surrounded by a gap or air dielectric. There is also no known structure relating to a combination of MEMS with copper wiring, and more particularly to a combination with copper wiring which also includes an air dielectric.
Generally, MEMS structures are defined in a complete process block, independent of the process blocks used to define the transistors and wiring of the electrical circuits. Since the MEMS also occupy their own regions of silicon, cost savings are minimal compared to an approach which is able to combine a large number of process steps, each of which contributes to simultaneous formation of an element of both the circuit and the MEMS structures, or compared to an approach which is able to form MEMS structures above regions of silicon substrate which have transistors. Bustillo shows a structure (
Since the MEMS structure is already at the top of the substrate, there is an advantage that the electrical connections do not need to go back up to overlying wiring. However, there are severe restrictions placed upon the composition and conductivity of the wiring based partly on the fact that the MEMS structure is made of polysilicon and therefore requires temperatures higher than can be tolerated by many wiring materials. A low temperature process by Nguyen could replace the polysilicon with nickel, but the process would still require a block of processes independent from those required for the CMOS wiring. In any case, no prior art teaches MEMs overlying transistors with high conductivity wiring or in particular with a high performance dielectric.
Attempts to integrate MEMS with CMOS also pose problems. For instance, polysilicon gates in CMOS do not need to connect to the substrate, but prior art MEMS polysilicon does need to be supported by the substrate. Also, there is a need for BEOL MEMS which can be easily integrated with conventional CMOS BEOL. In particular, it is necessary to be able to pattern dissimilar metals on the same level so that the identity of the CMOS metal can be optimized for CMOS and the identity of the MEMS metal can be optimized for MEMS.
Also, MEMS structures are plagued by stress induced deformation of electrodes because electrodes/structures form internal stresses and strains during the construction of the structure which are relieved by deformation when the material surrounding the structure is etched to form a “released” or free-standing structure. (See for example Bustillo, page 1559 at the top of the second column.) Very narrow gaps are often required between the released structure and the counter-electrode on the substrate in order for the voltages required to operate the MEM device to be low enough so that they are compatible with the voltages required in associated electrical circuits. There is thus a trade off between wider gaps with higher device yields and a desire for low voltage operation with corresponding narrow gaps and therefore reduced yields.
Another limitation is that most MEMS structures use one element (electrode) which is freestanding and another element (substrate) which is not freestanding in fact, the substrate is fixed. Also, a light, stiff moveable element has less susceptibility to acceleration, but drive voltages are increased (Proceedings of Aerospace conferences, 1997, IEEE, p. 285, modulus discussion). There is thus a need to simultaneously improve both the susceptibility and increased voltages to accelerations.
Materials and Processing
Materials used in prior art methods for creating air dielectrics are exotic and, so, are expensive to develop and difficult to remove. Kaanta, for example, teaches using parylene as a removable dielectric. Parylene has a low decomposition temperature, which severely restricts the materials that can be used for the freestanding structures.
Furthermore, typical prior art methods use aqueous chemicals to etch the removable material. It is uncertain whether these aqueous chemicals can penetrate the convoluted paths to regions buried deep within the wiring that must be cleared of removable dielectric. In particular, when dielectric removal is deferred until the end, or, for structures with vented planar layers such as U.S. Pat. No. 5,324,683 to Fitch et al. entitled “Method of Forming a Semiconductor Structure having an Air Region” (which is even more complex than Kaanta), these aqueous chemicals penetrate vent holes with considerable difficulty.
Further, after reaction and drying, the reaction products may not be removed completely from the nearly enclosed air dielectric compartments. These small openings make it difficult for reactants to diffuse in, or for waste products to diffuse out, when the cavities are filled with a liquid.
Additional problems arise when aqueous HF is used to remove oxides from the exposed metal lines. The HF in the aqueous solution can attack the metal, especially when the lines are a composite metal. Electrochemical potentials further contribute to corrosion of one metal of the composite. Such an attack can result in open electrical circuits, higher line resistivity, and the metal lines separating from their supports.
Thus, there is a need for a way to remove dielectric from metal lines without attacking the metal, with adequate penetration of small openings and subsequent removal of reaction waste products from the structure. Further there is a need for a way to form air dielectric structures on integrated circuit chips without increasing the number of masks, requiring complex vent and fill procedures or difficult support alignment.
It is a purpose of the invention to provide a manufacturable integrated circuit structure with an air dielectric wiring.
It is another purpose of the present invention to anchor the wiring in an air dielectric structure for mechanical strength to minimize shorts between wires.
It is yet another purpose of the present invention to provide a manufacturing process for fabricating integrated circuit structures with air dielectric wiring.
It is yet another purpose of the present invention to simplify manufacturing integrated circuit structures with air dielectric wiring.
It is yet another purpose of the present invention to provide a method of manufacturing air dielectric structures that can define wiring support after wiring definition.
It is yet another purpose of the present invention to provide a method of manufacturing air dielectric structures that does not require removing the dielectric and forming wires on a weak substrate.
It is yet another purpose of the present invention to provide a method of manufacturing air dielectric structures using existing integrated circuits and materials to create the air dielectric structure.
It is yet another purpose of the present invention to provide wiring which has a non-planar contact with a planar supporting plane.
It is yet another purpose of the present invention to provide air formation with Copper.
It is yet another purpose of the present invention to provide simultaneous MEMS cavity and air dielectric planar support in wiring and sidewall support in MEMS.
It is yet another purpose of the present invention to provide a process sequence using multiple common steps to lower the costs of manufacturing.
It is yet another purpose of the present invention to provide copper wiring with a dissimilar MEMS material between MEMS and wiring.
It is yet another purpose of the present invention to provide an AC/DC switch and voltage operated capacitor.
It is yet another purpose of the present invention to provide MEMS having a structure with less sensitivity to stresses and less susceptible to acceleration.
It is yet another purpose of the present invention to provide MEMS with high electrical conductivity.
It is yet another purpose of the present invention to provide MEMS elements with compliant support.
It is yet another purpose of the present invention to provide MEMS devices with improved drive voltage/gap trade-off.
It is yet another purpose of the present invention to provide suspension of MEMS devices without substrate contact which provides a simplified construction.
It is yet another purpose of the present invention to provide MEMS devices with unrelated wiring underneath the substrate.
It is yet another purposes of the present invention to improve an effective dielectric constant and the structure of the class of wiring structures which include a combination of wires, dielectric supports and air gaps.
The present invention is an air dielectric wiring structure and method of manufacture therefor. Successively formed wiring layers synergistically combine with interwire supports, either a subsequently formed sidewall or an improved planar layer, to form a self supporting air dielectric interconnection matrix.
Complex venting and plugging problems are avoided by using an easily removable dielectric, that can be virtually completely removed. Wires are supported by vertical sidewalls or an improved planar support layer in combination with wiring studs. An optional dielectric cladding may be left on the metal wires for short and oxidation protection. Because sidewalls or planar layers are formed after wiring, with the wiring at each level providing support definition, complex support alignment is unnecessary.
In one embodiment, sidewalls are formed after removing dielectric between the wires support and the otherwise free-standing wires. The sidewalls hold the wires vertically and connection between the successive perpendicularly aligned wiring levels interact to anchor each other. The dielectric wiring structure may include a thin dielectric covering, preferably of the same material as the sidewalls, that completely or partially covers the wiring and extends from each wire side down to lower levels of the air dielectric structure. The dielectric covering coats and protects the wires and anchors the wires in position. Thus, the incidence of shorting between wires in the air dielectric structure is reduced.
In the methods of manufacturing the air dielectric structure, after completing wiring layers for an integrated circuit, dielectric, preferably SiO2 and possibly including nitride planar layers, is isotropically etched away in a pre-defined region, or anisotropically etched to a depth traversing at least a part of two or more wiring layers, leaving each wire on each exposed or partially exposed layer on or embedded within lengthwise SiO2 pillars. A conformal layer of etch resistant (to SiO2 etch) material is formed on the etched structure to form sidewalls at each SiO2 pillar, ie., at the edges of each exposed or partially exposed wire. Alternately, the previously removed (by the etch) SiO2 may be replaced with etch-resistant material filling between the wires. The remaining SiO2 fill is removed through vents formed in the etch-resistant material.
In another embodiment, fill dielectric is anisotropically sub-etched away from the wiring layers by a first etch step, using the circuit wiring as an etch mask. The sub-etch traverses a portion of at least two orthogonally aligned wiring layers and terminates slightly before reaching an underlying etch resistant insulating material layer or at the layer, if the resistant insulating material layer is non-planar. A conformal layer of an etch resistant insulating material is applied. The structure is etched with an anisotropic etch to remove horizontal surfaces of the conformal coating and, especially to open the conformal layer at the bottom of the structure, thereby exposing the underlying fill dielectric. The exposed fill dielectric and all fill dielectric in contact with the exposed fill dielectric is then removed.
In one embodiment, the fill dielectric is silicon dioxide and the etch resistant insulating material is silicon nitride. The exposed silicon dioxide is etched using reactive ion etching (RIE) to a point above a silicon nitride layer. A thin layer of silicon nitride is then conformally deposited on the structure. A second anisotropic reactive ion etching step opens the silicon nitride and exposes the underlying silicon dioxide. A vapor HF etch is used to remove the remaining silicon dioxide until only the silicon nitride, the circuit wiring, or other etch resistant materials remain and are exposed to air. The result is an embodiment integrated circuit with air dielectric wiring having a thin silicon nitride layer stabilizing and holding the suspended wires in their original position.
In another embodiment, a permanent vented planar layer of dielectric is formed on the top of (overlying) each successive wiring layer. The top surface of the wires of each wiring level is made non-planar, prior to deposition of each permanent vented planar layer. Making the top surface of each wire non-planar offers the key advantage that the wiring, especially in long wiring runs to be more resistant to shear stresses than in prior art structures which include a planar layer which underlies the wiring and where the surface of the wire in contact with the planar layer is also planar. In an embodiment which has even greater resistance to shear stress, the sides of the wiring layers are tapered and/or the removable material which lies between the wires is further recessed below the top surface of the wiring prior to deposition of the vented planar layer. The removable material is removed through the vents after all of the wiring levels are formed. In fact, the vents can be formed after the completion of the wiring levels. An additional advantage of the invention is the placement of a planar layer over the top of the wiring rather than under the wiring. In this manner, the present invention is compatible with copper wiring formed by the “dual damascene” method where lines and studs are simultaneously formed and the wiring is patterned by Chemical Mechanical Polishing (CMP) after filling a trench in a dielectric with copper. The process of the present invention requires only a few additional steps to implement with copper wiring.
In another aspect of the invention, the air dielectric wiring is combined with micro-electromechanical (MEMS) devices. This aspect benefits from a hybrid of two embodiments described above. Sidewall support of the MEMS devices enables use of symmetrical parallel electrode structures where there is less susceptibility to residual stresses than previously obtainable. The hybrid design also enables easy, economical combination with copper wiring with an air dielectric. However, the resistance to stress in the sidewall supported MEMS is obtained whether or not the wiring elsewhere on the integrated circuit has an air dielectric. Accordingly, in yet another advantage of the present invention only minimal extra steps are required to form the hybrid MEM device.
When the present invention omits wiring down to the substrate when creating MEMS there is process and structure simplification. This facilitates construction of parallel freestanding structures which gives rise to an additional benefit, i.e., less susceptibility to interference from shock/acceleration, because both parallel structures are freestanding. For example, when one electrode (substrate) is fixed, then the substrate electrode and the freestanding electrode have differing response to forces which are felt by both the substrate and the electrode. Likewise, if the construction shapes are vastly different, then the responses will also be vastly different. If instead of one electrode being fixed to the substrate, both the electrodes can move and are symmetric, then there is addition benefit of reduced voltages required for a given deflection. Movement of both electrodes contribute to a change in relative position in contrast to when one electrode is fixed by the substrate. Then, relative motion must come from the single moveable electrode.
The foregoing and other objects, aspects and advantages will be better understood from the following detailed description of a preferred embodiment of the invention with reference to the drawings, in which:
The inventor of the present invention discovered that gaseous HF may be used to remove silicon dioxide (SiO2) from a layered wiring structure without the normal damage to the wires. The damage that occurred in prior art methods was the result of using an aqueous solution to remove fill dielectric. The prior art aqueous solution invariably attacked the metal wires as it removed the fill dielectric. Although gaseous HF has been used to remove thin reactive ion etch (RIE) residues from metal lines, it was heretofore believed that the long exposures necessary for oxide dielectric removal were similarly corrosive.
However, as the inventor has found, using gaseous HF, preferably at a partial pressure between 5 and 30 Torr., SiO2 may be stripped completely away from a wiring structure, leaving the metal wires and studs behind unharmed. The gaseous reaction operates through formation of a thin aqueous film.
As a result of that discovery, the inventor further discovered that, in the microscopic world of these IC wires, other residual forces from stresses and strains introduced during construction overshadow gravitational forces. By removing the SiO2 dielectric that normally encases long IC wiring runs, the freestanding wires are as likely to relax in a lateral or even an upward direction as in a downward direction, i.e., they will bow up, down or sideways.
Consequently, in the embodiment a gaseous material, preferably gaseous HF, is used to remove fill material, preferably SiO2, encasing a wiring structure. As fill material is removed, sidewall supports are formed to hold the wires in place. Thus, structures formed according to the embodiment method have wires that are supported in all directions.
Referring now to the drawings, and more particularly to
Although generally referred to herein as metal wiring surrounded by an air dielectric, the present invention may be applied to any microstructure that is desired to be freestanding, or entirely unsupported by underlying material layers. Further, as described herein, the air dielectric structure is shown as being formed in metal wiring layers 100, 102 and 104. However, an air dielectric structure may extend above and below layers 100, 102 and 104 and throughout the layers of an integrated circuit chip with a bottom layer being a polysilicon gate layer.
Thus, to form an air dielectric structure, first wiring layer 100 is formed above a semiconductor body 106 which may be a silicon substrate or the surface of an insulator layer in, for example, a silicon on insulator (SOI) wafer. After forming the first wiring layer 100 according to any well known process, a thin etch resistant layer 108, preferably silicon nitride or diamond-like crystallized carbon, is formed on the wiring layer 100, at least in an area where a preferred air dielectric structure is to be formed. A first fill material layer 110, e.g. an oxide layer, is formed on the thin etch resistant layer 108. The second wiring layer 102 is formed on the first insulating layer 110. A second fill layer 112 is formed on the second wiring layer 102. The second fill layer 112 is of the same type of fill material as in the first 110. The third wiring layer 104 is formed in the second fill layer 112 using a damascene process where metal is formed by: a) etching channels in layer 112; b) filling the channels with metal; and, then c) polishing the metal off the top of the insulator to leave it in the channels 114. Alternately, the third wiring layer 104 may be formed on the second fill layer 112 with fill material formed over the third wiring layer 104 to fill between the wires 114 in the third wiring layer 104.
Further, to protect the topmost wiring layer from attack during RIE removal of the fill oxide, a patterned resist material layer having the same pattern as the topmost wiring layer may be added to protect the upper wiring layer. Thus, for example an upper aluminum wiring layer may be protected using the same resist used to define the metal. Thus, immediately after patterning the metal, and before stripping the photoresist, the oxide is removed in a RIE step.
Horizontal portions of conformal layer 130 are removed using an appropriate anisotropic RIE, leaving sidewalls 132 in
An isotropic etch using gaseous HF removes all of the remaining accessible fill material through the accesses, i.e., all fill material between sidewalls 132 under wiring layers 102 and 104, as well as layer 128, leaving behind a honeycomb-like sidewall structure. Thus, virtually all of the fill material is removed, leaving behind the wires in layers 100, 102 and 104 held in place by the honeycomb-like sidewalls 132. The synergistic matrix of interconnected wires and sidewalls so formed is self supporting.
It is important to note that for preferred embodiment wiring, sidewall pedestals between wiring layers need not be aligned throughout the resulting multilayer structure. It is only necessary that each sidewall pedestal rest on or support either another sidewall pedestal or a previous/subsequent level wire. Furthermore, it is unnecessary that each sidewall pedestal align with a sidewall pedestal in adjacent layers. It is only necessary that each sidewall pedestal intersect with another sidewall pedestal in an adjacent layer. A thin, sub-lithographic layer of dielectric material sidewall may both sufficiently support the wiring and partially coat the wires with dielectric (protecting them from shorts) without requiring extra masks. As a result a large percentage of volume of the final structure is air.
The sidewall pedestals may rest on and be supported by studs of an underlying wiring level, or by a stiff overlying layer, or some combination of the two. If the sidewall pedestals do contact an underlying substrate it is advantageous that they contact a non-planar substrate, so that the sidewall pedestals do not seal in the removable fill material, i.e., the SiO2 pedestals.
The resulting structure is shown in
Although the method of the preferred embodiment may be used to form a single suspended wire, preferably it is used to form multiple levels of wires in a complex structure. Increased rigidity and improved electrical insulation also prevents shorts from deformed wiring observed with prior art freestanding wire.
The final etch in the embodiment is an isotropic oxide etch which must etch oxide with high selectivity to the metal lines and the nitride masking layers and, further, through channels with a very high aspect ratio. The worst case aspect ratios encountered are when directionally oriented wiring layers align and have the same pitch, e.g. layers 100 and 104 in
In an alternate embodiment wiring layer 100 is formed in an undoped oxide. Fill layers 110 and 112 at wiring layers 102 and 104 are doped silicon dioxide such as phosphosilica glass (PSG). Since vapor HF etches PSG with high selectivity to undoped silicon dioxide, in this embodiment etch resistant nitride layer 108 may be eliminated. After stripping PSG, stripping ends at the underlying undoped silicon dioxide, making nitride layer etch resistant layer 108 unnecessary.
Further, although nitride is the preferred etch resistant material for sidewalls, other suitable materials, such as diamond or diamond-like carbon which is resistant to etching by vapor HF, and has a low dielectric constant may be used as well. A suitable sidewall material must be an electrical insulator capable of forming along sidewalls, providing structural support, and must be etch resistant to the etch used to remove the fill material when form the air dielectric.
In a second alternate embodiment, the fill material is silicon and the sidewalls are formed by oxidation of the silicon. After silicon oxidation, the remaining underlying silicon may be removed with an isotropic, wet etch using, for example KOH or pyrocatechol. Optionally Chemical Dry Etching (CDE) or another appropriate dry etch may be used to remove the silicon.
In yet another alternate embodiment, the fill material is removed by dissolution. Using, for example, a damascene process to define metal patterns directly in a layer of photoresist, the photoresist is anisotropically etched with the metal lines as a mask. Then, a sidewall is deposited. The bottoms of the sidewall are etched using a RIE. Then, the remaining photoresist is removed with a solvent. Alternately, a downstream or other plasma source may be used to remove the residual photoresist. Further, the fill material may be a water soluble inorganic, such as boron or germanium oxides. Many organics and inorganics can be easily removed by evaporation or thermal decomposition. Thus, making the fill material of such an organic or inorganic material, it may be removed by thermal decomposition or by evaporation.
Alternately, to minimize exposing the wiring layers 100, 102 and 104 to the oxide RIE, the sidewall layer may be formed stage by stage as each wiring layer is formed as represented in
Although each stage is described as a wiring layer, it is contemplated that a stage may be two or more layers and that the individual stages may each be different multiples of wiring layers. Thus, the first layer 140 of layered metal structure is formed of a conductive material such as aluminum, copper or the like, and patterned by any typical method. In this embodiment, the wiring layer 140 or a resist cap (not shown) on the wiring layer 140 acts as a RIE mask. With the wiring layer as mask, fill material is removed from between the wire patterns.
A conformal sidewall layer 148 is deposited on the stripped wiring layer 140 and anisotropically etched to remove horizontal portions of the sidewall layer (not shown). A fill material is deposited to fill spaces between sidewalls, forming a planar surface. Each subsequent via or wiring layer, e.g., layers 144 and 146, is formed by repeating these steps, i.e., pattern wiring, RIE to strip fill down to the next lower wiring layer, deposit a conformal layer 148′ and 148″, anisotropic RIE to remove horizontal conformal layer portions and deposition of interlayer dielectric. After forming all metal levels, the remaining fill is removed using a vapor HF process as described in the above embodiment.
In another alternate embodiment shown in
In this embodiment, after the anisotropic etch, a conformal sidewall material is deposited as in the above embodiment. Sidewall material may be deposited before or after removing the patterned etch resistant material 150. For this embodiment, the conformal sidewall layer may be vented either: by an anisotropic etch removing portions of the conformal layer from horizontal surfaces, as described hereinabove or, by using CMP to polish portions away from the upper horizontal surfaces. Optionally, if the topmost surface of the region protected by the resist mask 150 may be polished down to expose removable material; then, CMP may be used to form a vent by removing the top surface until underlying removable material is exposed.
An additional sidewall 182 extends upward from the top of wiring layer 104 and is present only if the resist pattern 150 is present before the conformal layer is deposited. In this case, sidewalls 174, 176 also extend upward from the top of wiring layer 104. Sidewalls 176, 174 provide additional lateral support for lines on wiring layer 104. Sidewalls 174 and 184 provide extra lateral support for lines on wiring layer 100. Sidewall 184 is defined by a metal line 124 on wiring layer 102 and is freestanding at layer 100. Sidewall 184, along wiring layer 102, as well as wiring layer 102 itself provide lateral support to wire 158. Lateral support to line 124 is provided by intersection with sidewalls from lines 152, 154, 156 and 158 in overlying layer 104.
When removing the fill dielectric, the fill dielectric under line 158 on wiring layer 104 is vented from wiring layer 100 between the freestanding sidewalls 186. Line 152 is vented from regions 190 and 192 in layer 100 and region 188 at the upper wiring layer 104. While in this example the dielectric under line 178 would not be vented, this can occur only if there is overlapping wiring of the same pitch and features.
In a variation on this alternate embodiment, as shown in
Preferably, an anisotropic etch is used to open the openings 196. The etch resistant layer 150′ may be a composite layer, such as an oxide, nitride, photoresist combination. The structure of
Thus, the methods of the present invention define supporting sidewall pedestals after the wiring is defined. The sidewall pedestals are etched by techniques that leave wiring substantially intact and are formed after the wiring is formed on or in a removable dielectric. If a directional etch is used to define the sidewall pedestals, then wiring acts as a mask to underlying removable material, and the sidewall pedestals are mainly to the side of the supported wires.
Further, the preferred removable dielectric is silicon dioxide, widely used in integrated circuit devices. Thus, the present invention does not require extensive process development that might otherwise be required when using completely new combinations of metal, dielectric, and sidewall. The present invention adds only an oxide RIE step, a sidewall deposition step, sidewall RIE open, and dielectric removal step to well known integrated circuit fabrication processes. With the possible addition of an optional step of including a single buried nitride layer to block vapor HF from attacking underlying silicon, these additional steps may all occur after the circuit itself is complete. Thus, the present invention is based on well known techniques of building wires in SiO2 that are not available in using completely new structures with dielectrics such as parylene that lack capability of deferred dielectric removal.
A conformal sidewall layer 199 may be formed before or after removing resist or etch resistant layer 202. Alternatively, the space left by fill material removal may be filled with etch resistant material. Vents may be opened in the sidewall layer (not shown) at the bottom of space 204 using a RIE to allow fill material removal. Alternatively, CMP or RIE may be used at the upper surface to open vents. Venting may be done using isotropic etching, anisotropic etching or combinations thereof. An isotropic etch is then used to remove any remaining fill material.
A more detailed description follows. After fill, or removable interlevel dielectric is removed to dotted line 204 of
Optionally, in any of the above embodiments, dummy wires may be selectively included with the circuit wiring to provide additional wiring support. Further, not all of the fill material may be removed. Some material may be left behind for added strength, while some is removed for wiring improved capacitance.
A wide range of shapes can be etched by a combination of shallow RIE or deep (see description of
Dielectric structures can be improved by a variation of the method described above. By way of example, consider the structure of
An alternative method is to form the hemisphere or to etch to completion (complete removal of the removable dielectric) with an etch which also attacks the sidewall, but at a reduced rate. The regions of sidewall exposed the longest will be removed or thinned the most.
Moreover, there is a whole class of prior art and yet to be conceived structures which combine wiring, air gaps or air dielectric, and dielectric supports. There will exist in each of these structures, as applied to actual circuitry, at least some regions where the dielectric supports can be removed (as described above), reduced in size, or reduced in number by etching without causing a detrimental effect upon overall support of the wiring structure. Such a reduction in dielectric support will result in a favorable reduction in the effective dielectric constant for the wiring of the circuit and corresponding increase in circuit performance and/or reduction in power dissipated within the circuitry. Intermixing some regions having increased support of wires amongst other regions having reduced support enables using increased support of wiring in a region where it is needed without increasing the effective dielectric constant in regions where support is not needed.
In the above-described embodiments, the region to be etched is defined by etching through a small vent to produce a hemispherical region if the etch resistant layer 202 is just opened by RIE; however, the etched region will be cylindrical if the RIE proceeds deep into the underlying dielectric, or of arbitrary shape if the unmasked RIE etched region of
In some respects an etch region which is a section of a hemisphere, as in
The support dielectric in the etched region can be etched by the same isotropic or anisotropic etch used to define the etched region, or by a separate isotropic etch. For instance, in the supported air dielectric wiring structures of
Alternatively, in the supported air dielectric wiring structures of
As shown in
The metal lines 312 shown in
A more complete description of the venting of the structure with permanent planar overlayers is now provided in
The layer 1150 is covered with a photoresist layer 1151 which is patterned to form an opening 1115. Reactive ion etching of the layer 1150 forms a vent opening 1114 which extends down between wires 1158 and 1152. Further RIE opens the next layer 1123 (such as silicon nitride or diamond like carbon, carbon doped dielectric when combined with a removable dielectric of silicon dioxide) which is chosen to be resistant to attack during the subsequent removal of the interlayer dielectric. The vent opening 1169 does not fully overly the metal line 1124 so RIE can continue to a lower depth of the structure, terminating at 1168 in
In a preferred embodiment, a gaseous HF process is used to remove a silicon dioxide removable interlevel dielectric after all vents are formed (Carbon containing layer/oxygen plasma or even organic polymer removed by decomposition thermally or by evaporation may be substituted for the oxide/vapor HF). Optionally, the interlevel dielectric is not fully removed so that if an array of vent holes is used, there are some regions in the array where remaining interlevel dielectric increases strength and rigidity of the resulting partial air dielectric structure.
In an alternative embodiment the vent is formed by an isotropic etch as shown in
Although layer 202 in
In another aspect of the invention, the air dielectric wiring is combined with micro-electromechanical (MEMS) devices. This aspect of the present invention benefits from a hybrid of two major embodiments already described. Sidewall support of the MEMS devices enables use of symmetrical vertical structures where there is less susceptibility to residual stresses than in prior art designs which are substrate supported. The hybrid design also enables easy, economical combination with copper wiring with an air dielectric. However, the resistance to stress in the sidewall supported MEMS is obtained whether or not the wiring elsewhere on the integrated circuit has an air dielectric. The detailed embodiment showing how MEMS can be combined with transistor circuit wiring is described below. The transistor circuits can be CMOS, bipolar, a combination or other transistors.
As mentioned previously, a wide range of materials can be used for the removable material or removable interlevel dielectric, besides silicon dioxide. For instance, organic or carbon containing layers like polymers or other carbon containing layers can be used as the removable layer when removed by oxygen plasmas or remote oxygen plasmas, or even organics which thermally decompose or evaporate can be used. The permanent layers or permanent dielectric structures can be composed of materials other than silicon nitride including carbon doped dielectrics or diamond-like carbon if vapor HF etching is used to remove the removable interlevel dielectric. The permanent layer is resistant to the etch used to remove the removable interlevel dielectric, or other removable material but not necessarily completely impervious toward etching. For instance, certain vapor HF etches slowly attack plasma deposited silicon nitride. It is also interesting to note that although a removeable interlevel dielectric is specified in the embodiments, a dielectric is only preferrable. The embodiments which completely remove the removable layer could in fact use a removable conductor or semiconductor. The wiring would remain shorted until the removable material is completely removed.
Transistor gates 531, and 532, were previously formed and underly the circuit wiring and are part of the circuit. Transistor gates 533 and 534 underly the MEMS region. MOS transistors are shown but they could be bipolar or other transistors. The wire 535, preferably copper, is shown interconnecting transistors 531 and 532 as part of a circuit, and wire 536 interconnects transistor 533 and 534 as part of a circuit. The layer 537 is a layer resistant to the etch used to remove interlevel dielectric 500. The layer 537 is horizontal and planar as is layer 520 (except where they contact the surface of wire 535, 536, 510, 515 or others not shown where the contacting surface of the wire may be concave, convex, or raised relative to the neighboring removable dielectric). Substrate 538 is the silicon in which the transistors are formed. These transistors are understood to be present in
After the resist 530 is stripped then a multilayer structure is deposited in the MEMS region of
After trench formation, the deep trenches 670 and 680 are filled with a resistant material, which is resistant to the etch used to remove the removable dielectric. A layer 690 of the resistant material is simultaneously formed on the wires or contacts 700 (
To this end, consider the previously described embodiment; if layer 500 is made of a permanent material instead of a removable material, then electrode 540 is fixed by 500 instead of being moveable. There is only one moveable electrode 560 with sidewall support down to the underlying fixed substrate support. A MEMS device with a single moveable electrode which is supported by a sidewall support likewise has simplified construction and reduced interference, reduced energy dissipation, and reduced electrode bowing with a sidewall support, especially if the sidewall is made very thin. If the sidewall is compliant, some stress can be relieved by motion of the sidewall support instead of by electrode bowing.
The MEMS device of
In the embodiment just described, a number of processes can be carried out simultaneously in the MEMS and the transistor circuit regions. For instance, the wiring, 700, in the circuit region and the wiring used to make electrical contact to the MEMS device, 700, are formed simultaneously, the supports in the MEM region, 670 and 690, and for the wiring in the transistor region, 680 and 690, are formed simultaneously. The dielectric, 500 and 610, in the transistor region and in the MEMS region are simultaneously removed.
Thus, as seen in
It is important to note that since both electrodes of the MEMS device are freestanding, and since both electrodes have experienced similar process treatments, the stresses within each electrode is similar. Also, since both electrodes are supported in a similar fashion, the movements and deformations of the final structure which enable relief of those “stresses of construction” are similar. This enables a narrower gap between the electrodes. This is in contrast to a device with one electrode fixed on a substrate and one movable electrode. In this case stresses of construction will be released by motion of only one electrode, and resulting bowing or motion will alter the gap between the electrodes and perhaps even cause shorting of electrodes. Also, both electrodes of the present invention are able to move in response to an applied voltage, therefore switches or capacitors or resonators constructed with two movable electrodes will have a greater response to a given applied voltage than with one electrode fixed and only one moveable.
The resulting structure of the present invention is also resistant to undesireable relative motion of the two MEMS electrodes caused by sudden acceleration of the device (such as caused by dropping). Since both electrode plates are movable and are of similar construction, most motion will be experienced by both plates, leading to little relative motion. This again is in contrast to prior art construction where one plate is fixed by a substrate. Neither MEMS electrode nor sidewall supports must make contact with the underlying substrate enabling transistors to underly the MEMS device and unrelated wiring to coexist in the same region. The MEMS electrodes are suspended above the silicon substrate.
In view of the above description, those of ordinary skill in the art should now recognize, in addition to the above, the following advantages of the present invention:
As described herein, the embodiments include wiring structures from which SiO2 has been removed using gaseous HF. Prior art wiring structures may be improved using an SiO2 fill which is subsequently removed using gaseous HF. For example support type wiring structures may be formed much more simply by forming the HF resistant supports in SiO2 and then removing the SiO2 using gaseous HF.
While the invention has been described in terms of preferred embodiments, those skilled in the art will recognize that the invention can be practiced