US20050157471A1 - Integrated heat spreader package for heat transfer and for bond line thickness control and process of making - Google Patents
Integrated heat spreader package for heat transfer and for bond line thickness control and process of making Download PDFInfo
- Publication number
- US20050157471A1 US20050157471A1 US11/080,028 US8002805A US2005157471A1 US 20050157471 A1 US20050157471 A1 US 20050157471A1 US 8002805 A US8002805 A US 8002805A US 2005157471 A1 US2005157471 A1 US 2005157471A1
- Authority
- US
- United States
- Prior art keywords
- heat transfer
- transfer material
- die
- solder
- heat
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
A system includes a thermal interface material (TIM) to transfer heat from a die to a heat spreader. The system includes a heat transfer subsystem disposed on the backside surface of the die. In one embodiment, the heat transfer subsystem comprises a first heat transfer material and a second heat transfer material discretely disposed within the first heat transfer material. A method of bonding a die to a heat spreader uses a die-referenced process as opposed to a substrate-referenced process.
Description
- This application is a divisional of U.S. patent application Ser. No. 10/266996, filed on Oct. 8, 2002, which is incorporated herein by reference.
- 1. Technical Field
- Embodiments of the present invention relate to an integrated heat spreader as it is bonded to a die. The bond includes a high-temperature bump or other structure that is discretely intermingled with a lower-temperature material.
- 2. Description of Related Art
- One of the issues encountered when using an integrated heat spreader (IHS) is getting a balance between sufficient adhesion to the die, and a high enough heat flow to meet the cooling load of the die. To deal with this issue, different bonding materials have been tried with varying results. If the adhesion is insufficient, the IHS may spall off from the thermal interface material (TIM) and result in a yield issue or a field failure. Another issue encountered is achieving an acceptable IHS standoff from the die and the board to which the board is mounted. Because of various existing processes, a substrate-referenced process is used that may cause a significant variation in bond-line thickness (BLT) between the top of the die and the bonding surface of the IHS.
- TIM BLT is maintained for mechanical reliability of the thermal interface during thermal cycling. Due to the difference in the coefficients of thermal expansion of the IHS and the die, there is a large amount of shear stress imposed on the TIM. Thicker bond lines assist the TIM to withstand these high stresses without failing.
- TIM BLT is also an element in the thermal resistance of the thermal interface. A thinner TIM BLT can result in a lower thermal resistance. Due to these limits in TIM BLT, which can be required for acceptable package performance, TIM BLT must be tightly controlled.
- In order to understand the manner in which embodiments of the present invention are obtained, a more particular description of various embodiments of the invention briefly described above will be rendered by reference to the appended drawings. Understanding that these drawings depict only typical embodiments of the invention that are not necessarily drawn to scale and are not therefore to be considered to be limiting of its scope, the embodiments of the invention will be described and explained with additional specificity and detail through the use of the accompanying drawings in which:
-
FIG. 1 is an elevational cross-section of a package according to an embodiment; -
FIG. 2 is a partial cut-away cross-sectional view of the packaging system depicted inFIG. 1 taken along the section line 2-2; -
FIG. 3 is a cut-away cross-sectional view of a portion of the packaging system depicted inFIG. 1 taken along the section line 3-3; -
FIG. 4 is a cutaway cross-sectional view of a portion of an elongate, rectangular package according to an embodiment; -
FIG. 5 is a cross-sectional view of an interface subsystem according to an embodiment; -
FIG. 6 is a cross-sectional view of an interface subsystem according to an embodiment; -
FIG. 7 is a cross-sectional view of an interface subsystem according to an embodiment; and -
FIG. 8 is a process flow diagram that depicts non-limiting packaging process embodiments. - One embodiment of the present invention relates to a system that includes a thermal interface material (TIM) intermediary between a heat spreader and a die for heat transfer out of the die. One embodiment includes a method of bonding a die to a heat spreader that uses a die-referenced process as opposed to a substrate-referenced process.
- The following description includes terms, such as upper, lower, first, second, etc. that are used for descriptive purposes only and are not to be construed as limiting. The embodiments of a device or article described herein can be manufactured, used, or shipped in a number of positions and orientations. The terms “die” and “processor” generally refer to the physical object that is the basic workpiece that is transformed by various process operations into the desired integrated circuit device. A board is typically a resin-impregnated fiberglass structure that acts as a mounting substrate for the die. A die is usually singulated from a wafer, and wafers may be made of semiconducting, non-semiconducting, or combinations of semiconducting and non-semiconducting materials.
- Reference will now be made to the drawings wherein like structures will be provided with like reference designations. In order to show the structures of embodiments most clearly, the drawings included herein are diagrammatic representations of inventive articles. Thus, the actual appearance of the fabricated structures, for example in a photomicrograph, may appear different while still incorporating the essential structures of embodiments. Moreover, the drawings show only the structures necessary to understand the embodiments. Additional structures known in the art have not been included to maintain the clarity of the drawings.
-
FIG. 1 is an elevational cross-section of apackaging system 10 according to an embodiment. Thepackaging system 10 includes adie 12 with anactive surface 14 and abackside surface 16. The die 12 is connected to a thermal management device. In one embodiment, the thermal management device is integratedheat spreader 18 that is disposed above thebackside surface 16 of the die 12. Aninterface subsystem 20, in the form of a TIM, is disposed between abackside surface 16 and the integratedheat spreader 18. Theinterface subsystem 20 includes a firstheat transfer material 22 and a secondheat transfer material 24 that is discretely disposed within the firstheat transfer material 22. In one embodiment, the secondheat transfer material 24 has a higher thermal conductivity that the firstheat transfer material 22. - In one embodiment where the two heat transfer materials are metals, the second
heat transfer material 24 has a higher melting point than the firstheat transfer material 22. In one embodiment where the first heat transfer material is an organic, the secondheat transfer material 24 has a melting point that is higher than the curing temperature of the firstheat transfer material 22. - In another embodiment, the first
heat transfer material 22 in an organic-inorganic composite. The organic-inorganic composite in one embodiment includes a polymer, optionally an inorganic dielectric, and optionally at least one metallic. The inorganic dielectric may be a material as is used as filler in thermal interface structures. One embodiment of an inorganic dielectric is fused silica and the like. Where a metallic material is used as a portion of an organic-inorganic composite, the metallic material in one embodiment is a low melting-point solder or the like. - As depicted in
FIG. 1 , theinterface subsystem 20 is depicted as having a low melting-point solder firstheat transfer material 22 having a first melting point and a high melting-point solder secondheat transfer material 24 that is discretely disposed within the firstheat transfer material 22 and having a second melting point that is higher than that of the first melting point. In one embodiment, thepackaging system 10 includes a secondheat transfer material 24 that is at least one solder island that is discretely disposed within the firstheat transfer material 22. - In one embodiment, a reactive solder system is used. A reactive solder material includes properties that allow for adhesive and/or heat-transfer qualities. For example, the reactive solder material can melt and resolidify without a pre-flux cleaning that was previously required. Further, a reactive solder embodiment can also include bonding without a metal surface. Without the need of a metal surface for bonding, processing can be simplified.
- In one embodiment, a reactive solder includes a base solder that is alloyed with an active element material. In one embodiment, a base solder is indium. In one embodiment, a base solder is tin. In one embodiment, a base solder is silver. In one embodiment, a base solder is tin-silver. In one embodiment, a base solder is at least one lower-melting-point metal with any of the above base solders. In one embodiment, a base solder is a combination of at least two of the above base solders. Additionally, conventional lower-melting-point metals/alloys can be used.
- The active element material is alloyed with the base solder. In one embodiment, the active element material is provided in a range from about 2% to about 30% of the total solder. In one embodiment, the active element material is provided in a range from about 2% to about 10%. In one embodiment, the active element material is provided in a range from about 0.1% to about 2%.
- Various elements can be used as the active element material. In one embodiment, the active element material is selected from hafnium, cerium, lutetium, other rare earth elements, and combinations thereof. In one embodiment, the active element material is a refractory metal selected from titanium, tantalum, niobium, and combinations thereof. In one embodiment, the active element material is a transition metal selected from nickel, cobalt, palladium, and combinations thereof. In one embodiment, the active element material is selected from copper, iron, and combinations thereof. In one embodiment, the active element material is selected from magnesium, strontium, cadmium, and combinations thereof.
- The active element material when alloyed with the base solder can cause the alloy to become reactive with a semiconductive material such as the
backside surface 16 of thedie 12. The alloy can also become reactive with an oxide layer of a semiconductive material such as silicon oxide, gallium arsenide oxide, and the like. The alloy can also become reactive with a nitride layer of a semiconductive material such as silicon nitride, silicon oxynitride, gallium arsenide nitride, gallium arsenide oxynitride, and the like. - Reaction of the alloy with the die 12 can be carried out by thermal processing. Heat can be applied by conventional processes, such that the active element materials reach the melting zone of the base solder. For example, where the base solder includes indium, heating is carried out in a range from about 150° C. to about 200° C.
- During reflow of the alloy, the active element(s) dissolve and migrate to the
backside surface 16 of thedie 12. Simultaneously, the base solder bonds to theintegrated heat spreader 18. It is not necessary that thebackside surface 16 be metalized prior to soldering. The solder joint (not depicted) that is formed by the reactive solder material can display a bond strength in a range from about 1,000 psi and about 2,000 psi. -
FIG. 2 is a partial cut-away cross-sectional view of thepackaging system 10 taken along the section line 2-2′. It is noted that inFIG. 1 , theintegrated heat spreader 18 is attached to a mountingsubstrate 26 such as a printed circuit board (PCB), such as a main board, a motherboard, a mezzanine board, an expansion card, or another mounting substrate, with abonding material 28 that secures alip portion 30 of theintegrated heat spreader 18 thereto. In one embodiment, the thermal management device is a heat sink without a lip structure such as a simple planar heat sink. In one embodiment the thermal management device includes a heat pipe configuration. It is noted inFIG. 1 that thedie 12 is disposed between theinterface subsystem 20 and a series ofelectrical bumps 32 that are in turn each mounted on a series ofbond pads 34. Theelectrical bumps 32 make contact with theactive surface 14 of thedie 12. Contrariwise, theinterface subsystem 20 makes thermal contact with thebackside surface 16 of thedie 12. - As taken along the section line 2-2′,
FIG. 2 illustrates a cross-section of thebonding material 28 that fastens a lip portion 30 (FIG. 1 ) of the integrated heat spreader 18 (FIG. 1 ) to the mounting substrate 26 (FIG. 1 ). Additionally, theelectrical bumps 32 are depicted in a ball grid array as is known in the art. -
FIG. 3 is a cut-away cross-sectional view of a portion of thepackaging system 10 depicted inFIG. 1 taken along the section line 3-3′. It can be seen inFIG. 3 , that thelip portion 30 of theintegrated heat spreader 18 is exposed in this view. Additionally,FIG. 3 depicts a cross-section of theinterface subsystem 20, which includes a pattern of solder islands that are the secondheat transfer material 24 and that are discretely disposed within the firstheat transfer material 22. Although the pattern of solder islands in the secondheat transfer material 24 is depicted as a five-element grouping, patterning according to various embodiments includes a single solder island, two solder islands, three solder islands that are either linearly arranged or otherwise, and multiple solder islands that are arrayed according to the needs of a given application of an embodiment. - According to an embodiment, the heat transfer materials include solder. The solder may contain lead (Pb) or be a substantially Pb-free solder. By “substantially Pb-free solder”, it is meant that the solder is not designed with Pb content according to industry trends. A substantially Pb-free solder in one embodiment includes an SnAgCu solder as is known in the art.
- One example of a Pb-containing solder includes a tin-lead solder. In selected embodiments, Pb-containing solder is a tin-lead solder composition such as from 97% tin (Sn)/3% lead (Sn3Pb). A tin-lead solder composition that may be used as the first
heat transfer material 22 or as the secondheat transfer material 24 is a Sn63Pb composition of 37% tin/63% lead. In any event, the Pb-containing solder may be a tin-lead solder comprising SnxPby, wherein x+y total 1, and wherein x is in a range from about 0.3 to about 0.99. In one embodiment, the Pb-containing solder is a tin-lead solder composition of Sn3Pb for the firstheat transfer material 22, and for the secondheat transfer material 24, it is a tin-lead solder composition of Sn63Pb. - The following discussion refers specifically to structures depicted in
FIGS. 1-3 , but it applies generally to embodiments set forth herein. In one embodiment, the firstheat transfer material 22 includes a Pb-containing solder, and the secondheat transfer material 24 contains a Pb-containing solder that has a higher melting point than the firstheat transfer material 22. In another embodiment, the firstheat transfer material 22 includes a Pb-containing solder, and the secondheat transfer material 24 contains a substantially Pb-free solder that has a higher melting point than the firstheat transfer material 22. In another embodiment, the firstheat transfer material 22 includes a substantially Pb-free solder, and the secondheat transfer material 24 also contains a substantially Pb-free solder that has a higher melting point than the firstheat transfer material 22. In another embodiment, the firstheat transfer material 22 includes a substantially Pb-free solder, and the secondheat transfer material 24 includes a Pb-containing solder that has a higher melting point than the firstheat transfer material 22. - In one embodiment, the solder islands are arranged in an elongate, rectangular configuration that may follow the outline of a rectangular die, as will now be discussed with reference to
FIG. 4 . -
FIG. 4 is a cut-away cross-sectional view of a portion of an elongate, rectangular package according to an embodiment.FIG. 4 depicts the packaging system 110 that would be taken along a section line similar to the section line 3-3′ fromFIG. 1 and is analogous in its view to the view taken inFIG. 3 . In this embodiment, an elongate, rectangulardie heat spreader 118 has a symmetry to match an elongate, rectangular die (not pictured). The elongate, rectangular die is bonded to a likewise elongate,rectangular interface subsystem 120. It is noted that a collection of solder islands, such as depicted inFIG. 3 , includessolder islands heat transfer material 24. The varying sizes and orientations of larger and smaller discrete occurrences of the secondheat transfer material 24 are depicted inFIG. 3 in arbitrary number, shape, size, and location. As is noted, there are larger solder islands that are selected to be disposed adjacent to a die at the more active regions thereof. By way of non-limiting example, a givensolder island 124B that is larger is disposed directly above a more active region of the die 112 (not pictured) such as an array of embedded dynamic random access memory (DRAM), the sense amplifiers thereof, and the like. A more active region of a die is understood to be, in one embodiment, a region that generates a greater amount of heat than the average per area heat generation. By placing a larger solder island above the die at a more active region, a larger solder island acts as a heat transfer conduit that has a higher overall heat transfer coefficient than the heat transfer capability of a smaller solder island, or, for that matter, the firstheat transfer material 122 alone. This larger heat transfer capability represents a lowered resistance to heat flow between the heat-generating die and the heat-sinkingheat spreader 118. In one embodiment, theheat spreader 118 includes alip portion 130 similar to the embodiment depicted inFIGS. 1 and 3 . -
FIG. 5 is a cross-sectional view of aninterface subsystem 220 according to an embodiment. Theinterface subsystem 220 ofFIG. 5 is similar to theinterface subsystem 20 that is depicted inFIG. 1 . According to various embodiments, theinterface subsystem 220 is a combination of a low melting-point solder firstheat transfer material 222 and a higher melting-point solder secondheat transfer material 224. As set forth herein, the two heat transfer materials are selected from a combination of a Pb-containing solder and a substantially Pb-free solder. In another embodiment, theinterface subsystem 220 includes an organic firstheat transfer material 222 and a metallic secondheat transfer material 224. As set forth herein, the firstheat transfer material 222 has a first cure temperature that is lower than the melting point of the secondheat transfer material 224. Similar to other embodiments as set forth herein, the placement of secondheat transfer material 224 as discrete occurrences thereof may be located above a more active region of a die in order to expedite heat transfer away from the die. -
FIG. 6 is a cross-sectional view of aninterface system 320 according to an embodiment.Interface subsystem 320 includes an organic/inorganic composite. In one embodiment, the organic/inorganic composite includes anorganic matrix 322 and ametal flake 323 along with a secondheat transfer material 324. Although themetal flake 323 is depicted in this embodiment as a flake, the metal may be in other shapes. In one embodiment, themetal flake 323 is a substantially spherical powder that has an average diameter in a range from about 0.1 micron to about 10 micron. The secondheat transfer material 324, which is in one embodiment a high melting-point solder, is either a Pb-containing solder or a substantially Pb-free solder as set forth herein. -
FIG. 7 is a cross-sectional view of aninterface subsystem 420 according to an embodiment. Theinterface subsystem 420 includes a metal/nonmetal composite in anorganic matrix 422. In one embodiment, theorganic matrix 422 includes an organic material that acts as a matrix for an inorganicdielectric material 421 and ametallic material 423. In this embodiment, themetallic material 423 is depicted as having reflowed under a thermal load and has at least partially wetted the inorganicdielectric material 421. The combination of the inorganicdielectric material 421 and themetallic material 423 presents a conglomerate channel from one surface of theinterface subsystem 420 to an opposite surface thereof. As such, heat transfer through theorganic matrix material 422 is expedited. Similarly, a high melting-point solder is depicted in an embodiment as the secondheat transfer material 424. - Another embodiment relates to a die system. An embodiment of the die system is depicted in some of the structures illustrated in
FIG. 1 by way of non-limiting example. With reference toFIG. 1 , in one embodiment, the die system includes thedie 12 and theinterface subsystem 20 as set forth herein according to the various embodiments. Further, the die system in one embodiment includes theinterface subsystem 20 that is the firstheat transfer material 22 alone. In another embodiment, the die system includes theinterface subsystem 20 with the firstheat transfer material 22 and the secondheat transfer material 24 disposed in the firstheat transfer material 22. In another embodiment, the die system includes the secondheat transfer material 24 alone that has a discrete patterning upon thedie backside surface 16. The discrete patterning of the secondheat transfer material 24 alone, upon thedie backside surface 16, is a subset embodiment of thepackaging system 10, as depicted inFIG. 1 , wherein the discrete patterning upon the die 12 may be produced by a distinct business entity. For example, the heat spreader may be produced by a first company or division within a company, and the die with discrete patterning may be produced by a second company or division. - The die system in another embodiment includes the mounting
substrate 26 disposed below thedie 12. In other words, thedie 12, theelectrical bumps 32, and theirbond pads 34 as mounted upon the mountingsubstrate 26, represent a package precursor according to this embodiment. In another embodiment, the die system includes the mountingsubstrate 26 and other structures as set forth herein and theintegrated heat spreader 18 disposed above thedie 12. As depicted inFIG. 1 , theinterface subsystem 20 is disposed between to the die 12 and theintegrated heat spreader 18. - Another embodiment relates to a thermal interface alone as depicted in
FIG. 1 (interface subsystem 20),FIG. 5 (interface subsystem 220),FIG. 6 (interface subsystem 320), andFIG. 7 (interface subsystem 420). According to an embodiment, the high melting-point solder second heat transfer material 24 (FIG. 1 , for example) has at least one solder island that has a characteristic thickness that is in a range from about 0.1 micron to about 25 micron. The characteristic thickness is selected to achieve a preferred bond line thickness (BLT) as is understood in the art. Referring toFIG. 1 , theBLT 36 in this embodiment closely tracks the solder island characteristic thickness, and it is larger than the solder island characteristic thickness. In other words, theBLT 36 has substantially the same thickness as theinterface subsystem 20. In one embodiment, theBLT 36 is in a range from about 1 mil to about 25 mils. In one embodiment, theBLT 36 is in a range from about 2 mils to about 10 mils. In another embodiment, theBLT 36 is in a range from about 10 mils to about 20 mils. In one embodiment, theBLT 36 of a polymer matrix-containing material is less than theBLT 36 of a metal matrix-containing material. - In another embodiment, the high melting-point solder second heat transfer material 24 (
FIG. 1 , for example) is present in relation to the firstheat transfer material 22 in a volume range from about 0.1% to about 5%. In another embodiment, the high melting-point solder secondheat transfer material 24 is present in relation to the firstheat transfer material 22 in a volume range from about 0% to about 0.1 %. In another embodiment, the high melting-point solder secondheat transfer material 24 is present in relation to the firstheat transfer material 22 in a volume range from about 0% to about 100%. In another embodiment, the high melting-point solder secondheat transfer material 24 is present in relation to the firstheat transfer material 22 in a volume range from about 2% to about 10%. - Another embodiment relates to
packaging process embodiments 800 that includes bringing an integrated heat spreader and a die into TIM intermediary contact through an interface subsystem to achieve a BLT according to embodiments set forth herein. -
FIG. 8 is a process flow diagram that depicts non-limiting packaging process embodiments. According to the various process flow embodiments depicted inFIG. 8 , the interface subsystem may be configured partially on the integrated heat spreader, partially on the die, entirely on the integrated heat spreader, or entirely on the die. - At 810, representing a first process flow embodiment, an integrated heat spreader (IHS) is contacted with a first heat transfer material, and the first heat transfer material is contacted with a die. The double-headed arrows in
FIG. 8 indicate that the process flow may be in either direction. In other words, the first heat transfer material in one embodiment is disposed first against the integrated heat spreader, followed by disposition of the first heat transfer material against the die. Alternatively, the first heat transfer material in one embodiment is disposed first against the die, followed by disposition of the first heat transfer material against the integrated heat spreader. - At 820, representing a second process flow embodiment, an integrated heat spreader is contacted with a first heat transfer material. The first heat transfer material is contacted with a second heat transfer material that is disposed on a die. The double-headed arrows indicate alternative process flows as set forth above.
- At 830, representing a third process flow embodiment, an integrated heat spreader is contacted with a second heat transfer material. The second heat transfer material is contacted with a first heat transfer material that is disposed on a die. The double-headed arrows indicate alternative process flows as set forth above.
- At 840, representing a fourth process flow embodiment, an integrated heat spreader is contacted with combined first and second heat transfer materials. The combined first and second heat transfer materials are contacted with a die. The double-headed arrows indicate alternative process flows as set forth above. In another embodiment, the order of placing the first and second heat transfer materials onto the IHS is reversed.
- At 850, representing a fifth process flow embodiment, a die is contacted with combined first and second heat transfer materials. The combined first and second heat transfer materials are contacted with a die. The double-headed arrows indicate alternative process flows as set forth above. In another embodiment, the order of placing the first and second heat transfer materials onto the die is reversed.
- As depicted in the various process flow embodiments depicted in
FIG. 8 , it is noted that the die 12 (FIG. 1 ) is previously disposed upon a mounting substrate 26 (alsoFIG. 1 ). Further as depicted inFIG. 1 , it is noted that an integratedheat spreader clip 38 is used to impart a pressure to the die-interface-heat spreader at least partially through aspring 40. Depending upon the combination ofinterface subsystem 20 and other factors such as adhesive gelling time, organic curing time, low melting-point reflow time, and others, the exact tension of thespring 40 is selected to the requirements of a given packaging system. - According to an embodiment, the bonding process of bringing an integrated heat spreader and a die into intermediary contact through an
interface subsystem die 12 is already affixed upon the mountingsubstrate 26. And as in some embodiments, a secondheat transfer material 24 is disposed between theintegrated heat spreader 18 and thebackside surface 16 of the die 12 while tensing the system with thespring 40. Accordingly, the variability in bonding thickness may often largely be in thebonding material 28 as it bridges the space between thelip 30 of theintegrated heat spreader 18 and the mountingsubstrate 26. - In a general embodiment, after bringing the integrated heat spreader into intermediary contact with the die through the interface subsystem according to various embodiments, bonding the interface subsystem includes reflowing the low melting-point solder first heat transfer material, and/or curing an organic first heat transfer material. Additionally, where a second heat transfer material is disposed in a first heat transfer material, the solder reflowing process is carried out after bringing the structures together. Where the first heat transfer material is an organic material, a curing and/or hardening process is carried out after bringing the structures together. Where the first heat transfer material is an organic/inorganic composite, curing, hardening, and/or reflowing is carried out after bringing the structures together.
- It is emphasized that the Abstract is provided to comply with 37 C.F.R. § 1.72(b) requiring an Abstract that will allow the reader to quickly ascertain the nature and gist of the technical disclosure. It is submitted with the understanding that it will not be used to interpret or limit the scope or meaning of the claims.
- In the foregoing Detailed Description, various features are grouped together in a single embodiment for the purpose of streamlining the disclosure. This method of disclosure is not to be interpreted as reflecting an intention that the claimed embodiments of the invention require more features than are expressly recited in each claim. Rather, as the following claims reflect, inventive subject matter lies in less than all features of a single disclosed embodiment. Thus the following claims are hereby incorporated into the Detailed Description of Embodiments of the Invention, with each claim standing on its own as a separate preferred embodiment.
- It will be readily understood to those skilled in the art that various other changes in the details, material, and arrangements of the parts and method stages which have been described and illustrated in order to explain the nature of this invention may be made without departing from the principles and scope of the invention as expressed in the subjoined claims.
Claims (18)
1-9. (canceled)
10. An integrated heat spreader system comprising:
a heat spreader body having a recess;
an interface subsystem in the recess, wherein the interface subsystem is selected from (1) a first heat transfer material, (2) the first heat transfer material and a second heat transfer material discretely disposed within the first heat transfer material, and (3) the second heat transfer material alone having a discrete patterning within the recess.
11-13. (canceled)
14. The integrated heat spreader system according to claim 10 , wherein the first heat transfer material includes an organic-inorganic composite.
15. The integrated heat spreader system according to claim 10 , wherein the first heat transfer material further includes:
an organic-inorganic composite including a polymer or a resin;
optionally an inorganic dielectric; and
optionally at least one metallic.
16-18. (canceled)
19. A thermal interface comprising:
a first heat transfer material, selected from a low melting point solder, a polymer, a polymer and a low melting point solder, a polymer and an inorganic dielectric, and a polymer and a low melting-point solder and an inorganic dielectric; and
a high melting-point solder second heat transfer material, discretely disposed within the first heat transfer material, wherein the high melting-point solder second heat transfer material has a higher thermal conductivity than the first heat transfer material.
20. The thermal interface according to claim 19 , wherein the high melting point solder second heat transfer material includes at least one solder island that has a characteristic thickness in a range from about 0.1 micron to about 25 micron.
21. (canceled)
22. The thermal interface according to claim 19 , further including:
an integrated heat spreader, wherein the thermal interface is on the integrated heat spreader.
23. (canceled)
24. The thermal interface according to claim 19 , wherein the first heat transfer material is a low melting point solder, and the high melting-point solder second heat transfer material is present in a volume range from about 0% to about 5%.
25. A packaging process comprising:
coupling a thermal management device to a die through an interface subsystem,
wherein the thermal management device is selected from
an integrated heat spreader,
a heat pipe, and
a planar heat sink, and
wherein the interface subsystem is selected from
a first heat transfer material, and
the first heat transfer material and a second heat transfer material discretely disposed within the first heat transfer material, wherein the first heat transfer material has either a first melting temperature or a first curing temperature, and the second heat transfer material has a second melting temperature higher than the first temperature; and
bonding the interface subsystem to the thermal management device and the die.
26. The process according to claim 25 , wherein the first heat transfer material is selected from a low melting-point solder, an organic composition, and a combination thereof, and wherein bonding the interface subsystem includes reflowing the low melting-point solder or curing and hardening the organic composition.
27. The process according to claim 25 , wherein the first heat transfer material includes a low melting-point solder, wherein the second heat transfer material includes a high melting-point solder, and wherein bonding the interface subsystem includes reflowing the low melting-point solder.
28. The process according to claim 25 , wherein coupling the thermal management device to the die through an interface subsystem further includes:
disposing the first heat transfer material against the thermal management device;
disposing the second heat transfer material against the die; and
coupling the first heat transfer material and the second heat transfer material.
29. The process according to claim 25 , wherein coupling the thermal management device to the die through an interface subsystem further includes:
disposing the first heat transfer material and the second heat transfer material against the thermal management device; and
coupling the first heat transfer material and the second heat transfer material with the die.
30. The process according to claim 25 , wherein coupling the thermal management device to the die through an interface subsystem further includes:
disposing the first heat transfer material and the second heat transfer material against the die; and
coupling the first heat transfer material and the second heat transfer material with the thermal management device.