The invention is intended for providing a semiconductor package structure which prevents degradation in characteristics of a semiconductor device, and breakage of interconnections, when the semiconductor device is packaged on a circuit substrate. In the package structure having the semiconductor device mounted on the circuit substrate, bump electrodes of the semiconductor device are placed on input/output terminal electrodes of the circuit substrate and are electrically and mechanically connected thereto by bonding with a conductive adhesive, and the semiconductor device is bonded and fixed to the circuit substrate by a resin film formed previously on a surface of a main body of the circuit substrate. The structure does no damage to a semiconductor functional part and to interconnections, and allows mounting with a lower load as compared to structures using conventional anisotropic conductive films and the like.
15. A method of producing a circuit substrate onto which a semiconductor device is to be mounted, comprising:
printing conductive adhesive onto input/output terminal electrodes on a surface of a main body, thereby forming conductive adhesive portions; and
after curing said conductive adhesive portions, coating said surface of said main body with a resin film so as to cover said conductive adhesive portions and said input/output terminal electrodes.
16. A method of producing a circuit substrate for packaging a semiconductor device, comprising:
forming conductive adhesive portions on a resin film;
covering with said resin film a surface of a main body having input/output terminal electrodes thereon, such that said conductive adhesive portions face said input/output terminal electrodes; and
bonding said resin film to said main body.
17. The method according to
forming conductive adhesive portions on a resin film comprises printing conductive adhesive paste onto said resin film in a pattern.
18. The method according to
forming conductive adhesive portions on a resin film comprises
(i) bonding a masking sheet to said resin film,
(ii) boring holes that extend through said masking sheet,
(iii) filling said holes with conductive adhesive, and then
(iv) removing said masking sheet from said resin film.
19. The method according to
such that bonding said masking sheet to said resin film comprises bonding said resin sheet to said resin film.
20. The method according to
boring holes that extend through said masking sheet comprises using a laser to form perforations through said masking sheet.
21. The method according to
boring holes that extend through said masking sheet comprises using ultraviolet radiation to form perforations through said masking sheet.
22. A method of producing a package structure, comprising:
applying conductive adhesive onto input/output terminal electrodes on a surface of a substrate, thereby forming conductive adhesive portions; and
covering said surface of said substrate body with a resin material such that said conductive adhesive portions are covered by said resin material;
pressing bump electrodes of a semiconductor device into said resin material, while said resin material is in a molten state due to being heated, such that said bump electrodes penetrate through and become fixed to said conductive adhesive portions, whereby said bump electrodes become electrically connected to corresponding ones of said input/output terminal electrodes; and then
curing said resin material so as to join said semiconductor device to said substrate.
23. The method according to
24. The method according to
25. The method according to
26. The method according to
such that pressing said bump electrodes into said resin material results in said elastomer layer being interposed between said resin material and said semiconductor device.
27. The method according to
28. A method of producing a package structure, comprising:
positioning a resin film, having conductive adhesive portions on one surface thereof and an elastomer layer on another surface thereof that is to correspond to a semiconductor device, on a substrate having input/output terminal electrodes on a surface thereof, such that said conductive adhesive portions correspond to said input/output terminal electrodes, respectively;
pressing bump electrodes of a semiconductor device into said resin film, while said resin film is in a molten state, such that said bump electrodes reach said conductive adhesive portions and become connected to corresponding ones of said input/output terminal electrodes; and
curing said resin film so as to join said semiconductor device to said substrate.
This application is a divisional of U.S. Ser. No. 10/030,739, filed Jan. 11, 2002, which is a National Stage of International Application No. PCT/JP01/03922, filed May 11, 2001.
The present invention relates to a circuit substrate to have mounted thereon a semiconductor device and a method of producing the same. The invention also relates to a method of mounting a semiconductor device, with use of such a circuit substrate.
As one of techniques for mounting semiconductor devices on a circuit substrate, a flip chip mounting method has been known. In this method, bump electrodes are formed on a surface of a semiconductor chip on the same side that a functional element thereof is formed, and the bump electrodes are connected through an adhesive layer to input/output terminal electrodes arranged on a circuit substrate. In this method, the bump electrodes are formed of gold (Au), nickel (Ni) or the like by plating, and for an adhesive layer solder, conductive organic adhesive or the like is used. As the conductive organic adhesive, an anisotropic conductive film or paste, or the like is used besides an isotropic adhesive.
Although solder paste and isotropic conductive adhesive require little load for connection in packaging, an anisotropic conductive film and an anisotropic conductive paste are required to be loaded to at least 200 g per pin during packaging processes in order to secure stability of conductivity and reliability.
Japanese Patent Publication 8-037206 discloses a method of semiconductor device packaging in which, as shown in
Japanese Patent Publication 10-199932 discloses a method for packaging a semiconductor device in which electrically conductive and plastically deformable bumps are formed on a large number of pad electrodes on a semiconductor chip, are leveled in a height direction, and are pressed against and bonded to corresponding pads on a circuit substrate. To bond, adhesive is applied to flat head planes of the leveled bumps which are joined to the corresponding pads.
In recent years, semiconductor devices have increasingly been required to be very compact, and to be capable of performance for use in portable electronic equipment. In order to fulfill these requirements, it is important that semiconductor devices to be mounted on, and interconnected with, circuit substrates should be provided with an increased number of pins for input/output terminals with a much smaller pitch between adjacent terminals, and that an area array of electrodes can be achieved in a zone where the electrodes can be arranged. This requires further development of techniques for achieving narrower-pitch connection.
An area array arrangement of electrodes has been established by conventional solder bump methods. A solder bump technique has advantages in that stresses acting on active elements on an integrated circuit chip during mounting are relatively small, thereby allowing the integrated circuit chip to sustain no damage. However, a diameter of solder bumps is so large that an electrode arrangement for mounting with area array arrangement has been limited to an electrode pitch of about 250 μm, if necessity of miniaturizing processes of substrates and package reliability are considered.
The above heat-press bonding technique using an anisotropic conductive adhesive has been noted from the viewpoint of production efficiency improvement for cost reduction, because productivity of a packaging process is expected to be higher than ever.
In the above heat-press bonding method using an anisotropic conductive resin film, by pressing the conductive resin film between each of bump electrodes on a semiconductor substrate and corresponding input/output terminal electrodes on a circuit substrate, conductive particles are brought into contact with one another to impart electrical conductivity between the bump electrodes on the semiconductor substrate and corresponding input/output terminal electrodes of the circuit substrate. For providing connection between the electrodes, a considerably large load between the electrodes during mounting is required to be, for example, not less than 200 g per bump electrode. This force may damage a semiconductor circuit or may cause failures, or breakage, of A1 interconnections on the semiconductor substrate.
In packaging by using this method, the conductive resin in its entirety is cured while the semiconductor substrate is being pressed with a large force so as to be brought into direct contact with the input/output terminal electrodes of the substrate, so that stress occurring between electrodes facing each other produces residual stress within the semiconductor substrate, thereby reducing performance of a semiconductor circuit. In particular, pressure exerted on the bump electrodes at a time of mounting may cause the input/output terminal electrodes of the circuit substrate to be deformed into fracture during via hole filling of the substrate connected to the electrodes, resulting in faulty connections in the circuit substrate.
This may happen because, in a case of an anisotropic conductive resin, conductive particles contained in the anisotropic conductive resin and silica filled therein for controlling a thermal expansion coefficient can stress a surface on a side of a semiconductor functional part of the semiconductor substrate due to pressure during packaging.
In the packaging technique disclosed in Japanese Patent Publication No. 8-037206, there has been a problem in that bonding of a large number of ball bumps to adhesive layers reduces reliability because small pieces of a conductive sheet punched from a conductive adhesive sheet must be handled. While loads during packaging are partially applied only to the vicinity of the electrodes, thereby reducing damage to a semiconductor device, an increase in pressure for ensuring bonding may cause a risk with regard to destructing via holes beneath pad electrodes on a circuit substrate because bump electrodes apply pressure to the pad electrodes and stress the pad electrodes. Another problem is that the conductive adhesive sheet is very weak in terms of adhesive strength for joining the semiconductor device to the circuit substrate, thereby resulting in reducing reliability of a semiconductor package.
In the above method of Japanese Patent Publication No. 10-199932, adhesive is applied to tops of bumps on a semiconductor chip and then the bumps are joined to surfaces of pads, resulting in unevenness in height of the bumps which causes faulty bonding; therefore, in order to improve reliability of adhesion between all opposing electrodes, the bumps are required to be previously leveled in height. Though the bumps might be deformed so as to collapse and bonding could be thereby reinforced, there is a danger that such a deformation might result in damage to the semiconductor chip as described above.
It is an object of the present invention to provide a circuit substrate, which is to constitute a package structure by mounting a semiconductor device thereon, which allows connections between electrodes without exerting stress to electrodes or degrading characteristics of the semiconductor device while being mounted onto the circuit substrate.
It is another object of the invention to provide a method for allowing connections between electrodes without development of residual stress between these electrodes when mounting a semiconductor device onto a circuit substrate, and a method of producing such a package structure.
The circuit substrate of the invention includes conductive resin adhesive layers (portions) which are bonded to input/output electrodes, respectively, on a surface of the circuit substrate, and a resin film that has previously covered the surface of the substrate including the conductive resin adhesive layers. Bump electrodes corresponding to these input/output electrodes, having pointed heads, are formed on electrodes of a semiconductor device.
When the semiconductor device is mounted onto the circuit substrate, the bump electrodes of the semiconductor device are pressed toward the input/output electrodes on the circuit substrate such that the pointed heads of the bump electrodes pierce the resin film on the circuit substrate and reach respective conductive adhesive layers. The conductive adhesive layers receive the bump electrodes, attach fixedly thereto, and relax stresses to be applied to the semiconductor device by the bump electrodes, which avoids damaging semiconductor circuits and interconnections on the semiconductor device. Even if the heads of some of the bump electrodes do not reach the input/output electrodes because of warp in the circuit substrate or unevenness in height of the pointed heads, the pointed heads are received within the conductive adhesive layers so that electrical connection between opposing electrodes can be secured by conductivity of the conductive adhesive layers.
In the present invention, the resin film serves also as a protective coating which protects the input/output electrodes of the circuit substrate. For a package structure, the resin film has a function of supporting and reinforcing connection regions, including the bump electrodes and the conductive adhesive layers, to integrally join a surface of the circuit substrate to a surface of a semiconductor circuit, thus ensuring electrical and mechanical reliability of the package structure and enabling heat-press packaging that is suitable for high productivity.
The package structure of the present invention is capable of preventing degradation in characteristics of a semiconductor functional part, and failures such as breaks in interconnections that have been problems with conventional anisotropic conductive films, because the conductive adhesive layers relax stress during packaging. Besides, use of conductive adhesive layers allows mounting with a low load, because such a mounting load that deforms the input/output electrodes of the circuit substrate is not required. Moreover, addition of conductive adhesive layers having a flexible nature into a junction layer leads to provision of a package structure that is more reliable than conventional structures. The package structure can be assembled with heat-press bonding mounting with high productivity and low cost that causes no damage, in contrast to typical package structures for an integrated circuit.
A circuit substrate of the present invention is a circuit substrate to have mounted thereon a semiconductor device. The circuit substrate comprises input/output terminal electrodes formed on a surface of a main body of the substrate, conductive adhesive layers (portions) attached to the terminal electrodes, and a resin film formed on the surface of the main body of the substrate so as to cover the terminal electrodes and the conductive adhesive layers.
Such a circuit substrate may be produced as follows. Conductive adhesive is applied by printing the adhesive onto input/output terminal electrodes formed on a surface of a main body of the substrate, and the conductive adhesive layers are thereby formed. After the conductive adhesive layers are cured, the surface of the main body of the substrate is coated with a resin film so that the film covers the conductive adhesive layers together with the terminal electrodes.
The circuit substrate of the invention is used such that a semiconductor device may be mounted on the circuit substrate for producing a package structure of the semiconductor device. In the package structure, bump electrodes on the semiconductor device are electrically connected through the conductive adhesive to the input/output terminal electrodes on the main body of the circuit substrate, and the semiconductor device is bonded and fixed to the circuit substrate by the resin film which has previously been formed on the main body of the circuit substrate.
At a time such a package structure is assembled, the bump electrodes have pointed heads that have previously been formed on input/output electrodes of the semiconductor device, and the circuit substrate is provided with its input/output terminal electrodes on the surface of the main body of the circuit substrate. The conductive adhesive layers are formed on these terminal electrodes, and also formed is the resin film covering the surface of the main body of the substrate and the conductive adhesive layers. The package structure is assembled and produced as follows. The semiconductor device is pressed to the circuit substrate so as to insert the bump electrodes into the resin film, after the film has been melted on the circuit substrate through heating, such that the bump electrodes become fixed to respective conductive adhesive layers. Then, the bump electrodes are electrically connected to corresponding terminal electrodes of the circuit substrate before the resin film is cured so as to join the semiconductor device to the circuit substrate.
In the present invention, at a time of packaging, the conductive adhesive layers, which comprise composite material containing conductive particles dispersed in high density in a resin component, have already been heated, thereby remaining softened. When fitted onto the terminal electrodes on the main body of the circuit substrate, the bump electrodes having the pointed heads on the semiconductor device have only to reach the softened conductive adhesive layers, but do not require so high a pressure as to deform the electrodes of the circuit substrate, i.e., the semiconductor device can be joined to the circuit substrate even with a low mounting load. The conductive adhesive layers of the circuit substrate receive the bump electrodes, and deform to lessen stress which is to be developed by such reception, and therefore prevents residual stress from remaining in the semiconductor device. As a result, degradation in characteristics of the semiconductor device, breaks in interconnection, and the like can be effectively prevented.
Moreover, the circuit substrate may originally be provided with the conductive adhesive layers on the electrodes on the surface of the main body of the circuit substrate, and with the resin film (film) which fully covers the surface of the main body of the substrate together with the conductive adhesive layers so that the semiconductor device can be packaged by performing one procedure of heat-press bonding, thus achieving a packaging operation at a low cost.
The conductive adhesive may be prepared by kneading a pasty mixture of a resin component and conductive particles as conductive filler. When used, the adhesive is coated, in a thin layer, onto a top surface of each of the input/output terminal electrodes (i.e., pad electrodes) on the main body of the circuit substrate to form the conductive adhesive layers.
The resin component of the conductive adhesive may be selected from thermoplastic resins and thermosetting resins, and epoxy resin may preferably be used in view of stability and electric insulation, especially high-frequency performance and strength, and high heat resistance. The resin component is solid at ordinary temperatures, and preferably, may be suitably softened or melted when being moderately heated during a mounting operation.
As the conductive particles, there can be used particles formed of a metal selected from noble metals of Cu, Ag, and Au, an iron group of Fe, Ni and Co, a platinum group of Pt, Pd, et al, and other metals such as Zn, and carbon C. Resin particles coated with metal, such as Au-coated resin particles, also can be used.
On the other hand, the resin film is made of a resin selected from among thermosetting resins which, during a mounting operation, can be softened or melted under moderate heat applied to the circuit substrate in its entirety. As such a resin, for example, thermosetting epoxy resin, silicone resin, urethane resin, polyvinyl chloride resin, phenolic resin, acrylic resin, polyester, polycarbonate, and polyacetal can be used, and particularly, epoxy resin may be preferable.
The resin film may further contain a powdery filler that is suitable for viscosity control, an expander or reinforcement. As the filler, for example, there can be used inorganic particles such as silica SiO2, alumina Al2O3, silicon nitride Si3N4, silicon carbide SiC, and aluminum nitride AlN. In this case, the resin film exhibits insulation.
It is preferable for such conductive adhesive layers, on the electrodes, to have a thickness of not greater than 10 μm, and it is particularly preferable for the layers to have a thickness on the order of 0.1 to 3 μm.
The resin film may contain conductive particles as the filler, with these conductive particles being used, for example, for an anisotropic conductive resin film containing suitable metal particles. In this case, the resin film has only to be insulating under no load or pressure during mounting, even when the resin film is sandwiched between electrodes. Electrical connections between the electrodes is provided by the conductive adhesive layers that are separately provided on the electrodes of the circuit substrate.
In the semiconductor device 5 of this example in
As described above, the circuit substrate to receive the semiconductor device 5 is originally formed with conductive resin adhesive layers 3 positioned on the input/output terminal electrodes 2 on the surface of the main body 1 of the circuit substrate, corresponding to the bump electrodes 7 of the semiconductor device 5, and with a resin film 4 which covers the main body 1 of the circuit substrate.
During a mounting operation, the semiconductor device is sucked by a heated head of a mounting machine, that is provided with a heater, and is heated and pressed to the circuit substrate so that the bump electrodes 7 are inserted into corresponding conductive adhesive layers 3 of the substrate, and later, the semiconductor device is cooled. The bump electrodes 7 are thereby bonded to the conductive adhesive layers 3, and the semiconductor substrate 50 of the semiconductor device is bonded and fixed to the circuit substrate by the resin film 4. In this process, the circuit substrate also may be heated such that the conductive adhesive 3 and the resin film 4 are softened.
This circuit substrate as described above, configured by formation of the adhesive layers on the input/output terminal electrodes 2 of the substrate, and by coating of the resin film 4 thereon, may be formed as follows. The input/output terminal electrodes 2 (pad electrodes) have previously been formed on the surface of the main body of the circuit substrate so as to correspond accurately to the input/output terminal electrodes 6 of the semiconductor device 5 and, during a process of forming the conductive adhesive layers 3, conductive adhesive is preferably applied by a printing process onto the input/output terminal electrodes 2 formed on the surface of the main body of the substrate. Alternatively, conductive adhesive transferred onto the bump electrodes 7 of the semiconductor device may be transferred again onto the input/output terminal electrodes of the circuit substrate.
For the printing process of forming the adhesive layers,
In a subsequent resin film coating process, a thermosetting resin film 40 may be used, which has previously been formed, for the resin film and which has an appropriate adhesive property, in which case, as shown in
For bump electrode 7 of the semiconductor device a structure can be used which has a projecting portion 70 at an extremity thereof, and is capable of piercing the resin film 4 and conductive adhesive layer 3. For example, there can be used projected conductive electrodes made with use of a wire bonding method, or projected electrodes formed with use of an electroplating or electroless plating method. In particular, projected electrodes shaped by plucking away molten metal using a wire bonding method may be used as the bump electrodes 7, and, during a mounting operation, a pointed head of each of the bump electrodes can produce an increased force to pierce into the resin film 4 at a time of mounting, thereby providing stable connections between the electrodes 2 and 7 by pressing with a low load. For such bump electrodes, for example, a low-melting metal or alloy thereof, containing Au, Sn, Ag, Pb, Bi, Zn, Sb, Pd, C, Pt, or the like may be used. The pointed heads of the bump electrodes preferably may have a rectangular, circular, or elliptical shape, with a size of one side or a diameter of an extremity thereof being not greater than about 20 μm. It is particularly preferable for the size of each pointed head to be not greater than 10 μm.
Another method of producing the circuit substrate may include steps of: previously forming conductive adhesive layers 3 on separate resin film 40 as described above to prepare resin film 4; covering the main body of the circuit substrate with the resin film 40 such that the conductive adhesive layers face input/output terminal electrodes 2 of circuit substrate 1; and bonding the resin film to the main body of the circuit substrate. In order to form the conductive adhesive layers 3 on the resin film 40, there can be used a method of applying conductive adhesive paste 30 onto a thermoplastic resin film by performing a printing process with a pattern corresponding to an arrangement of the terminal electrodes 2 on the main body of the circuit substrate.
As shown in
Another method of forming conductive adhesive layers 3 on resin film 40, as shown in
In this method, the through holes 85 are bored through the masking sheet 81 so as to coincide with positions on the resin film 40 that are to correspond to terminal electrodes 2 on the main body 1 of the circuit substrate. The through holes 85 end at a surface of the resin film 40 that defines bottom surfaces of the through holes, and are filled with conductive adhesive paste 30. After this filling, only the masking sheet 81 is removed. With removal of the masking sheet 81, the paste 30 that has filled the through holes 85 remains as the conductive adhesive layers 3, with a desired pattern, on the resin film 40. The masking sheet 81 is preferably composed of two layers, i.e., a separate resin sheet 84 to be bonded onto the resin film 40, and a release sheet 83 that adheres to the sheet 84. The through holes are formed so as to pierce the resin sheet 84 and the release sheet 83. The masking sheet composed of two layers has an advantage of improving formability of conductive adhesive, for the following reason. At a time of filling, some of conductive adhesive paste 30 remains on the release sheet 83 outside of the through holes, and there is a fear that the conductive adhesive paste inside the through holes might be exfoliated and removed simultaneously with removal of the resin sheet 84 if the paste that has overflowed the through holes is cured. If only the release sheet 83 can immediately be stripped off while the paste is in a soft state after filling, however, conductive adhesive can be reliably and fully fed only into the through holes and the cured resin sheet 84 has only to be stripped off afterward.
In the method of producing the circuit substrate, which is shown in
In a next step, as shown in
The through holes can be formed by ultraviolet irradiation instead of laser irradiation. In an ultraviolet irradiation method, a resin sensitive to ultraviolet rays is used. As the resin for this purpose, ultraviolet curing epoxy or acrylic resin can be preferably used. When portions of uncured release sheet 83 are masked for interception of rays of light and the sheet is irradiated with ultraviolet rays in this method, portions of the sheet other than the masked portions are cured, whereas portions to be removed directly under an intercepting mask remain uncured. Then, removal of the uncured portions results in formation of the through holes.
In a next step, as shown in
The resin film 40, thus having patterned conductive adhesive layers 3, is bonded onto a main body of a circuit substrate as shown in
In a package structure using the circuit substrate of the invention in which bump electrodes of a semiconductor device are electrically and mechanically connected to input/output terminal electrodes 2 of the circuit substrate 1 through conductive adhesive, the semiconductor device is bonded by a resin film 4 formed previously on the main body 1 of the circuit substrate. An elastomer layer, which is elastically softer than the resin film 4, or a sealing resin, may be interposed between the semiconductor device and the resin film 4.
In a method of producing the package structure, semiconductor device 5 has bump electrodes 7, main body 1 of the circuit substrate has input/output terminal electrodes 2 on a surface thereof, and a separate resin film 4 is previously provided with conductive adhesive layers 3 corresponding to the terminal electrodes 2 on the main body of the circuit substrate, on one side of the film, and an elastomer layer corresponding to the semiconductor device 5 is provided on another side of the film.
In this embodiment, the circuit substrate has a main body 1 on which terminal electrodes 2 as described above are arranged, conductive adhesive layers 3 are on the terminal electrodes 2, a resin film 4 covers the conductive adhesive layers, and an elastomer layer is provided on the resin film 4. The elastomer layer on the resin film 4 may be interposed between a semiconductor functional part of the semiconductor device 5 and the resin film 4 on the main body of the circuit substrate, thus constituting a package structure.
As the elastomer layer, a layer of synthetic resin (including elastic synthetic rubber) may be used, which is softer and has a lower elasticity modulus than the resin film 4. In this arrangement, at least the semiconductor functional part of the semiconductor device 5 is protected by the elastomer layer. The elastomer layer absorbs and reduces a stress that acts through rigid resin film 4, or an exterior impulsive force, and therefore prevents damage to and degradation in function of the semiconductor functional part, e.g., an integrated circuit portion on a semiconductor substrate 50.
The elastomer layer may preferably be a silicone elastomer layer while resin film 4 is of epoxy.
In a package structure of a third embodiment of the invention, a space between a circuit substrate and a semiconductor device may be filled with a liquid sealing resin together with a resin film. In a method of producing such a circuit substrate, such liquid sealing resin may be used instead of the resin film, or with the resin film by being applied to the resin film.
The liquid sealing resin may be porous. Existence of air bubbles in the sealing resin provides an advantageous structure in that a semiconductor device does not reduce much in a high-frequency property apparently because a dielectric constant of air is lower than that of the resin. Such a sealing resin may contain foaming components which generate air bubbles when resin components react to be cured. After curing, the air bubbles generated in the liquid resin remain as pores such that the sealing resin becomes porous. An amount of the air bubbles can be changed, for example, by controlling quantities of a reactive diluent and the like.
When using a liquid resin, as shown in
In Embodiment 1, Au bumps formed as the bump electrodes by performing a wire bonding method were mounted on the input/output terminal electrodes of the circuit substrate through conductive adhesive as the junction layers, and sealing with an epoxy sealing resin was executed.
In conventional example 1, Ni—Au electroless plated bumps were used as bump electrodes, solder was used as junction layers, and an ultraviolet curing epoxy resin was used as a sealing resin.
In each of Embodiment 1 and conventional example 1, a package structure for an n-channel MOS transistor was produced, and deterioration of the transistor was examined by a change in threshold voltage.
In results of a test, the n-channel MOS transistor of Embodiment 1 exhibited a change in threshold voltage of not greater than 0.7% with respect to a mounting load of 1 g per bump.
In conventional example 1 employing a conventional soldering method, by contrast, a threshold voltage of the n-channel MOS transistor changed by approximately 10% in comparison with that of an initial stage, after mounting with a mounting load of 10 g per bump.
Other package structures for SRAM according to the embodiment of the invention were produced in the same manner under mounting loads of 1 g and 20 g per bump, and achieved good connections after mounting, with no bit error (0/228) occurring due to a mounting operation.
In consideration of these results, it is found that, in the soldering method of conventional example 1, the junction layers have no component that is capable of relaxing a shrinkage stress which acts when the sealing resin is cured so that this stress acts directly on a semiconductor device and changes its threshold voltages. To the contrary, in the embodiment of the invention, soft conductive adhesive as junction layers can relax a curing shrinkage stress caused by the sealing resin, and therefore no stress acts on a semiconductor substrate of the semiconductor device, so that a satisfactory result can be obtained. A result of stress analysis also indicates that a package structure using conductive adhesive layers 3 can hardly produce stress therein. Therefore, it should be understood that conductive resin adhesive is an effective component for stress relaxation.
As a conventional example, tests of packaging a semiconductor device were conducted using a conventional anisotropic conductive film 49 shown schematically in
Packaging tests were conducted with use of a circuit substrate of the invention. A circuit substrate having a glass-epoxy main body (FR4) was used, and the package structure shown in
As bump electrodes of a semiconductor device, Au bumps with a size of its pointed head being 20 square μm were formed according to a wire bonding method. In a mounting structure, semiconductor device 5 had the bump electrodes on a chip pressed against and connected to the input/output terminal electrodes of the circuit substrate having the resin film previously bonded to the main body thereof, and the structure was reinforced by sealing resin filled into a space between the resin film and the chip. Tests were conducted with a variation of loads for pressing the bump electrodes of the semiconductor device to the input/output terminal electrodes of the circuit substrate.
A package structure obtained was tested regarding initial connection performance with respect to the mounting loads per bump, and regarding connection performance after reflowing and, in addition, tests were made when the structure was repeatedly heated five times at 270° C.
Table 1 shows these test results. Samples having this package structure exhibited stable and good electrical and mechanical connection performance over all connections between the bump electrodes of the semiconductor device and the terminal electrodes, with loads of not lower than 20 g per bump being applied at a time of mounting.
The circuit substrate of the invention, and the method of producing the same, can be utilized for producing and using substrates which are provided for an electrical industry, particularly for a semiconductor manufacturing industry. A method of producing a package structure of a semiconductor device can be widely used for production and use of semiconductor package structures in the electrical industry, particularly in the semiconductor manufacturing industry.