|Publication number||US20050180284 A1|
|Application number||US 11/101,833|
|Publication date||Aug 18, 2005|
|Filing date||Apr 8, 2005|
|Priority date||Mar 29, 2001|
|Also published as||CN1620690A, EP1459310A1, US7300690, US7309518, US20020197438, US20050202201, US20080032086, WO2003052757A1|
|Publication number||101833, 11101833, US 2005/0180284 A1, US 2005/180284 A1, US 20050180284 A1, US 20050180284A1, US 2005180284 A1, US 2005180284A1, US-A1-20050180284, US-A1-2005180284, US2005/0180284A1, US2005/180284A1, US20050180284 A1, US20050180284A1, US2005180284 A1, US2005180284A1|
|Inventors||Grant Hay, Azar Alizadeh, Wit Bushko, Irene Dris, Thomas Feist|
|Original Assignee||Grant Hay, Azar Alizadeh, Wit Bushko, Irene Dris, Thomas Feist|
|Export Citation||BiBTeX, EndNote, RefMan|
|Patent Citations (24), Referenced by (18), Classifications (56)|
|External Links: USPTO, USPTO Assignment, Espacenet|
This application Claims the benefit of U.S. Provisional Application Ser. No. 60/316,126 filed Aug. 30, 2001, and U.S. Provisional Application Ser. No. 60/279,887 filed Mar. 29, 2001, which are incorporated herein by reference.
Optical, magnetic and magneto-optic media are primary sources of high performance storage technology that enables high storage capacity coupled with a reasonable price per megabyte of storage. Areal density, typically expressed as billions of bits per square inch of disk surface area (Gbits per square inch (Gbits/in2)), is equivalent to the linear density (bits of information per inch of track) multiplied by the track density in tracks per inch. Improved areal density has been one of the key factors in the price reduction per megabyte, and further increases in areal density continue to be demanded by the industry.
In the area of optical storage, advances focus on access time, system volume, and competitive costing. Increasing areal density is being addressed by focusing on the diffraction limits of optics (using near-field optics), investigating three dimensional storage, investigating potential holographic recording methods and other techniques.
Conventional polymeric data storage media has been employed in areas such as compact disks (CD-ROM) and recordable or re-writable compact disks (e.g., CD-RW), and similar relatively low areal density devices, e.g., less than about 1 Gbits/in2, which are typically optical devices requiring the employment of a good optical quality substrate having low birefringence.
Conventionally, the above issues associated with employing first surface, including near field, techniques have been addressed by utilizing metal, e.g., aluminum, and glass substrates. These substrates are formed into a disk and the desired layers are disposed upon the substrate using various techniques, such as sputtering. Possible layers include reflective layers, dielectric layers, data storage layers and protective layers. Once the desired magnetic layers have been added, the disk may be partitioned into radial and tangential sectors through magnetic read/write techniques. Sector structure may also be added through physical or chemical techniques, e.g. etching, however this must occur prior to the deposition of the magnetic layers.
As is evident from the fast pace of the industry, the demand for greater storage capacities at lower prices, the desire to have re-writable disks, and the numerous techniques being investigated, further advances in the technology are constantly desired and sought.
Disclosed herein is a storage media having a radial deviation of less than or equal to about 1.15 degrees at a radius of 55 mm. In one embodiment, the storage media comprises: a plastic substrate, an optical layer and a data storage layer disposed therebetween. A reflective layer is disposed between the data storage layer and the substrate.
The above described and other features are exemplified by the following figures and detailed description.
Referring now to the drawings, wherein like elements are numbered alike:
In this specification and in the Claims that follow, reference will be made to a number of terms that shall be defined. For example, the singular forms “a”, “an” and “the” include plural referents unless the context clearly dictates otherwise. “Optional” or “optionally” mean that the subsequently described event or circumstance may or may not occur, and that the description includes instances where the event or circumstance occurs and instances where it does not. “Tilt” as used herein refers to the degrees by which a material bends on a horizontal axis and is typically measured as the vertical deviation at the outer radius of the storage medium. The “maximum radial tilt range” as used herein is the disk curvature during absorption and subsequent desorption of water and is hence twice the radial tilt specification as usually specified by the developers in the industry.
High-density re-recordable optical media formats are being developed to replace existing VHS tape recorders for consumer entertainment consumption. The goal is to produce a removable media format approaching or even exceeding 20 gigabites (Gb) in storage and having data transfer rates of approaching or even exceeding 100 megabites per second (Mbps). Thinner readthrough mediums are required for these types of media with as thin as 80 micrometers currently are being developed. Most of the formats are asymmetric in structure with the above mentioned thin readthrough medium being supported by a thicker substrate. Curvature in the readthrough medium is induced by changes in the surrounding environment. Humidity and temperature changes will induce curvature into the total asymmetric structure and hence the readthrough medium. The curvature induces spherical aberrations that lead to poor performance of the optical drive. Disclosed below are ranges of material parameters and material parameter ratios for the substrate and film that lead to improved dimensional stability of the total structure. This technology minimizes curvature variation in the readthrough medium induced by environmental humidity changes.
Optical media format developers are currently moving towards re-recordable optical media formats that will replace the consumer VHS market. In these formats the areal density is increased by: adding extra information layers, decreasing laser wavelength, and/or increasing numerical aperture.
Both increasing the numerical aperture and decreasing the wavelength has a detrimental impact on the magnitude of the optical aberrations and hence read noise/errors. These aberrations are considerably sensitive to tilt of the optical medium. Materials utilized for manufacture of optical media generally adsorb water that in turn causes a volume change of the material better known as swell. Any asymmetry in the water absorption/swell will incur a bending moment within the media. Asymmetry in the water absorption in optical disks is caused by the need for impermeable metallic and inorganic layers adjacent to the information layer. The bending moment causes curvature in the media and hence the readthrough medium.
Disc curvature is determined by measuring a laser beam deflection off the disc surface. The angle of inclination from a flat horizontal disc is compared to the angle of inclination of the disc of interest; the difference in the angles is referred to as disc tilt. From geometrical considerations the laser beam deflection is equal to twice the disc tilt and is commonly referred to as radial deviation. The tilt range is defined as the maximum range in the tilt measured on a disc at a specific disc radius on both absorption and subsequent desorption of water.
To attain high areal densities in optical storage media the laser beam spot diameter (i.e., the diameter of the laser light beam that strikes the media) needs to be decreased. In the pure diffraction limited case the beam diameter is related to the numerical aperture and wavelength in the following way:
In the optical media formats laser wavelength and/or numerical aperture may be altered to achieve the desired density increase. The inherent problem with moving to lower wavelengths and higher numerical apertures is the retrospective noise tolerance collapse; e.g., tilt tolerance, which is related to the above in the following way:
d=thickness of readthrough medium
In media formats being developed the thickness of the optical medium is being reduced, relative to current formats, to increase the disc tilt tolerance. This optical layer or optical film is then bonded to a thicker substrate for mechanical stability and final use in an optical drive. There are other instances where more than one of these optical layers is bonded together to obtain a multilayer format similar to the DVD format. The film is the optical medium and the information layer is on the injection-molded substrate. These thin optical mediums can be thought of as optical films.
Assuming that the structure is an elastic plate that extends infinitely in the in-plane directions and that the material properties are not a function of thickness then the isotropic strain due to water absorption is given by the below expression:
β=swell coefficient where ε(t)=βC(Z,t)
The curvature of the substrate is related to the first moment of the water distribution in the disk as shown below:
For multiple layer systems the above integrals are summations of integrals across the specific layer thicknesses including material parameters for each layer. The concentration of water as a function of thickness and time c(z,t) is calculated from a solution to the diffusion equation. In the case of a two layer system the time dependant curvature change induced by a set humidity change is given by the below general expression:
Δφ=change in relative humidity
ratio of layer thickness,
ratio of mechanical stiffness,
ratio of water strains,
ratio of diffusivities
subscript “2” refers to the film and subscript “1” refers to the substrate
If all of the material parameters are supplied, the two layer structure dynamic curvature change can be determined.
Optical media manufacturers specify upper and lower specification limits on structure curvature. This requires that the substrate curvature falls within these specification limits at all times during any environmental humidity change. The curvature range (
The maximum in the dynamic curvature on absorption and desorption of water for a single substrate is given by the following relation:
This shows that reducing the solubility and swell coefficient of the material can minimize the pure substrate tilt. Consequently, an optical film is chosen to minimize system curvature. The curvature can be converted into a tilt and the maximum tilt range experienced by the structure on sorption and subsequent desorption is given by the below expression:
Max Radial Tilt Range (rad)
K is the curvature (length−1);
Δrh is step relative humidity;
βis strain/mass fraction water at a given temperature(T);
s is mass fraction water at relative humidity (rh)=1 and T;
ε=βs is water strain at rh=l and T;
t is substrate thickness; and
r is radius of interest.
The “maximum radial tilt range” as used herein is the disk curvature during absorption and subsequent desorption of water and is hence twice the radial tilt specification as usually specified by the developers in the industry.
hence arriving at a value of one and minus one at the maximum and minimum respectively for a substrate without film. By adding a film comprising a different chemical composition than the substrate, the asymmetry can be reduced, hence reducing the value of the maximum tilt.
As the thickness of the optical film (matching film and mismatched film) is increased, the maximum tilt will also reduce to the point where there is no tilt for a film of the same thickness as the substrate (e.g., DVD, DVR (digital video recordings), and the like).
If the thickness of the film is fixed then material properties of the film can be optimized to reduce the tilt range. By mismatching the material of the film to that of the substrate, the tilt range can also be reduced. For example, Table 1 gives ratios of parameters for a disc system (100 micrometer (μm) film and 1.1 millimeter (mm) substrate) that lead to a curvature range that is 11% that of the substrate curvature range. This is a four fold improvement over a matched film/substrate system for a given thickness.
TABLE 1 Ratios Value Thickness ρ 0.09 Stiffness γ 3 Swell δ 1.01 Diffusivity q 0.15 Minimum Range 0.11
For a given film thickness the curvature is more sensitive to the strain ratio and stiffness ratio and less sensitive to the diffusion ratio.
Based upon the above information, the optical film can be a plastic having the desired stiffness ratio (γ) (Youngs modulus(megapascals)/(1-Poisson ratio)), swell ratio(δ) (percentage growth of the material at equilibrium), and diffusivity ratio(q), wherein all ratios refer to the ratio of the optical film to the substrate. The desired amounts of these parameters are dependent upon the thickness of the optical film. The ultimate desire is to reduce the tilt, e.g., curvature, to a radial deviation range of less than or equal to about 1.15 degrees at a radius of 55 mm, with less than or equal to about 1.0 degrees at a radius of 55 mm preferred, less than or equal to about 0.80 degrees at a radius of 55 mm more preferred, less than or equal to about 0.70 degrees at a radius of 55 mm even more preferred, less than or equal to about 0.50 degrees at a radius of 55 mm yet even more preferred, and less than or equal to about 0.25 degrees at a radius of 55 mm desired. Generally, the stiffness ratio can be greater than or equal to about 0.5, with a stiffness ratio of greater than or equal to about 0.70 preferred, and a stiffness ratio of greater than or equal to about 1.25 more preferred. Preferably, the stiffness ratio is less than or equal to about 5, with a stiffness ratio of less than or equal to about 3 preferred, and a stiffness ratio of less than or equal to about 2.5 even more preferred. The stiffness of the optical film and substrate is measured in tensile deformation at room temperature using an Instron testing machine. With respect to the swell ratio, it can be greater than or equal to about 0.50, with greater than or equal to about 0.75 preferred, and greater than or equal to about 1.0 more preferred. Preferably, the swell ratio is less than or equal to about 5, with less than or equal to about 3 more preferred, and less than or equal to about 2.5 even more preferred. The swell strain is measured using a Thermomechanical analyzer from TA instruments. The diffusivity ratio can be greater than or equal to about 0.05, with greater than or equal to about 0.10 preferred. Preferably the diffusivity is less than or equal to about 2.0, with less than or equal to about 1.0 preferred
With respect to thickness, the optical film can have a thickness of about 0.2 micrometers to about 0.6 mm. Within the film thickness range, less than or equal to about 0.6 mm is preferred, less than or equal to about 250 micrometers is more preferred, and less than or equal to about 120 micrometers is even more preferred, in some applications. Also preferred within this range is the optical thickness of greater than or equal to about 0.2 micrometers, with greater than or equal to about 5 micrometers more preferred, and greater than or equal to about 50 micrometers even more preferred. In contrast, the substrate typically has a thickness of greater than or equal to about 0.3 mm, with greater than or equal to about 0.6 mm preferred, and greater than or equal to about 1.1 mm more preferred. Also preferred is a substrate thickness of less than or equal to about 2.5 mm, with less than or equal to about 2.0 mm more preferred, and less than or equal to about 1.5 mm even more preferred. Due to current equipment and due to industry specifications, a substrate thickness of about 1.1 mm is generally preferred. If decreased substrate thicknesses are employed (e.g., less than about 1.2 mm), it is preferred to maintain a optical film to substrate thickness ratio of less than or equal to about 1, with a thickness ratio of less than or equal to about 0.5 preferred, and less than or equal to about 0.1 more preferred. Also preferred is a thickness ratio of greater than or equal to about 0.001, with greater than or equal to about 0.005 more preferred, and greater than or equal to about 0.025 even more preferred.
Possible optical film materials that can be any plastic that exhibits appropriate properties, including thermoplastics, thermosets, as well as homopolymers, copolymers, reaction products, and combinations comprising at least one of the foregoing materials including, but not limited to addition and condensation polymers. Illustrative, non-limiting examples of thermoplastic polymers are olefin-derived polymers such as polyethylene, polypropylene, and their copolymers; chlorinated polyethylene, polyvinyl chloride, polymethylpentane; ethylene-tetrafluoroethylene copolymers, polyvinyl fluoride, polyvinylidene fluoride, polyvinylidene chloride, polytetrafluoroethylene, ethylene-vinyl acetate copolymers, polyvinyl acetate, diene-derived polymers such as polybutadiene, polyisoprene, and their copolymers; polymers of ethylenically unsaturated carboxylic acids and their functional derivatives, including acrylic polymers such as poly(alkyl acrylates), poly(alkyl methacrylates), polyacrylamides, polyacrylonitrile and polyacrylic acid; alkenylaromatic polymers such as polystyrene, poly-alpha-methylstyrene, hydrogenated polystyrenes, syndiotactic and atactic polystyrenes, polycyclohexyl ethylene, styrene-co-acrylonitrile, styrene-co-maleic anhydride, polyvinyltoluene, and rubber-modified polystyrenes; polyamides such as nylon-6, nylon-66, nylon-11, and nylon-12; polyacetals, polyesters such as polyethylene terephthalate, polybutylene terephthalate, and polycyclohexylmethylene terephthalate; polycarbonates; polyestercarbonates; high heat polycarbonates, polyethers such as polyarylene ethers especially polyphenylene ethers derived from 2,6-dimethylphenol and copolymers with 2,3,6-trimethylphenol, polyethersulfones, polyetherethersulfones, polyetherketones, polyetheretherketones, and polyetherimides; polyarylene sulfides, polysulfones, and polysulfidesulfones; and liquid crystalline polymers.
Non-limiting examples of thermosetting resins are epoxies, phenolics, alkyds, polyesters, polyimides, polyurethanes, mineral filled silicones, bis-maleimides, cyanate esters, multifunctional allylic compounds such as diallylphthalate, acrylics, alkyds, phenol-formaldehyde, novolacs, resoles, bismaleimides, PMR resins, melamine-formaldehyde, urea-formaldehyde, benzocyclobutanes, hydroxymethylfurans, and isocyanates benzocyclobutene resins, as well as homopolymers, copolymers, reaction products, and combinations comprising at least one of the foregoing thermosetting resins. In one embodiment, the thermoset polymer further comprises at least one thermoplastic polymer, such as, polyphenylene ether, polyphenylene sulfide, polysulfone, polyetherimide, polyester, and the like, as well as homopolymers, copolymers, reaction products, and combinations comprising at least one of the foregoing thermoplastic polymers. The thermoplastic polymer is typically combined with a thermoset monomer mixture before curing of the thermoset.
Both thermoplastic polyesters and thermoplastic elastomeric polyesters can be employed. Illustrative, non-limiting examples of thermoplastic polyesters include poly(ethylene terephthalate), poly(1,4-butylene terephthalate), poly(1,3-propylene terephthalate), poly(cyclohexanedimethanol terephthalate), poly(cyclohexanedimethanol-co-ethylene terephthalate), poly(ethylene naphthalate), poly(butylene naphthalate), and polyarylates. Illustrative, non-limiting examples of thermoplastic elastomeric polyesters (commonly known as TPE) include polyetheresters such as poly(alkylene terephthalate)s (particularly poly[ethylene terephthalate] and poly[butylene terephthalate]) containing soft-block segments of poly(alkylene oxide), particularly segments of poly(ethylene oxide) and poly(butylene oxide); and polyesteramides such as those synthesized by the condensation of an aromatic diisocyanate with dicarboxylic acids and a carboxylic acid-terminated polyester or polyether prepolymer.
Suitable polyarylates include, but are not limited to, the polyphthalate esters of 2,2-bis(4-hydroxyphenyl)propane (commonly known as bisphenol A), and polyesters consisting of structural units of the formula I:
wherein R16 is hydrogen or C1-4 alkyl, optionally in combination with structural units of the formula II:
wherein R17 is a divalent C4-12 aliphatic, alicyclic or mixed aliphatic-alicyclic radical. The latter polyesters may be prepared by the reaction of a 1,3-dihydroxybenzene moiety with at least one aromatic dicarboxylic acid chloride under alkaline conditions. Structural units of formula II contain a 1,3-dihydroxybenzene moiety which may be substituted with halogen, usually chlorine or bromine, or preferably with C1-4 alkyl; e.g., methyl, ethyl, isopropyl, propyl, butyl. The alkyl groups are preferably primary or secondary groups, with methyl being more preferred, and are most often located in the ortho position to both oxygen atoms although other positions are also contemplated. The most preferred moieties are resorcinol moieties, in which R16 is hydrogen. The 1,3-dihydroxybenzene moieties are linked to aromatic dicarboxylic acid moieties which may be monocyclic moieties, e.g., isophthalate or terephthalate, or polycyclic moieties, e.g., naphthalenedicarboxylate.
In the optional soft block units of formula II, resorcinol or alkylresorcinol moieties are present in ester-forming combination with R17 which is a divalent C4-12 aliphatic, alicyclic or mixed aliphatic-alicyclic radical.
Possible polycarbonates include those comprising structural units of the formula III:
wherein at least about 60 percent of the total number of R18 groups are aromatic organic radicals and the balance thereof are aliphatic, alicyclic, or aromatic radicals. Suitable R18 radicals include m-phenylene, p-phenylene, 4,4′-biphenylene, 4,4′-bi(3,5-dimethyl)-phenylene, 2,2-bis(4-phenylene)propane, 6,6′-(3,3,3′,3′-tetramethyl-1,1′-spirobi[1 H-indane]), 1,1′-bis(4-phenylene)-3,3,5-trimethylcyclohexane, and similar radicals such as those which correspond to the dihydroxy-substituted aromatic hydrocarbons disclosed by name or formula (generic or specific) in U.S. Pat. 4,217,438.
More preferably, R18 is an aromatic organic radical and still more preferably a radical of the formula IV:
wherein each A1 and A2 is a monocyclic divalent aryl radical and Y1 is a bridging radical in which one or two atoms separate A1 and A2. For example, A1 and A2 typically represent unsubstituted phenylene or substituted derivatives thereof. The bridging radical Y1 is most often a hydrocarbon group and particularly a saturated group such as methylene; cyclohexylidene; 3,3,5-trimethylcyclohexylidene; or isopropylidene. The most preferred polycarbonates are bisphenol A polycarbonates, in which each of A1 and A2 is p-phenylene and Y1 is isopropylidene. Suitable polycarbonates may be made using various processes, including interfacial, solution, solid state, or melt processes.
In one embodiment, the storage media comprises at least one layer with at least one polycarbonate. In another embodiment, the storage media comprises at least one layer with two different polycarbonates. Homopolycarbonates derived from a single dihydroxy compound monomer and copolycarbonates derived from more than one dihydroxy compound monomer are encompassed.
In one embodiment, the substrate and/or at least one other layer of the storage media comprise a polycarbonate or copolycarbonate comprising structural units (V) or (VI):
where R1, R2, R3, R4, R5, and R6 are, independently chosen from C1-C6 alkyl and hydrogen; R7 and R8 are, independently, C1-C6 alkyl, phenyl, C1-C6 alkyl substituted phenyl, or hydrogen; m is an integer of 0 to about 12; q is an integer of 0 to about 12; m+q is an integer of about 4 to about 12; n is an integer of about 1 to about 2; and p is an integer of about 1 to about 2.
Representative units of structure (V) include, but are not limited, to residues of 1,1-bis(4-hydroxy-3-methylphenyl)cyclohexane (DMBPC); 1,1-bis(4-hydroxy-3-methylphenyl)cyclopentane; 1,1-bis(4-hydroxy-3-methylphenyl)cycloheptane; 1,1 -bis(4-hydroxy-3-methylphenyl)-3,3,5-trimethylcyclohexane (DMBPI); and mixtures comprising at least one of the foregoing units.
Representative units of structure (VI) include, but are not limited, to residues of 2,2-bis(4-hydroxy-3-methyl)propane (DMBPA); and 4,4′-(1-phenylethylidene)bis(2-methylphenol) (DMbisAP).
In an even further embodiment, the substrate and/or at least one other layer of the storage media can comprise polycarbonate or copolycarbonate comprises structural units (VII):
where R9, R10, R13 and R14 are independently C1-C6 alkyl, R11 and R12 are independently H or C1-C5 alkyl, each R15 is independently selected from H and C1-C3 alkyl and each n is independently selected from 0, 1 and 2.
Representative units of structure (VII) include, but are not limited to, 6,6′-dihydroxy-3,3,3′,3′-tetramethyl spirobiindane (SBI); 6,6′-dihydroxy-3,3,5,3′,3′,5′-hexamethyl spirobiindane; 6,6′-dihydroxy-3,3,5,7,3′,3′,5′,7′-octamethylspirobiindane; 5,5′-diethyl-6,6′-dihydroxy 3,3,3′,3′-tetramethylspirobiindane, and mixtures comprising at least one of the foregoing units.
The polyphenylene ethers are polymers comprising a plurality of structural units of the formula (VIII)
wherein in each of the units independently, each Q1 is independently halogen, primary or secondary lower alkyl (i.e., alkyl containing up to 7 carbon atoms), phenyl, haloalkyl, aminoalkyl, hydrocarbonoxy, or halohydrocarbonoxy wherein at least two carbon atoms separate the halogen and oxygen atoms; and each Q2 is independently hydrogen, halogen, primary or secondary lower alkyl, phenyl, haloalkyl, hydrocarbonoxy or halohydrocarbonoxy as defined for Q1. Most often, each Q1 is alkyl or phenyl, especially C1-4 alkyl, and each Q2 is hydrogen.
Both homopolymer and copolymer polyphenylene ethers are can be employed. Suitable copolymers include random copolymers containing such units in combination with (for example) 2,3,6-trimethyl-1,4-phenylene ether units. Also included are polyphenylene ethers containing moieties prepared by grafting onto the polyphenylene ether in a known manner such materials as vinyl monomers or polymers such as polystyrenes and elastomers, as well as coupled polyphenylene ethers in which coupling agents such as low molecular weight polycarbonates, quinones, heterocycles and formals undergo reaction in known manner with the hydroxy groups of two polyphenylene ether chains to produce a higher molecular weight polymer, provided a substantial proportion of free OH groups remains.
Particularly useful polyphenylene ethers for many purposes are those that comprise molecules having at least one aminoalkyl-containing end group. The aminoalkyl radical is typically located in an ortho position to the hydroxy group. Polymers containing such end groups may be obtained by incorporating an appropriate primary or secondary monoamine such as di-n-butylamine or dimethylamine as one of the constituents of the oxidative coupling reaction mixture. Also frequently present are 4-hydroxybiphenyl end groups, typically obtained from reaction mixtures in which a by-product diphenoquinone is present, especially in a copper-halide-secondary or tertiary amine system. A substantial proportion of the polymer molecules, typically constituting as much as about 90% by weight of the polymer, may contain at least one of the aminoalkyl-containing and 4-hydroxybiphenyl end groups.
It will be apparent that the contemplated polyphenylene ethers include all those presently known, irrespective of variations in structural units or ancillary chemical features, including, but not limited to homopolymer and copolymer thermoplastic polymers, and mixtures comprising at least one of the foregoing polyphenylene ethers. Copolymers may include random, block or graft type. Thus, for example, suitable polystyrenes include homopolymers, such as amorphous polystyrene and syndiotactic polystyrene, and copolymers containing these species. The latter embraces high impact polystyrene (HIPS), a genus of rubber-modified polystyrenes comprising blends and grafts wherein the rubber is a polybutadiene or a rubbery copolymer of styrene in a range between about 70% by weight and about 98% by weight and diene monomer in a range between about 2% by weight and about 30% by weight. Also included are ABS copolymers, which are typically grafts of styrene and acrylonitrile on a previously formed diene polymer backbone (e.g., polybutadiene or polyisoprene). Suitable ABS copolymers may be produced by various methods.
In a preferred embodiment the optical film comprises thermoplastic resins and the substrate comprises thermosetting resins. It is also possible for the optical film to comprises thermosetting resins while the substrate comprises thermoplastic resins. Similarly it is possible for the optical film and the substrate to comprise a mixture of thermoplastic and thermosetting resins and wherein at least one element of the composition of the optical film is different from that of the substrate.
The optical layer or film can be deposited by a variety of techniques, including vapor deposition (e.g., plasma enhanced chemical vapor deposition, and the like), coating (e.g., electrodeposition coating, meniscus coating, spray coating, extrusion coating, spin coating, solution coating, and the like), casting (e.g., extrusion casting, solution casting, and the like), injection molding, film blowing, calendaring, and the like, as well as combinations comprising at least one of the foregoing techniques. Meanwhile, the substrate is typically manufactured by an extrusion, molding (e.g., injection molding, extrusion molding, compression molding, and the like), and the like, as well as combinations comprising at least one of the foregoing techniques.
Although the substrate is typically a polycarbonate material, it is clearly understood that the substrate can also comprise any plastic mentioned above in relation to the optical film. For example, the substrate can comprise thermoplastics wherein the thermoplastic is bisphenol A polycarbonate, copolyester polycarbonate of bisphenol A and dodecanoic acid containing 7 mole % of polyester and 93 mole % of bisphenol A polycarbonate, 39 mole % of polyphenylene ether and 61 mole % polystyrene, 1,3-bis(4-hydroxyphenyl methane), 90 mole % bisphenol A and 10 mole % disecbutyl bisphenol A, polycarbonate of tetramethyl cyclobutanediol and high flow polycarbonate tetra xylyl hydroquinone diphosphite, and the like, as well as mixtures comprising at least one of the foregoing thermoplastics. Similarly, the optical layer can comprise thermoplastics including 80 wt % isophthalate terephthalate resorcinol-20 wt % polycarbonate, styrene acrylonitrile, bisphenol A polycarbonate, copolyester polycarbonate of bisphenol A and dodecanoic acid containing 7 mole % of polyester and 93 mole % of bisphenol A polycarbonate, 39 mole % of polyphenylene ether and 61 mole % polystyrene, 1,3-bis(4-hydroxyphenyl methane), 90 mole % bisphenol A and 10 mole % disecbutyl bisphenol A, polycarbonate of tetramethyl cyclobutanediol and high flow polycarbonate tetra xylyl hydroquinone diphosphite, and the like, as well as reaction products and mixtures comprising at least one of the foregoing thermoplastics. Furthermore, the film for these high density formats preferably has optical properties such as in-plane retardations of less than or equal to about 10 nanometers (nm). The films also have low thickness non-uniformity and surface roughness. For a 100 micrometer film, thickness uniformity at length scales longer than 2 centimeters (cm) is on the order of less than or equal to about 2 micrometers and the surface roughness at the 1 millimeter (mm) length scale is on the order of less than or equal to about 40 nm.
The substrate may further include energy absorption. Dampening can be achieved through a variety of approaches such as by addition of an energy absorbing component or through slip mechanisms involving various fillers and reinforcing agents. Useful materials that may improve the damping characteristics include elastic materials with high damping capabilities (e.g., a damping coefficient of greater than or equal to about 0.05), such as vulcanized rubbers, acrylic rubbers, silicone rubbers, butadiene rubbers, isobutylene rubbers, polyether rubbers, isobutylene-isoprene copolymers and isocyanate rubber, nitrile rubbers, chloroprene rubbers, chlorosulfonated polyethylene, polysulfide rubbers and fluorine rubber, block copolymers including polystyrene-polyisoprene copolymers such as described in U.S. Pat. No. 4,987,194, thermoplastic elastomeric materials, including polyurethanes, and combinations comprising at least one of the foregoing, among others. Vibration-damping materials also include resins in which large amounts of particles (such as ferrites, metals, ceramics, and the like), flakes (such as of talc, mica and the like), and various fibers (such as zinc oxide, wollastonite, carbon fibers, glass fibers, and the like), and mixtures comprising at least one of the foregoing, can be employed. Microfibers, fibrils, nanotubes, and whiskers, foamed and honeycombed structures may also be useful as are various combinations of the foregoing.
Beside the optical layer, which is typically the top layer, other layers which may be applied to the substrate may include one or more data storage layer(s), lubricating layer(s), adhesive layer(s), dielectric layer(s), reflective layer(s), insulating layer(s), combinations comprising at least one of these layers, and others. The data storage layer(s) may comprise any material capable of storing retrievable data, such as an optical layer, magnetic layer, or more preferably a magneto-optic layer, having a thickness of less than or equal to about 600 Å, with a thickness of less than or equal to about 300 Å preferred. Possible data storage layers include, but are not limited to, oxides (such as silicone oxide), rare earth element-transition metal alloy, nickel, cobalt, chromium, tantalum, platinum, terbium, gadolinium, iron, boron, as well as alloys and combinations comprising at least one of the foregoing, and others, such as organic dye (e.g., cyanine or phthalocyanine type dyes), and inorganic phase change compounds (e.g., TeSeSn or InAgSb). Preferably, the data layer has a coercivity of greater than or equal to about 1,500 oersted, with a coercivity of greater than or equal to about 3,000 oersted especially preferred.
The dielectric layer(s) which are often employed as heat controllers, can typically have a thickness of up to or exceeding about 1000 Å and as low as about 200 Å. Possible dielectric layers include nitrides (e.g., silicon nitride, aluminum nitride, and others); oxides (e.g., aluminum oxide); carbides (e.g., silicon carbide); and combinations comprising at least one of the foregoing dielectric layers, among other materials compatible within the environment and preferably not reactive with the surrounding layers.
The reflective layer(s) should have a sufficient thickness to reflect a sufficient amount of energy to enable data retrieval. Typically the reflective layer(s) can have a thickness of up to and sometimes exceeding about 700 Å, with a thickness of about 300 Å to about 600 Å generally preferred. Possible reflective layers include any material capable of reflecting the particular energy field, including metals (e.g., aluminum, silver, gold, titanium, and alloys and mixtures comprising at least one of the foregoing materials and others). The reflective layers may be disposed on the substrate by various techniques such as sputtering, chemical vapor deposition, electroplating and the like.
Optionally disposed between the optical layer and the data storage layer, and/or between other layers, is an adhesive layer that can, for example, adhere the optical film to the other layers supported by the substrate. The adhesive layer can also be employed to enhance the dampening of the disc, with the thickness and nature of the adhesive determining the amount of dampening provided by the layer. The adhesive layer, which can have a thickness of up to about 50 micrometers (μm) or so, with thicknesses of about 1 micrometers to about 30 micrometers preferred, can comprise rubber based or elastomeric thermosets, flexible thermoplastics, and the like. Typical adhesives are rubber-based or rubberlike materials, such as natural rubber or silicone rubber or acrylic ester polymers, and the like. Non-rigid polymeric adhesives such as those based on rubber or acrylic polymers and the like have some of the properties of elastomers, such as flexibility, creep resistance, resilience, and elasticity, and do provide useful dampening to enhance the quality of playback of the data storage disc. The chemistry of non-rigid polymeric adhesives is diverse, and includes polymers of the types of materials described herein as elastomers and rubbers, as flexible thermoplastics, and as thermoplastic elastomers. Suitable examples of such adhesives include polyisoprene, styrene butadiene rubber, ethylene propylene rubber, fluoro vinyl methyl siloxane, chlorinated isobutene-isoprene, chloroprene, chlorinated polyethylene, chlorosulfonated polyethylene, butyl acrylate, expanded polystyrene, expanded polyethylene, expanded polypropylene, foamed polyurethane, plasticized polyvinyl chloride, dimethyl silicone polymers, methyl vinyl silicone, polyvinyl acetate, and the like, as well as compositions comprising at least one of the foregoing adhesives. This layer may also comprise any combination comprising at least one of the above adhesives. Typically pressure sensitive adhesives are preferred for use in data storage disc applications. The adhesive layer may be added to the data storage disc by methods such as vapor deposition, spin casting, solution deposition, injection molding, extrusion molding, and the like.
In addition to the data storage layer(s), dielectric layer(s), protective layer(s) and reflective layer(s), other layers can be employed such as lubrication layer and others. Useful lubricants include fluoro compounds, especially fluoro oils and greases, and the like.
The storage media disclosed herein reduces tilt as compared to a substrate without an optical layer and/or a substrate with a matched optical layer (e.g., where the optical layer comprises the same material as the substrate) by controlling the thickness and/or mismatching the optical layer and substrate compositions. Some of the advantages are illustrated in
In this example (simulated) Bisphenol A Polycarbonate (BPA-PC) was retained as the substrate material, while isophthalate terephthalate resorcinol—polycarbonate (ITR-PC 80-20) blend, styrene acrylonitrile (SAN 576) or BPA-PC was chosen as the optical film. The optical film has a thickness of about 100 micrometers while the substrate has a thickness of 1.1 millimeters giving a film to substrate thickness ratio of 0.09.
Both the substrate and optical film stiffness were measured in tensile deformation at room temperature using an Instron tensile testing machine. The swell of a polymeric material as defined herein is the percentage of volume growth of the totally dry material when subjected to a 100% relative humidity environment at a specific temperature. The swell is measured utilizing a TMA 2940 Thermomechanical Analyzer from TA instruments. A film is mounted under a very low constant load and initially held in a dry atmosphere. The length change is then measured upon absorption of water when the material is exposed to 100% relative humidity. The water strain or swell is taken to be the strain of the material (length change divided by the original gauge length).
Table 2 below outlines the stiffness and swell ratio of the film to substrate as well as the radial tilt range for the different material combinations. It can be clearly seen that when polymeric materials chosen for the optical film and the substrate are different from each other, the radial tilt range is much smaller than for the purely matched material system where BPA-PC alone is used as material for the substrate and optical film
TABLE 2 Stiffness ratio Swell ratio Radial Tilt Range Film Material (film to substrate) (film to substrate) (degrees) ITR-PC 80-20 1.101 1.781 0.292 SAN 576 1.378 1.649 0.236 BPA-PC 1.000 1.000 0.560
Generally an optical film that is stiffer and has a greater swell (water strain) than the substrate material will have better performance when compared to a matched film/substrate system.
In this example BPA-PC is the polymeric material used for the optical film and different polymeric materials were used as the substrate as shown in Table 2. The optical film has a thickness of about 100 micrometers while the substrate has a thickness of 1.1 millimeters giving a film to substrate thickness ratio of 0.09. The substrate materials are listed as follows: copolyester polycarbonate of Bisphenol A and dodecanoic acid containing 7 mole % of polyester and 93 mole % of BPA-PC (RL-7553), 39 mole % of polyphenylene ether and 61 mole % polystyrene (PPE/PS 101), 1,3-bis(4-hydroxyphenyl methane) (BHPM), 90 mole % bisphenol A and 10 mole % disecbutyl bisphenol A (BPA disecbutyl BPA), polycarbonate of tetramethyl cyclobutanediol (TMCBD-PC) and blend of BPA-polycarbonate with polycarbonate tetra xylyl hydroquinone diphosphite (BPA-PC+1 wt % TXHQDR).
TABLE 3 Stiffness ratio Swell ratio Radial Tilt (film to (film to Range Substrate Material substrate) substrate) (degrees) RL 7553 (SPOQ) 1.311 1.209 0.297 PPE/PS 101 0.744 2.141 0.196 39%/61% BHPM 1.000 1.724 0.208 BPA-disecbutyl 0.908 1.560 0.284 BPA 90-10 TMCBD-PC 1.478 2.451 0.167 BPA-PC + 1 wt % 1.188 1.200 0.339 TXHQDP BPA-PC 1.000 1.000 0.560
Both the substrate and optical film stiffness were measured in tensile deformation at room temperature using an Instron tensile testing machine. The swell of a polymeric material as defined herein is the percentage of volume growth of the totally dry material when subjected to a 100% relative humidity environment at a specific temperature. The swell is measured utilizing a TMA 2940 Thermomechanical Analyzer from TA instruments. A film is mounted under a very low constant load and initially held in a dry atmosphere. The length change is then measured upon absorption of water when the material is exposed to 100% relative humidity. The water strain or swell is taken to be the strain of the material (length change divided by the original gauge length). Table 3 above outlines the stiffness and swell ratio of the film to substrate as well as the radial tilt range for the different material combinations. Once again it can be seen that when the polymeric material used as the optical film differs from that used for the substrate, the radial tilt range is significantly decreased which in turn allows for the increased storage capacity.
In this example, BPA-PC was replaced in both the optical film and substrate by different materials as indicated in Table 4 below. The optical film has a thickness of about 100 micrometers, while the substrate has a thickness of 1.1 millimeter giving a film to substrate thickness ratio of 0.09.
TABLE 4 Stiffness ratio Swell ratio Radial Tilt Film Substrate (film to (film to Range Material Material substrate) substrate) (degrees) PS 101 PPE/PS 101 1.039 0.010 0.154 39%/61% BHPM PPE/PS 101 1.000 2.935 0.142 39%/61%
Here the optical film was polystyrene (PS) in one case while 1,3-bis(4-hydroxyphenyl methane) (BHPM) was used in the other. A blend of 39 mole % of polyphenylene ether and 61 mole % polystyrene was used as the substrate in both cases. Both the substrate and optical film stiffness were measured in tensile deformation at room temperature using an Instron tensile testing machine. The swell of a polymeric material as defined herein is the percentage of volume growth of the totally dry material when subjected to a 100% relative humidity environment at a specific temperature. The swell is measured utilizing a TMA 2940 Thermomechanical Analyzer from TA instruments. A film is mounted under a very low constant load and initially held in a dry atmosphere. The length change is then measured upon absorption of water when the material is exposed to 100% relative humidity. The water strain or swell is taken to be the strain of the material (length change divided by the original gauge length). Table 4 above outlines the stiffness and swell ratio of the film to substrate as well as the radial tilt range for the different material combinations. Once again it can be seen that when the polymeric material used as the optical film differs from that used for the substrate, the radial tilt range is significantly decreased which in turn allows for the increased storage capacity.
The storage media disclosed herein reduces radial tilt by mismatching the compositions of the optical film and substrate, and by optionally employing mis-matched thicknesses of the substrate and optical film. The mismatched compositions contribute in enabling higher areal density storage (about 20 Gb or greater) when compared to a disc without a mis-matched composition of the optical film and the substrate.
While the invention has been described with reference to an exemplary embodiment, it will be understood by those skilled in the art that various changes may be made and equivalents may be substituted for elements thereof without departing from the scope of the invention. In addition, many modifications may be made to adapt a particular situation or material to the teachings of the invention without departing from the essential scope thereof. Therefore, it is intended that the invention not be limited to the particular embodiment disclosed as the best mode contemplated for carrying out this invention, but that the invention will include all embodiments falling within the scope of the appended claims.
|Cited Patent||Filing date||Publication date||Applicant||Title|
|US4217438 *||Dec 15, 1978||Aug 12, 1980||General Electric Company||Polycarbonate transesterification process|
|US4373065 *||Feb 17, 1981||Feb 8, 1983||Xerox Corporation||Optically isotropic devices|
|US4680211 *||Jul 25, 1985||Jul 14, 1987||The Dow Chemical Company||Recording disks|
|US4719594 *||Aug 26, 1985||Jan 12, 1988||Energy Conversion Devices, Inc.||Grooved optical data storage device including a chalcogenide memory layer|
|US4845142 *||Jun 13, 1988||Jul 4, 1989||Sumitomo Chemical Company, Limited||Magneto optical disk substrate comprising an aromatic vinyl monomer and a polyphenylene ether|
|US4957776 *||Jan 3, 1989||Sep 18, 1990||Sanyo Electric Co., Ltd.||Method of manufacturing optical disc|
|US4987194 *||Sep 22, 1989||Jan 22, 1991||Kuraray Company, Limited||Block copolymers and composition containing the same|
|US5053288 *||Nov 18, 1988||Oct 1, 1991||Teijin Limited||Optical recording medium|
|US5135791 *||Nov 20, 1990||Aug 4, 1992||Sumitomo Chemical Company, Limited||Optical device|
|US5312663 *||Dec 27, 1991||May 17, 1994||Eastman Kodak Company||Optical element having durability enhancing layer|
|US5586110 *||Dec 23, 1994||Dec 17, 1996||Mitsubishi Denki Kabushiki Kaisha||Optical/magneto-optical recording medium having a hygroscopic swelling layer|
|US5609990 *||Feb 8, 1995||Mar 11, 1997||Imation Corp.||Optical recording disk having a sealcoat layer|
|US6042919 *||May 7, 1998||Mar 28, 2000||Zomax Optical Media, Inc.||Structurally stable optical data storage medium|
|US6066218 *||Apr 23, 1998||May 23, 2000||3M Innovative Properties Company||Method and apparatus for assembling an optical recording medium|
|US6128274 *||Nov 9, 1998||Oct 3, 2000||Sharp Kabushiki Kaisha||Optical recording disk capable of suppressing bimetallic effects caused by thermal expansion|
|US6316071 *||Aug 23, 1999||Nov 13, 2001||Idemitsu Petrochemical Co., Ltd.||Substrate for digital versatile disk and process for producing the same|
|US6475589 *||Dec 17, 2001||Nov 5, 2002||General Electric Company||Colored optical discs and methods for making the same|
|US6645596 *||Dec 7, 2000||Nov 11, 2003||Dainippon Ink And Chemicals, Inc.||Optical disk and ultraviolet-curing composition for optical disk|
|US6924017 *||Jan 24, 2001||Aug 2, 2005||Dainippon Ink And Chemicals, Inc.||Ultraviolet-curable composition and optical recording|
|US20020094455 *||Mar 11, 2002||Jul 18, 2002||Feist Thomas Paul||Poly(arylene ether) data storage media|
|US20020197441 *||Aug 31, 2001||Dec 26, 2002||Ramesh Hariharan||Storage medium for data|
|US20030044564 *||Jan 9, 2002||Mar 6, 2003||General Electric Company Crd||Storage medium for data with improved dimensional stability|
|US20030198774 *||Apr 17, 2003||Oct 23, 2003||Irene Dris||Storage medium for data with improved dimensional stability|
|US20040063031 *||Aug 7, 2003||Apr 1, 2004||Gallucci Robert R.||Data storage medium and method for the preparation thereof|
|Citing Patent||Filing date||Publication date||Applicant||Title|
|US7244813||Aug 26, 2003||Jul 17, 2007||General Electric Company||Methods of purifying polymeric material|
|US7256225||Aug 26, 2003||Aug 14, 2007||General Electric Company||Methods of preparing a polymeric material|
|US7309518||Apr 8, 2005||Dec 18, 2007||General Electric Company||Radial tilt reduced media|
|US7314658 *||Dec 14, 2005||Jan 1, 2008||General Electric Company||Storage medium for data|
|US7314907||Aug 19, 2004||Jan 1, 2008||General Electric Company||Purified polymeric materials and methods of purifying polymeric materials|
|US7354990||Jul 18, 2005||Apr 8, 2008||General Electric Company||Purified polymeric materials and methods of purifying polymeric materials|
|US7585935||Apr 7, 2008||Sep 8, 2009||Sabic Innovative Plastics Ip B.V.||Purified polymeric materials and methods of purifying polymeric materials|
|US7655746||Sep 16, 2005||Feb 2, 2010||Eastman Chemical Company||Phosphorus containing compounds for reducing acetaldehyde in polyesters polymers|
|US7662880||Nov 24, 2004||Feb 16, 2010||Eastman Chemical Company||Polyester polymer and copolymer compositions containing metallic nickel particles|
|US7745512||Sep 16, 2005||Jun 29, 2010||Eastman Chemical Company||Polyester polymer and copolymer compositions containing carbon-coated iron particles|
|US7776942||Sep 16, 2005||Aug 17, 2010||Eastman Chemical Company||Polyester polymer and copolymer compositions containing particles of titanium nitride and carbon-coated iron|
|US7799891||Nov 3, 2009||Sep 21, 2010||Eastman Chemical Company||Phosphorus containing compounds for reducing acetaldehyde in polyesters polymers|
|US20050046056 *||Aug 26, 2003||Mar 3, 2005||Jiawen Dong||Method of molding articles|
|US20050046070 *||Aug 26, 2003||Mar 3, 2005||Jiawen Dong||Methods of purifying polymeric material|
|US20050048252 *||Aug 26, 2003||Mar 3, 2005||Irene Dris||Substrate and storage media for data prepared therefrom|
|US20050049333 *||Aug 26, 2003||Mar 3, 2005||Buckley Paul W.||Methods of preparing a polymeric material|
|US20050064129 *||Aug 19, 2004||Mar 24, 2005||Jiawen Dong||Purified polymeric materials and methods of purifying polymeric materials|
|US20050250932 *||Jul 18, 2005||Nov 10, 2005||Hossan Robert J||Purified polymeric materials and methods of purifying polymeric materials|
|U.S. Classification||369/53.21, 369/275.3, G9B/7.172, G9B/7.159|
|International Classification||G11B7/258, G11B7/257, G11B7/243, G11B7/2536, G11B7/2433, G11B7/2585, G11B7/2533, G11B7/2534, G11B7/259, G11B7/2542, G11B7/2535, G11B7/2472, G11B7/24056, G11B7/2578, G11B7/2595, G11B7/24027, B32B3/02, B32B7/00, G11B7/09|
|Cooperative Classification||Y10T428/26, Y10T428/2495, Y10T428/21, G11B2007/24312, G11B2007/24316, G11B7/2595, G11B7/256, G11B7/252, G11B2007/25711, G11B7/259, G11B7/2472, G11B7/2585, G11B2007/24308, G11B2007/2571, G11B2007/25708, G11B7/258, G11B7/2534, G11B7/2536, G11B2007/25715, G11B7/2578, G11B7/248, G11B7/2433, G11B7/2542, G11B7/2535, G11B2007/25713, G11B2007/24314, G11B7/2533, G11B2007/2432, G11B7/24056, G11B2007/2431|
|European Classification||G11B7/24, G11B7/2542, G11B7/2533|