US 20050255703 A1
An etching process yields an optimized formation of via holes through the combination of semiconductor material selection and etchant parameters. Over an interlayer dielectric layer is formed a stop layer having a SiON layer over which is a SiC layer. Selective etching will attack the SiC layer while leaving the SiON layer undisturbed. When etching the via hole, a proportion of about 7:90 O2:CO was observed to yield a superior etch.
1. A process for manufacturing a semiconductor device, which comprises:
providing an insulation layer in which a wiring layer is embedded;
forming a first stopper layer over the insulation layer;
forming a first interlayer dielectric over the first stopper layer;
forming a second stopper layer over the first interlayer dielectric;
forming a second interlayer dielectric over the second stopper layer;
forming a third stopper layer over the second dielectric; and
etching a via hole in the semiconductor device, with at least one etchant gas that has a proportion of oxygen to carbon monoxide of about 7:90, and ashing using not more than 8% oxygen.
2. The process of
3. The process of
4. The process of
5. The process of
6. The process of
7. The process of
(1) etching using a gas mixture comprising Ar:C4F8:C2F6:O2;
(2) etching using a gas mixture comprising Ar:O2:C4F8:CO;
(3) etching using a gas mixture comprising Ar:CHF3:C2F6:N2;
(4) etching using a gas mixture comprising Ar:O2:C4F8:CO; and
(5) etching using a gas mixture comprising Ar:N2:C4F8:CO.
8. The process of
(1) etching using a gas mixture comprising Ar:C4F8:C2F6:O2 in a proportion of about 11:1:2:2;
(2) etching using a gas mixture comprising Ar:O2:C4F8:CO in a proportion of about 9:1:2:13;
(3) etching using a gas mixture comprising Ar:CHF3:C2F6:N2 in a proportion of about 13:1:4:2;
(4) etching using a gas mixture comprising Ar:O2:C4F8:CO in a proportion of about 15:1:3:23; and
(5) etching using a gas mixture comprising Ar:N2:C4F8:CO in a proportion of about 8:1:2:13.
An improved etching process creates a via hole using a 1-step dual damascene method.
Damascene refers to a process in which interconnect metal lines are delineated by isolating dielectrics. Damascening is not performed by lithography and etching, but by chemical-mechanical planarization (CMP). In damascening, an interconnect pattern is first lithographically defined in the layer of dielectric, and then metal is deposited to fill in the resulting trenches. Then excess metal is removed by means of chemical-mechanical polishing (planarization).
Chemical-mechanical polishing (CMP), also called chemical-mechanical planarization, refers to a method of removing layers of solid by chemical-mechanical polishing carried out for the purpose of surface planarization and definition of the metal interconnect pattern.
Dual damascene is a modified version of the damascene process that is used to form metal interconnect geometry using a CMP process instead of metal etching. In dual damascene, two interlayer dielectric patterning steps and one CMP step create a pattern that would otherwise require two patterning steps and two metal CMP steps when using a conventional damascene process.
FIGS. 1(a) through
In a first conventional method of manufacturing a semiconductor shown in
Next, as is shown in
When the etching to open via hole 8 is finished, the first photoresist 7 is removed from above the second silicon oxide film 6. Optionally, a second photoresist 9 that has an open portion that corresponds to the wiring slot 10 is formed in its place, as shown in
Next, anisotropic dry etching to open wiring slot 10 is performed using the second photoresist 9 as a mask. This etching is performed under the condition that a silicon oxide film can be removed with a significant selection ratio to the silicon nitride film. At this time, the first silicon nitride film 3 and the second nitride film 5 are both used as stopper films that stop the progress of etching. Next, etching for the purpose of removing the second silicon nitride film 5 exposed in the bottom of wiring slot 10 and the first silicon nitride film 3 exposed in the bottom of via hole 8 is performed. If this processing is done properly, via hole 8 which exposes the surface of first wiring layer 1 and wiring slot 10 which leads to via hole 8 are formed as shown in
A typical damascene structure according to the conventional art is described by D. Edeletein et al., Proc. IEEE IEDM (1997) and S. Venkatesan et al., Proc. IEEE IEDM (1997).
Via hole formation according to the conventional art gives rise to a number of problems as feature size decreases. For example, etch selectivity must be controlled during the etch to prevent photoresist from being prematurely removed to cause damage to the underlying layers. For example, if a plasma etch uses a gas mixture that contains a 1:1 proportion of oxygen to carbon monoxide, then both the photoresist and the material not covered by the photoresist would be etched at the same rate. In order to prevent damage to the semiconductor device, it would then be necessary to use a very thick layer of photoresist, which could then cause poor line, trench and via hole definition.
Additional difficulties in conventional etch processes arise when silicon is etched using a fluorocarbon gas such as CF4. The etch process converts the silicon to SiF4, but a polymeric carbon residue remains on the semiconductor, frequently appearing as a “fence” around the via hole.
As has been shown, the conventional art technologies have disadvantages arising from inefficient etching. These disadvantages give rise to manufacturing inefficiency, semiconductor damage and such phenomena as the creation of fences from residual materials around the via holes. These fences give rise to such unwanted effects such as parasitic capacitance and reduced conductance by the metal component. Accordingly there is a need to provide new etch technologies that minimize these disadvantageous phenomena.
The invention, in part, pertains to a method for forming a via hole on a dual damascene structure that overcomes the disadvantages of the conventional art.
The invention, in part, pertains to a process for manufacturing a semiconductor device that includes forming a first stopper layer over an insulation layer in which a wiring layer is embedded, forming a first interlayer dielectric over the first stopper layer, forming a second stopper film over the first interlayer dielectric, forming a second interlayer dielectric over the second stopper film, forming a third stopper film over the second dielectric, and etching a via hole in the semiconductor device, wherein the etching comprises at least one etch using an etchant gas that has a proportion of oxygen to carbon monoxide of about 7:90. In preferred embodiments of the invention, the first stopper layer comprises SiN, the second stopper layer comprises SiC, and the third stopper layer comprises a layer of SiON over the second dielectric and a layer of SiC over the layer of SiON. The wiring layer preferably comprises copper.
The invention, in in a preferred embodiment pertains to a series of sequential etch steps that includes (1) etching using a gas mixture comprising Ar:C4F8:C2F6:O2 in a proportion of about 200:19:30:30, (2) etching using a gas mixture comprising Ar:O2:C4F8:CO in a proportion of about 60:7:12:90, (3) etching using a gas mixture comprising Ar:CHF3:C2F6:N2 in a proportion of about 125:10:40:20, (4) etching using a gas mixture comprising Ar:O2:C4F8:CO in a proportion of about 60:4:12:90, and (5) etching using a gas mixture comprising Ar:N2:C4F8:CO in a proportion of about 60:8:12:100. In a preferred embodiment of the invention, in part, the method further comprises ashing using not more than 8% oxygen. Step (2) has a high selectivity to SiC. Step (5) does not require a high selectivity to SiC as it is a SiC etch step. The use of oxygen in the etch gas of step (5) is avoided to suppress CuO formation. Accordingly, the etch gas of step (5) should contain zero mol percent oxygen to minimize CuO formation.
It is to be understood that both the foregoing general description and the following detailed description are exemplary and explanatory and are intended to provide further explanation of the invention as claimed.
The accompanying drawings are included to provide a further understanding of the invention. The drawings illustrate embodiments of the invention and together with the description serve to explain the principles of the embodiments of the invention.
Advantages of the present invention will become more apparent from the detailed description given hereinafter. However, it should be understood that the detailed description and specific examples, while indicating preferred embodiments of the invention, are given by way of illustration only, since various changes and modifications within the spirit and scope of the invention will become apparent to those skilled in the art from this detailed description.
The thicknesses of the layers shown in the embodiment of the invention shown in
Over a wafer substrate was formed a 100 nm layer of Organic BARC, over which was consecutively formed a 50 nm layer of SiC, a 120 nm layer of SiON, a layer of FSG, a layer of SiN, a layer of FSG and a layer of SiN. The FSG layers have thicknesses of about 500 nm, and the SiN layers have thicknesses of about 50 nm. After forming the trench, a via hole was etched using the etch sequence set forth in Table 1.
In order to maintain a constant depth of all the via holes, an end point detector system was used. Optical emission spectroscopy is the most common method for etch endpoint detection because it is easy to implement with high sensitivity.
When etching the via hole, the etch selectivity must be controlled to prevent the photoresist from being prematurely removed. If, for example, in the second etch step corresponding to No. 2 in Table 1., the ratio of O2:CO is 1:1, then the photoresist and the material underlying the via hole portion would both etch at the same rate, which is disadvantageous because there is no selectivity. However, an optimal selectivity was unexpectedly found at a O2:CO ratio of about 7:90 (about 1:13) for the second etch step No. 2 in Table 1.
After the second etch step, there is an ashing step in the sequence. This ashing step removes excess polymer that forms during the etching, as is explained in comparing equation 1 for SiO2 and equation 2 for Si.
In an ashing process according to the conventional art, a high concentration of oxygen is used to ash the photoresist, but the k value (dielectric constant) of the FSG increases. This is not preferable because the capacitance of the embedded lines changes the speed of the transistor. That is, the speed of the transistor decreases as the dielectric constant increases. In the conventional art, the ashing was typically performed using 100 percent oxygen. However, in a preferred embodiment of the invention, the oxygen is diluted with argon to about 8% oxygen or less. Helium and neon can also be used instead of argon as the diluent gas.
The foregoing embodiments and advantages are merely exemplary and are not to be construed as limiting the present invention. The present teaching can be readily applied to other types of methods and apparatuses. The description of the present invention is intended to be illustrative, and not to limit the scope of the claims. Many alternatives, modifications, and variations will be apparent to those skilled in the art. It is to be understood that the foregoing descriptions and specific embodiments shown herein are merely illustrative of the best mode of the invention and the principles thereof, which is therefore understood to be limited only by the scope of the appended claims.