|Publication number||US20050280051 A1|
|Application number||US 11/200,958|
|Publication date||Dec 22, 2005|
|Filing date||Aug 10, 2005|
|Priority date||Dec 12, 2002|
|Also published as||CN1270370C, CN1507032A, US6974981, US20040113174|
|Publication number||11200958, 200958, US 2005/0280051 A1, US 2005/280051 A1, US 20050280051 A1, US 20050280051A1, US 2005280051 A1, US 2005280051A1, US-A1-20050280051, US-A1-2005280051, US2005/0280051A1, US2005/280051A1, US20050280051 A1, US20050280051A1, US2005280051 A1, US2005280051A1|
|Inventors||Dureseti Chidambarrao, Omer Dokumaci, Bruce Doris, Jack Mandelman|
|Original Assignee||Dureseti Chidambarrao, Dokumaci Omer H, Doris Bruce B, Mandelman Jack A|
|Export Citation||BiBTeX, EndNote, RefMan|
|Referenced by (39), Classifications (20)|
|External Links: USPTO, USPTO Assignment, Espacenet|
U.S. patent application Ser. No. 10/______, entitled “Stress Inducing Spacers” filed concurrently herewith is assigned to the same assignee hereof and contains subject matter related, in certain respect, to the subject matter of the present application. The above-identified patent application is incorporated herein by reference.
1. Technical Field of the Invention
This invention pertains to inventive methods of manufacturing a semiconductor device for improving device performance, and to the resulting unique high-performance device structure. In particular, this invention has improved charge mobility in FET devices by structurally imposing tensile and compression forces in a device substrate during device fabrication.
Within the field of semiconductor device design, it is known that mechanical stresses within the device substrate can modulate device performance. Individual stress tensor components affect device behavior of PFETs and NFETs differently. Previous improvements that utilized stress enhancements tended to focus on one or the other type of device outside of a practical performance environment, such as in an IC chip. In order to maximize the performance of both PFETs and NFETs within IC chips, the stress components need to be engineered and applied differently, yet simultaneously. In the present invention we show fabrication methods and resulting structures that have imposed the appropriate stress fields needed to improve the performance of a single device and of at least two devices simultaneously in a common substrate.
2. Description of the Prior Art
Hamada et al, IEEE Transactions on Electron Devices, Vol. 38 No. 4, A New Aspect of Mechanical Stress Effects in Scaled MOS Devices (April 1991) show data correlating weight induced (bending a sample silicon chip) longitudinal and transverse tensile and compressive stress with Transconductance deviation. Within the PFET device a longitudinally applied uniaxial compressive stress had an effect reversed from the effect induced on an NFET. This data can be interpreted such that if you apply an in-plane biaxial tensile stress, the NFET device performance will improve about two-fold as compared to that of a uniaxial tensile situation, while the PFET experiences no change because the longitudinal and transverse tensile stress effects cancel each other out.
In the Symposium on VLSI Technology Digest of Technical Papers (2001), Rim et. al. shows that, using strained Si which has in-plane biaxial tensile stress, improvements occurred for an NFET with a 70% increase in electron mobility. Prior known solutions and methods using mechanical stress for device performance enhancement could not improve both NFETs and PFETs simultaneously. Moreover, prior solutions do not address the feasibility of any kind of device structures or methods of fabricating them.
In this invention we show methods and structures by which we have applied in-plane biaxial (two-dimensional) tensile stress for the NFET while at the same time applying in-plane compressive longitudinal stress and a tensile transverse stress on the PFET device. The structures and methods of making each device individually is also unique. The primary advantage of these methods and structures is that they have provided two-fold device performance improvement relative to merely uniaxial stresses. Another advantage is the method for fabricating NFETs and PFETs simultaneously on a common substrate, wherein each device is designed to enhance performance using stress inducing isolation material. A secondary advantage is the structure and method of building an individual device with enhanced performance provided via stress inducing trench isolation structures.
It is an object of the present invention to provide device performance improvements for NFETs, PFETs, and for both NFETs and PFETs simultaneously. It is another object of the present invention to be readily integratible into present manufacturing processes cheaply for significant device performance improvements by adding a single mask step. It is another object of the present invention to be manufacturable in bulk silicon, silicon-on-insulator (“SOI”), and strained silicon structures.
This invention comprises a trench isolation structure for an NFET device and for a PFET device. An isolation region for the NFET device contains therein a first isolation material which applies a first type of mechanical stress on the NFET device in a longitudinal direction and in a transverse direction. A first isolation region for the PFET device applies mechanical stress on the PFET device in the transverse direction. A second isolation region for the PFET device applies another type of mechanical stress on the PFET device in the longitudinal direction. The isolation regions may comprise similar or different isolation materials depending upon which type of mechanical stress is desired. Typically, the mechanical stresses are either tensile or compressive.
In another aspect, this invention comprises a method for making NFET and PFET devices. This aspect incorporates the formation of isolation regions at the sides and at the ends of the NFET device. Another isolation region is formed at the sides of the PFET device. Another (third) trench isolation region is formed at the ends of the PFET device. Isolation materials in these isolation regions are selected to apply a first type of mechanical stress on the NFET device both in a longitudinal direction and in a transverse direction, and on the PFET device in the transverse direction. Isolation material in the third trench isolation region can be selected to apply a compressive type of mechanical stress in the longitudinal direction of the PFET. In another method of inducing stress vectors, it is useful to oxidize, in order to expand, at least a portion of the isolation material in the third trench isolation region to apply the compressive mechanical stress on the PFET device in the longitudinal direction. Thus, the isolation materials selected may be the same or different for each device depending on whether oxidation is used to induce stress components.
In another aspect, the present invention comprises source and drain regions formed in a substrate. The substrate having a channel region between each of the source and drain regions. A gate region adjacent the channel region controls conduction through the channel region. Stress inducing isolation material adjacent selected sides of the source and drain regions imparts stress, i.e. tension or compression, beyond the source and drain regions of the substrate at least into the channel region.
Other features and advantages of this invention will become apparent from the following detailed description of the presently preferred embodiment of the invention, taken in conjunction with the accompanying drawings.
The present invention involves filling isolation regions, preferably shallow trench isolation (“STI”) with different intrinsically stress inducing materials to impart selected longitudinal and transverse stress components upon active device regions formed in a substrate. For example, using a stress inducing material that is intrinsically tensile causes a tensile state of stress in the substrate and an intrinsically compressive material causes compression in the substrate. In order to impart these different stresses in devices, we use deposited films that impose different intrinsic stresses. For example, TEOS (TETRAETHYLORTHOSILICATE) is known to be tensile because it undergoes densification under anneal and so it shrinks, thereby imposing upon an adjacent substrate a tensile stress. HDP (High density Plasma) oxide is known to be intrinsically compressive. The key here is to integrate two different intrinsically stress inducing structures adjacent the NFET and PFET structures or, individually, one or two stress inducing structures adjacent one of these devices. The process steps for integrating TEOS, which has tensile intrinsic stress, and HDP, which has compressive intrinsic stress, are shown and described below in
The present inventive method also includes a novel STI process flow that results in a SiN (silicon nitride) liner for both transverse and longitudinal components for NFETs but only in a transverse component for PFETs. This process incorporates TEOS for the STI fill because TEOS is permeable to O2 and the SiN liner prevents oxidation from occurring at the Si/TEOS boundary. Therefore, only the longitudinal component of the PFET will be oxidized, which causes the Si/TEOS boundary to expand. The amount and time of oxidation can be used to controllably increase the compressive stress for the PFET in the longitudinal direction. Also, since TEOS is intrinsically a tensile film and a SiN liner is used for both transverse and longitudinal components of the NFET and the transverse component of the PFET, there will be a tensile stress exerted by the TEOS STI in these directions.
Standard STI processes typically utilize a single type of oxide film (a nitride liner is optional) for isolation together with an isolation fill material. In the present invention, different types of oxide film are selectively placed in substrate regions surrounding FET devices. By controlling the fabrication process conditions, the type of stress imparted to adjacent FET devices can also be controlled.
NFET and PFET devices require different stress vectors, or patterns, to enhance charge mobility. The isolation material can be fined tuned to produce a desired stress pattern in the device. Some materials are amenable to further fine tuning via process controls, such as RF power, for example. TEOS is harder to fine tune via process controls because it's a loosely structured material, but it tends to shrink when densified (annealed), thereby imparting one type of intrinsic stress—tensile. HDP is somewhat more controllable than TEOS, it also does not require densification (heat treatment) and typically provides intrinsic compressive stress.
In another embodiment, the end structure comprises an NFET with SiN liner on both longitudinal and transverse components, a PFET with SiN liner on transverse component, and oxidized Si with no SiN liner on the longitudinal component. Several process flows are possible to arrive at the final structure.
The location of the HDP and the TEOS stress inducing regions, in relation to the device regions, is also shown in
In the simultaneous PFET/NFET embodiment of the present invention, the NFET and PFET can be used together simultaneously, for example, in a ring oscillator. The ring oscillator performs ideally when beneficial aspects of the present invention in both devices are balanced, i.e. charge mobility is equivalently enhanced. Another structural use for the present invention includes formation of the silicon source and drain regions in “island” configurations, wherein a substrate device area is surrounded by dielectric STI material, or in SOI (silicon-on-insulator) devices.
The two preferred trench isolation materials, HDP and TEOS, differ in several aspects. The deposition processes of TEOS and HDP are different: TEOS deposition involves a CVD (chemical vapor deposition) process. HDP plasma deposition is a directional process wherein the material is accelerated by an electric field because, in the plasma, HDP is composed of charged particles. HDP has an intrinsic (as deposited) compressive stress and densifies as part of its deposition process. TEOS requires a densification anneal after its deposition, but is intrinsically tensile.
The substrate stresses can be imparted because of shrinking/expansion of a stress inducing material or they can be imposed intrinsically when the stress inducing material is being grown adjacent to the substrate. HDP has a built-in intrinsic stress which is imparted to the substrate upon deposition (while the HDP is grown). Contraction occurs during heat treatment (densification) for TEOS. The underlying elemental mechanisms which induce stresses are not part of the present invention. Therefore, further theoretical details of those mechanisms will not be further addressed.
The structure and choice of isolation materials, selected and formed in substrate regions surrounding FET devices for isolation, are novel. Generally speaking, a mask is used to open regions in the substrate. Next, a unique integration scheme is used to deposit TEOS and HDP in selected portions of the wafer. In one of several embodiments, the HDP regions are inlaid into a TEOS background.
The tensile components and the compressive components are decoupled. The tensile component is established first, by varying the densification process of the TEOS. Temperature and time can vary the stress built into the TEOS, which control the amount of shrinkage (800-1050 C., 1 to 30 minutes, varying inversely). These variables determine how much the TEOS shrinks to some degree (densification). The TEOS molecules become more closely packed in densification and thereby cause tension in the adjacent Si island. The compression in the HDP SiO2, is controlled mostly by the deposition conditions. Tuning of the compressive stress is achieved by control of RF the power. Increased power leads to more compression in the film. Pressure and Flow can also be used to modulate the compression in the HDP SiO2 film.
The process for fabricating NFETs and PFETs with different stresses in the channel region, on a common substrate is illustrated in
Up to this point, the present inventive process follows conventional process steps.
A second method for fabricating the structure of
Because we want to induce longitudinal compressive stress in the PFET, we remove the nitride liner surrounding the silicon island (it is removed from the PFET regions where compressive stress is desired). This allows oxygen to reach the silicon sidewalls during subsequent oxidation steps, and so in this aspect the nitride liner layer acts as an oxidation blocking layer. The nitride liner would block the oxidation, and thus the compression, because it is an excellent oxygen diffusion barrier. In areas where the SiN liner is removed, a portion of the Si on the sidewall of the Si island may be oxidized, thereby causing a controlled amount of compression in the direction longitudinal to current flow for the PFET. Good control in the oxide sidewall growth may be achieved using this method, because you can dial in the amount of compression achieved because of the amount of oxide grown, instead of relying on the HDP deposition conditions. The oxidation causes a compressive stress to be generated due to volume expansion on the sidewall of the Si island. The oxygen will diffuse through the TEOS oxidizing the silicon sidewall, growing a wedge of oxide and will push against the TEOS, causing the desired compression.
At this point, a silicon trench etch with corresponding hard masking produces the result as shown in
The benefit of using this scheme for achieving tension in the NFET and transverse component for PFET and compressive stress in the longitudinal component for the PFET is that the oxidation time and temperature can be used to tune the stress for the longitudinal component for the PFET.
In the prior art, Rim et. al. apply biaxial tension in strained silicon using a SiGe relaxed sub-layer. The problems there are many. While the NFET shows what may be considered significant improvement, they could not simultaneously improve both devices. Also, since the requirement is a relaxed SiGe layer, misfit dislocations are needed at the SiGe/Si interface. One of the major mechanisms by which the misfit dislocations are formed is from threading dislocations. Unfortunately, the threading dislocations can cause significant reliability, yield, and major leakage issues and are difficult to remove in practice.
Mechanical Stress Effect of Etch-Stop Nitride and its Impact on Deep Submicron Transistor Design, Ito et al (IEDM, 2000) impose stress using an etch-stop nitride superlayer that is deposited after the device is completely constructed. Again, here the films have a built-in intrinsic biaxial stress. They found that when the film is in compression NFET performance is degraded, while the PFET is enhanced. Also, they did not improve the performance of both the PFET and NFET simultaneously. Also, since the film is well above the device the stress translated down into the silicon will be somewhat lessened, particularly when compared to something that is directly adjacent the device.
The present solution shows how to apply the correct states of stress through modifying the STI process to benefit both the NFET and PFET simultaneously. It also differs substantially from both of these other approaches since the tension and compression are done through the STI structure and process whereas prior art listed above shows the stress is imposed through strained Si in one case and from intrinsic stress in a layer that comes well after the device build (and not adjacent the device as we do) in another.
The advantages of the method of the preferred embodiment of this invention include: device performance improvements for NFETs, PFETs, and for both NFETs and PFETs simultaneously by inducing in-plane stress patterns; a process readily integratible into present manufacturing processes for bulk silicon, silicon-on-insulator (“SOI”), and strained silicon structures; and improved devices be integrated into present processes cheaply for significant device performance improvements by adding a single mask step.
It will be appreciated that, although specific embodiments of the invention have been described herein for purposes of illustration, various modifications may be made without departing from the spirit and scope of the invention. In particular, other isolation materials can be used, such as ceramics and silicon carbide, which can also impart intrinsic stresses. The general view of stresses in silicon is that it's disadvantageous. Stresses lead to ruptures or dislocations in the lattice structure, which lead to junction leakage, etc. In the present invention, we're intentionally building in a stress pattern.
As another example, nitride films can be readily modulated to have very high intrinsic stress. For example, as shown in Ito et al (IEDM, 2000) the PECVD nitride etch stop film stress could be modulated (by changing the deposition conditions such as SiH4/N2/He flow rates, pressure, HF power, and electrode gap) between −1.4 GPa and +0.3 GPa. Of course, since nitride films have a higher dielectric constant, they will need deeper STI with perhaps larger isolation distances between devices. Hu (JAP, 1991) provides a partial listing of intrinsic stresses in some films. One could use a combination of highly intrinsic stressed films as part of the STI. This adds complexity, but allows for perhaps better tailoring of the stress.
Intrinsic stress is not the only way to add stress into this structural system. By choosing the correct materials with the appropriate thermal expansion coefficient mismatch, we can modulate the tensile stress. Since cool down is when the stress is imposed (operating conditions are between 25 C. and 85 C.), the net thermal mismatch stress will always be tensile. The magnitude of tensile stress is determined by the coefficients of thermal expansion. In the NFET tension in both dimensions (biaxial) is good, while for the PFET we would like to use this material property difference that causes tension only in the transverse direction, while still using a highly compressive intrinsic material in the longitudinal direction.
Nonconventional devices can also be fabricated using the present invention, such as pillar FETs and fin FETS. In a pillar FET, the body of the device is a cylindrical shape formed in a substrate with source/drain diffusions formed at the top and bottom of the cylinder. The gate region typically is adjacent to, or surrounds, the middle portion of the cylinder. A fin FET comprises a thin, elongated, raised substrate region with source and drain diffusions at the ends of the raised region. The gate is typically adjacent three sides of the raised region, the two vertical sides and the top surface of the raised region, between the source/drain diffusions. The general concept is to inlay isolation to produce a stress pattern at least in the channel region of the devices or at least in the source/drain diffusion regions. The appended claims are intended not to exclude various device geometries such as pillar FETs and fin FETs. Providing a uniform background of TEOS fill, then selectively opening regions for HDP deposition is a process that can accommodate device geometries other than those specifically illustrated in the present specification as preferred, currently known embodiments.
Accordingly, the scope of protection of this invention is limited only by the following claims and their equivalents.
|Citing Patent||Filing date||Publication date||Applicant||Title|
|US7118999||Jan 16, 2004||Oct 10, 2006||International Business Machines Corporation||Method and apparatus to increase strain effect in a transistor channel|
|US7144767||Sep 23, 2003||Dec 5, 2006||International Business Machines Corporation||NFETs using gate induced stress modulation|
|US7202132||Jan 16, 2004||Apr 10, 2007||International Business Machines Corporation||Protecting silicon germanium sidewall with silicon for strained silicon/silicon germanium MOSFETs|
|US7205207||Feb 18, 2005||Apr 17, 2007||International Business Machines Corporation||High performance strained CMOS devices|
|US7256081||Feb 1, 2005||Aug 14, 2007||International Business Machines Corporation||Structure and method to induce strain in a semiconductor device channel with stressed film under the gate|
|US7297601||Nov 22, 2005||Nov 20, 2007||International Business Machines Corporation||Method for reduced N+ diffusion in strained Si on SiGe substrate|
|US7381609||Jan 16, 2004||Jun 3, 2008||International Business Machines Corporation||Method and structure for controlling stress in a transistor channel|
|US7410846||Sep 9, 2003||Aug 12, 2008||International Business Machines Corporation||Method for reduced N+ diffusion in strained Si on SiGe substrate|
|US7494886||Jan 12, 2007||Feb 24, 2009||International Business Machines Corporation||Uniaxial strain relaxation of biaxial-strained thin films using ion implantation|
|US7615435||Jul 31, 2007||Nov 10, 2009||International Business Machines Corporation||Semiconductor device and method of manufacture|
|US7682859||Oct 31, 2007||Mar 23, 2010||International Business Machines Corporation||Patterned strained semiconductor substrate and device|
|US7691698||Feb 21, 2006||Apr 6, 2010||International Business Machines Corporation||Pseudomorphic Si/SiGe/Si body device with embedded SiGe source/drain|
|US7700951||Jul 15, 2008||Apr 20, 2010||International Business Machines Corporation||Method and structure for forming strained Si for CMOS devices|
|US7745277||Feb 25, 2005||Jun 29, 2010||International Business Machines Corporation||MOSFET performance improvement using deformation in SOI structure|
|US7749842||May 29, 2007||Jul 6, 2010||International Business Machines Corporation||Structures and methods for making strained MOSFETs|
|US7790540||Aug 25, 2006||Sep 7, 2010||International Business Machines Corporation||Structure and method to use low k stress liner to reduce parasitic capacitance|
|US7790558||Aug 18, 2006||Sep 7, 2010||International Business Machines Corporation||Method and apparatus for increase strain effect in a transistor channel|
|US7791144||Jul 21, 2009||Sep 7, 2010||International Business Machines Corporation||High performance stress-enhance MOSFET and method of manufacture|
|US7821077||Jun 29, 2005||Oct 26, 2010||Fujitsu Semiconductor Limited||Semiconductor device|
|US7843024||Dec 4, 2008||Nov 30, 2010||International Business Machines Corporation||Method and structure for improving device performance variation in dual stress liner technology|
|US7847358||Aug 4, 2006||Dec 7, 2010||International Business Machines Corporation||High performance strained CMOS devices|
|US7928443||Jan 11, 2010||Apr 19, 2011||International Business Machines Corporation||Method and structure for forming strained SI for CMOS devices|
|US7935993||Dec 21, 2009||May 3, 2011||International Business Machines Corporation||Semiconductor device structure having enhanced performance FET device|
|US7964865||Feb 3, 2005||Jun 21, 2011||International Business Machines Corporation||Strained silicon on relaxed sige film with uniform misfit dislocation density|
|US8232180||Sep 20, 2010||Jul 31, 2012||Fujitsu Semiconductor Limited||Manufacturing method of semiconductor device comprising active region divided by STI element isolation structure|
|US8354719 *||Feb 18, 2010||Jan 15, 2013||GlobalFoundries, Inc.||Finned semiconductor device with oxygen diffusion barrier regions, and related fabrication methods|
|US8772127 *||Jan 27, 2011||Jul 8, 2014||Institute of Microelectronics, Chinese Academy of Sciences||Semiconductor device and method for manufacturing the same|
|US8846488||Nov 30, 2011||Sep 30, 2014||Institute of Microelectronics, Chinese Academy of Sciences||Semiconductor device and method for manufacturing the same|
|US8853746||Jun 29, 2006||Oct 7, 2014||International Business Machines Corporation||CMOS devices with stressed channel regions, and methods for fabricating the same|
|US9006836||Apr 17, 2008||Apr 14, 2015||International Business Machines Corporation||Method and structure for controlling stress in a transistor channel|
|US9040373||Dec 13, 2013||May 26, 2015||International Business Machines Corporation||Silicon device on SI:C-OI and SGOI and method of manufacture|
|US9053970||Jan 12, 2010||Jun 9, 2015||International Business Machines Corporation||Patterned strained semiconductor substrate and device|
|US20050054145 *||Sep 9, 2003||Mar 10, 2005||International Business Machines Corporation||Method for reduced n+ diffusion in strained si on sige substrate|
|US20050082634 *||Oct 16, 2003||Apr 21, 2005||International Business Machines Corporation||High performance strained cmos devices|
|US20050148146 *||Feb 18, 2005||Jul 7, 2005||Doris Bruce D.||High performance strained CMOS devices|
|US20050158955 *||Jan 16, 2004||Jul 21, 2005||International Business Machines Corporation||Method and apparatus to increase strain effect in a transistor channel|
|US20110198696 *||Feb 18, 2010||Aug 18, 2011||Globalfoundries Inc.||Finned semiconductor device with oxygen diffusion barrier regions, and related fabrication methods|
|US20120168881 *||Jan 27, 2011||Jul 5, 2012||Haizhou Yin||Semiconductor device and method for manufacturing the same|
|US20140346607 *||May 23, 2013||Nov 27, 2014||Taiwan Semiconductor Manufacturing Company, Ltd.||Tuning Tensile Strain on FinFET|
|U.S. Classification||257/274, 257/E21.633, 257/E21.549, 438/199, 257/E21.642|
|International Classification||H01L29/80, H01L21/8238, H01L31/109, H01L21/76, H01L31/112, H01L21/762|
|Cooperative Classification||H01L21/76232, H01L29/7846, H01L21/823878, H01L21/823807, H01L29/785|
|European Classification||H01L29/78R4, H01L21/762C6, H01L21/8238U, H01L21/8238C|