US 20050282313 A1
One or more stabilizers are disposed on the surface of a semiconductor device component prior to bonding the same to a higher-level substrate. The one or more stabilizers may be formed on or secured to the surface. Upon assembly of the semiconductor device component face down upon a higher-level substrate and joining conductive structures between the contact pads of the semiconductor device component and corresponding contact pads of the higher-level substrate, the stabilizers at least partially stabilize the semiconductor device component on the higher-level substrate to maintain a substantially parallel relation therebetween. The stabilizers can also be positioned and configured to define a minimum, substantially uniform distance between the semiconductor device component and the higher-level substrate.
1. A method for modifying a semiconductor die, comprising:
providing at least one semiconductor die having an active surface; and
disposing on the active surface at least one stabilizer, the at least one stabilizer comprising a plurality of adjacent, mutually adhered regions comprising a dielectric material and protruding from the active surface.
2. The method of
3. The method of
4. The method of
5. The method of
6. The method of
7. The method of
8. The method of
9. The method of
10. The method of
11. The method of
disposing at least one conductive structure on at least one bond pad of the at least one semiconductor die.
12. The method of
13. The method of
storing data including at least one physical parameter of the at least one substrate in computer memory, and using the stored data in conjunction with a machine vision system to recognize the location and orientation of the at least one substrate and to form the at least one stabilizer.
14. The method of
15. The method of
using stored data, in conjunction with the machine vision system, to selectively form the at least one stabilizer.
16. A method for electrically connecting a semiconductor die that includes a surface and conductive structures protruding from the surface to a substrate with contacts positioned correspondingly to the conductive structures, the method comprising:
disposing at least one stabilizer structure comprising a plurality of adjacent, mutually adhered regions, each comprising a dielectric material, on at least one of the surface and the substrate for positioning between the surface and the substrate;
inverting and positioning the semiconductor die on the substrate to contact the conductive structures to corresponding contacts; and
bonding the conductive structures to the corresponding contacts.
17. The method of
18. The method of
19. The method of
20. The method of
This application is a continuation of application Ser. No. 09/590,621, filed Jun. 8, 2000, pending.
1. Field of the Invention
The present invention relates generally to methods and structures for stabilizing a semiconductor device, such as a flip-chip type semiconductor die or a chip scale package (CSP), when disposed in face-down orientation over a carrier substrate, such as a circuit board. The stabilizer structures of the present invention are also useful for spacing a semiconductor device a substantially uniform desired distance away from the carrier substrate. More specifically, the invention pertains to stereolithographically fabricated stabilizers and to the use of stereolithographic methods to fabricate the stabilizers.
2. State of the Art
Flip-chip technology, including chip scale packaging technology, is widely used in the electronics industry. In both the generic flip-chip and the chip scale packaging technologies, a semiconductor device having a pattern of conductive pads on an active surface thereof is joined face down to a higher-level substrate, such as a printed circuit board. The contact pads of the higher-level substrate are arranged in a mirror image to corresponding contact pads on the semiconductor device. Conductive structures, typically solder bumps (as exemplified by the so-called C-4 technology), conductive epoxy bumps or pillars, conductor-filled epoxy, or an anisotropically conductive z-axis elastomer, join contact pads on the surface of the semiconductor device with their corresponding contact pads on the higher-level substrate, establishing electrical communication between the semiconductor device and the higher-level substrate.
When the semiconductor device is a flip-chip type semiconductor die, the spacing or pitch between adjacent contact pads, or bond pads, is relatively small. The contact pads themselves are also very small. State of the art flip-chip type semiconductor dice typically include many contact pads in an array on the active surfaces thereof. The high density, small feature size, and large number of conductive pads on state of the art semiconductor dice make the disposal of uniformly sized and configured conductive structures thereon a challenging process. Relatively small variations in the size or shape of the conductive structures can be accommodated during bonding of the conductive structures to the contact pads of the higher-level substrate. However, due to larger dimensional variations in the conductive structures on flip-chip type semiconductor dice, higher bonding temperatures or compressive forces are typically required to ensure the formation of adequate bonds between the bond pads of a flip-chip type semiconductor die and the corresponding contact pads of a higher-level substrate. The use of higher temperatures can damage the circuitry and other features of the semiconductor die, as well as impair the integrity of the conductive structures. Overcompression of the conductive structures can also be detrimental. When a compressed conductive structure spreads over and contacts the glass (e.g., borophosphosilicate glass (BPSG), phosphosilicate glass (PSG), or borosilicate glass (BSG)) passivation layer that typically surrounds the bond pads of a semiconductor die, thermal cycling of the semiconductor die during subsequent processing or in use can fracture the conductive structure and diminish the electrical conductivity thereof.
Moreover, some semiconductor dice have bond pads that are positioned in locations that will not adequately and stably support these dice when conductive structures are secured thereto and the dice are disposed face down (i.e., in a flip-chip orientation) over a higher-level substrate. Examples of such dice include leads over chip (LOC)-configured semiconductor dice and semiconductor dice with one or two rows of bond pads along the central axes of the dice with bond pads positioned adjacent only a single peripheral edge thereof. Thus, when conductive structures are secured to the bond pads of such a semiconductor die and the semiconductor die is then positioned face down relative to a higher-level substrate, the die is prone to being tipped or tilted from an intended orientation that is substantially parallel to a plane of the contact pad-bearing surface of the higher-level substrate. As a consequence, such dice are thought to be unsuitable for flip-chip applications without rerouting of the bond pads to a more stable arrangement. In addition, one or two rows of bond pads bearing solder bumps may not exhibit sufficient surface tension during reflow of the solder to support the die, resulting in collapse or flattening of the masses of molten solder and shorts of adjacent connections. Inadequate support strength may also be a problem with other materials.
State of the art chip scale packages also have numerous densely packed features of small sizes and are, therefore, susceptible to many of the same connection problems described above in reference to other flip-chip type semiconductor dice.
Bond pads 202 are typically connected to their corresponding contact pads 230 by way of conductive structures disposed between bond pads 202 and contact pads 230. The conductive structures illustrated in
As noted previously and illustrated in
When tipping or tilting occurs before bond pads 202 and contact pads 230 are joined by conductor structures 220, such as solder bumps, or other conductive structures, if the angle at which die 200 tips or tilts relative to carrier substrate 210 is great enough, bond pads 202 in one of the rows can be lifted away from contact pads 230 by a sufficient distance to break electrical connections therebetween.
Tilting or tipping of die 200 relative to carrier substrate 210 prior to bonding conductor structures 220, such as solder bumps, or other conductive structures between bond pads 202 and contact pads 230 can also result in an assembly with conductive structures of different heights and thicknesses. For example, conductor structures 220, such as solder bumps, can form a variety of nonuniform joints, some of which are shorter and thicker, while others are taller and thinner, than desired. As is well-known in the art, thermal stresses or inefficient thermal dissipation can cause failure of solder joints that are too short and thick or too tall and thin or of semiconductor devices joined by such solder joints. When a die 200 includes a combination of varied joints, the joints experience even greater stresses as die 200 heats and cools during operational cycling.
In addition, if die 200 tips or tilts too much relative to carrier substrate 210 prior to connecting bond pads 202 to contact pads 230, die 200 may contact carrier substrate 210 and cause an electrical short to occur.
If greater forces 222, 224 are applied to one edge 226, 228 of die 200 than to an opposite edge 226, 228 thereof after bond pads 202 have been connected to their corresponding contact pads 230 by way of conductive structures such as conductor structures 220, such as solder bumps, one or more of the conductive structures may break, disrupting the electrical connection between one or more of bond pads 202 and their corresponding contact pads 230. In addition, the application of such stresses may cause die 200 itself to tilt or fracture. Tilting or tipping of die 200 may also adversely affect the electrical characteristics of a system of which die 200 is a part.
Thus, it is apparent that a need exists for a method and apparatus for adequately stabilizing a semiconductor device, such as a semiconductor die or chip scale package bearing few conductive structures and/or bearing conductive structures in an inherently unstable arrangement, when disposed face down over a higher-level substrate, such as a carrier substrate. There is also a need for a method and structure that facilitate spacing a semiconductor device face down over a higher-level substrate a substantially uniform distance and that facilitate the maintenance of conductive structures in desired shapes and dimensions following the connection of the semiconductor device to the higher-level substrate by way of the conductive structures.
In the past decade, a manufacturing technique termed “stereolithography,” also known as “layered manufacturing,” has evolved to a degree where it is employed in many industries.
Essentially, stereolithography as conventionally practiced involves utilizing a computer to generate a three-dimensional (3-D) mathematical simulation or model of an object to be fabricated, such generation usually effected with 3-D computer-aided design (CAD) software. The model or simulation is mathematically separated or “sliced” into a large number of relatively thin, parallel, usually vertically superimposed layers, each layer having defined boundaries and other features associated with the model (and thus the actual object to be fabricated) at the level of that layer within the exterior boundaries of the object. A complete assembly or stack of all of the layers defines the entire object, and surface resolution of the object is, in part, dependent upon the thickness of the layers.
The mathematical simulation or model is then employed to generate an actual object by building the object, layer by superimposed layer. A wide variety of approaches to stereolithography by different companies has resulted in techniques for fabrication of objects from both metallic and nonmetallic materials. Regardless of the material employed to fabricate an object, stereolithographic techniques usually involve disposition of a layer of unconsolidated or unfixed material corresponding to each layer within the object boundaries, followed by selective consolidation or fixation of the material to at least a partially consolidated, or semisolid, state in those areas of a given layer corresponding to portions of the object, the consolidated or fixed material also at that time being substantially concurrently bonded to a lower layer. The unconsolidated material employed to build an object may be supplied in particulate or liquid form, and the material itself may be consolidated or fixed or a separate binder material may be employed to bond material particles to one another and to those of a previously formed layer. In some instances, thin sheets of material may be superimposed to build an object, each sheet being fixed to a next lower sheet and unwanted portions of each sheet removed, a stack of such sheets defining the completed object. When particulate materials are employed, resolution of object surfaces is highly dependent upon particle size, whereas when a liquid is employed, surface resolution is highly dependent upon the minimum surface area of the liquid which can be fixed and the minimum thickness of a layer that can be generated. Of course, in either case, resolution and accuracy of object reproduction from the CAD file is also dependent upon the ability of the apparatus used to fix the material to precisely track the mathematical instructions indicating solid areas and boundaries for each layer of material. Toward that end, and depending upon the layer being fixed, various fixation approaches have been employed, including particle bombardment (electron beams), disposing a binder or other fixative (such as by ink-jet printing techniques), or irradiation using heat or specific wavelength ranges.
An early application of stereolithography was to enable rapid fabrication of molds and prototypes of objects from CAD files. Thus, either male or female forms on which mold material might be disposed might be rapidly generated. Prototypes of objects might be built to verify the accuracy of the CAD file defining the object and to detect any design deficiencies and possible fabrication problems before a design was committed to large-scale production.
In more recent years, stereolithography has been employed to develop and refine object designs in relatively inexpensive materials and has also been used to fabricate small quantities of objects where the cost of conventional fabrication techniques is prohibitive for same, such as in the case of plastic objects conventionally formed by injection molding. It is also known to employ stereolithography in the custom fabrication of products generally built in small quantities or where a product design is rendered only once. Finally, it has been appreciated in some industries that stereolithography provides a capability to fabricate products, such as those including closed interior chambers or convoluted passageways, which cannot be fabricated satisfactorily using conventional manufacturing techniques. It has also been recognized in some industries that a stereolithographic object or component may be formed or built around another, pre-existing object or component to create a larger product.
However, to the inventors' knowledge, stereolithography has yet to be applied to mass production of articles in volumes of thousands or millions, or employed to produce, augment or enhance products including other, pre-existing components in large quantities, where minute component sizes are involved, and where extremely high resolution and a high degree of reproducibility of results is required. In particular, the inventor is not aware of the use of stereolithography to fabricate stabilizer or stabilization structures for use on semiconductor devices, such as flip-chip type semiconductor devices or ball grid array packages. Furthermore, conventional stereolithography apparatus and methods fail to address the difficulties of precisely locating and orienting a number of pre-existing components for stereolithographic application of material thereto without the use of mechanical alignment techniques or to otherwise assuring precise, repeatable placement of components.
The present invention includes stabilizers, which are also referred to herein as spacers, as support structures, or as outriggers, that are positionable on a surface of a semiconductor device, such as on the active surface of a semiconductor die to be disposed face down through use of projecting conductive structures over a higher-level substrate, as on the surface of a chip scale package from which conductive structures protrude. The stabilizers of the present invention may be used with semiconductor devices having bond pads arranged in such a manner that conductive structures, or elements, secured thereto will not adequately support the semiconductor device when disposed face down on a higher-level substrate.
Stabilizers incorporating teachings of the present invention are configured and located to, along with conductive structures, stabilize a semiconductor device when disposed face down over a higher-level substrate.
The stabilizers of the present invention may also be configured to maintain a substantially parallel relation between a carrier substrate and a semiconductor device to be disposed in a face-down orientation over the carrier substrate. Stabilizers are also configured to space the semiconductor device and the carrier substrate a minimum distance apart from one another during and after the electrical connection of contact pads of the semiconductor device to corresponding contact pads of the carrier substrate. The stabilizers are configured to support the semiconductor device in spaced apart relation on the carrier substrate before, during, and after electrical connections are established between the semiconductor device and the carrier substrate.
The stabilizers of the present invention may be configured as linear structures of substantially uniform height or as columns, bumps, or structures of other shapes that have substantially uniform maximum heights. The height of the stabilizers on a semiconductor device is preferably less than or equal to the distance a conductive structure, such as a conductive bump, ball, or pillar, will extend between the plane of a surface of the semiconductor device and the plane of the facing surface of the carrier substrate upon which the semiconductor device is to be disposed.
While one or more linearly configured stabilizers support a semiconductor device disposed upon a carrier substrate by traversing a portion of a surface of the semiconductor device, stabilizers of other configurations are positioned at locations relative to the surface of the semiconductor device that will provide the desired level of stability. For example, the stabilizers can be positioned at or near the comers of the surface of the semiconductor device, at or near the edges of the semiconductor device, or in an array over the surface of the semiconductor device.
Preferably, the stabilizers of the present invention are also configured to permit an insulative underfill material to flow into the space between the semiconductor device and the carrier substrate while preventing the occurrence of air pockets or other voids in the underfill material.
The stabilizers can be fabricated directly on a substrate (e.g., the semiconductor device, a wafer including a plurality of semiconductor devices, or a carrier substrate) or initially fabricated separately from the substrate, then positioned in desired locations on the surface of the substrate and secured thereto. When the stabilizers of the present invention are fabricated on a semiconductor die, the stabilizers can be fabricated on a single die, a collection of individual, singulated dice, or on a wafer including a plurality of unsingulated dice. The stabilizers can similarly be fabricated on other substrates, either singly or collectively.
The stabilizers of the invention can be made by various known methods for fabricating features of semiconductor devices. By way of example and not limitation, mask and etch processes can be used to fabricate the stabilizers from dielectric materials, photoresist material can be patterned to form the stabilizers, or the stabilizers can be die cut from a layer of dielectric material. In a preferred embodiment of the invention, stereolithography, or layered manufacturing, processes are employed to fabricate the stabilizers.
The present invention preferably employs computer-controlled, 3-D CAD initiated, stereolithography techniques to fabricate the stabilizers of the present invention. When stereolithographic processes are employed, the stabilizers are each formed as either a single layer or a series of superimposed, contiguous, mutually adhered layers of material.
When the stabilizers are fabricated directly on a substrate by use of stereolithography, the stabilizers can be fabricated to extend to a given plane regardless of any irregularities on or nonplanarity of the surface of the semiconductor device on which the stabilizers are fabricated.
The stereolithographic method of fabricating the stabilizers of the present invention preferably includes the use of a machine vision system to locate the semiconductor devices on which the stabilizers are to be fabricated, as well as the features or other components on or associated with the semiconductor devices (e.g., lead frames, bond wires, solder bumps, etc.). A machine vision system is preferably used to direct the alignment of a stereolithography system with the substrate for material disposition purposes. Accordingly, the substrate need not be precisely, mechanically aligned with respect to any component of the stereolithography system to practice the stereolithographic embodiment of the method of the present invention.
In a preferred embodiment, the stabilizers to be fabricated upon or positioned upon and secured to a substrate, such as a semiconductor die or chip scale package, in accordance with the invention are fabricated using precisely focused electromagnetic radiation in the form of an ultraviolet (UV) wavelength laser under control of a computer and responsive to input from a machine vision system, such as a pattern recognition system, to fix or cure selected regions of a layer of a liquid photopolymer material disposed on the substrate.
Other features and advantages of the present invention will become apparent to those of skill in the art through consideration of the ensuing description, the accompanying drawings, and the appended claims.
The accompanying drawings illustrate exemplary embodiments of the invention, wherein some dimensions may be exaggerated for the sake of clarity, and wherein:
FIGS. 10(A)-10(H) are partial perspective views of semiconductor devices having differently configured stabilizers secured to a surface thereof;
As depicted in
Substrate 20 includes contact pads 40, such as the terminals of printed circuit board, exposed at a surface 24 thereof. Contact pads 40 are positioned to correspond to the arrangement of bond pads 12 of semiconductor device 10. Solder bumps 30 protruding from bond pads 12 are therefore located so as to contact corresponding contact pads 40 upon assembly of semiconductor device 10 and substrate 20 in the manner shown in
As shown in
With continued reference to
Thus, stabilizers 50 may each protrude from active surface 14 a distance 54 that is less than or equal to the distance 60 that conductive structures, such as solder bumps 30, including the shortest solder bump 30B, will protrude from active surface 14, or the distance conductive structures extend between active surface 14 and surface 24. Accordingly, stabilizers 50 will not prevent the shortest conductive structure, such as solder bump 30B, from contacting a contact pad 40 during bonding of a conductive structure, such as during thermally reflowing a solder bump 30, to contact pad 40.
If the conductive material of the conductive structures, such as solder bumps 30, will sag when reflowed, stabilizers 50 may protrude from active surface 14 a greater distance 54 than the distance 60 that conductive structures, such as solder bumps 30, protrude from active surface 14. Such sagging of the conductive material during reflow facilitates the formation of electrical connections between bond pads 12 and contact pads 40 even when stabilizers 50 are taller than the conductive structures. Thus, the use of taller stabilizers 50 may facilitate the formation of taller, thinner conductive structures.
When semiconductor device 10 and substrate 20 are assembled and bond pads 12 are bonding to corresponding contact pads 40 by way of solder bumps 30 or other conductive structures, stabilizers 50 maintain a substantially uniform distance between active surface 14 of semiconductor device 10 and surface 24 of substrate 20. Stabilizers 50 also horizontally stabilize semiconductor device 10 relative to substrate 20.
Moreover, distance 54 that stabilizers 50 protrude from active surface 14 is preferably great enough so that, upon bonding bond pads 12 of semiconductor device 10 to contact pads 40 exposed at surface 24 of substrate 20, a minimum, substantially uniform distance can be maintained between active surface 14 and surface 24. Distance 54 is also preferably great enough to prevent overcompression of any of solder bumps 30 or other conductive structures during bonding.
While semiconductor device 10 is illustrated in
Referring again to
In addition, stabilizers 50 are configured to have sufficient strength and rigidity to maintain a substantially uniform minimum distance 28 between semiconductor device 10 and substrate 20 during the bonding of bond pads 12 of semiconductor device 10 to contact pads 40 of substrate 20. Stabilizers are also preferably configured to substantially maintain their configurations, dimensions, strength, and rigidity during any subsequent processing of the assembly of semiconductor device 10 and substrate 20, such as during the introduction of an underfill material therebetween, as well as during testing and normal operation of semiconductor device 10. Stabilizers 50 are also preferably configured to prevent tipping or tilting of semiconductor device 10 relative to substrate 20.
The configurations and locations of stabilizers 50 on active surface 14 preferably permit an underfill material having appropriate flow properties to flow into and fill the space between semiconductor device 10 and substrate 20 while preventing the occurrence of air pockets or other voids in the underfill material.
Although stabilizers 50 are depicted in
By way of example, and not to limit the scope of the present invention,
As stabilizers 50 are illustrated as contacting active surface 14 of semiconductor device 10 and since stabilizers 50 can also contact surface 24 of substrate 20, stabilizers 50 are preferably fabricated from a dielectric material. In addition, the material from which stabilizers 50 are fabricated may preferably be readily formed to precise dimensions and secured to the surface of a substrate, such as a semiconductor die or other semiconductor device substrate. Examples of such materials include plastics, photoimageable resins, silicon dioxide, glass (e.g., borophosphosilicate glass (“BPSG”), phosphosilicate glass (“PSG”), borosilicate glass (“BSG”)), and silicon nitride.
As shown in
Several different processes can be used to fabricate stabilizers 50 in accordance with teachings of the present invention. As an example, stabilizers 50 can be preformed from plastic, epoxy or other resins by known processes, such as by molding or micromachining processes. These stabilizers 50 are then secured to the surface of a semiconductor device 10 by known processes, such as by the use of an adhesive.
As another example, stabilizers 50 can be fabricated on the active surface 14 of a semiconductor device 10 by applying a layer of insulative material onto active surface 14 of semiconductor device 10 (e.g., by known deposition processes such as chemical vapor deposition (“CVD”) or spin-on-glass (“SOG”) processes) followed by removing unwanted portions of the layer (e.g., by use of photomask and etch processes).
In yet another example of a method that can be used to fabricate stabilizers 50, a photoresist material is applied to active surface 14 of semiconductor device 10. The photoresist is then masked, exposed, and developed to form stabilizers 50 in desired locations on active surface 14.
Stereolithographic processes are also useful for forming stabilizers 50. When stereolithographic processes are used, stabilizers 50 can have one or more layers of at least partially consolidated material. Stereolithographic processes can be used to fabricate stabilizers 50 in situ on semiconductor device 10 or test substrate, or separately therefrom.
Of the above methods, the stereolithographic process is currently the preferred embodiment of the method of the present invention and will, therefore, be discussed at length.
With reference again to
The data is preferably formatted in an STL (for STereoLithography) file, STL being a standardized format employed by a majority of manufacturers of stereolithography equipment. Fortunately, the format has been adopted for use in many solid-modeling CAD programs, so often translation from another internal geometric database format is unnecessary. In an STL file, the boundary surfaces of an object are defined as a mesh of interconnected triangles.
Apparatus 80 also includes a reservoir 84 (which may comprise a removable reservoir interchangeable with others containing different materials) of liquid material 86 to be employed in fabricating the intended object. In the currently preferred embodiment, the liquid is a photo-curable polymer, or “photopolymer,” that cures in response to light in the UV wavelength range. The surface level 88 of material 86 is automatically maintained at an extremely precise, constant magnitude by devices known in the art responsive to output of sensors within apparatus 80 and preferably under control of computer 82. A support platform or elevator 90, precisely vertically movable in fine, repeatable increments responsive to control of computer 82, is located for movement downward into and upward out of material 86 in reservoir 84.
An object may be fabricated directly on platform 90, or on a substrate disposed in platform 90. When the object is to be fabricated on a substrate disposed on platform 90, the substrate may be positioned on platform 90 and secured thereto by way of one or more base supports 122 (
Apparatus 80 has a UV wavelength range laser plus associated optics and galvanometers (collectively identified as laser 92) for controlling the scan of laser beam 96 in the X-Y plane across platform 90, which has associated therewith mirror 94 to reflect beam 96 downwardly as beam 98 toward surface 100 of platform 90. Beam 98 is traversed in a selected pattern in the X-Y plane, that is to say in a plane parallel to surface 100, by initiation of the galvanometers under control of computer 82 to at least partially cure, by impingement thereon, selected portions of material 86 disposed over surface 100 to at least a semisolid state. The use of mirror 94 lengthens the path of the laser beam, effectively doubling same, and provides a more vertical beam 98 than would be possible if the laser 92 itself were mounted directly above platform surface 100, thus enhancing resolution.
Referring now to
When one or more base supports 122 are to be stereolithographically fabricated, supports 122 may be programmed as a separate STL file from the other objects to be fabricated. The primary STL file for the object or objects to be fabricated and the STL file for base support(s) 122 are merged.
Before fabrication of a first layer for a support 122 or an object to be fabricated is commenced, the operational parameters for apparatus 80 are set to adjust the size (diameter if circular) of the laser light beam used to cure material 86. In addition, computer 82 automatically checks and, if necessary, adjusts by means known in the art, the surface level 88 of material 86 in reservoir 84 to maintain same at an appropriate focal length for laser beam 98. U.S. Pat. No. 5,174,931, referenced above and previously incorporated herein by reference, discloses one suitable level control system. Alternatively, the height of mirror 94 may be adjusted responsive to a detected surface level 88 to cause the focal point 148 of laser beam 98 to be located precisely at the surface of material 86 at surface level 88 if level 88 is permitted to vary, although this approach is more complex. Platform 90 may then be submerged in material 86 in reservoir 84 to a depth equal to the thickness of one layer or slice of the object to be formed, and the liquid surface level 88 is readjusted as required to accommodate material 86 displaced by submergence of platform 90. Laser 92 is then activated so laser beam 98 will scan unconsolidated (e.g., liquid or powdered) material 86 disposed over surface 100 of platform 90 to at least partially consolidate (e.g., polymerize to at least a semisolid state) material 86 at selected locations, defining the boundaries of a first layer 122A of base support 122 and filling in solid portions thereof. Platform 90 is then lowered by a distance equal to thickness of second layer 122B, and laser beam 98 scanned to define and fill in the second layer while simultaneously bonding the second layer to the first. The process may be then repeated, as often as necessary, layer by layer, until base support 122 is completed. Platform 90 is then moved relative to the mirror 94 to form any additional base supports 122 on platform 90 or a substrate disposed thereon or to fabricate objects upon platform 90, base support 122, or a substrate, as provided in the control software. The number of layers required to erect support 122 or other objects to be formed depends upon the height of the object to be formed and the desired layer thickness 108, 1 10. The layers of a stereolithographically fabricated structure with a plurality of layers may have different thicknesses.
If a recoater blade 102 is employed, the process sequence is somewhat different. In this instance, surface 100 of platform 90 is lowered into unconsolidated (e.g., liquid) material 86 below surface level 88 a distance greater than a thickness of a single layer of material 86 to be cured, then raised above surface level 88 until platform 90, a substrate disposed thereon, or a structure being formed on platform 90 or a substrate is precisely one layer's thickness below blade 102. Blade 102 then sweeps horizontally over platform 90 or (to save time) at least over a portion thereof on which one or more objects are to be fabricated to remove excess material 86 and leave a film of precisely the desired thickness. Platform 90 is then lowered so that the surface of the film and surface level 88 are coplanar and the surface of the unconsolidated material 86 is still. Laser 92 is then initiated to scan with laser beam 98 and define the first layer 130. The process is repeated, layer by layer, to define each succeeding layer 130 and simultaneously bond same to the next lower layer 130 until all of the layers of the object or objects to be fabricated are completed. A more detailed discussion of this sequence and apparatus for performing same is disclosed in U.S. Pat. No. 5,174,931, previously incorporated herein by reference.
As an alternative to the above approach to preparing a layer of material 86 for scanning with laser beam 98, a layer of unconsolidated (e.g., liquid) material 86 may be formed on surface 100 of support platform 90, on a substrate disposed on platform 90, or on one or more objects being fabricated by lowering platform 90 to flood material over surface 100, over a substrate disposed thereon, or over the highest completed layer of the object or objects being formed, then raising platform 90 and horizontally traversing a so-called “meniscus” blade horizontally over platform 90 to form a layer of unconsolidated material having the desired thickness over platform 90, the substrate, or each of the objects being formed. Laser 92 is then initiated and a laser beam 98 scanned over the layer of unconsolidated material to define at least the boundaries of the solid regions the next higher layer.
Yet another alternative to layer preparation of unconsolidated (e.g., liquid) material 86 is to merely lower platform 90 to a depth 87 equal to that of a layer of material 86 to be scanned, and to then traverse a combination flood bar and meniscus bar assembly horizontally over platform 90, a substrate disposed on platform 90, or one or more objects being formed to substantially concurrently flood material 86 thereover and to define a precise layer thickness of material 86 for scanning.
All of the foregoing approaches to liquid material flooding and layer definition and apparatus for initiation thereof are known in the art and are not material to practice of the present invention, so no further details relating thereto will be provided herein.
In practicing the present invention, a commercially available stereolithography apparatus operating generally in the manner as that described above with respect to apparatus 80 of
By way of example and not limitation, the layer thickness of material 86 to be formed, for purposes of the invention, may be on the order of about 0.0001 to 0.0300 inch, with a high degree of uniformity. It should be noted that different material layers may have different heights, so as to form a structure of a precise, intended total height or to provide different material thicknesses for different portions of the structure. The size of the laser beam “spot” or focal point 148 impinging on the surface of material 86 to cure same may be on the order of 0.001 inch to 0.008 inch. Resolution is preferably ±0.0003 inch in the X-Y plane (parallel to surface 100) over at least a 0.5 inch×0.25 inch field from a center point, permitting a high resolution scan effectively across a 1.0 inch×0.5 inch area. Of course, it is desirable to have substantially this high a resolution across the entirety of surface 100 of platform 90 to be scanned by laser beam 98, such area being termed the “field of exposure,” such area being substantially coextensive with the vision field of a machine vision system employed in the apparatus of the invention as explained in more detail below. The longer and more effectively vertical the path of laser beam 96/98, the greater the achievable resolution.
Referring again to
It is noted that a variety of machine vision systems are in existence, examples of which and their various structures and uses are described, without limitation, in U.S. Pat. Nos. 4,526,646; 4,543,659; 4,736,437; 4,899,921; 5,059,559; 5,113,565; 5,145,099; 5,238,174; 5,463,227; 5,288,698; 5,471,310; 5,506,684; 5,516,023; 5,516,026; and 5,644,245. The disclosure of each of the immediately foregoing patents is hereby incorporated by this reference.
In order to facilitate fabrication of one or more stabilizers 50 in accordance with the method of the present invention with apparatus 80, a data file representative of the size, configuration, thickness and surface topography of, for example, a particular type and design of semiconductor device 10 or other substrate upon which one or more stabilizers 50 are to be mounted, is placed in the memory of computer 82. Also, if it is desired that the stabilizers 50 be so positioned on semiconductor device 10 taking into consideration features of substrate 20 (see
One or more semiconductor devices 10, or a wafer 72 (see
Camera 140 is then activated to locate the position and orientation of each semiconductor device 10, including those of a wafer 72 (
Continuing with reference to
Laser 92 is then activated and scanned to direct beam 98, under control of computer 82, toward specific locations of surface level 88 relative to each semiconductor device 10 to effect the aforementioned partial cure of material 86 to form a first layer 50A of each stabilizer 50. Platform 90 is then lowered into reservoir 84 and raised a distance equal to the desired thickness of another layer 130 of each stabilizer 50, and laser 92 is activated to add another layer 130 to each stabilizer 50 under construction. This sequence continues, layer by layer, until each of the layers of stabilizers 50 have been completed.
Each layer 130 of stabilizer 50 is preferably built by first defining any internal and external object boundaries of that layer 130 with laser beam 98, then hatching solid areas of stabilizer 50 located within the object boundaries with laser beam 98. An internal boundary of a layer 130 may comprise a through-hole, a void, or a recess in stabilizer 50, for example. If a particular layer 130 includes a boundary of a void in the object above or below that layer 130, then laser beam 98 is scanned in a series of closely spaced, parallel vectors so as to develop a continuous surface, or skin, with improved strength and resolution. The time it takes to form each layer 130 depends upon its geometry, the surface tension and viscosity of material 86, and the thickness of the layer.
Alternatively, stabilizers 50 may each be formed as a partially cured outer skin extending above active surface 14 of semiconductor device 10 and forming a dam within which unconsolidated material 86 can be contained. This may be particularly useful where the stabilizers 50 protrude a relatively high distance 54 from active surface 14. In this instance, support platform 90 may be submerged so that material 86 enters the area within the dam, raised above surface level 88, 88A, 88B and then laser beam 98 activated and scanned to at least partially cure material 86 residing within the dam or, alternatively, to merely cure a “skin” comprising the contact surface 52, a final cure of the material of the stabilizers 50 being effected subsequently by broad-source UV radiation in a chamber, or by thermal cure in an oven. In this manner, stabilizers 50 of extremely precise dimensions may be formed of material 86 by apparatus 80 in minimal time.
Once stabilizers 50, or at least the outer skins thereof, have been fabricated, platform 90 is elevated above surface level 88 of material 86 and platform 90 is removed from apparatus 80, along with any substrate (e.g., semiconductor device 10 or wafer 72 (see
Stabilizers 50 and semiconductor device 10 may also be cleaned by use of known solvents that will not substantially degrade, deform, or damage stabilizers 50 or a substrate to which stabilizers 50 are secured.
As noted previously, stabilizers 50 may then require postcuring. Stabilizers 50 may have regions of unconsolidated material contained within a boundary or skin thereof, or material 86 may be only partially consolidated (e.g., polymerized or cured) and exhibit only a portion (typically 40% to 60%) of its fully consolidated strength. Postcuring to completely harden stabilizers 50 may be effected in another apparatus projecting UV radiation in a continuous manner over stabilizers 50 or by thermal completion of the initial, UV-initiated partial cure.
It should be noted that the height, shape, or placement of each stabilizer 50 on each specific semiconductor device 10 may vary, again responsive to output of camera 140 or one or more additional cameras 144 or 146, shown in
While a variety of methods may be used to fabricate stabilizers 50, the use of a stereolithographic process as exemplified above is a preferred method because a large number of stabilizers 50 may be fabricated in a short time, the stabilizer height and position are computer-controlled to be extremely precise, wastage of unconsolidated material 86 is minimal, solder coverage of passivation materials is reliably avoided through precise spacer height control, and the stereolithography method requires less handling of semiconductor devices 10 or other substrates than the other viable methods indicated above.
Stereolithography is also an advantageous method of fabricating stabilizers 50 according to the present invention since stereolithography can be conducted at substantially ambient temperature, the small spot size and rapid traverse of laser beam 98 resulting in negligible thermal stress upon the semiconductor devices 10, other substrates, or the features thereof.
Moreover, as disclosed herein, the stereolithography method of the present invention recognizes specific semiconductor devices 10 or other substrates, so that variations between individual substrates are accommodated. In addition, as shown in
While the present invention has been disclosed in terms of certain preferred embodiments, those of ordinary skill in the art will recognize and appreciate that the invention is not so limited. Additions, deletions and modifications to the disclosed embodiments may be effected without departing from the scope of the invention as claimed herein. Similarly, features from one embodiment may be combined with those of another while remaining within the scope of the invention.