US 20060276907 A1
The present invention relates to an implant comprising two or more bone fragments that are combined to form a single unit. Cancellous bone or cortical bone is removed from a source and fashioned into bone components with desirable shapes and sizes. The bone components may be integrated to form implants for implantation in the body. Bone stock may be formed by combining sections of various bones of the body, and the bone stock may be further fashioned for use as implants with particular geometries.
1. An implant comprising a body having two outer annular members and at least one inner annular member, wherein at least one of the annular members is formed from bone and the annular members are coupled together to define a central chamber.
2. The implant of
3. The implant of
4. The implant of
5. The implant of
6. The implant of
7. The implant of
8. The implant of
9. The implant of
10. The implant of
11. The implant of
12. The implant of
13. The implant of
14. The implant of
15. The implant of
16. The implant of
17. The implant of
18. The implant of
19. The implant of
20. The implant of
The benefit of Provisional Application No. 60/191,099 filed Mar. 22, 2000 is claimed under 35 U.S.C. § 119(e).
The invention relates to an implant for orthopedic applications. More particularly, the invention is related to an implant formed from two or more bone portions.
Bone grafts have become an important and accepted means for treating bone fractures and defects. In the United States alone, approximately half a million bone grafting procedures are performed annually, directed to a diverse array of medical interventions for complications such as fractures involving bone loss, injuries or other conditions necessitating immobilization by fusion (such as for the spine or joints), and other bone defects that may be present due to trauma, infection, or disease. Bone grafting involves the surgical transplantation of pieces of bone within the body, and generally is effectuated through the use of graft material acquired from a human source. This is primarily due to the limited applicability of xenografts, transplants from another species.
Orthopedic autografts or autogenous grafts involve source bone acquired from the same individual that will receive the transplantation. Thus, this type of transplant moves bony material from one location in a body to another location in the same body, and has the advantage of producing minimal immunological complications. It is not always possible or even desirable to use an autograft. The acquisition of bone material from the body of a patient typically requires a separate operation from the implantation procedure. Furthermore, the removal of material, oftentimes involving the use of healthy material from the pelvic area or ribs, has the tendency to result in additional patient discomfort during rehabilitation, particularly at the location of the material removal. Grafts formed from synthetic material have also been developed, but the difficulty in mimicking the properties of bone limits the efficacy of these implants.
As a result of the challenges posed by autografts and synthetic grafts, many orthopedic procedures alternatively involve the use of allografts, which are bone grafts from other human sources (normally cadavers). The bone grafts, for example, are placed in a host bone and serve as the substructure for supporting new bone tissue growth from the host bone. The grafts are sculpted to assume a shape that is appropriate for insertion at the fracture or defect area, and often require fixation to that area as by screws or pins. Due to the availability of allograft source material, and the widespread acceptance of this material in the medical community, the use of allograft tissues is certain to expand in the field of musculoskeletal surgery.
Sections of bones with regions having narrow cross-sections, as seen for example with thicknesses X1 and X3, may be rejected for use in certain applications because the wall thickness does not have sufficient strength. Preferably, no region of a bone section has a thickness less than 5 millimeters, although in some applications smaller wall thicknesses may be employed. Thus, in the case that a bone section is found to have a region with a wall thickness less than a minimum acceptable thickness, such a bone section is rejected as being unsuitable for use in a bulk configuration. Often, such a section is ground into bone particulate that is then used in other applications. The minimum thickness standards imposed on the use of bone sections results in the rejection of substantial quantities of bone sections, and thus an inefficient use of the material. Bone sections that do not meet the minimum thickness standards are often found in older individuals.
As a collagen-rich and mineralized tissue, bone is composed of about forty percent organic material (mainly collagen), with the remainder being inorganic material (mainly a near-hydroxyapatite composition resembling 3Ca3(PO4)2.Ca(OH)2). Structurally, the collagen assumes a fibril formation, with hydroxyapatite crystals disposed along the length of the fibril, and the individual fibrils are disposed parallel to each other forming fibers. Depending on the type of bone, the fibrils are either interwoven, or arranged in lamellae that are disposed perpendicular to each other.
There is little doubt that bone tissues have a complex design, and there are substantial variations in the properties of bone tissues with respect to the type of bone (i.e., leg, arm, vertebra) as well as the overall structure of each type. For example, when tested in the longitudinal direction, leg and arm bones have a modulus of elasticity of about 17 to 19 GPa, while vertebra tissue has a modulus of elasticity of less than 1 GPa. The tensile strength of leg and arm bones varies between about 120 MPa and about 150 MPa, while vertebra have a tensile strength of less than 4 MPa. Notably, the compressive strength of bone varies, with the femur and humerus each having a maximum compressive strength of about 167 MPa and 132 MPa respectively. Again, the vertebra have a far lower compressive strength of no more than about 10 MPa.
With respect to the overall structure of a given bone, the mechanical properties vary throughout the bone. For example, a long bone (leg bone) such as the femur has both compact bone and spongy bone. Cortical bone, the compact and dense bone that surrounds the marrow cavity, is generally solid and thus carries the majority of the load in major bones. Cancellous bone, the spongy inner bone, is generally porous and ductile, and when compared to cortical bone is only about one-third to one-quarter as dense, one-tenth to one-twentieth as stiff, but five times as ductile. While cancellous bone has a tensile strength of about 10-20 MPa and a density of about 0.7, cortical bone has a tensile strength of about 100-200 MPa and a density of about 2. Additionally, the strain to failure of cancellous bone is about 5-7%, while cortical bone can only withstand 1-3% strain before failure. It should also be noted that these mechanical characteristics may degrade as a result of numerous factors such as any chemical treatment applied to the bone material, and the manner of storage after removal but prior to implantation (i.e. drying of the bone).
Notably, implants of cancellous bone incorporate more readily with the surrounding host bone, due to the superior osteoconductive nature of cancellous bone as compared to cortical bone. Furthermore, cancellous bone from different regions of the body is known to have a range of porosities. Thus, the design of an implant using cancellous bone may be tailored to specifically incorporate material of a desired porosity.
It is essential to recognize the distinctions in the types and properties of bones when considering the design of implants. Surgeons often work with bones using similar tools as would be found in carpentry, adapted for use in the operating room environment. This suggests that bones have some properties which are similar to some types of wood, for example ease in sawing and drilling. Notably, however, are many differences from wood such as the abrasive nature of hydroxyapatite and the poor response to local heating during machining of a bone. The combination of tensile and compressive strengths found in bone, resulting from the properties of the collagen and hydroxyapatite, is thus more aptly compared to the tensile and compressive strengths found in reinforced concrete, due to steel and cement. Furthermore, while wood is readily available in considerable quantity, bone material is an extremely limited resource that must be used in an extremely efficient manner.
Various types of bone grafts are known. For example, as disclosed in U.S. Pat. No. 5,989,289 to Coates et al., a spinal spacer includes a body formed of a bone composition such as cortical bone. The spacer has walls that define a chamber that is sized to receive an osteogenic composition to facilitate bone growth.
U.S. Pat. No. 5,899,939 to Boyce et al. discloses a bone-derived implant for load-supporting applications. The implant has one or more layers of fully mineralized or partially demineralized cortical bone and, optionally, one or more layers of some other material. The layers constituting the implant are assembled into a unitary structure, as by joining layers to each other in edge-to-edge fashion in a manner analogous to planking.
Another bone-grafting material is disclosed in U.S. Pat. No. 4,678,470 to Nashef et al., and is formed using a tanning procedure involving glutaraldehyde that renders the material osteoinvasive. A bone block is shaped into a precise predetermined form and size using conventional machining techniques. A paste-like suspension is also formed using known methods of comminuting bone, such as milling, grinding, and pulverizing, and adding the pulverized or powdered bone to a carrier. The treatment with glutaraldehyde allows the use of bovine, ovine, equine, and porcine bone sources. However, if the final desired form of the bone grafting material is a block of bone or machined shape, the bone stock must be large enough to provide a block of the required size. U.S. Pat. No. 5,981,828 to Nelson et al. discloses a “composite” acetabular allograft cup for use in hip replacement surgery. A press is used to form the cup from impacted cancellous bone chips and cement. The composite is a hollow hemispherical dome having an outer surface comprised essentially of exposed cancellous bone chips and an inner surface comprised essentially of hardened bone cement. The cancellous bone chips are first placed in a mold and subjected to a load to form a compact and consolidated mass that conforms to the shape of the mold. The mold is then opened, cement is applied, and the mold is then reapplied. While an allograft of a particular shape may be formed using this process, the process is limited to forming an allograft by compressing cancellous bone chips. Thus, numerous molds are required in order to produce allografts of different sizes, and the use of bulk-size allograft source material is not facilitated.
With a rapidly increasing demand in the medical profession for devices incorporating bone material, the tremendous need for the tissue material itself, particularly allograft tissue material, presents a considerable challenge to the industry that supplies the material. Due to the size and shape of the bones from which the material is harvested, and the dimensional limitations of any particular type of bone in terms of naturally occurring length and thickness (i.e. cortical or cancellous), there is a need for a means by which individual bone fragments can be combined to form larger, integral implants that are more suitable for use in areas of larger fractures or defects. For example, the size of cortical bone fragments needed to repair a fracture or defect site is often not available in a thick enough form. While multiple fragments may together meet the size and shape requirements, several prominent concerns have placed a practical limitation on the implementation of this concept. There is considerable uncertainty regarding the structural integrity provided by fragments positioned adjacent to one another without bonding or other means of securing the fragments to each other. Moreover, there is concern over the possibility that a fragment may slip out of position, resulting in migration of the fragment and possible further damage in or near the area of implantation.
In addition, due to the geometry of bones such as the femur and tibia, all portions of the bones are not readily usable as a result of size limitations. Thus, prior art implants, specifically allografts, are produced with an inefficient use of source bones.
There is a need for new, fundamental approaches to working with and processing tissues, in particular allograft material, especially with regard to machining, mating, and assembling bone fragments. Specifically, there is a need for an implant that allows more efficient use of source material. More specifically, there is a need for an implant that is an integrated implant comprising two or more bone fragments that are interlocked to form a mechanically effective, strong unit.
The present invention is related to an implant including a body having an inner sheath and at least one outer sheath. Each sheath is formed from a different bone and has an interior surface and an exterior surface. The exterior surface of each outer sheath contacts the interior surface of no more than one other outer sheath. In one embodiment, a core is disposed in the inner sheath and is formed from a bone other than the bones of the sheaths. The core can be formed of cancellous bone, while at least one sheath can be formed of cortical bone. In another embodiment, at least one sheath can be formed of cancellous bone and the core can be formed of cortical bone. The bones are at least one of autograft, allograft, and xenograft bone tissue, and the bone tissue of at least one bone may be partially demineralized or demineralized. In a further embodiment, the body is formed from a cross-section of the sheaths and core, with the cross-section including at least a portion of each sheath and core. The sheaths and core can be coupled together with at least one fastener that may intersect each of the sheaths and core, with the fastener being a screw, key, pin, peg, rivet, cotter, nail, spike, bolt, stud, staple, boss, clamp, clip, dowel, stake, hook, anchor, tie, band, crimp, or wedge. Also, the sheaths and core can be bonded together with a bonding agent. At least one sheath may be packed with bone growth materials and may include alignment indicia. The exterior surface may be separated from a portion of the interior surface.
At least one of the inner sheath, an outer sheath, and the core can be at least partially dehydrated to fit against a surrounding mating surface. Furthermore, at least one of the inner sheath, an outer sheath, and the core can be at least partially dehydrated to fit within a surrounding inner sheath or outer sheath provided with a greater moisture content.
Contacting surfaces of adjacent sheaths can be machined surfaces so that the contour of the contacting surfaces is about the same. The machined surfaces permit press-fitting of one sheath into another sheath. In some embodiments, the bones are selected from a femur, tibia, humerus, fibula, ulna, and radius.
At least one supplemental sheath having an interior surface and an exterior surface also may be included, with the exterior surface of each supplemental sheath contacting the interior surface of no more than one other sheath and the interior surface of each supplemental sheath contacting the exterior surface of no more than one other sheath. The at least one supplemental sheath is formed of a material selected from metals, alloys, ceramics, polymers, and composites.
The present invention is also related to an implant having a body formed from a cross-section of a core and a plurality of sheaths. Each sheath has an inner surface and an outer surface, and at least two sheaths are formed from different bones. The outer surface of a first sheath has about the same contour as the inner surface of a second sheath so that the first and second sheaths mate together, and the cross-section includes at least a portion of each sheath and core. The core may be formed from a bone other than the bones of the sheaths, and in one embodiment the core is formed of cancellous bone and at least one sheath is formed of cortical bone. In another embodiment, at least one sheath is formed of cancellous bone and the core is formed of cortical bone.
Also, the present invention is related to an implant with a body that includes at least one sheath defining a hole, with a core fit therein. The body is formed from at least two different bones selected from a femur, tibia, humerus, fibula, ulna, and radius.
Furthermore, the present invention is related to an implant with a body having two outer annular members and at least one inner annular member. At least one of the annular members is formed from bone and the annular members are coupled together to create a central chamber. In one embodiment, each annular member has at least one surface that is press-fit with the surface of another annular member. The outside diameter of the outer annular members may be smaller than the outside diameter of the at least one inner annular member. The implant can be symmetrical about an innermost annular member, with the diameter of the implant progressively decreasing from the innermost annular member to each outer annular member. The central chamber can be packed with at least one of bone material and bone inducing substances.
In one embodiment, at least one annular member is formed of cancellous bone and at least one annular member is formed of cortical bone. A plurality of annular members may be coupled together with at least one fastener. Also, a plurality of annular members may be bonded together with a bonding agent. In some embodiments, the annular members have non-circular shapes, such as generally oblong shapes. At least one supplemental annular member may be coupled to at least one of the annular members formed from bone, with the at least one supplemental annular member being formed of a material selected from metals, alloys, ceramics, polymers, and composites. At least one annular member may include alignment indicia, and adjacent surfaces of at least two annular members may not completely contact each other.
The invention further relates to an implant with a body having at least two ring-shaped members formed from bone that are coupled together to create a central chamber. The ring-shaped members may have ridges that mate and press-fit together.
Another implant of the present invention includes at least two layers of bone components coupled to each other, the components together defining at least one securing region, and at least one insertable securing element adapted for placement in the at least one securing region. The at least one securing region may be a recess or hole, and each layer may be formed from a different bone selected from a femur, tibia, humerus, fibula, ulna, and radius. At least one layer may be formed of cancellous bone and at least one layer may be formed of cortical bone. Also, the layers may include at least one of autograft, allograft, and xenograft bone tissue, and the layers may be bonded together with a bonding agent. The bone tissue of at least one bone may be partially demineralized or demineralized, and the layers may be bonded together with a bonding agent. A first layer may be at least partially dehydrated to mate against at least one other layer. Adjacent layers may be provided with mutually contacting surfaces that are machined to have about the same contour, and the contacting surfaces of adjacent layers may be press-fit together.
In addition, the implant may further include at least one supplemental layer coupled to at least one of the layers of bone components, with the at least one supplemental layer being formed of a material selected from metals, alloys, ceramics, polymers, and composites. Also, the implant may further include a chamber packed with bone growth materials. In some embodiments, at least one layer includes alignment indicia, and the outer surface may be separated from a portion of the inner surface.
The present invention is further related to a hollow body having a minimum wall thickness, the body being formed from a plurality of portions of bone sections with each section having a thick-walled portion and a thin-walled portion. The thick-walled portion has a wall thickness at least as thick as the minimum wall thickness, and the thin-walled section has a wall thickness less than the minimum wall thickness. Only thick-walled portions are coupled together to form the body. The thick-walled portions are coupled together with at least one portion having a first coupling and at least one portion having a second coupling, with the portions being joined together by interfitting together the first and second couplings. At least one coupling may be at least partially dehydrated to mate against another coupling. In one embodiment, the first coupling is a male coupling and the second coupling is a female coupling so that the portions are mated in a male-female relationship. The male coupling may be a tenon and the female coupling may be a mortise, or the male coupling may be a tongue and the female coupling may be a groove.
The present invention is also related to an implant including a layer formed of a first bone and at least one layer formed by a curable carrier, with the at least one layer being molded to the first bone. The layer formed of a first bone may include a primary sleeve with a top surface, a bottom surface, an inner surface, and an outer surface, with the at least one layer of curable carrier being molded to the inner surface or the outer surface. In one embodiment, the curable carrier further includes bone or ceramic in powder, chips, or fibers. At least one secondary sleeve may be provided, with each secondary sleeve being coupled to a primary sleeve or another secondary sleeve by a layer of curable carrier.
Additionally, the present invention is related to a method of forming an implant including: surrounding at least a portion of a bone section with a first mold to create a cavity therebetween; filling the cavity with a first substance, and coupling the first substance to the bone section. The first substance may be at least one of a curable carrier, bone powder, bone chips bone fibers, or ceramic, and be coupled to the bone section by curing or by compaction.
Preferred features of the present invention are disclosed in the accompanying drawings, wherein similar reference characters denote similar elements throughout the several views, and wherein:
Any of a wide variety of different implant structures, particularly allograft, autograft, and/or xenograft implant structures, can be prepared according to the teachings of the present invention. While a representative selection of implant structures are described and depicted herein, additional disclosure is found in U.S. Provisional Application No. 60/191,099 filed Mar. 22, 2000, which is hereby incorporated herein in its entirety by reference, including all figures.
The present invention allows a more efficient use of bone sections, by permitting those sections that would otherwise have been rejected due to insufficient wall thickness to instead be incorporated in a composite bone section. The composite implant is created by taking two or more bone sections and combining them to create a greater wall thickness. Some or all of the natural shape of each bone may be retained. Furthermore, the composite may be formed of a shape appropriate for implantation, or instead may be formed of a shape that is suitable as bone stock for eventual fashioning into a particular implant or forms.
As used in the description of the present invention, the words fitting, interfitting, mating, locking, interlocking, meshing, and interlacing are all used generically to describe the joining of bone sections or pieces together. Thus, these words are not limited to the use of any particular manner of joining. Thus, for example, the press-fitting of one bone section within a cavity formed in another bone section may be described using any of the above-mentioned terms. In addition, although various preferred mechanical fastening approaches are described, the present invention allows the use of any mechanical device for joining two or more separate parts of an article or structure. Such mechanical devices include, but are not limited to the following: screws, keys, pins, pegs, rivets, cotters, nails, spikes, bolts, studs, staples, bosses, clamps, clips, dowels, stakes, hooks, anchors, ties, bands, and crimps. Also, bonding agents or other chemical means for joining two separate parts may be employed alone or in combination with the mechanical devices. Thus, as appropriate, the means disclosed herein for fixing bone sections to each other may be substituted, as with the above-mentioned mechanical devices, bonding devices, or chemical means. Furthermore, although particular types of joints are disclosed, the present invention is directed to the creation of implants that may be joined using other joints.
While the present invention is preferably directed to the creation of implants from allograft material, the present invention may also be applied to implants that utilize other materials, including but not limited to the following: xenograft, autograft, metals, alloys, ceramics, polymers, composites, and encapsulated fluids or gels. Furthermore, the implants described herein may be formed of materials with varying levels of porosity, such as by combined bone sections from different bones or different types of tissue having varying levels of porosity. For example, cancellous bone is available in a range of porosities based on the location in the body from which the bone is harvested. Extremely porous cancellous bone may be harvested from various areas such as the iliac crest, while less porous bone may be harvested from areas such as a tibial condyle. Thus, the materials properties—particularly the porosity—of the bone components may be selected to meet the needs of a given application.
Cancellous bone components may be attached to syringes or aspirators, and blood or other fluids such as bone-growth inducing substances may be drawn into the plugs. The use of mechanically applied pressure, such as with aspiration devices, permits a greater degree of fluid absorption and/or concentration to be achieved than otherwise readily obtainable by soaking bone in such fluids without applying pressure from a device. In embodiments of the present invention that include hollow regions, a plug of cancellous bone formed using the aforementioned technique may be inserted therein. Alternatively, the plugs may be soaked in a suitable fluid.
Also, the implants described herein may be formed of bone materials with varying mineral content. For example, cancellous or cortical bone may be provided in natural, partially demineralized, or demineralized states. Demineralization is typically achieved with a variety of chemical processing techniques, including the use of an acid such as hydrochloric acid, chelating agents, electrolysis or other treatments. The demineralization treatment removes the minerals contained in the natural bone, leaving collagen fibers with bone growth factors including bone morphogenic protein (BMP). Variation in the mechanical properties of bone sections is obtainable through demineralization. Advantageously, use of a demineralizing agent on natural bone transforms the properties of the bone from a stiff structure to a relatively pliable structure when it is hydrated. Some portions of interfitting bone components may be demineralized in order to achieve improved interfitting. For example, a tissue form may include two bone components having portions that are coupled together with an interference fit. The interference fit may be enhanced if the surface region of one or more of the components is demineralized so that it is pliable and exhibits some elasticity and/or malleability.
In addition, while many of the embodiments described herein show bone components disposed at right angles, or joints formed with right angles, angles that are greater or less than ninety degrees may alternatively be used in implants of the present development.
The components that are used to create implant 16 may all be formed from cortical bone, all from cancellous bone, or a combination of components formed from cortical and cancellous bone. The interfitting of the components may be achieved through a variety of means, including but not limited to the following: pinning, bonding with a suitable bone bonding agent or chemical means, press fitting, threadably engaging (as by helically screwing one component into another), inserting a tapered component into a component with a matching inner surface, twist-locking, or other interlocking means such as will be described in other embodiments. While the present development preferably allows the creation of an implant 16 from all bone material, it is also anticipated that one or more components used to create implant 16 may be formed of non-bone material such as a synthetic or other material.
As shown in
The moisture content of the bone sections also may be varied to advantageously permit improved interlocking. Bone sections initially may be provided with moisture content as follows: (1) bone in the natural state fresh out of the donor without freezing, (2) bone in the frozen state, typically at −40° C., with moisture content intact, (3) bone with moisture removed such as freeze-dried bone, and (4) bone in the hydrated state, such as when submersed in water. The expansion and contraction properties that can be obtained from bone during heating, cooling, dehydrating, and hydrating permit an alternate approach to achieving a tight press-fit. In addition, the use of such approaches can provide a tighter press-fit than otherwise obtainable, as well as loosen the manufacturing tolerances required for mating sections of bone.
For example, in the embodiment shown in
Turning to FIGS. 1J-K, a hole 23 of similar dimension may be created in each bone section, and when the holes are aligned to be coaxial, a pin 24 may be inserted in the holes 23 for fixation. Alternatively, the bone sections may have a slot formed therethrough, similar in orientation to pin 24, and a key can be inserted or press-fitted into the slot to fix the sections with respect to each other. Other bones may also be used, for example an ulna (lower arm) is similar in configuration to radius 13, and thus may be readily substituted. In addition, a fibula can also be readily used in some embodiments, accounting for the size of the bone and any required machining. Also, although the embodiment shown in
Bone stock 25′ is preferably solid, and formed by fitting a smaller diameter bone core within at least one larger diameter sheath. Thus, the availability of precisely machined cores and sheaths permits bone stock 25′ to be sized according to the application or anatomy encountered in any given situation. In addition, implants may be constructed from a supply of standardized core and sheath sizes or bone stock sizes so that any required wall thickness can be obtained. The ability to create composite implants of varying sizes has widespread use, particularly in applications such as femoral ring allografts which can benefit from increased wall thicknesses.
In alternate embodiments of bone stock 25′, components having non-circular shape may be provided, although not necessarily the natural shape of the original bone. For example, an outer sheath can mate with an inner sheath which has a generally triangular shape, with the inside surface of the outer sheath geometrically conforming to the outside surface of inner sheath. Other polygonal shapes are also contemplated, including parallelograms such as rectangles. In addition, a core may be provided with a shape distinct from both the cylindrical outside surface of the outer sheath and the outside surface of the inner sheath. Thus, the present development permits components with varying outside surface shapes to be interfit to create an implant.
The availability of larger bone stock, as by combining several bone sections, makes it possible to create implants that are properly configured for implantation during a wide variety of procedures. For example, anterior interbody fusion is a surgical procedure which replaces some or all of a disc with a bony graft (implant) by using an anterior approach to the disc. Such a procedure is typically employed in the cervical spine, and implantation of an implant is an effective modality for the treatment of such conditions as degenerative disc disease and herniated nucleus pulposus (slipped disc). Anterior interbody fusion is also used in the lumbar spine in cases of unsuccessful posterior approaches, or in procedures directed to destroyed or damaged facet joints, procedures that combine posterior instrumentation with an anterior discectomy (i.e. removal of herniated disc material from the spinal canal so that the spinal cord or nerve is restored to an unpinched state) and fusion (which allows vertebrae to effectively be knit together into a solid bony mass), along with other procedures that cannot employ a posterior approach. Thus, the implants may also be employed in anterior discectomy and fusion, which involves the removal of an intervertebral disc and the replacement of that disc with an implant that will undergo fusion, both steps being undertaken via an anterior approach. Other surgical procedures employing the anterior approach, including procedures used in fusing the thoracic region, may also make use of the implants.
Alternatively, surgical procedures involving a posterior approach may also employ the implants created using the current invention. For example, posterior lumbar interbody fusion, another surgical technique used for spinal fusion, involves the posterior insertion of an implant into the intervertebral space following posterior excision of a disc through the spinal canal.
Bone stock 25′ as shown in
While bone stock 25′ utilizes four separate bone pieces, other numbers of pieces are contemplated. For example, a core may be surrounded by only two sleeves to produce a desired stock size. Also, pins 24 may be formed from bone.
Another composite implant is shown in
Yet another approach to maximizing the use of a bone sections with thin wall areas is shown in
Interfitting may also be achieved using the design of implant 74 shown in
Numerous types of joints are useful in the present development, including joints that permit articulation such as a ball and socket type of joint, and particularly joints that permit firm interlocking between two components to prevent relative movement between the components. Preferably, mortise and tenon joints can be used to interfit multiple bone components to create an implant as shown for example in
The use of insertable securing elements such as keys, pegs, pins, wedges, or other suitable components in joints to assist in securing bone components to each other is also an effective approach to providing a stable joint. Keys, for example, may be inserted in notched or grooved areas in bone components, serving as the securing element between two or more bone components. Parameters that may be varied when using insertable securing elements, such as keys, include the angle of application, the spacing of the elements, and the thicknesses of the elements.
Alignment indicia 210 may be provided on the outer surface of implant 200, as with a line or other aid. Preferably, indicia 210 is an imprint, i.e. with ink, although indicia 210 may instead be provided in the form of surface scoring. The indicia suitable for the present invention includes, but is not limited to, markers such as lines, arrows, lettering, and symbols. In addition, alignment indicia 210 preferably is provided on the anterior side of implant 200 to aid in alignment with the natural anatomy encountered during surgery, and particularly to aid in alignment with the anterior longitudinal ligament (ALL) that extends over the length of the lumbar spine anterior to the vertebral bodies. In particular, the ALL may be used as a landmark in combination with alignment indicia 210, for example, to permit a surgeon to properly align implant 200 with respect to surrounding anatomy.
Turning to FIGS. 8A-E, another spacer implant 1100 according to the present invention is shown. Two bone pieces 1102,1104 are provided with mating portions 1107, 1108 respectively. Once interfitted, bone pieces 1102, 1104 provide a multi-layer, oval-shaped implant structure with a central hole 1112, which may be packed with bone-growth inducing substances. Preferably, one or more of the outer surfaces on implant 1100, such as outer surface 1106, is provided with teeth 1110. In a preferred embodiment, teeth 1110 are pyrimidal in shape with edges formed at an angle β of about 60°. Preferably, at least a portion of an inner surface of a bone piece 1102, 1104 is provided with a protrusion that is received in an opposing groove. For example, as shown in
Referring to FIGS. 9A-C, various other configurations of bone portions may be provided. For example, an implant 1200 may be formed with interfitting washer 1202 and base 1204 bone pieces. Alternatively, an implant 1220 may be formed with multiple washer-like pieces 1222, 1224 that interfit with a core 1226. In addition, an implant 1240 may be formed with washer-like pieces 1242, 1244, an intermediate piece 1246, and a core 1248 that extends the length of all pieces 1242, 1244, 1246. The mating surfaces of the components of these embodiments may be fixed to each other using any of the aforementioned means such as pins and adhesives. In addition, different types of bone may be selected for the components of these embodiments. In one embodiment, implant 1200 includes a cancellous ring 1202 and a cortical base 1204. In another embodiment, implant 1240 includes cortical washer-like pieces 1242, 1244, a cancellous intermediate piece 1246, and a cortical core 1248.
Another embodiment according to the present invention is shown in
Yet another embodiment of an implant 1280 is shown in
Further embodiments of multipiece implants are shown in
As shown in
Referring now to
Additional embodiments of implants with combinations of cortical and cancellous bone are shown in
Implants may be formed from composites of bone material and material that is molded thereto. For example, femur section 46 shown in
Once the bone cement has set, molds 1402, 1406 may be removed, leaving a tissue form 1410 with a composite wall of the original femur section 46 and bone cement sections 1412, 1414. Other filler materials can be used with molds 1402, 1406, such as a mixture of hydroxyapatite and cement that sets in place. In alternate embodiments, materials are molded only to portions of bone sections, instead of being molded to completely surround inner and/or outer surfaces of bone sections. Additional molds can be used for surrounding adjacent bone sections in implants formed with multiple pieces of bone, thereby permitting multiple bone sections to be coupled together with an intermediary layer of bone cement.
Molded sections such as sections 1412, 1414 may include mixtures or suspensions of cancellous and/or cortical bone powder, bone chips, and bone fibers, in natural or demineralized conditions, in combination with bonding agents such as bone cements, water, fat, blood, thrombin, and fibrin. The fibers, in particular, may be oriented to provide particular mechanical properties. For example, fibers may be oriented generally parallel to axis 1416, transverse to axis 1416, or in mixed orientations in order to achieve desired strength when encased in bone cement that is cured. Other materials also may be combined with bonding agents or other carriers, such as hydroxyapatite. Furthermore, sections 1412, 1414 may additionally be formed by applying pressure while curing occurs.
Alternatively, compactable powders and/or fibers of various sizes and shapes may be pressed and compacted in place, without bonding agents or with minimal use thereof. Such pressed structures may be further encapsulated in thin layers of bone cements or polymers such as biodegradable polymers. While loose powder of varying particle sizes may be compressed and densified to produce a compact of the powder, it is difficult to apply uniform pressures while producing the compact. The so-called “single action” pressing technique, which typically applies a force to the powder in a single direction, may be used in the present invention. However, in some embodiments, because it is desirable to produce a compact with a more uniform density throughout the structure, other pressing techniques may be used.
Furthermore, the components of the implants described herein may be formed by molding various materials onto support structures such as meshes or other structures that are known to one skilled in the art. For example, titanium mesh indicated for reinforcement of bony regions in orthopedic procedures is typically available in preformed round and oval-shaped cylinders. The metal mesh may be encapsulated or otherwise surrounded by another material such as bone powder or bone fiber impregnated bone cement that has dried in place around the mesh. Multiple bone components may be interfitted together and further encapsulated or otherwise surrounded by molded materials for additional reinforcement. Also, molded material may be used to further couple two or more pieces of bone together. For example, a polymer such as polymethylmethacrylate may be placed in the central chamber of an implant and allowed to cure in place.
While various descriptions of the present invention are described above, it should be understood that the various features can be used singly or in any combination thereof. The various types of joints and connections can be used on bone implants or bone stock of different size or configuration, such that the invention is not to be limited to only the specifically preferred embodiments depicted in the drawings.
Further, it should be understood that variations and modifications within the spirit and scope of the invention may occur to those skilled in the art to which the invention pertains. For example, multiple, differently shaped and sized bone portions can be constructed for interfitting or interconnection to form a multiple part bone implant that serves the desired purpose. Accordingly, all expedient modifications readily attainable by one versed in the art from the disclosure set forth herein are within the scope and spirit of the present invention and are to be included as further embodiments. The scope of the resent invention is accordingly defined as set forth in the appended claims.