US20090026246A9 - Superplastic forming of titanium assemblies - Google Patents
Superplastic forming of titanium assemblies Download PDFInfo
- Publication number
- US20090026246A9 US20090026246A9 US11/272,244 US27224405A US2009026246A9 US 20090026246 A9 US20090026246 A9 US 20090026246A9 US 27224405 A US27224405 A US 27224405A US 2009026246 A9 US2009026246 A9 US 2009026246A9
- Authority
- US
- United States
- Prior art keywords
- sheet
- sheets
- sub
- assembly
- grain size
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
- 1) Field of the Invention
- The present invention relates to the forming and bonding of structural members and, more particularly, relates to the use of different grain titanium for superplastic forming and/or diffusion bonding.
- 2) Description of Related Art
- Superplastic forming (SPF) generally refers to a process in which a material is superplastically deformed beyond its normal limits of plastic deformation. Superplastic forming can be performed with certain materials that exhibit superplastic properties within limited ranges of temperature and strain rate. For example, workpieces formed of titanium alloys are typically superplastically formed in a temperature range between about 1450° F. and 1850° F. at a strain rate up to about 3×10−4 per second.
- Diffusion bonding (DB) generally refers to a process of joining members using heat and pressure to form a solid-state coalescence between the materials of the joined members. Joining by diffusion bonding occurs at a temperature below the melting point of the materials that are being joined, and the coalescence therebetween is produced with loads below those that would cause macroscopic deformation of the article.
- According to one conventional process, superplastic forming is performed by providing one or more superplastically formable metal sheets in a die cavity defined between cooperable dies, heating the sheets to an elevated temperature at which the sheets exhibit superplasticity, and then using a gas to apply differential pressures to the opposite sides of the sheets in order to form the sheets. The pressure is selected to strain the material at a strain rate that is within its superplasticity range at the elevated temperature, stretch the sheet, and cause it to assume the shape of the die surface. In this way, the sheet can be formed to a complex shape defined by the dies.
- Further, in some cases, superplastic forming and diffusion bonding are performed in a combined forming/bonding operation. For example, in one typical combined SPF/DB process, three metal sheets are stacked to form a pack. A stop-off material is selectively provided between the sheets to prevent portions of the adjacent surfaces of the sheets from being bonded. The pack is heated and compressed in a die cavity with sufficient gas pressure so that the adjacent portions of the sheets that are not treated with the stop-off material are joined by diffusion bonding. Thereafter, a pressurized gas is injected between the sheets to inflate the pack, and thereby superplastically form the pack to a configuration defined by the surface of the die cavity. This process is described further in U.S. Pat. No. 3,927,817 to Hamilton, et al. Such a combined SPF/DB process can be used, e.g., to produce complex honeycomb sandwich structures that are formed and diffusion bonded to define hollow internal cells. Generally, the simplicity of the superplastic forming and/or diffusion bonding processes can result in lighter and less expensive structures with fewer fasteners and higher potential geometric complexity. Applications of SPF and/or DB include the manufacturing of parts for aircraft, other aerospace structures, non-aerospace vehicles and structures, and the like.
- The individual sheets of a pack for forming according to the foregoing conventional process are typically provided as a flat sheets in a stacked relationship.
FIG. 1 illustrates a portion of a three-sheet pack after being diffusion bonded and superplastically formed according to the conventional process. As shown, the space S between the outer sheets (or “face sheets”) F1, F2 has been expanded by the gas and the middle sheet (or “inner sheet” or “core sheet”) C has been superplastically formed to a corrugated or otherwise non-linear shape so that the middle sheet C extends in alternating directions between the outer sheets F1, F2 and defines the cells of the pack. As the outer sheets are expanded outward, the middle sheet tends to exert a reactive force on the outer sheets, thereby causing the outer sheets to be deformed. The effect of this reactive force is shown inFIG. 1 as deformation of the outer sheet where the middle sheet is connected thereto. In particular, instead of the outer sheet defining a flat surface, the outer sheet has been deformed to form a depression M, typically referred to as “markoff,” on its surface opposite the connection to the middle sheet. - Such markoff of the outer sheets of a pack during superplastic forming can be reduced by providing a middle sheet that is significantly thinner than the outer sheets, thereby increasing the relative stiffness of the outer sheets and reducing the inward force on the outer sheets during forming. The ratio of the thickness of the middle sheet to the thickness of each outer sheet is typically no more than about 25%. Therefore, if the design requirements for a particular application require a thicker middle sheet, superplastic forming is not typically used. The production of two-sheet assemblies and assemblies having other numbers of sheets can similarly be limited by a desire to avoid markoff.
- While the conventional methods for SPF/DB processing have proven effective for manufacturing a variety of structural assemblies, including assemblies formed of titanium, there exists a continued need for improved SPF/DB methods and assemblies. In particular, the method should allow the production of assemblies with a greater range of desired dimensions, including assemblies with sheets of particular dimensions.
- Embodiments of the present invention provide a method of superplastically forming titanium sheets and an assembly that is formed by such a method. Titanium sheets having different granular structures are used in the method so that the different sheets are adapted to superplastically form at different temperatures. In some cases, the sheets can be formed without markoff (or without substantial markoff) occurring, even though one or more of the sheets of substantial thickness is subjected to significant forming.
- According to one embodiment of the present invention, a structural assembly having a predetermined configuration is produced by superplastically forming a pack having first and second titanium sheets in a stacked configuration. The first sheet has a grain size that is at least about twice a grain size of the second sheet. For example, the first sheet can define a grain size that is greater than about 5 micron and in some cases greater than 8 micron, and the second sheet can define a grain size less than about 2 micron such as between about 0.8 and 1.2 micron. The pack is heated to at least a superplastic forming temperature of the second sheet, and the second sheet is superplastically formed to a predetermined configuration to thereby form the assembly. The second sheet can be superplastically formed at a temperature that is less than the superplastic forming temperature of the first sheet, e.g., at a temperature between about 1400° F. and 1450° F. In some cases, the second sheet is formed without superplastically forming the first sheet, e.g., with the first sheet being only nonsuperplastically formed. The second sheet can be at least 75% as thick as the first sheet. The sheets can be diffusion bonded, and the second sheet can be formed in a direction away from the first sheet. In some cases, the second sheet can also be bonded to a third sheet having a grain size that is less than the grain size of the first sheet so that the third sheet can also be superplastically formed.
- According to one aspect of the invention, the first and second sheets form a first structural sub-assembly that is joined to other sub-assemblies, e.g., to form an engine exhaust heat shield. For example, a second sub-assembly can be formed by repeating the providing, heating, and superplastically forming operations used to form the first sub-assembly. The first and second sub-assemblies can be joined to opposite transverse edges of a third sub-assembly, which can also be superplastically formed. The third sub-assembly can define transversely extending channels and each of the first and second sub-assemblies can define transversely extending cells that are offset from the channels of third sub-assembly.
- Embodiments of the present invention also provide a superplastically formed structural assembly. The assembly includes a first titanium sheet and a second titanium sheet that is joined to the first sheet in a stacked configuration, e.g., with the sheets joined by diffusion bonds. The second sheet is superplastically formed to a contoured configuration so that the first and second sheets define cells therebetween. Further, the first sheet has a grain size that is at least about twice a grain size of the second sheet so that the first sheet has a superplastic forming temperature that is higher than the superplastic forming temperature of the second sheet. For example, the first sheet can define a grain size of greater than about 5 micron or 8 micron and the second sheet can define a grain size less than about 2 micron such as between about 0.8 and 1.2 micron. The second sheet can be adapted to be superplastically formed at a temperature of between about 1400° F. and 1450° F. The second sheet can have a thickness that is substantial relative to the first sheet, e.g., about 75% of the thickness of the first sheet. Further, the first sheet can define a surface opposite the second sheet, and the surface can have a substantially planar configuration opposite a plurality of joints that connect the first and second sheets, i.e., without markoff or without substantial markoff of the first sheet. In some cases, the assembly can also include a third sheet that is bonded to the second sheet, the third sheet having a grain size less than the grain size of the first sheet.
- The first and second sheets can define a first structural sub-assembly of an engine exhaust shield, which can also include second and third sub-assemblies. Similar to the first sub-assembly, the second sub-assembly can include first and second titanium sheets that are joined in a stacked configuration, with the second sheet superplastically formed to a contoured configuration to define cells, and with the first sheet of the second sub-assembly having a grain size that is at least about twice a grain size of the second sheet of the second sub-assembly and a correspondingly higher superplastic forming temperature. The first and second sub-assemblies can be joined to opposite transverse edges of the third sub-assembly, and each of the first and second sub-assemblies can define transversely extending cells that are longitudinally offset from transversely extending channels defined by the third sub-assembly.
- Thus, the present invention provides an improved assembly and method for superplastic forming and/or diffusion bonding, in which titanium sheets having different granular structures can be used to produce the assembly. The superplastic forming can be performed at particular temperatures, such as temperatures that are below the superplastic forming temperatures of some or all of the sheets, and the formation of markoff can potentially be reduced or eliminated.
- Having thus described the invention in general terms, reference will now be made to the accompanying drawings, which are not necessarily drawn to scale, and wherein:
-
FIG. 1 is a perspective view illustrating a portion of a structural assembly manufactured by diffusion bonding and superplastically forming a three-sheet pack according to a conventional process; -
FIG. 2 is a perspective view illustrating a portion of a structural assembly manufactured according to one embodiment of the present invention; -
FIG. 3 is a section view illustrating a pack configured in a die for superplastic forming to form the structural assembly ofFIG. 2 ; -
FIG. 4 is a section view illustrating the pack and die ofFIG. 3 , shown after the pack has been superplastic formed to the desired configuration of the structural assembly ofFIG. 2 ; -
FIG. 5 is a section view illustrating a pack configured in a die for forming a structural assembly according to another embodiment of the present invention; -
FIG. 6 is a section view illustrating a portion of the structural assembly manufactured from the pack ofFIG. 5 ; -
FIG. 7 is a perspective view illustrating an engine exhaust heat shield according to yet another embodiment of the present invention; -
FIG. 8 is a perspective view illustrating first and third sub-assemblies of the engine exhaust heat shield ofFIG. 7 ; -
FIG. 9 is a plan view illustrating the first and third sub-assemblies ofFIG. 8 ; -
FIG. 10 is another perspective view illustrating first and third sub-assemblies ofFIG. 8 , with frame members installed; -
FIG. 11 is a perspective view illustrating the frame members installed in the first and third sub-assemblies ofFIG. 10 ; -
FIG. 12 is a perspective view illustrating a fitting of the engine exhaust heat shield ofFIG. 7 ; -
FIG. 13 is a perspective view illustrating first and third sub-assemblies of a first portion of a heat shield according to another embodiment of the present invention, shown with the third sub-assembly in sectional view; -
FIG. 14 is a plan view illustrating an access door manufactured according to another embodiment of the present invention; and -
FIG. 15 is a section view illustrating the access door ofFIG. 14 , as seen along line 15-15 ofFIG. 14 . - The present invention now will be described more fully hereinafter with reference to the accompanying drawings, in which some, but not all embodiments of the invention are shown. Indeed, this invention may be embodied in many different forms and should not be construed as limited to the embodiments set forth herein; rather, these embodiments are provided so that this disclosure will satisfy applicable legal requirements. Like numbers refer to like elements throughout.
- Referring now to the figures and in particular to
FIG. 2 , there is shown a portion of astructural assembly 10 manufactured according to one embodiment of the present invention. The structural assemblies of the present invention are typically formed of two or more sheets of titanium that are bonded and subjected to a forming operation, in which one or more of the sheets are superplastically formed. The resulting assemblies can be used in a variety of applications, for example, as a member of an aircraft wing, aircraft fuselage, other aeronautical vehicle, or the like. As illustrated inFIGS. 7-13 and described below, thestructural assembly 10 b can be formed as an engine exhaust heat shield. The structural assemblies can also be formed for and used in a wide variety of other applications including, without limitation, as structural panels or other members for automotive or marine applications, building or other structures, or the like. - The
structural assembly 10 is typically manufactured from a pack, i.e., a blank or preform that includes two or more sheets, which are provided in a stacked configuration, and which can be formed to various configurations. For example,FIG. 3 illustrates apack 12 having twosheets sheet sheets pack 12. As described below, one or more of thesheets - As noted above, the
sheets sheets sheets various sheets single assembly 10 can be formed of the same or different alloys of titanium. For example, one or more of thesheets assembly 10 can be formed of Ti-6Al-4V (or “Ti 6-4”), which includes approximately 6% by weight aluminum, 4% by weight vanadium, and the remainder titanium, a titanium alloy that is often used for superplastic forming with or without diffusion bonding. Alternatively, one or more of thesheets - Further, the
various sheets assembly 10 can define different properties, e.g., as a result of variations in the forming or processing operations performed on thesheets sheets first sheet 14 of thepack 12 illustrated inFIG. 3 is formed of titanium having a grain size that is significantly larger than the grain size of thesecond sheet 16 of thepack 12. That is, thefirst sheet 14 can be formed of titanium with a standard grain size, e.g., conventional Ti-6Al-4V, which is typically a dual phase material with an equiaxed grain size of between about 5 and 10 micron. Thesecond sheet 16 can also be formed of Ti-6Al-4V, but the grain size of the material of thesecond sheet 16 can be less than about 5 micron. - The difference in the grain sizes of the materials of the first and
second sheets first sheet 14 can be at least twice the grain size of thesecond sheet 16. For example, the grain size of thefirst sheet 14 can be over 5 microns, and in some cases, over 8 microns, e.g., between about 8 and 10 microns. The grain size of thesecond sheet 16 can be less than 5 microns, such as less than 3 microns or less than 2 microns. In particular, the grain size of thesecond sheet 16 can be between about 0.8 and 1.2 micron and, more particularly, about 1 micron. - The term “grain size” as used herein generally refers to a nominal grain size of the material of the
sheets sheet sheet sheet - It has been discovered that a variation in the grain size affects the forming characteristics of titanium. In particular, titanium having refined or reduced grain sizes can typically be superplastically formed at temperatures less than the superplastic forming temperatures of titanium having larger grain sizes. Thus, the
second sheet 16 can be superplastically formed at temperatures lower than thefirst sheet 14. For example, Ti-6Al-4V with a grain size of about 8-10 microns can typically be superplastically formed at a minimum temperature of about 1650° F. On the other hand, Ti-6Al-4V with a grain size of 1 micron can be superplastically formed at a temperature of less than about 1500° F. and typically less than about 1450° F., such as between about 1400° F. and 1425° F. - Thus, in some cases, the
second sheet 16 can be superplastically formed at a temperature that is significantly less than the minimum superplastic forming temperature of thefirst sheet 14. Typically, thesheets second sheet 16 is between about 25° F. and 300° F. less, and more typically between about 100° F. and 250° F. less, than the superplastic forming temperature of thefirst sheet 14. That is, if the superplastic forming temperature of thefirst sheet 14 is about 1650° F., the superplastic forming temperature of thesecond sheet 16 can be between about 1350° F. and 1625° F. or between about 1400° F. and 1550° F., such as about 1425° F. By virtue of this difference in the superplastic forming temperatures of thevarious sheets pack 12, one or more of the sheets can be superplastically formed while one or more of the other sheets are not superplastically formed. In particular, thesecond sheet 16 of thepack 12 illustrated inFIG. 3 can be superplastically formed to a predetermined, desired configuration illustrated inFIG. 4 , while thefirst sheet 14 remains unsuperplastically formed. Further, even if thefirst sheet 14 is superplastically formed during the forming of thesecond sheet 16, thefirst sheet 14 can remain less formable than thesecond sheet 16. - For example,
FIGS. 3 and 4 illustrate anapparatus 20 for superplastically forming thepack 12 to a desired configuration. Superplastic forming generally refers to a process in which a material is subjected to conditions under which the material exhibits superplastic properties such as the capability of the material to develop unusually high tensile elongations and plastic deformation at elevated temperatures, with a reduced tendency toward necking or thinning. Superplastic forming typically refers to a forming operation in which at least a portion of a member is heated to a superplastic forming temperature and subjected to elongation or strain of at least 50% and, more typically, more than about 100%. The superplastic forming temperature of a material generally refers to the minimum temperature at which the material becomes superplastically formable. The characteristics of superplastic forming are further described in U.S. Pat. No. 3,927,817 to Hamilton, U.S. Pat. No. 4,361,262 to Israeli, and U.S. Pa. No. 5,214,948 to Sanders, each of which is incorporated in its entirety herein by reference, and which generally describe apparatuses in which the methods of the present invention can be performed. As described in the foregoing patents, superplastic forming of a sheet can be performed by applying a pressure differential on opposite sides of the sheet so that the pressure exerts a sufficient force for forming the sheet against a die that defines the desired configuration of the sheet. In addition, multiple sheets can be diffusion bonded or otherwise joined to define internal spaces, such that one or more of the sheets are superplastically formed when the internal spaces are inflated to form an expanded structure, such as honeycomb structure or other cellular structure. - As illustrated in
FIG. 3 , the formingapparatus 20 includes opposed dies 22, 24 that cooperatively define adie cavity 26 therebetween in which thepack 12 is supported. Thefirst die 22 defines acontour surface 28 corresponding to the desired configuration of thefirst sheet 14, and thesecond die 24 defines acontour surface 30 corresponding to the desired configuration of thesecond sheet 16.Fluid ports 32, which are illustrated only schematically in the figures, fluidly connect to a space defined between the first andsecond sheets pack 12. Afluid source 34 is connected to theports 32 and provides a pressurized fluid to the space between thesheets fluid source 36, can also be configured to provide a pressurized fluid to thedie cavity 26 outside thepack 12. For example, argon gas can be used as the pressurized fluid for superplastically forming and diffusion bonding titanium. Tubes are provided for injecting the pressurized fluid between thesheets sheets pack 12 and the die surfaces 28, 30. - As shown in
FIG. 3 , a stop-off material 40, which can include yttrium oxide, is selectively provided between thesheets diffusion bonds 42 between thesheets sheets fluid source 36 pressurizes thedie cavity 26 by providing a pressurized fluid to thedie cavity 26 outside thepack 12, i.e., to the spaces between thepack 12 and the dies 22, 24. Thesheets diffusion bonds 42 to form between the adjacent surfaces of thesheets off material 40 generally prevents portions of thesheets diffusion bonds 42 are formed selectively between thesheets - It has also been discovered that the granular structure of the
sheets second sheet 16 or the resultingassembly 10 that is described above can be diffusion bonded to a conventional member formed of a titanium alloy such as Ti-6Al-4V with a grain size of more than 1 micron at a temperature of less than about 1500° F. In some embodiments of the present invention, this diffusion bonding operation can be performed at a temperature of between about 1400° F. and 1450° F. or between about 1400° F. and 1425° F. In one particular embodiment, the diffusion bonding operation is performed by subjecting thesheets second sheet 16, e.g., less than 1500° F. such as between about 1400° F. and 1450° F. or between about 1400° F. and 1425° F. While subjected to the heating, thesheets sheets FIG. 3 . - It is appreciated that the diffusion bonding operation can be performed while the
sheets apparatus 20 or outside the apparatus, e.g., in another device for supporting thesheets sheets sheets - After the
bonds 42 are formed by diffusion bonding or otherwise, the pressurized fluid in thedie cavity 26 is released. Thepack 12 and/or the dies 22, 24 are heated to a superplastic forming temperature, i.e., a temperature within the superplastic forming temperature range of thesecond sheet 16. The pressurized fluid is injected between thesheets source 34 to inflate thepack 12 and thereby superplastically form at least one of thesheets FIGS. 3 and 4 , thefirst sheet 14 is generally maintained or nonsuperplastically formed against thefirst surface 28, and thesecond sheet 16 is superplastically formed against thesurface 30 of thesecond die 24 to a generally corrugated configuration as determined by thediffusion bonds 42 between thesheets second sheet 14 deforms superplastically and is urged against thecontour surface 30 of thesecond die 24, as shown inFIG. 4 , thereby inflating the internal spaces of the pack 12 (i.e., coincident with the stop-off material 40 at locations between the diffusion bonds 42) to form expandedcells 48 and forming the desired contoured shape. Thefirst sheet 14, in this embodiment, is not superplastically formed, but is instead slightly (and nonsuperplastically) formed to a desired form, such as the gentle curvature illustrated inFIG. 2 . In a typical embodiment, thefirst sheet 14 can be subjected to maximum elongation or strain of less than 10%, such as less than 5%, and thesecond sheet 16 can be subjected to maximum elongation or strain of greater than 50%, such as greater than 100%. - The heating for forming and bonding can be provided using various heaters, such as an oven that receives the
pack 12 or aheater 50 that is integrated into the dies 22, 24. In some embodiments, the dies 22, 24 can remain relatively unheated while thepack 12 is heated to the superplastic forming temperature by a susceptor in which an electrical current is induced by an induction coil, as described in U.S. Pat. No. 5,683,607 to Gillespie, et al, the entirety of which is incorporated herein by reference. - If the
second sheet 16 is superplastically formed at a temperature that is less than the superplastic forming temperature of thefirst sheet 14, and thefirst sheet 16 is therefore not heated to its own superplastic forming temperature during the forming operation of thesecond sheet 16, the deformation of thefirst sheet 14 can be limited or otherwise controlled. That is, while thefirst sheet 14 can be slightly formed to conform to the contour of thefirst die 22, thefirst sheet 14 typically does not become superplastic and therefore maintains sufficient stiffness during forming to resist being deformed by the formation of thesecond sheet 16. In particular, even though uneven forces may be exerted on thefirst sheet 14, e.g., with thefirst sheet 14 being pulled by thesecond sheet 16 at the locations of thediffusion bonds 42 therebetween, thefirst sheet 14 can resist deformation thereby. Thus, after forming to the desired shape of thestructural assembly 10 as shown inFIG. 2 , the surface of thefirst sheet 14 opposite thesecond sheet 16 can show little or no signs of markoff. That is, if thefirst sheet 14 is supported in a generally planar or slightly curved configuration in the dies 22, 24, the surface of thefirst sheet 14 can remain generally flat at eachlocal region 44 opposite thediffusion bonds 42 as illustrated inFIG. 2 . - Each of the
sheets FIGS. 2 and 3 , the thickness of thesecond sheet 16 can be about the same as the thickness of thefirst sheet 14. - In addition, it is appreciated that the superplastic forming and/or diffusion bonding operation of the present invention can generally be performed at reduced temperatures, i.e., at temperatures lower than those required for superplastically forming the coarsest grain materials of the
pack 12. For example, if thesecond sheet 16 is formed of titanium with a refined grain structure, thesecond sheet 16 can generally be superplastically formed and/or diffusion bonded at temperatures lower than those of conventional superplastic forming and/or diffusion bonding operations. This reduction in processing temperature can reduce the thermal stresses exerted on the dies 22, 24 or other tooling used during the operation, thereby reducing pitting or other degradation of the dies 22, 24 and potentially extending the useful life of the dies 22, 24 and other tooling and reducing cleaning, dressing, or other maintenance. In addition, the lower forming/bonding temperatures generally put less demand on theheater 50 that is used for heating thepack 12 to the forming/bonding temperature, and also require less energy. In fact, the reduction in heating can reduce the initial cost of the heaters, reduce the cost of operating heaters used to heat the packs during forming and/or bonding, and/or extend the useful life of the heaters. Further, in some cases, the use of sheets with refined granular structures can also reduce the necessary forming stress for superplastically forming the materials, and/or increase the strain rates that can be achieved during forming so that the forming operation can be completed more quickly. In addition, the reduction in the forming temperature and time required for forming can reduce both the formation of oxides and a layer of alpha case on the sheets during forming. Methods of superplastically forming refined grain materials, and features of such methods, are further described in U.S. patent application Ser. No. 10/813,892, titled “Superplastic forming and diffusion bonding of fine grain titanium,” filed Mar. 31, 2004, the entirety of which is incorporated herein by reference. - In other embodiments of the present invention, any number of sheets can be bonded and formed. For example, a pack can include three or more sheets, and one or more of the sheets can be superplastically formed, e.g., against multiple contour surfaces. Devices and methods for forming single sheets and multiple-sheet packs are further described in U.S. patent application Ser. No. 10/813,892, titled “Superplastic forming and diffusion bonding of fine grain titanium,” incorporated above. In this regard,
FIGS. 5 and 6 illustrate the formation of a structural assembly 10 a from a pack 12 a or preform having threesheets FIG. 5 , the threesheets off material 40 a selectively disposed between thesheets cells 48 a are to be formed between thesheets die cavity 26 a defined by two cooperable dies 22 a, 24 a of an formingapparatus 20 a, and pressure is applied to the pack 12 a, e.g., by controlling the flow of pressurized gas fromfluid source 36 a throughports 32 a to facilitate diffusion bonding between thesheets Diffusion bonds 42 a are formed between the first andsecond sheets third sheets off material 40 a has not been disposed. - Thereafter, the diffusion bonded pack 12 a is heated in the
apparatus 20 a to a superplastic forming temperature of at least one of thesheets third sheets first sheet 14 a, and the pack 12 a can be heated to a temperature that is greater than the superplastic temperature of the second andthird sheets first sheet 14 a. With the pack 12 a so heated, pressurized fluid is injected fromfluid source 34 a between thesheets third sheets cells 48 a defined between thesheets third sheet 18 a is disposed against the contouredsurface 30 a of thesecond die 24. Thefirst sheet 14 a can also be formed during this operation, e.g., to form a slightly curved contour corresponding to surface 28 a, but thefirst sheet 14 a is typically not superplastically formed. In this embodiment, the formation of markoff or other undesired deformation of thefirst sheet 14 a can be avoided atregions 44 a, even though the thicknesses of the second andthird sheets first sheet 14 a or otherwise relatively great compared to the thickness of thefirst sheet 14 a. -
FIGS. 7-12 illustrate the various portions of an assembly manufactured according to one embodiment of the present invention and, in particular, an engineexhaust heat shield 10 b. Theheat shield 10 b is adapted for use with a pylon-mounted gas turbine engine, i.e., a gas turbine/turbo fan jet engine that is mounted on a pylon underneath a wing of an aircraft. The pylon supports the engine and is typically designed to minimize drag of the propulsion system and the airplane. Such pylon-mounted engines are further described in U.S. patent application Ser. No. 10/136,817, titled “Hybrid Exhaust Heat Shield for Pylon Mounted Gas Turbine Engines,” filed Apr. 30, 2002, the entirety of which is incorporated herein by reference. Theheat shield 10 b is typically positioned at the bottom of the aft portion of the pylon and above the primary nozzle exhaust and provides a thermal barrier to protect the pylon and/or the wing from the high temperatures generated by the engine at the primary nozzle exhaust thereof. - The
heat shield 10 b illustrated inFIG. 7 includes twoportions portion first portion 60 includes three joinedsub-assemblies second portion 62 includes three joinedsub-assemblies sub-assemblies sub-assemblies heat shield 10 b.Frame members 76 can also be provided to connect thesub-assemblies - Each of the
structural sub-assemblies second sub-assemblies portions outer sheet 78 and aninner sheet 80. Eachinner sheet 80 is diffusion bonded or otherwise joined to theouter sheet 78 of therespective sub-assembly inner sheet 80 is formed of a material that is characterized by a superplastic forming temperature that is less than the minimum superplastic forming temperature of the respectiveouter sheet 78. Thus, theinner sheets 80 can be superplastically formed at a temperature that is insufficient for superplastically forming the respectiveouter sheet 78, e.g., to avoid deforming theouter sheet 78 so as to cause markoff as described above. In particular, theinner sheet 80 of each sub-assembly 64, 66, 70, 72 can be formed of titanium with a grain size of less than 5 microns, e.g., about 1 micron, and theouter sheet 78 of each sub-assembly can be formed of titanium with a grain size that is greater than 5 microns, e.g., greater than about 8 microns. - Each
inner sheet 80 is superplastically formed to define a number of transversely extendingcells 82. For example, as described above, the outer andinner sheets sheets cells 82. In this way, thesheets sheets cells 82. Thereafter, thesheets inner sheet 80, and gas can be injected between thesheets cells 82. Thecells 82 of each sub-assembly 64, 66, 70, 72 can be fluidly joined by one or more longitudinally extendingtubes 86 or bead-like passages, e.g., by applying the stop-off material at the location of thetubes 86 to prevent diffusion bonding. Thus, thecells 82 can be inflated during the superplastic forming of theinner sheet 80 by injected the gas into thetubes 86 so that the gas flows therefrom into each of thecells 82. Thecells 82 are normally defined as inwardly extending channels in theinner sheet 80 as shown inFIG. 7 . - Each of the
third sub-assemblies FIGS. 7-12 , eachthird sub-assembly third sub-assembly channels 88, as shown inFIGS. 7 and 8 . As illustrated inFIG. 9 , the transversely extendingchannels 88 of thethird sub-assemblies cells 82 of the first andsecond sub-assemblies channels 88 andcells 82 proximate to thetransverse edges 90 of thethird sub-assemblies second sub-assemblies - The
frame members 76 disposed in theheat shield 10 b can also be formed of titanium and can be superplastically formed. As shown inFIGS. 10 and 11 , theframe members 76 can be connected to thesub-assemblies fasteners 92 such as rivets or the like. A closeout fitting 94, shown individually inFIG. 12 , can be provided at the trailing edge of the heat shield lb. In some cases, thevarious assemblies second sub-assemblies third sub-assemblies - In some embodiments, the
sub-assemblies heat shield 10 b can be formed and assembled in a configuration that reduces drag and the potential paths for leaking of hot gases into the cavity defined by theheat shield 10 b. In addition, the use of superplastic forming and/or diffusion bonding can reduce the weight of theheat shield 10 b and reduce the manufacturing cost. - It is also appreciated that each of the
various sub-assemblies heat shield 10 b can be formed of any number of sheets, one or more of which can be superplastically formed and one or more of which can be non-superplastically formed or unformed. In this regard,FIG. 13 illustrates a perspective view of thefirst portion 60 of theheat shield 10 b according to another embodiment of the present invention with the thirdstructural sub-assembly 68 shown in section view. In this embodiment, the thirdstructural sub-assembly 68 is formed of threestacked sheets middle sheets outer sheet 100 is non-superplastically formed. In particular, themiddle sheet 98 can define a corrugated configuration similar to that of themiddle sheet 16 a described above in connection withFIG. 6 , such that thethird sub-assembly 68 defines transversely extendingcells 102 between the inner andmiddle sheets outer sheets middle sheets outer sheet 100 so that the inner andmiddle sheets outer sheet 100. -
FIGS. 14 and 15 illustrate anotherstructural assembly 10 c formed according to another embodiment of the present invention and, in particular, an access door. The illustratedaccess door 10 c is configured for use on an aircraft and, more particular, as the access door for the landing gear compartment of an airplane. Theaccess door 10 c is formed by diffusion bonding and forming a pack in a method similar to that described above in connection withFIGS. 2-4 . That is, theaccess door 10 c includes first andsecond sheets access door 10 c. Thefirst sheet 14, which is formed of titanium having a grain size that is significantly larger than the grain size of thesecond sheet 16, has a flat or slightly curved configuration and is therefore substantially unformed or only slightly formed during manufacture. Thesecond sheet 16, on the other hand, is superplastically formed during manufacture and defines a contoured configuration as illustrated inFIG. 15 so that the twosheets cells 48 therebetween. The two sheets are joined bydiffusion bonds 42. Thus, thefirst sheet 14 defines an outer surface of thedoor 10 c, which typically defines an outer surface or skin surface of the aircraft, while the second sheet defines ribs or other stiffening structures to support thefirst sheet 14. Other members can be mounted to theaccess door 10 c, including, e.g., hingemembers 19, latches, locks, other supports, or the like. - Many modifications and other embodiments of the invention set forth herein will come to mind to one skilled in the art to which this invention pertains having the benefit of the teachings presented in the foregoing descriptions and the associated drawings. Therefore, it is to be understood that the invention is not to be limited to the specific embodiments disclosed and that modifications and other embodiments are intended to be included within the scope of the appended claims. Although specific terms are employed herein, they are used in a generic and descriptive sense only and not for purposes of limitation.
Claims (27)