US 20090173964 A1
Manufacturers encounter limitations in forming low resistance ohmic electrical contact to semiconductor material P-type Gallium Nitride (p-GaN), commonly used in photonic applications, such that the contact is highly transparent to the light emission of the device. Carbon nanotubes (CNTs) can address this problem due to their combined metallic and semiconducting characteristics in conjunction with the fact that a fabric of CNTs has high optical transparency. The physical structure of the contact scheme is broken down into three components, a) the GaN, b) an interface material and c) the metallic conductor. The role of the interface material is to make suitable contact to both the GaN and the metal so that the GaN, in turn, will make good electrical contact to the metallic conductor that interfaces the device to external circuitry. A method of fabricating contact to GaN using CNTs and metal while maintaining protection of the GaN surface is provided.
1. A conductive article comprising:
a semiconductor material substrate;
a patterned conductive trace disposed on the semiconductor material substrate wherein the trace includes:
a non-woven nanotube fabric layer comprising a plurality of
unaligned nanotubes providing a plurality of conductive pathways along the extent of the trace, and
a metal layer adjacent to the non-woven nanotube fabric layer.
2. The conductive article of
3. The conductive article of
4. The conductive article of
5. The conductive article of
6. The patterned conductive trace of
7. The patterned conductive trace of
8. The conductive article of
9. The conductive article of
10. The conductive article of
11. The conductive article of
12. The conductive article of
13. The conductive article of
14. A light-emitting semiconductor device comprising:
a semiconductor material substrate;
a metal contact in electrical communication with the semiconductor;
an interface structure comprising a nonwoven nanotube fabric layer and a metal layer, wherein said interface structure:
is interposed between the metal contact and the semiconductor;
electrically couples the metal contact to the semiconductor; and
includes at least one active region, adjacent to said metal
contact, that is at least partially optically transparent in at least a portion of the visible light range.
15. The light-emitting semiconductor device of
16. The light-emitting semiconductor device of
17. The light-emitting semiconductor device of
18. A method of making a conductive article on a semiconductor comprising:
providing a semiconductor;
forming on the semiconductor a conductive trace including a nonwoven nanotube fabric layer and a thin metal layer;
depositing a mask layer over the conductive trace;
defining a pattern in the mask layer, the pattern corresponding to the shape of the article; and
removing portions of the nanotube fabric layer and portions of the metal layer in accordance with the pattern of the mask layer so that the remaining conductive trace forms the conductive article and the semiconductor is substantially preserved.
19. The method of
20. The method of
21. The method of
22. The method of
23. The method of
24. The method of
25. The method of
26. The method of
27. The method of
28. The method of
29. The method of
This application is a continuation-in-part of and claims priority under 35 U.S.C. § 120 to U.S. patent application Ser. No. 11/111,582, filed on Apr. 21, 2005, entitled NANOTUBE FILMS AND ARTICLES, which is a continuation of U.S. patent application Ser. No. 10/776,573, filed on Feb. 11, 2004, now U.S. Pat. No. 6,942,921, which is a continuation of U.S. patent application Ser. No. 10/128,118, filed Apr. 23, 2002, now U.S. Pat. No. 6,706,402, and hereby incorporates such references in their entirety.
This application also claims priority under 35 U.S.C. § 119(e) to U.S. Provisional Patent Application No. 60/775,461, filed on Feb. 21, 2006, entitled METHOD OF FORMING CARBON NANOTUBE-BASED CONTACT TO SEMICONDUCTOR which is incorporated herein by reference in its entirety.
Additionally, this application claims priority under 35 U.S.C. § 120 to U.S. patent application Ser. No. 10/341,130, filed on Jan. 13, 2003, entitled CARBON NANOTUBE FILMS LAYERS FABRICS RIBBONS ELEMENTS AND ARTICLES, which is hereby incorporated by reference in its entirety.
1. Technical Field
The present application generally relates to methods of forming carbon nanotube-based contacts to semiconductors and more particularly to method of manufacturing carbon-nanotube based contacts to semiconductors for electronic and photonic applications.
2. Discussion of Related Art
III-V semiconductors, specifically GaN (Eg˜3.37 eV), are widely employed for optoelectronic and electronic devices. These materials have many advantages compared to silicon based technology. However, the lack of a stable oxide high manufacturing costs of the III-V semiconductors have prevented them from replacing silicon electronics beyond niche devices and optoelectronic devices (a substantial market itself).
Carbon nanotubes (CNTs) are a new material that is finding various uses especially in the nanoelectronics industry. CNTs contain a tubular structure with diameters ranging from 1-2 nm and have many unique and valuable properties such as dual metallic and semiconductor conduction, high mechanical strength (modulus around 1 TPa), excellent thermal and optical properties and chemical inertness/resilience.
A major challenge in the optoelectronics industry is the ability to form an ohmic, low contact resistance between a metallic (or conductive metal-oxides) thin film and the active p-GaN substrate, which has a very low conductivity. The metal contact must also have a high optical transmittance at the desired operation wavelength, which mandates the use of ultra-thin metal films (<50 nm). These thinner metal films may lead to current uniformity and current injection problems into the p-GaN. Therefore, a balance must be struck between the thin film sheet resistance, the thickness of the metal film and the metal film's optical transmittance. Ideally, a metal or conductive metal-oxide film should form an ohmic contact to the p-GaN, have a contact resistivity of <10−3 Ohms-cm2, have a sheet resistance of <100 Ohms per square, have an index of refraction >1.5 and have an optical transmission of >85% at the desired wavelength. Further complicating the development of GaN optical devices are the many issues with processing p-GaN; such as, sensitivity of the active region to photoresists, dry etching and some solvents.
Currently, a scalable, manufacturable process does not exist for making CNT-based contacts to p-GaN devices. For a process to be manufacturable, it should be useable with the tools and procedures employed in industry. The process outlined in this invention not only conforms to such guidelines, but results in encapsulation of the GaN surface during processing thereby maximizing the quality of the interface of the product.
The idea of using nanotubes to make contact to p-GaN has been published by Lee, K., at al. (“Single wall carbon nanotubes for p-type ohmic contacts to GaN light-emitting diodes”, Nano Letters, 4(5), (2004), 911-914) and patented by Rinzler, A. G., et al, (“Semiconductor device and method using nanotube contacts” US Application number: US 20050199894 (2205)), which both use a thick layer of carbon nanotubes to make a low contact resistance contact to a GaN substrate that was able to transmit blue light centered around 434 nm. However, neither of these references present or purport to have implemented a process suitable in a manufacturing environment. More particularly, in both references, the type of nanotubes and the technique employed to deposit the fabric cannot be reproduced in a suitable manufacturing process. Both the publication by Lee, et. al, and the patent by Rinzler et. al report the use of metal lift-off, which will degrade the device characteristics since the active region is exposed to photoresist, basic developers and solvent chemistries, which damages the active region of the p-GaN, a very sensitive material. The present disclosure details techniques that avoids the abovementioned difficulties and provides new methods of making a desired contact besides using just a nanotube fabric.
This invention provides a method of forming low contact resistance interfaces between a semiconductor, a fabric of carbon nanotubes and a metal layer, while allowing for a high optical transmittance of the carbon nanotube fabric.
Under one aspect of the invention, a conductive article is provided. A semiconductor material substrate is provided and a patterned conductive trace is disposed on the semiconductor material substrate. The trace includes a non-woven nanotube fabric layer comprising a plurality of unaligned nanotubes providing a plurality of conductive pathways along the extent of the trace, and a metal layer adjacent to the non-woven nanotube fabric layer.
Under another aspect of the invention the metal layer is a thin film disposed on the non-woven nanotube fabric layer and is of generally planar extension and substantially parallel to the major surface of the semiconductor.
Under another aspect of the invention, the conductive article further comprises a metal electrode disposed over and in electrical communication with the metal layer.
Under another aspect of the invention, the non-woven nanotube fabric layer is disposed on the metal layer and the metal layer is a thin film of generally planar extension and substantially parallel to the major surface of the semiconductor.
Under another aspect of the invention, the conductive article further comprises a metal electrode disposed over and in electrical communication with the non-woven nanotube fabric.
Under another aspect of the invention, the conductive article further comprising multiple layers of metal and multiple layers of non-woven nanotube fabric, alternately disposed.
Under another aspect of the invention, each layer of metal and each layer of non-woven nanotube fabric is of generally planar extension and substantially parallel to the major surface of the semiconductor.
According to another aspect of the invention, at least a portion of the patterned conductive trace includes an active region that is constructed and arranged to be substantially optically transparent in at least a portion of the visible light range.
According to another aspect of the invention, the metal layer is a thin film of less than 10 nanometers thickness in the dimension substantially perpendicular to the major surface of the semiconductor.
According to another aspect of the invention, the semiconductor includes a p-GaN layer and a n-GaN layer disposed in adjacent and substantially parallel layers.
According to another aspect of the invention, the semiconductor material substrate is selected from a set including Group III-V, V and II-VI semiconductor materials.
According to another aspect of the invention, the non-woven nanotube fabric includes single-walled carbon nanotubes and multi-walled carbon nanotubes.
According to another aspect of the invention, the non-woven nanotube fabric includes metallic nanotubes and semiconducting nanotubes and the relative composition of metallic and semiconducting nanotubes in the fabric is controlled.
Under another aspect of the invention, a light-emitting semiconductor device is provided. The light-emitting semiconductor device includes a semiconductor material substrate and a metal contact in electrical communication with the semiconductor. The light-emitting semiconductor device also includes an interface structure comprising a nonwoven nanotube fabric layer and a metal layer, such that the interface structure is interposed between the metal contact and the semiconductor, electrically couples the metal contact to the semiconductor, and includes at least one active region, adjacent to said metal contact, that is at least partially optically transparent in at least a portion of the visible light range.
Under another aspect of the invention, the interface structure is constructed and arranged to provide a low resistance electrical pathway between the semiconductor and the metal contact.
Under another aspect of the invention, the metal layer of the interface structure is selected and arranged to provide an ohmic contact to the layer of non-woven nanotube fabric and to the metal contact.
According to another aspect of the invention, a method of making a conductive article on a semiconductor is provided. The method of making a conductive article on a semiconductor includes providing a semiconductor, forming on the semiconductor a conductive trace including a nonwoven nanotube fabric layer and a thin metal layer, and depositing a mask layer over the conductive trace. The method of making a conductive article on a semiconductor also includes defining a pattern in the mask layer, the pattern corresponding to the shape of the article, and removing portions of the nanotube fabric layer and portions of the metal layer in accordance with the pattern of the mask layer so that the remaining conductive trace forms the conductive article and the semiconductor is substantially preserved.
According to another aspect of the invention, forming a nonwoven nanotube fabric layer includes applying carbon nanotubes via at least one of spincoating and spraycoating operations.
According to another aspect of the invention, removing portions of the nanotube fabric and portions of the thin metal layer in accordance with the pattern of the mask layer includes at least one of wet etching and dry etching operations.
According to another aspect of the invention, forming a metal contact on the conductive trace wherein the metal contact is in electrical communication with the semiconductor.
According to another aspect of the invention, forming a metal contact includes at least one of wet etching and reactive ion etching operations.
According to another aspect of the invention, the thin metal layer of the conductive trace is constructed and arranged to provide a low resistance contact to the layer of non-woven nanotube fabric and to the metal contact.
According to another aspect of the invention, forming a conductive trace includes disposing the thin metal layer on the nanotube fabric layer.
According to another aspect of the invention, forming a conductive trace includes disposing the nanotube fabric layer on thin metal layer.
According to another aspect of the invention, forming a conductive trace further includes providing multiple layers of carbon nanotube fabric and multiple thin layers of metal, alternately disposed.
The foregoing and other objects of this invention, the various features thereof, as well as the invention itself, may be more fully understood from the following description when read together with the accompanying drawings in which:
P-type Gallium Nitride (p-GaN) is a semiconductor material used in applications such as light emitting diodes (LEDs). Currently, manufacturers encounter limitations in forming low resistance ohmic electrical contact to p-GaN such that the contact is highly transparent to the light emission of the device. It has been demonstrated that carbon nanotubes (CNTs) can address this problem due to their combined metallic and semiconducting characteristics in conjunction with the fact that a fabric of CNTs (CNTs dispersed on a surface) has excellent transparency. The physical structure of the contact scheme is broken down into three components, a) the GaN, b) an interface material and c) the metallic conductor. The metallic conductor interfaces the device to external circuitry. The role of the interface material is to make suitable contact to both the GaN and the metal so that the GaN, in turn, will make sufficient electrical contact to the external circuitry. As an additional fabrication constraint, the GaN surface is sensitive to various chemistries and should remain protected during the manufacturing process. A method of fabricating contact to GaN using CNTs and metal while maintaining protection of the GaN surface is provided. A CNT-based interface film can have high optical transparency while simultaneously forming good electrical contact. This characteristic makes this contact useful for photonic applications. Another benefit of a CNT-based contact is that CNT contacts are expected to be more durable during high temperature operation.
Aspects of the present invention regard manufacturing technique and integration of p-GaN. Because p-GaN is generally a very difficult material to integrate, using spinning techniques to provide nanotubes and depositing metal contacts is challenging. Certain techniques well-known in the relevant art are incompatible: p-GaN cannot be exposed to photoresist and solvents and any RIE processing of the active area will destroy the device. The present invention includes techniques that were developed to overcome these challenges.
Other key aspects of the present invention concern the type of metal contact provided. For example, in certain multilayered embodiments the use of CNT-metal-CNT-metal structures lowers the contact resistance and improves the current spread. In yet other embodiments a CNT fabric and a thin Pt layer, which is typically non-conductive, is used to both lower the resistance of the active contact region, improve current spreading, while maintaining the high transmission of the contacts
The growth, deposition, patterning, and etching operations of carbon nanotube films, layers, fabrics and articles may use conventional techniques, such as lithographic patterning. Methods for forming carbon nanotube films, layers fabrics and articles on various surfaces and methods for then providing other materials over carbon nanotube surfaces is described in detail in U.S. Pat. No. 6,706,402 and U.S. Pat. No. 6,835,591, the entire contents of which are both herein incorporated by reference.
Conventional interconnect technologies have a tendency to suffer from thermal damage and metal diffusion eroding the performance of the semiconductor devices especially from degradation of the electrical properties. These effects become even more pronounced with size reduction in current generation 0.18 um and 0.13 um structures, e.g. by metal diffusion through ultra-thin gate oxide layers. In contrast, carbon nanotube ribbons are not beset with these problems. They are substantially more robust having the highest known thermal conductivities and are not prone to thermal failure. Furthermore, no metal or dopant diffusion can occur since they are constructed entirely of covalently bound carbon atoms.
Approaches for forming intermediate structures are described in detail in U.S. Pat. No. 6,706,402. In certain embodiments, a silicon substrate having a silicon dioxide layer receives a patterned photoresist layer. For example, a photoresist layer may be spin-coated on layer and subsequently exposed and lithographically developed yielding cavities and a mask pattern.
Afterwards, n-doped silicon or metal such as molybdenum, tungsten or tantalum and a sacrificial layer such as aluminum oxide may be deposited in the cavities.
A photoresist, material and aluminum oxide (Al2O3) on top of the photoresist may then be stripped away to form an intermediate structure with electrodes and sacrificial layer. A spin-on-glass (SOG) such as flowable oxide (FOX) is spin-coated over the structure and annealed using a ramped temperature protocol using standard techniques forming a SiO2 layer above the top of the sacrificial layer.
Reactive ion etching (RIE) or the like may then be used to etch the SiO2 layer to form a structure with supports.
The choice of electrode material is limited by the method by which the nanotubes are placed upon the substrate surface.
In the event that nanotubes are deposited on a surface at room temperature by spin-coating of a solution or suspension of nanotubes then the choice of electrode materials is expanded substantially. In this case there is no high temperature step and any metal typically compatible with standard CMOS metallization conditions would be acceptable especially, aluminum, and alloys thereof.
A sacrificial layer can be constructed of Al2O3, metal oxides, metals and other materials. An intermediate structure can be formed using a variety of materials to form supports including SOG, SiO2 and others. In the event that a low temperature spin-coating of nanotube protocol is chosen the materials suitable to be sacrificial layers expands substantially. This could include materials such as PMMA or other polymers, metals such tungsten, chromium, aluminum, bismuth and other transition and main group metals. Also other semiconductors such as germanium and insulators such as oxides and other chalcogenides may be used.
The choice of materials for the support layer greatly depends upon the method chosen for nanotube growth and other factors. In the even that a low-temperature process is chosen for placing nanotubes on the surface, one can envision utilizing such materials as Al2O3, silicon monoxide, semiconductors, insulators and polymers such as polyimide.
The materials selection process is confined to those materials that are compatible with the fabrication process described above. It is understood by those sufficiently skilled in the art that upon selection of a particular electrode material, the sacrificial layer and support materials naturally become limited based upon typical processing steps available in semiconductor fabrication. Likewise if a particular sacrificial layer is chosen the choices of electrode and sacrificial layer materials is suitably limited. Furthermore, upon selection of a particular support material it follows that the electrode and sacrificial layer materials choice is likewise limited.
Under certain embodiments, the nanotube ribbons may be held in position at the supports by friction. In other embodiments the ribbon may be held by other means, such as by anchoring the ribbons to the supports using any of a variety of techniques. This friction can be increased through the use of chemical interactions including covalent bonding through the use of carbon compounds such as pyrenes or other chemically reactive species. Evaporated or spin-coated material such as metals, semiconductors or insulators especially silicon, titanium, silicon oxide or polyimide could also be added to increase the pinning strength.
In the present disclosure, the terms “interface material” and “interface film” are used interchangeably.
The present invention includes a method of forming a low contact resistance a n d high optical transparent film of carbon nanotubes on top of p-GaN.
In another embodiment (
The above embodiment portrays one variant of the interface layer labeled as 250 (also 250′ and 250″) in
The role of the metal component of the interface layer may be as an etch-stop (for either RIE etch or wet etch) to define the metal pad 240 in
A primary effect of the CNTs at the interface layer is to provide enhanced contact to the GaN and/or to aid in conductance of the interface layer while maintaining high optical transparency.
Step 1: The process starting point is shown in
Step 5: The pattern of structure 3003 is transferred to the interface layer 350 by either wet etching or dry etching metal 330 and then dry etching CNT fabric 335, forming structure 3004, depicted in
Step 7: In
The main goal of metal 330 is to provide a low resistance contact between bond pad metal 340 and CNT fabric 335. Most metals form a Schottky barrier contact to CNTs; however, some metals such as Ti and Pd form a nearly ohmic contact to a CNT fabric, which is ideal for this invention. Therefore, the main purpose of metal 330 is to provide an low resistance contact to CNT fabric 335 and to provide an additional ohmic contact to metal bond pad 340. Ideally, the metal film 330 should be removed from the active region (360 and 360′ of
This device was made using GaN wafers obtained from CREE, Inc., consisting of a p-GaN/n-GaN heterojunction on a SiC substrate and a protective oxide layer. The backside of the wafer was coated with Shipley 1805 photoresist to protect the backside of the wafer during the stripping of the oxide. The wafer was then immersed in a buffered oxide etch to strip the oxide exposing a clean p-GaN surface.
CNTs were then spun onto the wafer repeatedly until the resistance as measured by a 4-point-probe was about 100Ω. The wafer was then annealed in vacuum at 300° C. for 30 minutes in order to promote adhesion of the CNT fabric and remove residual solvent.
A metal bi-layer film of 4 nm of Ti and 150 nm of Al were then deposited on top of the CNT fabric by electron beam evaporation. In this case, the CNTs and the 4 nm of Ti comprise the interface layer 350 mentioned in
Shipley 1805 positive photoresist was then spun onto the Al film. The resist was then exposed and developed in MicroChem MF-321 developer (a Tetra-methyl-ammonium-hydroxide solution). A secondary advantage of the TMAH developer is that it also etches Al; therefore, the developer was also allowed to etch the aluminum such that the resist pattern transferred to the aluminum during the same step. The wafer was rinsed in DI water and dried.
The photoresist was stripped in Shipley 1165 (1-methyl-2-pyrrolidinone or NMP) at a temperature of 80° C. The wafer was then rinsed in isopropyl alcohol and dried to neutralize and remove residual NMP.
The wafer was then etched in RIE for 2 min in oxygen plasma at 200 W. After the etch process, the wafer was measured in the 4-point-probe, yielding an infinite resistance and indicating that the regions between the contacts are electrically nullified.
The wafer was then spun with Shipley 1805 photoresist and patterned by exposing and developing as above. This process matches
Without stripping the photoresist, the wafer was then immersed in an HCl-based Ti etchant for 25 sec in order to remove the 4 nm of Ti in the active region adjacent to the pad (360 and 360′ in
The photoresist was finally stripped in NMP, rinsed in IPA and dried.
This structure was electrically tested, providing the Current-Voltage (I-V) curve shown in
In another embodiment of this invention, only a single metal is employed for contact to the CNT fabric and as the bond pad metal, structure 7000 in
The following is an example of a process sequence used to form CNT contacts to p-GaN with aluminum contacting the CNT pad. This particular embodiment of the invention should be considered illustrative and not restrictive.
The substrates used in the experiment described in this example were films p-GaN on sapphire (alumina) substrates which had gold contacts on the bottom side of the wafer and came with a protective sputtered SiO2 layer on the p-GaN layer to protect the film from corrosion, oxidation and damage. The samples were obtained from CREE Inc.
The following process steps were employed:
The resulting structure is shown in the
In another embodiment of this invention, a sacrificial material such as, but not limited to, alumina, Ge or a bi-layer alumina/Ge thin film is used to pattern the active region of the CNT fabric. Therefore, after patterning film 330 and CNT fabric 335 (
Another embodiment of this invention is that the CNT fabric layers may be a monolayer or multilayer fabric, which is deposited by means of spin-coating or spray-coating. The CNT solution may be aqueous or solvent based. The CNTs may be single-walled (SWNTs), multi-walled (MWNTs), or bundles thereof. The CNTs may be fabricated by any means including: Chemical vapor deposition (CVD), laser ablation technique or electric arc furnace.
In another embodiment of this invention, the patterning and electrical contacting of a CNT fabric on top of a semiconductor material is not limited to p-GaN. Other important Group V, III-V or II-VI substrates that may be of interest include, but are not limited to, diamond, Silicon, GaAs, AlN, AlGaN, GaP, SiC, InP and any combination of the materials Al, N, Ga, In, P, As, etc that would be used to form an optical emitting device.
In another embodiment, an anneal can be performed on the final structure to lower the contact resistance between the bond pad, CNT fabric and p-GaN substrate. This anneal may be a vacuum anneal, a forming gas anneal (4% H2 in N2) or a Rapid Thermal Anneal at various temperatures, depending on the metals used for the bond pad contact.
In yet other embodiments, the application of purified nanotubes is preferable. With regard to application of purified nanotubes, using proper bulk nanotube preparations which contain primarily metallic or semiconducting nanotubes would allow application of a nanotube fabric to a substrate. The application of single-walled, multiwalled or mixtures of such nanotubes can be envisioned with subsequent patterning and etching to generate desired structures.
Certain embodiments involve controlled composition of carbon nanotube fabrics. Specifically, methods may be employed to control the relative amount of metallic and semiconducting nanotubes in the nanofabric to achieve the desired characteristics and make an appropriate contact to the GaN and metal bond pads. In this fashion, the nanofabric may be made to have a higher or lower percentage of metallic nanotubes relative to semiconducting nanotubes. Correspondingly, other properties of the nanofabric (e.g., resistance) will change. Further, in some embodiments it may be preferable to separate metallic nanotubes from semiconducting nanotubes, first applying a semiconducting nanotube layer to make contact to the GaN, followed by a metallic layer to make contact to the metal bond pads.
This application is related to the following references which are assigned to the assignee of this application and are hereby incorporated by reference in their entireties:
The invention may be embodied in other specific forms without departing from the spirit or essential characteristics thereof. The present embodiments are therefore to be considered in respects as illustrative and not restrictive.