|Publication number||USH1848 H|
|Application number||US 08/914,073|
|Publication date||May 2, 2000|
|Filing date||Aug 18, 1997|
|Priority date||Aug 18, 1997|
|Publication number||08914073, 914073, US H1848 H, US H1848H, US-H-H1848, USH1848 H, USH1848H|
|Inventors||Jaymin Amin, John Andrew Aust, Norman A. Sanford, Mark P. Bendett|
|Original Assignee||Amin; Jaymin, Aust; John Andrew, Sanford; Norman A., Bendett; Mark P.|
|Export Citation||BiBTeX, EndNote, RefMan|
|Patent Citations (12), Non-Patent Citations (23), Referenced by (13), Classifications (12), Legal Events (1)|
|External Links: USPTO, USPTO Assignment, Espacenet|
This application is a continuation-in-part of provisional patent application Ser. No. 60/023,581 filed on Aug. 19, 1996, entitled "Z-Propagating Waveguide Lasers in Rare-Earth-Doped LiNbO3 ".
1. Field of the Invention
The present invention relates to rare-earth-doped LiNbO3 laser devices and, more particularly, it relates to z-propagating and near z-propagating waveguide laser devices in rare-earth doped LiNbO3 in which the optical waveguide is oriented parallel or nearly parallel to the crystallographic z-axis of the LiNbO3.
2. Description of the Prior Art
The success of fiber amplifiers and lasers has recently stimulated a great deal of interest in rare-earth-doped planar waveguide devices for providing signal-processing functions on a local scale both in optical communications and sensor systems. In particular, rare-earth-doped LiNbO3 is extremely attractive for signal processing functions since the rare-earth-doped LiNbO3 potentially permits a high degree of integration through a combination of the existing mature waveguide fabrication techniques, the intrinsically good material properties in the rare-earth-doped LiNbO3, and the optical gain produced by the rare-earth ion dopants. Moreover, the incorporation of rare-earth ions in the LiNbO3 crystals by indiffusion demonstrates a degree of versatility not readily available in bulk rare-earth-doped planar waveguide devices.
Numerous integrated laser and amplifier devices have been demonstrated in the past in Nd- and Er-diffused LiNbO3. See J. Amin et al, Opt. Lett. 19, 1541 (1994); H. Suche, Proceedings of the 7th European Conference on Integrated Optics, session ThA4 (Delft, 1995), pg. 565. The most common method of waveguide fabrication in rare-earth-diffused LiNbO3 is by Ti-indiffusion allowing for low propagation losses and maintaining the spectral characteristics of the rare-earth ions. However, an inherent problem with Ti:LiNbO3 guided wave devices is the devices' relative instability at visible and near-infrared wavelengths as a result of photorefractive damage induced by the high optical power densities in these guides. This has limited the demonstration of cw room-temperature operation of Nd-doped devices almost exclusively to the case where the waveguides were fabricated by the annealed proton exchange process in MgO:LiNbO3.
Photorefractive damage has also been one of the main reasons that the majority of Er:Ti:LiNbO3 lasers and amplifiers have been pumped at 1480 nm. The only report of a 980 nm pumped Er:Ti:LiNbO3 device is described by Huang et al, Electron. Lett 32,215, 1996. It should be noted that the device described by Huang was only an amplifier. His work demonstrated no laser action. In the Huang et al reference, the detrimental effect of photorefractive damage on the amplifier gain was evident and it is unclear as to whether net gain was obtained in the device. It is widely accepted, however, that the photorefractive effect is due to photogeneration of electrons through ionization of Fe2+ impurities in the Fe3+ state, and the subsequent migration of these electrons along the z-axis (photovoltaic effect). As described by Becker et al, Appl. Phys. Lett. 47, 1024, 1995, trapping of the electrons, presumably in areas outside the waveguide, results in regions of space charge which perturb the waveguide modes through the electro-optic effect. In general, waveguides are fabricated in LiNbO3 with the propagation direction primarily perpendicular to the crystalline z-axis, in order to use the highest electro-optic coefficient (r33) for on-chip modulation. However, the space charge separation caused by the photovoltaic effect is on the order of the mode diameter, and therefore the associated fields remain largely within the waveguide, causing serious perturbation to the guided modes.
As was first reported by Holman, Proc. SPIE 408, 14, 1983, one way of considerably reducing the optical damage is by orienting the waveguide such that light is constrained to propagate substantially parallel to the crystalline z-axis. In this way, the charge separation is then along the guide length, and therefore the overlap between the fields associated with this separation and the optical mode is minimized. A disadvantage for the Holman z-propagation scheme is that it only allows for convenient use of the r22 electro-optic coefficient, which is lower than the commonly used r33 coefficient by a factor of approximately 9. However, the voltage requirement for switching in a z-propagating waveguide structure can be optimally made to be less than 15 V. Moreover, the effect of temperature changes in this z-propagating waveguide orientation, where both TE and TM modes are ordinary modes, are likely to be less than other orientations as dictated by the temperature-dependent Sellmeier dispersion equations and the associated temperature-dependent birefringence of the material. Also, because the z-propagating waveguide of the Holman reference does not support extraordinary modes, measures do not have to be taken during fabrication to suppress outdiffusion of lithium and spurious extraordinary waveguide modes which are known to arise from such lithium outdiffusion will not occur in the present invention. The fabrication of the present invention is therefore simpler. Even through the work of Holman illustrates the advantage of reduced photorefractive instabilities in optical waveguides which are oriented parallel to the crystallographic z-axis in LiNbO3, published work also exists which illustrates that in some instances the photorefractive damage may be significant. For example, in the paper of Sanford and Robinson, Proceedings of the 6th IEEE International Symposium on Applications of Ferroelectrics, 4 (1986), the authors show data which clearly indicates that the z-propagating waveguide geometry in LiNbO3 may exhibit serious polarization switching photorefractive instabilities. Furthermore, the same authors in a second paper, Proceeding of the SPIE, Vol. 704, 58 (1987), showed that these polarization switching artifacts may occur on the time scale of milliseconds. These polarization switching photorefractive artifacts were found in some cases to be so severe that upwards of 100% of the optical power could be exchanged between TE and TM modes. Consequently, with the work of Holman in conjunction with the work of Suche, in combination with the work of Sanford, a person skilled in the art would conclude that the z-propagating geometry is by no means an a-priori guaranteed success. Only demonstration of the fact that such a laser will indeed function, as done by the inventors of the present invention, and reducing the device to practice, as described herein, is conclusive evidence that such a laser can indeed by realized.
Thus, there is a need for a rare-earth-doped waveguide laser with improved stability at visible and near-infrared wavelengths. There is also a need for a rare-earth-doped waveguide laser with reduced photorefractive damage induced by high power densities. There is still a further need for an Er-doped waveguide laser and amplifier which can effectively be pumped at γp =980 nm given that 980 nm pumping has proven to be more effective than 1480 nm pumping for locally pumped fiber amplifiers and the cost/mW of 980 nm pump diodes is currently lower than that of the 1480 nm diodes.
It is an object of the present invention to provide rare-earth-doped, or multiple rare-earth-doped, LiNbO3 waveguide lasers which are configured such that the guided optical modes propagate substantially parallel to the crystalline z-axis and can be pumped at any wavelength (from the visible to the near-infrared) as required by the rare-earth-dopant(s), and which produces laser action without concern for photorefractive instabilities which may be introduced by various visible or near-infrared pump wavelengths, i.e., γp less than 1000 nm or such photorefractive instabilities which may result from the laser action produced by the present invention itself. The waveguide laser device of the present invention has improved stability at visible and near-infrared wavelengths and reduced photorefractive damage, and improved stability when operating as a laser or an optical amplifier.
The present invention is a waveguide device which may be reproducibly fabricated and produces stable cw laser output in a room-temperature environment. The waveguide device comprises a z-propagating structure on either an x-cut or y-cut LiNbO3 substrate having at least one optical waveguide placed substantially parallel to the crystallographic z-axis. Rare-earth ions are incorporated into the LiNbO3 substrate by diffusion in undoped LiNbO3 crystalline plates, or by incorporation into the bulk crystal, from which such plates are cut, as the bulk crystal is grown thereby forming a rare-earth-doped substrate. If the rare-earth ions are incorporated into the LiNbO3 plate by diffusion, the diffusion of the rare-earth species may be distributed over the entire surface of the LiNbO3 plate, incorporating singularly or in combination one or more of the dopant ion species Er3+, Nd3+, Yb3+, and Tm3+, or the rare-earth dopant species may be concentrated in localized portions of the LiNbO3 plate by selective diffusion of any required combination or geometric pattern as necessary to obtain doping over only selected areas as required by the design of the laser or amplifier in consideration.
At least one metal-diffused waveguide channel is incorporated into the rare-earth-doped substrate. Each metal-diffused waveguide channel is substantially parallel to the crystallographic z-axis of the LiNbO3 substrate with the waveguide channel and the rare-earth-doped substrate forming a rare-earth-doped z-propagating waveguide wherein the rare-earth-doped z-propagating waveguide provides room-temperature laser operation substantially free from photorefractive instability.
In an embodiment of the waveguide device of the present invention, the rare-earth ions are selected from the group consisting of Er3+, Nd3+, Yb3+, and Tm3+. Preferably, the rare-earth ions are selected from one or more of the group consisting of Er3+, Nd3+, Yb3+, and Tm3+. If more than one rare-earth ion is used, the multiwavelength operation is possible by pumping at a single wavelength or two different wavelengths depending on which combination of rare-earth ions are selected, i.e., Er/Yb combination is pumped at a single wavelength, near 980 nm for example, then the device will lase near 1550 nm due to the direct excitation of the Er3+ ions by the pump in addition to the excitation of the Er3+ ions by means of energy transfer from the exited Yb3+ ions to the Er3+ ions wherein the Yb3+ ions were also excited by the pump. Alternatively, if the device is pumped around 945 nm, the Yb3+ ions alone will be excited such that they will provide laser action near 1031 nm. Therefore, such a laser, or optical amplifier, pumped near either or both 980 nm and 945 nm could simultaneously produce lasing or optical amplification at near either or both 1550 nm and 1031 nm. Furthermore, the rare-earth ions are preferably indiffused into the LiNbO3 substrate or may have been incorporated into the bulk LiNbO3 crystal when it was grown.
In another embodiment of the waveguide device of the present invention, the LiNbO3 substrate allows multiwavelength operation. Additionally, preferably, the metal channels are metals which increase the refractive index and form a waveguide with the metals being selected from the group consisting of Ti, Zn, Ni, and Cu. Also, the metal channels are preferably diffused into the LiNbO3 substrate.
In yet another embodiment of the waveguide device of the present invention, the rare-earth-doped LiNbO3 substrate which supports an optical waveguide that is oriented substantially parallel to the crystallographic z-axis also has modulator structure in the vicinity of, or overlapping with, the waveguide. It is understood that the rare-earth-doped LiNbO3 substrate may be selected to be either an x-cut or y-cut crystal. The modulator structure could then be used for, either singularly or in combination, mode-locking, Q-switching, or frequency tuning of the waveguide laser device.
In still another embodiment of the waveguide device of the present invention, the waveguide device further comprises a TE-TM polarization switching device formed in the rare-earth doped LiNbO3 substrate which supports optical waveguides oriented parallel, or nearly parallel, to the crystallographic z-axis. Preferably, the switching device allows Q-switching of the waveguide device.
In yet still another embodiment of the waveguide device of the present invention, the waveguide device further comprises a pump light wave or suitable collection of pump light waves. The pump light waves are coupled into the waveguide channel as guided modes and singularly or together provide an excitation source for the rare earth ions composed of one or more of the group consisting of Er3+, Nd3+, Yb3+, and Tm3+, In some instances, the pump light may not be constrained as a guided mode and still suitably excite the rare earth ion(s). This may be the case if the pump light is directed at the waveguide channel from the side rather than the end face of the waveguide channel. The suitably-excited rare-earth ions then enable laser action in the waveguide when the endfaces of the waveguide are provided with the proper reflectivity to enable optical feedback at the lasing wavelength, or wavelengths, of interest. Moreover, the present invention acts as an optical amplifier when, in addition to the injection of guided pump light waves into the waveguide, signal light waves of the appropriate wavelengths are also injected as guided modes into the waveguide and experience gain and amplification through interaction with the excited rare-earth ions.
The present invention is also a method of forming optical waveguides oriented parallel or nearly parallel to the crystalline z-axis of the rare-earth-doped substrate. The method comprises selecting an x-cut or y-cut LiNbO3 sample substrate, depositing a film or films of one or more rare-earth metals from the group consisting of Er, Nd, Yb, and Tm, onto the substrate and introducing these by thermal diffusion into the LiNbO3 sample substrate to produce dopants of Er3+, Nd3+, Yb3+, or Tm3+ in the LiNbO3 sample substrate. The distribution of these rare-earth dopants diffused into the LiNbO3 substrate may cover completely or partially the surface of the LiNbO3 substrate as required by the operation of the particular laser or optical amplifier in question. Alternatively, Er3+, Nd3+, Yb3+, and Tm3+ may already have been incorporated into the rare-earth-doped LiNbO3 plates when the bulk crystal, from which the plates were cut, was grown. The optical waveguides are formed in the rare-earth-doped LiNbO3 plates by depositing, either singularly or a series, of metal stripes which are oriented parallel or nearly parallel to the crystallographic z-axis. The metal stripes are subsequently incorporated into the LiNbO3 by thermal diffusion.
In an embodiment of the method of the present invention, the method further comprises positioning the LiNbO3 sample on a Pt pad, positioning the pad on an alumina pedestal, and placing the LiNbO3 sample, pad, and pedestal into an electric furnace. Further creating a flowing oxygen atmosphere about the LiNbO3 sample, pad, and pedestal as they are heated at high temperature in the electric furnace.
In another embodiment of the method of the present invention, the rare-earth ions are selected from the group consisting of Er3+, Nd3+, Yb3+, and Tm3+. Preferably, the rare-earth ions are selected from at least two of the group consisting of Er3+, Nd3+, Yb3+, and Tm3+. Furthermore, the rare-earth ions are preferably indiffused into the LiNbO3 substrate.
In yet another embodiment of the method of the present invention, the waveguide channels are formed by the diffusion of metal stripes into the rare-earth-doped LiNbO3 which increases the refractive index of the rare-earth doped LiNbO3 in the areas where the diffused metal stripes are present. The waveguide-forming metals are selected either singularly or multiply, from a group consisting of Ti, Zn, Ni, and Cu.
Further objects, features, and advantages of the present invention will become apparent from a consideration of the following description and the appended claims when taken in connection with the accompanying drawings.
FIG. 1 is a perspective view of illustrating the structure and orientation of the waveguide laser device in which the optical channel is oriented parallel or nearly parallel to the crystalline z-axis of the rare-earth-doped LiNbO3 substrate constructed in accordance with the present invention;
FIG. 2a is a graph illustrating the cw laser characteristics of an embodiment of the Er-doped waveguide laser device in which the optical waveguide is oriented parallel or nearly parallel to the crystalline z-axis of the Er-doped LiNbO3 substrate with the waveguide laser being pumped at or near 980 nm and constructed in accordance with the present invention;
FIG. 2b is a graph illustrating the laser spectrum of the embodiment Er-doped waveguide laser device constructed in accordance with the present invention in which the optical waveguide is oriented parallel or nearly parallel to the crystalline z-axis of the Er-doped LiNbO3 substrate;
FIG. 3a is a graph illustrating the cw laser characteristics of an embodiment of the Nd-doped waveguide laser device in which the optical waveguide is oriented parallel or nearly parallel to the crystalline z-axis of the Nd-doped LiNbO3 substrate with the waveguide laser device being pumped at or near 814 nm and constructed in accordance with the present invention;
FIG. 3b is a graph illustrating the laser spectrum of an embodiment of the Nd-doped waveguide laser device constructed in accordance with the present invention in which the optical waveguide is oriented parallel or nearly parallel to the crystalline z-axis of the Nd-doped LiNbO3 substrate;
FIG. 4a is a graph illustrating the cw laser characteristics of an embodiment of a waveguide laser device in which the rare-earth dopant ions are a combination of Er3+ and Yb3+ and the optical waveguide is oriented parallel or nearly parallel to the crystalline z-axis of the combined Er- and Yb-doped LiNbO3 substrate. The lasing characteristic shown is from the Er3+ ion with the signal being emitted at approximately 1531 nm. The device was pumped at or near 980 nm;
FIG. 4b is a graph illustrating the laser spectrum of the embodiment of a waveguide laser device in which the rare-earth dopant ions are a combination of Er3+ and Yb3+ and the optical waveguide is oriented parallel or nearly parallel to the crystalline z-axis of the combined Er- and Yb-doped LiNbO3 substrate with the laser output near 1031 nm from the excited Yb3+ ions being pumped with a pump wavelength near 945 nm, thereby illustrating that, in accordance with the present invention, lasing at multiple wavelengths due to multiple rare-earth dopants are possible;
FIG. 5 is a plan view illustrating a modulator structure constructed in accordance with the present invention that can phase-modulate, polarization modulate, or amplitude modulate guided waveguide modes in optical waveguides fabricated parallel or nearly parallel to the crystalline z-axis of an x-cut LiNbO3 substrate; and
FIG. 6 is a plan view illustrating a modulator structure constructed in accordance with the present invention that can phase-modulate, polarization modulate, or amplitude modulate guided waveguide modes in optical waveguides fabricated parallel or nearly parallel to the crystalline z-axis of a y-cut LiNbO3 substrate.
As illustrated in FIG. 1, the present invention is a z-propagating or near z-propagating waveguide laser device, indicated generally at 10, in rare-earth-doped Ti:LiNbO3, where the rare-earth dopants are composed of Er, Nd, Yb, and Tm, either singularly or in combination, and the optical waveguide channel is placed parallel or nearly parallel to the crystalline z-axis and formed by the diffusion of Ti. The diffusion of other waveguide-forming dopants may be used as described above The waveguide device 10 is made "z-propagating" by configuring the waveguide 12 to be oriented parallel or nearly parallel to the crystallographic z-axis of the substrate 14. The z-propagating geometry allows for the formation of a very efficient TE-TM polarization switching device. It should be noted that the waveguide device 10 can be formed on either an x-cut LiNbO3 plate, as illustrated in FIG. 4a, or a y-cut LiNbO3 plate, as illustrated in FIG. 4b. The fabrication of such a polarization switch delivers a very efficient and easily realized means for Q-switching, mode-locking, or wavelength tuning the waveguide laser device 10.
Three representative functional examples for embodiments of the present invention are now presented. It should be noted that variations of the processing details presented will also be effective in producing functional laser devices within the scope of the present invention. In describing the construction of the waveguide device of the present invention, three samples, Sample A, Sample B, and Sample C, will be discussed. Fabrication of the rare-earth-doped Ti:LiNbO3 begins by selecting an x-cut or y-cut LiNbO3 sample. Using e-beam techniques, approximately 8 nm of Nd is deposited on sample A and approximately 15 nm of Er is deposited on sample B. The Nd3+ ions are then preferably driven into Sample A by indiffusion at approximately 1100° C. over a period of approximately 240 hours, and the Er3+ ions are preferably indiffused into Sample B at approximately 1100° C. over approximately 144 hours. On Sample A, Ti stripes approximately 6 μm wide and approximately 90 nm thick are delineated along the z-axis using standard photolithography and vacuum evaporation techniques. A similar process is used on Sample B to form Ti stripes approximately 7 μm wide and approximately 110 nm thick. The Ti is then diffused into both Sample A and Sample B over a period of approximately 9 hours with Sample A being diffused at a temperature of approximately 1005° C. and Sample B being diffused at a temperature of approximately 1030° C. The rare earth diffusions and the waveguide diffusions are preferably conducted in a ceramic tube placed in an electric furnace. Both Sample A and Sample B are next placed on a Pt pad, which in turn is placed on an alumina pedestal with the alumina pedestal placed in the ceramic tube. Oxygen runs through the ceramic tube placed in the electric furnace with a flow rate of 1 liter/minute. Finally, both samples are cut and end-polished, yielding waveguides with a range of different lengths with end-faces that are polished substantially perpendicular to the z-axis.
Another x-cut or y-cut wafer of LiNbO3 referred to as Sample C is also within the scope of the present invention. Using e-beam techniques, a stack of rare-earth ions, consisting of alternating layers of Er and Yb2 O3 are deposited on Sample C. Each individual rare-earth ion layer in the stack is approximately 2 nm thick with the total thickness of the stack being approximately 28 nm. The layers are then diffused into the LiNbO3 substrate at approximately 1100° C., for a total of approximately 360 hours. Ti stripes having a thickness of approximately 110 nm and a width of approximately 7 μm are delineated on the LiNbO3 substrate using standard photolithography. The Ti diffusion is conducted at approximately 1030° C., for approximately 9 hours. All of the Ti diffusions are preferably in flowing oxygen, in an alumina tube placed in an electric furnace with the Sample C sitting on a Pt pad. The finished Sample C device yielded waveguides which were approximately 2 cm long.
It should be noted that while certain variables in time, temperature, and thickness have been set forth above in construction of Sample A, Sample B, and Sample C, it is within the scope of the present invention to use lesser or greater time, temperature, and thickness variables to yield similar results.
A near-field analysis was performed on the guides on the Er:Ti:LiNbO3 device using a Nd:YLF laser operating near 1040 nm. At this wavelength, the waveguides were slightly double-moded, with the fundamental mode diameters (1/e full width)5.2(±0.3) μm in width and 2.8(±0.15) μm in depth. The waveguide also supported two transverse modes at approximately 800 nm. Transmission measurements made at 809 and 850 nm revealed a coupling efficiency of 68% in Sample A. With an estimated 20 mW coupled into the waveguide, a single-exponential fluorescence decay was observed, with a 1/e lifetime of 89 μs. The acousto-optic (AO) modulator was then removed, and the lasing characteristics of a 1.8-cm-long device were measured. The device lased in a stable, cw manner at 1093.1 nm with the feedback provided by the 14% Fresnel reflectance from the polished endfaces. Both the pump and laser emission were TE polarized.
FIGS. 3a and 3b illustrate the lasing characteristics of Sample A, with FIG. 3b illustrating a laser spectrum. The output power indicated in FIGS. 3a and 3b is the total power from the pumped and unpumped end of the device. For the case of this particular example, the absorbed pump power was 70% of that launched. The threshold for laser oscillation was 68 mW of absorbed pump power, and the slope efficiency was 40%. The inventors of the present invention were able to extract approximately 40 mW from Sample A, limited only by the available pump power, without any discernible sign of photorefractive damage. Note that the performance of this laser is representative only for the case described. Attaching mirrors with various reflectivities to the end facets of the waveguide device will result in modified laser behavior in terms of the output power, the precise output wavelength, and the laser threshold.
Near-field analysis was carried out on the Er:Ti:LiNbO3 device using a 1.5 μm light-emitting diode (LED), revealing the 7-μm-wide Er:Ti:LiNbO3 waveguides to be single-moded at this wavelength, with 1/e mode diameters of 7.9 μm×4.6 μm (width×depth). The guides supported three transverse modes at 980 nm. Laser characteristics were measured in this 2.9-cm-long device, with cw pumping from the Ti:Al2 O3 at 980 nm. The pump mode was TE polarized. A mirror with a reflectivity of >99% at 1530, and which transmitted 85% of the pump, was attached to the front face of the device and fluorinated liquid provided index-matching. At the output end of the device, no mirror was attached, and Fresnel reflection from the polished end-face was used to complete the laser cavity. The device operated very stably, with the output TE polarized; FIGS. 2a and 2b illustrate the cw laser characteristics. In particular, FIG. 2b illustrates the laser output spectrum which occurs near 1531.4 nm. For the particular reflectivities of the mirrors attached to the end facets of the waveguide laser device, the lasing threshold was approximately 10.5 mW of absorbed pump power and the device exhibited a slope efficiency of 8.5%. Stable laser output at power of 1 mW near 1550 nm was obtained. In general, it was possible to make the device lase by attaching to the end facets a wide selection of mirrors that had various reflectivities. Furthermore, the laser would still operate if no mirrors were attached and only the Fresnel reflection of the end facets provided the optical feedback.
Near field analysis was carried out on the Er:Yb:Ti:LiNbO3 device using a 1550 nm LED revealing the waveguides to be single moded, with 1/e mode intensity diameters of approximately 7.9 (±0.4) μm×4.6 (±0.25) μm. The guide supports three transverse modes at 980 nm. Laser characteristics were measured in Sample C, with cw pumping at 980 nm, with a high reflector at the input end and a 95% reflector at the output end. The device lased in a stable cw mode at approximately 1531.4 nm, with a threshold of approximately 45 mW of coupled pump power and a slope efficiency of approximately 0.6%.
The laser characteristics of Sample C are best illustrated in FIG. 4a. The laser waveguide was pumped at or near 980 nm where the pump light directly excited the Er3+ dopant ions and also excited the Yb3+ dopant ions which in turn transferred their energy to the Er3+ dopant ions. Laser action near 1531 nm from the excited Er3+ ions then resulted. The presence of the Yb3+ ions thus enabled more efficient optical pumping of the E3+ lasing ions than would be possible if the Er3+ ions were the sole rare-earth dopant.
Mirrors with high reflectivity near 1060 nm were attached to the waveguide laser end faces to promote lasing from the Yb3+ ions. The laser would then operate near 1031 nm which is the peak which the maximum gain in the Yb:LiNbO3 emission spectrum when pumped near 945 nm. This is an illustration of selecting laser action from the Yb3+ dopants alone, even with the Er3+ dopants present, by tuning the pump light wavelength to a range where the Yb3+ is primarily sensitive. The laser output spectrum is illustrated in FIG. 4b. It is also possible that with appropriate choice of mirrors, the device can be made to lase simultaneously near 1030 nm and near 1530 nm by pumping near 980 nm.
The z-propagating waveguide laser device of the present invention is a stable, room-temperature operating laser fabricated by Ti-indiffusion in rare-earth-doped LiNbO3. The z-propagation scheme has been utilized in constructing the z-propagating waveguide laser device of the present invention thereby allowing effective curbing of the instabilities arising from photorefractive optical damage. During experimentations with a z-propagating waveguide laser device constructed in accordance with the present invention, a Nd:Ti:LiNbO3 waveguide laser device lased continuously using only the polished endfaces to provide feedback. The absorbed pump power at threshold was approximately 68 mW and the slope efficiency was approximately 40%. A similar z-propagating Er:Ti:LiNbO3 waveguide laser device constructed in accordance with the present invention was made to lase by pumping at approximately 980 nm, with an absorbed pump threshold of approximately 10.5 mW and a slope efficiency of approximately 8.5%, obtained using a high reflector on the input face and only the polished output face as the second mirror. Further yet, a z-propagating Er/Yb-doped TiLiNbO3 waveguide laser device constructed in accordance with the present invention was made to lase by pumping at approximately 945 nm with stable lasing at approximately 1031 nm at a threshold of approximately 120 mW of coupled pump power.
When pumped by a suitable light source, optical feedback is provided from the end-facets of the waveguide by attaching to the end-facets suitable mirrors that enable laser action of the excited rare-earth ions and do not impede or restrict the injection of pump light into the waveguide device. The mirrors may be directly deposited on the waveguide end-facets by means of well-known vacuum evaporation techniques for dielectric thin films. Alternatively, the mirrors may be separately formed on thin transparent substrates of a suitable material and mechanically attached to the waveguide end-facets with optical adhesives or clips.
FIGS. 5 and 6 illustrate plan views of a modulator structure that can phase-modulate, polarization modulate, or amplitude modulate guided waveguide modes in optical waveguides fabricated parallel or nearly parallel to the crystalline z-axis of x-cut LiNbO3 or y-cut LiNbO3 plates. Fabrication of a modulator structure on the waveguide laser device described in the present invention will enable greater functionality by enabling mode-locking, of the waveguide laser, Q-switching of the waveguide laser, or separately controlling the polarization of the waveguide laser and allow wavelength tuning of the waveguide laser. Furthermore, all four of these functions, i.e., mode-locking, Q-switching, polarization control, and wavelength tuning, can occur simultaneously or separately as required by the intended use of the present invention. The voltages V2 and V1 as indicated in FIGS. 5 and 6 control the degree of phase modulation and TE-TM polarization conversion. The TE pass polarizer illustrated in FIGS. 5 and 6 enables Q-switching by means of providing amplitude modulation of the laser through polarization switching and therefore loss modulation of the TE lasing mode. Additionally, the modulator structure may be used in such a manner that it will enable, either continuous or discrete, wavelength tuning of the laser output of the rare-earth-doped LiNbO3 waveguide laser.
Furthermore, the waveguide laser device described in the present invention can be mode-locked, Q-switched or simultaneously mode-locked and Q-switched by attaching a semiconductor saturable absorber to the end facet of the waveguide rather than, or in combination with, the electrode structures described above.
The discovery and demonstration of a rare-earth doped LiNbO3 waveguide laser device, especially an Er:LiNbO3 waveguide laser device, pumped at approximately 980 nm is a very important result, in view of the inexpensive and readily available pump laser diodes at the 980 nm wavelength. The discovery also opens up many opportunities for advanced active and passive circuits incorporating, for example, on-chip wavelength division multiplexers for independent pump and signal routing.
The foregoing exemplary descriptions and the illustrative preferred embodiments of the present invention have been explained in the drawings and described in detail, with varying modifications and alternative embodiments being taught. While the invention has been so shown, described and illustrated, it should be understood by those skilled in the art that equivalent changes in form and detail may be made therein without departing from the true spirit and scope of the invention, and that the scope of the present invention is to be limited only to the claims except as precluded by the prior art. Moreover, the invention as disclosed herein, may be suitably practiced in the absence of the specific elements which are disclosed herein.
|Cited Patent||Filing date||Publication date||Applicant||Title|
|US4695121 *||Jan 28, 1985||Sep 22, 1987||Polaroid Corporation||Integrated optic resonant structres and fabrication method|
|US4705346 *||May 13, 1985||Nov 10, 1987||Canon Kabushiki Kaisha||Thin film type optical device|
|US4717228 *||Nov 18, 1985||Jan 5, 1988||Telefonaktiebolaget Lm Ericsson||Optical directional coupler with amplification|
|US4791388 *||Apr 27, 1987||Dec 13, 1988||Polaroid Corporation||Channel waveguide modulator|
|US4840816 *||Mar 24, 1987||Jun 20, 1989||The United States Of America As Represented By The United States Department Of Energy||Method of fabricating optical waveguides by ion implantation doping|
|US5128948 *||Mar 26, 1991||Jul 7, 1992||Thomson-Csf||Laser device with monolithically integrated frequency changer|
|US5197072 *||Jun 13, 1991||Mar 23, 1993||Fuji Photo Film Co., Ltd.||Optical wavelength converting device, and laser diode pumped solid laser|
|US5206925 *||Apr 26, 1991||Apr 27, 1993||Hitachi Cable Limited||Rare earth element-doped optical waveguide and process for producing the same|
|US5282260 *||Aug 25, 1992||Jan 25, 1994||Forschungszentrum Julich Gmbh||Optical waveguide component and formed with rare earth ions|
|US5473722 *||Feb 1, 1991||Dec 5, 1995||Pirelli Cavi S.P.A.||Rare-earth-doped lithium niobate waveguide structures|
|US5499256 *||Feb 14, 1995||Mar 12, 1996||Deacon Research||Polarized frequency-selective optical source|
|US5526371 *||Jan 13, 1995||Jun 11, 1996||At&T Corp.||Pumping arrangements for arrays of planar optical devices|
|1||*||A. Donaldson et al, Phase Matched Mode Converter in LiNbO 3 , Using Near A Axis Propagation, Electronics Letters, vol. 23, No. 25, Dec. 3, 1987.|
|2||A. Donaldson et al, Phase-Matched Mode Converter in LiNbO3, Using Near-A-Axis Propagation, Electronics Letters, vol. 23, No. 25, Dec. 3, 1987.|
|3||*||C.H. Huang et al, Er Indiffused Ti:LiNbO 3 Channel Waveguide Optical Amplifiers pumped at 980 nm, Electronics Letters, 32, 215 (1996).|
|4||C.H. Huang et al, Er-Indiffused Ti:LiNbO3 Channel Waveguide Optical Amplifiers pumped at 980 nm, Electronics Letters, 32, 215 (1996).|
|5||*||H. Suche, Erbium Doped Integrated Lasers and Amplifiers, Proc. 7th Eur. Conf. on Int. Opt. pp. 565 570 (1995).|
|6||H. Suche, Erbium-Doped Integrated Lasers and Amplifiers, Proc. 7th Eur. Conf. on Int. Opt. pp. 565-570 (1995).|
|7||*||J. Amin et al, Tunable Coupled Cavity Waveguide Laser at Room Temperature in Nd Diffused Ti:LiNbO 3 , Optics Letters, vol. 19, 1541 (1994).|
|8||J. Amin et al, Tunable Coupled Cavity Waveguide Laser at Room-Temperature in Nd-Diffused Ti:LiNbO3, Optics Letters, vol. 19, 1541 (1994).|
|9||*||M. Fujimura et al, CW and Q SW Laser Oscillation in Thermally Nd Diffused Z Propagation Ti:LiNbO 3 Waveguide, 2nd Optoelectronics & Communications Conference Technical Digest, Jul. 1997, pp. 114 115.|
|10||M. Fujimura et al, CW and Q-SW Laser Oscillation in Thermally Nd-Diffused Z-Propagation Ti:LiNbO3 Waveguide, 2nd Optoelectronics & Communications Conference Technical Digest, Jul. 1997, pp. 114-115.|
|11||*||N.A. Sanford et al, Direct current Bias Stable Ti:LiNbO 3 TE TM Mode Convertors Produced by Magnesium Postdiffusion, Optics Letters, vol. 12, No. 7, Jul. 1987, pp. 531 5.33.|
|12||N.A. Sanford et al, Direct-current Bias Stable Ti:LiNbO3 TE-TM Mode Convertors Produced by Magnesium Postdiffusion, Optics Letters, vol. 12, No. 7, Jul. 1987, pp. 531-5.33.|
|13||*||N.A. Sanford et al, Optical Damage Effects in Z axis Oriented LiNbO 3 Channel Waveguides, Proceedings of the Sixth IEEE Int l Symposium on Applications of Ferroelectrics, pp. 4 7 (1986).|
|14||*||N.A. Sanford et al, Optical Damage Effects in Z Propagating LiNbO 3 Channel Waveguides Fabricated on X and Y Cut Substrates, SPIE Vo. 704 Integrated Optical Circuit Engineering IV, pp. 58 61 (1986).|
|15||N.A. Sanford et al, Optical Damage Effects in Z-axis Oriented LiNbO3 Channel Waveguides, Proceedings of the Sixth IEEE Int'l Symposium on Applications of Ferroelectrics, pp. 4-7 (1986).|
|16||N.A. Sanford et al, Optical Damage Effects in Z-Propagating LiNbO3 Channel Waveguides Fabricated on X-and Y-Cut Substrates, SPIE Vo. 704 Integrated Optical Circuit Engineering IV, pp. 58-61 (1986).|
|17||*||N.A. Sanford et al, Simplified Z Propagating DC Bias Stable TE TM Mode Convertor Fabricated in Y Cut Lithium Niobate, Journal of Lightwave Technology, vol. 6, No. 6, Jun. 1988, pp. 898 902.|
|18||N.A. Sanford et al, Simplified Z-Propagating DC Bias Stable TE-TM Mode Convertor Fabricated in Y-Cut Lithium Niobate, Journal of Lightwave Technology, vol. 6, No. 6, Jun. 1988, pp. 898-902.|
|19||*||R.A. Becker et al, Photorefractive Effects in LiNbO 3 Channel Waveguides: Model and Experimental Verification, Applied Physics Letters, 47, 1024 (1985).|
|20||R.A. Becker et al, Photorefractive Effects in LiNbO3 Channel Waveguides: Model and Experimental Verification, Applied Physics Letters, 47, 1024 (1985).|
|21||*||R.L. Holman, The Optical Properties and Processing of Lithium Niobate Optical Waveguides, Proceedings SPIE, 408, 14 (1983).|
|22||*||S. Thaniyavarn, Wavelength Independent, Optical Damage Immune LiNbO 3 TE TM Mode Convertor, Optics Letters, vol. 11, No. 1, Jan. 1986, pp. 39 41.|
|23||S. Thaniyavarn, Wavelength-Independent, Optical-Damage-Immune LiNbO3 TE-TM Mode Convertor, Optics Letters, vol. 11, No. 1, Jan. 1986, pp. 39-41.|
|Citing Patent||Filing date||Publication date||Applicant||Title|
|US6330388 *||Jan 22, 2000||Dec 11, 2001||Northstar Photonics, Inc.||Method and apparatus for waveguide optics and devices|
|US6493476||Nov 27, 2001||Dec 10, 2002||Teem Photonics||Apparatus and method for integrated photonic devices having gain and wavelength-selectivity|
|US6640040 *||Mar 15, 2002||Oct 28, 2003||The Regents Of The University Of California||Compact cladding-pumped planar waveguide amplifier and fabrication method|
|US6661567 *||Dec 6, 2000||Dec 9, 2003||Bookham Technology Plc||Optical amplifier, optical amplifier hybrid assembly and method of manufacture|
|US6690873||Dec 6, 2001||Feb 10, 2004||Teem Photonics||Method and apparatus for waveguide optics and devices|
|US6813405||Mar 29, 2002||Nov 2, 2004||Teem Photonics||Compact apparatus and method for integrated photonic devices having folded directional couplers|
|US6954564||Nov 27, 2001||Oct 11, 2005||Teem Photonics||Apparatus and method for integrated photonic devices having high-performance waveguides and multicompositional substrates|
|US6970494||Jan 25, 2000||Nov 29, 2005||Teem Photonics, S.A.||Rare-earth doped phosphate-glass lasers and associated methods|
|US20020085270 *||Nov 27, 2001||Jul 4, 2002||Bendett Mark P.||Apparatus and method for integrated photonic devices having add/drop ports and gain|
|US20020131746 *||Mar 15, 2002||Sep 19, 2002||The Regents Of The University Of California||Compact cladding-pumped planar waveguide amplifier and fabrication method|
|US20030185514 *||Mar 29, 2002||Oct 2, 2003||Bendett Mark P.||Method and apparatus for tapping a waveguide on a substrate|
|US20030196455 *||Apr 17, 2002||Oct 23, 2003||Mccov Michael A.||Apparatus and method for photonic waveguide fabrication|
|US20040208579 *||Mar 29, 2002||Oct 21, 2004||Bendett Mark P.||Compact apparatus and method for integrated photonic devices having folded directional couplers|
|International Classification||G02B6/12, H01S3/16, H01S3/063, G02B6/134|
|Cooperative Classification||G02B2006/1204, H01S3/1603, H01S3/063, H01S3/1671, G02B2006/12121, G02B6/1342|
|Aug 27, 1998||AS||Assignment|
Owner name: GOVERNMENT OF THE UNITED STATES OF AMERICA, AS REP
Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:SANFORD, NORMAN A.;AUST, JOHN ANDREW;REEL/FRAME:009468/0920;SIGNING DATES FROM 19980819 TO 19980821