|Publication number||USH1934 H1|
|Application number||US 08/539,491|
|Publication date||Jan 2, 2001|
|Filing date||Oct 6, 1995|
|Priority date||May 1, 1992|
|Publication number||08539491, 539491, US H1934 H1, US H1934H1, US-H1-H1934, USH1934 H1, USH1934H1|
|Inventors||Mindaugas Fernand Dautartas|
|Original Assignee||Lucent Technologies, Inc.|
|Export Citation||BiBTeX, EndNote, RefMan|
|Patent Citations (8), Non-Patent Citations (1), Referenced by (8), Classifications (9), Legal Events (1)|
|External Links: USPTO, USPTO Assignment, Espacenet|
This application is a continuation of application Ser. No. 07/877,335, filed on May 1, 1992, which is a continuation-in-part of application Ser. No. 47,169, filed on Apr. 12, 1993, with both now abandoned.
1. Technical Field
The present invention relates to a gold-tin solder and, more particularly, to a tin-rich, gold-tin solder.
2. Description of the Prior Art
Soldering is a well-known technique for securing metal piece parts in a permanent fashion. Solder material must have the capacity to form metallurgical bonds with the two base metals that are to be joined. The bonding process results in the formation of an alloy in the surface of the base metal characterized by atoms of the soldering composition interspersed between atoms of the base metal.
When the solder is heated to a molten state, it exists as a round droplet as a result of the attraction between the molecules forming the alloy. This attraction is commonly referred to as surface tension. For many technologically advanced applications, such as semiconductor and lightwave technologies, a solder composition of choice is a eutectic gold-tin material which is approximately 80% by weight gold and 20% by weight tin. The eutectic god-tin is often used in soldering components to gold (or gold-plated) bond pad sites.
In a conventional solder process, discrete portions, or preforms of the solder material are disposed or otherwise deposited (e.g., vapor deposition or silk screen paste )on a surface of one of the pieces to be mated (for example, to the bond pad site). The two pieces are joined and heated to a temperature where the solder liquifies (i.e., approximately 315° C. in a nitrogen ambient) and reflows over the mating surfaces to provide attachment upon cooling.
There are many known disadvantages to this procedure. First, the reproducibility of the reflow is questionable and sensitive to process variations, particularly since commonly available eutectic Au/Sn solder may only be guaranteed ±1% around the eutectic 80/20 composition. Additionally, the solid state diffusion of tin into an underlying gold bond pad will shift the preform composition to the gold-rich side of the eutectic and could result in poor reflow by raising the melting temperature of the resulting alloy.
In spite of the above drawbacks, however, Au/Sn remains the solder composition of choice since it is compatible with the materials (in particular, gold) used to plate most device surfaces.
Thus, a need remains in the art for some means of overcoming the various drawbacks associated with the eutectic Au/Sn solder.
The need remaining in the prior art is addressed by the present invention which relates to a gold-tin solder and, more particularly, to a gold-tin solder suitable for self-aligning applications.
In accordance with the teachings of the present invention, a tin-rich Au/Sn solder (Au80-xSn20+x, 0<x≦6) is utilized, preferably in the range of 78/22 to 74/26 (weight % composition). Therefore, if solid state (or liquid state) diffusion of tin into a contacting gold plating layer occurs, the melt temperature will actually drop as the tin is depleted in the solder composition, until the eutectic composition is reached. The use of the tin-rich solder thus insures that the alloy will remain molten during solder reflow.
Further, the soldering process of the present invention may be optimized by heating the solder preform within a reducing ambient such that the further growth of any tin oxide on the surface of the preform (skin oxide) is significantly reduced.
An advantage of the solder composition of the present invention is that self-alignment of piece parts may be achieved. In particular, the utilization of a tin-rich solder allows for the solder to remain liquid and completely cover (i.e., “wet”) both bonding surfaces. Therefore, by controlling the size and location of the bonding surfaces, the liquification of the tin-rich solder will result, through surface tension effects, in registration (i.e., centering) of the device with respect to the underlying bond pad.
Other advantages of the present invention will become apparent during the course of the following discussion and by reference to the accompanying drawings.
Referring now to the drawings, where like numerals represent like parts in several views:
FIGS. 1-3 illustrate an exemplary sequence of steps utilized to provide self-aligned solder attachment in accordance with the teachings of the present invention;
FIG. 4 illustrates in particular the self-aligning ability of the system of the present invention;
FIG. 5 contains a Au/Sn phase diagram useful in understanding the process of the present invention;
FIG. 6 contains an optically-scanned, computer-generated image of a photograph of bond pad coverage when utilizing a conventional prior art eutectic Au/Sn solder; and
FIG. 7 contains an optically-scanned, computer-generated image of a photograph of improved bond pad coverage when utilizing an exemplary tin-rich Au/Sn solder of the present invention.
An exemplary process for providing self-aligned solder attachment of a pair of components is illustrated in FIGS. 1-3. The inventive bonding process will be particularly described in association with the self-aligned attachment of an LED to a bond pad. However, it is to be understood that the tin-rich solder of the present invention is ubiquitous in nature and can be utilized within virtually any desired soldering process. Referring back to FIG. 1, a device submount 10, which may be formed of silicon, is illustrated as including a bond pad 12. Conventionally, bond pad 12 is formed of a highly conductive material and, in particular, may comprise a tri-layer structure of titanium, platinum and gold. Gold, in general, is often used for bond pads due to its inert nature and relatively high conductivity. A device 14, such as an LED, is illustrated in FIG. 1 as positioned above bond pad 12. Device 14 also includes a conductive layer 16 (which may also comprise a tri-level, or gold plated layer) to facilitate bonding. In order to provide alignment of device 14 to submount 10, conductive layer 16 should be substantially similar in dimension to bond pad 12.
Bonding is achieved, in accordance with the present invention, by utilizing a tin-rich (with respect to the eutectic 80/20) Au/Sn solder preform 18 which is disposed over and brought into contact with bond pad 12. Initially, solder preform 18 may comprise a solid compound, and exhibit a weight percent composition within the range of, for example, 74/26 to 78/22. To initiate bonding, as shown in FIG. 2, device 14 is brought into contact with solder preform 18 and the combination is heated to a temperature (for example, 400° C.) at which the tin-rich solder will liquify. As the ambient temperature increases, the rate of solid state diffusion of the tin out of solder 18 and into gold layers 12 and 16 will increase, as indicated by the arrows in FIG. 2. The solid state diffusion is also known to occur with the conventional eutectic solder. In particular, problems arise when utilizing the prior art eutectic in that as the tin diffuses out, the solder becomes gold-rich, and the temperature required for liquifying the solder raises. FIG. 5 contains a Au/Sn phase diagram illustrating the effect of the composition on the phase state of the material. Thus, when soldering at the temperature associated with a “eutectic” solder (e.g., 278° C.), a portion of the solder will remain in the solid state and will not completely coat (i.e., “wet”) the underlying bond pad.
In contrast, when utilizing the tin-rich solder of the present invention, the solid state diffusion of tin from solder preform 18 into bond pad 12 and contact layer 16 results in moving the composition closer to the eutectic, as indicated by the arrow in FIG. 5. That is, as the tin is depleted, the temperature required for liquifying the solder actually drops (following along the line from 419.3° C. toward the limit of 278° C.), and essentially all of the solder will remain in the liquid state. FIG. 3 illustrates the relative location of device 14 with respect to the liquified solder preform 18. As shown, when completely liquified, solder 18 will completely cover the top surfaces 20,22 of bond pad 12 and conductive layer 16, respectfully. The surface tension created at the outer bound of solder 18 will cause device 14 to center itself, thus resulting in device 14 to be self-aligned with respect to the underlying bond pad 12.
It is known that the soldering operation such as that discussed above will cause a tin oxide layer to form (or an existing layer to increase) at the outer surface of solder 18. The presence of this oxide may necessarily affect the solder reflow. Thus, in the preferred technique of the present invention, the heating step is performed in a reducing ambient which inhibits the formation of this oxide. For example, formic acid may be used to prevent tin oxide formation. Other reducing environments (indicated as “R.E.” in FIG. 2) include, but are not limited to, forming gas (20%H2/80%N2), carbon monoxide, or any suitable liquid flux.
As mentioned above, an advantage of utilizing the tin-rich solder of the present invention is the ability to provide automatic alignment of a device to an underlying bond pad. Referring to FIG. 3 in particular, the tin-rich solder allows for a device 14 to be aligned with bond pad 12. The coverage of liquified solder 18 with respect to surfaces 20 and 22 of bond areas results in alignment since the solder material will naturally move so as to reduce its overall surface area. Reference is made to FIG. 4 which illustrates a device 14′ offset with respect to the underlying bond pad 12. As shown, liquified solder 18 will exhibit an increased surface area with respect to a minimum, as a function of the amount of offset. Thus, the liquified solder will naturally move, in the direction as indicated by the arrows, so as to minimize the surface area. The natural tendency of the solder movement thus results in alignment of the device to the bond pad. Experimentally, it has been found that misalignment on the order of 100 μm can be corrected to within a one μm limit.
FIGS. 6 and 7 contain top views of actual bond pad sites including a reflowed solder preform (original preform being circular in shape). Both figures are optically-scanned, computer-generated images taken from actual color photographs. The bond pad of FIG. 6 contains a conventional eutectic 80/20 Au/Sn solder after reflow. As shown, the solder does not completely coat the surface of the bond pad. As discussed above, the out-diffusion of tin into the bond pad results in a gold-rich solder which does not completely liquify and, hence, has poor reflow qualities. In contrast, the bond pad of FIG. 7 contains a tin-rich (76/24) solder of the present invention. As shown, essentially all of the bond pad surface has been coated with the reflowed material.
Advantageously, the utilization of a tin-rich solder in accordance with the present invention results in a significant manufacturing achievement. In particular, by virtue of using a tin-rich solder, a bonding hierarchy may be employed, without the need of first employing a soldering hierarchy. That is, as one proceeds through sequential bonding operations, all using the same solder and bonding compositions, previous bonds will not be disturbed (i.e., reflow).
As long as the component and/or substrate is conventionally metallized (with Ti/Pt/Au or Ti/Ni/Au, for example), the utilization of the tin-rich solder of the present invention results in the intermetallic compound formation of Pt with Sn (when using Ti/Pt/Au) as well as interdiffusion of Sn into the Au metallization. Both of these processes result in significantly raising the melt temperature of the resultant bond, to above 400° C., for example.
Therefore, when the next component is bonded, using the tin-rich solder again, at a nominal temperature of 315° C., the first component will remain fixed, since bonding was carried out at a temperature well below the melt temperature. The process may be repeated time and again, without disturbing any of the previously-formed bonds. Such an advantage, realized by using the tin-rich solder compound of the present invention, is especially critical in optical applications, where alignment of bonded components cannot be subjected to movement subsequent to bonding.
It is to be understood that the arrangement described above is exemplary only, and the tin-rich Au/Sn solder of the present invention is applicable to any system which requires the soldering of a component to a gold, or gold-plated bond pad.
|Cited Patent||Filing date||Publication date||Applicant||Title|
|US3340602 *||Feb 1, 1965||Sep 12, 1967||Philco Ford Corp||Process for sealing|
|US4214904 *||Dec 12, 1978||Jul 29, 1980||The United States Of America As Represented By The Secretary Of The Air Force||Gold-tin-silicon alloy for brazing silicon to metal|
|US4385029 *||Apr 27, 1981||May 24, 1983||The United States Of America As Represented By The Secretary Of The Navy||Gold based compounds for electrical contact materials|
|US4670217||Jul 26, 1985||Jun 2, 1987||J. W. Harris Company||Solder composition|
|US4922322||Feb 9, 1989||May 1, 1990||National Semiconductor Corporation||Bump structure for reflow bonding of IC devices|
|US5066614||Sep 28, 1990||Nov 19, 1991||Honeywell Inc.||Method of manufacturing a leadframe having conductive elements preformed with solder bumps|
|JPS5516525A||Title not available|
|RU406673A||Title not available|
|Citing Patent||Filing date||Publication date||Applicant||Title|
|US7114644||Feb 11, 2005||Oct 3, 2006||Tanaka Kikinzoku Kogyo K.K.||Joining method by Au-Sn brazing material|
|US7495333 *||May 6, 2005||Feb 24, 2009||Tanaka Kikinzoku Kogyo K.K.||Seal cover structure comprising a nickel-tin (Ni—Sn) alloy barrier layer formed between a nickel (Ni) plating layer and a gold-tin (Au—Sn) brazing layer having Sn content of 20.65 to 25 WT % formed on the seal cover main body|
|US9721913 *||Aug 18, 2016||Aug 1, 2017||Chipmos Technologies Inc||Semiconductor package and method of manufacturing thereof|
|US20040029304 *||Aug 5, 2003||Feb 12, 2004||Intel Corporation||Packaging of multiple active optical devices|
|US20050184135 *||Feb 11, 2005||Aug 25, 2005||Tanaka Kikinzoku Kogyo K.K.||Joining method by Au-Sn brazing material|
|US20060001172 *||May 6, 2005||Jan 5, 2006||Tanaka Kikinzoku Kogyo K.K.||Hermetic seal cover and manufacturing method thereof|
|US20080096365 *||Oct 20, 2006||Apr 24, 2008||Cree, Inc.||Permanent wafer bonding using metal alloy preform discs|
|EP1591191A1 *||Feb 10, 2005||Nov 2, 2005||Tanaka Kikinzoku Kogyo K.K.||Joining method by Au-Sn brazing material, its thickness being i.a. dependent on the Sn-content|
|U.S. Classification||420/507, 148/430|
|International Classification||B23K35/00, B23K35/30|
|Cooperative Classification||B23K35/001, B23K2035/008, B23K35/3013|
|European Classification||B23K35/00B, B23K35/30C|
|Oct 6, 1995||AS||Assignment|
Owner name: AT&T CORP., NEW YORK
Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNOR:DAUTARTAS, MINDAUGAS F.;REEL/FRAME:007698/0063
Effective date: 19951004