|Publication number||USH1965 H1|
|Application number||US 08/714,876|
|Publication date||Jun 5, 2001|
|Filing date||Sep 17, 1996|
|Priority date||Sep 17, 1996|
|Publication number||08714876, 714876, US H1965 H1, US H1965H1, US-H1-H1965, USH1965 H1, USH1965H1|
|Inventors||William K. Burns, Lew Goldberg, Wayne McElhanon|
|Original Assignee||William K. Burns, Lew Goldberg, Mcelhanon Wayne|
|Export Citation||BiBTeX, EndNote, RefMan|
|Referenced by (22), Classifications (4)|
|External Links: USPTO, USPTO Assignment, Espacenet|
1. Field of the Invention
The present invention relates generally to mid-range infrared (IR) laser sources. More specifically, the present invention relates to mid-range IR laser sources produced by difference-frequency generating (DFG) optical circuits using bulk crystals.
2. Description of the Background Art
Mid-range IR (2-4 μm) sources are of interest in the field of spectroscopy, pollution monitoring, electronic warfare (EW) applications, etc. Adequate sources in this wavelength range generally do not exist. Filament, or black body emitters, have low, uncollimated power and provide poor spectral resolution. Semiconductor laser sources require low temperature operation and have limited tunability.
Tunable laser-like sources are generally obtained from optical parametric oscillators (OPO's), which have been available for some time. However these usually have kilowatt power thresholds, which require complicated Q-switched lasers. Often, these lasers must be water cooled. OPO's are usually thermally tuned, often up to 180 degrees C; thus tuning is slow. OPO's are generally considered laboratory setups, as opposed to portable instruments.
Difference frequency generation (DFG), i.e., the subtraction of photons from two laser inputs, has also been used for IR generation. Such nonlinear processes must be phase matched for efficient conversion. It will be appreciated that birefringence phase matching in birefringent crystals is typically used. Characteristic outputs have been low (≈50 μW) and these outputs not widely tunable due primarily to limitations of bifringence phase matching.
U.S. Pat. No. 5,434,700 discloses an optical wavelength converter formed from semiconductor materials. This patent also discusses a number of other publications which are cited therein, including a reference by Hermann et al., which discusses the use of a lithium niobate material for difference-frequency generation of tunable, mid-infrared radiation, and the Lim et al. reference, which allegedly discloses the use of a periodically poled lithium niobate waveguide for generating infrared radiation by quasi-phase-matched, difference-frequency mixing.
U.S. Pat. No. 5,412,502 discloses a quasi-phase-matching second harmonic generating optical element. Although this patent is directed to second harmonic generation, as opposed to difference-frequency generation, it will be appreciated that such non-linear ferroelectric optical elements can be used for both applications. In particular, this patent discloses a non-linear ferroelectric optical element, which may be lithium niobate, that is periodically poled, and notes that “inclining the substrate allows the wavelength to be adjusted” to compensate for the dispersion of the semiconductor laser.
U.S. Pat. No. 5,504,616 discloses a wavelength conversion device formed by adding a laser-active material to a non-linear optical crystal. In the Background section, it is noted that the same type of nonlinear optical crystals as are used for second harmonic generation can be used for difference-frequency generation when two different wavelengths are input to the crystal.
U.S. Pat. No. 5,506,722 discloses an optical wavelength converting device utilizing a non-linear periodically poled optical device. Of particular interest is the disclosure of the electromagnetic domains formed in the crystal being rotated relative to the crystal faces.
U.S. Pat. No. 5,058,970 discloses a quasi-phase matching optical waveguide. As discussed therein with reference to FIG. 6, where the width and spacing of the electromagnetic domains are respectively uniform, the substrate may be rotated in order to lengthen or shorten the optical path, while still providing efficient generation of a second harmonic output.
It will be appreciated that these patents are generally directed to low power optical waveguide devices not suited to the output power requirements of many industrial and military applications.
The principal purpose of the present invention is to overcome the express and implicit limitations of the previously developed mid-range IR generators.
An object according to the present invention is to produce a laser system applying a difference-frequency generation (DFG) process which provides a narrow bandwidth resultant output responsive to fixed and variable inputs. According to one aspect of the invention, a bulk, quasi-periodic phase-matched difference-frequency generation (DFG) process in field-poled LiNbO3 bulk crystal permits continuous tunability of the output radiation in the 3.0-4.1 μm wavelength range through grating rotation.
Another object according to the present invention is to provide a laser system applying a difference-frequency generation (DFG) process which provides a broad bandwidth resultant output responsive to fixed and variable inputs.
According to another aspect of the present invention, DFG in QPM-LiNbO3 carried out using a Nd:YAG laser and a high power semi-conductor laser at the quasi-phased matched (QPM) degeneracy point results in an ultra wide 0.5 μm acceptance bandwidth, permitting crystal rotation-free wavelength tuning of 4.0-4.5 μm, with 0.2 mW output power at 4.5 μm.
These and other objects, features and advantages according to the present invention are provided by a combination generating a resultant laser beam of desired wavelength. Preferably, the combination includes a first laser device generating a first beam of adjustable wavelength, a second laser device generating a second beam of fixed wavelength, a periodically poled non-linear crystal receiving the first and second beams at one face of the crystal and a rotating mechanism for rotating the crystal so as to control the angle of incidence of the first and second beams with respect to the face of the crystal so as to permit the first and the second beams to combine and thereby form the resultant beam.
These and other objects, features and advantages according to the present invention are provided by a combination generating a resultant laser beam in a desired wavelength range. Preferably, the combination includes a first laser device generating a first beam of adjustable wavelength, a second laser device generating a second beam of fixed wavelength, and a periodically poled non-linear crystal receiving the first and second beams at one face of the crystal, wherein the period of the crystal is substantially equal to but less than the degeneracy point for the crystal, the crystal combining the first and the second beams to thereby form the resultant beam in the desired frequency range.
These and other objects, features and advantages of the invention are disclosed in or will be apparent from the following description of preferred embodiments.
The preferred embodiments are described with reference to the drawings in which like elements are denoted by like or similar numbers and in which:
FIG. 1 is a schematic diagram illustrating a preferred embodiment of a narrowband difference-frequency generating (DFG) optical circuit according to the present invention;
FIG. 2 is a photographic illustration of the etched domain pattern of a bulk crystal which can be employed in the optical circuit of FIG. 1;
FIG. 3 is a graph showing output power with respect to the product of the input lasers for the optical circuit shown in FIG. 1;
FIG. 4 is a graph illustrating the relationship between output wavelength and rotation angle for the optical circuit of FIG. 1;
FIG. 5 is a graph depicting DFG power with respect to wavelength for the optical circuit of FIG. 1;
FIG. 6 is a graph showing DFG power with respect to lateral position in the optical circuit of FIG. 1;
FIG. 7 is a schematic diagram illustrating another preferred embodiment for a narrowband DFG optical circuit according to the present invention;
FIG. 8 is a graph illustrating DFG power with respect to pump power product for the optical circuit of FIG. 7, wherein the included insert illustrates actual and theoretical phasematching bandwidths for a selected grating;
FIG. 9 is a graph illustrating the output DFG wavelength with respect to the external angle of the bulk crystal for the optical circuit of FIG. 7;
FIG. 10 is a graph illustrating DFG output power with respect to output (difference) wavelength for the optical circuit for a typical fixed pump beam DFG apparatus; and
FIG. 11 is a graph illustrating DFG output power with respect to DFG output wavelength for the optical circuit of FIG. 7.
Coherent optical sources are required throughout the 2-5 μm mid-IR wavelength range for a wide range of industrial applications, e.g., fiber-optic chemical sensors, biomedical technology, chemical analysis, high-resolution spectroscopy, industrial process monitoring, and atmospheric and environmental sensing. Although laser diodes are available at some of the wavelengths of interest, laser diodes require low-temperature operation and exhibit poor spectral characteristics, with narrow discontinuous tuning ranges. Desirable mid-IR source characteristics include compactness, high efficiency, narrow linewidth, and wide, continuous, and rapid tunability. Sources based on difference-frequency generation (DFG) advantageously can meet all of these requirements if near-IR laser diodes are used as pump sources. It will be appreciated that, in one implementation, a 50 -μW output was generated at 4.3 μm by the mixing of the emission of a Ti:Al2O3 laser and the emission of a high-power semiconductor amplifier in AgGaS2. Significant increases in DFG power were also achieved by intracavity mixing in a Nd:YAG laser.
Although appropriate nonlinear materials for carrying out DFG in the 2-5 μm range are available, the alternative use of quasi-phase matching (QPM) in LiNbO3 has only recently been investigated. It will be appreciated that the advantages of QPM in LiNbO3 are its high nonlinear coefficient d33, zero walk-off angle, low material costs and large available crystal sizes, good transparency at pump wavelengths, and well-established fabrication techniques for waveguides, which features are all required for high conversion efficiencies with low-power laser-diode pumps. DFG by use of Nd:YAG and Ti:Al2O3 lasers and a periodically surface-poled LiNbO3 waveguide has been demonstrated and produced 1.8 μW of output power at 2.1 μm.
In addition to surface poling, which is appropriate for waveguide frequency conversion, bulk periodic poling advantageously can be used when much greater power-handling capabilities are required. Bulk QPM frequency-conversion processes were recently demonstrated in LiNbO3 for use in second-harmonic generation of, for example, blue light, and for a 1.7-3.0 μm optical parametric oscillator pumped by a Q-switched Nd:YAG laser and a laser diode. Bulk poling has also been demonstrated in KTP.
However, a widely tunable DFG in bulk periodically field-poled LiNbO3 has not been previously reported or achieved. Using grating rotation to alter the effective grating period, the emission wavelength advantageously can be varied from 3.0 to 4.1 μm by nonlinear mixing of Nd:YAG and tunable Ti:Al2O3 emissions in a 245 μm thick 6 mm long bulk crystal. As discussed in greater detail below, a maximum DFG output power of 0.5 mW was measured for an optical circuit according to a preferred embodiment of the present invention shown in FIG. 1.
Referring to FIG. 1, the optical circuit, i.e., the DFG device, includes a rotatable crystal 28, which advantageously can be a z-cut LiNbO3 bulk crystal having a metal ground plane electrode on the −c side and a patterned electrode on the +c side. It will be noted that the bulk crystal was field poled using, in an exemplary case, 5.8-kV 500 μs-long pulses. Gratings with periods of Λ=21.2, 22.6, 23.2 μm, calculated for phase matching at pump wavelengths λ3=787, 816, 840 nm, and DFG wavelengths λ13.0, 3.5, and 4.0 μm, respectively, were tested using the optical circuit configuration illustrated in FIG. 1. It will be noted that the device for rotating the bulk crystal advantageously can be any number of suitable electromechanical or mechanical devices such as a turntable 30. An example of the etched grating pattern is shown in FIG. 2.
DFG was achieved in the optical circuit of FIG. 1 by superimposing the λ2=1064 nm emission from a Nd:YAG laser 10 and a tunable Ti:Al2O3 laser 20, using a dichroic beam splitter 22, as shown in FIG. 1. The lamp-pumped cw Nd:YAG laser 10 delivered as much as 4 W of power to the nonlinear crystal 28. This power level is comparable with that obtainable from commercially available diode-pumped Nd:YAG lasers. Similarly, the maximum 426 mW of incident Ti:Al2O3 power used is below that generated by recently developed large-active-area GaAs semiconductor amplifiers. A telescope 18 in the Ti:Al2O3 beam was used to superimpose beam waists longitudinally and to equalize diameters of the two laser beams. Combined beams were focused into the QPM sample by an f=8 cm lens 24. A Gaussian beam waist of ω0=27 μm was produced for the 1064 -nm beam in the horizontal and vertical planes, while beam waists of ω0x=20 μm and ω0y=35 μm were produced in the two planes for the elliptically shaped Ti:Al2O3 beam. These focusing conditions were experimentally found to maximize the DFG power.
The output power for the DFG process of ω1=ω3−ω2 is given by
where k1, k2, and k3 are the wave vectors at the three interacting wavelengths and h(μ, ξ) is the focusing parameter, which is a function of μ=k2/k3 and the ratio ξ=L/b of the interaction length L to the confocal parameter b. It should be mentioned that equation (1) applies when the confocal parameters of the two input beams are equal. For the exemplary case under discussion, b=2πω02n/λ=9.5 mm at 1064 nm and b=13 mm at 787 nm, given a mean Gaussian waist ω0=(ω0x+ω0y)/2 =27.5 μm for the Ti:Al2O3 beam. Approximating the confocal parameter for the two input beams by a mean value of ba=11 mm, corresponding to ξ=0.55, a focusing parameter value of h(μ, ξ)≈0.26 can be estimated using μ=0.74 and plots shown in the article by P. Canarelli et al. which was published in the Journal of the Optical Society of America at Vol. B 9, page 197 (1992), which reference is incorporated herein by reference for all purposes. It will be appreciated that this is only slightly smaller than the maximum value of h≈0.3 predicted for optimum focusing corresponding to ξ≈1.3.
It should also be mentioned that, using Millers delta value corresponding to a nonlinear coefficient of d33=27 pm/V measured for 1064 nm frequency doubling, a nonlinear coefficient of d33=24 pm/V for DFG at λ1=3.0 μm, which corresponds to an effective nonlinear coefficient of deff=2d33/π=15 pm/V for the QPM process, can be calculated. For interaction length L=6 mm and P2P3=1 W2, Eq. (1) predicts that P1=0.61 mW, which corresponds to a length—normalized slope efficiency of η=1.0 mW/(CM W2) [0.10%/(W cm)]. After correction for reflective losses at the input and output facets, a slope efficiency of 0.65 mW/(cm W2) is predicted for the exemplary case under discussion.
Measured values of DFG power at 3.0 μm generated in a Λ=21.2 μm grating are plotted as a function of the input power product P2P3 in FIG. 3. It should be mentioned that the first five data points were derived at a fixed P2=1.0 W, whereas all other points, except for the last data point, were taken with P2=2.0 W. A maximum of P1=450 μW was measured at P2=4.0 W, P3=0.42 W. The DFG power versus P2P3 dependence was linear, with a length—normalized slope efficiency of η=048 mW/(cm W2). It will be appreciated that this is in good agreement with the value calculated using Eq. (1), particularly in view of the elliptical shape of the λ3 beam. The close-to-theoretical DFG power is evidence of the near-ideal geometry of the fabricated QPM grating. Similar results were obtained at λ1=3.5 μm in the Λ=22.6 μm grating. Grating quality was further verified when, in a different experimental arrangement (not illustrated), the phase-matching bandwidth for the Λ=21.2 μm grating was measured to be 1.2 nm full-width half-maximum (FWHM) beam width, which is substantially equal to that calculated for a 6.0 mm interaction length.
Using the optical circuit illustrated in FIG. 1, the DFG wavelength was varied by tuning the Ti:Al2O3 laser and rotating the bulk crystal 28, to thereby change the input beam incidence angle θ and the effective grating period. As shown in FIG. 4, continuous wavelength coverage extended from 3.0 μm at θ=0° and λ3=787 nm to 4.1 μm at θ=55° and λ3=844 nm. For comparison, angle-tuning characteristics calculated by use of published Sellmeier coefficients are also shown.
Measured and calculated variations of the relative DFG output power with the DFG wavelength are shown in FIG. 5, wherein the dashed curve represents the wavelength dependence of Eq. (1) with the wave length dependence of the refractive index and h being neglected. In FIG. 5, the solid curve represents the combined effects of the wavelength dependence of Eq. (1) and variations of facet reflectivity and beam path length inside the active region with θ. Although there is good agreement between the measurement and calculation for λ1≦3.2 μm (θ≦26°), a more-rapid-than-predicted falloff in P1 occurs at the longer wavelengths. Apparently, this rapid falloff is primarily due to a reduction of the acceptance angle and partially due to an increased pump beam ellipticity and astigmatism at large incidence angles. At normal incidence ((θ=0°) the calculated half-acceptance angle (defined as the interior angle at which P1 is down by 3 dB) of θa=3.2° is in good agreement with the measured value of θa=3.5°. It should be noted that at large values of θ, the acceptance angle is significantly reduced owing to a more rapid change of the effective grating period with increasing θ. For example, at θ=50° (21° inside the bulk crystal) it is estimated that θ=0.25°, which is less than the 0.32° full-divergence angle (1/e2 power points) of a λ=787 nm Gaussian beam with ω0x=20 μm. A less rapid falloff in P1 versus λ1 dependence advantageously may be achieved by increasing the input beam waists to reduce beam divergence. In addition, the power drop that is due to increased facet reflectivity and beam ellipticity at large θ advantageously can be reduced by polishing the facets of the bulk crystal 28 at an offset angle relative to the grating, so that achieving the maximum effective grating period for generation of 4.1 μm output would require a smaller incidence angle. It should also be noted that good uniformity of the QPM region was verified by measuring P1 at θ=0° while translating the bulk crystal 28 in the lateral direction. The results, which are shown in FIG. 6, exhibit a less than 10% power variation across the entire 2-mm active-region width, indicating a less than 5% variation in deff.
As discussed above, coherent 2-5 μm mid-IR sources are required for applications such as fiberoptic chemical sensors, spectroscopy, industrial process monitoring atmospheric and environmental monitoring. It will be appreciated that the required source characteristics include narrow spectral width (100 MHz is typically desirable), room temperature operation, compactness, high efficiency, wide and continuous tuning. These requirements cannot be directly met by typical semiconductor lasers, but can be satisfied by difference frequency generation (DFG) using semiconductor lasers or diode pumped solid state lasers. Compared with tunable optical parametric oscillators (OPO), DFG process devices have no oscillation threshold and therefore can produce a continuous wave (cw) using available laser diodes or diode pumped solid state lasers, generate narrowband emission, and have a simple optical configuration.
Although birefringently phasematched nonlinear materials for 2-5 μm DFG are available, the alternative use of quasi phasematching (QPM) in LiNbO3 offers advantages of high nonlinear coefficient d33, noncritical phasematching with zero walk-off, low material costs, and good transparency at pump wavelengths. Bulk poled QPM-LiNbO3 can be used to generate 0.5 mW at 3.0 μm by DFG of Ti:Al2O3 and Nd:YAG laser, as disclosed immediately above, and in OPO's pumped by a high power Nd:YAG amplifiers and laser diodes. Alternatively, a practical mid-IR DFG source can be provided using a high power, external cavity semiconductor laser and a Nd:YAG laser, as discussed immediately below.
QPM LiNbO3 exhibits an ultra-wide phasematching bandwidth of approximately 500 nm when operated at the wavelength vs. effective domain period degeneracy point. This unique property is absent in conventional, birefringently phasematched materials where typical phasematching bandwidths are more than two orders of magnitude smaller. The wide acceptance bandwidth allows single knob wavelength tuning from 4-4.5 μm by varying the wavelength of one of the mixing sources, without requiring adjustments of the QPM crystal angle. A maximum of 0.2 mW was generated at 4.5 μm, which power is significantly higher than that generated by previous laser diode and solid state laser pumped DFG devices.
It should be noted that a DFG wavelength coverage of λ1=3.0-5.5 μm can be demonstrated using a Ti:AL2O3 laser in a single QPM crystal using angle tuning.
FIG. 7 shows a DFG optical circuit according to another preferred embodiment of the present invention, including first and second output lasers 110, 120. Preferably, λ2=1064 nm laser emission from a first, Nd:YAG laser source 110, is combined with that of a cw external cavity semiconductor laser 120 using a dichroic beam splitter 122. Advantageously, the laser 120 can be a tapered GaAlAs amplifier-external cavity laser, although other laser sources are also usable. More specifically, the compound external cavity of the semiconductor laser may contain a GaAlAs tapered stripe amplifier 112 with a 130 μm output aperture and a peak gain near 855 nm, a diffraction grating 114 for tuning, and a single stripe semiconductor amplifier 116. It will be appreciated that although a diffraction grating alone can be used to provide optical feedback required to achieve laser actions, the narrow stripe amplifier 116 lowers the lasing threshold while increasing output power available. The laser threshold occurs at a tapered amplifier current of I=1.1 A, and the output power (exiting the amplifier) is 820 mW at I=2.0 A, with 0.5 W transmitted to the QPM bulk crystal. As noted in FIG. 7, the output of laser 110 is provided to beam splitter 122 via a Faraday isolator 126.
Referring again to FIG. 7, the pump beams are focused by a f=8 cm lens 124, producing a 29 μm FWHM beam waist (ω0=25 μm) at the center of a 245 μm thick, 6 mm long, bulk field poled QPM LiNbO3 crystal 128. The z cut crystals, with a patterned electrode on the +c side, preferably are field poled using 5.8 kV, 500 μsec pulses. It should be mentioned that samples with QPM domain periods of Λ=22.6 and 21.2 μm, designed for phasematching at λ1=3.5 μm and λ1=3.0 μm, respectively, were used in the optical circuit of FIG. 7.
DFG power at λ1=4,.47 μm, generated by tuning the semiconductor laser to λ3+859.4 nm, is shown as a function of the pump power product P2P3 in FIG. 8, where P3=0.48 W and the Nd:YAG power P2 was varied. For phasematching, the effective QPM period Λe advantageously can be changed by rotating a Λ=22.6 μn samples by θ=18° (θ1=8.2° internal angle) in the x-y plane, relative to the facet normal, resulting in an effective period of Λe=Λ/cos θi=22.8 μm. It should be noted that a maximum of 0.2 mW was generated by the optical circuit of FIG. 7 for P2=5.0 W with a normalized nonlinear conversion efficiency of 0.015%/W cm. The theoretical efficiency was calculated using d33=22 pm/V, obtained from Miller's delta rule and d33=27 pm/V for 1064 nm second harmonic generation (SHG). For the focusing conditions associated with the optical circuit of FIG. 7, corresponding to an average confocal parameter b=2πω0n/λ=8.7 mm (2λ=λ2+λ3) an estimated Boyd & Kleinman focusing parameter of h=0.28 is obtained, yielding an efficiency of 0.022%/W cm. Accounting for facet reflective losses, this predicts an efficiency of 0.014%/W cm, which is in agreement with actually measured values. It should also be noted that a quality output was verified by measuring the phasematching bandwidth, shown for a Λ=21.2 grating, which grating was designed for phasematching at λ1=786 nm, λ1=3.0 μm, as illustrated in the insert of FIG. 8. The 1.2 nm FWHM of the sinc2 dependence equals that calculated using published Sellmeier coefficients.
Phasematching wavelength versus θ dependence, measured using a Ti:Al2O3 laser, is shown in FIG. 9 for two grating periods. Also shown is the calculated dependence, where the discrepancy at longer wavelengths is attributed to inaccuracies in the Sellmeier coeffients. A special condition of dθ/dλ, which is equivalent to dΛe/dλ=0, occurs at the degeneracy point of θ=21°, λ1=4.2 μm for the 22.6 μm grating. It should be noted that this important property is a consequence of the fact that the n(λ) dependence has a minimum slope at ≈2.0 μm, and for DFG at λ1≈4.2 μm, λ3≈0.85 μm the phasematching condition 1/Λ=n3/λ3−n2/λ2−n1/λ1 can be maintained over a large wavelength range because the values of dn(λ)/dλ near λ1 and λ3 are such that n3/λ3−n1/λ1 remains relatively constant as λ3 changes. The degeneracy condition dΛe/dλ=0 can be moved to other λ1 wavelengths by choosing a different λ2 pump wavelength.
The ultra-wide phasematching bandwidth near the dΛe/dλ=0 point advantageously allows simple one knob DFG wavelength tuning by varying λ3 only, with no sample rotation required. FIG. 10 shows the fixed-angle tuning range which can be achieved by varying λ3 from 842 nm to 865 nm. The phasematching bandwidth, centered at λ1=4.2 μm, is 0.5 μm FWHM. By way of comparison, the theoretical dependence is also shown. It should be noted that in order to get good agreement with the measured bandwidth, a QPM period of Λ=23.3 μm was assumed. It should also be noted that discrepancies between the actual and theoretical values are attributed to inaccuracies in the Sellmeier coefficients coupled with the fact that the minimum value of λ1 was determined with a 842 nm laser tuning limit.
In addition to rotation free operation near the degeneracy point, the wavelength coverage advantageously can be further extended by sample rotation. As shown in FIG. 9, 3.6-4.8 μm tuning can be achieved with a Λ=22.6 μm QPM sample over an angular range of θ=0-21°, and, as discussed above, a tuning range of 3-4.1 μm was achieved for a Λ=21.2 μm sample. FIG. 11 shows the results of DFG in the range of λ1=3.0-5.5 μm, measured in a Λ=21.2 μm sample using a Ti:Al2O3 laser. Incidence angles were varied from θ=0° at 3.0 μm to a maximum of 54° at 4.2 μm. For purposes of comparison, a theoretical DFG power vs. wavelength dependence is also plotted. The calculation represents the wavelength dependence suggested in various references, and includes variation of d33 and focusing parameter h with λ1 (in contrast with the alternative preferred embodiment discussed above where constant d33 and h were assumed). It will be noted that the smaller than predicted DFG power at longer wavelengths apparently is a consequence of several factors not accounted for in the calculation: increasing facet reflectivity and decreasing acceptance angles for large θ values, and LiNbO3 absorption for λ1>4.5 μm. The theoretical values therefore represent the best case, or the power generated in absence of absorption and for θ=0 at all λ1. As shown in FIG. 11, a maximum power of 0.45 mW was measured at 3.0 μm with 4.0 W of Nd:YAG power and 0.42 W of Ti:Al2O3 power incident on the bulk crystal 28.
In summary, 3.0-4.1 μm tunability and 0.5 mW cw maximum output power were generated using the optical circuit of FIG. 1 using DFG processing in 6-mm-long periodically poled bulk LiNbO3 crystal. It will be appreciated that this represents significant improvements in tuning range and power over previous DFG system results and demonstrates a near-theoretical nonlinear conversion efficiency in field-poled LiNbO3. With increased active region length, output powers in the several-milliwatt range should be possible. It will also be appreciated that this approach is well suited for use with high-power cw semiconductor amplifiers and diode-pumped lasers and offers the possibility for a compact, efficient, room-temperature, widely tunable, narrow-band source required in spectroscopic, monitoring, and sensing applications.
In addition, a practical, widely tunable, mid-IR DFG source advantageously can be fabricated using a high power semiconductor laser, a Nd:YAG laser, and bulk field poled QPM-LiNbO3 crystal operated near the degeneracy point. A DFG power of 0.2 mW and a near-theoretical nonlinear conversion efficiency at 4.5 μm can be obtained with this optical circuit. It should again be noted that QPM LiNbO3 is shown to have an ultra-wide acceptance bandwidth of 0.5 μm near the 4.2 μm wavelength degeneracy point. This unique feature, which is absent in conventional birefringently tuned nonlinear materials, advantageously allows simple single knob DFG wavelength tuning. The wide, rotation-free bandwidth is also important for intracavity DFG where λ2 is fixed and crystal rotation is undesirable because of its effects on the cavity alignment and laser spectrum. The optical circuit illustrated in FIG. 7 and the results obtained using this optical circuit provide a practical, narrowband, tunable mid-IR source for gas sensing and other applications.
Other modifications and variations to the invention will be apparent to those skilled in the art from the foregoing disclosure and teachings. Thus, while only certain embodiments of the invention have been specifically described herein, it will be apparent that numerous modifications may be made thereto without departing from the spirit and scope of the invention.
|Citing Patent||Filing date||Publication date||Applicant||Title|
|US6587486 *||Oct 15, 1998||Jul 1, 2003||Eads Deutschland Gmbh||Laser beam source for a directional infrared countermeasures (DIRCM) weapon system|
|US6904066 *||Nov 13, 2002||Jun 7, 2005||Yen-Chieh Huang||Optical parametric oscillator with distributed feedback grating or distributing Bragg reflector|
|US6975402||Nov 19, 2002||Dec 13, 2005||Sandia National Laboratories||Tunable light source for use in photoacoustic spectrometers|
|US7151787||Sep 10, 2003||Dec 19, 2006||Sandia National Laboratories||Backscatter absorption gas imaging systems and light sources therefore|
|US7177340 *||Nov 4, 2003||Feb 13, 2007||Jds Uniphase Corporation||Extended cavity laser device with bulk transmission grating|
|US7269189 *||Jan 21, 2005||Sep 11, 2007||Cobolt Ab||Coherent light source based on sum-frequency mixing|
|US7362783 *||Jun 13, 2002||Apr 22, 2008||Cobolt Ab||Optical frequency mixing|
|US7375812 *||Feb 22, 2005||May 20, 2008||Axsun Technologies, Inc.||Method and system for reducing parasitic spectral noise in tunable semiconductor source spectroscopy system|
|US7375814||Mar 11, 2005||May 20, 2008||Sandia Corporation||Natural gas leak mapper|
|US7486435||Mar 30, 2007||Feb 3, 2009||Textron Systems Corporation||Multi-port optical parametric oscillator|
|US8339580||Jun 30, 2004||Dec 25, 2012||Lawrence Livermore National Security, Llc||Sensor-guided threat countermeasure system|
|US9012851||Sep 9, 2011||Apr 21, 2015||Thermo Fisher Scientific (Bremen) Gmbh||Optical chamber module assembly|
|US20030123497 *||Nov 13, 2002||Jul 3, 2003||Yen-Chieh Huang||Optical parametric oscillator with distributed feedback grating or distributed Bragg reflector|
|US20040095579 *||Nov 19, 2002||May 20, 2004||Bisson Scott E.||Tunable light source for use in photoacoustic spectrometers|
|US20040165639 *||Nov 4, 2003||Aug 26, 2004||Jds Uniphase Corporation, State Of Incorporation: Delaware||Laser device|
|US20050053104 *||Sep 10, 2003||Mar 10, 2005||Kulp Thomas Jan||Backscatter absorption gas imaging systems and light sources therefore|
|US20060000988 *||Jun 30, 2004||Jan 5, 2006||The Regents Of The University Of California||Sensor-guided threat countermeasure system|
|US20060165136 *||Jan 21, 2005||Jul 27, 2006||Cobolt Ab||Coherent light source based on sum-frequency mixing|
|US20060187457 *||Feb 22, 2005||Aug 24, 2006||Axsun Technologies, Inc.||Method and system for reducing parasitic spectral noise in tunable semiconductor source spectroscopy system|
|US20060203248 *||Mar 11, 2005||Sep 14, 2006||Reichardt Thomas A||Natural gas leak mapper|
|US20070236780 *||Mar 30, 2007||Oct 11, 2007||Textron Systems Corporation||Multi-port optical parametric oscillator|
|USH2197 *||Dec 22, 2004||Aug 7, 2007||The United States Of America As Represented By The Secretary Of The Air Force||Diode-laser-based mid-infrared absorption sensor for carbon monoxide|