|Publication number||USRE31618 E|
|Application number||US 06/369,962|
|Publication date||Jul 3, 1984|
|Filing date||Apr 19, 1982|
|Priority date||Oct 12, 1978|
|Also published as||CA1143105A, CA1143105A1, DE2941279A1, US4306318|
|Publication number||06369962, 369962, US RE31618 E, US RE31618E, US-E-RE31618, USRE31618 E, USRE31618E|
|Inventors||Hiroshi Mano, Toshisaburo Oga|
|Original Assignee||Sumitomo Electric Industries, Ltd.|
|Export Citation||BiBTeX, EndNote, RefMan|
|Patent Citations (5), Referenced by (83), Classifications (10)|
|External Links: USPTO, USPTO Assignment, Espacenet|
1. Field of the Invention
This invention relates to an improvement in and relating to a tubular organic prosthesis composed of a porous tubing of polytetrafluoroethylene (abbreviated "PTFE"), and is directed to increasing the strength of the tubing and its ability to connect with the tissues of a patient.
2. Description of the Prior Art
Many reports have been made heretofore to show that a porous tubing of PTFE produced by a stretching method can be clinically used as a tubular organic prosthesis, especially as a vascular prosthesis. Such a prosthesis is regarded as better than conventional prostheses made of knitted or woven fabrics. A PTFE tubing which has been subjected to a stretching treatment has a microstructure composed of very fine fibers and nodes connected to one another by the fibers. The diameters of the fibers vary depending on stretching conditions, and can be made much smaller than those of the fibers of the knitted or woven fabrics mentioned above. Moreover, since the pore diameter and porosity of the tubing can be varied freely, when it is used, for example, as an artifical vessel, it is pliable and scarcely permits formation of thrombus. The tubing also shows good formation of a pseudointima on the inner surface without any appreciable adverse effect on the surrounding tissues. Thus, the stretched tubing is regarded as one of the best prostheses for tubular organs.
The stretched PTFE tubing, however, has the disadvantage that when it is used as a tubular organic prosthesis and joined with the living body, the needle or suture tends to tear the tubing. This tearing frequently occurs in the axial direction of the porous PTFE tubing. Since this is due to the orientation of the fine PTFE fibers formed as a result of stretching, it can be reduced to some extent by biaxially stretching the tubing, namely stretching it in the axial direction and expanding its diameter, thereby to change the structure of the fine fibers to a radial orientation. A great improvement in strength, however, cannot be expected from this process alone. Furthermore, it is difficult for natural occlusion of suture holes to occur based on the elasticity of the porous PTFE tubing alone, and when it is used as an artificial vessel, bleeding from the suture holes is also a problem. Further, when it is sharply bent it buckles and cannot retain a cylindrical shape. This is also a drawback in practical application.
The present invention offers a solution to these problems in a junction operation.
It is an object of this invention to provide a tubular organic prosthesis comprising a porous PTFE tubing and elastic fibers provided helically on its outside surface.
Another object of this invention is to provide a tubular organic prosthesis which permits easy entry and attachment of the surrounding tissues to promote the assimilation of the prosthesis.
According to this invention, there is provided a tubular organic prosthesis comprising a porous tubing of polytetrafluoroethylene and elastic fibers provided helically on its outside surface.
In another aspect, the invention provides a process for producing a tubular organic prosthesis which comprises wrapping elastic fibers helically about the outside surface of a porous tubing of polytetrafluoroethylene, impregnating the resulting structure with a solvent capable of dissolving or swelling the elastic fibers to thereby bond them to the PTFE tubing, drying the structure, and then heat-setting.
The FIGURE is a side view of the tubular prosthesis showing the essential elements thereof. Said tubular prosthesis is provided with a body of porous PTFE 1, which body is helically provided with elastic fibers upon its outer surface 2.
As a result of providing elastic fibers helically on the outside surface of the porous PTFE tubing, the porous PTFE tubing of the present invention does not undergo tearing by a joining needle or suture. It also has the advantage that when the tubing together with the elastic fibers is sutured at the time of a junction operation, the holes left after joining are occluded by the elasticity of the fibers. Furthermore, since the elastic fibers are helically oriented, the tubing is pliable in the longitudinal direction, and even when it is sharply bent, it does not easily buckle. In addition, spaces for easy entry of the surrounding tissues of a patient are available on the outside surface of the tubing and this accelerate the assimilation of the porous PTFE tubing as an organic prosthesis.
The porous tubing of PTFE in accordance with this invention is produced by the method described in Japanese Patent Publication No. 13560/67 and, e.g., U.S. Pat. Nos. 3,953,566 and 3,962,153. A liquid lubricant is mixed with an unsintered powder of polytetrafluoroethylene and the mixture is extruded into a tubular form by a ram-type extruder. The PTFE used in this invention preferably has a molecular weight of 106 to 107. The tubing is stretched at least monoaxially after the liquid lubricant is optionally removed. Preferably, the tubing is stretched in the axial direction, and its diameter is expanded. The tubing is heated at a temperature above 327° C. which is the sintering temperature while fixing it in place to avoid shrinkage. Thus, the stretched and expanded structure is fixed and a tubing having increased strength is obtained. The resulting porous PTFE tubing has a microstructure composed of very fine fibers and nodes connected to one another by these fibers. Because the diameters and lengths of these fibers and the sizes and number of the nodes can be varied depending upon the stretching and sintering conditions, the pore diameter and porosity of the resulting porous tubing can be determined freely. It has been clinically confirmed that when this tubing is used as a vascular prosthesis, it suitably has an average pore diameter of about 2 μm to about 100 μm, a porosity of at least about 70%, and a wall thickness of about 0.3 to 1.0 mm.
In the microstructure of the porous PTFE tubing preferred in this invention, the fibers are distributed not unidirectionally but radially. This fibrous structure is obtained by biaxially stretching the PTFE tubing, namely by stretching it in the axial direction and expanding its diameter. Expansion of its diameter can be achieved by reducing the pressure on the outside surface of the tubing, or pressing its inside surface, or simultaneously performing these two procedures, while heating. Alternatively, the diameter of the tubing may be mechanically enlarged by passing an article of a suitable configuration through the inside of the tubing. Stretching of the tubing in the axial direction and expansion of its diameter are carried out simultaneously or successively, or may be carried out simultaneously with the final sintering step. The porous PTFE tubing obtained by the biaxial stretching method is more pliable and less prone to longitudinal tearing than a porous PTFE tubing stretched only in the axial direction because the fibers are distributed not only in the axial direction but radially in all directions. However, to perform a junction operation using this biaxially stretched porous PTFE tubing, more improvements in strength, natural occlusion of the suture holes, bending property, and the ability to connect with the tissues of a patient are desired.
In accordance with this invention elastic fibers are helically provided on the outside surface of the porous PTFE tubing to solve the aforesaid problems.
The elastic fibers are fibers produced from at least 50% elastomer. They include polyurethane fibers and fibers from various rubbers (so-called rubber yarns), e.g., silicone rubbers, fluorine rubbers, acrylic rubbers, natural rubber, etc. Examples of non-elastomers which may be present in combination with the elastomers include polyamides, polyesters, polypropylenes, etc. The elastic fibers used in this invention are described in detail below with reference to polyurethane fibers which constitute a preferred embodiment of the present invention. Substantially the same description will apply to other elastic fibers.
Preferably fibers are selected and wrapped around the prosthesis to give it a suture tear resistance of at least 300 g/ply. The polyurethane elastic fibers are made from an organic diisocyanate and a polyether or polyester and are characterized by their elasticity. Polyurethane fibers normally used for apparel are also suitable for the purposes of this invention. Polyurethane elastic fibers of the polyether type are especially suitable for organic prostheses.
The fibers may be in the form of monofilaments or multifilaments. Not only bare yarns of polyurethane but also processed or modified yarns can be used to achieve the objects of this invention. Commercally available processed yarns include covered yarns having other fibers wrapped thereabout, core spun yarns having polyurethane fibers as a core, ply yarns, etc. All of these yarns can be used in this invention. The polyurethane elastic yarns usually have a tensile strength of about 1 to 1.5 g/denier (ASTM D-638) and those having a size of about 150 denier to about 5,000 denier are effective.
To provide the elastic fibers helically on the outside surface of the porous PTFE tubing, the fibers are first helically wrapped about the outside surface of the tubing. The fibers may be wrapped in close contact with one another, or at some interval, preferably not exceeding the diameter of the prosthesis. A suitable thickness of the fiber wrapping ranges from about 0.05 mm to about 1 mm.
After wrapping, the fibers are impregnated with a solvent capable of dissolving or swelling the elastic fibers to dissolve the elastic fibers partly and bond them to the PTFE tubing. Suitable solvents for the polyurethane elastic fibers include phenol, m-cresol, benzene, toluene, formic acid, tetrahydrofuran, N,N-dimethylformamide and N,N-dimethylacetamide. The structure impregnated with the solvent is dried, and then heated at a suitable temperature to heat-set it. This heat-setting relaxes the residual stress of the helically wrapped elastic fibers, and sets their configuration. The heat-setting temperature and time are determined according to the material of the elastic fibers. In the case of polyurethane elastic fibers, heat-setting is usually carried out at a temperature of about 120° to 230° C. for a period of 1 to 60 minutes. Heating may be effected in air or with steam or the like.
The tubular organic prosthesis of this invention described hereinabove is very useful as an artificial vessel, but can also be used for the prosthesis of other tubular organs including the esophagus, trachea, biliary duct, ureter, and urethra.
The following Examples illustrate the present invention more specifically. It should be understood that the scope of the invention is not limited by these Examples.
One hundred parts by weight of fine PTFE powder, Polyflon F-104 (a trademark for a product of Daikin Kogyo Co., Ltd.), was mixed uniformly with 29 parts by weight of a liquid lubricant (Deobase). The mixture was pre-formed under pressure, and extruded by a ram-type extruder into a tubing having an inside diameter of 3.0 mm and an outside diameter of 4.5 mm. The tubing was dipped in trichloroethylene to extract and remove the liquid lubricant, and then stretched 200% in the axial direction of the tubing while it was heated at about 250° C. The stretched tubing was then heated at 350° C. while reducing the pressure on the outside surface of the tubing to expand its diameter and simultaneously sinter the tubing. The tubing obtained was a porous tubing having an inside diameter of 4.0 mm, and outside diameter of 4.9 mm, and a porosity of 79%.
A stainless steel rod having a diameter of 4.0 mm was inserted in the porous PTFE tubing, and elastic polyurethane multifilaments having a size of 1,120 denier were densely wrapped helically about the outside surface of the tubing. The filaments were fixed at both ends, and impregnated with tetrahydrofuran to bond them. The resulting structure was dried and heated at 170° C. for 10 minutes to heat-set the fibers. The resulting tubing did not deform even when the stainless steel rod was withdrawn. It was pliable and had high flexibility. When a stainless steel wire having a diameter of 0.40 mm was inserted in a loop-like configuration into the wall of the tubing at 5 mm from one end of the tubing, and pulled in the axial direction of the tubing at a speed of 50 mm/min., tearing occurred in the tubing under a load of 1,250 g which is much larger than the load (180 g) under which tearing occurred in the tubing without the elastic fibers. Holes left after inserting a surgical suturing needle were naturally occluded by the elasticity of the elastic fibers. Thus, the resulting product had various superior characteristics as a tubular organic prosthesis.
Elastic polyurethane multifilaments having a size of 2,240 denier were wrapped helically at intervals of 0.5 mm about the outside surface of the same porous PTFE tubing as used in Example 1, and treated in the same way as in Example 1. The load under which tearing occurred in the resulting tubing was 860 g. Thus, the product had superior characteristics as a tubular organic prosthesis as in the case of the tubing obtained in Example 1.
While the invention has been described in detail and with reference to specific embodiments thereof, it will be apparent to one skilled in the art that various changes and modifications can be made therein without departing from the spirit and scope thereof.
|Cited Patent||Filing date||Publication date||Applicant||Title|
|US3105492 *||Oct 1, 1958||Oct 1, 1963||Us Catheter & Instr Corp||Synthetic blood vessel grafts|
|US3479670 *||Oct 19, 1966||Nov 25, 1969||Ethicon Inc||Tubular prosthetic implant having helical thermoplastic wrapping therearound|
|US3490975 *||Oct 10, 1966||Jan 20, 1970||Univ Of Birmingham The||Method of making an artificial artery of wound silicone rubber thread|
|US4229838 *||Jul 3, 1978||Oct 28, 1980||Sumitomo Electric Industries, Ltd.||Vascular prosthesis having a composite structure|
|FR2248015A1 *||Title not available|
|Citing Patent||Filing date||Publication date||Applicant||Title|
|US5100422 *||May 26, 1989||Mar 31, 1992||Impra, Inc.||Blood vessel patch|
|US5104400 *||Aug 28, 1991||Apr 14, 1992||Impra, Inc.||Blood vessel patch|
|US5152782 *||May 26, 1989||Oct 6, 1992||Impra, Inc.||Non-porous coated ptfe graft|
|US5207705 *||Dec 8, 1989||May 4, 1993||Brigham And Women's Hospital||Prosthesis of foam polyurethane and collagen and uses thereof|
|US5282823 *||Mar 19, 1992||Feb 1, 1994||Medtronic, Inc.||Intravascular radially expandable stent|
|US5433909 *||Mar 12, 1993||Jul 18, 1995||Atrium Medical Corporation||Method of making controlled porosity expanded polytetrafluoroethylene products|
|US5443496 *||Oct 15, 1993||Aug 22, 1995||Medtronic, Inc.||Intravascular radially expandable stent|
|US5527353 *||Dec 2, 1993||Jun 18, 1996||Meadox Medicals, Inc.||Implantable tubular prosthesis|
|US5556426 *||Aug 2, 1994||Sep 17, 1996||Meadox Medicals, Inc.||PTFE implantable tubular prostheses with external coil support|
|US5641373 *||Apr 17, 1995||Jun 24, 1997||Baxter International Inc.||Method of manufacturing a radially-enlargeable PTFE tape-reinforced vascular graft|
|US5651174 *||Apr 27, 1995||Jul 29, 1997||Medtronic, Inc.||Intravascular radially expandable stent|
|US5800510 *||Jun 6, 1995||Sep 1, 1998||Meadox Medicals, Inc.||Implantable tubular prosthesis|
|US5800512 *||Jan 22, 1996||Sep 1, 1998||Meadox Medicals, Inc.||PTFE vascular graft|
|US5861033 *||Jan 30, 1997||Jan 19, 1999||Atrium Medical Corporation||Method of making controlled porosity expanded polytetrafluoroethylene products and fabrication|
|US5980799||Jun 16, 1998||Nov 9, 1999||Atrium Medical Corporation||Methods of making controlled porosity expanded polytetrafluoroethylene products and fabrication|
|US6245100||Feb 1, 2000||Jun 12, 2001||Cordis Corporation||Method for making a self-expanding stent-graft|
|US6270523||Oct 15, 1999||Aug 7, 2001||Atrium Medical Corporation||Expandable shielded vessel support|
|US6287337||Feb 8, 1999||Sep 11, 2001||Atrium Medical Corporation||Multi-stage prosthesis|
|US6296661||Feb 1, 2000||Oct 2, 2001||Luis A. Davila||Self-expanding stent-graft|
|US6312458 *||Jan 19, 2000||Nov 6, 2001||Scimed Life Systems, Inc.||Tubular structure/stent/stent securement member|
|US6355063||Jan 20, 2000||Mar 12, 2002||Impra, Inc.||Expanded PTFE drug delivery graft|
|US6416537||Jun 27, 2000||Jul 9, 2002||Atrium Medical Corporation||Multi-stage prosthesis|
|US6423089||Apr 22, 1999||Jul 23, 2002||Atrium Medical Corporation||Vascular endoprosthesis and method|
|US6428571||Mar 14, 2000||Aug 6, 2002||Scimed Life Systems, Inc.||Self-sealing PTFE vascular graft and manufacturing methods|
|US6478813||Dec 29, 1999||Nov 12, 2002||Peter T. Keith||Method for joining grafts in a common body passageway|
|US6482227||Nov 16, 2000||Nov 19, 2002||Cordis Corporation||Stent graft having improved attachment within a body vessel|
|US6575994||Nov 10, 2000||Jun 10, 2003||Teramed, Inc.||Method and apparatus concerning bypass grafts|
|US6589468||May 12, 2000||Jul 8, 2003||Meadox Medical, Inc.||Method of forming an implantable tubular prosthesis|
|US6626938||Nov 16, 2000||Sep 30, 2003||Cordis Corporation||Stent graft having a pleated graft member|
|US6719783||Aug 5, 2002||Apr 13, 2004||Scimed Life Systems, Inc.||PTFE vascular graft and method of manufacture|
|US6814753||May 7, 2003||Nov 9, 2004||Scimed Life Systems, Inc.||Implantable tubular prosthesis|
|US6840958 *||May 14, 2003||Jan 11, 2005||Scimed Life Systems, Inc.||Shaped woven tubular soft-tissue prostheses and method of manufacturing the same|
|US6843802||Nov 16, 2000||Jan 18, 2005||Cordis Corporation||Delivery apparatus for a self expanding retractable stent|
|US6863686||Jul 24, 2001||Mar 8, 2005||Donald Shannon||Radially expandable tape-reinforced vascular grafts|
|US6881221 *||Sep 28, 2001||Apr 19, 2005||Scimed Life Systems, Inc.||Tubular structure/stent/stent securement member|
|US6887268||Jan 8, 2002||May 3, 2005||Cordis Corporation||Extension prosthesis for an arterial repair|
|US6942692||Jan 8, 2002||Sep 13, 2005||Cordis Corporation||Supra-renal prosthesis and renal artery bypass|
|US7229472||Jan 8, 2002||Jun 12, 2007||Cordis Corporation||Thoracic aneurysm repair prosthesis and system|
|US7244271||Apr 9, 2004||Jul 17, 2007||Boston Scientific Scimed, Inc.||Self-sealing PTFE vascular graft and manufacturing methods|
|US7267685||Jan 8, 2002||Sep 11, 2007||Cordis Corporation||Bilateral extension prosthesis and method of delivery|
|US7314483||Jan 8, 2002||Jan 1, 2008||Cordis Corp.||Stent graft with branch leg|
|US7326237||Jan 8, 2002||Feb 5, 2008||Cordis Corporation||Supra-renal anchoring prosthesis|
|US7462675||Sep 14, 2005||Dec 9, 2008||Gore Enterprise Holdings, Inc.||Thermoplastic copolymer of tetrafluoroethylene and perfluoromethyl vinyl ether and medical devices employing the copolymer|
|US7500988||Nov 16, 2000||Mar 10, 2009||Cordis Corporation||Stent for use in a stent graft|
|US7862609||Jul 18, 2003||Jan 4, 2011||Cordis Corporation||Stent graft having a pleated graft member|
|US8029563||Nov 29, 2004||Oct 4, 2011||Gore Enterprise Holdings, Inc.||Implantable devices with reduced needle puncture site leakage|
|US8048440||Mar 16, 2006||Nov 1, 2011||Gore Enterprise Holdings, Inc.||Thermoplastic fluoropolymer-coated medical devices|
|US8062354||Dec 10, 2004||Nov 22, 2011||Edwards Lifesciences Corporation||Radially-expandable PTFE tape-reinforced vascular grafts|
|US8066758||Dec 28, 2005||Nov 29, 2011||C. R. Bard, Inc.||Vascular graft with kink resistance after clamping|
|US8157940||Aug 24, 2009||Apr 17, 2012||Bard Peripheral Vascular, Inc.||Methods for making a supported graft|
|US8196279||Feb 24, 2009||Jun 12, 2012||C. R. Bard, Inc.||Stent-graft covering process|
|US8313524||Aug 30, 2005||Nov 20, 2012||C. R. Bard, Inc.||Self-sealing PTFE graft with kink resistance|
|US8337650||Mar 29, 2012||Dec 25, 2012||Bard Peripheral Vascular, Inc.||Methods for making a supported graft|
|US8609125||Oct 27, 2011||Dec 17, 2013||W. L. Gore & Associates, Inc.||Thermoplastic fluoropolymer-coated medical devices|
|US8617337||Feb 8, 2011||Dec 31, 2013||Bard Peripheral Vascular, Inc.||Partial encapsulation of stents|
|US8617441||Feb 17, 2012||Dec 31, 2013||Bard Peripheral Vascular, Inc.||Methods for making an encapsulated stent|
|US8636794||Nov 9, 2006||Jan 28, 2014||C. R. Bard, Inc.||Grafts and stent grafts having a radiopaque marker|
|US8647458||Dec 14, 2012||Feb 11, 2014||Bard Peripheral Vascular, Inc.||Methods for making a supported graft|
|US8652284||Nov 21, 2011||Feb 18, 2014||C. R. Bard, Inc.||Vascular graft with kink resistance after clamping|
|US8696738 *||May 20, 2010||Apr 15, 2014||Maquet Cardiovascular Llc||Composite prosthesis with external polymeric support structure and methods of manufacturing the same|
|US8906087||Sep 30, 2011||Dec 9, 2014||W. L. Gore & Associates, Inc.||Method of making implantable devices with reduced needle puncture site leakage|
|US9155491||Jan 23, 2014||Oct 13, 2015||C.R. Bard, Inc.||Grafts and stent grafts having a radiopaque marker|
|US9198749||Oct 12, 2007||Dec 1, 2015||C. R. Bard, Inc.||Vascular grafts with multiple channels and methods for making|
|US9375326||Apr 14, 2014||Jun 28, 2016||Maquet Cardiovascular Llc||Composite prosthesis with external polymeric support structure and methods of manufacturing the same|
|US9572654||Nov 14, 2012||Feb 21, 2017||C.R. Bard, Inc.||Self-sealing PTFE graft with kink resistance|
|US20010050132 *||Jul 24, 2001||Dec 13, 2001||Donald Shannon||Radially expandable tape-reinforced vascular grafts|
|US20030196717 *||May 14, 2003||Oct 23, 2003||Meadox Medicals, Inc.||Shaped woven tubular soft-tissue prostheses and method of manufacturing the same|
|US20040059356 *||Jul 17, 2003||Mar 25, 2004||Peter Gingras||Soft tissue implants and methods for making same|
|US20040193242 *||Apr 9, 2004||Sep 30, 2004||Scimed Life Systems, Inc.||Self-sealing PTFE vascular graft and manufacturing methods|
|US20060041091 *||Sep 14, 2005||Feb 23, 2006||Chang James W||Thermoplastic copolymer of tetrafluoroethylene and perfluoromethyl vinyl ether and medical devices employing the copolymer|
|US20060118236 *||Nov 29, 2004||Jun 8, 2006||House Wayne D||Implantable devices with reduced needle puncture site leakage|
|US20070152367 *||Mar 13, 2007||Jul 5, 2007||Valentin Kramer||Eptfe process and product for medical applications|
|US20070244539 *||Jun 7, 2007||Oct 18, 2007||Boston Scientific Scimed, Inc.||Self-sealing PTFE vascular graft and manufacturing methods|
|US20080027534 *||Aug 30, 2005||Jan 31, 2008||Edwin Tarun J||Self-Sealing Ptfe Graft with Kink Resistance|
|US20090171436 *||Nov 9, 2006||Jul 2, 2009||Casanova R Michael||Grafts and stent grafts having a radiopaque beading|
|US20090216338 *||Sep 12, 2006||Aug 27, 2009||Peter Gingras||Soft tissue implants and methods for making same|
|US20090311132 *||Aug 24, 2009||Dec 17, 2009||C.R. Bard, Inc.||Methods for making a supported graft|
|US20100057196 *||Oct 12, 2007||Mar 4, 2010||C.R. Bard, Inc.||Vascular grafts with multiple channels and methods for making|
|US20100179642 *||Dec 28, 2005||Jul 15, 2010||C.R. Bard, Inc.||Vascular Graft With Kink Resistance After Clamping|
|US20110125253 *||Nov 9, 2006||May 26, 2011||C.R. Bard Inc.||Grafts and stent grafts having a radiopaque marker|
|US20110126966 *||Feb 8, 2011||Jun 2, 2011||C.R. Bard, Inc.||Partial encapsulation of stents|
|US20110288628 *||May 20, 2010||Nov 24, 2011||Maquet Cardiovascular LLC.||Composite prosthesis with external polymeric support structure and methods of manufacturing the same|
|US20130095228 *||Dec 3, 2012||Apr 18, 2013||Cook Medical Technologies Llc||Introducer sheath with encapsulated reinforcing member|
|International Classification||A61L27/00, A61F2/06, A61L27/16, A61F2/04, A61F2/02|
|Cooperative Classification||A61L27/16, A61F2/06|
|European Classification||A61L27/16, A61F2/06|