Publication numberUSRE33677 E
Publication typeGrant
Application numberUS 07/380,755
Publication dateAug 27, 1991
Filing dateJul 17, 1989
Priority dateMay 26, 1976
Publication number07380755, 380755, US RE33677 E, US RE33677E, US-E-RE33677, USRE33677 E, USRE33677E
InventorsHargovind N. Vazirani
Export CitationBiBTeX, EndNote, RefMan
External Links: USPTO, USPTO Assignment, Espacenet
Coating of fiber lightguides with UV cured polymerization
US RE33677 E
Glass fiber lightguides require polymer coatings for protection. A new coating system comprising an acrylate-epoxy polymer that is UV curved is convenient to apply and gives excellent strength and durability to fiber lightguides.
Previous page
Next page
What is claimed is:
1. An optical fiber waveguide comprising a glass fiber and a polymer coating the fiber, the invention characterized in that the polymer coating comprises the polymerization product of a prepolymer mixture resulting from reacting acrylic acid with a 0.4 to 1.0 weight ratio mixture of aliphatic diglycidyl ether to aromatic diglycidyl ether, and further characterized in that the polymerization product contains a UV sensitizer in order to cure said prepolymer mixture with ultra violet light. light.
2. The waveguide of claim 1 in which the aliphatic ether is 1,4-butanediol diglycidyl ether.
3. The waveguide of claim 2 in which the aromatic ether is diglycidyl ether of halogenated bisphenol A.
4. The waveguide of claim 1 in which the polymerization product additionally contains a silane or titanate coupling agent. .Iadd.
5. Optical fiber waveguide comprising a glass optical fiber having a continuous flexible adherent cured coating on the surface of said fiber said coating formed by immersing said fiber in a bath of liquid radiation curable material thus coating said fiber with said material and passing said coated optical fiber through a die and thereafter exposing said coated optical fiber to UV radiation for a time sufficient to cure said coating on said fiber. .Iaddend. .Iadd.
6. An optical fiber waveguide suitable for optical communication comprising a glass fiber and a polymer coating characterized in that said polymer coating comprises 1) the polymerization product of a UV curable polymer and 2) a UV sensitizer wherein said polymerization is induced by UV light. .Iaddend.

.Iadd.This application is a continuation of application Ser. No. 054,123 (abandoned), filed on May 15, 1987 which is a continuation of application Ser. No. 576,766 (abandoned) filed on Feb. 2, 1984, which is a continuation of application Ser. No. 32,129 (abandoned)filed on Apr. 23, 1979 which is a reissue of U.S. Pat. No. 4,099,837. .Iaddend.


It is well known that glass fibers have exceptional tensile strength. It is also well known that long lengths of pristine fibers rarely possess the tensile strength of short glass fibers. This is because the surface of glass is fragile and susceptible to scratches and contaminants that produce breaks. The number of potential break sites increases with the length of the fiber so the tensile strength is length dependent. (The actual relationship is non-trivial. There is some evidence that the dependence is bimodal).

It has been recognized widely that the strength of a long fiber can be improved by protecting the fiber from surface contaminants and physical abuse. Abuse in this context has been found to mean any physical contact--such is the fragility of the unprotected surface. It is therefore standard in the art to apply a protective plastic coating to the fiber as it is formed. Considerable effort has been expended in the technology of coating long fibers. Such fibers are of interest mainly for the transmission of intelligent information via light signals, and are referred to as optical fibers.


This invention is a new coating system for fiber lightguides. It is a UV cured epoxy-acrylate coating which through considerable development effort has been found to impart high strength to pristine fibers and can be applied by simple and effective coating procedures.


The FIGURE is a schematic arrangement of an apparatus arranged for applying to an optical fiber a coating according to the invention.


The FIGURE shows a preform 10 being drawn into an endless glass fiber 11 with the aid of a heat source 12 applied in a conventional way. A coating vessel 13 is arranged to coat the fiber with a fluid 14 which later, upon curing, becomes the protective coating for the fiber. The coating vessel is shown here as a simple cup with a flooded exit capillary, through which the fiber is threaded. A more detailed account of a suitable coating apparatus appears in U.S. patent application, Ser. No. 600,280, filed July 31, 1975, by R. V. Albarino and S. Torza, now U.S. Pat. No. 4,073,974. The fiber exiting from the coating vessel and carrying uncured resin, passes through the curing stage, which is shown here as one or more UV lamps 15 arranged with UV light incident efficiently on the fiber. The finished fiber, now coated with a cured resin, is taken up on conventional reel 16.

The material contained in the coating vessel is, according to the invention, a prepolymer made by mixing certain epoxy resins and reacting the mixture with arcylic and/or methacrylic acid. The mixture contains an aliphatic type glycidyl ether and an aromatic type glycidyl ether. Excellent results have been obtained with a mixture of 1, 4-butanediol diglycidyl ether and a diglycidyl ether of bisphenol A or substituted, e.g., halogenated, bisphenol A, and specifically with brominated bisphenol A. The recommended proportion of aliphatic diglycidyl ether to aromatic diglycidyl ether is 0.4 to 1.0 on a weight ratio basis.

The epoxy resin mixture is reacted with acrylic and/or methacrylic acid on an equivalent basis with between 0.5 to 1.0 mol acid per epoxy equivalent weight, and preferably 0.8-0.95 mol acid per equivalent weight. Either acrylic acid or methacrylic acid function adequately and can be mixed in any proportion to give the recommended molar quantity.

The reaction to form the prepolymer proceeds more effectively in the presence of a tertiary amine. The amine functions as a catalyst to the epoxy-acrylic acid addition reaction. In quantity, 0.05 percent to 1 percent amine by weight of the total mix is adequate. Diethylaminoethanol has been found useful for this purpose.

A particularly useful ingredient of the prepolymer mixture is a UV sensitizer which promotes the efficiency with which the polymer is cured during the fiber coating operation. UV sensitizers, which are basically UV absorbers, are conventional in the art. Good results have been obtained with benzoin and its methyl isobutyl ethers. The sensitizer is typically added in an amount in the range of 0.1 percen to 5 percent by weight of the total prepolymer mix and preferably in the range of 0.5 percent to 1.0 percent.

Also found beneficial in conventional coating compositions for glass fibers are coupling agents that prevent adsorption of water at the glass surface. It is known that water is hostile to glass fibers and reduces fiber strength. Coupling agents that improve the wet strength of fibers are stable in the presence of moisture and chemisorb to the silanol groups on the glass surface which otherwise tend to hydrolize with water and impair the strength of the fiber. The most effective coupling agents for fiber coating also have unsaturated sites that attach to the polymer and improve the bond between the polymer coating and the glass surface. Coupling agents that have been proposed for optical fiber coatings are typically silanes and titanates.

Various coupling agents have been used in amounts of 0.1 percent to 5 percent by weight, and preferably 0.5 percent to 1.0 percent, in the coating compositions of this invention. However, it has been demonstrated that the particular UV cured epoxy-acrylate system of this invention functions adequately without a coupling agent. It appears that the integrity of the coating and the resistance to moisture contamination is of the same order with or without the coupling agents tested. It may be that significant differences with particular coupling compounds in certain formulations exist as compared with the same formulations without coupling agents, but clear evidence points to the advantage of this system is not always requiring the addition of coupling agents. It can be theorized that the epoxy-acrylate molecule serves itself the function of a coupling agent. The structure of the coating compounds includes hydroxyl groups that are available for coupling with the silanol groups on the glass. The molecule also contains an unsaturated tail, in the acrylate group, for bonding to the polymer coating.

It may also be desirable in some cases to add to the prepolymer mix a thermal inhibitor such as hydroquinone, or a substituted hydroquinone, e.g., the methyl ether of hydroquinone. Amounts of the order of 0.1-0.5 parts per hundred resin are effective.

The foregoing components are mixed and reacted at a temperature in the range of 100 to 170 C. to form the prepolymer. In the event the prepolymer is to be stored prior to use, the shelf life can be extended by the addition to the prepolymer mix of a stabilizer such as 4-tertiary butyl catechol in an amount of 0.01 to 0.5 percent by weight of the resin.


The following ingredients were mixed to proportions indicated to give a prepolymer:

______________________________________                Approximate                Weight Percent______________________________________1,4-butanediol diglycidyl ether                  28brominated bisphenol A diglycidyl ether                  46acrylic acid           26______________________________________

An addition reaction catalyst, 0.2 parts per hundred resin of diethylaminoethanol, and an equal amount of hydroquinone as a stabilizer were also added. These ingredients are regarded as preferred but not essential.

This prepolymer mix was reacted at 140 C. with stirring for approximately 1-2 hours or until an acid value of 1.50.5 was obtained.

The prepolymer contains approximately 75 percent of the following species: ##STR1## The remaining 25 percent consists of: ##STR2## Where R' is an aromatic glycidyl ether group and R" is an aliphatic glycidyl ether group. In this particular embodiment, ##STR3## and R"=--O--(CH2)4 --O--.

The prepolymer mix included also 0.5 parts by weight to 100 parts of prepolymer of VICURE 10, a benzoin type sensitizer obtained from the Stauffer Chemical Corporation, and 1 part per 100 parts prepolymer polymer of Z-6032, a silane coupling agent made by Dow Corning Corporation. As indicated above the silane coupling agent is considered to be optional.

Optical fibers were drawn vertically by a conventional drawing technique and passed through a coating applicator of the kind described in the aforementioned application. The applicator contained the prepolymer mix just described. The exit port or die of the applicator was varied to yield coatings ranging in thickness from 25 to 100 micrometers. The coatings on the fiber were cured at a speed of 25 meters per minute by passing the prepolymer coated fiber between two water-cooled or air-cooled, 12 inches 200 watt/in medium pressure mercury UV lamps. Faster drawing and curing speeds can be obtained by using longer lamps or gangs of lamps or by increasing the amount of UV sensitizer in the prepolymer. The coated fibers were taken up on a standard 11' aluminum drum. The glass fiber after coating exhibited a tensile strength of 1,010 psi for short lengths.

The physical properties of the polymer coating are as follows:

Young's Modulus--˜6,000 psi

Elongation at Break--˜20%

The cured polymer forming the coating is a highly crosslinked material which does not fuse, even at temperatures as high as 325 C. The material when exposed to such high temperatures for reasonably short time periods remains quite flexible.

Curing of the polymer system of the invention can be enhanced thermally, or the polymer can be completely cured thermally. In the latter case the addition of peroxides or other thermally sensitive oxidants will aid the curing process.

Various additional information and extensions of this invention will become apparent to those skilled in the art. All such variations and deviations which basically rely on the teachings through which this invention has advanced the art are properly considered to be within the spirit and scope of this invention.

Patent Citations
Cited PatentFiling datePublication dateApplicantTitle
US3673140 *Jan 6, 1971Jun 27, 1972Inmont CorpActinic radiation curing compositions and method of coating and printing using same
US3873499 *Nov 29, 1973Mar 25, 1975Dow CorningFast curing mercaptoalkyl vinyl siloxane resins
US3876432 *Oct 3, 1974Apr 8, 1975Sun Chemical CorpFatty ester modified epoxy resin photopolymerizable compositions
US3980390 *Mar 20, 1975Sep 14, 1976Sumitomo Electric Industries, Ltd.Optical transmission fiber
US4073974 *Jul 31, 1975Feb 14, 1978Bell Telephone Laboratories, IncorporatedCoating continuous filaments
FR2233637A1 * Title not available
Referenced by
Citing PatentFiling datePublication dateApplicantTitle
US6246824Mar 18, 1998Jun 12, 2001Dsm N.V.Method for curing optical glass fiber coatings and inks by low power electron beam radiation
US6316516Apr 29, 1999Nov 13, 2001Corning IncorporatedCoating composition for optical fibers
US6338878Nov 7, 2000Jan 15, 2002AlcatelMethod to improve degree of cure for ultraviolet curable optical fiber coating by actively removing heat from the coating during irradiation
US6370920Apr 28, 1999Apr 16, 2002AlcatelApparatus to improve degree of cure for ultraviolet curable optical fiber coating by actively removing heat from the coating during irradiation
US6436484Dec 9, 1997Aug 20, 2002Coats American, Inc.Processes for coating sewing thread
US6553169 *Nov 29, 2000Apr 22, 2003Corning IncorporatedOptical fiber coating compositions and coated optical fibers
US6577802Jul 13, 2000Jun 10, 2003Corning IncorporatedApplication of silane-enhanced adhesion promoters for optical fibers and fiber ribbons
US6599956Dec 26, 2001Jul 29, 2003Dsm N.V.Non-crystal-forming oligomers for use in radiation-curable fiber optice coatings
US6828023Jul 2, 2002Dec 7, 2004Coats American, Inc.Coated sewing thread
US6845637Feb 22, 2002Jan 25, 2005AlcatelApparatus to improve degree of cure for ultraviolet curable optical fiber coating by actively removing heat from the coating during irradiation
US6872760Feb 6, 2003Mar 29, 2005Ppg Industries Ohio, Inc.Radiation-curable composition for optical fiber coating materials
US7064154Jan 9, 2004Jun 20, 2006Ppg Industries Ohio, Inc.Radiation-curable composition for optical fiber coating materials
US8506740Nov 12, 2009Aug 13, 2013Pepex Biomedical, LlcManufacturing electrochemical sensor module
US8702932Aug 28, 2008Apr 22, 2014Pepex Biomedical, Inc.Electrochemical sensor and method for manufacturing
US8951377May 21, 2012Feb 10, 2015Pepex Biomedical, Inc.Manufacturing electrochemical sensor module
US9044178Aug 28, 2008Jun 2, 2015Pepex Biomedical, LlcElectrochemical sensor and method for manufacturing
US9445755Nov 12, 2009Sep 20, 2016Pepex Biomedical, LlcElectrochemical sensor module
US9459228Apr 21, 2014Oct 4, 2016Pepex Biomedical, Inc.Electrochemical sensor and method for manufacturing
US9504162May 18, 2012Nov 22, 2016Pepex Biomedical, Inc.Manufacturing electrochemical sensor modules
US20020078888 *Feb 22, 2002Jun 27, 2002AlcatelMethod and apparatus to improve degree of cure for ultraviolet curable optical fiber coating by actively removing heat from the coating during irradiation
US20020168481 *Jul 2, 2002Nov 14, 2002Coats North AmericaCoated sewing thread
US20030148025 *Jan 24, 2003Aug 7, 2003Fujikura Ltd.Manufacturing method of optical fiber
US20090035574 *Jul 31, 2007Feb 5, 2009Peter GableFiber Coating System
US20090053561 *May 8, 2007Feb 26, 2009Juan JiangCatalyst layers and related methods
US20110189762 *Aug 28, 2008Aug 4, 2011Pepex Biomedical LlcElectrochemical sensor and method for manufacturing
WO2002006176A1May 23, 2001Jan 24, 2002Corning IncorporatedApplication of silane-enhanced adhesion promoters for optical fibers and fiber ribbons
U.S. Classification385/123, 427/513, 427/163.2, 65/432
International ClassificationG02B6/02, C03C25/10, B05D7/20
Cooperative ClassificationB05D1/18, B05D3/067, C03C25/106, B05D7/20, G02B6/02395
European ClassificationB05D7/20, C03C25/10P2D2, G02B6/02