|Publication number||USRE34937 E|
|Application number||US 07/965,102|
|Publication date||May 16, 1995|
|Filing date||Oct 22, 1992|
|Priority date||Oct 13, 1987|
|Publication number||07965102, 965102, US RE34937 E, US RE34937E, US-E-RE34937, USRE34937 E, USRE34937E|
|Inventors||Robert L. Ibsen, William R. Glace, Donald R. Pacropis|
|Original Assignee||Den-Mat Corporation|
|Export Citation||BiBTeX, EndNote, RefMan|
|Patent Citations (6), Non-Patent Citations (2), Referenced by (14), Classifications (10), Legal Events (7)|
|External Links: USPTO, USPTO Assignment, Espacenet|
This is a continuation-in-part of application Ser. No. 107,012, filed Oct. 13, 1987, now abandoned.
1. Field of the Invention
This invention relates to improved methods and materials for providing adhesive bonding of acrylic resins to industrial, natural, and dental substrates, and more particularly to dental restoration methods and methods of improving adhesion of dental composite restoratives to dentin. More specifically, methods and materials for strong adhesive bonding of composite resins to dentin are disclosed with the objects of improving the treatment of cervical erosions, root caries, and other dental conditions, eliminating much of the mechanical cutting of dentin and enamel currently required for mechanical retention of restorations.
2. Description of the Prior Art
For many years, advances in the study of methods of adhesive bonding of composite materials to hard tooth tissues have evolved in small increments. Swiss Patent No. 687,299 to deTrey, Inc. described a material for bonding to dentin. A more recent patent, U.S. Pat. No. 4,540,722 to 3M Company describes a modification of the original deTrey material, U.S. Pat. Nos. 4,514,527; 4,521,550; 4,588,756; and 4,659,751 all to R. L. Bowen, assigned to the American Dental Association Health Foundation, disclose more recent developments based on the use of mordants and adhesion promoting coupling agents. Each of these steps has resulted in incremental improvements in bonding to dentin, to the point where it is presently feasible for the dentist to use adhesive bonding to retain composite restorations.
The prior art closest to the present invention is the Bowen U.S. Pat. No. 4,659,751, which preferably employed a two-step technique. This technique comprised, first, treating the surface to be bonded with an acidic solution preferably containing nitric or other strong acid, polyvalent cations, and compounds such as oxalic acid or other polyfunctional acids which can form relatively water-insoluble precipitates with calcium and other polyvalent cations at pH values above that of the acidic aqueous treatment solution, and also containing at least one compound selected from the group consisting of (1) N-phenylglycine ("NPG"), (2) the adduct of N(p-tolyl)glycine and glycidyl methacrylate ("NTG-GMA"), (3) the addition reaction product of N-phenylglycine and glycidyl methacrylate ("NPG-GMA"), and (4) other amino acids. Second, the technique called for applying a solution containing at least one monomeric compound selected from the group consisting of (1) the addition reaction product of pyromellitic acid dianhydride and 2-hydroxyethyl methacrylate ("PMDM"), (2) the addition reaction product of 3,3',4,4'-benzophenonetetracarboxylic dianhydride and 2-hydroxyethyl methacrylate ("BTDA-HEMA"), and (3) 4-methacryloxyethyltrimellitic anhydride ("4-META").
Alternatively, but less preferred, in the case of vital dentin, according to the Bowen U.S. Pat. No. 4,659,751, the surface to be treated could be contacted with a strongly acidic solution, but still containing NPG, NTG-GMA, NPG-GMA, and/or other amino acids, followed by contacting with PMDM, BTDA-HEMA and/or 4-META monomer solution. Also, an acidic solution and the NPG or other amino acid solution could be applied separately, one after the other (instead of as a combined solution) before the PMDM or other monomer is applied. The components for practicing the method of this Bowen invention are said to be conveniently made available in the form of a kit or article of manufacture described in that patent.
A particularly preferred method of the Bowen invention of U.S. Pat. No. 4,659,751 is accomplished by treating the surface of the dentin, enamel or other substrate containing or capable of binding metallic ions with a solution with contains (1) at least one salt of a polyvalent cation which can bind to substrate surface sizes; (2) a compound which contains at least one acid group and preferably two or more acidic groups (3) a strong acid; and (4) at least one surface-active compound selected from the group consisting of NPG, alpha or beta amino acids, and other compounds, each of which contain at least one of each of the following groups: carboxyl and amino. The surface-active compound may be a surface-active comonomer which contains a moiety capable of free radical polymerization as well as the carboxyl and amino groups. The resultant substrate surface is then treated with a solution which contains at least one compound selected from the group consisting of (1) PMDM, (2) BTDA-HEMA, (3) 4-META, (4) other compounds containing at least one group or moiety capable of free radical polymerization, and at least one aromatic ring or moiety containing, electron-withdrawing substituents which do not interfere with free radical polymerization, and which compound preferably also contains one or more free carboxyl groups, or anhydride groups which can form free carboxyl groups upon hydrolysis, and (5) camphoroquinone.
The present invention comprises the use of certain alternative materials--especially the alkali metal salts of NPG, NPG-GMA, and NTG-GMA .[.and mixtures thereof with NPG, NPG-GMA or NTG-GMA.].--with the other ingredients specified by the Bowen patent U.S. Pat. No. 4,659,751. It also comprises the use of simplified methods. The present invention produces even stronger adhesive bonds between composite materials or resin and dentin and also results in effective bonding between these materials or resin and enamel and other natural or industrial substrates. There is also greater color stability in the resultant composition than was previously achieved.
An advantage of this invention is that it provides better materials and methods which make it easier to obtain aesthetic adhesive bonding of composite and unfilled resins of the type polymerized by free radicals to dentin, enamel, industrial substrates, and/or other substrates containing or capable of binding metallic ions (i.e., ions of elements on the left side and in the center of the periodic table). The resulting products are also within the scope of this invention.
Some of the materials disclosed in the present invention replaced a much more expensive material used in some of the previous patents.
.[.It has recently been discovered that what has been furnished as the sodium salt of NTG-GMA is really a mixture of the NGT-GMA with the sodium salt. The two are at equilibrium, not only about 50% of each but varying from 40% of one ingredient and 60% of the other to 60% of the one ingredient and 40% of the other. It had been thought that material was the sodium salt of NTG, but recent information has come that that was a mistake and that the correct analysis showed the two ingredients mixed together in equivalent amounts; so that they would be roughly 50:50 in proportion, but not exactly. The mixture of the acid and the sodium salt has special benefits that have been noted and were attributed to the pure sodium salt. However, when the device was first purified, transforming all the portion that was the sodium salt into the substantially pure NTG and when material was converted back to the sodium salt, results were different. Therefore, the results apparently follow from the use of a mixture of the acid with the sodium salt..].
The present invention may be summarized as follows:
First, pretreating the dentin with an acidic solution preferably containing a strong acid (such as nitric acid, phosphoric acid, or a mixture of phosphoric and nitric acids) which may also contain polyvalent cations, and compounds such as oxalic acid or other polyfunctional acids which can form relatively water-insoluble precipitates with calcium and other polyvalent cations at pH values above that of the aqueous treatment solution.
Second, applying a solution containing an alkali metal salt of one of the group consisting of (1) N-phenyl glycine ("NPG"), (2) the adduct of N-(p-tolyl) glycine and glycidyl methacrylate ("NTG-GMA"), (3) the addition reaction product of N-phenylglycine and glycidyl methacrylate ("NPG-GMA"), and (4) other amino acids. This solution is in a solvent composed of a mixture of water and a polar organic solvent, such as acetone. This solution may contain, in addition to the alkali metal salt, an approximately equal amount of the actual NPG, NTG-GMA, NPG-GMA or the amino acids used in the salt.
Third, a solution is applied which contains at least one monomeric compound selected from the group specified by Bowen, preferably the addition reaction product of pyromellitic acid dianhydride and 2-hydroxyethyl methacrylate ("PMDM").
A combined solution containing both (.Iadd.a) .Iaddend.the .[.(a).]. alkali metal salt of the amino acid, or amino acid adduct or reaction product (as stated in the "second" solution above.Iadd.) .Iaddend..[.and the acid or adduct or addition reaction product as in the "second" solution.]., and (b) the PMDM may be applied, rather than applying each solution separately.[., the.]..Iadd.. The .Iaddend.results may be less satisfactory or more satisfactory.
The components for practicing the method of the invention may be commonly made available in the form of a kit or article of manufacture.
The preferred method for preparing the substrate surface for adhesion of composite materials and resins comprises contacting the surface with three separate solutions, one after the other.
The first solution comprises (1) a strong acid or combination of acids and may include (2) one or more polyvalent cations (preferably Al+++) which can form relatively water-insoluble precipitates with phosphate ions.
The preferred polyvalent cation, when used, is the trivalent aluminum ion, at least as to dental applications where aesthetics is important. Aluminum oxalate gives excellent results. The ferric ion, while usable in some applications, can lead to staining by reduction to ferrous ion in the presence of sulfide. The ferrous sulfide can be generated by the metabolic activity of anaerobic microorganisms. However, sulfides do not form black complexes with aluminum ions under the conditions of interest.
Although literature references list aluminum oxalate as insoluble in water, it has been discovered by others, including Bowen, that aluminum oxalate is soluble in water when formulated with the other ingredients of the present invention. The solubility of aluminum oxalate in water depends upon the stoichiometry and pH. Aluminum oxalate does not precipitate from the aqueous solution of the present invention. Aluminum ions can form insoluble, metastable, microporous, quasi-amorphous precipitates of phosphate surfaces. Aluminum ions can strengthen the altered substrate surface structures by crosslinking and reinforcing the collagenous component of dentin surface reacted upon by the first aqueous solution of the present invention.
In applications where color stability and aesthetics are not deciding factors, aluminum ions, ferric ions, and other polyvalent cations can be used separately or in combinations in the first aqueous solution of the present invention.
An important function of the precipitation of one or more polyvalent cations with phosphate ions and/or collagenous and/or organic components is thought to be the occluding or obturating of dential tubules in vital dentin, so as to protect the odontoblasts and pupal tissues from ingress of foreign matter.
The function of the incorporation of a compound with one or more carboxyl groups, such as, for example, oxalic acid or an "oligocarboxylic acid" as exemplified by aluminum oxalate, is believed to be the precipitation of insoluble calcium and the other complexes which also can assist in obturating the dential tubules of vital dentin, when it is treated with the first aqueous solution of the present invention.
The strong acid which is also preferably present in the first aqueous treatment solution renders the solution low in pH value. The purposes of the low pH are (1) to dissolve the smeared (disturbed) surface layer on cut dentin, enamel, or other substrates, (2) to partially decalcify intertubular dentin, (3) to remove pellicle, plaque, or other surface contaminants from the substrate, and (4) to "acid etch" enamel and other substrate surfaces. Another function of the strong acid component which renders the first aqueous solution strongly acidic (low pH) is to render soluble some or all of the other components in the solution. The preferred acids for use in the method of this invention is phosphoric acid, or a mixture of phosphoric acid and nitric acids, ranging in concentration from about one-tenth percent to about 50% by weight, preferably, from about 0.1% to 10% by weight and most preferably on the order of about 2 to 5% by weight of the aqueous solution. It has been discovered that compounds such as Al(NO3)3 can hydrolyze in the aqueous formulation of the first solution to provide the strong acid and necessary low pH. Such strong acids as hydrochloric acid, perchloric acid, sulfuric acid and others, and acid mixtures may or may not be effective in improving the bond strengths obtainable in the use of the present invention.
The second solution comprises a solution in an acetone/water solvent of the sodium or other alkali metal salt of (1) N-phenylglycine or NPG (e.g., NaNPG), (2) the adduct of N-phenylglycine-glycidyl methacrylate (e.g., NaNPG-GMA), or (3) .[.N-tolylglycine-glycidylmethacrylate.]. .Iadd.N(p-tolyl)glycine-glycidylmethacrylate .Iaddend.e.g., NaNTG-GMA) either alone or with the NPG, NPG-GMA, or NTG-GMA. .[.It appears that the crude material thought originally to be a sodium salt of NPG, NPG-GMA, or NTG-GMA has recently been found to be actually a mixture of the NPG, NPG-GMA, or NTG-GMA with the sodium salt of the same, varying between the values of 40-60 to 60-40 of the respective ingredients and being closer to a 50-50 mixture..]. The commercial product is not pure, either as an acid or as the sodium salt, without special treatment. The water content of the acetone/water solvent is preferably between about 15% and about 50%. The total content of the NaNTG-GMA .[.mixture with NTG-GMA.]. is between about 1% and about 10%, as may be the NaNPG .[.and NPG.]. or NaNPG-GMA .[.and NPG-GMA.]. content, the remainder being the solvent.
Although the specific function of the NaNTG-GMA (or NaNPG or NaNPG-GMA) in the present invention has not been ascertained, it is essential in obtaining the necessary high bond strengths. It may be speculated that it is surface-active, that it forms complexes with cations, absorbs on the nascent surfaces formed within the substrate structures, and that it plays a role in the initiation of polymerization of compounds laid down in later steps.
The alkali-metal salts of the amino acids and/or their complexes as used are essential to this invention for two reasons--significantly stronger bonds are formed than with NPG, NPG-GMA, or NTG-GMA, alone, and the material is much less costly to manufacture than where pure NPG, NPG-GMA, and NTG-GMA are used, instead of the sodium or other alkali metal salt thereof.
Additional examples of alkali metal salts containing at least one amino group and at least one carboxyl group include the alkali metal salts or esters of: the amino acids in general, N-phenylglycine, N(p-tolyl)glycine, N-phenylalanine, sarkosine, N-lauroylsarkosine, glycine, N,N-dimethylglycine, 3(N-phenyl) amino propionic acid, 3(N-p-tolyl) amino propionic acid, omegaamino fatty acids, N-substituted -omega-amino fatty acids, the addition reaction product of N-phenyl glycine and glycidyl reagents, and the reaction product of N(substituted phenyl) glycine and glycidyl reagents.
It is anticipated that the alkali-metal salts of many or all of these compounds would be effective to one degree or another.
The third solution contains a solution of PMDM at a percentage of between 1% and 25%, the solvent being acetone with a water content of from 0% to about 25%. PMDM is the addition reaction product of pyromellitic acid dianhydride and 2 moles of 2-hydroxyethyl methacrylate. While the structure(s) of PMDM are not definitely known, and it is best characterized as the above-recited addition reaction product, the structures of the two isomers of PMDM are postulated to be as follows: ##STR1##
The PMDM isomer may be applied to the dentin or enamel surface in any desired proportions, dissolved in a solvent or a mixture of solvents. Again, the preferred solvent is acetone, although other solvents may be used. A 10% solution of PMDM in acetone is efficacious, although other concentrations, preferably in a range of about 0.1% to a saturated solution, may be used.
Preferably, the excess solution of PMDM is not removed, but rather, the solvent is removed by evaporation that may be speeded by applying a gentle stream of air at any feasible temperature.
Advantageously, the components necessary to effect the method of this invention may be packaged in an article of manufacture of "kit" for use by the dentist.
For application after the dentin is prepared as described above, a mix of composite or unfilled resin may be applied. Adhesion tests utilizing extracted human and bovine teeth indicated strong adhesive bonding when utilizing the most preferred embodiments of the invention, as shown in Table 1 below.
Although the formulations shown in Table I do not necessarily represent optimized proportionalities of the ingredients, the data indicate that very strong adhesive bonding can be obtained with various proportions, concentrations, and recipes for the preparation of the solutions. Here, as an example, the same amount of each of the three solutions is used.
TABLE 1______________________________________Sheer Stress Adhesive Strengths of a CompositeBonded to Treated Surfaces AverageSolution Solution Solution Adhesion1 2 3 psi______________________________________Al.sub.2 (C.sub.2 O.sub.4).sub.3 /HNO.sub.3 10% .[.equilibrium 5% 965 mixture of.]. NaNTG--GMA.[.with NTG--GMA.].Al.sub.2 (C.sub.2 O.sub.4).sub.3 /HNO.sub.3 5% .[.equilibrium 20% 1035 mixture of.]. PMDM NaNTG--GMA.[.with NTG--GMA.].Al.sub.2 (C.sub.2 O.sub.4).sub.3 /HNO.sub.3 5% .[.equilibrium 5% 936 mixture.]. PMDM NaNTG--GMA.[.with NTG--GMA.].Al.sub.2 (C.sub.2 O.sub.4).sub.3 /HNO.sub.3 5% .[.equilibrium 10% 1140 mixture of.]. PMDM NaNTG--GMA.[.with NTG--GMA.].______________________________________
Table .Badd.2 lists bond strengths obtained by the same test method when state-of-the-art commercial dentin adhesives are utilized with the same composite recommended by the manufacturers.
TABLE 2______________________________________Sheer Stress Adhesive Strengths of CompositesBonded to Treated Dentin SurfacesDentin Surface TreatmentMaterial Average Adhesion (psi)______________________________________Scotchbond 428Dentin Adhesit 465Bondlite 645Universal Bond 285Creation 3-in-1 490GLUMA* 249Tenure** 938______________________________________ *Not commercially available in U.S. **Similar to invention but using NTG--GMA alone in Solution 2 instead .[.of the mixture.].of the sodium salt of NTG--GMA .[.with NTG--GMA.].
Five extracted teeth were ground to give a flat surface of dentin. An aqueous solution of 2.5% HNO3 was applied for 60 seconds, then rinsed away with water and the surface dried. No polyvalent metal carboxylate was uses. Next, a 10% solution of NPG-GMA in acetone was applied and allowed to dry, followed by a solution of 5% PMDM in acetone, A cylinder of a commercially available light-cured dental composite was bonded to the surface and tested to failure in sheer after 15 minutes in water. The average bond strength was 1454 psi in these However, the above experiment was repeated with samples stored three days in water at 37° C. until testing. Then, the bond strength dropped to 600 psi, illustrating that the absence of carboxylate ions in the first nitric acid solution greatly affected the bond strength to well-wet teeth, which correspond closely to teeth in the mouth.
Five extracted teeth were ground to give a flat dentin surface. Each was treated with a solution of aluminum oxalate (Al2 (C2 O4)3) for 60 seconds, after which the solution was rinsed away and the surface air dried. NO second solution (as defined in Table 1) was used. Next, a solution of 5% PMDM in acetone (the third solution of Table 1) was applied and allowed to dry. A cylinder of dental composite was bonded to the treated surface. The samples were stored in water at 37° C. for one week and tested in sheer until failure. The average bond strength was 468 psi, illustrating that a surface-active monomer is necessary for optimum bonding.
Ten bovine teeth were ground to a flat dentin surface. Each was painted with a solution of Al2 (CO2 O4)3 in 2.5% nitric acid, which was allowed to remain for 60 seconds, then washed away and dried. Next a solution of 10% mixture of NaNTG-GMA .[.with NTG-GMA.]. in 85/15 acetone/water was applied and allowed to dry. .[.There is from 40% NaNTG-GMA and 60% NTG-GMA to 60% NaNTG-GMA and 40% NTG-GMA..]. Finally, a solution of 5% PMDM was applied and allowed to dry. A cylinder of light-cured dental composite was applied to the treated surface and cured in place.
These samples were stored in distilled water at 37° C. for four hours, then stressed in sheer until failure. Bond strengths averaged 904 psi with a standard deviation of 250 psi--much better than in Examples 1 and 2.
Twelve samples were prepared as in Example 3 with the exception that the treating solutions were 5% NaNTG-GMA and 5% PMDM. Bond strengths averaged 824 psi with a standard deviation of 153 psi.
Thirty-three bovine teeth were prepared as in Example 3 except that the treating solutions were 5% .[.of a mixture.]. of NaNTG-GMA .[.with NTG-GMA.]. and 10% PMDM. Bond strengths averaged 764 psi with a standard deviation of 203 psi.
Twenty-nine bovine teeth were prepared as in Example 5 except that PMDM concentration was 20%. Bond strengths were an average of 1087 psi and a standard deviation of 249 psi.
Ten bovine teeth were prepared as in Example 5. Storage in 37° C. water was maintained for 24 hours instead of 4 hours. Bond strengths were an average of 655 psi with a standard deviation of 142 psi. Other tests indicate that the weakest bonds are obtained with such 24-hour storage. Storage for four hours and storage for three days have resulted in stronger bonds.
Forty-four bovine teeth were prepared as in Example 3, except that each was painted with a solution of 21/2% phosphoric acid in water (not containing the aluminum oxalate) which was allowed to remain for sixty seconds and then washed away and dried. Next, a solution of 5% .[.of an equilibrated mixture of.]. sodium NTG-GMA .[.and NTG-GMA.]. in a mixture of 85% acetone and 15% water was applied and allowed to dry. Finally, a solution of 20% PMDM in a mixture of 85% acetone and 15% water was applied and allowed to dry. A cylinder of composite was bonded to each treated tooth surface and was stored in water at 37° C. Five samples were tested at four hours; five samples were tested at one day; five samples were tested at one week; five samples were tested at two weeks; and five samples were tested at thirty days. Results are shown below:
______________________________________ 30Soak Time 4 Hours 1 Day 1 Week 2 Weeks Days______________________________________No. of Teeth 14 5 15 5 5Average Bond 1139 1228 924 1094 1152Strength (psi)Standard 201 196 296 206 201Deviation______________________________________
Twenty-eight bovine teeth were prepared as in Example 8, the only difference being that the initial mordant solution was 21/2% phosphoric acid and 1/2% aluminum oxalate in water instead of the phosphoric acid alone. Samples were tested at four hours, one day and one week. Results are shown below:
______________________________________Soak Time 4 Hours 1 Day 1 Week______________________________________No. of Teeth 9 10 9Average Bond 1053 992 1088Strength (psi)Standard 180 152 244.Deviation______________________________________
Twenty bovine teeth were prepared as in Example 8 with the exception that the initial mordant solution was 21/2% phosphoric acid, 1% nitric acid, and 0.5% aluminum oxalate in water. Samples were tested at one hour, one day, and one week. Results are shown below:
______________________________________Soak Time 1 Hour 1 Day 1 Week______________________________________No. of Teeth 10 5 5Average Bond 1424 1029 906Strength (psi)Standard 249 65 37.Deviation______________________________________
Ten bovine teeth were prepared as in Example 8 with the exception that the initial mordant solution was 5% phosphoric acid in water. Samples were tested at two hours and one day. Results are shown below:
______________________________________Soak Time 2 Hours 1 Day______________________________________No. of Teeth 5 5Average Bond 1088 1128Strength (psi)Standard 328 94.Deviation______________________________________
To those skilled in the art to which this invention relates, many changes in construction and widely differing embodiments and applications of the invention will suggest themselves without departing from the spirit and scope of the invention. The disclosures and the descriptions herein are purely illustrative and are not intended to be in any sense limiting.
|Cited Patent||Filing date||Publication date||Applicant||Title|
|US3785832 *||Oct 13, 1971||Jan 15, 1974||Us Health Education & Welfare||Dental primer varnish|
|US4514527 *||Jan 10, 1983||Apr 30, 1985||American Dental Association Health Foundation||Method for obtaining strong adhesive bonding of composites to dentin enamel and other substrates|
|US4521550 *||Jul 25, 1983||Jun 4, 1985||American Dental Association Health Foundation||Method for obtaining strong adhesive bonding of composites to dentin, enamel and other substrates|
|US4540722 *||Jan 15, 1982||Sep 10, 1985||Minnesota Mining And Manufacturing Company||Dentin and enamel adhesive|
|US4588756 *||Feb 7, 1985||May 13, 1986||American Dental Association Health Foundation||Multi-step method for obtaining strong adhesive bonding of composites to dentin, enamel and other substrates|
|US4659751 *||Feb 3, 1986||Apr 21, 1987||American Dental Association Health Foundation||Simplified method for obtained strong adhesive bonding of composites to dentin, enamel and other substrates|
|1||*||Antonucci and Bowen, J. Dent. Res. Aug. 1977 pp. 937 942.|
|2||Antonucci and Bowen, J. Dent. Res. Aug. 1977 pp. 937-942.|
|Citing Patent||Filing date||Publication date||Applicant||Title|
|US5683249 *||Mar 22, 1995||Nov 4, 1997||Den-Mat Corporation||Dental implant process and treated prosthetic|
|US5767170 *||Apr 30, 1996||Jun 16, 1998||Den-Mat Corporation||Dental adhesive comprising an unsaturated monomer, a coupling agent, a crosslinker, leachable fluoride and a photoinitiator|
|US5847020 *||Jun 6, 1997||Dec 8, 1998||Den-Mat Corporation||Dental adhesive comprising a homogeneous mixture of an unsaturated monomer a coupling agent a crosslinking agent and a photoinitiator|
|US5876743 *||Sep 22, 1997||Mar 2, 1999||Den-Mat Corporation||Biocompatible adhesion in tissue repair|
|US6406529 *||Apr 13, 1998||Jun 18, 2002||Mcg Research Institute||Method of reducing dentin sensitivity and compositions therefor|
|US6506055 *||Oct 13, 1999||Jan 14, 2003||Mcg Research Institute||Method of reducing dentin sensitivity and compositions therefor|
|US6575752||May 11, 2000||Jun 10, 2003||Dentsply Detrey Gmbh||Tooth surface treatment composition and methods|
|US7452925 *||Feb 23, 2006||Nov 18, 2008||John A. Kanca, III||Three part dental bonding compositions and methods of use|
|US7665992 *||Nov 17, 2008||Feb 23, 2010||John A. Kanca, III||Three part dental bonding compositions and methods of use|
|US8052421||Oct 7, 2009||Nov 8, 2011||Dentsply International, Inc.||Dispensing syringe having multiple barrels for discharging a dental composition|
|US20070021525 *||Feb 23, 2006||Jan 25, 2007||Kanca John A Iii||Three part dental bonding compositions and methods of use|
|US20090098514 *||Nov 17, 2008||Apr 16, 2009||Kanca Iii John A||Three part dental bonding compositions and methods of use|
|US20100222451 *||Feb 23, 2010||Sep 2, 2010||John A. Kanca, III||Three part dental bonding compositions and methods of use|
|EP2674145A1||Feb 15, 2013||Dec 18, 2013||Bisco, Inc.||Hydrophobic self-etching dental adhesive compositions|
|U.S. Classification||106/35, 260/998.11, 523/116, 523/120, 523/118, 433/228.1|
|International Classification||A61C13/23, A61K6/00|
|Dec 13, 1994||AS||Assignment|
Owner name: DEN-MAT CORPORATION, CALIFORNIA
Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:IBSEN, ROBERT L.;GLACE, WILLIAM R.;PACROPIS, DONALD R.;REEL/FRAME:007238/0373
Effective date: 19941212
|Apr 23, 1998||FPAY||Fee payment|
Year of fee payment: 8
|Apr 11, 2002||FPAY||Fee payment|
Year of fee payment: 12
|Sep 5, 2007||AS||Assignment|
Owner name: DEN-MAT HOLDINGS LLC, CALIFORNIA
Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNOR:DEN-MAT CORPORATION;REEL/FRAME:019781/0024
Effective date: 20070822
Owner name: DEN-MAT HOLDINGS LLC,CALIFORNIA
Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNOR:DEN-MAT CORPORATION;REEL/FRAME:019781/0024
Effective date: 20070822
|Jan 2, 2008||AS||Assignment|
Owner name: DYMAS FUNDING COMPANY, LLC, AS ADMINISTRATIVE AGEN
Free format text: SECURITY AGREEMENT;ASSIGNOR:DEN-MAT HOLDINGS, LLC;REEL/FRAME:020299/0955
Effective date: 20071213
|Nov 15, 2011||AS||Assignment|
Owner name: DEN-MAT HOLDINGS, LLC, CALIFORNIA
Free format text: RELEASE BY SECURED PARTY;ASSIGNOR:DYMAS FUNDING COMPANY, LLC;REEL/FRAME:027226/0873
Effective date: 20111114
|Aug 2, 2012||AS||Assignment|
Owner name: MIDCAP FINANCIAL, LLC, MARYLAND
Free format text: SECURITY AGREEMENT;ASSIGNOR:DEN-MAT HOLDINGS, LLC;REEL/FRAME:028706/0198
Effective date: 20120731