|Publication number||USRE36249 E|
|Application number||US 09/016,706|
|Publication date||Jul 13, 1999|
|Filing date||Jan 30, 1998|
|Priority date||Jun 4, 1993|
|Also published as||DE69401031D1, DE69401031T2, EP0627256A1, EP0627256B1, US5487771|
|Publication number||016706, 09016706, US RE36249 E, US RE36249E, US-E-RE36249, USRE36249 E, USRE36249E|
|Inventors||Robert S. Zeller|
|Original Assignee||Millipore Investment Holdings, Inc.|
|Export Citation||BiBTeX, EndNote, RefMan|
|Patent Citations (26), Non-Patent Citations (63), Referenced by (9), Classifications (27), Legal Events (8)|
|External Links: USPTO, USPTO Assignment, Espacenet|
This is a continuation of application Ser. No. 08/071,554 filed on Jun. 4, 1993, now abandoned.
1. Field of the Invention
The present invention generally relates to a fluid filter and a process for making it. In particular, the invention is a novel all-metal gas filter with high efficiency and low outgassing characteristics that is useful as a point-of-use filter for semiconductor process gases.
2. Description of the Prior Art
Semiconductor manufacturing is constrained by the limitations of purity. In chemical vapor deposition of the alternating layers of silicon and dopant, a critical aspect of the process involves the absence of any particulate impurities. The presence of a minute particle can destroy an entire silicon wafer representing many dollars of potential end-product. To that end, an entire industry has developed concerned with only one thing--the filtering of the gases that may come into contact with semiconductor product during its formation.
Clean rooms equipped with HEPA (High Efficiency Particulate Air) filters are the first line of defense. Process equipment is located within "clean rooms" that are filled with carefully filtered air. The design of the equipment itself endeavors to minimize particle shedding, outgassing, and contamination from the materials used to transport and deliver high-purity gases such as silane, arsine, hydrochloric acid and phosphine. An important component in these delivery systems is the filter which insures that particulate contamination does not reach the point where the gas is discharged onto the work (point of use). These filters must not only remove any particulate material, but also must not add any gaseous contamination to the high purity gases. In addition, the gas delivery systems must also be as compact as possible to eliminate contamination, both particulate and gaseous, which might arise from either the installation of such systems, or the normal wear associated with usage. This is especially the case with highly corrosive gases such as hydrochloric acid. Therefore the filters must not only remove particulate material and not be a contributor of gaseous impurities, but they must also be as compact as possible and have small internal and filter volumes.
Various filters are used for filtration of such gaseous fluids to insure ultra high levels of purity in terms of particulate contamination. These include: organic membrane filters, ceramic filters, filters formed from porous metal structures and filters formed from metal fibers. Although some of these various filter media are capable of providing particulate contamination control to levels less than one part per million or greater in terms of particulate control, they are characterized by large filter areas. Due to the large flow area required to sustain flow at reasonable pressures and maintain low face velocities to insure particulate retention, gaseous impurities such as moisture, oxygen and especially hydrocarbons are often present in detectable levels (parts per million). This contamination can occur during manufacture of the filter, during installation of the filter when it is exposed to an atmosphere other than a high purity gas, or even as a result of outgassing from the material the filter is packaged in. In addition, large filter volumes require relatively larger housings to contain them. This in turn results in a greater likelihood of contamination due both to installation and usage and the need for larger gas delivery systems to fit the filters.
Present metal filters include stainless steel, nickel, or nickel alloy sintered-powder types such as the Wafergard® II SF ( Millipore Corporation, Bedford, Mass.), and the Mott GasShield (Mott Metallurgical Corporation, Farmington, Conn.) (See U.S. Pat. No. 5,114,447, Davis) line of filters. Such filters, being all metal, exhibit low outgassing, high efficiency, corrosion and temperature resistance, low porosity and gas throughput, and high structural strength. However, low porosity has continued to be a drawback for typical sintered metal powder filter elements. Porosities for the above filters range from 40 to 44%, limiting the flow-through characteristics of these filters. The low porosities are inherent in the processes used to manufacture sintered metal powder filters. Typically, the powders are compacted into a mold to form a "green form," then sintered to join the metal particles together to impart the necessary strength. The final filter elements (or "membranes") may be cut from a flat sintered sheet of metallic powder, or molded into the final shape in the molding step. The temperatures at which the sintering proceeds are a critical factor in determining the final porosity. Higher temperatures lead to increased strength, but lower porosity; lower temperatures lead to decreased strength and high porosity. Until now, the final porosity was limited to about 45% in the sintered metal powder art.
There exists a need for increased porosity and gas throughput in the metal filter art. Increased porosity would allow for the construction of smaller filters with all the positive aspects of highly porous metal filters, with less outgassing and particulate shedding problems.
In accordance with the present invention it has been found that highly porous, high-flow filter devices made front filamentary metal powders can be made which require a fraction of the filter volume found in existing filters. The filters of the present invention retain the high level of particulate efficiency (less that one part per million passage through the filter) found in existing filters, while operating at exponentially higher face velocities. In addition, the gas pressure required to sustain these velocities is equivalent to or less than existing filters. The filter of the present invention has minimal internal volume and is highly compact, resulting in very low contaminant generation due to exposure to atmospheres other than high purity gases and the wear associated with usage. In addition, the present invention shares other advantages characteristics of porous metal filters, namely good mechanical and thermal properties allowing operation at elevated temperatures and high differential pressures, and the absence of particulate shedding associated with prolonged usage.
The present invention is a high-porosity metallic membrane element, comprising a sintered element having at least about 55% porosity, the sintered element comprising a matrix of substantially interconnected pores, each of the pores being defined by a plurality of dendritic metallic particles. A preferred form of the invention is made from dendritic nickel powder and has a porosity in excess of 65%. In a preferred embodiment a low sintering temperature of from about 675 degrees to about 725 degrees centigrade is employed. No binder is employed, practically eliminating outgassing in the final membrane element.
The invention also includes a high-porosity metallic membrane filter device. The filter includes a sintered membrane element having at least about 55% porosity, the sintered element comprising a matrix of substantially interconnected pores, each of the pores being defined by a plurality of dendritic metallic particles. The filter also includes a filter housing defining a fluid conduit, the conduit being a casing for retaining the filter element in the fluid flow path, the casing having a front and a back with the element being located between them. In a preferred embodiment, the filter element is welded to the casing wall. Means for sealably connecting the casing to a fluid to be filtered are provided by utilizing typical Swagelock®-style connectors.
Another aspect of the invention is a method of making a high-porosity metallic membrane element comprising the steps of first depositing a substantially uniform low-density bed of a sinterable dendritic material into a mold suitable for applying compressive force thereto. The second step is compressing the low-density bed of sinterable dendritic material to form a green form. The last step is sintering the green form at a temperature below the melting point of the metallic material. In a preferred method of the invention, depositing the substantially uniform low-density bed includes, but is not limited to, the steps of first air-laying the sinterable dendritic material into a mold suitable for applying compressive force thereto, the air-laid bed having a density less than or equal to the density of the sinterable dendritic material. In a preferred embodiment, the sinterable dendritic material is filamentary nickel powder. Compressing the bed of nickel is accomplished at a pressure below about 500 psi, in the absence of any binder. The sintered green form is compressed at a second higher pressure, thereby imparting additional structural rigidity to the element. The higher pressure is generally in the range of 600-1000 psi. The final porosity of the sintered membrane element is generally from about 55% to about 70%.
Accordingly, it is an object of the present invention to provide a highly efficient high-porosity metallic membrane element useful as a point-of-use filter in the semiconductor industry. The high efficiency of the invention allows a substantial savings in space utilized in the process instrumentation, reduced outgassing due to decreased internal surface area, and reduced pressure drop over the length of the filter.
It is another object of the invention to provide a method for forming high-porosity metallic membranes with excellent structural strength, very high porosity, and without the use of any binders.
It is still another object of the invention to provide a membrane element that may be formed in any of numerous shapes for inclusion into a filter housing.
FIG. 1(a) is an photomicrograph of the surface of a sintered nickel membrane element made in accordance with the present invention. A 10 μm scale is provided for purposes of illuminating the relative sizes of the pores.
FIG. 1(b) is an photomicrograph of the surface of a prior art sintered nickel membrane element, taken under the same conditions as FIG. 1(a). Pore sizes appear similar, but the apparent pore density is visibly lower.
FIGS. 2(a-f) are schematic representations of the process for producing a metallic membrane element. FIG. 2(a) depicts the air-laying step and apparatus used therein. FIG. 2(b) shows the second step of low-pressure compression of the air-laid powder into a green form. Porosity (PO) of the green form is about 80-90%. FIG. 2(c) depicts the high-temperature vacuum bake/hydrogen reduction, resulting in a sintered green form with a PO ranging from 70-80%. FIG. 2(d) shows the second compression at a higher pressure, typically from 600-1110 psi. PO decreases to between 55-70%, FIG. 2(e) shows the cutting step. Wire EDM cutting is depicted. FIG. 2(f) shows the final low-temperature vacuum bake step.
FIG. 3 is a graph of total hydrocarbons (ppb) versus time (minutes) representing total hydrocarbon outgassing from the Mott GasShield™ model POU-05 and the present invention.
FIG. 4 is a graph of face velocity (slpm/cm2) versus the log reduction values (LRV) for the invention, and for various prior art products. The invention (labeled "nf") shows higher LRVs at all face velocities. Prior art products are the "sf" filter (Wafergard® II SF Mini In-line Gas Filter, Millipore Corporation, Bedford, Mass.); Ultramet-L Gaskleen™, model #GLFF4000VMM4, (Pall Corporation, East Hills, N.Y.); Mott GasShield model POU-05 (Mott Mettalurgical Corporation, Farmington, Conn.).
FIG. 5 is a graph plotting face velocities (slpm/cm2) against pressure for the same products as in FIG. 4.
FIG. 6 is a graph showing the realtionship between porosity and permeability of the membrane of the present invention.
FIG. 7 is a cross-sectional schematic of the filter device of the present invention prior to welding the membrane element to the inner circumference of the filter housing.
FIG. 8 is a cross-sectional schematic of the filter device of the present invention after welding the membrane element to the inner circumference of the filter housing.
The invention provides a high efficiency high-porosity all metal filter membrane and a method for making it. Filters incorporating the membrane exhibit increased fluid throughput, decreased pressure loss, substantially lower outgassing, and decreased size and complexity. These characteristics make this filter ideal as a point-of-use process gas filter in the semiconductor, and related, industries.
The following terms are used in this application. The term "porosity" is defined as the amount of pore volume per total volume of the membrane element. Per cent porosity is the pore volume divided by the total membrane element volume, multiplied by 100.
As used herein, the term "metallic" is meant to describe all metal-containing materials. This includes, but is not limited to, pure metals, mettaloids, metal oxides, metal alloys, and similar combinations that would be obvious to one of ordinary skill in the metalworking art.
As used herein the term "membrane element" describes the wafer-like product of this invention. It is characterized in that it has a high internal pore volume, excellent structural rigidity and strength, and low pressure drop when fluids, specifically gases, are passed through it. Other shapes may be used in addition to wafers.
As used herein the term "matrix" describes a physical structure comprising a network of interrelated pores or crevice-like areas. The matrix, while generally a uniform structure, is not necessarily 100% uniform. Some pores may be completely unconnected to other pores, and thus may not be connected to the matrix. "Substantially interconnected" can thus be interpreted to mean that the majority of the pores will touch upon or share elements of at least one other pore, thereby allowing communication between the pores.
As used herein the term "dendritic" refers to the tree-like appendages that the metallic particles display. The term comes from "dendrite" which is a highly branched nerve cell. The dendritic property of the metallic powder makes it possible to attain a higher pore area than with non-dendritic metal powders because of the interactions of the branches with each other. Other metal powders which are or may be made dendritic come within the scope of this invention.
As used herein the term "green form" is a term well-known in the sintering art. It refers to the compressed metal powder structure before it is sintered. The green form displays a higher porosity than the final sintered membrane, but is very fragile.
As used herein the term "sinterable dendritic material" refers to any matter whose individual particles have a highly branched external surface, the particle also being capable of being sintered.
As used herein the term "substantially uniform" when used to describe the low-density bed means that there are few or no significant local variations in the density of the air-laid bed.
With reference now to FIG. 1(a), a close-up photomicrograph of a sintered metallic membrane element made in accordance with the method of the invention is shown. The membrane depicted is comprised of a filamentary nickel powder. In a preferred embodiment a filamentary nickel powder such as commercially available INCO 255 (Novamet Specialty Products, Wyckoff, N.J.) is used. Applicant has discovered that under the proper conditions of pressure, temperature and time, a novel and surprisingly porous material can be fabricated. While the present invention is primarily described as employing filamentary nickel powders with a Fisher size of between 2 and 3 μm (ASTM B 330), it is understood that other metal powders having the physical characteristics of this filamentary, dendritic powder may be employed to produce highly porous metal membranes, using the same techniques as described herein. Applicant has discovered that manipulation of certain critical conditions results in a surprisingly porous yet strong metallic membrane structure. In this regard, other filamentary metal powders may also be used or later developed which may be successfully used in this invention. The size of the pores shown in FIG. 1(a) ranges from about 2 to about 10 μm. The density of the starting filamentary powdered metal is typically 0.5 to 1.0 g/cc. The final product density is between about 2.75 and 3.0 g/cc.
FIG. 1(b) is a similar photomicrograph of a prior art nickel filter taken under identical conditions. Note that the pore size is approximately the same as the present invention, but the pore frequency is visibly less. This is reflected in the fact that the density of the prior art filter is 5.0-5.75 g/cc, while the density of the membrane of the present invention is from about 2.75 to 3.0 g/cc.
FIG. 2 is a schematic generally describing the process of making a metallic membrane element. In accordance with the process of the present invention, a highly porous metal membrane is prepared by employing a variety of novel operations. Generally, the steps of the process include depositing a uniform bed of metal powder by air-laying a bed of sinterable dendritic metallic powder to form a highly uniform, exceedingly low-density powder bed whose apparent density is equal to or less than that of the powder as it is obtained from its container (FIG. 2(a)). The next step is the low-pressure press of such a bed to form a high-porosity semi-self supporting green form (FIG. 2(b)), and then the low temperature sintering of the green form to produce a self-supporting highly porous metal membrane with porosity exceeding 70% (FIG. 2(c)).
FIG. 2(a) depicts the first step of air-laying. As mentioned above, the formation of an exceedingly low-density bed of high uniformity is accomplished through the use of air-laying procedures. The term "air-laying" as used herein refers to the procedure whereby a pre-determined mass of powder 10 is sifted through a screen sieve 20 and allowed to fall under the influence of gravity into a mold 30 below of fixed volume. Since the powder is "fluffed up" in this manner, its density becomes lower than that of the packaged powder. The distance the powder falls before coming into contact with the mold will necessarily vary depending on the area and shape of the mold. A variety of individual molds can be used depending upon the final shape and size of the desired product. For example, a 13 cm diameter round mold requires a falling height of at least 25 cm when using filamentary nickel powders to insure a powder bed 40 of substantially uniform thickness and density. A larger diameter mold would require a larger falling distance. One of ordinary skill in the art will be able to determine this height through the use of routine experimentation, given the examples set forth herein. The bed 40, formed in the manner described, has a density equal to or less than that of the apparent density of the powder 10. Apparent density is determined following the procedure outlined in ASTM B 329. For filamentary nickel powders with an apparent density of approximately 1.0 g/cc the air-laid bed density can be as low as 0.7 g/cc.
Now with reference to FIG. 2(b) the air-laid bed 40 formed as described is then pressed using compressing means 50 to the desired thickness using relatively low pressure, forming a green form 60. The resulting porosity ranges from 80-90%. The degree of pressure required necessarily depends on three variables, namely the density of the air-laid bed 40, the thickness of the bed, and the desired thickness of the pressed green form 60. For example, for a bed with a density of 0.8 g/cc and a thickness of 0.6 cm, a force of 30 kg/cm2 (430 psi) is required to obtain a green form thickness of 0.4 cm. The density of such a green form would be 1.3 g/cc and have a porosity of 85%. The green form 60 is self-supporting only to the extent that it can, with care, be removed from the mold while retaining its structure. However, the introduction of relatively minor stress on green form 60 can cause it to lose its integrity.
Now with reference to FIG. 2(c), self-supporting green form 60 is given additional strength through the sintering step depicted therein. Generally, sintering is accomplished by heating a metallic powder in a sintering oven 70 to a temperature below its melting point in the presence of an inert or reducing atmosphere, or in vacuum. One of ordinary skill in the an of sintering will be able to determine the specific atmospheric conditions in which to sinter. The temperature and, to a lesser degree, the duration of the sintering process, are two critical factors which determine the final dimensions, and hence porosity, of the metal membrane. The porosity of the sintered product typically decreases to 70-80%. This occurs as a result of both sinter bonding of the powder particles and shrinkage of the membrane. A lower temperature and shorter sinter duration result in a membrane with smaller degrees of both sinter bonding and shrinkage. For example, a green form with a porosity of 80% sintered at 950° C. for 5 minutes results in a membrane with a porosity of 58%. The same green form sintered at 800° C. for 5 minutes results in a membrane with 72% porosity. It is apparent that a decrease in temperature results in an increase in resultant porosity. Applicant has discovered that sintering at even lower temperatures is possible. However, a lower limit to temperature does exist insofar as a given metal will not sinter unless given sufficient heat. The lower limit for sintering for filamentary nickel powder with a Fisher size of 2-3 μm has generally been found to be between about 500° and 600° C. The preferred form of the invention utilizes temperatures between about 675° and 725° C., as this results in the appropriate membrane porosity and dimensions when combined with the proper formation of the air-laid bed and green form. A most preferred form of the invention utilizes a sintering temperature of 675° C.
As shown in FIG. 2(d), the next step is to press the sintered green form 80 in compressing means 50 to attain the final dimensions desired. The pressing is generally done at a higher pressure than the initial compaction step, given the fact that the sintered form 80 is now much more rigid. The pressures generally used in this step are usually from about 600 to 1100 psi. In a preferred embodiment, the sintered green form is pressed at greater than 1000 psi. This step reduces the porosity of the product to its final porosity value to produce membrane element sheet 90. The final porosity is typically greater than 55%, and in a preferred embodiment greater than 65%.
As shown in FIG. 2(e), the metallic membrane element sheet 90 may be cut into forms that allow construction of useful filter devices. In a preferred embodiment, wire Electrical Discharge Machining (EDM) is employed for this purpose. Wire EDM cutting is defined as the cutting of metals with a thin wire 100 through which a high electrical current is passed. This method of cutting the membrane element sheet 90 into membrane elements has given the best results. However, one of ordinary skill in the an will be able to adapt other cutting methods that may work equally well. For instance, cutting with an abrasive wheel or laser may effect adequate separation. In a preferred embodiment the size of the nickel membrane element 110 is approximately 1.2 cm in diameter and 0.25 cm in thickness.
Referring now to FIG. 2(f), the membrane elements 110 are low-temperature vacuum-baked to remove any volatiles introduced during the process. The temperature is usually less than 200° C. The final product exhibits minimal outgassing as depicted in FIG. 3. FIG. 3 is a graph of total hydrocarbons (ppb) versus time (minutes). When compared against the prior an, outgassing from the present invention is negligible. Outgassing was measured on a Beckman Model 400A THC Analyzer. The analyzer utilizes a flame ionization detector (FID) to determine the amount of total hydrocarbons (hydrocarbons of all molecular weights) present in a gaseous sample. In the present case, the gas was passed through the filter and on to the analyzer.
The small-diameter membrane element disks demonstrate high efficiency and flow rates. As depicted in FIG. 4, a filter made in accordance with the present method (designated "nf") clearly shows the high efficiency of a nickel membrane element. FIG. 4 is a graph of face velocity (standard liters per minute, hereinafter "slpm") versus log reduction value (LRV). LRV is defined as the log of the ratio of two numbers. In the present case, the ratio is that of the number of particles impacting the filter membrane element on the upstream side of the filter, to the number of particles detected downstream of the filter. Therefore, an LRV value of 7 would imply a challenge of 107 particles and the detection of 1 particle downstream, the log of this ratio being 7. The test is conducted by generating an aerosol containing several million particles with a size distribution centered around 0.014 m, passing this aerosol through the filter and counting those that pass with a condensation nucleus counter (CNC).
The nickel membrane element of the present invention demonstrates excellent gas permeability and exponential flow characteristics. FIG. 5 is a graph of slpm/cm2 versus pressure. Compared are the sintered metal nickel powder filter of the present invention ("nf"), one from Mott Metallurgical Corporation (Mott GasShield™), a sintered steel powder filter from Millipore Corporation, Bedford Mass. (model Wafergard® II SF Mini Inline Gas Filter), and a steel mesh filter from Pall Corporation (Ultramet-L Gaskleen™, model #GLFF4000VMM4, East Hills, N.Y.). Of the three sintered metal powder filters, the 63% porous nf filter exhibits significantly greater permeability at all operating pressures above approximately 5 psi. At 10 psi, the nf filter has a face velocity of 2.4 slpm/cm2 while the other two are at 0.8 and 1.5, respectively. At 20 psi the difference is even greater, with the nf filter at 7.5 versus 1.8 slpm/cm2 for the Mott filter.
FIG. 6 is a further demonstration of the exponential increase in gas flow made possible by the present invention. FIG. 6 is a graph of permeabilty in standard liters per minute for a given pressure (slpm/psi) versus per cent porosity. The data points shown are normalized for a common thickness of 0.10 inch (0.254 cm), having an area of 1 cm2. Typical prior art devices with porosities of 44% (material shown in FIG. 1(b)) have a permeability of approximately 1.2 slpm/psi. However, an 11% increase in porosity to 55% (a 25% increase in porosity) leads to a permeability of 2.2 slpm/psi, an 83% increase in permeability. A 65% porous filter membrane element has a permeability of 4.0 slpm/psi, an increase of 233% over the 44% porous membrane. Finally, a 70% porous membrane is 333% more permeable than a 44% porous membrane. The impact of the exponential relationship shown in FIG. 6 is demonstrated by the increased face velocities for the 63% porous nf filter, as compared to the prior art devices (FIG. 5).
It is clear that the present invention is a clear departure from the prior art. Typical prior art porosities range from 40-44%, with accompanying low permeabilities. The present invention demonstrates permeabilites of from 83% to 333% greater than those demonstrated by materials of the prior art, a surprising result.
As shown in FIGS. 7 and 8, the membrane element 110 may be incorporated into a filter device 120. The filter device 120 comprises a filter housing 130 defining a fluid conduit 140, filter housing 130 comprising a casing for retaining the element in the fluid flow path, the casing having an anterior 132 and a posterior 134 with the element being located therebetween and being sealably joined to the interior casing wall 136 and 138, the housing 130 thereby defining a filtered fluid flow path. Means for sealably connecting the casing to a fluid to be filtered are provided. These include Swagelok® fittings and the like. The main requirement for the connecting means is that it be fluid-tight, i.e., does not leak. One of ordinary skill will be able to determine what means are appropriate under the particular connecting scenarios.
Fabrication of filter devices incorporating the membrane elements is accomplished according to the following general procedure. First, a suitable material is selected for the filter housing 130. The material must be suitable for use under the ultra-clean conditions necessary in the semiconductor fabrication art. Stainless steel is a preferred material, although one of ordinary skill in the an is able to select a suitable filter housing material. The housing is usually constructed of two symmetric halves 132 and 134. The metal membrane element 110 is situated between the two halves 132 and 134. A lip 145 is machined or cast into the outer surfaces of the two housing halves 132 and 134 prior to assembly. Halves 132 and 134 are then united with membrane 110, touching the inner circumference of the housing as depicted in FIG. 7. The two halves 132 and 134 are welded together by heating or other means, sealing membrane 110 within the two halves of the housing. When it solidifies, the result is a solid steel-nickel weld bead 150 which extends from the periphery of the filter housing 160 to the interior of the membrane 110 as shown in FIG. 8. Examination of photomicrographs of sectioned devices have shown this to be the case when correct welding parameters are followed. One of ordinary skill in the art is able to determine the welding parameters through routine trial and error.
Having now generally described this invention, the same will become better understood by reference to certain specific examples which are included herein for purposes of illustration only and are not intended to be limiting unless otherwise specified. All patents and publications cited herein are fully incorporated by reference in their entirety.
Effect of varying the thickness of the air-laid bed on green form density
This example shows that differences in the green form density are directly related to the amount of compaction selected during the initial compressing step. To start, three grams of filamentary nickel powder (INCO 255) were sifted into a 2.54 cm diameter mold as previously described under air-laying techniques, and two individual but identical green forms were made. The initial thickness of both air-laid beds was 0.3-0.4 cm. The first mold (green form number 1) was pressed at 150 psi to a green form with a thickness of 373 cm and a porosity before sintering of 82%. The same mold with the same air-laid bed of INCO 255 nickel powder is compressed again at 500 psi to a thickness of 0.261 cm and a porosity of 74% before sintering. Both are sintered in vacuum at 675° C. for 20 minutes. Number 1 has a final porosity of 75% (a change of -7%), number 2 a final porosity of 63% (a change of -11%). Clearly there is a direct relationship between the pressure applied to the INCO 255 nickel powder and the final porosity. With this teaching one of ordinary skill in the art is able to determine with routine experimentation what pressure will be necessary to attain a certain desired final sintered density.
Effect of varying the weight of the green form on the final density
Adding weight (i.e. more powder) to the mold results in a thicker product with higher density. Two green forms of different weight but identical dimensions are made as previously described in Example 1. The first (number 3) had an initial weight of 2.50 g, and an initial porosity of 75% and was pressed at 500 psi. The second (number 4) had an initial weight of 3.50 g and tin initial porosity of 66% and was pressed at 1000 psi. Both green forms had a thickness of 0.230 cm. Both were sintered at 675° C. for 20 minutes in vacuum. Number 3 had a final porosity of 66% (a change of -9% from the initial porosity). Number 4 had a final porosity of 54% (a change of -12%).
Effect of varying the sintering temperature on the density
Four green forms were made to the same specification as 1, 2, 3 and 4 as described above, number 5 having the same weight and dimensions as number 1, number 6 as number 2 and so on. All 4 green forms were sintered at 775° C. for 20 minutes. An additional four green forms (numbers 9-12) were made, again as numbers 1-4, and sintered in vacuum at 725° C. for 20 minutes.
The results of the three examples below clearly indicate that both green form density and sintering temperature have a direct impact on the final porosity of the metal membrane. It is apparent that the more dense the green form, the greater the decrease in porosity due to sintering. It is also quite clear that higher sintering temperatures result in increased shrinkage and lower porosity. Table 1 is a summary of the results:
TABLE 1______________________________________ Green Porosity Final porosity Change from# Temp. (° C.) (%) (%) Green______________________________________1 675 82 75 -72 675 74 63 -113 675 75 66 -94 675 66 54 -125 775 82 68 -146 775 74 56 -187 775 75 58 -178 775 66 42 -249 725 82 71 -1110 725 74 63 -1111 725 75 63 -1212 725 66 49 -17______________________________________
A preferred fabrication process for making metal powder membranes
70 grams of filamentary nickel powder are sifted into a 12.7 cm diameter mold from a height of 20 cm to give a 0.7 cm-thick bed. This bed is pressed at approximately 30 kg/cm2 (430 psi) to a thickness of 0.4 cm and a density of 1.3 g/cc. The green form has a porosity of 85%. It is sintered at 675° C. for 20 minutes in vacuum. After sintering, the green form (now with a diameter of 11 cm and a thickness of 0.28 cm) is pressed at approx 72 kg/cm2 (1032 psi) to a thickness of 0.25 cm and a density of 2.95 g/cc. The final product has a porosity of 67%.
Although the foregoing invention has been described by way of illustration and example for purposes of clarity and understanding, it will be obvious that certain changes and modifications may be practiced within the scope of the invention, as limited only by the scope of the appended claims.
|Cited Patent||Filing date||Publication date||Applicant||Title|
|US2300048 *||Mar 27, 1940||Oct 27, 1942||Gen Motors Corp||Method of making porous material|
|US2309018 *||Jun 19, 1940||Jan 19, 1943||Gen Motors Corp||Method of making composite strip stock|
|US3505038 *||Aug 24, 1964||Apr 7, 1970||Brunswick Corp||Metal fibril compacts|
|US3759709 *||Apr 28, 1970||Sep 18, 1973||Atomic Energy Commission||Method for producing porous metal products|
|US3933652 *||Apr 25, 1973||Jan 20, 1976||Sherwood Medical Industries Inc.||Process of manufacturing a porous, stainless steel filter element and sealing it in a tubular fitting, and resulting filter|
|US3965010 *||Feb 4, 1975||Jun 22, 1976||E. I. Du Pont De Nemours And Company||Metal filter for melt spinning packs|
|US3980445 *||Jul 3, 1974||Sep 14, 1976||Vasily Alexeevich Aleshin||Method of making filtering metal material|
|US4225346 *||Sep 8, 1978||Sep 30, 1980||Bell Telephone Laboratories, Incorporated||Process for fabricating porous nickel bodies|
|US4430294 *||Jun 3, 1981||Feb 7, 1984||Inco Europe Limited||Process for producing porous nickel bodies|
|US4560478 *||Feb 24, 1983||Dec 24, 1985||Bridgestone Tire Co., Ltd.||Porous ceramic article|
|US4568595 *||Apr 26, 1984||Feb 4, 1986||Morris Jeffrey R||Coated ceramic structure and method of making same|
|US4637877 *||Sep 3, 1985||Jan 20, 1987||Hr Textron Inc.||Filter disc|
|US4707184 *||May 31, 1985||Nov 17, 1987||Scm Metal Products, Inc.||Porous metal parts and method for making the same|
|US4758272 *||May 27, 1987||Jul 19, 1988||Corning Glass Works||Porous metal bodies|
|US4894158 *||Jul 31, 1987||Jan 16, 1990||Kirin Beer Kabushiki Kaisha||Porous filter element with undulations|
|US4912076 *||Oct 3, 1988||Mar 27, 1990||Swiss Aluminium Ltd.||Filter for cleaning exhaust gases of diesel engines|
|US4976760 *||Sep 8, 1989||Dec 11, 1990||Cercona, Inc.||Porous ceramic article for use as a filter for removing particulates from diesel exhaust gases|
|US5069697 *||Aug 3, 1989||Dec 3, 1991||Ngk Insulators, Ltd.||Porous ceramic honeycomb filter and method of producing the same|
|US5072592 *||Jun 26, 1990||Dec 17, 1991||Smc Corporation||Gas cleaner|
|US5114447 *||Mar 12, 1991||May 19, 1992||Mott Metallurgical Corporation||Ultra-high efficiency porous metal filter|
|US5177035 *||Aug 7, 1990||Jan 5, 1993||The Carborundum Company||Molten metal filter and method for making same|
|US5204067 *||Jul 11, 1991||Apr 20, 1993||Schwaebische Huettenwerke Gmbh||Filter|
|JPH0356631A *||Title not available|
|JPH01304022A *||Title not available|
|JPS61118227A *||Title not available|
|JPS62287027A *||Title not available|
|1||Bagshaw, N.E., Barnes, M.P. and Evans, J.A., "The Properties of Porous Nickel Produced by Pressing and Sintering," Powder Metallurgy, vol. 10, No. 19:13-32 (1967).|
|2||*||Bagshaw, N.E., Barnes, M.P. and Evans, J.A., The Properties of Porous Nickel Produced by Pressing and Sintering, Powder Metallurgy, vol. 10, No. 19:13 32 (1967).|
|3||*||Brochure: INCO Nickel Powders, Properties and Applications (1983).|
|4||*||Brochure: Mott GasShield : All Metal Gas Filters.|
|5||Brochure: Mott GasShield™: All Metal Gas Filters.|
|6||Callister, W. D. et al., "Sintering Chromium Oxide with the Aid of TiO2 ", J. Am. Ceramics Soc. 62(3-4): 208-211 (1979).|
|7||*||Callister, W. D. et al., Sintering Chromium Oxide with the Aid of TiO 2 , J. Am. Ceramics Soc. 62(3 4): 208 211 (1979).|
|8||Fleischer, A., "Sintered Plates for Nickel-Cadmium Batteries," Transactions of the Electrochemical Society, vol. 94, No. 6:289-299 (1948).|
|9||*||Fleischer, A., Sintered Plates for Nickel Cadmium Batteries, Transactions of the Electrochemical Society, vol. 94, No. 6:289 299 (1948).|
|10||Gotlinsky, B., et al., "Testing of all Metal Filters for High Purity Semiconductor Process Gasses," 1991 Proceedings--Institute of Environmental Sciences, San Diego, CA, May 1991, pp. 575-584.|
|11||*||Gotlinsky, B., et al., Testing of all Metal Filters for High Purity Semiconductor Process Gasses, 1991 Proceedings Institute of Environmental Sciences, San Diego, CA, May 1991, pp. 575 584.|
|12||Hagel, W. C. et al., "Initial Sintering of α-Cr2 O3 ", J. Am. Ceramic Soc. 49(1): 23-26 (1966).|
|13||*||Hagel, W. C. et al., Initial Sintering of Cr 2 O 3 , J. Am. Ceramic Soc. 49(1): 23 26 (1966).|
|14||Huppmann, W. J.; "Cold Isostatic Pressing of Stainless Steel Filter Cartridges", pp. 579-588.|
|15||*||Huppmann, W. J.; Cold Isostatic Pressing of Stainless Steel Filter Cartridges , pp. 579 588.|
|16||Katayama, H. G., "The Hydrogen Reduction Kinetics of Chronic Oxide Pellet", J. Japan Inst. Metals 50(11): 993-998 (1986).|
|17||*||Katayama, H. G., The Hydrogen Reduction Kinetics of Chronic Oxide Pellet , J. Japan Inst. Metals 50(11): 993 998 (1986).|
|18||Lenel, F.V., "Loose Powder Sintering, Slip Casting and Infiltration." In Powder Metallurgy: Principles and Applications, Metal Powder Industries Federation (New Jersey), pp. 309-311, 318 (1980).|
|19||Lenel, F.V., "Powder Metallurgy, Principles and Applications," Metal Powder Industries Federation, 309-312 (1980).|
|20||*||Lenel, F.V., Loose Powder Sintering, Slip Casting and Infiltration. In Powder Metallurgy: Principles and Applications, Metal Powder Industries Federation (New Jersey), pp. 309 311, 318 (1980).|
|21||*||Lenel, F.V., Powder Metallurgy, Principles and Applications, Metal Powder Industries Federation, 309 312 (1980).|
|22||Neve, J. M. et al., "Initial Sintering of Cr2 O3 ", J. Am. Ceramic Soc.--Discussions and Notes 57(6): 274-275 (1974).|
|23||*||Neve, J. M. et al., Initial Sintering of Cr 2 O 3 , J. Am. Ceramic Soc. Discussions and Notes 57(6): 274 275 (1974).|
|24||Ownby, P. D. et al., "Final Sintering of Cr2 O3 ", J. Am. Ceramic Soc. 55(9): 433-436 (1972).|
|25||*||Ownby, P. D. et al., Final Sintering of Cr 2 O 3 , J. Am. Ceramic Soc. 55(9): 433 436 (1972).|
|26||Plante, W. and Jaillet, J.B., "Downstream Cleanliness of Inorganic Filters for Ultra High Purity Gases," 1991 Proceedings--Institute of Environmental Sciences, San Diego, CA, May 1991, pp. 712-718.|
|27||*||Plante, W. and Jaillet, J.B., Downstream Cleanliness of Inorganic Filters for Ultra High Purity Gases, 1991 Proceedings Institute of Environmental Sciences, San Diego, CA, May 1991, pp. 712 718.|
|28||Rubow, K. L. et al., "Particle Penetration Characteristics of Porous Metal Filter Media For High Purity Gas Filtration", Institute of Environmental Sciences; 1991, pp. 834-840.|
|29||*||Rubow, K. L. et al., Particle Penetration Characteristics of Porous Metal Filter Media For High Purity Gas Filtration , Institute of Environmental Sciences; 1991, pp. 834 840.|
|30||Tracey, V. A.; "Effect of Sintering Conditions on Structure and Strength of Porous Nickel", Powder Mettalurgy 2:45-48 (1979).|
|31||*||Tracey, V. A.; Effect of Sintering Conditions on Structure and Strength of Porous Nickel , Powder Mettalurgy 2:45 48 (1979).|
|32||Tracey, V.A. and Llewelyn, D.M., "Effect of Powder Characteristics on the Sintering of Nickel," 4th European Symp. for Powder Metallurgy, Grenoble, 1975, vol. 3, pp. 671-675.|
|33||Tracey, V.A. and Llewelyn, D.M., "Effect of Powder Characteristics on the Sintering of Nickel," Powder Metallurgy International, 8:126-128, 192 (1976).|
|34||*||Tracey, V.A. and Llewelyn, D.M., Effect of Powder Characteristics on the Sintering of Nickel, 4th European Symp. for Powder Metallurgy, Grenoble, 1975, vol. 3, pp. 671 675.|
|35||*||Tracey, V.A. and Llewelyn, D.M., Effect of Powder Characteristics on the Sintering of Nickel, Powder Metallurgy International, 8:126 128, 192 (1976).|
|36||Tracey, V.A. and Perks, R.P., "The Structure and Properties of Sintered Carbonyl-Nickel Powders," Powder Metallurgy, No. 12:54-71 (1963).|
|37||*||Tracey, V.A. and Perks, R.P., The Structure and Properties of Sintered Carbonyl Nickel Powders, Powder Metallurgy, No. 12:54 71 (1963).|
|38||Tracey, V.A., "A Critical Assessment of Strength Development in Porous Materials," Modern Developments in Powder Metallurgy, Orlando, FL, Jun. 1988, vol. 21, pp. 745-754.|
|39||Tracey, V.A., "An Analysis of the Development of Strength in Porous Nickel Structures" Modern Developments in Powder Metallurgy,: Principles and Processes, Toronto, Jun. 1984, vol. 15, pp. 289-306.|
|40||Tracey, V.A., "Effect of Sintering Conditions on the Structure and Strength of Porous Nickel," 5th European Powder Metallurgy Symposium, Stockholm, 1978, pp. 175-180.|
|41||Tracey, V.A., "Nickel Powders into Sintered Structures for the Alkaline Battery: Porosity Studies," Ind. Eng. Chem. Prod. Res. Dev., 25:582-585 (1986).|
|42||Tracey, V.A., "Nickel Sintered Steels: Developments, Status and Prospects," Adv. Powder Metall. Part. Mater., pp. 303-313 (1992).|
|43||Tracey, V.A., "Porous Materials: Current and Future Trends," Int'l J. of Powder Metallurgy and Powder Technology, vol. 12, No. 1:25-35 (1976).|
|44||Tracey, V.A., "Production of Porous Nickel for Alkaline-Battery and Fuel-Cell Electrodes: Practical and Economic Considerations," Powder Metallurgy, vol. 8, No. 16:241-255 (1965).|
|45||Tracey, V.A., "Sinering of Porous Nickel--Theoretical and Practical Considerations," Proc. 1980 Int'l Powder Metallurgy Conf., vol. 12:423-438 (1980).|
|46||Tracey, V.A., "Usage, Manufacture and Properties of Porous Sintered Nickel", Powder Mettalurgy Int'l. 16(4): 167-170 (1984).|
|47||Tracey, V.A., "Usage, Manufacture, and Properties of Porous Sintered Nickel," Powder Metallurgy International, vol. 16, No. 4:271-274 (1984).|
|48||*||Tracey, V.A., A Critical Assessment of Strength Development in Porous Materials, Modern Developments in Powder Metallurgy, Orlando, FL, Jun. 1988, vol. 21, pp. 745 754.|
|49||*||Tracey, V.A., An Analysis of the Development of Strength in Porous Nickel Structures Modern Developments in Powder Metallurgy,: Principles and Processes, Toronto, Jun. 1984, vol. 15, pp. 289 306.|
|50||*||Tracey, V.A., Effect of Sintering Conditions on the Structure and Strength of Porous Nickel, 5th European Powder Metallurgy Symposium, Stockholm, 1978, pp. 175 180.|
|51||*||Tracey, V.A., Nickel Powders into Sintered Structures for the Alkaline Battery: Porosity Studies, Ind. Eng. Chem. Prod. Res. Dev., 25:582 585 (1986).|
|52||*||Tracey, V.A., Nickel Sintered Steels: Developments, Status and Prospects, Adv. Powder Metall. Part. Mater., pp. 303 313 (1992).|
|53||*||Tracey, V.A., Porous Materials: Current and Future Trends, Int l J. of Powder Metallurgy and Powder Technology, vol. 12, No. 1:25 35 (1976).|
|54||*||Tracey, V.A., Production of Porous Nickel for Alkaline Battery and Fuel Cell Electrodes: Practical and Economic Considerations, Powder Metallurgy, vol. 8, No. 16:241 255 (1965).|
|55||*||Tracey, V.A., Sinering of Porous Nickel Theoretical and Practical Considerations, Proc. 1980 Int l Powder Metallurgy Conf., vol. 12:423 438 (1980).|
|56||*||Tracey, V.A., Usage, Manufacture and Properties of Porous Sintered Nickel , Powder Mettalurgy Int l. 16(4): 167 170 (1984).|
|57||*||Tracey, V.A., Usage, Manufacture, and Properties of Porous Sintered Nickel, Powder Metallurgy International, vol. 16, No. 4:271 274 (1984).|
|58||V.A. Tracey, "Sintering of Porous Nickel," Powder Metallurgy, 26:89-92 (1983).|
|59||*||V.A. Tracey, Sintering of Porous Nickel, Powder Metallurgy, 26:89 92 (1983).|
|60||Wang, H. and Kasper, G., "Evaluating Elements of a Particle test Sequence for Point-of Use Filters," Microcontamination, Jan. 1991, pp. 29-33, 61.|
|61||*||Wang, H. and Kasper, G., Evaluating Elements of a Particle test Sequence for Point of Use Filters, Microcontamination, Jan. 1991, pp. 29 33, 61.|
|62||Williams, N.J. and Tracey, V.A., "Porous Nickel for Alkaline Battery and Fuel Cell Electrodes: Production by Roll-Compaction," International Journal of Powder Metallurgy, 4:47-62 (1968).|
|63||*||Williams, N.J. and Tracey, V.A., Porous Nickel for Alkaline Battery and Fuel Cell Electrodes: Production by Roll Compaction, International Journal of Powder Metallurgy, 4:47 62 (1968).|
|Citing Patent||Filing date||Publication date||Applicant||Title|
|US6372165||Sep 22, 2000||Apr 16, 2002||Praxair Technology, Inc.||Cold isopressing method|
|US6524421||Sep 22, 2000||Feb 25, 2003||Praxair Technology, Inc.||Cold isopressing method|
|US6776941||Jun 6, 2002||Aug 17, 2004||Praxair Technology, Inc.||Cold isopressing method and mold|
|US8097071 *||Oct 22, 2008||Jan 17, 2012||Mott Corporation||Sintered fiber filter|
|US8673065||Jan 12, 2012||Mar 18, 2014||Mott Corporation||Sintered fiber filter|
|US8932381 *||Jun 16, 2010||Jan 13, 2015||Entegris, Inc.||Sintered porous material comprising particles of different average sizes|
|US20080138712 *||Nov 15, 2007||Jun 12, 2008||Toyo Roki Seizo Kabushiki Kaisha||Filter medium and filtration system utilizing the same|
|US20090165651 *||Oct 22, 2008||Jul 2, 2009||Mott Corporation||Sintered fiber filter|
|US20120079940 *||Jun 16, 2010||Apr 5, 2012||Zeller Robert S||Sintered Porous Material Comprising Particles Of Different Average Sizes|
|U.S. Classification||55/523, 55/502, 419/2, 55/503, 95/273, 419/24, 55/DIG.5, 419/39|
|International Classification||B01D46/10, B01D71/02, B22F3/11, B01D39/20|
|Cooperative Classification||B01D71/022, B22F3/1103, B01D69/02, B01D2325/02, B01D67/0041, Y10S55/05, B01D39/2044, B01D2323/08, B01D39/2034|
|European Classification||B01D67/00M10, B01D71/02M, B01D69/02, B22F3/11B, B01D39/20D4B, B01D39/20D2B|
|Jul 28, 1999||FPAY||Fee payment|
Year of fee payment: 4
|Aug 6, 2001||AS||Assignment|
|Sep 14, 2001||AS||Assignment|
|Feb 19, 2003||FPAY||Fee payment|
Year of fee payment: 8
|Apr 4, 2006||AS||Assignment|
Owner name: ENTEGRIS, INC., MINNESOTA
Free format text: MERGER;ASSIGNOR:MYKROLIS CORPORATION;REEL/FRAME:017411/0626
Effective date: 20050805
|Jul 30, 2007||FPAY||Fee payment|
Year of fee payment: 12
|Mar 9, 2009||AS||Assignment|
Owner name: WELLS FARGO BANK, NATIONAL ASSOCIATION, AS AGENT,
Free format text: SECURITY AGREEMENT;ASSIGNOR:ENTEGRIS, INC.;REEL/FRAME:022354/0784
Effective date: 20090302
Free format text: SECURITY AGREEMENT;ASSIGNOR:ENTEGRIS, INC.;REEL/FRAME:022354/0784
Effective date: 20090302
Owner name: WELLS FARGO BANK, NATIONAL ASSOCIATION, AS AGENT,M
Effective date: 20090302
|Aug 17, 2011||AS||Assignment|
Owner name: ENTEGRIS, INC., MASSACHUSETTS
Free format text: RELEASE BY SECURED PARTY;ASSIGNOR:WELLS FARGO BANK NATIONAL ASSOCIATION;REEL/FRAME:026764/0880
Effective date: 20110609