|Publication number||USRE38769 E1|
|Application number||US 10/053,845|
|Publication date||Aug 9, 2005|
|Filing date||Jan 22, 2002|
|Priority date||Apr 17, 1997|
|Publication number||053845, 10053845, US RE38769 E1, US RE38769E1, US-E1-RE38769, USRE38769 E1, USRE38769E1|
|Inventors||Ramesh Keshavaraj, Michael D. Hurst|
|Original Assignee||Milliken & Company|
|Export Citation||BiBTeX, EndNote, RefMan|
|Patent Citations (31), Referenced by (2), Classifications (20), Legal Events (3)|
|External Links: USPTO, USPTO Assignment, Espacenet|
This application is a continuation-in-part of our pending prior application Ser. No. 08/842,825, pending, filed on Apr. 17, 1997, for AIR BAG FABRIC POSSESSING IMPROVED PACKED VOLUME CHARACTERISTICS the contents of which are incorporated herein by reference.
The invention relates generally to synthetic filament yarn fabric for use in the manufacture of an air bag and more particularly to fabric structures which can be packed into small volumes without unduly affecting air permeability.
Fabrics used for manufacturing air bags are required in general to process a limited and controlled air permeability. As will be appreciated, such fabrics are generally woven structures formed from synthetic yarns made up of a plurality of individual filaments. Formation of such fabrics may be carried out on weaving machines using air-jet, water-jet or mechanical means for insertion of filling yarns between a plurality of warp yarns in a manner well known to those of skill in the art. Such woven textile materials are disclosed for example in U.S. Pat. No. 5,704,402 to Bowen et al.; U.S. Pat. No. 5,566,434 to Beasley; U.S. Pat. No. 5,508,073 to Krummheuer et al.; U.S. Pat. No. 5,503,197 to Bower et al.; U.S. Pat. No. 5,356,680 to Krumrheuer et al.; U.S. Pat. No. 5,421,378 to Bower et al.; U.S. Pat. No. 5,277,230 to Sollars, Jr.; U.S. Pat. No. 5,259,645 to Hirabayashi et al.; U.S. Pat. No. 5,110,666 to Menzel, et al.; U.S. Pat. No. 5,093,163 to Krummheuer et al.; U.S. Pat. No. 5,073,418 to Thornton et al.; U.S. Pat. No. 5,011,183 to Thornton et al.; U.S. Pat. No. 4,977,016 to Thornton et al.; U.S. Pat. No. 4,921,735 to Bloch and U.S. Pat. No. 3,814,141 to Iribe et al. (all specifically incorporated herein by reference).
As will be appreciated, very low controlled air permeabilities may be achieved through the use of coatings applied to the fabric construction. The primary coatings of use have been chloroprene (neoprene), silicone and other elastomeric resins. However, the use of such coatings presents a disadvantage from both an economic as well as a functional standpoint. Specifically, the use of coatings may add substantial cost while at the same time adding bulk to the finished product which translates to a greater folded volume of the final configuration thereby requiring a greater allocation of space within the vehicle deployment system.
In the attempt to avoid the use of coatings while at the same time achieving low and controlled air permeabilities, a number of approaches have been taken. The patents to Thornton et al. and Bloch propose the achievement of low permeability through the use of calendering to close the voids at the interstices between overlapping yarns in the fabric. While such calendering operations may reduce permeability, such operations also generally stiffen the fabric thereby increasing the volume requirements for a packed bag formed on such calendered material. Fabrics have also been produced using extremely tight weave constructions thereby packaging the yarns so tightly together as to achieve the desired low air permeability. One such known construction is a 420 denier nylon 6,6 fabric having 57 threads per inch in the warp and 53 threads per inch in the fill and sold under the trade designation MICROPERM® by Milliken & Company in LaGrange, Ga. A problem associated with this practice is once again the fact that the fabric produced may have relatively poor foldability due to the very high number of threads per inch within the woven construction which increases the stiffness and hence the packed volume requirement.
Packed volume (i.e. foldability) is becoming an increasingly important feature of air bag fabrics. Specifically, good foldability is crucial if the air bag is to be accommodated in the steering wheel of motor vehicles in the least amount of space. In addition, good foldability also makes possible the trouble-free inflation of the air bag for protecting a vehicle occupant in the event of a collision. Further, these issues of packing and trouble-free inflation become even more important as complex folding patterns are utilized to control initial impact in instances where an occupant may be directly facing the deploying cushion.
The difficulty in improving foldability in that processes which are recognized to generally improve the drape of a fabric and thereby its foldability such as for example, physical, pneumatic or hydraulic impingement practices also tend to dramatically increase the air permeability of the fabric to levels outside the range generally considered to be desirable. U.S. Pat. No. 5,508,073 to Krummheuer et al. (incorporated by reference), it has been proposed that improved foldability of air bag fabric can be achieved without sacrificing air permeability so long as yarns having very low filament linear densities are utilized in the construction.
In light of the above, a need exists for a fabric for use in an air bag which can be produced with improved foldability without sacrificing physical properties and without being restricted to the use of low DPF yarns. The present invention provides such a fabric and methods for producing the same and therefore represents a useful advancement over the state of the art
In recognition of the foregoing and other limitations in the prior art constructions, it is a general object of the present invention to provide an air bag fabric of improved foldability which may be constructed from a broad range of yarn types.
It is a further object of the present invention to provide an air bag fabric of improved foldability wherein such improved foldability is achieved by means of inexpensive mechanical treatment processes without substantially increasing air permeability characteristics of the fabric.
It is yet a further object of the present invention to provide an air bag fabric of improved foldability wherein such improved foldability is achieved by means of mechanical treatment processes which additionally reduce variations in physical properties across the width of the fabric as may be introduced during weaving.
It is a further object of the present invention to provide a woven air bag fabric which does not exhibit substantial increases in permeability when subjected to biaxial forces in the warp and fill directions.
Surprisingly, it has been found that the above objects of improved foldability as measured by packed volume under compressive loading and elimination of substantial increases in permeability can be achieved by mechanically compressing the fabric.
Accordingly, in one aspect of the present invention a woven fabric constructed substantially of synthetic yarn is provided which has undergone processing by mechanical compression. The compressed fabric has a packed volume per unit area of fabric which is less than the packed volume per unit area of the fabric prior to mechanical compression.
In another aspect of the present invention, a woven fabric constructed substantially of synthetic yarn is provided which has undergone processing such that the compressed fabric has a packaged volume per unit area of fabric which is less than the packed volume per unit area of the fabric prior to processing. In addition, the static air permeability of the fabric does not substantially increase beyond the value measured in the untensioned state when the fabric is subjected to biaxial tensions in the range up to about 150 pounds force per linear inch.
In another aspect of the present invention, these permeability characteristics are achieved for fabric formed using highly efficient plain and basket weave constructions.
Other objects, features and aspects of the present invention will be apparent through reference to the description of preferred embodiments and accompanying figures as set forth below.
A full and enabling disclosure of the present invention, including the best mode thereof, directed to one of ordinary skill in the art is set forth more particularly in the remainder of the specification including reference to the accompanying figures in which:
Repeat use of reference characters in the present specification and drawings is intended to represent to same or analogous features or elements of the invention.
It is to be understood that the illustrated and described exemplary and potentially preferred embodiments are in no way intended as limiting the broader aspects of the present invention to such illustrated and described embodiments. On the contrary, it is intended to cover all alternatives, modifications and equivalents as may be included within the true spirit and scope of the invention as defined by the appended claims and equivalents thereto.
Referring now to
As will be appreciated, the material of construction for the air bag 12 typically includes at least a portion of woven fabric. Such fabric is generally woven from synthetic yarns which yarns are, in turn, formed from a plurality of filaments twisted together in known configurations. Filaments formed of polyester or nylon are generally preferred and filaments formed of nylon 6,6 may be most preferred. It is contemplated that suitable linear densities for the yarn used in the fabric according to the present invention may range from about 40 denier to about 1200 denier while the denier of the individual filaments therein may range from between 1 denier to about 10 denier.
The fabrics according to the present invention are preferably manufactured in a relatively tight construction, using either a plain or Panama weave. However, twill weaves may also be utilized if desired. By way of illustration only, and not limitation, some typical constructions for the fabric according to the present invention are set forth in Table I below.
Nylon 6,6 Air bag Fabric
Threads Per Inch
In looking to the data of Table I, it is be understood that filament deniers of about 3 are believed to be representative of low denier per filament constructions while deniers of about 6, are believed to be representative of regular denier per filament constructions. The designation of threads per inch is in the state to which the fabric may be finished. That is, the thread density may be achieved either on the loom or through finishing (i.e. scouring and drying). In any event, it is understood that these constructions are in no way intended to be limiting to the scope of the invention herein but are provided only as illustrative of air bag fabric types which may benefit from further processing to improve foldability (i.e. reduce packed volume characteristics) through further processing in accordance with the present invention.
Testing was carried out on each of the fabric constructions listed in Table I to evaluate both air permeability and packed volume characteristics before and after being subjected to further processing in accordance with the preferred practices of the present invention. Specifically, following formation and any finishing which may have been desired to achieve the constructions as listed in Table I, the fabric was thereafter subjected to compressive forces so as to force the yarns of the fabric closer together thereby tending to increase the density (mass per unit area) of the resulting fabric by about 4-10 percent or more in comparison to that of the fabric before compression.
In a potentially preferred practice illustrated in
While the particular operating parameters utilized in practice of the process as illustrated in
As previously indicated, it has surprisingly been found that air bag fabrics which undergo such compression actually demonstrate improved foldability on a per area basis compared to that demonstrated prior to undergoing such treatment despite the fact that the post treatment fabric is denser on an area basis. At the same time, the air permeability of the fabric is not adversely affected and, in fact, in many instances actually decreases. The fabric produced thus exhibits unexpectedly good properties for use in a folded air bag configuration wherein packed volume and air permeability represent critical parameters.
The dynamic air permeability measurements for each of the fabrics is set forth in Table II below as is the packed volume measurements for such fabric for a fixed area of fabric both before and after processing. The fabric reference designations correspond to those set forth in Table I.
Nylon 6,6 Air Bag Fabric
at 0.4 Pounds
at 0.4 Pounds
Force Per in2
at 50 KPa
Force Per in2
at 50 KPa
As indicated, the air permeability measurements set forth in Table II above are for dynamic air permeability which represents the performance of the fabric under instantaneous application of a differential pressure. Such dynamic testing is believed to provide a more realistic portrayal of fabric performance in an air bag during a collision event wherein the bag is inflated within a few milliseconds. In actually carrying out the testing procedures, the equipment is set at a particular differential pressure desired. The set pressure is then built up within a cylinder exhausted quickly across the fabric. The measurement in millimeters per second represents the flow of a volume of gas (mm3) through a given area of fabric (mm2) within a short length of time (sec) upon application of a defined differential pressure drop across the fabric.
In reference to the data of Table II, values are provided for packed volume of both the pre-treatment and post-treatment fabric at an applied pressure of 0.4 pounds force per in2. While performance parameters at a specific pressure have been listed, it is to be understood that such measurements are only for purposes of comparative evaluation between fabric which has undergone treatment to enhance foldability and fabric which has not undergone such treatment evaluated under comparable conditions.
As illustrated, this plain weave fabric is characterized by an air permeability of slightly greater than 1 cfm in the untensioned state when measured with a differential pressure of 124 Pascal (0.5 inches of water) across the fabric. As the fabric is subjected to biaxial loading in both the warp and the fill direction, the measured air permeability initially decreases and thereafter recovers to a level just above 1 cfm.
Importantly, the permeability of the fabric according to the present invention does not spike upwardly as biaxial tensions are applied. This is in dramatic contrast to prior art plain weave fabrics which are known to exhibit permeability increases of several hundred percent when subjected to biaxial tension in the range of interest. In
An important feature of the fabric according to the present invention resides in the fact that although its initial untensioned air permeability is greater than 1 cfm per square foot of fabric at half an inch of water, as is generally advocated for good permeability performance, the fact that the permeability does not substantially increase when tension is applied indicates that this fabric will actually perform as well as a high weave density, low permeability fabric with a starting untensioned air permeability of substantially less than 1 cfm.
Aside for the benefits associated with nonincreasing permeabilities, the fabric according to the present invention also exhibits excellent performance character when measured according to other recognized standards. By way of example only and not limitation, the grab tensile strength of the 630 denier fabric according to the present invention has been measured to be in excess of 650 pounds pursuant to ASTM D-5034; the stiffness of the 630 denier fabric according to the present invention has been measured to be less than 2 pounds pursuant to ASTM D-4032; the trapezoidal tear of the 630 denier fabric has been measured to be about 150 pounds; the tongue tear of the 630 denier fabric according to the present invention has been measured to be about 60 pounds pursuant to ASTM D-2661; and seam strength of the 630 denier fabric as measured pursuant to ASTM D-1683 is about 340 pounds force in the warp direction, about 320 pounds force in the full direction and about 590 pounds force in the bias direction. The weight of this 630 denier fabric is about 7.1 ounces/square yard.
The comparative evaluation of packed volume characteristics for treated and untreated fabric as set forth in Table II was carried out using a testing technique and apparatus substantially as illustrated in
As can be seen through reference to Table II, the packed volume of the pre-treatment fabric was in each case greater than the packed volume of the post-treatment fabric when measured under the same applied pressure. In addition, this beneficial result was achieved without substantially increasing air permeability of the fabric.
In addition to the above-identified advantages of improved foldability with retained air permeability character, the processed fabric according to the present invention is believed to provide the further benefit of reducing any variation in physical properties such as air permeability which may exist across the width of a woven fabric. These variations are generally understood to be due to different levels of residual stress induced during the weaving process. Such stresses may differ from yam to yarn and machine to machine due to slight differences in gripping mechanisms and yarn beat-up. Such residual stresses introduced during the weaving operation can be reduced by balancing the uneven yam crimp as may exist across the fabric width. This may be achieved by subjecting the fabric to mechanical compression in accordance with the preferred practice of the present invention.
The advantages of the fabric according to the present invention can thus be seen to result in a more compact air bag system which does not sacrifice air permeability thereby providing designers with additional flexibility in choices regarding the use of such systems. The air bag system comprises the air bag itself, the accommodation for the air bag in the vehicle, and the control system for releasing the air bag function.
Other embodiments of the invention will, of course, be apparent to those skilled in the art from consideration of the specification and practice of the invention disclosed herein. However, it is intended that the specification and example contained herein be considered as exemplary only, with the true spirit and scope of the invention being defined only by allowable claims and equivalents thereto.
|Cited Patent||Filing date||Publication date||Applicant||Title|
|US3814141||Mar 7, 1973||Jun 4, 1974||Teijin Ltd||Method of weaving on water jet loom|
|US4921735||Sep 14, 1988||May 1, 1990||Klaus Bloch||Air bag for motor vehicles|
|US4955114||Oct 5, 1989||Sep 11, 1990||Sperotto Rimar S.P.A.||Apparatus for causing the shrinking of a cloth|
|US4977016||Oct 28, 1988||Dec 11, 1990||Stern & Stern Industries, Inc.||Low permeability fabric|
|US5010663||Jun 26, 1990||Apr 30, 1991||Stern & Stern Industries, Inc.||Low permeability fabric and method of making same|
|US5011183||Jun 8, 1990||Apr 30, 1991||Stern & Stern Industries, Inc.||Bag, airbag, and method of making the same|
|US5073418||Aug 9, 1990||Dec 17, 1991||Stern & Stern Industries, Inc.||Low permeability fabric, airbag made of same and method of making same|
|US5093163||Sep 6, 1990||Mar 3, 1992||Akzo N.V.||Uncoated fabric for airbags|
|US5110666||May 6, 1991||May 5, 1992||Reeves Brothers, Inc.||Coated fabric structure for air bag applications|
|US5236775||Dec 11, 1992||Aug 17, 1993||Hoechst Aktiengesellschaft||Fabric for airbag|
|US5259645||Dec 18, 1991||Nov 9, 1993||Nissan Motor Co., Ltd.||Method of producing an airbag having doubly woven and singly woven cloth portions, for an airbag restraint system|
|US5277230||Feb 22, 1993||Jan 11, 1994||Milliken Research Corporation||Double twillwoven air bag fabric|
|US5356680||Jul 16, 1992||Oct 18, 1994||Akzo N.V.||Industrial fabrics of controlled air permeability and high ageing resistance and manufacture thereof|
|US5375878||Nov 22, 1993||Dec 27, 1994||Trw Repa Gmbh||Gas bag for a vehicle occupant restraining system and fabric for its production|
|US5421378||Mar 30, 1994||Jun 6, 1995||Milliken Research Corporation||Airbag weaving on a water-jet loom using yarns|
|US5477890||Jul 28, 1994||Dec 26, 1995||Akzo Nobel Nv||Integrated weaving and wet treatment method for manufacturing uncoated industrial woven fabrics|
|US5503197||Jun 5, 1995||Apr 2, 1996||Milliken Research Corporation||Method for producing high weave density airbag fabric on a water-jet loom using unsized yarns|
|US5508073||Aug 27, 1993||Apr 16, 1996||Akzo Nv||Uncoated fabric for manufacturing air bags|
|US5542703||Apr 24, 1995||Aug 6, 1996||Jps Automotive Products Corporation||Air bag having panels with different permeabilities|
|US5566434||Jun 15, 1994||Oct 22, 1996||Jps Automotive Products Corporation||Air bag for use in a motor vehicle and method of producing same|
|US5612124||Aug 17, 1994||Mar 18, 1997||Akzo Nobel Nv||Fabrics of high thermal stability|
|US5637114||Jan 12, 1995||Jun 10, 1997||Hoechst Aktiengesellschaft||Fabric of high drapability, manufacture thereof, use thereof for making airbags, and airbag made thereof|
|US5650207||Sep 29, 1995||Jul 22, 1997||Highland Industries, Inc.||Airbag fabric|
|US5662354||Aug 16, 1994||Sep 2, 1997||Trw Repa Gmbh||Gas bag for a restraining system in vehicles and a fabric for the production thereof|
|US5704402||Apr 1, 1996||Jan 6, 1998||Milliken Research Corporation||Air bag fabric|
|US5713598||Mar 10, 1993||Feb 3, 1998||Takata Corporation||Air bag|
|US5858886||Jul 2, 1996||Jan 12, 1999||Milliken Research Corporation||Low permeability airbag fabric|
|US5865464||Jan 27, 1995||Feb 2, 1999||Asahi Kasei Kogyo Kabushiki Kaisha||Air bag|
|US5881776||Jan 24, 1997||Mar 16, 1999||Safety Components Fabric Technologies, Inc.||Rapier woven low permeability air bag fabric|
|US5941556||Apr 18, 1997||Aug 24, 1999||Autoliv Asp, Inc.||Simplified passenger airbag module using the inflator as a structural member|
|US5984852||Aug 19, 1997||Nov 16, 1999||Takata (Europe) Vehicle Safety Technology Gmbh||Method for accommodating an airbag of an airbag apparatus in a container|
|Citing Patent||Filing date||Publication date||Applicant||Title|
|US9279200 *||May 8, 2013||Mar 8, 2016||Toyobo Co., Ltd.||Base fabric for air bag which hardly causes “bottoming” upon collision|
|US20150084319 *||May 8, 2013||Mar 26, 2015||Toyobo Co., Ltd.||Base fabric for air bag which hardly causes "bottoming" upon collision|
|U.S. Classification||26/18.6, 280/728.1, 28/103, 28/116, 428/35.5, 428/35.2, 428/36.1|
|International Classification||B60R21/237, D03D1/02, B60R21/235, B60R21/16|
|Cooperative Classification||D03D1/02, Y10T428/1362, Y10T428/1345, B60R21/235, B60R2021/2375, Y10T428/1334, B60R21/237|
|European Classification||D03D1/02, B60R21/235|
|Jun 11, 2009||FPAY||Fee payment|
Year of fee payment: 8
|Jul 19, 2013||REMI||Maintenance fee reminder mailed|
|Dec 11, 2013||LAPS||Lapse for failure to pay maintenance fees|