|Publication number||USRE40218 E1|
|Application number||US 10/622,001|
|Publication date||Apr 8, 2008|
|Filing date||Jul 17, 2003|
|Priority date||Apr 21, 1998|
|Also published as||DE69929967D1, DE69929967T2, EP0991795A1, EP0991795B1, US6261433, WO1999054527A2, WO1999054527A3|
|Publication number||10622001, 622001, US RE40218 E1, US RE40218E1, US-E1-RE40218, USRE40218 E1, USRE40218E1|
|Original Assignee||Uziel Landau|
|Export Citation||BiBTeX, EndNote, RefMan|
|Patent Citations (137), Non-Patent Citations (13), Referenced by (32), Classifications (26), Legal Events (3)|
|External Links: USPTO, USPTO Assignment, Espacenet|
This application claims the benefit of U.S. Provisional Application Ser. No. 60/082,521, entitled “Electroplating on Substrates,” filed on Apr. 21, 1998.
1. Field of the Invention
The present invention generally relates to deposition of a metal layer onto a substrate. More particularly, the present invention relates to an apparatus and a method for electroplating a metal layer onto a substrate.
2. Background of the Related Art
Sub-micron multi-level metallization is one of the key technologies for the next generation of ultra large scale integration (ULSI). The multilevel interconnects that lie at the heart of this technology require planarization of interconnect features formed in high aspect ratio apertures, including contacts, vias, lines and other features. Reliable formation of these interconnect features is very important to the success of ULSI and to the continued effort to increase circuit density and quality on individual substrates and die.
As circuit densities increases, the widths of vias, contacts and other features, as well as the dielectric materials between them, decrease to sub-micron dimensions, whereas the thickness of the dielectric layers remains substantially constant, with the result that the aspect ratios for the features, i.e., their height divided by width, increases. Many traditional deposition processes have difficulty filling sub-micron structures where the aspect ratio exceed 2:1, and particularly where it exceeds 4:1. Therefore, there is a great amount of ongoing effort being directed at the formation of void-free, sub-micron features having high aspect ratios.
Elemental aluminum (Al) and its alloys have been the traditional metals used to form lines and plugs in semiconductor processing because of aluminum's low electrical resistivity, its superior adhesion to silicon dioxide (SiO2), its ease of patterning, and the ability to obtain it in a highly pure form. However, aluminum has a higher electrical resistivity than other more conductive metals such as copper and silver, and aluminum also can suffer from electromigration phenomena. Electromigration is considered as the motion of atoms of a metal conductor in response to the passage of high current density through it, and it is a phenomenon that occurs in a metal circuit while the circuit is in operation, as opposed to a failure occurring during fabrication. Electromigration can lead to the formation of voids in the conductor. A void may accumulate and/or grow to a size where the immediate cross-section of the conductor is insufficient to support the quantity of current passing through the conductor, and may also lead to an open circuit. The area of conductor available to conduct heat therealong likewise decreases where the void forms, increasing the risk of conductor failure. This problem is sometimes overcome by doping aluminum with copper and with tight texture or crystalline structure control of the material. However, electromigration in aluminum becomes increasingly problematic as the current density increases.
Copper and its alloys have lower resistivity than aluminum and higher electromigration resistance as compared to aluminum. These characteristics are important for supporting the higher current densities experienced at high levels of integration and increased device speed. Copper also has good thermal conductivity and is available in a highly pure state. Therefore, copper is becoming a choice metal for filling sub-micron, high aspect ratio interconnect features on semiconductor substrates.
Despite the desirability of using copper for semiconductor device fabrication, choices of fabrication methods for depositing copper into high aspect ratio features are limited. Precursors for CVD deposition of copper are ill-developed and involve complex and costly chemistry. Physical vapor deposition into such features produces unsatisfactory results because of limitations in ‘step coverage’ and voids formed in the features.
As a result of these process limitations, electroplating, which had previously been limited to the fabrication of patterns on circuit boards, is just now emerging as a method to fill vias and contacts on semiconductor devices.
Metal electroplating in general is a well-known art and can be achieved by a variety of techniques. Common designs of cells for electroplating a metal on wafer-based substrates involve a fountain configuration. The substrate is positioned with the plating surface at a fixed distance above a cylindrical electrolyte container, and the electrolyte impinges perpendicularly on the substrate plating surface. The substrate is the cathode of the plating system, such that ions in the plating solution deposit on the conductive exposed surface of the substrate and the micro-sites on the substrate. However, a number of obstacles impair consistent reliable electroplating of copper onto substrates having a sub-micron scale, high aspect ratio features. Generally, these obstacles involve difficulty with providing uniform current density distribution across the substrate plating surface, which is needed to form a metal layer having uniform thickness. A primary obstacle is how to get current to the substrate and how to ensure that the current is uniformly distributed thereon.
One current method for providing power to the plating surface uses contacts (e.g., pins, ‘fingers’, or springs) which contact the substrate seed layer. The contacts touch the seed layer as close as practically possible to the edge of the substrate, to minimize the wasted area on the wafer due to the presence of the contacts. The ‘excluded’ area can no longer be used to ultimately form devices on the substrate. However, the contact resistance of the contacts to the seed layer may vary from contact to contact, resulting in a non-uniform distribution of current densities across the substrate. Also, the contact resistance at the contract to seed layer interface may vary from substrate to substrate, resulting in inconsistent plating distribution between different substrates using the same equipment. Furthermore, the plating rate tends to be higher near the region of the contacts and be lower at regions remote from the contacts due to the resistivity of the thin seed layer that has been deposited on the substrate. A fringing effect of the electrical field also occurs at the edge of the substrate due to the highly localized electrical field formed at the edge of the plated region, causing a higher deposition rate near the edge of the substrate.
A resistive substrate effect is usually pronounced during the initial phase of the electroplating process and reduces the deposition uniformity because the seed layer and the electroplated layers on the substrate deposition surface are typically thin. The metal plating tends to concentrate near the current feed contacts, i.e., the plating rate is greatest adjacent the contacts, because the current density across the substrate decreases as the distance from the current feed contacts increases due to insufficient conductive material on the seed layer to provide a uniform current density across the substrate plating surface. As the deposition film layer becomes thicker due to the plating, the resistive substrate effect diminishes because a sufficient thickness of deposited material becomes available across the substrate plating surface to provide uniform current densities across the substrate. It is desirable to reduce the resistive substrate effect during electroplating.
Traditional fountain plater designs also provide non-uniform flow of the electrolyte across the substrate plating surface, which compounds the effects of the non-uniform current distribution on the plating surface by providing non-uniform replenishment of plating ions and where applicable, plating additives, across the substrate, resulting in non-uniform plating. The electrolyte flow uniformity across the substrate can be improved by rotating the substrate at a high rate during the plating process. Such rotation introduces complexity into the plating cell design due to the need to furnish current across and revolving interface. However, the plating uniformity still deteriorates at the boundaries or edges of the substrate because of the fringing effects of the electrical field near the edge of the substrate, the seed layer resistance and the potentially variable contact resistance.
There is also a problem in maintaining an electroplating solution to the system having consistent properties over the duration of a plating cycle and/or over a run of multiple wafers being plated. Traditional fountain plater designs generally require continual replenishing of the metal being deposited into the electrolyte. The metal electrolyte replenishing scheme is difficult to control and causes build-up of co-ions in the electrolyte, resulting in difficult to control variations in the ions concentration in the electrolyte. Thus, the electroplating process produces inconsistent results because of inconsistent ion concentration in the electrolyte.
Additionally, operation of a plating cell incorporating a non-consumable anode may cause bubble-related problems because oxygen evolves on the anode during the electroplating process. Bubble-related problems include plating defects caused by bubbles that reach the substrate plating surface and prevent adequate electrolyte contact with the plating surface. It is desirable to eliminate or reduce bubble formation from the system and to remove formed bubbles from the system.
Therefore, there remains a need for a reliable, consistent metal electroplating apparatus and method to deposit uniform, high quality metal layers on substrates to form sub-micron features. There is also a need to form metal layers on substrates having micron-sized, high aspect ratio features to fill the features without voids in the features.
The invention provides an apparatus and a method for achieving reliable, consistent metal electroplating or electrochemical deposition onto substrates. More particularly, the invention provides uniform and void-free deposition of metal onto substrates having sub-micron features formed thereon and a metal seed layer formed thereover. The invention provides an electro-chemical deposition cell comprising a substrate holder, a cathode electrically contacting a substrate plating surface, an electrolyte container having an electrolyte inlet, an electrolyte outlet and an opening adapted to receive a substrate and an anode electrically connect to an electrolyte. The configuration and dimensions of the deposition cell and its components are designed to provide uniform current distribution across the substrate. The cell is equipped with a flow-through anode and a diaphragm unit that provide a combination of relatively uniform flow of particular-free electrolyte in an easy to maintain configuration. Additionally, an agitation device may be mounted to the substrate holder to vibrate the substrate in one or more directions, ie., x, y and/or z directions. Still further, an auxiliary electrode can be disposed adjacent the electrolyte outlet to provide uniform deposition across the substrate surface and to shape as necessary the electrical field at the edge of the substrate and at the contacts. Still further, time variable current waveforms including periodic reverse and pulsed current can be applied during the plating period to provide a void-free metal layer within sub-micron features on the substrate.
So that the manner in which the above recited features, advantages and objects of the present invention are attained can be understood in detail, a more particular description of the invention, briefly summarized above, may be had by reference to the embodiments thereof which are illustrated in the appended drawings.
It is to be noted, however, that the appended drawings illustrate only typical embodiments of this invention and are therefore not to be considered limiting of its scope, for the invention may admit to other equally effective embodiments.
The present invention generally provides several embodiments of a new electrochemical cell and a method of operation of the cells to deposit high quality metal layers on substrates. The invention also provides new electrolyte solutions which can be used to advantage in the deposition of metals, and copper in particular, into very small features, i.e., micron sized features and smaller. The invention will be described below first in reference to the hardware, then operation of the hardware and then chemistry of the electrolyte solutions.
Electrochemical Cell Hardware
An electroplating solution inlet 50 is disposed at the bottom portion of the container body 42. The electroplating solution is pumped into the container body 42 by a suitable pump 51 connected to the inlet 50 and flows upwardly inside the container body 42 toward the substrate 48 to contact the exposed substrate surface 54.
The substrate 48 is secured on the substrate supporting surface 46 of the substrate holder 44, preferably by a plurality of passages in the surface 46 maintainable at vacuum to form a vacuum chuck (not shown). A cathode contact member 52 is disposed on the lower surface of the substrate holder 44 and supports a substrate over the container. The cathode contact member 52 includes one or more contacts which provide electrical connection between a power supply 49 and a substrate 48. The cathode contact member 52 may comprise a continuous conductive ring or wire or a plurality of conductive contact fingers or wires 56 (Shown in
The cathode contact member 52 provides electrical current to the substrate plating surface 54 to enable the electroplating process and therefore is preferably comprised of a metallic or semi-metallic conductor. The contact member 52 may also include a non-plating or insulative coating to prevent plating on surfaces that are exposed to the electrolyte on the contact member. Plating on the cathode contact member may change the current and potential distributions adjacent to the contact member and is likely to lead to defects on the wafer. The non-plating or insulation coating material can comprise of a polymeric coating, such as TeflonŽ, PVDF, PVC, rubber or an appropriate elastomer. Alternatively, the contact member may be made of a metal that resists being coated by copper, such as tantalum (Ta), tantalum nitride (TaN), titanium nitride (TiN), titanium (Ti), or aluminum. The coating material prevents plating onto the contact and ensures predictable conduction characteristics through the contact to the surface of the substrate. If the contact members are made of metals that are stable in the chemical environment of the cell but may be coated with copper throughout the plating process, such as platinum, gold, and/or their alloys, the contact member is preferably protected by an insulative sheet, an elastomer gasket or coating. The contacts preferably provide low contact resistance to the substrate surface or are coated, particularly in the contact region with a material that provides low contact resistance to the substrate surface. Examples include copper or platinum. Plating on the contact region of the cathode contact member 52 may change the physical and chemical characteristics of the conductor and may eventually deteriorate the contact performance, resulting in plating variations or defects. Hence, the contact region is preferably insulated from the electrolyte by a surrounding insulating ring, sleeve, gasket or coating disposed on the contact member outside the region where the contact physically contacts the substrate. Examples of such coatings include PVDF, PVC, TeflonŽ, rubbers or other appropriate elastomer. If the contact member becomes plated, an anodic current may be passed through the contacts periodically for a brief time to deplate the contact member. The cathode for this rejuvenation process may be either the regular anode (reverse biased) or the auxiliary electrodes described later.
Typically, one power supply is connected to all of the contact pins of the cathode contact member, resulting in parallel circuits through the contact pins. As the pin-to-substrate interface resistance varies, between pin locations, more current will flow, and thus more plating will occur, at the site of lowest resistance. However, by placing an external resistor in series with each contact pin, the value or quantity of electrical current passed through each contact pin becomes controlled mainly by the value of the external resistor, because the overall resistance of each contact pin-substrate contact plus the control resistor branch of the power supply to substrate circuit is substantially equal to that of the control resistor. As a result, the variations in the electrical properties between each contact pin do not affect the current distribution on the substrate, and a uniform current density results across the plating surface which contributes to uniform plating thickness. To provide, a uniform current distribution between each of the contact pins 56 of the radial array configuration of cathode contact member 52, both during the plating cycle on a single substrate and between substrates in a plating run of multiple substrates, an external resistor 58 is connected in series with each contact pin 56.
As each substrate is plated, and over multiple substrate plating cycles, the contact-pin-substrate interface resistance still may vary, eventually reaching an unacceptable value. An electronic sensor/alarm 60 can be connected across the external resistor 58 to monitor the voltage/current across the external resistor to address this problem. If the voltage/current across any external resistor 58 falls outside of a preset operating range that is indicative of a high pin-substrate resistance, the sensor/alarm 60 triggers corrective measures such as shutting down the plating process until the problems are corrected by an operator. Alternatively, a separate power supply can be connected to each contact pin and can be separately controlled and monitored to provide a uniform current distribution across the substrate.
An alternative to the contact pin arrangement is a cathode contact member 52 comprising a continuous ring that contacts the peripheral edge of the substrate.
Referring again to
Optionally, the substrate holder 44 may include a gas inflated bladder 64 disposed adjacent the elastomer ring 62 to enhance the seal created by the elastomer ring 62 and improve the electrical contact between the cathode contact member 52 and the substrate plating surface 54. The gas inflated bladder 64 is disposed in an annular cavity adjacent the elastomer ring 62 and can be inflated by a gas to exert pressure on the elastomer ring 62 and urge the substrate to exert pressure on the elastomer ring 62 and urge the substrate into contact with the contact member 52. To relieve the contact pressure between the elastomer ring 62 and the backside of the substrate 48, a relief valve deflates the gas inflated bladder 64 to allow the elastomer ring 62 to retract into the substrate holder 44.
The substrate holder 44 is positioned above the container body 42 so that the substrate plating surface 54 of a substrate faces the opening of the container body 42. The substrate holder 44 is disposed on an outer ring 66 that is connected to the top portion of container body 42. An insulating O-ring 68 is disposed between the substrate holder 44 and an outer ring shoulder 66. Preferably, the substrate holder 44 includes a beveled lower portion 70 that corresponds to a beveled upper edge 72 of the container body 42 which together form at least a partial circumferential outlet 74, from about 1 mm to about 30 mm, between the substrate holder 44 and the container body 42 for electrolyte flow therethrough. The outlet 74 preferably extends around the perimeter of the container body and cover, but it may alternatively be segmented as shown in
A ring or sleeve insert 80 disposed in the upper portion of the container body 42 can be used to precisely define the plating area of the substrate. The insert 80 is modularly changeable to adapt an electroplating cell for various substrate sizes, including 200 mm and 300 mm sizes, and shapes, including circular, rectangular, square, etc. The size and the shape of the container body 42 are preferably changed correspondingly for each size and shape of substrate to approximate the size and shape of the substrate. The insert 80 also insulates and protects the edge of the substrate 48 from non-uniform plating by limiting the current flow to the circumference of the plating surface, thereby reducing the fringing effects encountered when the cell size is larger than the plating surface.
As plating occurs on the substrate, ions in solution plate (deposit) from the solution onto the substrate. To provide additional plating material, ions must diffuse through a diffusion boundary layer adjacent the plating surface. Typically, in the prior art, replenishment is provided through hydrodynamic means by the flow of solution past the substrate and by substrate rotation. However, hydrodynamic replenishment schemes still provide inadequate replenishment because of the no slip condition at the boundary layer where the electrolyte immediately adjacent the plating surface has zero velocity and is stagnant. To address these limitation and increase replenishment, a vibrational agitation member 82 is provided to control the mass transport rates (boundary layer thickness) at the surface of the substrate. The vibrational agitation member 82 is preferably mounted to the substrate holder 44 to vibrate the substrate 48. The vibrational agitation member 82 usually comprises a motor or a vibrational transducer that moves the substrate holder 44 back and forth on one or more axes at a frequency from about 10 Hz to about 20,000 Hz. The amplitude of the vibration is preferably between about 0.5 micron and about 100,000 micron. The vibrational agitation member 82 may also provide additional vibration in a second direction that is parallel to the substrate plating surface 54, such as vibrating the substrate in the x-y directions, or in a direction orthogonal to the substrate plating surface 54, such as in the x-z directions. Alternatively, the vibrational agitation member 82 may vibrate the substrate in multiple directions, such as the x-y-z directions.
The frequency of the vibration can be synchronized to the plating cycles (discussed in detail below) to tailor-fit the mass transport rates to the deposition process needs. Conventional electroplating systems cannot incorporate this feature because high frequency interruptions or reversals cannot be made in pumped induced electrolyte flow due to the fluid's inertia in conventional electroplating systems. The vibration also enhances removal of residual plating and rinse solution from the substrate surface after completion of the plating cycle.
The substrate holder 44 can also be rotated, either fully or partially, in addition to the vibrational agitation to further enhance uniform plating thickness. A rotational actuator (not shown) can be attached to the substrate holder 44 and spin, or partially rotate in an oscillatory manner, the substrate holder about a central axis through the center of the substrate holder. The rotational movement of the plating surface against the electrolyte enhances the exposure of fresh electrolyte across the plating surface to improve deposition uniformity.
Another advantage of vibrating the substrate 48 is that the vibration exposes the vias and trenches to fresh electroplating solutions. As the solution adjacent to the substrate becomes depleted of the deposition metal, the reciprocation of the substrate replenishes the areas adjacent to the vias and trenches with fresh electroplating solution preferably having a high concentration of copper or other deposition metal. This is achieved by translating the mouth of the trench or the via on a substrate plating surface to a region of the solution that has not been facing the trench or via and is therefore less depleted of the reactant. An alternative to vibrating the substrate holder 44 and the substrate 48 is vibrating the electrolyte. A vibrational transducer (not shown) can be placed within the container body to directly agitate the electrolyte, or the vibrational transducer can be placed outside of the container body and indirectly agitate the electrolyte by vibrating the container body. The vibrational agitation member 82 also helps to eliminate bubble related defects by encouraging bubbles to move from the plating surface 54 and be evacuated from the cell 40.
Gas bubbles may be trapped with the substrate installation into the cell, carried by the electrolyte flow through the system, or generated by the electrochemical reaction at the anode or the cathode. The gas bubbles are preferably exhausted from the cell to prevent defects in the plating process. A plurality of gas diverting vanes may be disposed above the anode to divert evolved gases toward the sidewall of the electrolyte container. Generally, gas bubbles will move to a higher elevation because of their lower specific gravity, and the gas bubbles flows along with the electrolyte that flows generally upward and outward with respect to the substrate. The vibration is applied to the electrolyte or the substrate support member detaches the bubbles from the substrate surface and enhances the movement of the gas bubbles out of the cell. Preferably, a plurality of gas release ports 81 (as shown in
In addition to the anode electrode and the cathode electrode, an auxiliary electrode can be disposed in contact with the electrolyte to change the shape of the electrical field over the substrate plating surface. An auxiliary electrode 84 is preferably disposed outside the container body to control the deposition thickness, current density and potential distribution in the electroplating cell to achieve the desired electroplating results on the substrate. As shown in
The auxiliary electrode 84 may comprise a ring, a series of concentric rings, a series of segmented rings, or an array of spaced electrodes to match a corresponding array of cathode contact pins 56. The auxiliary electrode 84 may be positioned on the same plane as the substrate plating surface 54 or on varying planes to tailor fit the current and potential distribution on the substrate 48. Alternatively, a plurality of concentric ring auxiliary electrodes can be configured to activate at different potentials or to activate potentials in sequence according to the desired process.
Alternatively, the auxiliary electrode comprises a segmented resistive material having multiple contact points such that the voltage of the auxiliary electrode varies at different distances from the contact points. This configuration provides corresponding variations of potential for a discrete cathode contacting member configuration. Another variation of the auxiliary electrode provides a variable width electrode that corresponds to a configuration of discrete cathode contacting pins so that an effective higher voltage (and current) is provided at the substrate contacting points of the cathode contact member while an effective lower voltage (and current) is provided in the region between the substrate/cathode contacting points. Because the effective voltage provided by the variable width auxiliary electrode decreases as the distance increases between the auxiliary electrode and the edge of the substrate, the variable width auxiliary electrode provides a closer distance between the auxiliary electrode and the edge of the substrate where the cathode contact member are located.
Preferably, a consumable anode 90 is disposed in the container body 42 to provide a metal source in the electrolyte. As shown in
Preferably, the anode 90 is a modular unit that can be replaced easily to minimize interruptions and to allow easy maintenance. Preferably, the anode 90 is positioned a distance greater than one (1) inch, and more preferably, greater than 4 inches, away from the substrate plating surface 54 (for a 200 mm substrate) to assure that the effects of level variations in the anode copper caused by anode dissolution, particulate fluidization and assembly tolerances become negligible once the electrolyte flow reaches the substrate surface.
A flow adjuster 110 comprising a variable thickness conical profile porous barrier can be disposed in the container body between the anode and the substrate to enhance flow uniformity across the substrate plating surface. Preferably, the flow adjuster 110 comprises a porous material such as a ceramic or a polymer which is used to provide a selected variation in electrolyte flow at discrete locations across the face of the substrate.
A broken substrate catcher (not shown) can be placed within the container body to catch broken substrate pieces. Preferably, the broken substrate catcher comprises a mesh, a porous plate or membrane. The porous wedge or the perforated plate described above may also serve for this purpose.
A refining electrode (not shown) can be placed in the sump (not shown) for pre-electrolysis of the electrolyte and for removal of metal and other chemical deposit buildup in the sump. The refining electrode can be continuously activated or periodically activated according to the needs of the system. The refining electrode when made of copper and polarized anodically can be used to replenish copper in the bath. This external electrode can thus be used to precisely adjust the copper concentration in the bath.
A reference electrode (not shown) can be employed to determine precisely the polarization of the anode, the cathode and the auxiliary electrode.
Once the electroplating process is completed, the electrolyte can be drained from the container body to an electrolyte reservoir or sump, and a gas knife can be incorporated to remove the film of electrolyte remaining on the substrate plating surface. The gas knife comprises a gas inlet, such as a retractable tube or an extension air tube connected to a hollow anode electrode, which supplies a gas stream or a gas/liquid dispersion that pushes the electrolyte off the substrate surface. The gas can also be supplied through the gap between the substrate holder 44 and the container body 42 to blow on the substrate surface.
A deionized water rinse system (not shown) can also be incorporated into the electroplating system to rinse the substrate free of electrolyte. A supply of deionized water or other rinsing solutions can be connected to the inlet 50 and selectively accessed through a inlet valve. After the electrolyte has been drained from the container body, the deionized water or other rinsing solution can be pumped into the system through inlet 50 and circulated through the container body to rinse the substrate surface. While the processed substrate is being rinsed, the cathode and anode power supply is preferably inactivated in the cell. The deionized water fills the cell and flows across the surface of the substrate to rinse the remaining electrolyte off the surface. The vibrational member may be activated to enhance rinsing of the plated surface. A number of separate deionized water tanks can be utilized sequentially to increase the degree of purity of the rinse water. To utilize more than one rinsing solution supply, a rinsing cycle is preferably completed and the rinsing solution completely drained from the cell before the next rinsing solution is introduced into the cell for the next rinsing cycle. The used deionized water rinse can also be purified by plating out the metal traces acquired during the rinse cycle by the rinsing solution or by circulating the used deionized water through an ion exchange system.
A plurality of auxiliary electrodes 216 can be placed in the cell at the corners of the polygon. Alternatively, ring shaped or segmented ring auxiliary electrodes 218 can be placed around each substrate 48 to match the cathode contact members 212 similarly to the arrangement of the auxiliary electrodes shown in FIG. 3. Preferably, the auxiliary electrodes dynamically adjust to compensate current distribution over the substrate by gradually decreasing the current of the auxiliary electrodes as the resistive substrate effect tapers off after the initial deposition period. A porous separator/filter (not shown) can be placed between the anode and the cathode to trap particulates.
A vibrational agitation member (not shown) can be connected to the container body to vibrate the substrates. However, substrate vibration may be unnecessary when the polygonal anode drum is rotated sufficient fast, preferably between about 5 revolutions per minute (RPM) and about 100 RPM, to provide a high degree of agitation to the electrolyte. The rotating polygonal anode also provides a pulsed or transient electrical power (voltage/current combination) due to the varying distance between the active anode surfaces and the substrate because of the rotation. Because the anode is polygonal in shape, as the anode rotates, the distance between cathode and the anode varies from a maximum when the anode polygon faces are aligned with the cathode polygon faces in parallel planes and a minimum when the anode polygon corners are aligned with the centers of the cathode polygon faces. As the distance between the anode and the cathode varies, the electrical current between the anode and the cathode varies correspondingly.
Another variation provides a horizontally positioned polygonal drum. The container body is rotated around the horizontal axis to position one polygon face on top to allow loading and unloading of a substrate while the other substrates are still being processed.
Yet another variation provides the substrates to be mounted on the outer surfaces of the inner polygon drum which now is the cathode, and the container body becomes the anode. This configuration allows the cathode drum to be lifted from the electrolyte for easy loading and unloading of the substrates.
In one embodiment of the invention, a periodic reverse potential and/or current pulse or an intermittent pulse current is delivered to the substrate to control the mass transfer boundary layer thickness and the grain size of the deposited material. The periodic reverse and pulse current/potential also enhances deposit thickness uniformity. The process conditions for both the deposition stage and the dissolution stage can be adjusted to provide the desired deposit profile, usually a uniform, flat surface. In general, plating/deposition is accomplished with a relatively low current density for a relatively long interval because low current density promotes deposition uniformity, and dissolution is accomplished with a relatively high current density for a relatively short interval because high current density leads to highly non-uniform distribution that preferentially shaves or dissolves deposited peaks.
For a pre-determined grain size, a current pulse comprising a higher negative current density for a short time (between about 50 mA/cm2 and about 180 mA/cm2 for about 0.1 to 100 ms) is applied to nucleate an initial layer of copper deposits followed by a constant current density applied for a long interval (between about 5 mA/cm2 and about 80 mA/cm2 for up to a few minutes) to continue deposition. The length of the deposition interval can be adjusted according to the deposition rate to achieve the desired deposition thickness over the substrate surface.
To completely fill high aspect ratio trenches, vias or other interconnect features, a current reversal or dissolution interval may be applied to achieve some dissolution of the deposited metal. The dissolution interval is preferably applied at a current density much higher than the current density of the deposition current but for a short time interval to ensure a net deposit. The dissolution interval can be applied once or periodically during a deposition process to achieve the desired results. The deposition interval can be divided into a number of short intervals followed by a corresponding number of even shorter dissolution intervals to completely fill high aspect ratio interconnect features. Then, a constant deposition current density is applied to achieve a uniform deposition thickness across the field. Typically, a deposition cycle comprises a deposition current density of between about 5 mA/cm2 and about 40 mA/cm2 followed by a dissolution current density between about 5 mA/cm2 and about 80 mA/cm2. The deposition cycle is repeated to achieve complete, void-free filling of high aspect ratio features, and optionally, a final application of the deposition current density is applied to form a uniform field deposition thickness across the substrate plating surface. Alternatively, the current reversal/dissolution cycle can be achieved by providing a constant reverse voltage instead of a constant reverse current density.
Because the resistive substrate effect is dominant during the beginning of the plating cycle, a relatively low current density, preferably about 5 mA/cm2, is applied during the initial plating. The low current density provides very conformal plating substantially uniformly over the plating surface, and the current density is gradually increased as the deposition thickness increases. Also, no current reversal for dissolution is applied during the initial stage of the plating process so that the metal seed layer is not at risk of being dissolved. However, if a current reversal is introduced for striking or nucleation purposes, the reverse current density is applied at a low magnitude to ensure that no appreciable metal seed layer is dissolved.
Optionally, a relaxation interval between the deposition interval and the dissolution interval allows recovery of depleted concentration profiles and also provides improved deposition properties. For example, a relaxation interval where no current/voltage is applied between the deposition interval and the dissolution interval, allows the electrolyte to return to optimal conditions for the processes.
Preferably, the vibration frequency, the pulse and/or periodic reverse plating, the auxiliary electrode current/voltage and the electrolyte flow are all synchronized for optimal deposition properties. One example of synchronization is to provide vibration only during the deposition interval so that the boundary diffusion layer is minimized during deposition and to eliminate vibration during the dissolution interval so that the dissolution proceeds under mass transport control.
To improve adhesion of the metal to the seed layer during plating, a very short, high current density strike is applied at the beginning of the plating cycle. To minimize bubble related defects, the strike must be short, and the current density must not exceed values at which hydrogen evolves. This current density, preferably between about 100 mA/cm2 to about 1000 mA/cm2, corresponds to an overpotential not exceeding −0.34 V (cathodic) versus for the reference electrode. A separate striking process using a different electrolyte may be required for adhesion of the metal plating material. Separate striking can be accomplished in a separate cell with different electrolytes or in the same cell by introducing and evacuating different electrolytes. The electrolytes used for separate striking is typically more dilute in metal concentration and may even be a cyanide based formulation.
The metal seed layer is susceptible to dissolution in the electrolyte by the exchange current density of the electrolyte (about 1 mA/cm2 for copper). For example, 1500 Å of copper can be dissolved in about 6 minutes in an electrolyte with no current applied. To minimize the risk of the seed layer being dissolved in the electrolyte, a voltage is applied to the substrate before the substrate is introduced to the electrolyte. Alternatively, the current is applied instantaneously as the substrate comes in contact with the electrolyte. When a deposition current is applied to the substrate plating surface, the metal seed layer is protected from dissolution in the electrolyte because the deposition current dominates over the equilibrium exchange current density of the electrolyte.
The invention also provides for in situ electroplanarization during periodic reverse plating. Preferably, both deposition and dissolution steps are incorporated during a single pulse or a sequence of rapid pulses such that at the end of the process the trenches, vias and other interconnect features are completely filled and planarized. The electrochemical planarization step comprises applying a high current density during dissolution. For example, a dissolution reverse current density of about 300 mA/cm2 is applied for about 45 seconds as an electrochemical planarization step that leads to a substantially flat surface with just a residual dimple of about 0.03 μm. This electrochemical planarization substantially reduces the need for chemical mechanical polishing (CMP) and may even eliminate the need for CMP in some applications.
An electrolyte having a high copper concentration (e.g., >0.5M and preferably between 0.8M to 1.2M) is beneficial to overcome mass transport limitations that are encountered with plating of sub-micron features. In particular, because sub-micron features with high aspect ratios typical allow only minimal or no electrolyte flow therein, the ionic transport relies solely on diffusion to deposit metal into these small features. A high copper concentration preferably about 0.8M or greater, in the electrolyte enhances the diffusion process and eliminates the mass transport limitations because the diffusion flux is proportional in magnitude to the bulk electrolyte concentration. A preferred metal concentration is between about 0.8 and about 1.2 M. Generally, the higher the metal concentration the better; however, one must be careful not to approach the solubility limit where the metal salt will precipitate.
The conventional copper plating electrolyte includes a high sulfuric acid concentration (about 1 M) to provide high conductivity to the electrolyte. The high conductivity is necessary to reduce the non-uniformity in the deposit thickness caused by the cell configuration of conventional copper electroplating cells. However, the present invention (including the cell configuration) provides a more uniform current distribution. In this situation a high acid concentration is detrimental to deposition uniformity because the resistive substrate effects are amplified by a highly conductive electrolyte. Furthermore, the dissolution step during periodic reverse cycle requires a relatively low electrolyte conductivity because a highly conductive electrolyte may promote non-uniformity as a result of the high reverse current density. Also, the presence of a supporting electrolyte, e.g. acid or base, will lower the ionic mass transport rates, which, as explained above, are essential for good quality plating. Also, a lower sulfuric acid concentration provides a higher copper sulfate concentration due to elimination of the common ion effect. Furthermore, particularly for the soluble copper anode, a lower acidic concentration minimizes harmful corrosion and material stability problems. Thus, the invention contemplates an electroplating solution having no acid or very low acid concentrations. Preferably, the sulfuric acid concentration is in the range of 0 (absence) to about 0.2M. Additionally, a pure or relatively pure copper anode can be used in this arrangement.
In addition to copper sulfate, the invention contemplates copper salts other than copper sulfate such as copper gluconate and copper sulfamate that offer high solubility and other benefits, as well as salts such as copper nitrate, copper phosphate, copper chloride and the like.
The invention also contemplates the addition of acids other than sulfuric acid into the electrolyte to provide for better complexation and/or solubility for the copper ions and the copper metal which results in improved deposition properties. These compounds include anthranilic acid, acetic acid, citric acid, lactic acid, sulfamic acid, ascorbic acid, glycolic acid, oxalic acid, benzenedisulfonic acid, tartaric acid and/or malic acid.
The invention also contemplates additives to produce asymmetrical anodic transfer coefficient (α) and cathodic transfer coefficient (β) to enhance filling of the high aspect ratio features during reverse plating cycle.
Ultra pure water can be introduced to the substrate plating surface to ensure complete wetting of the substrate plating surface which enhances the electroplating process into the small features. Steam can also be used to pre-wet the substrate plating surface.
Surfactants improve wetting by reducing surface tension of the solution. Surfactants contemplated by the present invention include: sodium xylene sulfonate, polyethers (polyethylene oxide), carbowax, sodium benzoate, ADMA8 amine, Adogen, Alamine, Amaizo, Brij, Crodesta, Dapral, Darnyl, didodecylmethyl propane sultaine, Dowex, Empol, Ethomeen, Ethomid, Enordet, Generol, Grilloten, Heloxy, hexadecyltrimethylammonium bromide, Hyamine, Hysoft, Igepal, Neodol, Octadecylbenzyl propane sultaine, Olcyl betaine, Peganate, Pluronic, Polystep, Span Surfynol, Tamol, Tergitol, Triton, Trilon, Trylox, Unithox, Varonic, Varamide, Zonyl, Benzylmethyl propane sultaine, alkyl or aryl betaine, alkyl or aryl sultaine.
Levellers improve deposition thickness uniformity. Brighteners improves the the reflectivity of the deposition surface by enhancing uniformity of the crystalline structure. Grain refiners produce smaller grains to be deposited. Levellers, brighteners and grain refiners can be specially formulated and optimized for the low acid, high copper electrolyte provided by the invention. In optimizing these compounds for use with the invention, the effects of the periodic reverse current need to also be considered. Levellers, brighteners and grain refiners contemplated by the present invention include:
inorganic minor components from: Salts of Se, As, In, Ga, Bi, Sb, TI, or Te; and/or
organic minor components selected from (singly or in combination): acetyl-coenzyme, aminothiols; acrylamine; azo dyes; alkane thiols, Alloxazine; 2-Aminopyrimidine; 2-Amino-1,3,4, thiadiazole; Amino methyl thiadiazole; 2-Aminothiadiazole; 3-amino 1,2,4, triazole; benzal acetone, Benzopurpurin; benzophnon, Behzotriazole, hydroxylbenzotriazole, Betizyldene acetone, Benzoic acid, Benzoil acetic acid ethyl ester, Boric acid, cacodylic acid, Corcumin Pyonin Y; Carminic Acid; Cinamic aldehyde, cocobetaine or decyl betaine, cetyl betaine, cysteine; DETAPAC; 2′,7′-dichlorofluorescein; dextrose, dicarboxilic amino acids; dipeptide diaminoacid (camsine=beta alanyl hystadine), 5-p-dimethylamine benzyldene Rhodamine, 5(p-Dimethylamino-benzylidene)-2-thio barbituric, dithizone, 4-(p-Ethoxyphnylazo)-m-phenylendi-amine, ethoxilated tetramethyl decynediol, ethoxilated quarternary amonium salts, ethyl benzoil acetate, ethoxylated beta-naphtol, EDTA, Evan Blue; di ethylene triamine penta acetic acid or salts, diethylenetriamine pentacetate, penta sodium salt, glucamine, glycerol compounds, di-glycine, d-glucamine, triglycine, glycogen, gluter aldehyde, glutamic acid, its salts and esters (MSG), sodium glucoheptonate, hydroxylbenzotriazole, hydroxysuccinimide, hydantoin, 4-(8-Hydroxy-5-quinolylazo)-1-naphtalenesulfonic acid, p-(p-hydroxyphenylazo) benzene sulfonic, insulin, hydroxybenzaldehyde, imidazoline; lignosulfonates; methionine; mercaptobenzi-imidazoles; Martius Yellow; 2-methyl-1-p-tolyltriazene, 3-(p-Nitrophenyl)-1-(p-phenylazophnyl)triazene; 4-(p-Nitrophenylazo) resorcinol, 4-(p-Nitrophenylazo)-1-naphthol, OCBA-orthochloro benzaldehyde, Phenyl propiolic acid, polyoxyethylene alcohols, quarternary amonium ethoxilated alcohols, and their fullyacid esters, polyethyleneimine, phosphalipides, sulfasalicilic acid, linear alkyl sulfonate, sulfacetamide, Solochrome cyanin; sugars; sorbitol, sodium glucoheptonate, sodium glycerophosphate, sodium mercaptobenzotriazole, tetrahydropyranyl amides, thiocarboxylic amides, thiocarbonyl-di-imidazole; thiocarbamid, thiohydantoin; thionine acetate, thiosalicilic acid, 2-thiolhistadine, thionine, thiodicarb, thioglycolic acid, thiodiglycols, thiodiglycolic acid, thiodipropionic acid, thioglycerol, dithiobenzoic acid, tetrabutylamonium, thiosulfone, thiosulfonic acid, thionicotineamide, thionyl chloride or bromide; thiourea; TIPA; tolyltriazole, triethanolamine; tri-benzylamine; 4,5,6, triaminopyrimidine; xylene cyanole.
While the foregoing is directed to the preferred embodiment of the present invention, other and further embodiments of the invention may be devised without departing from the basic scope thereof. The scope of the invention is determined by the claims which follow.
|Cited Patent||Filing date||Publication date||Applicant||Title|
|US2882209||May 20, 1957||Apr 14, 1959||Udylite Res Corp||Electrodeposition of copper from an acid bath|
|US3649509 *||Jul 8, 1969||Mar 14, 1972||Buckbee Mears Co||Electrodeposition systems|
|US3727620 *||Mar 18, 1970||Apr 17, 1973||Fluoroware Of California Inc||Rinsing and drying device|
|US3770598 *||Jan 21, 1972||Nov 6, 1973||Oxy Metal Finishing Corp||Electrodeposition of copper from acid baths|
|US4027686 *||Jan 2, 1973||Jun 7, 1977||Texas Instruments Incorporated||Method and apparatus for cleaning the surface of a semiconductor slice with a liquid spray of de-ionized water|
|US4092176 *||Dec 7, 1976||May 30, 1978||Nippon Electric Co., Ltd.||Apparatus for washing semiconductor wafers|
|US4110176 *||May 4, 1977||Aug 29, 1978||Oxy Metal Industries Corporation||Electrodeposition of copper|
|US4113492 *||Apr 8, 1977||Sep 12, 1978||Fuji Photo Film Co., Ltd.||Spin coating process|
|US4120711||Sep 30, 1977||Oct 17, 1978||Universal Water Systems, Inc.||Process for sealing end caps to filter cartridges|
|US4120771||Sep 7, 1977||Oct 17, 1978||Fabrication Belge de Disques "Fabeldis"||Device for manufacturing substantially flat dies|
|US4304641||Nov 24, 1980||Dec 8, 1981||International Business Machines Corporation||Rotary electroplating cell with controlled current distribution|
|US4315059 *||Jul 18, 1980||Feb 9, 1982||The United States Of America As Represented By The United States Department Of Energy||Molten salt lithium cells|
|US4326940 *||May 21, 1979||Apr 27, 1982||Rohco Incorporated||Automatic analyzer and control system for electroplating baths|
|US4336114 *||Mar 26, 1981||Jun 22, 1982||Hooker Chemicals & Plastics Corp.||Electrodeposition of bright copper|
|US4376685 *||Jun 24, 1981||Mar 15, 1983||M&T Chemicals Inc.||Acid copper electroplating baths containing brightening and leveling additives|
|US4405416 *||Sep 15, 1981||Sep 20, 1983||Raistrick Ian D||Molten salt lithium cells|
|US4428815 *||Apr 28, 1983||Jan 31, 1984||Western Electric Co., Inc.||Vacuum-type article holder and methods of supportively retaining articles|
|US4435266 *||Sep 30, 1982||Mar 6, 1984||Emi Limited||Electroplating arrangements|
|US4489740 *||Dec 27, 1982||Dec 25, 1984||General Signal Corporation||Disc cleaning machine|
|US4510176 *||Sep 26, 1983||Apr 9, 1985||At&T Bell Laboratories||Removal of coating from periphery of a semiconductor wafer|
|US4518678 *||Dec 16, 1983||May 21, 1985||Advanced Micro Devices, Inc.||Selective removal of coating material on a coated substrate|
|US4519846 *||Mar 8, 1984||May 28, 1985||Seiichiro Aigo||Process for washing and drying a semiconductor element|
|US4693805 *||Feb 14, 1986||Sep 15, 1987||Boe Limited||Method and apparatus for sputtering a dielectric target or for reactive sputtering|
|US4732785 *||Sep 26, 1986||Mar 22, 1988||Motorola, Inc.||Edge bead removal process for spin on films|
|US4789445 *||Nov 19, 1986||Dec 6, 1988||Asarco Incorporated||Method for the electrodeposition of metals|
|US5039381 *||May 25, 1989||Aug 13, 1991||Mullarkey Edward J||Method of electroplating a precious metal on a semiconductor device, integrated circuit or the like|
|US5055425 *||Jun 1, 1989||Oct 8, 1991||Hewlett-Packard Company||Stacked solid via formation in integrated circuit systems|
|US5092975 *||Jun 15, 1989||Mar 3, 1992||Yamaha Corporation||Metal plating apparatus|
|US5155336 *||Oct 24, 1991||Oct 13, 1992||Applied Materials, Inc.||Rapid thermal heating apparatus and method|
|US5162260 *||Jan 7, 1991||Nov 10, 1992||Hewlett-Packard Company||Stacked solid via formation in integrated circuit systems|
|US5168887||May 18, 1990||Dec 8, 1992||Semitool, Inc.||Single wafer processor apparatus|
|US5222310 *||Jan 11, 1991||Jun 29, 1993||Semitool, Inc.||Single wafer processor with a frame|
|US5224504 *||Jul 30, 1992||Jul 6, 1993||Semitool, Inc.||Single wafer processor|
|US5230743 *||Jul 30, 1992||Jul 27, 1993||Semitool, Inc.||Method for single wafer processing in which a semiconductor wafer is contacted with a fluid|
|US5252807 *||Oct 23, 1991||Oct 12, 1993||George Chizinsky||Heated plate rapid thermal processor|
|US5256274 *||Nov 22, 1991||Oct 26, 1993||Jaime Poris||Selective metal electrodeposition process|
|US5259407 *||Jun 14, 1991||Nov 9, 1993||Matrix Inc.||Surface treatment method and apparatus for a semiconductor wafer|
|US5290361 *||Jan 23, 1992||Mar 1, 1994||Wako Pure Chemical Industries, Ltd.||Surface treating cleaning method|
|US5302256||Jun 15, 1992||Apr 12, 1994||Learonal Japan Inc.||Immersion tin/lead alloy plating bath|
|US5316974 *||Apr 30, 1990||May 31, 1994||Texas Instruments Incorporated||Integrated circuit copper metallization process using a lift-off seed layer and a thick-plated conductor layer|
|US5328589 *||Dec 23, 1992||Jul 12, 1994||Enthone-Omi, Inc.||Functional fluid additives for acid copper electroplating baths|
|US5349978 *||Jun 4, 1993||Sep 27, 1994||Tokyo Ohka Kogyo Co., Ltd.||Cleaning device for cleaning planar workpiece|
|US5368711 *||Apr 29, 1993||Nov 29, 1994||Poris; Jaime||Selective metal electrodeposition process and apparatus|
|US5377708 *||Apr 26, 1993||Jan 3, 1995||Semitool, Inc.||Multi-station semiconductor processor with volatilization|
|US5429733 *||May 4, 1993||Jul 4, 1995||Electroplating Engineers Of Japan, Ltd.||Plating device for wafer|
|US5447615 *||Jun 22, 1994||Sep 5, 1995||Electroplating Engineers Of Japan Limited||Plating device for wafer|
|US5512163||Apr 1, 1994||Apr 30, 1996||Motorola, Inc.||Method for forming a planarization etch stop|
|US5516412 *||May 16, 1995||May 14, 1996||International Business Machines Corporation||Vertical paddle plating cell|
|US5544421||Apr 28, 1994||Aug 13, 1996||Semitool, Inc.||Semiconductor wafer processing system|
|US5605615||Dec 5, 1994||Feb 25, 1997||Motorola, Inc.||Method and apparatus for plating metals|
|US5605866||Nov 30, 1995||Feb 25, 1997||Varian Associates, Inc.||Clamp with wafer release for semiconductor wafer processing equipment|
|US5608943 *||Aug 22, 1994||Mar 11, 1997||Tokyo Electron Limited||Apparatus for removing process liquid|
|US5620581||Nov 29, 1995||Apr 15, 1997||Aiwa Research And Development, Inc.||Apparatus for electroplating metal films including a cathode ring, insulator ring and thief ring|
|US5625170 *||Jan 18, 1994||Apr 29, 1997||Nanometrics Incorporated||Precision weighing to monitor the thickness and uniformity of deposited or etched thin film|
|US5651865 *||Jun 17, 1994||Jul 29, 1997||Eni||Preferential sputtering of insulators from conductive targets|
|US5664337||Jul 15, 1996||Sep 9, 1997||Semitool, Inc.||Automated semiconductor processing systems|
|US5678320||Apr 3, 1995||Oct 21, 1997||Semitool, Inc.||Semiconductor processing systems|
|US5705223 *||Dec 5, 1995||Jan 6, 1998||International Business Machine Corp.||Method and apparatus for coating a semiconductor wafer|
|US5718813 *||Apr 2, 1993||Feb 17, 1998||Advanced Energy Industries, Inc.||Enhanced reactive DC sputtering system|
|US5723028 *||Oct 19, 1994||Mar 3, 1998||Poris; Jaime||Electrodeposition apparatus with virtual anode|
|US5744019||Jan 31, 1997||Apr 28, 1998||Aiwa Research And Development, Inc.||Method for electroplating metal films including use a cathode ring insulator ring and thief ring|
|US5762751||Aug 17, 1995||Jun 9, 1998||Semitool, Inc.||Semiconductor processor with wafer face protection|
|US5788454||Mar 29, 1996||Aug 4, 1998||Semitool, Inc.||Semiconductor wafer processing system|
|US5882168||Jun 24, 1997||Mar 16, 1999||Semitool, Inc.||Semiconductor processing systems|
|US5972192||Jul 23, 1997||Oct 26, 1999||Advanced Micro Devices, Inc.||Pulse electroplating copper or copper alloys|
|US5980706||Jul 15, 1996||Nov 9, 1999||Semitool, Inc.||Electrode semiconductor workpiece holder|
|US5985126||Sep 30, 1997||Nov 16, 1999||Semitool, Inc.||Semiconductor plating system workpiece support having workpiece engaging electrodes with distal contact part and dielectric cover|
|US6001234||Sep 30, 1997||Dec 14, 1999||Semitool, Inc.||Methods for plating semiconductor workpieces using a workpiece-engaging electrode assembly with sealing boot|
|US6004440||Sep 18, 1997||Dec 21, 1999||Semitool, Inc.||Cathode current control system for a wafer electroplating apparatus|
|US6004828||Sep 30, 1997||Dec 21, 1999||Semitool, Inc,||Semiconductor processing workpiece support with sensory subsystem for detection of wafers or other semiconductor workpieces|
|US6024857||Oct 8, 1997||Feb 15, 2000||Novellus Systems, Inc.||Electroplating additive for filling sub-micron features|
|US6027631||Nov 13, 1997||Feb 22, 2000||Novellus Systems, Inc.||Electroplating system with shields for varying thickness profile of deposited layer|
|US6074544||Jul 22, 1998||Jun 13, 2000||Novellus Systems, Inc.||Method of electroplating semiconductor wafer using variable currents and mass transfer to obtain uniform plated layer|
|US6090711||Sep 30, 1997||Jul 18, 2000||Semitool, Inc.||Methods for controlling semiconductor workpiece surface exposure to processing liquids|
|US6091498||Dec 15, 1997||Jul 18, 2000||Semitool, Inc.||Semiconductor processing apparatus having lift and tilt mechanism|
|US6099712||Sep 30, 1997||Aug 8, 2000||Semitool, Inc.||Semiconductor plating bowl and method using anode shield|
|US6110346||Sep 9, 1999||Aug 29, 2000||Novellus Systems, Inc.||Method of electroplating semicoductor wafer using variable currents and mass transfer to obtain uniform plated layer|
|US6126798||Nov 13, 1997||Oct 3, 2000||Novellus Systems, Inc.||Electroplating anode including membrane partition system and method of preventing passivation of same|
|US6132857||Dec 18, 1998||Oct 17, 2000||Societe Nationale D'etude Et De Construction De Moterus D'aviation "Snecma"||Hybrid component with high strength/mass ratio and method of manufacturing said component|
|US6139703||Dec 20, 1999||Oct 31, 2000||Semitool, Inc.||Cathode current control system for a wafer electroplating apparatus|
|US6139712||Dec 14, 1999||Oct 31, 2000||Novellus Systems, Inc.||Method of depositing metal layer|
|US6156167||Nov 13, 1997||Dec 5, 2000||Novellus Systems, Inc.||Clamshell apparatus for electrochemically treating semiconductor wafers|
|US6159354||Nov 13, 1997||Dec 12, 2000||Novellus Systems, Inc.||Electric potential shaping method for electroplating|
|US6162344||Sep 9, 1999||Dec 19, 2000||Novellus Systems, Inc.||Method of electroplating semiconductor wafer using variable currents and mass transfer to obtain uniform plated layer|
|US6168693||Jan 22, 1998||Jan 2, 2001||International Business Machines Corporation||Apparatus for controlling the uniformity of an electroplated workpiece|
|US6174425||May 14, 1997||Jan 16, 2001||Motorola, Inc.||Process for depositing a layer of material over a substrate|
|US6179983||Nov 13, 1997||Jan 30, 2001||Novellus Systems, Inc.||Method and apparatus for treating surface including virtual anode|
|US6197181||Mar 20, 1998||Mar 6, 2001||Semitool, Inc.||Apparatus and method for electrolytically depositing a metal on a microelectronic workpiece|
|US6203582||Jul 15, 1996||Mar 20, 2001||Semitool, Inc.||Modular semiconductor workpiece processing tool|
|US6228231||Sep 27, 1999||May 8, 2001||International Business Machines Corporation||Electroplating workpiece fixture having liquid gap spacer|
|US6270647||Aug 31, 1999||Aug 7, 2001||Semitool, Inc.||Electroplating system having auxiliary electrode exterior to main reactor chamber for contact cleaning operations|
|US6280581||Dec 29, 1998||Aug 28, 2001||David Cheng||Method and apparatus for electroplating films on semiconductor wafers|
|US6322674||Nov 16, 1999||Nov 27, 2001||Semitool, Inc.||Cathode current control system for a wafer electroplating apparatus|
|US6322678||Jul 11, 1998||Nov 27, 2001||Semitool, Inc.||Electroplating reactor including back-side electrical contact apparatus|
|US6343793||Dec 2, 1999||Feb 5, 2002||Novellus Systems, Inc.||Dual channel rotary union|
|US6344125||Apr 6, 2000||Feb 5, 2002||International Business Machines Corporation||Pattern-sensitive electrolytic metal plating|
|US6391166||Jan 15, 1999||May 21, 2002||Acm Research, Inc.||Plating apparatus and method|
|US6436249||May 17, 2000||Aug 20, 2002||Novellus Systems, Inc.||Clamshell apparatus for electrochemically treating semiconductor wafers|
|US6444101||Nov 12, 1999||Sep 3, 2002||Applied Materials, Inc.||Conductive biasing member for metal layering|
|US6454926||Sep 30, 1997||Sep 24, 2002||Semitool Inc.||Semiconductor plating system workpiece support having workpiece-engaging electrode with submerged conductive current transfer areas|
|US6500316||Nov 17, 2000||Dec 31, 2002||International Business Machines Corporation||Apparatus for rotary cathode electroplating with wireless power transfer|
|US6500317||Dec 16, 1998||Dec 31, 2002||Ebara Corporation||Plating apparatus for detecting the conductivity between plating contacts on a substrate|
|US6517689||Jul 9, 1999||Feb 11, 2003||Ebara Corporation||Plating device|
|US6527926||Mar 13, 2001||Mar 4, 2003||Semitool, Inc.||Electroplating reactor including back-side electrical contact apparatus|
|US6547937||Jan 3, 2000||Apr 15, 2003||Semitool, Inc.||Microelectronic workpiece processing tool including a processing reactor having a paddle assembly for agitation of a processing fluid proximate to the workpiece|
|US6551483||May 10, 2001||Apr 22, 2003||Novellus Systems, Inc.||Method for potential controlled electroplating of fine patterns on semiconductor wafers|
|US6562204||May 10, 2001||May 13, 2003||Novellus Systems, Inc.||Apparatus for potential controlled electroplating of fine patterns on semiconductor wafers|
|US6589401||Nov 22, 2000||Jul 8, 2003||Novellus Systems, Inc.||Apparatus for electroplating copper onto semiconductor wafer|
|US6627051||Jul 20, 2001||Sep 30, 2003||Semitool, Inc.||Cathode current control system for a wafer electroplating apparatus|
|US6627052||Dec 12, 2000||Sep 30, 2003||International Business Machines Corporation||Electroplating apparatus with vertical electrical contact|
|US6693417||May 3, 2002||Feb 17, 2004||Commonwealth Of Australia||Micro-electronic bond degradation sensor and method of manufacture|
|US6761812||Nov 25, 2002||Jul 13, 2004||Advanced Micro Devices, Inc.||Apparatus and method for electrochemical metal deposition|
|US6783657||Aug 29, 2002||Aug 31, 2004||Micron Technology, Inc.||Systems and methods for the electrolytic removal of metals from substrates|
|US6802946||May 15, 2001||Oct 12, 2004||Nutool Inc.||Apparatus for controlling thickness uniformity of electroplated and electroetched layers|
|US6843894||Sep 22, 2003||Jan 18, 2005||Semitool, Inc.||Cathode current control system for a wafer electroplating apparatus|
|US6849167||Jan 7, 2003||Feb 1, 2005||Semitool, Inc.||Electroplating reactor including back-side electrical contact apparatus|
|US6908540||Jul 13, 2001||Jun 21, 2005||Applied Materials, Inc.||Method and apparatus for encapsulation of an edge of a substrate during an electro-chemical deposition process|
|US6921468||Jul 19, 2001||Jul 26, 2005||Semitool, Inc.||Electroplating system having auxiliary electrode exterior to main reactor chamber for contact cleaning operations|
|US7025862||Oct 22, 2002||Apr 11, 2006||Applied Materials||Plating uniformity control by contact ring shaping|
|US7087144||Jan 31, 2003||Aug 8, 2006||Applied Materials, Inc.||Contact ring with embedded flexible contacts|
|US20020022363 *||Feb 4, 1998||Feb 21, 2002||Thomas L. Ritzdorf||Method for filling recessed micro-structures with metallization in the production of a microelectronic device|
|US20050051436||Jul 1, 2004||Mar 10, 2005||Semitool, Inc.||Method of submicron metallization using electrochemical deposition of recesses including a first deposition at a first current density and a second deposition at an increased current density|
|JPH0617291A *||Title not available|
|JPH0714811A||Title not available|
|JPH04131395A *||Title not available|
|JPH04280993A *||Title not available|
|JPS58182823A *||Title not available|
|JPS63118093A *||Title not available|
|WO1997012079A1 *||Sep 19, 1996||Apr 3, 1997||Intel Corporation||Flexible continuous cathode contact circuit for electrolytic plating of c4, tab microbumps, and ultra large scale interconnects|
|WO1999016936A1||Jan 6, 1998||Apr 8, 1999||Semitool, Inc.||Electroplating system having auxiliary electrode exterior to main reactor chamber for contact cleaning operations|
|WO1999025902A1 *||Oct 26, 1998||May 27, 1999||Novellus Systems, Inc.||Membrane partition system for plating of wafers|
|WO1999025903A1 *||Oct 26, 1998||May 27, 1999||Novellus Systems, Inc.||Virtual anode design for use in wafer plating|
|WO1999025904A1 *||Oct 26, 1998||May 27, 1999||Novellus Systems, Inc.||Electric potential shaping apparatus for holding a semiconductor wafer during electroplating|
|WO1999025905A1 *||Oct 26, 1998||May 27, 1999||Novellus Systems, Inc.||Clamshell apparatus for electrochemically treating semiconductor wafers|
|WO1999026275A2 *||Oct 26, 1998||May 27, 1999||Novellus Systems, Inc.||Electroplating system with shields for varying thickness profile of deposited layer|
|WO2000032835A2||Nov 29, 1999||Jun 8, 2000||Applied Materials, Inc.||Electro-chemical deposition system|
|WO2002004715A2||Jun 28, 2001||Jan 17, 2002||Applied Materials, Inc.||Deposition uniformity control for electroplating apparatus, and associated method|
|1||*||Kenneth E. Pitney, "Ney Contact Manual," Electrical Contacts for Low Energy Uses, 1973, no month available.|
|2||*||Laurell Technologies Corporation, "Two control configurations available-see WS 400 or WS-400 Lite." Oct. 19, 1998, 6 pages.|
|3||*||Lucio Colombo, "Wafer Back Surface Film Removal," Central R&D, SGS-Thompson, Microelectronics, Agrate, Italy, 6 pages, no month available.|
|4||*||PCT International Search Report dated Feb. 7, 2000.|
|5||PCT International Search Report dated Jul. 5, 2005, for PCT/US01/20622.|
|6||PCT International Search Report dated Jul. 5, 2005, for PCT/US01/31943.|
|7||PCT Notification of Transmittal of International Preliminary Examination Report dated Apr. 13, 2007 for PCT/US01/31943.|
|8||*||PCT Written Opinion citing additional references for PCT/US99/28159, dated Dec. 8, 2000.|
|9||PCT Written Opinion for International Application No. PCT/US01/20624 dated Aug. 8, 2006.|
|10||*||Peter Singer, "Tantalum, Copper and Damascene: The Future of Interconnects," Semiconductor International, Jun. 1998, pages cover, 91-91, 94, 96 & 98.|
|11||*||Peter Singer, "Wafer Processing," Semiconductor International, Jun., 1998, p. 70.|
|12||*||Semitool, Inc., "Metallization & Interconnect," 1998, 4 pages, no month available.|
|13||*||Verteq Online, "Products Overview," 1996-1998, 5 pages, no month available.|
|Citing Patent||Filing date||Publication date||Applicant||Title|
|US8221600 *||Sep 23, 2010||Jul 17, 2012||Sunpower Corporation||Sealed substrate carrier for electroplating|
|US8221601 *||Sep 23, 2010||Jul 17, 2012||Sunpower Corporation||Maintainable substrate carrier for electroplating|
|US8317987||Sep 23, 2010||Nov 27, 2012||Sunpower Corporation||Non-permeable substrate carrier for electroplating|
|US8460814||Jul 29, 2009||Jun 11, 2013||The Invention Science Fund I, Llc||Fluid-surfaced electrode|
|US8784618 *||Aug 19, 2010||Jul 22, 2014||International Business Machines Corporation||Working electrode design for electrochemical processing of electronic components|
|US8865361||Feb 16, 2010||Oct 21, 2014||The Invention Science Fund I, Llc||Instrumented fluid-surfaced electrode|
|US8889312||Jun 17, 2010||Nov 18, 2014||The Invention Science Fund I, Llc||Instrumented fluid-surfaced electrode|
|US8926820||Sep 12, 2012||Jan 6, 2015||International Business Machines Corporation||Working electrode design for electrochemical processing of electronic components|
|US8968903||Oct 20, 2009||Mar 3, 2015||The Invention Science Fund I, Llc||Fluid-surfaced electrode|
|US8974939||Oct 20, 2009||Mar 10, 2015||The Invention Science Fund I, Llc||Fluid-surfaced electrode|
|US9207515||Mar 15, 2013||Dec 8, 2015||Ashwin-Ushas Corporation, Inc.||Variable-emittance electrochromic devices and methods of preparing the same|
|US9274395||Nov 14, 2012||Mar 1, 2016||Ashwin-Ushas Corporation, Inc.||Complimentary polymer electrochromic device|
|US9482880||Sep 15, 2015||Nov 1, 2016||Ashwin-Ushas Corporation, Inc.||Electrochromic eyewear|
|US20050139477 *||Feb 17, 2003||Jun 30, 2005||Atotech Deutschland Gmbh||Method for storage of a metal ion supply source in a plating equipment|
|US20070202699 *||Feb 26, 2007||Aug 30, 2007||Kabushiki Kaisha Toshiba||Electronic component fabrication method|
|US20110027621 *||Jun 17, 2010||Feb 3, 2011||Searete Llc, A Limited Liability Corporation Of The State Of Delaware||Instrumented fluid-surfaced electrode|
|US20110027624 *||Jul 29, 2009||Feb 3, 2011||Searete Llc, A Limited Liability Corporation Of The State Of Delaware||Fluid-surfaced electrode|
|US20110027627 *||Oct 20, 2009||Feb 3, 2011||Searete Llc, A Limited Liability Corporation Of The State Of Delaware||Fluid-surfaced electrode|
|US20110027628 *||Feb 16, 2010||Feb 3, 2011||Searete Llc||Instrumented fluid-surfaced electrode|
|US20110027633 *||Jun 17, 2010||Feb 3, 2011||Searete Llc, A Limited Liability Corporation Of The State Of Delaware||Instrumented fluid-surfaced electrode|
|US20110027637 *||Oct 20, 2009||Feb 3, 2011||Searete Llc, A Limited Liability Corporation Of The State Of Delaware||Fluid-surfaced electrode|
|US20110027638 *||Oct 20, 2009||Feb 3, 2011||Searete Llc, A Limited Liability Corporation Of The State Of Delaware||Fluid-surfaced electrode|
|US20110027639 *||Oct 20, 2009||Feb 3, 2011||Searete Llc, A Limited Liability Corporation Of The State Of Delware||Fluid-surfaced electrode|
|US20120043216 *||Aug 19, 2010||Feb 23, 2012||International Business Machines Corporation||Working electrode design for electrochemical processing of electronic components|
|US20120073975 *||Sep 23, 2010||Mar 29, 2012||Ganti Kalyana Bhargava||Sealed substrate carrier for electroplating|
|US20120073976 *||Sep 23, 2010||Mar 29, 2012||Chen-An Chen||Maintainable substrate carrier for electroplating|
|USRE46088 *||May 5, 2015||Aug 2, 2016||Sunpower Corporation||Maintainable substrate carrier for electroplating|
|CN102714290A *||Jul 26, 2010||Oct 3, 2012||希尔莱特有限责任公司||Instrumented fluid-surfaced electrode|
|CN102714290B *||Jul 26, 2010||Jun 17, 2015||发明科学基金I有限责任公司||Instrumented fluid-surfaced electrode|
|WO2011014243A1 *||Jul 26, 2010||Feb 3, 2011||Searete, Llc||Instrumented fluid-surfaced electrode|
|WO2012039817A2 *||Jul 11, 2011||Mar 29, 2012||Sunpower Corporation||Sealed substrate carrier for electroplating|
|WO2012039817A3 *||Jul 11, 2011||Mar 20, 2014||Sunpower Corporation||Sealed substrate carrier for electroplating|
|U.S. Classification||205/96, 204/297.03, 204/297.01, 204/272, 205/149, 204/230.7, 204/260, 204/275.1, 205/157, 204/273, 204/230.2, 205/153, 205/103, 204/263, 205/128, 204/261, 205/123|
|International Classification||C25D3/38, C25D17/00, C25D5/00, C25D7/12|
|Cooperative Classification||C25D7/123, C25D3/38, C25D17/001|
|European Classification||C25D3/38, C25D7/12|
|Nov 11, 2008||CC||Certificate of correction|
|Jan 26, 2009||REMI||Maintenance fee reminder mailed|
|Jul 19, 2009||LAPS||Lapse for failure to pay maintenance fees|