|Publication number||USRE41616 E1|
|Application number||US 10/738,702|
|Publication date||Aug 31, 2010|
|Filing date||Dec 17, 2003|
|Priority date||Jul 11, 2001|
|Also published as||CN1547664A, EP1409997A1, US6514617, US20030021998, WO2003006965A1|
|Publication number||10738702, 738702, US RE41616 E1, US RE41616E1, US-E1-RE41616, USRE41616 E1, USRE41616E1|
|Inventors||Steven Frederick Hubbard, Radislav Alexandrovich Potyrailo, Philippe Schottland, Verghese Thomas|
|Original Assignee||Sabic Innovative Plastics Ip B.V.|
|Export Citation||BiBTeX, EndNote, RefMan|
|Patent Citations (30), Referenced by (1), Classifications (19), Legal Events (5)|
|External Links: USPTO, USPTO Assignment, Espacenet|
The present invention is related to identification of polymer compositions. More particularly, the present invention is related to non-destructive identification of polymer compositions via spectroscopic tags.
Automated identification of plastic compositions is desirable for a variety of applications, such as recycling, tracking a manufacturing source, anti-piracy protection, and the like. Historically, X-rays and infrared spectroscopy have been used to identify plastic materials. Tagging materials such as ultraviolet and near-infrared fluorescent dyes have also been used for the identification of plastic compositions.
In Cyr et al., U.S. Pat. No. 6,099,930, tagging materials are placed in materials such as digital compact discs. A near-infrared fluorophore is incorporated into the compact disc via coating, admixing, blending, or copolymerization. Fluorescence is detectable when the fluorophore is exposed to electromagnetic radiation having a wavelength ranging from 670 nanometers to 1100 nanometers.
Unfortunately, the use of fluorophores may be problematic under certain conditions. For instance, if multiple fluorophores are used, there may be an inaccuracy in the signals that are produced if the dye ages or leaches under normal use conditions, which can include, for example, exposure to ultraviolet light and high ambient temperatures. Additionally, additives used in the polymer can alter the ratio of fluoroescence intensities.
Due to the multitude of articles made by polymeric materials, there is a growing need to develop methods and tagging materials that a manufacturer can use to identify a product. Thus, methods and materials are constantly being sought which are effective, accurate, and easily detected.
The present invention provides a method for identifying a polymer, comprising providing in the polymer at least one tagging material wherein the tagging material comprises at least one organic fluorophore dye, or at least one inorganic fluorophore, or at least one organometallic fluorophore, or at least one semi-conducting luminescent nanoparticle, or combination thereof, wherein the tagging material has a temperature stability of at least 350° C. and is present in a sufficient quantity such that the tagging material is detectible via a spectrofluorometer at an excitation wavelength in a range between about 100 nanometers and about 1100 nanometers.
In a further embodiment of the present invention, a polymer is provided comprising a tagging material wherein the tagging material comprises at least one organic fluorophore dye, or at least one inorganic fluorophore, or at least one organometallic fluorophore, or at least one semi-conducting luminescent nanoparticle, or combination thereof, wherein the tagging material has a temperature stability of at least 350° C. and is present in a sufficient quantity such that the tagging material is detectible via a spectrofluorometer at an excitation wavelength in a range between about 100 nanometers and about 1100 nanometers.
In yet a further embodiment of the present invention, an article is provided comprising a polymer wherein the polymer comprises at least one tagging material, wherein the tagging material comprises at least one organic fluorophore dye, or at least one inorganic fluorophore, or at least one organometallic fluorophore, or at least one semi-conducting luminescent nanoparticle, or combinations thereof, wherein the tagging material has a temperature stability of at least 350° C. and is present in a sufficient quantity such that the tagging material is detectible via a spectrofluorometer at an excitation wavelength in a range between about 100 nanometers and about 1100 nanometers.
The present invention relates to spectroscopic tags incorporated into polymers. Spectroscopic tags include at least one organic fluorophore, or at least one inorganic fluorophore, or at least one organometallic fluorophore, or at least one semi-conducting luminescent nanoparticle, or combinations thereof. Spectroscopic tags make it possible to determine the thermal history and degradation of a polymer. In addition, the tagging materials used in the present invention are insensitive to polymer additives and to chemical and physical aging of the polymer.
These tagging materials are selected from classes of dyes that exhibit high robustness against ambient environmental conditions and temperature stability of at least about 350° C., preferably at least about 375° C., and more preferably at least about 400° C. Typically, the tagging materials have a temperature stability for a time period less than about 10 minutes and preferably, less than about 1 minute, and more preferably, less than 20 seconds.
The excitation range of these tagging materials is typically in a range between about 100 nanometers and about 1100 nanometers, and more typically in a range between about 200 nanometers and about 1000 nanometers, and most typically in a range between about 250 nanometers and about 950 nanometers. The emission range of these tagging materials is typically in a range between about 250 nanometers and about 250 nanometers.
The tags of the present invention include organic, inorganic, or organometallic fluorophores. Exemplary fluorophores include, but are not limited to, known dyes such as polyazaindacenes or coumarins, including those set forth in U.S. Pat. No. 5,573,909. Other suitable families of dyes include lanthanide complexes, hydrocarbon and substituted hydrocarbon dyes; polycyclic aromatic hydrocarbons; scintillation dyes (preferably oxazoles and oxidazoles); aryl- and heteroaryl-substituted polyolefins (C2-C8 olefin portion); carbocyanine dyes; phthalocyanine dyes and pigments; oxazine dyes; carbostyryl dyes; porphyrin dyes; acridine dyes; anthraquinone dyes; arylmethane dyes; azo dyes; diazonium dyes; nitro dyes; quinone imine dyes; tetrazolium dyes; thiazole dyes; perylene dyes, perinone dyes, bis-benzoxazolylthiophene (BBOT), and xanthene dyes. Fluorophores of the present invention also include anti-stokes shift dyes which absorb in the near infrared wavelength and emit in the visible wavelength.
The following is a partial list of commercially available, suitable luminescent dyes.
The tags of the present invention may also include semi-conducting luminescent nanoparticles of sizes in a range between about 1 nanometer and about 50 nanometers. Exemplary semi-conducting luminescent nanoparticles include, but are not limited to, CdS, ZnS, Cd3P2, Pbs, or combinations thereof. Semi-conducting luminescent nanoparticles also include rare earth aluminates including, but not limited to, strontium aluminates doped with Europium and Dysprosium.
In a preferred embodiment, tagging materials such as perylenes such as Anthra[2,1,9-def:6,5,10-d′e′f′] diisoquinoline-1,3,8,10(2H,9H)-tetrone, 2,9-bis[2,6-bis(1-methylethyl)phenyl]-5,6,12,13-tetraphenoxy are utilized.
Concentration of the tagging material depends on the quantum efficiency of the tagging material, excitation and emission wavelengths, and employed detection techniques, and can typically range from about 10−18 percent by weight and about 2 percent by weight of the total polymer, more typically range from about 10−15 percent by weight and about 0.5 percent by weight of the total polymer, and most typically range from about 10−12 percent by weight and about 0.05 percent by weight of the total polymer.
Some possible examples of polymers which can be utilized for the present invention include, but are not limited to, amorphous, crystalline and semi-crystalline thermoplastic materials: polyvinyl chloride, polyolefins (including, but not limited to, linear and cyclic polyolefins and including polyethylene, chlorinated polyethylene, polypropylene, and the like), polyesters (including, but not limited to, polyethylene terephthalate, polybutylene terephthalate, polycyclohexylmethylene terephthalate, and the like), polyamides, polysulfones (including, but not limited to, hydrogenated polysulfones, and the like), polyimides, polyether imides, polyether sulfones, polyphenylene sulfides, polyether ketones, polyether ether ketones, ABS resins, polystyrenes (including, but not limited to, hydrogenated polystyrenes, syndiotactic and atactic polystyrenes, polycyclohexyl ethylene, styrene-co-acrylonitrile, styrene-co-maleic anhydride, and the like), polybutadiene, polyacylates (including, but not limited to, polymethylmethacrylate, methyl methacrylate-polyimide copolymers, and the like), polyacrylonitrile, polyacetals, polycarbonates, polyphenylene ethers (including but not limited to, those derived from 2,6-dimethylphenol and copolymers with 2,3,6-trimethylphenol, and the like), ethylene-vinyl acetate copolymers, polyvinyl acetate, liquid crystal polymers, ethylene-tetrafluoroethylene copolymer, aromatic polyesters, polyvinyl fluoride, polyvinylidene fluoride, polyvinylidene chloride, Teflons, as well as thermosetting resins such as epoxy, phenolic, alkyds, polyester, polyimide, polyurethane, mineral fluid silicone, bis-maleimides, cyanate esters, vinyl, and benzocyclobutene resins, in addition to blends, copolymers, mixtures, reaction products and composites comprising at least one of the foregoing plastics.
As used herein, the terms “polycarbonate”, “polycarbonate composition”, and “composition comprising aromatic carbonate chain units” includes compositions having structural units of the formula (I):
in which at least about 60 percent of the total number of R1 groups are aromatic organic radicals and the balance thereof are aliphatic, alicyclic, or aromatic radicals. Preferably, R1 is an aromatic organic radical and, more preferably, a radical of the formula (II):
wherein each of A1 and A2 is a monocyclic divalent aryl radical and Y3 is a bridging radical having one or two atoms which separate A1 from A2. In an exemplary embodiment, one atom separates A1 from A2. Illustrative, non-limiting examples of radicals of this type are —O—, —S—, —S(O)—, —S(O2)—, —C(O)—, methylene, cyclohexylmethylene, 2-[2,2,1]-bicycloheptylidene, ethylidene, isopropylidene, neopentylidene, cyclohexylidene, cyclopentadecylidene, cyclododecylidene, and adamantylidene. The bridging radical Y1 can be a hydrocarbon group or a saturated hydrocarbon group such as methylene, cyclohexylidene or isopropylidene.
Polycarbonates can be produced by the interfacial reaction of dihydroxy compounds in which only one atom separates A1 and A2. As used herein, the term “dihydroxy compound” includes, for example, bisphenol compounds having general formula (III) as follows:
wherein Ra and Rb each represent a halogen atom or a monovalent hydrocarbon group and may be the same or different; p and q are each independently integers from 0 to 4; and Xa represents one of the groups of formula (IV):
wherein Rc and Rd each independently represent a hydrogen atom or a monovalent linear or cyclic hydrocarbon group and Rd is a divalent hydrocarbon group.
Some illustrative, non-limiting examples of suuitable dihydroxy compounds include dihydric phenols and the dihydroxy-substituted aromatic hydrocarbons disclosed by name or formula (generic or specific) in U.S. Pat. No. 4,217,438, which is incorporated herein by reference. A nonexlcusive list of specific examples of the types of bisphenol compounds that may be represented by formula (III) includes the following: 1,1-bis(4-hydroxyphenyl)methane; 1,1-bis(4-hydroxyphenyl)ethane; 2,2′-bis(4-hydroxyphenyl) propane (hereinafter “bisphenol A” or “BPA”); 2,2-bis(4-hydroxyphenyl)butane; 2,2-bis(4-hydroxyphenyl)octane; 1,1-bis(4-hydroxyphenyl)propane; 1,1-bis(4-hydroxyphenyl)n-butane; bis(4-hydroxyphenyl)phenylmethane; 2,2-bis(4-hydroxy-1-methylphenyl)propane; 1,1-bis(4-hydroxy-1-butylphenyl)propane; and (hydroxyaryl)alkanes such as 2,2-bis(4-hydroxy-3-bromophenyl)propane; 1,1-bis(4-hydroxyphenyl)cyclopentane; and bis(hydroxyaryl)cycloalkanes such as 1,1-bis(4-hydroxyphenyl)cyclohexane; and the like as well as combinations comprising at least one of the foregoing.
It is also possible to employ polycarbonates resulting from the polymerization of two or more different dihydric phenols or a copolymer of a dihydric phenol with a glycol or with a hydroxy- or acid-terminated polyester or with a dibasic acid or with a hydroxy acid or with an aliphatic diacid in the event a carbonate copolymer rather than a homopolymer is desired for use. Generally, useful aliphatic diacids have from 2 to about 40 carbons. A preferred aliphatic diacid is dodecandioic acid. Polyarylates and polyester-carbonate resins or their blends can also be employed. Branched polycarbonats are also useful, as well as blends of linear polycarbonate and a branched polycarbonate. The branched polycarbonates may be prepared by adding a branching agent during polymerization.
These branching agents are well known and may comprise polyfunctional organic compounds containing at least three functional groups which may be hydroxyl, carboxyl, carboxylic anhydride, haloformyl and mixtures comprising at least one of the foregoing. Specific examples include trimellitic acid, trimellitic anhydride, trimellitic trichloride, tris-p-hydroxyl phenyl ethane, isatin-bis-phenol, tris-phenol TC (1,3,5-tris((p-hydroxyphenyl)isopropyl)benzene), tris-phenol PA (4(4(1,1-bis(p-hydroxyphenyl)-ethyl) alpha, alpha-dimethyl benzyl)phenol), 4-chloroformyl phthalic anhydride, trimesic acid and benzophenone tetracarboxylic acid, and the like. The branching agents may be added at a level of about 0.05 to about 2.0 weight percent. Branching agents and procedures for making branched polycarbonates are described in U.S. Pat. Nos. 3,635,895 and 4,001,184. All types of polycarbonates end groups are herein contemplated.
Preferred polycarbonates are based on bisphenol A, in which each of A1 and A2 is p-phenylene and Y1 is isopropylidene. Preferably, the average molecular weight of the polycarbonate is about 5,000 to about 100,000, more preferably about 10,000 to about 65,000, and most preferably about 15,000 to about 35,000.
In monitoring and evaluating polycarbonate synthesis, it is of particular interest to determine the concentration of Fries product present in the polycarbonate. As noted, the generation of significant Fries product can lead to polymer branching, resulting in uncontrollable melt behavior. As used herein, the terms “Fries” and “Fires product” denote a repeating unit in polycarbonate having the formula (V):
wherein Xa is a bivalent radical as described in connection with Formula (III) described above.
The polycarbonate composition may also include various additives ordinarily incorporated in resin compositions of this type. Such additives are, for example, fillers or reinforcing agents; heat stabilizers; antioxidants; light stabilizers; plasticizers, antistatic agents; mold releasing agents; additional resins; blowing agents; and the like, as well as combinations comprising at least one of the foregoing additives. Examples of filler or reinforcing agents include glass fibers, asbestos, carbon fibers, silica, talc and calcium carbonate. Examples of heat stabilizers include triphenyl phosphite, tris-(2,6-dimethylphenyl)phosphite, tris-(mixed mono- and di-nonylphenyl)phosphite, dimethylbenzene phosphonate and trimethyl phosphate. Examples of antioxidants include octadecyl-3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate, and pentaerythrityl-tetrakis[3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate]. Examples of light stabilizers include 2-(2-hydroxy-5-methylphenyl)benzotriazole, 2-(2-hydroxy-5-tert-octylphenyl)benzotriazole and 2-hydroxy-4-n-octoxy benzophenone. Examples of plasticizers include dioctyl-4,5-epoxy-hexahydrophthalate, tris-(octoxycarbonylethyl) isocyanurate, tristearin and epoxidized soybean oil. Examples of the antistatic agent include glycerol monostearate, sodium stearyl sulfonate, and sodium dodecylbenzenesulfonate. Examples of mold releasing agents include stearyl stearate, beeswax, montan wax and paraffin wax. Examples of other resins include but are not limited to polypropylene, polystyrene, polymethyl methacrylate, and polyphenylene oxide. Combinations of any of the foregoing additives may be used. Such additives may be mixed at a suitable time during the mixing of the components for forming the composition.
In addition to the polymer and tagging material, the composition may optionally include various additives ordinarily incorporated in resin compositions of this type. Such additives may include antioxidants, heat stabilizers, antistatic agents (tetra alkylammonium benzene sulfonate salts, tetra alkylphosphonium benzene sulfonate salts, and the like), mold releasing agents (pentaerythritol tetrastearate; glycerol monostearate, and the like), and the like, the combinations comprising at least one of the foregoing. For example, the substrate can comprise heat stabilizer in a range between about 0.01 weight percent and about 0.1 weight percent; an antistatic agent in a range between about 0.01 weight percent and about 0.2 weight percent; and a mold releasing agent in a range between about 0.1 weight percent and about 1 weight percent of a mold releasing agent; based upon the total weight of the polymer.
Some possible antioxidants include, for example, organophosphites, e.g., tris(nonyl-phenyl)phosphite, tris(2,4-di-t-butylphenyl)phosphite, bis(2,4-di-t-butylphenyl)pentaerythritol diphosphite, distearyl pentaerythritol diphosphite and the like; alkylated monophenols, polyphenols and alkylated reaction products of polyphenols with dienes, such as, for example, tetrakis[methylene(3,5-di-tert-butyl-4-hydroxyhydrocinnamate)]methane, 3,5-di-tert-butyl-4-hydroxyhydrocinnamate octadecyl, 2,4-di-tert-butylphenyl phosphite, and the like; butylated reaction products of paracresol and dicyclopentadiene; alkylated hydroquinones; hydroxylated thiodiphenyl ethers; alkylidene-bisphenols; benzyl compounds; esters of beta-(3,5-di-tert-butyl-4-hydroxyphenyl)-propionic acid with monohydric or polyhydric alcohols; esters of beta-(5-tert-butyl-4-hydroxy-3-methylphenyl)-propionic acid with monohydric or polyhydric alcohols; esters of thioalkyl or thioaryl compounds, such as, for example, distearylthiopropionate, dilaurylthiopropionate, ditridecylthiodipropionate, and the like; amides of beta-(3,5-di-tert-butyl-4-hydroxyphenyl)-propionic acid; and the like, as well as combinations comprising at least one of the foregoing.
Other potential additives which may be employed comprise: UV absorbers; stabilizers such as light and thermal stabilizers (e.g., acidic phosphorous-based compounds); hindered phenols; zinc oxide, zinc sulfide particles, or combinations thereof; lubricants (mineral oil, and the like), plasticizers, dyes used as a coloring material (quinines, azobenzenes, and the like); among others, as well as combinations comprising at least one of the foregoing additives.
In order to aid in the processing of the polymer, particularly polycarbonate; catalyst(s) may also be employed, namley in the extruder or other mixing device. The catalyst typically assists in controlling the viscosity of the resulting material. Possible catalyses include hydroxides, such as tetraalkylammonium hydroxide, tetraalkylphosphonium hydroxide, and the like, with diethyldimethylammonium hydroxide and tetrabutylphosphonium hydroxide preferred. The catalyst(s) can be employed alone or in combination with quenchers such as acids, such as phosphoric acid, and the like. Additionally, water may be injected into the polymer melt during compounding and removed as water vapor through a vent to remove residual volatile compounds.
The polymer is produced by using a conventional reaction vessel capable of adequately mixing various precursors, such as a single or twin screw extruder, kneader, blender, or the like. Spectroscopic tags can be incorporated into the polymer in the polymer manufacturing stage, during polymer processing into articles, or combinations thereof. The spectroscopic tag can be incorporated into the polymer such that it is uniformly dispersed throughout the polymer or such that it is dispersed on a portion of the polymer. The polymer precursors can be premixed with the spectroscopic tag (e.g., in a pellet, powder, and/or liquid form) and simultaneously fed through a hopper into the extruder, or the spectroscopic tag can be optionally added in the feed throat or through an alternate injection port of the injection molding machine or other molding. Optionally, the polymer can be produced and the spectroscopic tag can be dispersed on a portin of the polymer. Methods for incorporating the spectroscopic tag into the polymer include, for example, coating, admixing, blending, or copolymerization.
The extruder should be maintained at a sufficiently high temperature to melt the polymer precursors without causing decomposition thereof. For polycarbonate, for example, temperatures of about 220° C. to about 360° C. can be used, with about 260° C. to about 320° C. preferred. Similarly, the residence time in the extruder should be controlled to minimize decomposition. Residence times of up to about 2 minutes or more can be employed, with up to about 1.5 minutes preferred, and up to about 1 minute especially preferred. Prior to extrusion into the desired form (typically pellets, sheet, web, or the like, the mixture can optionally be filtered, such as by melt filtering and/or the use of a screen pack, or the like, to remove undesirable contaminants or decomposition products.
The polymers of the present invention may be used for any application in which the physical and chemical properties of the material are desired. Typically, the polymers are used for data storage media. After the polymer composition has been produced, it can be formed into a data storage media using various molding techniques, processing techniques, or combination thereof. Possible molding techniques include injection molding, film casing, extrusion, press molding, blow molding, stamping, and the like. One possible process comprises an injection molding-compression technique where a mold is fileld with a molten polymer. The mold may contain a preform, inserts, fillers, etc. The polymer is cooled and, while still in an at least partially molten state, compressed to imprint the desired surface features (e.g., pits, grooves, edge features, smoothness, and the like), arranged in spiral concentric or other orientation, onto the desired portion(s) of the substrate, i.e. one or both sides in the desired areas. The substrate is then cooled to room temperature. Once the substrate has been produced, additional processing, such as electroplating, coating techniques (spin coating, spray coating, vapor deposition, screen printing, painting, dipping, and the like), lamination, sputtering, and combinations comprising at least one of the foregoing processing techniques, among others conventionally known in the art, may be employed to dispose desired layers on the substrate.
An example of a polycarbonate data storage media comprises an injection molded polycarbonate substrate which may optionally comprise a hollow (bubbles, cavity, and the like) or filled (metal, plastics, glass, ceramic, and the like, in various forms such as fibers, spheres, particles, and the like) core. Disposed on the substrate are various layers including: a data layer, dielectric layer(s), a reflective layer(s), and/or a protective layer, as well as combinations comprising at least one of the foregoing layers. These layers comprise conventional materials and are disposed in accordance with the type of media produced. For example, for a first surface media; the layers may be protective layer, dielectric layer, data storage layer, dielectric layer, and then the reflective layer disposed in contact with the substrate, with an optional decorative layer disposed on the opposite side of the substrate. Meanwhile, for an optical media, the layers may be optional decorative layer, protective layer, reflective layer, dielectric layer, and data storage layer, with a subsequent dielectric layer in contact with the substrate. Optical media may include, but is not limited to, any conventional pre-recorded, re-writable, or recordable formats such as: CD, CD-R, CD-RW, DVD, DVD-R, DVD-RW, DVD+RW, DVD-RAM, high-density DVd, magneto-optical, and others. It is understood that the form of the media is not limited to disk-shape, but may be any shape which can be accommodated in a readout device.
The data storage layer(s) may comprise any material capable of storing retrievable data, such as an optical layer, magnetic layer, or a magneto-optic layer. Typically the data layer has a thickness of up to about 600 Angstroms (Å) or so, with a thickness up to about 300 Å preferred. Possible data storage layers include, but are not limited to, oxides (such as silicon oxide), rare earth elements—transition metal alloys, nickel, cobalt, chromium, tantalum, platinum, terbium, gadolinium, iron, boron, others, and alloys and combinations comprising at least one of the foregoing organic dye (e.g., cyanine or phthalocyanine type dyes), and inorganic phase change compounds (e.g., TeSeSn, InAgSb, and the like).
The protective layer(s), which protect against dust, oils, and other contaminants, can have a thickness of greater than about 100 microns (μ) to less than about 10 Å, with a thickness of about 300 Å or less preferred in some embodiments, and a thickness of about 100 Å or less especially preferred. The thickness of the protective layer(s) is usually determined, at least in part, by the type of read/write mechaism employed, e.g., magnetic, optic, or magneto-optic. Possible protective layers include anti-corrosive materials such as gold, silver, nitrides (e.g., silicon nitrides and aluminum nitrides, among others), carbides (e.g., silicon carbide and others), oxides (e.g., silicon dioxide and others), polymeric materials (e.g., polyacrylates or polycarbonates), carbon film (diamond, diamond-like carbon, and the like), among others, and combinations comprising at least one of the foregoing.
The dielectric layer(s), which are disposed on one or both sides of the data storage layer and are often employed as heat controllers, can typically have a thickness of up to or exceeding about 1,000 Å and as low as about 200 Å or less. Possible dielectric layers include nitrides (e.g., silicon nitride, aluminum nitride, and others); oxides (e.g., aluminum oxide); carbides (e.g., silicon carbide); and combinations comprising at least one of the foregoing materials, among other materials compatible within the environment and preferably not reactive with the surrounding layers.
The reflective layer(s) should have a sufficient thickness to reflect a sufficient amount of energy (e.g., light) to enable data retrieval. Typically the reflective layer(s) can have a thickness of up to about 700 Å or so, with a thickness of about 300 Å to about 600 Å generally preferred. Possible reflective layers include any material capable of reflecting the particular energy field, including metals (e.g., aluminum, silver, gold, titanium, and alloys and mixtures comprising at least one of the foregoing metals, and others).
In addition to the data storage layer(s), dielectric layer(s), protective layer(s) and reflective layer(s), other layers can be employed such as lubrication layer and others. Useful lubricants include fluoro compounds, especially fluoro oils and greases, and the like.
The tagging materials of the present invention allows for a non-destructive means for the tracking of materials, determination of processing conditions such as the temperature at which an article was manufactured in addition to the thermal history and degradation.
In order that those skilled in the art will be better able to practice the invention, the following example is given by way of illustration and not by way of limitation.
An organic fluorophore (Lumogen Red 300 obtained from BASF) was used as a spectroscopic tag. It has a high melting point (300° C.) and high temperature stability. The tag was incorporated into the melt polycarbonate material during the melt polymerization reaction. The melt polymerization was performed in a lab reactor. For heat stability tests, small amounts of polymer (about 0.5 grams) were put into an oven at 400° C. for three minutes. Heating of the samples was done in air.
Fluorescence emission spectra of the tag before and after the heating test was performed to assess the temperature stability of the tag. Determinations were performed on a setup which included a white light source (450 Watt Xenon arc lamp, SLM Instruments, Inc., Urbana, Ill., Model FP-024), a monochromator for selection of the excitation wavelengths (SLM Instruments, Inc., Model FP-092) and a portable spectrofluorometer (Ocean Optics, Inc., Dunedin, Fla., Model ST2000). The spectrofluorometer was equipped with a 200 micron slit, 600 grooves per millimeter grating blazed at 400 nanometers and covering the spectral range from 250 to 800 nanometers with efficiency greater than 30% and a linear charge coupled device (CCD) array detector. Light from the monochromator was focused into one of the arms of a “six-around-one” bifurcated fiber-optic reflection probe (Ocean Optics, Inc., Model R400-7-UV/VIS). Light from the sampels was collected when the common end of the fiber-optic probe was position near the samples at a certain angle to minimize the amount of light directly reflected from the sample back int the probe. The second arm of the porbe was coupled to the spectrofluorometer.
While embodiments have been shown and described, various modifications and substitutions may be made thereto without departing from the spirit and the scope of the invention. Accordingly, it is to be understood that the present invention has been described by way of illustration and not limitation.
|Cited Patent||Filing date||Publication date||Applicant||Title|
|US4238524||Mar 6, 1978||Dec 9, 1980||American Optical Corporation||Process for identification marking clear plastic articles|
|US4813973||Jan 11, 1988||Mar 21, 1989||The University Of Toronto Innovations Foundation||Modified, water-soluble polymers containing amide groups reacted with xanthydrol and other dyes|
|US5005873||Apr 7, 1987||Apr 9, 1991||West Michael A||Marking of articles|
|US5030697||Sep 18, 1989||Jul 9, 1991||Bayer Aktiengesellschaft||Polymer-bound dyes, process for their production and use|
|US5128419||Aug 20, 1990||Jul 7, 1992||Nalco Chemical Company||Synthesis of tagged polymers by post-polymerization (trans) amidation reaction|
|US5171450||Mar 20, 1991||Dec 15, 1992||Nalco Chemical Company||Monitoring and dosage control of tagged polymers in cooling water systems|
|US5201921||Sep 6, 1991||Apr 13, 1993||Bayer Aktiengesellschaft||Process for identifying plastics by addition of fluorescent dye|
|US5314072||Sep 2, 1992||May 24, 1994||Rutgers, The State University||Sorting plastic bottles for recycling|
|US5329127||Apr 12, 1993||Jul 12, 1994||Bayer Ag||Method for the identification of plastics|
|US5510619||Nov 18, 1994||Apr 23, 1996||Brunker Analytische Messtechnik Gmbh||Method for the routine identification of plastics|
|US5553714||Nov 14, 1994||Sep 10, 1996||Eastman Chemical Company||Method for detecting and separating thermoplastic containers with near infrared fluorosphores|
|US5573909||May 20, 1994||Nov 12, 1996||Molecular Probes, Inc.||Fluorescent labeling using microparticles with controllable stokes shift|
|US5640010||May 11, 1995||Jun 17, 1997||Twerenbold; Damian||Mass spectrometer for macromolecules with cryogenic particle detectors|
|US5703229||Feb 29, 1996||Dec 30, 1997||Eastman Chemical Company||Method for tagging thermoplastic materials with near infrared fluorophores|
|US5925716||Jan 17, 1997||Jul 20, 1999||Rohm And Haas Company||Polymers from unsaturated acid monomers containing amine-sulfide moiety|
|US6051437 *||May 4, 1998||Apr 18, 2000||American Research Corporation Of Virginia||Optical chemical sensor based on multilayer self-assembled thin film sensors for aquaculture process control|
|US6099930||Dec 15, 1997||Aug 8, 2000||Isotag Technology, Inc.||Methods for marking digital compact discs as a means to determine its authenticity|
|US6219329||Jan 18, 1991||Apr 17, 2001||Fujitsu Limited||Fluorescent optical disk|
|US6251680||Feb 5, 1999||Jun 26, 2001||Rohm And Haas Company||Detectable polymers and methods for detecting polymers in Aqueous systems|
|US6355420||Aug 13, 1998||Mar 12, 2002||Us Genomics||Methods and products for analyzing polymers|
|US6403311||Aug 13, 1999||Jun 11, 2002||Us Genomics||Methods of analyzing polymers using ordered label strategies|
|US6514617||Jul 11, 2001||Feb 4, 2003||General Electric Company||Tagging materials for polymers, methods, and articles made thereby|
|US6740518 *||Sep 17, 1999||May 25, 2004||Clinical Micro Sensors, Inc.||Signal detection techniques for the detection of analytes|
|US20020110818||Aug 13, 2001||Aug 15, 2002||Us Genomics, Inc.||Methods of analyzing polymers using ordered label strategies|
|US20020119455||May 10, 2001||Aug 29, 2002||Chan Eugene Y.||Methods and products for analyzing polymers|
|EP0700961B1||Oct 13, 1992||Dec 23, 1998||Eastman Chemical Company||Thermoplastic polymer composition having admixed therein one or more monomeric near-infrared fluorescing compounds|
|EP1002831A1||Nov 20, 1998||May 24, 2000||E.I. Du Pont De Nemours And Company||Fluorescent fluoroplastics|
|GB2264558A||Title not available|
|GB2330408A||Title not available|
|WO2000014736A1||Aug 19, 1999||Mar 16, 2000||The Dow Chemical Company||Method for the prevention of unauthorized duplication of information-carrying substrates|
|Citing Patent||Filing date||Publication date||Applicant||Title|
|US9204598||Jul 9, 2013||Dec 8, 2015||Saudi Basic Indsutries Corporation||Solar energy funneling using thermoplastics for agricultural applications|
|U.S. Classification||528/196, 428/421, 528/271, 428/412, 526/342, 528/193, 528/272, 528/190, 436/56|
|International Classification||G01N21/64, C08G63/02, C08G64/00|
|Cooperative Classification||Y02W30/622, Y10T428/3154, Y10T428/31507, Y10T436/13, G01N21/6428, B29B2017/0279|
|May 1, 2008||AS||Assignment|
Owner name: SABIC INNOVATIVE PLASTICS IP B.V., NETHERLANDS
Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNOR:GENERAL ELECTRIC COMPANY;REEL/FRAME:020985/0551
Effective date: 20070831
|Aug 18, 2008||AS||Assignment|
Owner name: CITIBANK, N.A., AS COLLATERAL AGENT, NEW YORK
Free format text: SECURITY AGREEMENT;ASSIGNOR:SABIC INNOVATIVE PLASTICS IP B.V.;REEL/FRAME:021423/0001
Effective date: 20080307
|Oct 26, 2010||CC||Certificate of correction|
|Mar 17, 2014||AS||Assignment|
Owner name: SABIC INNOVATIVE PLASTICS IP B.V., NETHERLANDS
Free format text: RELEASE BY SECURED PARTY;ASSIGNOR:CITIBANK, N.A.;REEL/FRAME:032459/0798
Effective date: 20140312
|Jul 9, 2014||FPAY||Fee payment|
Year of fee payment: 12