|Publication number||USRE42389 E1|
|Application number||US 12/171,005|
|Publication date||May 24, 2011|
|Filing date||Jul 10, 2008|
|Priority date||Nov 25, 1998|
|Also published as||US7075707|
|Publication number||12171005, 171005, US RE42389 E1, US RE42389E1, US-E1-RE42389, USRE42389 E1, USRE42389E1|
|Inventors||Alexandra Rapaport-Zoubir, Anne Janet Milliez, Michael Bass, Hans P. Jenssen|
|Original Assignee||University Of Central Florida Research Foundation, Inc.|
|Export Citation||BiBTeX, EndNote, RefMan|
|Patent Citations (40), Non-Patent Citations (1), Classifications (34), Legal Events (2)|
|External Links: USPTO, USPTO Assignment, Espacenet|
This invention is a This is a reissue application of U.S. application Ser. No. 10/841,188 filed May 7, 2004, now issued as U.S. Pat. No. 7,075,707, which is a Continuation-In-Part of U.S. applications Ser. No. 09/919,130 filed Jul. 31, 2001, now issued as U.S. Pat. No. 6,844,387 and Ser. No. 09/919,131 filed Jul. 31, 2001, now issued as U.S. Pat. No. 6,654,161, which are Continuation-In-Part applications of U.S. application Ser. No. 09/448,657 filed Nov. 24, 1999, now U.S. Pat. No. 6,327,074, which claims the benefit of priority to U.S. Provisional Application 60/109,837 filed Nov. 25, 1998.
This invention was funded in part under U.S. Army Contract DAAD199910220.
This invention relates to the up-conversion efficiency of donor-acceptor doubly doped crystals dispersed in a stabilized polymer or other passive hosts and in particular to a class of fluoride crystals co-doped with ytterbium and erbium or thulium to provide composites and methods for use in luminescent displays.
Displays using liquid crystals have been proposed for generating color displays (see for example, U.S. Pat. Nos. 5,359,345 and 5,724,062 to Hunter). However, these patents require arranging individual pixels in rows and corresponding columns, (column 4, lines 36-39). The devices described can be expensive and complicated to manufacture, and can have narrow angular view ranges with low brightness. Additional display systems have been proposed with similar problems to those described above (see for example, U.S. Pat. No. 4,791,415 to Takahashi; U.S. Pat. No. 4,871,231 to Garcia, Jr.; U.S. Pat. No. 5,184,114 to Brown; U.S. Pat. No. 5,192,946 to Thompson et al.; and U.S. Pat. No. 5,317,348 to Knize).
Several patents have been proposed for displays using two-frequency up-conversion fluorescence (see for example, U.S. Pat. Nos. 5,684,621; 5,764,403; 5,914,807; 5,943,160; and 5,956,172 all to Downing). The Downing '403 patent appears to be the most relevant to the subject invention. Downing '403 is primarily concerned with embodiments where the use of different layers for red, green and blue emitters, abstract,
Other relevant known patents such as U.S. Pat. No. 5,003,179 to Pollack; 5,051,278 to Paz-Pujalt; U.S. Pat. No. 5,154,962 to Mertens et al.; U.S. Pat. No. 5,245,623 to McFarlane; U.S. Pat. No. 5,622,807 to Cutler; U.S. Pat. No. 5,846,684 to Paz-Pujalt et al. also fail to overcome the problems with the other patents described above.
The concept of frequency up-conversion (UC) of infrared-to-visible light in rare-earth (RE) doped materials was reported more than forty years ago for the first time. The efficiency that was observed or expected for this process was low in singly doped media, but it was quickly noticed that the mechanism could be made one or two orders of magnitude more efficient by using ytterbium (Yb) as a sensitizer ion in addition to the active ion: erbium (Er), holmium (Ho), or thulium (Tm). Efficient UC materials were extensively investigated, as they could be used for several potentially useful photonic applications, such as in UC lasers (visible lasers that are pumped by infrared diode lasers), or in display applications. However, because no powerful source existed in the 980-nm region in order to excite those up-converters, no practical product came out of the research. With the development of powerful 980-nm diode lasers lead by the telecommunication industry, a technology that appeared to be too inefficient in the past now has legitimate practical applications.
It has been noticed in the past that pumping conditions caused heating of the material and that higher efficiencies were obtained with low duty cycle excitation. It was also reported that for a same average input power, higher efficiencies were expected in pulsed excitation mode than in continuous wave (cw) excitation due to the quadratic nature of the process. The effect of the pumping conditions for display applications of UC materials need to be understood, as several technologies might be used to form the image. The infrared source can either be scanned (vector-addressed or raster-scan), or the image can be directly projected using Digital Micromirror Devices (MEMS) such as in the Texas Instrument Digital Light Processing (DLP™) technology. In the latter case the materials would be undergoing pulse-excitation, whereas they would be quasi-continuously excited in the second case.
As earlier noted, the development of powerful diode lasers emitting near 980-nm by the telecommunication industry is an enabling technology that allows up conversion to be used in displays. In the past no good pump source was available. Now these diodes provide for practical applications when the efficiency of up-conversion materials are enhanced to provide useful levels of fluorescence.
A primary objective of this invention is to provide an inexpensive display medium for two and possibly three dimensional displays.
A secondary objective of this invention is to provide a transparent polymer (plastic) containing particles doped with rare earth ions for use as display medium for two and three dimensional displays.
A third objective of this invention is to provide homogeneously dispersed rare earth doped crystalline particles in a polymer and illuminated with light with wavelength near 980 nm so illuminated and provided with thermal management to result in enhanced luminescence efficiency.
A fourth objective of this invention is to provide a display medium for the up-conversion of 980-nm light to the visible for two and three dimensional displays.
The invention can be used with up-conversion displays with specific applications for two and three dimensional displays such as those described in parent patent application Ser. No. 09/448,657 filed Nov. 24, 1999, now U.S. Pat. No. 6,327,074, by the same assignee as the subject invention and of which is incorporated by reference thereto.
Novel display media according to this invention includes a method for using an up-conversion phosphor as the emitting material in a reflective display comprising the step of designing the shape of said display to maximally remove any heat developed in the emitting material whereby the emittance level of said phosphor is markedly increased.
Further objects and advantages of this invention will be apparent from the following detailed descriptions of the presently preferred embodiments which are described in the following text.
Before explaining the disclosed embodiment of the present invention in detail it is to be understood that the invention is not limited in its application to the details of the particular arrangements shown since the invention is capable of other embodiments. Also, the terminology used herein is for the purpose of description and not of limitation.
It has been found in accordance with this invention that pumping with pulses as either by the irradiation or scanning process in a display, and providing proper means for thermal management of the emitting materials, both contribute to making efficient up-conversion displays with diode laser pumping attractive for display applications. This disclosure explains the techniques to achieve the desired higher efficiency.
As previously described, the subject invention can be used with up conversion displays with specific applications for two and three dimensional displays such as those described in parent patent applications U.S. application Ser. Nos. 09/919,130 and 09/919,131 both filed Jul. 31, 2001, now U.S. Pat. Nos. 6,844,387 and 6,654,161, respectively, and Ser. No. 09/448,657 filed Nov. 24, 1999, now U.S. Pat. No. 6,327,074, all to the same assignee as that of the subject invention and all of which are incorporated herein by reference thereto.
Table 1 is a list of various crystals and co-dopants and central wavelengths of the bands of visible emission detected following excitation with a diode laser source operating at approximately 968 nm.
Peak emission wavelength (nm)
Table 1: Visible emission of Tm, Er and Ho after Yb excitation in different hosts
In Table 1, Yb3+ refers to ytterbium, Tm3+ refers to thulium, Er3+ refers to erbium, Ho3+ refers to holmium, NaYF4 refers to crystal sodium yttrium fluoride, and the supercript 3+ refers to the triply ionized state of the atom. Referring again to Table 1, KYF is short for KYF4 and refers to crystal, potassium yttrium fluoride. YLF is short for YliF4 and refers to the crystal, yttrium lithium fluoride. LuPO4 refers to the crystal, lutetium orthophosphate.
The crystals and dopants listed in Table 1 are illustrative of a few of the combinations that can be used. Other lanthanide (rare earth) atoms in the 3+ state can also be used as dopants. For example, Nd3+, Pr3+, Ce3+ and the like, can also be used. There can be other oxide and flouride crystals that can serve as host crystals. Transition metal dopants such as but not limited to Cr3+, Ti3+ and the like, can serve as dopants in these host crystals as well. Additionally, other crystals and activators that can be used for this invention can include those listed from pages 171 to page 311 listed in Laser Crystals by Alexander Kaminski, (Springer Verlag, New York) SBN 0-387-09576-4, 1981. These crystals and their activators can include but are not limited to the following described activators and crystal combinations.
Activator Pr3+ and crystals can include: LiYF4, Ca(NbO3)2, CaWO4, and SrMoO4.
Activator Nd3+ and crystals can include: LiYF4, LiYO2, LiNbO3, LiNbP4O12, CaF2, SrF2, BaF2, LaF3, CeF3, NaF, NaCaYF6, NaCaCeF6, NaNdP4O12, YF3, CaYF, SrYF, CeO2, GdF3, YF3, LuF3, CdF2, KY(MoO4)2, KY(WO4)2, KNdP4O12, KGd(WO4)2, CaMg2Y2, CaAl4O7, CaAl12O19, Activator Nd3+ and crystals can include: LiYF4, LiYO2, LiNbO3, LiNbP4O12, CaF2, SrF2, BaF2, LaF3, CeF3, NaF, NaCaYF6, NaCaCeF6, NaNdP4O12, YF3, CaYF, SrYF, CeO2, GdF3, YF3, LuF3, CdF2, KY(MoO4)2, KY(WO4)2, KNdP4O12, KGd(WO4)2, CaMg2Y2, CaAl4O7, CaAl12O19, CaSc2O4, Ca3(VO4)2, Ca(NbO3)2, CaMoO4, CaWO4, SrA12O7, SrAl12O19, SrMoO4, SrWO4, Y2O3, YAlO3, Y3Al5O12, Y2SiO5, YP5O14, Y3Sc2Al3O12, Y3Sc2Ga3O12, YVO4, Y3Ga5O12, (Y, Lu)3Al5O12, Ba0.25Mg2.75Y2, LaBe2O5, La2O3, LaAlO3, LaP5O14, LaNbO4, CeP5O14, NdAl3(BO3)4, NdP5O14, Gd2O3, GdAlO3, GdP5O14, GdScO3, Gd3Sc2Al3O12, Gd3Sc2Ga3O12, Gd3Ga5O12, Gd2(MoO4)3, LuAlO3, Lu3Ga5O12, PbMoO4, Bi4Si3O12, Bi4Ge3O12, LiLa(MoO4)2, Li(Nd, La)P4O12, Li(Nd, Gd)P4O12, LiGd(MoO4)2, NaLa(MoO4)2, NaLa(WO4)2, Na3Nd(PO4)2, Na5Nd(WO4)2, Na3Gd(WO4)2, Na(Nd, Gd), Ka(MoO4)2, K3Nd(PO4)2, K3(Nd, La), K3Nd(MoO4)4, K5Bi(MoO4)4, CaY4(SiO4)3O, Ca0.25Ba0.75, CaLa4(SiO4)3O, CaLa(PO4)3O, CaGd4(SiO4)3O, YScO3, Y2Ti2O7, ZrO2—Y2O3, Ba2MgGe2O7, Ba2ZnGe2O7, (Nd, Sc)P5O14, (Nd, In)P5O14, (Nd, La)P5O14, (Nd, Gd)Al3, LuScO3, HfO2—Y2O3, Bi4(Si, Ge)3O12, Ca5(PO4)3F, Sr5(PP4)3F, and La2O2S, CeCl3, Pb5(PO4)3F.
Activator Ho3+ and crystals can include: LiYF4, Li(Y, Er)F4, LiNbO3, CaF2, LiHoF4, BaY2F8, Ba(Y, Er)2F8, HoF3, CaF2, YF3, ErF3, NaCaErF6, K(Y, Er)(WO4)2, KGd(WO4)2, Ca(NbO3)2, CaMoO4, CaWO4, YAlO3, Y3Al5O12, Y2SiO5, YVO4, Y3Fe5O12, Y3Ga5O12, (Y, Er)Al3, (Y, Er)3Al5O12, LaNbO4, GdAlO3, Ho3Al5O12, Ho3Sc2Al3O12, Ho3Ga5O12, Er2O3, ErAlO3, Er2SiO5, Er3Sc2Al3O12, ErVO4, (Er, Tm, Yb)3, (Er, Lu)AlO3, Yb3Al5O12, LuAlO3, Lu3Al5O12, NaLa (MoO4)2, CaY4(SiO4)3O, SrY4(SiO4)3O, SrLa4(SiO4)3O, ZrO2—Er2O3, Ba2NaNb5O15, and Ca5(PO4)3F.
Activator Er3+ and crystals can include: LiYF4, LiErF4, CaF2, BaY2F8, Ba(Y, Er)2F8, LaF3, YF3, ErF3, K(Y, Er) (WO4)2, KGd(WO4)2, CaAl4O7, Ca(NbO3)2, CaWO4, YAlO3, Y3Al5O12, (Y, Er)3Al5O12, GdAlO3, Er3Al5O12, (Er, Lu)3Al5O12, Yb3Al5O12, LuAlO3, and Lu3Al5O12.
Activator Ni2+ and crystals can include: MgF2, MnF2, and MgO. Activator V2+ and crystals can include: MgF2. Activator Co2+ and crystals can include: MgF2, KMgF2, and ZnF2. Activator Yb3+ and crystals can include: CaF2,:Nd3+, Y3Al5O12, Y3Ga5O12, (Y, Yb)3Al5O12, Gd3Sc2Al3O12, Gd3Ga5O12, (Yb, Lu)3Al5O12, Lu3Al5O12, Lu3Sc2Al3O12, and Lu3Ga5O12. Activator Sm2+ and crystals can include: CaF2, SrF2. Activator Dy2+ and crystals can include: CaF2, SrF2. Activator Dy3+ and crystals can include: Ba(Y,Er)2F8. Activator Tm2+ and crystals can include: CaF2.
Activator Tm3+ and crystals can include: CaF2, SrF2, ErF3, NaCaErF6, LiNbO3, Ca(NbO3)2, CaMoO4, CaWO4, YAlO3, Y3Al5O12, YVO4, (Y, Er)Al3, (Y, Er)3Al5O12, GdAlO3, Er2O3, ErAlO3, Er3Al5O12, (Er, Yb)3Al5O12, (Er, Lu)AlO3, Lu3Al5O12, and ZrO2—Er2O3.
Activator U3+ and crystals can include: CaF2, SrF2, and BaF2. Activator Pr3+ and crystals can include: LaF3, LaCl3, LaBr3, PrCl3, and PrBr3. Activator Cr3+ and crystals can include: BeAl2O4, Al2O3, and Y3Al5O12. Activator Eu3+ and crystals can include: Y2O3, YVO4. Activator Gd3+ and crystals can include: Y3Al5O12.
Some of the dopant-host combinations can also emit useful infrared light through excitation by absorption of a single photon. This invention can also include systems that emit infrared light by this process of down-conversion(e.g. absorbing a high energy photon and emitting one of lower energy) as well as systems that are excited by such two photon processes as up-conversion(e.g. absorbing more than one low energy photons and emitting one or more higher energy photons).
The rare earth doped crystalline particles are dispersed in a passive polymer host that can be comprised of a copolymer of alkyl acrylate or alkyl methacrylate and a dialkyl vinylbenzylphosphonate, alkyl vinylbenzylphosphonic acid monoester, or vinylbenzylphosphonic acid. The ratios of the acrylate or methacrylate to the phosphonate can range from approximately 95:5 molar ratio to approximately 20:80 molar ratio, respectively. Luminescent heavy metal ions such as rare earth compounds (for example, NaYF4:ErYb) loading in the host polymer matrix can range from approximately 5 up to approximately 80 weight percent. Stabilization of the dispersed heavy element luminophores can be accomplished through complexation with the phosphoryl moieties.
One can prepare the crystals as approximately 10 μm size particles and disperse them in a phosphorylated polymethylmethacrylate (p-PMMA) host. This results in a display medium that can be formed to any desired shape, e.g., as a pixel, can be transparent or not, as desired, and can be affixed to any desired substrate; preferably a heat conductive substrate capable of maximally heat removal.
In this disclosure of the invention, the role of temperature on the efficiency of our up-conversion materials is set forth as well as the effect of various substrate materials, pumping rates and duration on the performance of three of our best performing up-conversion (UC) materials. The materials used for the up-conversion material are characterized by color: green (Yb, Er doped sodium yttrium fluoride or Yb,Er:NYF4): red (Yb, Br doped yttrium fluoride or Yb,Er: YF3); and, blue (Yb, Tm doped yttrium lithium fluoride or Yb,Tm:YLF4).
The results of the investigation are hereafter set forth.
The performance of the blue up-conversion material was altered when pumping with a continuous source compared to when using short pulse excitation. An early analysis that solved the rate equations numerically illustrated that this behavior could be explained when temperature-dependent transfer and cross-relaxation rates were included. In order to better understand thermal effects, the emission spectra obtained for the three color up-conversion materials when pumped with various intensities and pulse durations was recorded. Reference should now be made to
The peaks at approximately 463 nm and approximately 481 nm originate from the same upper energy level but different Stark splittings sub-levels. Those sub-levels are thermalized and the spectral distribution is therefore a signature of the temperature inside the sample. It can be shown from
By using a hot plate and a thermocouple, the emission spectra after excitation with a low energy pulse the emission spectra can be recorded (no heating due to the excitation) at different pre-determined temperatures. From those measurements, one can determine the temperature in the sample at different output powers for various pump durations.
Reference should now be made to
Finally, the total output power as the temperature of the sample was measured. The results are shown in
Through the green phosphor is only slightly affected by heating, the blue and the red emitters' performance greatly diminish when operated at the temperature reached when no thermal management is included in the design of a display. Experimental results show that lowering the operating temperature is the key to optimizing up-conversion materials performance. As shown by the graph of
Photonic displays based on up-conversion materials have numerous advantages that make the technology appealing: the phosphors emit very narrow lines (˜40 nm wide) which produce a very wide color gamut (That is, they define area of the color response diagram much greater than that of conventional cathode ray tube phosphors) and saturated colors, high-brightness (several kCd/m2) can be achieved without damage to the phosphors, and no vacuum nor high-voltage is required. However, improving the materials' efficiency is paramount to making this technology able to compete with existing display technologies. In this work, one important step was identified in order to optimize the performance of the up-conversion phosphors: using heat-conductive substrate such as copper or aluminum or CVD diamond will reduce the operating temperature of the powder and improve the efficiency (efficiency is the ratio of the light power output of the display to the total power input to the display) of the display.
While the invention has been described, disclosed, illustrated and shown in various terms of certain embodiments or modifications which it has presumed in practice, the scope of the invention is not intended to be, nor should it be deemed to be, limited thereby and such other modifications or embodiments as may be suggested by the teachings herein are particularly reserved especially as they fall within the breadth and scope of the claims here appended.
|Cited Patent||Filing date||Publication date||Applicant||Title|
|US4448547||Jul 10, 1980||May 15, 1984||Luxtron Corporation||Optical temperature measurement technique utilizing phosphors|
|US4791415||Jan 29, 1986||Dec 13, 1988||Matsushita Electric Industrial Co., Ltd.||Digial driving type color display device|
|US4871231||Oct 16, 1987||Oct 3, 1989||Texas Instruments Incorporated||Three dimensional color display and system|
|US4978888||Jul 18, 1989||Dec 18, 1990||Thomas Electronics Incorporated||Thick-film integrated flat fluorescent lamp|
|US5003179||May 1, 1990||Mar 26, 1991||Hughes Aircraft Company||Full color upconversion display|
|US5051278||Jul 10, 1989||Sep 24, 1991||Eastman Kodak Company||Method of forming metal fluoride films by the decomposition of metallo-organic compounds in the presence of a fluorinating agent|
|US5142388||Dec 20, 1991||Aug 25, 1992||Futaba Denshi Kogyo K.K.||Color display device having liquid crystal cell and fluorescent display with two different luminous sections|
|US5154962||Sep 13, 1991||Oct 13, 1992||Minnesota Mining And Manufacturing Company||Indicia-receptive low adhesion backsize|
|US5184114||Mar 15, 1990||Feb 2, 1993||Integrated Systems Engineering, Inc.||Solid state color display system and light emitting diode pixels therefor|
|US5192946||May 30, 1991||Mar 9, 1993||Texas Instruments Incorporated||Digitized color video display system|
|US5245623||Dec 2, 1991||Sep 14, 1993||Hughes Aircraft Company||Infrared-to-visible upconversion display system and method operable at room temperature|
|US5317348||Dec 1, 1992||May 31, 1994||Knize Randall J||Full color solid state laser projector system|
|US5359345||Aug 5, 1992||Oct 25, 1994||Cree Research, Inc.||Shuttered and cycled light emitting diode display and method of producing the same|
|US5583393||Mar 24, 1994||Dec 10, 1996||Fed Corporation||Selectively shaped field emission electron beam source, and phosphor array for use therewith|
|US5622807||Nov 14, 1994||Apr 22, 1997||Hewlett-Packard Company||Phosphor film composition for use in image capture|
|US5684621||May 8, 1995||Nov 4, 1997||Downing; Elizabeth Anne||Method and system for three-dimensional display of information based on two-photon upconversion|
|US5724062||Sep 21, 1994||Mar 3, 1998||Cree Research, Inc.||High resolution, high brightness light emitting diode display and method and producing the same|
|US5746942||Jan 31, 1996||May 5, 1998||The United States Of America As Represented By The Secretary Of The Navy||Erbium-doped low phonon hosts as sources of fluorescent emission|
|US5764403||Jan 30, 1997||Jun 9, 1998||Downing; Elizabeth A.||Panel display using two-frequency upconversion fluorescence|
|US5786102||Jan 16, 1996||Jul 28, 1998||Eastman Kodak Company||Device for converting invisible and visible radiation to visible light and/or UV radiation|
|US5801792||Dec 13, 1995||Sep 1, 1998||Swz Engineering Ltd.||High resolution, high intensity video projection cathode ray tube provided with a cooled reflective phosphor screen support|
|US5846684||Jan 30, 1997||Dec 8, 1998||Eastman Kodak Company||Device for converting invisible and visible radiation to visible light and/or UV radiation|
|US5914807||Nov 3, 1997||Jun 22, 1999||3D Technology Laboratories, Inc.||Method and system for three-dimensional display of information based on two-photon upconversion|
|US5943160||Nov 3, 1997||Aug 24, 1999||3D Technology Laboratories, Inc.||System and method for co-doped three-dimensional display using two-photon upconversion|
|US5956172||Nov 3, 1997||Sep 21, 1999||3D Technology Laboratories, Inc.||System and method using layered structure for three-dimensional display of information based on two-photon upconversion|
|US5985990||Dec 29, 1995||Nov 16, 1999||3M Innovative Properties Company||Use of pendant free-radically polymerizable moieties with polar polymers to prepare hydrophilic pressure sensitive adhesive compositions|
|US5989799||Jun 18, 1998||Nov 23, 1999||Agfa-Gevaert. N.V.||Radiographic UV/blue intensifying screen-film combination|
|US6028977 *||Nov 8, 1996||Feb 22, 2000||Moriah Technologies, Inc.||All-optical, flat-panel display system|
|US6061179||Jan 22, 1997||May 9, 2000||Canon Kabushiki Kaisha||Stereoscopic image display apparatus with two-/three-dimensional image display switching function|
|US6117529||Dec 18, 1996||Sep 12, 2000||Gunther Leising||Organic electroluminescence devices and displays|
|US6128131||Nov 13, 1997||Oct 3, 2000||Eastman Kodak Company||Scaleable tiled flat-panel projection color display|
|US6276801||Aug 2, 1995||Aug 21, 2001||Digital Projection Limited||Display system|
|US6327074||Nov 24, 1999||Dec 4, 2001||University Of Central Florida||Display medium using emitting particles dispersed in a transparent host|
|US6501590||Oct 12, 2001||Dec 31, 2002||University Of Central Florida||Display medium using emitting particles dispersed in a transparent host|
|US6654161||Jul 31, 2001||Nov 25, 2003||University Of Central Florida||Dispersed crystallite up-conversion displays|
|US6844387||Jul 31, 2001||Jan 18, 2005||University Of Central Florida||Composites of inorganic luminophores stabilized in polymer hosts|
|US6897999||Dec 26, 2002||May 24, 2005||The Research Foundation Of The University Of Central Florida||Optically written display|
|US7075707||May 7, 2004||Jul 11, 2006||Research Foundation Of The University Of Central Florida, Incorporated||Substrate design for optimized performance of up-conversion phosphors utilizing proper thermal management|
|US7101061||Oct 17, 2003||Sep 5, 2006||Matsushita Electric Industrial Co., Ltd.||Light emission apparatus|
|US20040129946 *||Oct 17, 2003||Jul 8, 2004||Hideo Nagai||Light emission apparatus|
|1||Kaminskii, "Laser Crystals," Springer Series in Optical Sciences, Jan. 1, 1981, 14, pp. 170-311.|
|U.S. Classification||359/326, 365/151|
|International Classification||G02F1/355, G11C13/04|
|Cooperative Classification||C09K11/7774, C09K11/7776, C09K11/7706, C09K11/7778, C09K11/7772, C09K11/7773, C09K11/7711, C09K11/7758, G02F2/02, C09K11/7769, C09K11/7705, C09K11/616, C09K11/602, C09K11/7757, C09K11/7766|
|European Classification||C09K11/77D, C09K11/77S4B, G02F2/02, C09K11/77S4, C09K11/77G2B, C09K11/77S2H, C09K11/77S8, C09K11/61C2, C09K11/60B, C09K11/77Q6, C09K11/77S, C09K11/77S10B, C09K11/77S6, C09K11/77C2, C09K11/77Q4|
|Aug 14, 2012||CC||Certificate of correction|
|Dec 30, 2013||FPAY||Fee payment|
Year of fee payment: 8