WO1989012714A1 - Catalysts and processes for formaldehyde-free durable press finishing of cotton textiles with polycarboxylic acids - Google Patents

Catalysts and processes for formaldehyde-free durable press finishing of cotton textiles with polycarboxylic acids Download PDF

Info

Publication number
WO1989012714A1
WO1989012714A1 PCT/US1989/002628 US8902628W WO8912714A1 WO 1989012714 A1 WO1989012714 A1 WO 1989012714A1 US 8902628 W US8902628 W US 8902628W WO 8912714 A1 WO8912714 A1 WO 8912714A1
Authority
WO
WIPO (PCT)
Prior art keywords
acid
group
acids
carboxyl
fabric
Prior art date
Application number
PCT/US1989/002628
Other languages
French (fr)
Inventor
Clark M. Welch
Bethlehem K. Andrews
Original Assignee
The United States Of America, As Represented By Th
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from US07/207,461 external-priority patent/US4820307A/en
Application filed by The United States Of America, As Represented By Th filed Critical The United States Of America, As Represented By Th
Priority to KR1019900700321A priority Critical patent/KR930005933B1/en
Priority to JP1507149A priority patent/JPH0726321B2/en
Publication of WO1989012714A1 publication Critical patent/WO1989012714A1/en

Abstract

Catalysts for the rapid esterification and crosslinking of fibrous cellulose in textile form by polycarboxylic acids at elevated temperatures are disclosed. The catalysts are acidic or weakly basic salts selected from the alkali metal salts of phosphorous, hypophosphorous, and polyphosphoric acids. Suitable polycarboxylic acids include saturated, unsaturated and aromatic acids, as well as alpha-hydroxy acids. The textiles so treated exhibit high levels of wrinkle resistance and smooth drying properties durable to repeated laundering in alkaline detergents, and do not contain or release formaldehyde.

Description

-I'
CATALYSTS AND PROCESSES FOR FORMALDEHYDE-FREE
DURABLE PRESS FINISHING OF COTTON TEXTILES
WITH POLYCARBOXYLIC ACIDS
BACKGROUND OF THE INVENTION This invention relates to new esterification cata¬ lysts and esterification processes for crosslinking cellulose as a means of imparting wrinkle resistance and smooth drying properties to cellulosic textiles without the use of formaldehyde or derivatives that release for-
10 aldehyde.
There are numerous commercial processes for imparting wrinkle resistance, shrinkage resistance and smooth dry¬ ing properties to cotton fabrics and garments, so that they retain their dimensions, smooth appearance and
" normal shape while in use and also when machine washed and tumble dried. In most of these processes, formalde¬ hyde or an addition product of formaldehyde is applied to the cotton textile together with an acid catalyst, and heat is then applied to produce crosslinking of the 0 cotton cellulose molecules.
The crosslinks thus formed in the cellulose impart to the fabric a tendency to return to its original shape and smoothness when deformed by mechanical forces temporarily exerted on the fabric during its use or during laundering
25 and tumble drying.
Formaldehyde addition products with urea, cyclic ureas, carbamate esters or with other amides are widely used crosslinking agents for durable press finishing, as the above wrinkle resistant, smooth drying treatments are
-0 called. The formaldehyde addition products, also known as N-methylol agents or N-methylolamides, are effective and inexpensive, but have serious disadvantages. They continuously release vapors of formaldehyde during durable press finishing of cotton fabric, subsequent
^ storage of the treated fabric, manufacture of the result¬ ing garment, retailing of the garment, and finally during use of the garment or textile by the consumer. The irritating effect of formaldehyde vapor on the eyes and skin is a marked disadvantage of such finishes, but more serious is the knowledge that formaldehyde is a carci¬ nogen to animals and apparently also to humans con¬ tinuously exposed to formaldehyde vapor for very long periods. A need is evident for durable press finishing agents and processes that do not require formaldehyde or its unstable derivatives.
Another disadvantage of the use of N-methylol agents in durable press treatments is that Lewis acid catalysts and high temperatures are required to bring about suf- ficiently rapid crosslinking of the cotton cellulose by such finishing agents. The Lewis acid catalysts cause undesirable losses of breaking and tearing strength in cotton fabric during the heat curing step. The strength losses are due to degradation of cellulose molecules by the Lewis acid catalysts at elevated temperature. Such strength losses occur over and above the adverse effects on strength of the crosslinkages produced in the cellu¬ lose. An added disadvantage of certain nitrogenous finishes is their tendency to retain chlorine from chlorine bleaches, with resultant fabric discoloration and strength loss if subsequently given a touch-up iron¬ ing.
The use of polycarboxylic acids with or without catalysts in pad, dry and cure treatments to impart wrinkle resistance to cotton fabric was studied by
Gagliardi and Shippee, American Dyestuff Reporter 52,
P300-P303 (1963). They observed small increases in fabric wrinkle resistance after relatively long periods of heating, and noted larger fabric strength losses than are obtained with formaldehyde-based crosslinking agents. These excessive strength losses and the low yield of crosslinkages were attributed to the long heat curing times needed with the inefficient catalysts then available. ^ more rapid and effective curing process for introducing ester crosslinks into cotton cellulose was described by Rowland _et_ al, Textile Research Journal 37, 933-941 (1967). Polycarboxylic acids were partially neutralized with sodium carbonate or triethylamine prior to application to the fabric in a pad, dry and heat cure type of treatment. Crosslinking of cellulose was obtained whenever the polycarboxylic acid contained three or more carboxyl groups suitably located in each mole¬ cule. With certain polycarboxylic acids, a useful level of wrinkle resistance was imparted. The conditioned wrinkle recovery angle was measured before and after five laundering cycles, and was found to decrease somewhat as a result of laundering, even though no loss of ester groups was detected. Neutralization of carboxyl groups with 2% sodium carbonate even at room temperature caused a 30% loss of ester groups. This indicates a lack of durability of the finish to alkaline solutions such as solutions of alkaline laundering detergents. The curing time needed in fabric finishing was moreover too long to permit high speed, mill-scale production.
Subsequently it ws shown by Rowland and Brannan, Textile Research Journal 38, 634-643 (1968), that cotton fabrics given the above cellulose crosslinking treatment with polycarboxylic acids were recurable. Creases durable to 5 laundering cycles could be put into the fabrics by wetting the latter, folding, and applying a heated iron. Evidence was obtained that the ester cross- linkages are mobile under the influence of heat, due to a transesterification reaction taking place between ester groups and adjacent unesterified hydroxyl groups on cotton cellulose. These findings were elaborated by Rowland et al, U.S. Patent No. 3,526,048. Sodium carbonate or triethylamine were again the examples of bases used to partially neutralize the polycarboxylic acid subsequently applied as the cellulose crosslinking agent. Rowland et_ _al_ defined their process as requiring neutralization of 1% to 50% of all carboxylic acid functionality by a "strong base" selected from the group consisting of alkali metal hydroxides, carbonates, bicarbonates, acetates, phos¬ phates and borates, prior to impregnating the fibrous cellulose with the aqueous polycarboxylic acid and heat¬ ing to induce crosslinking. A strong base selected from the group consisting of ammonia and certain amines also was indicated as suitable for the partial neutralization of the polycarboxylic acid.
Stated limitations of the process of Rowland et al are that the process cannot be conducted with acids of fewer than three carboxyl groups per molecule, or with acids containing olefinic unsaturation or hydroxyl groups. The reasons were lack of reaction with cellulose and lack of effective crosslinking of cellulose chains for development of high levels of wrinkle resistance. The limited durability of the finishes noted above was also a disadvantage, and the time required for complete curing was too long to permit practical rates of cloth finishing.
SUMMARY OF THE INVENTION This invention provides rapid processes for durably imparting to fibrous cellulosic material, such as cotton and other cellulosic textiles, a high level of wrinkle resistance and smooth drying properties by means of non- nitrogenous cellulose crosslinking agents, without the use of formaldehyde or derivatives that release formalde¬ hyde, and with less loss of tearing strength and breaking strength than produced by conventional N-methylolamides.
The present invention comprises reacting a poly¬ carboxylic acid with the fibrous cellulosic material in the presence of a particular curing catalyst at elevated temperature. The material is impregnated with a treating solution containing the polycarboxylic acid and the curing catalyst after which the material is heat cured to produce esterification and crosslinking of the cellulose with the polycarboxylic acid. In a preferred embodiment, the process is carried out as a pad, dry and heat cure procedure with the drying and heat curing done either consecutively or simultaneously.
Curing catalysts suitable for this process are alkali metal salts of . phosphorus-containing acids which include phosphorous acid, hypophosphorous acid, and polyphoε- phoric acids. Most of the curing catalysts are weak bases, since they are alkali metal salts of acids stronger than ortho-phosphoric acid.
Polycarboxylic acids suitable as cellulose cross¬ linking agents for the process of the present invention are aliphatic, alicyclic and aromatic acids which contain at least three and preferably more carboxyl groups per molecule and are either olefinically saturated or unsatu¬ rated, or aliphatic, alicyclic and aromatic acids having two carboxyl groups per molecule with a carbon-carbon double bond present alpha, beta to one or both carboxyl groups. In the case of aliphatic and alicyclic acids, at least two of the carboxyl groups must be separated by only 2 to 3 carbon atoms on the chain or ring. In the case of aromatic acids, a carboxyl group must be ortho to second carboxyl group. Also suitable are aliphatic acids containing three or more carboxyl groups per molecule and having a hydroxyl group present on a carbon atom attached to one of the carboxyl groups.
An object of the present invention is to provide a process for improving the wrinkle resistance, shrinkage resistance and smooth drying properties of cellulosic fiber-containing textiles without the use of formaldehyde or agents that release formaldehyde.
A second object of the present invention is to pro- vide a non-nitrogenous durable press finish for cellu¬ losic fiber textiles in which the level of smooth drying performance, wrinkle resistance and shrinkage resistance imparted is comparable to that obtained with nitrogenous durable press finishing agents such as N-methylol agents. A third object of the present invention is to provide a durable press process producing less tearing and break¬ ing strength loss in the cellulosic textile than is produced by an *L-methylol agent at a given level of wrinkle resistance and durable press performance imparted.
A fourth object is to provide a wrinkle resistant and smooth drying fabric of polycarboxylic acid-esterified cellulosic fiber, such as cotton, that retains its durable press properties after repeated laundering with alkaline detergents at elevated wash temperatures.
A fifth object is to provide esterification catalysts giving sufficiently rapid esterification and crosslinking of cellulosic fiber by polycarboxylic acids to permit practical rates of durable press finishing of cellulosic fiber-containing fabrics at cure temperatures below the scorch temperature of the cellulose. A sixth object is to provide odor-free durable press finishes for cellulosic fiber-containing fabric that also impart thermal recurability, soil release properties and an affinity for basic or cationic dyes to the cellulosic fabric. DESCRIPTION OF THE PREFERRED EMBODIMENTS
The present invention is applicable to fibrous cellu¬ losic material containing not less than 30% by weight of cellulosic fibers including cotton, flax, jute, hemp, ramie and regenerated unsubstituted wood celluloses such as rayon. The disclosed process may be applied to fibrous cellulosic material in the form of woven and non- woven textiles such as yarns and woven or knit fabrics, and to fibers, linters, roving, slivers, or paper. The disclosed process is most advantageous with textiles containing 50%-100% cotton.
The present invention is based on the discovery that several classes of alkali metal salts of phosphorus- containing acids have a greater accelerating effect on the esterification and crosslinking of cellulose by polycarboxylic acids than is produced by the strong base catalysts used in prior art processes. Since the curing catalysts of the present invention are in most instances weak bases or even acidic salts, their greater effect in speeding the desired crosslinking of the cellulose in a fabric indicates new mechanisms of catalysis, which are not operative in the simple neutralization of a portion of the carboxyl groups of the polycarboxylic acid by a strong base acting as a buffering agent. Moreover the greater laundering durability of the fabric finishes of the present invention also demonstrates the operation of new principles. The most active and effective curing catalysts of this invention are alkali metal hypophosphites, which in anhydrous form have the formula MH2PO2 where M is an alkali metal atom. The mechanism of the catalysis is unknown. It is hypothesized that during the heat cure, the polycarboxylic acid forms cyclic anhydrides which then add to the alkali metal hypophosphite to form acylphosphinates, (H00C)xR[C(0)P(0)(H)0M]x where X is an integer from 1 to 3 equal to the number of cyclic anhy¬ dride rings that have formed and reacted with the alkali metal hypophosphite, and R represents the structure of the polycarboxylic acid molecule joined to the anhydride rings transitorily formed. The hypothetical acylphosphi¬ nates so formed may react with cellulose to yield the desired crosslinked esters of the polycarboxylic acid, and regenerate the alkali hypophosphite catalyst.
Experimentally it is found that the catalyst is effective at concentrations as low as 0.3% by weight in a treating bath, but the durability of the finish is great¬ est at higher concentrations. A concentration range of 0.3%-ll% is operable.
The weight gains of the fibrous cellulosic material are larger than accounted for by the polycarboxylic acid and any auxiliary agents such as fabric softeners that are applied. It is evident some of the curing agent is bound to the cellulose.
The alkali metal hypophosphites are effective even with a crosslinking agent such as maleic acid which has only two carboxyl groups per molecule. It is possible two molecules of maleic acid add to one molecule of alkali metal hypophosphite to yield a tetracarboxylic acid that is the actual cellulose crosslinking agent. A second class of curing catalysts employed in the present invention are alkali metal phosphites having the formula H2 O3 and M2HPO3. These are nearly as active as alkali metal hypophosphites, but the durable press finishes obtained by their use are slightly less durable to laundering. Their mode of action is not known, but it is possible the polycarboxylic acid on heat curing forms cyclic anhydrides which may react with the alkali metal phosphites to form acylphosphonates (H00C)xR[C(0)P(0)- (0H)0M]x and (H00C)xR[C(0)P(0)(0M)2]x where X and R are defined as above, and X has integral values of 1-3. The hypothetical intermediate so formed may react with cellu¬ lose to form the desired crosslinked esters of the poly¬ carboxylic acid, and regenerate the alkali metal phosphite catalyst. The concentrations of alkali metal phosphites effec¬ tive in accelerating the desired cellulose crosslinking are in the range of 0.3%-ll% by weight in the treating solution. For dibasic phosphite salts, however, it is preferable that the molar concentration of the catalyst does not exceed 65% of the normality of the poly¬ carboxylic acid in the treating bath used to impregnate the cellulosic fiber-containing material.
A third class of curing catalysts employed in the processes of the present invention are the alkali metal salts of polyphosphoric acids. These are condensed phos¬ phoric acids and encompass the cyclic oligomers trimetha- phosphoric acid and tetrametaphosphoric acid, and acyclic polyphosphoric acids containing 2 to 50 phosphorus atoms per molecule including pyrophosphoric acid. Specific examples of effective catalysts in this class are disodium acid pyrophosphate , tetrasodium pyrophosphate, pentasodium tripolyphosphate, the acyclic polymer known as sodium hexa etaphosphate, and the cyclic oligomers sodium trimetaphosphate and sodium tetrametaphosphate. These catalyts lead to finishes having the same initial durable press performance as the most effective prior art catalysts, but with greater durability to repeated laundering of the treated textile with alkaline detergents. The catalyst normality as a base should preferably not exceed 80% of the normality of the poly¬ carboxylic acid in the treating bath. Effective catalyst concentrations fall in the range of 0.3-11% by weight in the treating bath.
The mechanism of the curing action of alkali metal salts of condensed phosphoric acids is not known, but it is proposed here that such salts, being in all cases the salts of anhydrides of orthophosphoric acid, have the ability to react at elevated temperature with the poly¬ carboxylic acid used as the cellulose crosslinking agent, to form mixed carboxylic-phosphoric or carboxylic- polyphosphoric anhydrides which subsequently react with cellulose to form the desired crosslinked ester of the polycarboxylic acid with the cellulose of the fibrous material, along with a moderate amount of phosphorylated cellulose as a co-product. The latter in the form of the alkali metal salt is anionic, and would result in a greater negative charge in the substituted cellulose. This negative charge would repel negatively charged anions of the alkaline detergent as well as any hydroxyl ions present, thereby decreasing the rate of alkaline hydrolysis of the ester crosslinks during laundering. The processes of the present invention are carried out by first impregnating the fibrous cellulosic material with a treating solution containing the polycarboxylic acid, the curing catalyst, a solvent and optionally a fabric softener. This may be done, for example, by immersing the material in a bath of the treating solu¬ tion. The solvent used to prepare the treating solution is preferably water, although any inert volatile solvent in which the polycarboxylic acid and curing catalyst are soluble or uniformly dispersible can be used. The fabric softener, if present, should be an inert, emulsified nonionic or anionic material such as the usual nonionic polyethylene, polypropylene, or silicone softeners. After being thoroughly wet in the treating bath, the cellulosic material is passed between squeeze rolls to remove excess liquid, and is then oven-dried at any con¬ venient temperature just sufficient to remove the solvent within the desired time. The material is then oven-cured at 150-240°C for 5 seconds to 30 minutes to cause cellu¬ lose esterification and crosslinking to occur. Alterna¬ tively the above drying step may be omitted, and the material can be "flash-cured" to remove solvent at the same time that cellulose esterification and crosslinking take place. If desired, the cured material may subse¬ quently be given a water rinse to remove unreacted reagent and curing catalyst, and may then be redried.
The polycarboxylic acids effective as cellulose crosslinking agents in the processes of this invention include aliphatic, alicyclic and aromatic acids either olefinically saturated or unsaturated with at least three and preferably more carboxyl groups per molecule or with two carboxyl groups per molecule if a carbon-carbon double bond is present alpha, beta to one or both carboxyl groups. An additional requirement is that to be reactive in esterifying cellulose hydroxyl groups, a given carboxyl group in an aliphatic or alicyclic poly¬ carboxylic acid must be separated from a second carboxyl group by no less than 2 carbon atoms and no more than three carbon atoms. In an aromatic acid, a carboxyl group must be ortho to a second carboxyl group if the first carboxyl is to be effective in esterifying cellu¬ losic hydroxyl groups. It appears from these require- ments that for a carboxyl group to be reactive, it must be able to form a cyclic 5-or 6-membered anhydride ring with a neighboring carboxyl group in the polycarboxylic acid molecule. Where two carboxyl groups are separated by a carbon-carbon double bond or are both connected to the same ring, .the two carboxyl groups must be in the cis configuration relative to each other if they are to interact in this manner.
The aliphatic or alicyclic polycarboxylic acid may also contain an oxygen or sulfur atom in the chain or ring to which the carboxyl groups are attached.
In aliphatic acids containing three or more carboxyl groups per molecule, a hydroxyl group attached to a carbon atom alpha to a carboxyl group does not interfere with the esterification and crosslinking of cellulose by the acid, although the presence of the hydroxyl group causes a noticeable yellowing of the material during the heat cure. Such an aIpha-hydroxy acid is suitable for durable press finishing of suitably dyed cotton fabric, since the color of the dye conceals the discoloration caused by the hydroxyl group. Fabric discoloration is similarly observed with an unsaturated acid having an olefinic double bond that is not only alpha, beta to one carboxyl group but also beta, gamma to a second carboxyl group.
The discoloration produced in a white cellulosic material by crosslinking it with an alpha-hydroxy acid such as citric acid can be removed by impregnating the discolored material with an aqueous solution containing from 0.5% to 5% by weight of a decolorizing agent selected from the group consisting of magnesium mono- peroxyphthalate, sodium perborate, sodium tetraborate, boric acid, sodium borohydride, sodium hypochlorite, and hydrogen chloride. The material is immersed in the solu¬ tion of decolorizing agent and soaked for 5 to 120 minutes at ambient temperature or if necessary in such a solution warmed to a temperature not exceeding 60°C. The material is subsequently rinsed with water to remove excess chemicals and solubilized colored products, and then is dried. Examples of specific polycarboxylic acids which fall within the scope of this invention are the following: maleic acid; citraconic acid also called methylmaleic acid; citric acid also known as 2-hydroxy-l,2r3-propane- tricarboxylic acid; itaconic acid also called methylene- succinic acid; tricarballylic acid also known as 1,2,3- propanetricarboxylic acid; trans-aconitic acid also known as trans-l-propene-1,2,3-tricarboxylic acid; 1,2,3,4- butanetetracarboxylic acid; all-cis-1,2,3,4-cvclopentane- tetracarboxylic acid; ellitic acid also known as ben- zenehexacarboxylic acid; oxydisuccinic acid also known as 2,2'-oxybis(butanedioic acid); thiodisuccinic acid; and the like.
The concentration of polycarboxylic acid used in the treating solution may be in the range of 1% to 20% by weight depending on the solubility of the polycarboxylic acid and the degree of cellulose crosslinking required as determined by the level of wrinkle resistance, smooth drying properties and shrinkage resistance desired. In the examples to be given, the properties of the treated fabrics were measured by standard test methods, which were as follows: conditioned and wet wrinkle recovery angle-ASTM method D-1295-67, Elmendorf tearing strength-ASTM Method D-1424-63, strip breaking strength- ASTM Method D-1682-64, stiffness by the Tinius 01sen
Method (Federal Test 191, Method 5202) r durable press appearance ratings-AATCC Method 124-1967. The machine launderings were at a wash temperature of 50°C. The pH of the wash water was 9.8 due to use of standard AATCC detergent. Thus the laundering was at high alkalinity in order to test the durability to alkaline detergent of the durable press finishes of this invention.
In the following examples, all parts and percentages are by weight. The examples are only illustrative of the processes of the present invention. Changes and modifications in the specifically described embodiments can be carried out without departing from the scope of the invention which is intended to be limited only by the scope of the claims.
Example 1
Sodium Hypophosphite as a Curing Catalyst for the Durable Press Finishing of Cotton Fabric with 1,2,3,4-Butanetetracarboxylic Acid
An aqueous treating bath was prepared containing 6.3% by weight of 1,2,3,4-butanetetracarboxylic acid, a speci¬ fied concentration of sodium hypophosphite monohydrate as curing catalyst, and 1% emulsified nonionic polyethylene which served as a fabric softener. An all-cotton desized, scoured and bleached 80x80 printcloth weighing 3.2 oz/yd was thoroughly wetted by immersion in this treating bath, was passed between the rolls of a wringer, was again immersed in the treating bath, and was again passed through the wringer, the pressure of the wringer rolls being sufficient to give a wet pickup of 116%-134% of aqueous mixture on the fabric, based on the original weight of fabric sample. The fabric was then dried in a forced draft oven at 85°C for 5 minutes, and was heat-cured in a second forced draft oven at a specified temperature for a stated time. The fabric was subsequently rinsed for 30 minutes in hot running water to remove any unreacted agents, and Was oven dried at 85°C for 5 minutes.
The durable press appearance rating of the treated fabric after one machine laundering and tumble drying cycle was determined as a function of the curing temper¬ ature and time, as well as the concentration of sodium hypophosphite monohydrate used. The results appear in Table I. Table I
Dura¬
Cone. Fabric ble Fabric Color
NaH2P02.H20 Cure Cure Weight Press Before After
Catalyst Temp. Time Gain Rating Rinse Rinse
0.0% 180°C 90sec. 7.8% 2.9 pale faint tan tan
0.4 180 90 10.0 4.1 pale faint tan yellow
0.8 180 90 9.3 4.4 faint white yellow
1.6 180 90 9.9 4.6 off- white white
3.3 180 90 9.9 4.8 white white
6.5 180 90 12.1 4.5 white white
6.5 180 90 9.9 4.7 white white
6.5 180 45 11.8 4.6 white white
6.5 180 30 10.8 4.1 white white
6.5 195 30 11.1 4.6 white white
DMDHEUb 160 180 7.3 4.6 off- off- white white
6.5C 180 90 0.9 1.8 white white
Untreated fabric 1.5 white white
a No polyethylene present as fabric softener in this run.
A treating bath containing 6% dimethyloldihydroxy- ethyleneurea as the cellulose crosslinking agent, 1.5% MgCl2-6H2θ as catalyst, and 1.0% polyethylene was used in this run. c The treating bath contained sodium hypophosphite and polyethylene but no 1,2,3,4-butanetetracarboxylic acid.
Fibers were removed from cotton fabric which had been treated as above with 6.3% 1,2,3,4-butanetetracarboxylic acid and 6.5% sodium hypophosphite monohydrate with heat curing at 180° for 90 seconds. The fibers were complete¬ ly insoluble in 1.0M aqueous cupriethylenediamine hydroxide solution even after 1 hour. Fibers from untreated fabric dissolved within 30 seconds in this solution. The results show the cotton cellulose was highly crosslinked after being heat-cured with 1,2,3,4- butanetetracarboxylic acid and the sodium hypophosphite catalyst. The same positive test for crosslinking was obtained after the heat cure when 1% emulsified poly¬ ethylene was also present with the butanetetracarboxylic acid and sodium hypophosphite used to treat the fabric.
A number of textile properties were measured on the treated fabric samples prior to machine laundering, and are compared in Table II.
TABLE II
Stiff¬
WnrikQe Warp Warp ness,
Cone. Recovery Tear Break Bending
NaH2P02-H AnqtefW+F) Strength Strength Moment Catalyst ° , Cure Cond. Wet Retained Retained (Warp)
6.5 % 180°/90sec 300° 268° 60 % 54 % 5.8xl0"4in.-_lb.
6.5 180/45 293 267 58 57 4.3
6.5 195/30 288 276 54 59 4.3
DMDHEUa 160/180 303 271 54 44 4.2
Untreated fabric 200 141 (100) (100) 4.8
a The treating bath contained 6% dimethyloldihydroxy- ethyleneurea, 1.5% MgCl2.6H20 and 1.0% polyethylene in place of butanetetracarboxylic acid, sodium hypo¬ phosphite and polyethylene.
The data show that sodium hypophosphite induced very fast curing reactions of 1,2,3,4-butanetetracarboxylic acid with cotton to impart essentially the same durable press appearance ratings and wrinkle recovery angles to fabric as a conventional finishing agent, DMDHEU, and did so with less breaking and tearing strength loss in the fabric then did the conventional agent. Other properties of the two finishes were comparable. Example 2
Comparison of Sodium Hypophosphite and
Disodium Phosphite with other Catalysts for Durable Press Finishing of Cotton
Fabric with 1,2,3,4-Butanetetracarboxylic Acid
An aqueous treating bath was prepared containing 6.3% by weight of 1,2,3,4-butanetetracarboxylic acid, a speci¬ fied catalyst, and 1% emulsified nonionic polyethylene which served as a fabric softener. An all-cotton 0 desized, scoured and bleached 80x80 printcloth weighing 3.2 oz/yd was treated with this mixture by the procedure of Example 1. The heat cure was at 180°C for 90 seconds . After the final 30 minute water rinse and oven drying, the treated fabric samples were repeatedly
^ machine washed and tumble dried, and durable press appearance ratings were determined after a specified number of wash-and-tumble dry cycles. The ratings appear in Table III as a function of the number of cycles carried out and the type of catalyst used.
20 Table III
Catalyst Durable Press Appearance Rating Normal- After Repeated Washing and Curing ity As No. Tumble Drying Cycles Catalyst a Base3 Cycles: (1) (5) (20) (30) (35) (40) (65)
25
6.5% NaH2 P02*H2° °'61 4.5 4.4 4.6 4.5 4.5 equiv./ liter
6.6% Na2HP03.5H200.61 4.5 4.2 4.0 4.3 4.1 4.0
4.4% Na2HP0 0.62 4.2 4.0 3.8 3.7 3.4 3.6
30 7.7% Na3P04.12H200.61 3.8
5.8% Na3P04.12H200.46 4.3 3.9 3.9 3.8 3.5 3.5 3.6
2.9% Na3P04.12H200.23 4.0 3.9
3.3% Na2C03 0.60 2.9 2.8 3.2 2.9
1.6% Na C03 0.30 3.8 3.7 3.5 3.7 3.4 3.5 3.5
35 0.8% Na2C03 0.15 4.0 3.7
Numerically equal to the concentration of sodium ions available from the catalyst, in gram-ion/liter. The normality of 1,2,3,4-butanetetracarboxylic acid was 1.08 equiv./liter in the treating bath. The data show that the use of the sodium hypophos¬ phite and disodium phosphite catalysts of the present invention resulted in higher initial durable press appearance ratings, and greater durability of the smooth drying finish to repeated laundering, than was obtained with strongly alkaline trisodium phosphate and sodium carbonate catalysts. This was true when the catalysts were compared at the same normality as bases, and also when compared at the concentrations of maximum effective- ness. The teaching of Rowland et al., that the effec¬ tiveness of a given alkali metal salt as a curing agent for this type of cellulose crosslinking depends solely on the salt being a "strong base capable of forming a soluble, partial salt of polybasic acid in an effective concentration", proved inapplicable to sodium hypophos¬ phite. The latter is a very weak base derived from an acid much stronger than 1,2,3,4-butanetetracarboxylic acid, and is relatively ineffective in forming the partial sodium salts of 1,2,3,4-butanetetracarboxylic acid. The importance of catalyst structure rather than catalyst basicity is also evident in comparing disodium phosphite and disodium phosphate, the former being the more effective catalyst, even though appreciably less alkaline than the latter. Example 3
Comparison of Various Polycarboxylic Acids as Durable Press Finishing Agents for Cotton
Fabric with Sodium Hypophosphite or Disodium
Phosphite as the Curing Catalyst An aqueous treating bath was prepared containing a specified concentration of a given polycarboxylic acid, a stated catalyst, and 1% emulsified nonionic polyethylene which served as a fabric softener. An all-cotton desized, scoured and bleached 80x80 printcloth weighing 3.2 oz/yd2 was thoroughly wetted by immersion in this treating bath, was passed between the rolls of a wringer, was again immersed in the treating bath, and was again passed through the wringer, the pressure of the wringer rolls being sufficient to give a wet pickup of 112%-126% of aqueous mixture on the fabric, based on the original weight of fabric sample.
The fabric was then dried in a forced draft oven at 85°C for 5 minutes, and was heat-cured in a second forced draft oven at 180°C for 90 seconds. The fabric was sub¬ sequently rinsed for 30 minutes in hot running water to remove any unreacted agents, and was oven dried at 85°C for 5 minutes.
The durable press appearance ratings were determined after varying numbers of machine wash-and-tumble dry cycles, and are shown in Table IV as a function of the particular polycarboxylic acid and catalyst used.
Table IV
Durable Press Ratings
Poly¬ Fabric After Multiple carboxylic Weight No. Laundering Cycles Acid Catalyst Gain Cycles: (1) (5) (10) (20) (30)
9.5% 1,2,3- propanetri- 6.5% 11.0% 4.6 4.7 4.4 4.6 4.6 carbosylic NaH2P02. H20 acida
6.6% 13.2 4.4 3.9 3.8 3.7 3.6
Figure imgf000020_0001
7.7% 12.4 3.9
Na3P04.12H20
3.3% 11.0 3.7
Na2C03
1.6% 12.5 3.9
Na2C03
0.8% 10.6 3.6
Na2003
None 7.1 2.2
10.4% 6.5% citric NaH2P02. H20 12.3 4.7 4.5 4.0 3.8 3.7 Acid
4.4% 12.9 3.5 3.4
Figure imgf000020_0002
5.8% 12.0 3.5 3.5
Na3P0412H20 Table IV (Continued)
4.0% 13.9 3.5
Na3C6H507.2H2O
None 8.3 2.7
5 9.4% 2.9% 9.5 4.3 4.3 4.0 3.9 3.5 trans-1- NaH2P02.H20 prσpene-
1,2,3-tri- None 5.7 3.3
, - carboxylic 10 acidc
6.3% 2.9% 10.7 3.4 3.5 3.0 maleic Acid NaH2P02.H20
None 4.3 2.8 10.0 4.6 4.6 4.4 4.6 4.6
11.4 4.4 3.8 4.0 3.6 3.6
Figure imgf000021_0001
8.7 2.7
7.2% 6.5% 11.0 4.4 4.7 thiodisuc- NaH2P02.H2θ cinic acid
None 7.1 2.9 5 g.2% 6.5% 10.9 4.4 4.3 4.4 benzene- aH2P02. H2O hexa- carbgxylic None 11.0 3.7 4.0 3.0 acidd 0 6% DMDHEU*5 7.3 4.6 4.7 4.8 4.8 4.8
Untreated fabric 1.5 1.4 1.4 1.6 1.5
a Tricarballylic acid is the common name of this acid . b Trisodium citrate dihydrate . 5 c trans-Aconitic acid is the common name of this acid .
Mellitic Acid is the common name of this acid . e Same run with dimethyloldihydroxyethyleneurea as in
Tables I and II .
Other textile properties of certain of the above 0 treated fabrics were determined prior to machine laundering, and are shown in Table V. The curing catalyst was 6.5% sodium hypophosphite monohydrate in these runs . Table V
Warp Warp Stiffness,
Wrinkle Recovery Tear Break Bending
Polycarboxylic Angle (W+F) Strength Strength M-nient Acid Cond. Wet Retained Retained (Warp)
9.5% 1,2,3-pro- 300° 274° 61% 57% 5.3xl0"4in.-lb. panetricarbαxylic acid
10.4% citric 295 251 62 56 4.8 acida
9.4% trans-1- 296 238 72 58 3.9 ptopene—1r2,3— tricarboxylic acidb
6.3% all-cis- 298 262 68 54 4.9 1,2,3,4-cyclo- pentanetetra- carbcxylic acid
6% DMDHEU0 303 271 54 44 4.2
Untreated fabric 200 141 (100) (100) 4.8
The treated fabric had a light yellow discoloration after the hot water rinse. The durble press rating was 4.7 with or without polyethylene softener. k This agent caused a deep yellow discoloration in the rinsed fabric. ε Same run with dimethyloldihydroxyethyleneurea as in Tables I and II.
The data show aliphatic, alicyclic and aromatic poly¬ carboxylic acids having 2-6 carboxyl groups per molecule impart wrinkle resistance and smooth drying properties to cotton fabric when heat cured on the fabric in the presence of an alkali metal phosphite or hypophosphite as a curing catalyst. The polycarboxylic acid used may also contain a carbon-carbon double bond or a hydroxyl group on a carbon atom attached to a carboxyl group in the molecule without eliminating the effectiveness in impart¬ ing durable press properties. The appearance of a yellow discoloration in white fabric treated with polycarboxylic acids containing a double bond or hydroxyl group can be concealed by afterdyeing the fabric with a basic dye, or by the use of fabric suitably dyed prior to treatment. A carboxyalkylthio substituent on a carbon atom attached to a carboxyl group in the polycarboxylic acid had no adverse effect on fabric whiteness, and was beneficial to the smooth drying properties. The use of polycarboxylic acids as durable press finishing agents with sodium hypophosphite as the curing agent resulted in durable press appearance ratings and conditioned wrinkle recovery angles comparable to those imparted by the conventional durable press finishing agent. DMDHEU, but with consistently less loss of tear¬ ing and breaking strength than was produced by DMDHEU.
Example 4
Polyphosphate Salts as Curing Catalysts for the Durable Press Finishing of Cotton Fabric with 1,2,3,4-Butanetetracarboxylic Acid
An all-cotton desized, scoured and bleached 80x80 printcloth weighing 3.2 oz/yd2 was treated as in Example
1, except that in place of sodium hypophosphite, an alkali metal polyphosphate was used as the curing cata¬ lyst. The heat cure was at 180°C for 90 seconds.
The durable press appearance rating of the treated fabric was determined as a function of the curing catalyst and the number of laundering cycles carried out on the treated sample. The results are given in Table VI. Runs with disodium phosphate, trisodium phosphate and sodium carbonate as catalysts are included for comparison.
Table VE
Catalyst Durable Press Ratings Nor¬ Fabric After Multiple
Curing mality3 Weight No. laundering Cycles Catalyst As a Base Gain Cycles: (1) (30) (40) (50)
0.31 equiv/liter 12.0% 4.4 3.8 3.9 3.9
Figure imgf000024_0001
4.1% 0.62 11.8 4.3 3.9 3.8 4.0 Na^O 0
0.76 12.2 4.3 3.9 3.8 4.0
Figure imgf000024_0002
4.1%/ 0.40 10.6 4.3 4.0 3.9 (NaP03)6 e
6.3% 0.62 11.1 4.3 3.9 4.0 (NaP03)6 t
4.4% 0.62 12.0 4.2 3.7 3.4 3.5
0.61 10.8 3.8
Figure imgf000024_0003
5.8% 0.46 10.7 4.3 3.8 3.5 3.6 Na3PO4.12H20 1
3.3% 0.60 9.1 2.9 2.9 Na2C03
1.6% 0.30 9.6 3.8 3.7 3.5 3.7 Na2C03
0.8% 0.15 9.2 4.0 3.7 Na2C03
See footnote of Table III.
Disodium acid pyrophosphate.
Tetrasodium pyrophosphate.
Pentasodium tripolyphosphate.
Sodium hexametaphosphate.
The data show that use of the polyphosphate catalysts led to higher initial durable press ratings than were obtainable with sodium carbonate, and after 40 launder- ings of the treated fabrics, durable press ratings were higher with polyphosphates as curing catalysts, than when disodium phosphate or trisodium phosphate were used.
Other textile properties were determined on the treated samples prior to machine laundering. As shown in Table VII, the polyphosphate catalysts gave wrinkle recovery and strength retention equivalent to those obtainable with, the other catalysts tested.
Table VII
Warp Warp Stiffness
Wrinkle Recovery Tear Break Bending
Curing Anqle (W+F) Strength Strength Mxnent Catalyst Cαnd. Wet Ret i ed Retained (Warp)
4.1% Na4P207 284° 238° 65% 60% 4.7xl0"4in.-lb.
5.6% Na5P3O10 281 232 65 56 5.0
4.4% a2HP04 285 237 65 55 4.3
5.8% Na3P04.12H20281 226 66 61 4.0
Untreated fabric 200 141 (100) (100) 4.8
Example 5 Polyphosphate and Hypophosphite
Salts as Curing Catalysts for the
Durable Press Finishing of Cotton
Fabric with Citric Acid without Softener
An aqueous treating bath was prepared containing 6.9% citric acid, and a stated catalyst. An all-cotton desized, scoured and bleached 80x80 printcloth weighing
3.2 oz/yd was thoroughly wetted by immersion in this treating bath, was passed between the rolls of a wringer, was again immersed in the treating bath, and was again passed through the wringer, the pressure of the wringer rolls being sufficient to give a wet pickup of 90-100% of aqueous mixture on the fabric, based on the original weight of fabric sample. The fabric was then dried in a forced draft oven at 85°C for 5 minutes, and was heat- cured in a second forced draft oven at 180°C for 90 seconds, causing some fabric yellowing. The fabric was subsequently machine laundered and tumble dried. Textile properties after the one laundering cycle are reported in
Table VIII. Table VIII
Wrinkle
Catalyst Fabric Durable Recovery Tear Break
(% in pad weight press Angle, cond., Strength Strength
(bath) % gain, % rating deg, (W+F) retained,% retained,%
(NaP04)6
(11.0) 5.7 3.5 231 59 53
(6.6) 5.6 3.5 235 48 47
(4.4) 4.2 3.5 235 51 47
(2.2) 3.8 3.0 237 51 46
Na4P4012
(10.0) 7.4 3.5 231 60 59
(6.5) 6.0 3.5 236 59 53
(4.5) 4.4 3.3 241 53 48
(2.5) 3.8 3.0 236 52 46
Figure imgf000026_0001
(8.0) 3.0 2.0 212 73 62
(4.8) 2.8 1.5 226 65 57
(3.2) 2.9 2.0 224 64 55
(2.4) 3.0 1.5 232 59 53
Figure imgf000026_0002
(5.9) 3.3 3.5 245 49 43
(4.9) 3.3 3.5 248 49 47
(3.9) 3.4 3.5 251 52 45
(2.9) 2.9 3.5 249 52 48
Untreated 1.0 177 100 100 fabric
Referring to the catalysts in the order in which listed in Table VIII, sodium hexametaphosphate, sodium tetrametaphosphate , tetrasodium pyrophosphate r and sodium hypophosphite curing catalysts for durable press finishing of cotton fabric with citric acid improved the appearance properties over that of untreated cotton. Greatest improvements were obtained when sodium hexameta¬ phosphate, sodium tetrametaphosphate and sodium hypophos¬ phite were the curing catalysts. Improvements were realized over a range of catalyst concentrations . Example 6
Sodium Hypophosphite as a Curing Catalyst for the Durable Press Finishing of Cotton
Fabric with Citric Acid without Fabric Softener Aqueous treating baths were prepared containing citric acid in a range of concentrations and sodium hypo¬ phosphite curing catalysts as 50% of agent weight. An all-cotton desized, scoured and bleached 80x80 printcloth
•j weighing 3.2 oz/yd"1 was thoroughly wetted by immersion n the treating bath, was passed between the rolls of a wringer, was again immersed in the treating bath, and was again passed through the wringer, the pressure of the wringer rolls being sufficient to give a wet pickup of 90-100% of aqueous mixture on the fabric, based on the original weight of fabric sample. The fabric was then dried in a forced draft oven at 85°C for 5 minutes, and was heat-cured in a second forced draft oven at 180°C for 90 seconds. The fabric was subsequently machine laundered and tumble dried. Textile properties after the one laundering cycle are reported in Table IX.
TABLE IX
Citric acid Fabric Durable Wrinkle Tear Break
(% in pad weight press Recovery Angle, strength strength bath) % gain, % rating cαnd. , deg. , (W+F) retained, % retained,%
12 6.4 3.5 253 36 42
9 3.9 3.5 253 37 41
7 3.3 3.5 249 42 42
5 1.3 3.3 241 42 45
Sodium hypophosphite , used as a curing catalyst for citric acid, produced durable press properties in cotton fabric .
All of the samples of Examples 5 and 6 that were treated with citric acid to produce durable press appearance properties in cotton fabric were yellowed by the treatment ; the yellow color could be substantially removed by treatment with the following agents: 1.5% magnesium monoperoxide, 1.5% sodium perborate, 1.5% sodium tetraborate, 1.5% boric acid, 1.5% sodium borohydride, 2% HCl, and 1% NaOCl.

Claims

1. A process for treating fibrous cellulosic material, comprising: impregnating fibrous cellulosic material with a treating solution containing a poly¬ carboxylic acid and a curing catalyst; the polycarboxylic acid being selected from the group consisting of: aliphatic, alicyclic and aro¬ matic acids either olefinically saturated or unsaturated and having at least three carboxyl groups per molecule; aliphatic, alicyclic and aromatic acids having two car¬ boxyl groups per molecule and having a carbon-carbon double bond located alpha, beta to one or both of the carboxyl groups; aliphatic acids either olefinically saturated or unsaturated and having at least three car- boxyl groups per molecule and a hydroxyl group present on a carbon atom attached to one of the carboxyl groups of the molecule; and, said aliphatic and alicyclic acids wherein the acid contains an oxygen or sulfur atom in the chain or ring to which the carboxyl groups are attached; one carboxyl group being separated from a second carboxyl group by either two or three carbon atoms in the ali¬ phatic and alicyclic acids; one carboxyl group being ortho to a second carboxyl group in the aromatic acids; and, one carboxyl group being in the cis configuration relative to a second carboxyl group where two carboxyl groups are separated by a carbon-carbon double bond or are both connected to the same ring; the curing catalyst being selected from the group consisting of alkali metal hypophosphites, alkali metal phosphites, and alkali metal polyphosphates, and heating the material to produce esterifi¬ cation and crosslinking of the cellulose with the poly¬ carboxylic acid in the material.
2. The process of claim 1 wherein the poly- carboxylic acid is selected from the group consisting of: maleic acid, citraconic acid; citric acid; itaconic acid; tricarballylic acid; trans-aconitic acid; 1,2,3,4- butanetetracarboxylic acid; all-cis-1,2,3,4,-cyclopen- tanetetracarboxylic acid; mellitic acid; oxydisuccinic acid; and, thiodisuccinic acid.
3. The process of claim 2 wherein the curing catalyst is selected from the group consisting of sodium hypophosphite, disodium phosphite, disodium acid pyro¬ phosphate, tetrasodium pyrophosphate r pentasodium tri- polyphosphate, and sodium hexametaphosphate.
4. The process of claim 1 wherein the fibrous cellulosic material contains not less than 30% by weight of cellulosic fibers selected from the group consisting of cotton, flax, jute, hemp, ramie and regenerated unsub- stituted wood celluloses.
5. Fibrous cellulosic material treated by a process comprising: impregnating the fibrous cellulosic material with a treating solution containing a poly¬ carboxylic acid and a curing catalyst; the polycarboxylic acid being selected from the group consisting of aliphatic, alicyclic and aromatic acids either olefinically saturated or unsaturated and having at least three carboxyl groups per molecule; aliphatic, alicyclic and aromatic acids having two car¬ boxyl groups per molecule and having a carbon-carbon double bond located alpha, beta to one or both of the carboxyl groups; aliphatic acids either olefinically saturated or unsaturated and having at least three car¬ boxyl groups per molecule and a hydroxyl group present on a carbon atom attached to one of the carboxyl groups of the molecule; and, said aliphatic and alicyclic acids wherein the acid contains an oxygen or sulfur atom in the chain or ring to which the carboxyl groups are attached; one carboxyl group being separated from a second carboxyl group by either two or three carbon atoms in the ali- phatic and alicyclic acids; one carboxyl group being ortho to a second carboxyl group in the aromatic acids; and, one carboxyl group being in the cis configuration relative to a second carboxyl group where two carboxyl groups are separated by a carbon-carbon double bond or are both connected to the same ring; the curing catalyst being selected from the group consisting of alkali metal hypophosphites, alkali metal phosphites, and alkali metal polyphosphates; and, heating the material to produce esterifi¬ cation and crosslinking of the cellulose with the poly¬ carboxylic acid in the material.
6. The fibrous cellulosic material of claim 5 wherein the polycarboxylic acid is selected from the group consisting of maleic acid; citraconic acid; citric acid; itaconic acid; tricarballylic acid; trans-aconitic acid; 1,2,3,4-butanetetracarboxylic acid; all-cis- 1,2,3,4-cyclopentanetetracarboxylic acid; mellitic acid; oxydisuccinic acid; and thiodisuccinic acid.
7. The fibrous cellulosic material of claim 6 wherein the curing catalyst is selected from the group consisting of sodium hypophosphite, disodium phosphite, disodium acid pyrophosphate, tetrasodium pyrophosphate, pentasodium tripolyphosphate, and sodium hexametaphos¬ phate.
8. The fibrous cellulosic material of claim 5 wherein the polycarboxylic acid is 1,2,3,4-butanetetra- carboxylic acid and the curing catalyst is selected from the group consisting of sodium hypophosphite, disodium phosphite, disodium acid pyrophosphate, tetrasodium pyro¬ phosphate, pentasodium tripolyphosphate, and sodium hexa¬ metaphosphate.
PCT/US1989/002628 1988-06-16 1989-06-16 Catalysts and processes for formaldehyde-free durable press finishing of cotton textiles with polycarboxylic acids WO1989012714A1 (en)