WO1992009353A1 - Dioxole/tfe copolymer composites - Google Patents
Dioxole/tfe copolymer composites Download PDFInfo
- Publication number
- WO1992009353A1 WO1992009353A1 PCT/US1991/008629 US9108629W WO9209353A1 WO 1992009353 A1 WO1992009353 A1 WO 1992009353A1 US 9108629 W US9108629 W US 9108629W WO 9209353 A1 WO9209353 A1 WO 9209353A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- sample
- coating
- samples
- teflon
- test
- Prior art date
Abstract
Description
Claims