WO1995022083A2 - Photomask blanks - Google Patents
Photomask blanks Download PDFInfo
- Publication number
- WO1995022083A2 WO1995022083A2 PCT/US1995/001393 US9501393W WO9522083A2 WO 1995022083 A2 WO1995022083 A2 WO 1995022083A2 US 9501393 W US9501393 W US 9501393W WO 9522083 A2 WO9522083 A2 WO 9522083A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- film
- photomask blank
- eps
- phase shifter
- wavelength
- Prior art date
Abstract
Description
Claims