WO1996022485A1 - Plastics pipe - Google Patents
Plastics pipe Download PDFInfo
- Publication number
- WO1996022485A1 WO1996022485A1 PCT/EP1996/000211 EP9600211W WO9622485A1 WO 1996022485 A1 WO1996022485 A1 WO 1996022485A1 EP 9600211 W EP9600211 W EP 9600211W WO 9622485 A1 WO9622485 A1 WO 9622485A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- protective layer
- pipe
- outer protective
- inner core
- plastics
- Prior art date
Abstract
Description
Claims