WO1998008677A1 - Drag reduction article - Google Patents
Drag reduction article Download PDFInfo
- Publication number
- WO1998008677A1 WO1998008677A1 PCT/US1997/000171 US9700171W WO9808677A1 WO 1998008677 A1 WO1998008677 A1 WO 1998008677A1 US 9700171 W US9700171 W US 9700171W WO 9808677 A1 WO9808677 A1 WO 9808677A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- polymer
- layer
- drag reduction
- drag
- vinylidene fluoride
- Prior art date
Abstract
Description
Claims