WO2001063020A1 - Method and apparatus for growing low defect density silicon carbide and resulting material - Google Patents
Method and apparatus for growing low defect density silicon carbide and resulting material Download PDFInfo
- Publication number
- WO2001063020A1 WO2001063020A1 PCT/US2001/004601 US0104601W WO0163020A1 WO 2001063020 A1 WO2001063020 A1 WO 2001063020A1 US 0104601 W US0104601 W US 0104601W WO 0163020 A1 WO0163020 A1 WO 0163020A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- silicon carbide
- growth
- crystal
- single crystal
- defects
- Prior art date
Abstract
Description
Claims