WO2001080957A2 - Multi-core, multi-cover golf ball - Google Patents
Multi-core, multi-cover golf ball Download PDFInfo
- Publication number
- WO2001080957A2 WO2001080957A2 PCT/US2001/012235 US0112235W WO0180957A2 WO 2001080957 A2 WO2001080957 A2 WO 2001080957A2 US 0112235 W US0112235 W US 0112235W WO 0180957 A2 WO0180957 A2 WO 0180957A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- golf ball
- core
- layer
- ball
- specific gravity
- Prior art date
Abstract
Description
Claims