WO2002031243A1 - Tissu pour tente, fil retors de chanvre indien, et procede de production correspondant - Google Patents

Tissu pour tente, fil retors de chanvre indien, et procede de production correspondant Download PDF

Info

Publication number
WO2002031243A1
WO2002031243A1 PCT/JP2001/008767 JP0108767W WO0231243A1 WO 2002031243 A1 WO2002031243 A1 WO 2002031243A1 JP 0108767 W JP0108767 W JP 0108767W WO 0231243 A1 WO0231243 A1 WO 0231243A1
Authority
WO
WIPO (PCT)
Prior art keywords
yarn
kenaf
fiber
twisted
producing
Prior art date
Application number
PCT/JP2001/008767
Other languages
English (en)
French (fr)
Inventor
Tsuyoshi Torii
Hiroshi Toyoda
Kenji Tada
Haruyoshi Kinoshita
Original Assignee
Taiyo Kogyo Corporation
Asahi Textile Co., Ltd.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Taiyo Kogyo Corporation, Asahi Textile Co., Ltd. filed Critical Taiyo Kogyo Corporation
Priority to US10/275,578 priority Critical patent/US6968866B2/en
Priority to EP01972694A priority patent/EP1354990A4/en
Priority to JP2002534603A priority patent/JP3730621B2/ja
Priority to AU2001292357A priority patent/AU2001292357A1/en
Publication of WO2002031243A1 publication Critical patent/WO2002031243A1/ja

Description

テント生地及びケナフ交撚糸並びにその製造方法 技術分野
本発明は、 例えば、 ドーム型野球場などの各種競技場の屋根や、 運動会などに用 いられる小型テントの屋根や、 付帯設明備及び博覧会展示場などの屋根及び壁などに 用いられるテント生地及びケナフ交撚糸並田びにその製造方法に関する。 背景技術
従来、 例えば、 運動会に用いられる集会用天幕や、 博覧会の大型膜構造物の屋根 材などとして用いられるテント生地は、 各種の合成繊維糸からなる織物に、 防水性 付与のため軟質塩化ビニル樹脂などを被覆したものが一般的に用いられている。 ま た、 防炎性を付与するため、 被覆樹脂にハロゲン化合物等が含有されたテント生地 も用いられている。
しかしながら、 かかる合成繊維糸からなるテント生地は、 使用するとともに再生 することが困難な程度まで劣化することから、 使用後に焼却処分とされる傾向にあ る。 しかし、 焼却することによってダイォキシンなどの各種化学物質や有害ガスが 発生するおそれがある。 そのため、 従来、 テント生地は、 産業廃棄物として埋め立 て処分とされていることが多い。
本発明は、 上記の点に鑑み、 使用後、 容易に再利用を図ることができ、 省資源化 及び環境保護に資するテント生地を提供することを第一の課題とするものである。 また、 高密度で且つ高強度の織物が可能でテント生地に最適なケナフ交撚糸並び にその製造方法を提供することを第二の課題とするものである。 発明の開示
本発明が上記の課題を解決するために講じた技術的手段は、 テント生地及びケナ フ交撚糸並びにその製造方法としてなされたもので、 テント生地としての特徴は、 ケナフ繊維を含む繊維糸の織物からなるテント生地を解決手段とする。
さらに、 前記繊維糸は、 ケナフ繊維を 1 0重量％以上含んでいるものが好ましい。 かかるテント生地は、 ァオイ科植物から得られたケナフ繊維からなるので、 使用 後、 紙として容易に再利用を図ることができる。
ケナフ交撚糸としての特徴は、 ケナフ繊維からなる糸と、 化学繊維又は天然繊維 等からなる糸とを撚り合わせたケナフ交撚糸であつて、 前記化学繊維等からなる糸 は一定の張力でケナフ繊維からなる糸に撚り合わされていることにある。
ケナフ交撚糸の製造方法としての特徴は、 ケナフ繊維からなる糸と、 化学繊維又 は天然繊維等からなる糸とを撚り合わせて撚糸を製造するケナフ交撚糸の製造方法 において、 前記化学繊維等からなる糸を一定の張力で且つケナフ繊維からなる糸よ りも速く送り出すことにある。
また、 ケナフ繊維からなる糸と、 化学繊維又は天然繊維等からなる糸とを撚り合 わせて撚糸を製造するケナフ交撚糸の製造方法において、 引っ張り力でそれぞれの 糸が伸長して略同時に破断するように、 両方の糸の伸び率に基づいてそれぞれの送 り速度を制御することにある。
以上のように、 本発明に係るテント生地は、 それを構成する繊維糸としてケナフ 繊維を用いているので、 テント生地の使用後、 容易に紙に再生使用することができ る。
従って、 従来のテント生地のように、 廃棄処分する必要性がなく、 使用後の再利 用を図り、 省資源化が可能となり、 地球温暖化を間接的に抑制し、 環境保護に資す るものである。
また、 本発明のケナフ交撚糸は、 糸の太さと強度が安定し、 弓 Iつ張り強度が向上 し、 糸の滑りが良くなるので、 高密度及び高強度の織物が可能となり、 特に、 テン ト生地に最適である。 図面の簡単な説明
図 1は、 本発明の一実施の形態を示すケナフ交撚糸の断面図である。
図 2は、 本発明の一実施の形態を示すテント生地の断面図である。 発明を実施するための最良の形態
以下、 本発明の実施形態に関して説明する。
本発明のテント生地は、 ケナフ繊維を含む繊維糸からなる織物によって構成され ている。
ケナフ繊維は、 ケナフ （ァオイ科植物） 力 得られた繊維質をいい、 その原産地 などは問わず、 各種のものが使用できる。
ケナフ繊維からなる繊維糸は、 ケナフの繊維質のみから紡績糸 （ケナフ繊維が 1 0 0重量％) されていてもよいし、 ケナフ以外の繊維との混紡糸であってもよい。 ケナフ以外の繊維としては、 黄麻や綿などの他の天然繊維や、 レーヨン等の化学 繊維、 ポリエステル （P E T) などの合成繊維などを用いることができる。
混紡糸を用いた場合に於けるケナフ繊維とそれ以外の繊維の混合割合は、 特に限 定されないが、 ケナフ繊維が 1 0重量％以上、 好ましくは 5 0重量％以上が好まし い。
上記ケナフを含む繊維糸は、 公知の用法に従い、 原料ケナフを水に浸漬し、 靭皮 を分離し、 これを乾燥して靭皮繊維を得、 適当な長さ （5 0 mm程度） に切断し、 これを紡績機にかけて紡績することにより得ることができる。 混紡糸にする際には、 他の繊維を混合しながら紡績機にて紡績する。
得られた繊維糸は、 公知の用法に従い、 織物に形成される。 織り方は特に限定さ れず、 通常の平織り又は綾織り等にすればよい。
また、 織物は、 ケナフ繊維のみからなる繊維糸のみで織られたものや、 ケナフ繊 維とそれ以外の繊維との混紡糸のみで織られたものや、 前記ケナフ繊維のみからな る繊維糸と前記混紡糸とで織られたものや、 前記ケナフ繊維のみからなる繊維糸又 は 及び前記混紡糸とケナフ繊維を含まない他の繊維糸とで織られたものなど各種 の態様のものが例示される。
尚、 必要に応じて、 織物の少なくとも一面に防水処理ゃ耐光処理などの耐侯性処 理ゃ、 防火防炎処理などを行ってもよい。 この時の処理材料もポリオレフイン等、 紙としてリサイクルする時に、 妨害にならない環境に悪影響を与えないものを選択 する。
かかるケナフ繊維を含む織物は、 例えば、 適宜の形状に裁断されてテント生地と して使用される。 ケナフは、 生長が早く、 炭酸ガスの固定能に優れているので、 か かるケナフ繊維を用いたテント生地を使用することは、 地球温暖化を間接的に抑制 し、 環境浄化に貢献できるものとなる。
そして、 本発明のテント生地は、 長期間使用して劣ィ匕したり、 或いは一部破断し たりして使用できなくなった後には、 これを回収して紙に再生することが可能であ る。
紙への再生工程は、 従来の用法に従い、 廃テント生地を適当な大きさに裁断し、 ミキサーに投入して水と共に攪拌し、 薬品を入れて加熱し、 スクリーンに通して粗 ゴミを除去し、 その後、 再度スクリーンに通してシックナ一で脱水処理を行い、 古 紙パルプを得る。 これを、 必要に応じて新パルプを混合した後、 抄紙機を用いて漉 くことにより、 再生紙が製造される。
次に、 前記ケナフの繊維質のみから紡績糸又は混合糸等 （ケナフ糸） と化学繊維 からなる糸 （押え糸） としてのポリエステル糸との交撚糸ついて説明する。 図 1に 示す如く、 ケナフ糸 1とポリエステル糸の双糸 （PET双糸） 2とを撚り合わせる のであるが、 ケナフ糸 1の送り速度 （VI) よりも PET双糸 2の送り速度 (V 2) を若干速く設定する。 具体的には、 1< (V2ZV1) <1. 1の関係を満た す。 更に、 好ましくは 1く （V2/V1) <1. 05の関係にある。 また、 ケナフ 糸 1及び PET双糸 2は、 それぞれ一定の速度で且つ一定の張力で送り出され、 し かあ、 撚り状態は、 甘撚り糸とする。 撚り回数は、 例えば 100回 Zm程度とする のが好ましい。
ケナフ糸は、 他の天然繊維に比し、 繊維自体が太いので、 糸に凹凸があり （図 1 に仮想線で示す。 ） 、 太さと強度の安定が悪く、 ケナフ 100 %では強度の確保が できない。 しかしながら、 前記の方法で交撚糸 3を製造すると、 若干長めに送り出 された PET双糸 2が、 ケナフ糸 1に対して一定の張力で巻付けられるため、 ケナ フ糸 1の太い部分 l aは、 PET双糸 2に締め付けられて細く締まり、 毛羽を抑え、 細い部分 lbは、 PET双糸 2の締め付け力が小さいため、 ほとんど変化すること はなく、 ここに略一定太さで強度が安定し且つ強力な交撚糸 3を製造することがで ぎる。
力 る交撚糸 3を例えば、 緯糸として使用して織物とした場合には、 糸の滑りが 良く、 毛羽を抑えていることから、 高強度で且つ高密度の織物が可能となり、 前記 テント生地に最適である。 尚、 縦糸は、 表面の凹凸がほとんどないポリエステル系 のものを使用するのが好ましいが、 特に限定されるものではない。
また、 ケナフ交撚糸 3は、 前記の実施の形態に限らず、 次のようなものであって も良い。 具体的には、 ケナフ糸 1と、 PET双糸 2を使用するのは前記と同様であ るが、 両方の糸の伸び率に基づいてそれぞれの送り速度を制御することにより、 更 に、 弓 Iつ張り力に対して強力な撚糸とした。
例えば、 ケナフ糸のケナフはジユート番手で 7番単糸を、 PET糸は綿番手で 2 0番双糸をそれぞれ使用する。 そして、 両方の糸の単位長さ当り切断する限界の伸 び率を測定する。 例えば、 ケナフ糸の伸び率が 5%であり、 PET双糸の伸び率が 15%であったとする。 伸び率の大きい数値から小さい数値を引き、 両数値の差を 求める （15— 5 = 10%) 。 本実施の形態では、 P E T双糸 2はケナフ糸 1に比 し、 単位長さ当り 10%伸びることとなる。
従って、 伸び率の小さいケナフ糸 1を、 伸び率の大きな PET双糸 2に比し、 数 値差の分 （単位長さ当り 10%) だけ一定速度で且つ速く送り出して燃り合わせる ことによって、 ケナフ糸を緩めながら撚りをかける。 この結果、 ケナフ交撚糸 3に 張力が作用した際には、 両方の糸が略同時に切断するため、 更に強力な交撚糸が製 造できる。 しかも、 ケナフ糸 1は PET双糸 2と撚られていることから、 ケナフ糸 の凹凸が少なくでき、 毛羽も抑えることは可能である。 本発明は上記の実施の形態に限定されるものではなく、 押え糸としては P E T双 糸 2以外に、 3本以上のポリエステル糸からなるものや、 天然繊維等からなるもの が採用可能である。
尚、 前記それぞれの交撚糸を使用した織物は、 高強度及び高密度のものが得られ るため、 テント生地として最適であるが、 その他の生地としても使用できることは 無論である。
実施例
図 2にテント生地としての実施例を示す。 同図のテン卜生地 10は、 前記織物 (基布） 11の両面にコ一ティング層 12を設けたものである。
基布 11は、 縦糸としてポリエステル糸 13を、 緯糸として前記ケナフ交撚糸 3 をそれぞれ使用し、 2X 2の綾織とした。 尚、 ポリエステル糸とケナフ交撚糸 3 の重量比率は、 23 : 73である。
前記基布 11に EVA (エチレン '酢酸ビニル共重合体） を両面にコーティング した。
重量は、 基布が 403 (g/m2) 、 EVAが 400 (g/ra2) であり、 テン ト生地 10としては、 804 (gZm2) であった。
前記テント生地 10からパルプを取り出してリサイクルすべく、 以下のような実 験を行った。 具体的には、 アルカリ蒸解法を採用する。 公知の回転オートクレープ の中に、 前記テント生地の小片 （500 g) 、 水 （1リットル） 及び水酸化ナトリ ゥム （350 g) をそれぞれ投入した。
そして、 オートクレ一ブ内を温度が 170〜180° Cで且つ圧力が 7〜8 k g fZcm2に維持しながら、 4時間にわたって蒸解試験を行った。 その結果とし て、 EVAとポリエステル繊維は溶解し、 ケナフ繊維のみが残留するのを確認でき、 従って、 パルプの取り出しが可能となった。

Claims

請 求 の 範 囲
1. ケナフ繊維を含む繊維糸の織物からなることを特徴とするテント生地。
2. 前記繊維糸が、 ケナフ繊維を 10重量％以上含む請求項 1記載のテント生地。
3. 前記繊維糸が、 前記ケナフ繊維からなる糸 （1) と、 化学繊維又は天然繊維等 からなる糸 （2) を撚り合わせて形成されている請求項 1記載のテント生地。
4. ケナフ繊維からなる糸 （1) と、 化学繊維又は天然繊維等からなる糸 （2) と を撚り合わせたケナフ交撚糸であって、 前記化学繊維等からなる糸 （2) は一定の 張力でケナフ繊維からなる糸 （1) に撚り合わされていることを特徴とするケナフ 交撚糸。
5. ケナフ繊維からなる糸 （1) と、 化学繊維又は天然繊維等からなる糸 （2) と を撚り合わせて撚糸 (3) を製造するケナフ交撚糸の製造方法において、 前記化学 繊維等からなる糸 （2) を一定の張力で且つケナフ繊維からなる糸 （1) よりも速 く送り出すことを特徴とするケナフ交撚糸の製造方法。
6. ケナフ繊維からなる糸 （1) と、 化学繊維又は天然繊維等からなる糸 （2) と を撚り合わせて撚糸 (3) を製造するケナフ交撚糸の製造方法において、 引っ張り 力でそれぞれの糸が伸長して略同時に破断するように、 両方の糸 （1) ， （2) の 伸び率に基づいてそれぞれの送り速度を制御することを特徴とするケナフ交撚糸の 製造方法。
PCT/JP2001/008767 2000-10-10 2001-10-04 Tissu pour tente, fil retors de chanvre indien, et procede de production correspondant WO2002031243A1 (fr)