WO2002051892A1 - High refractive index microreplication resin - Google Patents
High refractive index microreplication resin Download PDFInfo
- Publication number
- WO2002051892A1 WO2002051892A1 PCT/US2001/014040 US0114040W WO02051892A1 WO 2002051892 A1 WO2002051892 A1 WO 2002051892A1 US 0114040 W US0114040 W US 0114040W WO 02051892 A1 WO02051892 A1 WO 02051892A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- composition
- monomer
- optical
- formula
- methyl
- Prior art date
Abstract
Description
Claims