WO2002053354A2 - Layer normalizing device for selective deposition modeling - Google Patents
Layer normalizing device for selective deposition modeling Download PDFInfo
- Publication number
- WO2002053354A2 WO2002053354A2 PCT/US2002/000631 US0200631W WO02053354A2 WO 2002053354 A2 WO2002053354 A2 WO 2002053354A2 US 0200631 W US0200631 W US 0200631W WO 02053354 A2 WO02053354 A2 WO 02053354A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- layer
- build material
- normalizing
- flowable
- wicking member
- Prior art date
Abstract
Description
Claims