WO2003020529A1 - Digitally printed products and process - Google Patents
Digitally printed products and process Download PDFInfo
- Publication number
- WO2003020529A1 WO2003020529A1 PCT/US2002/027640 US0227640W WO03020529A1 WO 2003020529 A1 WO2003020529 A1 WO 2003020529A1 US 0227640 W US0227640 W US 0227640W WO 03020529 A1 WO03020529 A1 WO 03020529A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- baseweb
- process according
- color
- printed
- ink
- Prior art date
Abstract
Description
Claims