WO2003020780A1 - Three-dimensional copolymers of polyphenylene ether resins and sytrenic resins - Google Patents
Three-dimensional copolymers of polyphenylene ether resins and sytrenic resins Download PDFInfo
- Publication number
- WO2003020780A1 WO2003020780A1 PCT/US2002/016263 US0216263W WO03020780A1 WO 2003020780 A1 WO2003020780 A1 WO 2003020780A1 US 0216263 W US0216263 W US 0216263W WO 03020780 A1 WO03020780 A1 WO 03020780A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- polyphenylene ether
- acrylonitrile
- monomers
- styrene
- composition
- Prior art date
Abstract
Description
Claims