WO2005086782A2 - Blue light emitting semiconductor nanocrystal materials - Google Patents
Blue light emitting semiconductor nanocrystal materials Download PDFInfo
- Publication number
- WO2005086782A2 WO2005086782A2 PCT/US2005/007454 US2005007454W WO2005086782A2 WO 2005086782 A2 WO2005086782 A2 WO 2005086782A2 US 2005007454 W US2005007454 W US 2005007454W WO 2005086782 A2 WO2005086782 A2 WO 2005086782A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- nanocrystal
- blue light
- population
- nanocrystals
- semiconductor material
- Prior art date
Abstract
Description
Claims